Patent Application
20210008507
Embodiments relate to diblock or multiblock copolymer based isoporous mesoporous asymmetric materials comprising macrovoids.
Mesoporous isoporous block copolymer materials are known and are useful due to their small, uniform pores. Combining an asymmetric structure with the mesoporous isoporous structure makes the materials very useful for high resolution, high flux separations wherein the mesoporous isoporous “skin” enables high resolution separations and the asymmetric structure enables high flux. The manufacturing of these materials, however, often results in macrovoids that are deemed undesirable. It is widely taught that macrovoids in membranes are undesirable as they cause mechanical weakness and can breach the skin causing defects.
Abetz 2014a and Abetz 2015 teach about self-assembled diblock copolymer membranes made with solvent mixtures primarily based on tetrahydrofuran (THF) and dimethylformamide (DMF) at different ratios with various poly(styrene-block-4-vinylpyridine) polymers at multiple concentration (19 to 35 wt %) and short evaporation windows (5-10 s). No macrovoids are shown in the materials' structures in the library of conditions explored. Abetz 2014b also characterizes the adsorption of lysozyme protein near its isoelectric point (11.4). However, these membranes demonstrate more than 120 μg/cm2 in lysozyme adsorption and it teaches that the lysozyme adsorption is independent of the membrane pore size and polymer used for the membrane formation.
Besides the well-known typically DMF/THF solvent composition, diblock copolymer membranes from solvents combination of: 1,4-dioxane (DOX)/THF, DOX/DMF, DOX/THF/DMF are also taught in Abetz 2012, Abetz 2014b, Abetz 2015, Abetz 2017, Peinemann 2010, Peinemann 2011, and Peinemann 2014a.
A method of forming isoporous membranes with a sponge-like structure based on self-assembly of block copolymers is described by Peinemann & Abetz 2007 (also see ‘694 application’). However, none of the structures include macrovoids. Additionally, in Peinemann & Nunes 2012, it is taught in paragraph [0011] that “The method (694 application) has been difficult to reproduce. When the procedure described in the '694 application is applied to commercially available purified block copolymers it does not lead to isoporous membranes.” Peinemann & Nunes 2012 also does not include the macrovoid structural feature. While the 694 application states that “Optionally, the casting solution can also contain one or more nonsolvents for the block copolymer in addition to a solvent” no mention of expected outcome is discussed.
Peinemann 2014b teaches a DMF/DOX/Acetone (24 wt %/42 wt %/16 wt %) solvent composition to make diblock copolymer membranes. However, the membranes made from this solution do not comprise macrovoids or a transition layer.
Journal of Membrane Science, 451, 2014 266-275
Polymer 2014, 55, 1327-1332
The following description of the embodiments is merely exemplary in nature and is in no way intended to limit the subject matter of the present disclosure, their application, or uses.
As used throughout, ranges are used as shorthand for describing each and every value that is within the range. Any value within the range can be selected as the terminus of the range.
For the purposes of this specification and appended claims, unless otherwise indicated, all numbers expressing quantities, percentages or proportions, and other numerical values used in the specification and claims, are to be understood as being modified in all instances by the term “about.” The use of the term “about” applies to all numeric values, whether or not explicitly indicated. This term generally refers to a range of numbers that one of ordinary skill in the art would consider as a reasonable amount of deviation to the recited numeric values (i.e., having the equivalent function or result). For example, this term can be construed as including a deviation of ±10 percent, alternatively ±5 percent, and alternatively ±1 percent of the given numeric value provided such a deviation does not alter the end function or result of the value. Accordingly, unless indicated to the contrary, the numerical parameters set forth in this specification and attached claims are approximations that can vary depending upon the desired properties sought to be obtained by the present invention.
It is noted that, as used in this specification and the appended claims, the singular forms “a,” “an,” and “the,” include plural references unless expressly and unequivocally limited to one referent. As used herein, the term “include” and its grammatical variants are intended to be non-limiting, such that recitation of items in a list is not to the exclusion of other like items that can be substituted or added to the listed items. For example, as used in this specification and the following claims, the terms “comprise” (as well as forms, derivatives, or variations thereof, such as “comprising” and “comprises”), “include” (as well as forms, derivatives, or variations thereof, such as “including” and “includes”) and “has” (as well as forms, derivatives, or variations thereof, such as “having” and “have”) are inclusive (i.e., open-ended) and do not exclude additional elements or steps. Accordingly, these terms are intended to not only cover the recited element(s) or step(s), but may also include other elements or steps not expressly recited. Furthermore, as used herein, the use of the terms “a” or “an” when used in conjunction with an element may mean “one,” but it is also consistent with the meaning of “one or more,” “at least one,” and “one or more than one.” Therefore, an element preceded by “a” or “an” does not, without more constraints, preclude the existence of additional identical elements.
The present disclosure relates to an isoporous mesoporous block copolymer asymmetric material comprising a transition layer and further comprising macrovoids. Embodiments disclosed herein also relate to methods of producing said materials. The disclosed materials show remarkably low protein adsorption and integrate with porous supports. Comparable materials lacking both macrovoids and a transition layer show much higher protein adsorption and do not integrate with porous supports, both of which are undesirable.
In the context of the disclosure, isoporous means having a substantially narrow pore diameter distribution. For example, a narrow pore size distribution. In the context of the disclosure, mesoporous means the pore diameters ranges from 1 nm to 200 nm. One surface of the material disclosed comprises isoporous mesopores, which is the selective layer, or “skin”. In the context of the disclosure, macroporous or macropore means that at least two pore dimensions are greater than 1 micron. In the context of the disclosure, freestanding means not integrally joined with a porous support material.
In some embodiments, the materials comprise at least one diblock copolymer or multiblock copolymer, having a structure in the form of A-B, B-A, B-A-B, A-B-A-B, B-A-B-A, or A-B-A, wherein A and B represent two distinct types of block chemistries. In a preferable embodiment, A is a hydrophilic and/or hydrogen-bonding block and B is a hydrophobic block. Suitable hydrogen-bonding and/or hydrophilic blocks include, but are not limited to, polyvinylpyridines, polyethylene oxides, polyacrylic acids, poly(hydroxystyrene), polvacrylates and polymethacrylates, substituted polyacrylates and polymethacrylates. More specific examples of hydrophilic blocks include: poly(acrylic acid), poly(acrylamide), poly(vinylpyridine), poly(vinylpyrrolidone), poly(vinyl alcohol), naturally derived polymers such as cellulose and chitosan, poly(ether), poly(maleic anhydride), poly(N-isopropylacrylamide), poly(styrene sulfonate), poly(allylhydrochloride), poly(sulfone), poly(ethersulfone), poly(ethylene glycol), poly(2-hydroxyethyl methacrylate). More specific examples of hydrogen-bonding blocks include: poly(vinylpyridine), poly(ethylene oxide), poly(methacrylate), poly(methyl methacrylate), poly(dimethylethyl amino ethyl methacrylate), poly(dimethylaminoethyl methacrylate) poly(acrylic acid), poly(hydroxystyrene), poly(dimethylacrylamide). Suitable hydrophobic blocks can include, but are not limited to, polystyrenes, e.g., polystyrene and poly(alkyl substituted styrene) such as poly(alpha-methyl styrene), polypropylenes, poly(vinyl chlorides), polybutadiene, poly(isoprene), poly(ethylene-stat-butylene), poly(ethylene-alt-propylene), and polytetrafluoroethylenes. Furthermore, substituted analogues of the above are suitable.
The materials' cross-sectional structures are asymmetric, wherein the average pore size increases as the distance from the skin increases. More specifically, in some embodiments the skin of the material comprises mesoporous isopores, and as the distance from this layer increases, the average pore size increases. The pore density can be in the range of at least 1013 pores/m2 to at least 1014 pores/m2.
Macrovoids, or macropores, are pores with at least one characteristic length substantially larger than the typical size of the surrounding pores. For the purpose of describing the disclosed invention, we define a macrovoid or macropore as a void with at least one characteristic length greater than about 0.5 micron. Typical shapes of macrovoids can be, but are not limited to, the following:
The isoporous mesoporous materials also comprise a transition layer with a thickness of at least about 300 nm wherein there is a low macrovoid density and one surface comprises the mesoporous isoporous “skin”. A low macrovoid density means a ratio of macrovoids to mesopores of at most 2×10−9 For example, for a typical mesoporous isoporous diblock material skin pore density of 1014 pores/m2, this correlates to 2×105 macrovoids/m2. This transition layer extends onto an adjacent sub-structure with a thickness of about 1 micron to about 500 microns. The macrovoids are present at high density in the sub-structure layer compared to the transition layer. A high macrovoid density means at least 10° macrovoids/m2. This high macrovoid density is significantly higher than the low macrovoid density of the transition layer. With a low macrovoid density within at least about 300 nm of the skin, it will reduce the fracturing resulting from the macrovoids, and enhance the overall mechanical integrity. Furthermore, the distance from the mesoporous isoporous skin can mitigate top surface defects caused by macrovoids intersecting the skin and can prevent any skin defects from propagating into the sub-structures.
In at least one embodiment, the transition layer is at least about 300 nm. In at least one embodiment, the transition layer is at least about 350 nm. In at least one embodiment, the transition layer is at least about 400 nm. In at least one embodiment, the transition layer is at least about 450 nm. In at least one embodiment, the transition layer is at least about 500 nm.
In some embodiments of the material, the mesopores are in the range of about 1 nm to about 200 nm. In some embodiments, the mesopores are in the range of about 5 nm to about 200 nm. In some embodiments, the mesopores are in the range of about 5 nm to about 100 nm. In some embodiments, the mesopores are in the range of about 5 nm to about 50 nm.
In some applications, macrovoids may also be desired to reduce the amount of polymer needed for the material, making large-scale synthesis more practical while using less starting materials. In some embodiments, the mesoporous isoporous material is freestanding and has a dried density of less than about 0.26 g/cm3. In some embodiments, the mesoporous isoporous material is freestanding and has a dried density of less than about 0.22 g/cm3. In some embodiments, the mesoporous isoporous material is freestanding and has a dried density of less than about 0.20 g/cm3. In some embodiments, the mesoporous isoporous material is freestanding and has a dried density of less than about 0.18 g/cm3. In some embodiments, the mesoporous isoporous material is freestanding and has a dried density of less than about 0.10 g/cm3. Area and mass measurements of the material can be measured on dried material and drying can be performed by heating in an oven at 65° C. for 48 h.
In some instances, a material in accordance with the present disclosure can be produced by a method comprising the following steps:
In some instances, a material in accordance with the present disclosure can be produced by a method comprising the following steps:
In some instances, a mesoporous isoporous asymmetric material comprising macrovoids and a transition layer can be produced by a method comprising the following steps:
In some instances, a mesoporous isoporous asymmetric material comprising macrovoids and a transition layer can be produced by a method comprising the following steps:
In some instances, a material in accordance with the present disclosure can be produced by a method comprising the following steps:
In some instances, a mesoporous isoporous asymmetric material comprising macrovoids and a transition layer can be produced by a method comprising the following steps:
In some embodiments, the concentration of polymer in the polymer solution is from about 3 to 16% by weight. In at least one embodiment, the concentration of polymer in the polymer solution is from about 5 to about 16% by weight. In at least one embodiment, the concentration of polymer in the polymer solution is from about 10 to about 16% by weight. In at least one embodiment, the concentration of polymer in the polymer solution is from about 8 to about 16% by weight. In at least one embodiment of the above materials or methods, at least one diblock copolymer or multiblock copolymer is dissolved in step 1 of one of the above embodiments. In at least one embodiment, more than one diblock or multiblock copolymer is included in the polymer solution and/or material.
In some embodiments, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 20 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 25 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 30 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 35 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 40 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed for at least about 45 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 50 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 55 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 60 seconds. In at least one embodiment, at least a portion of the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for at least about 65 seconds. In some embodiments, the solvent(s) and/or nonsolvent(s) are removed from the polymer solution for example, by an evaporation process. In some instances, the evaporation process can be performed under ambient pressure (1 atm). In some instances, the evaporation process can be performed under reduced pressure. In some instances, the evaporation process can be performed in an inert atmosphere such as nitrogen or argon.
In some embodiments, a polymer solution in accordance with the present disclosure comprises at least one solvent for the block copolymer or block copolymers, and at least one nonsolvent for the block copolymer or block copolymers. Any solvents and/or nonsolvents in the polymer solution should be miscible with each other. The designation of solubility or insolubility of a block copolymer or block in a given chemical or mixture of chemicals depends on the polymer chemistry and/or composition. In some embodiments, at least one solvent is an ether such as 1,4-dioxane or tetrahydrofuran. In some embodiments, at least one nonsolvent is one of the following classes: ketone, ester, alcohol, sulfoxide, sulfone. Some examples of nonsolvents include: acetone, methyl ethyl ketone, methyl isobutyl ketone, methyl amyl ketone, dimethyl ketone, cyclohexanone, propanone, ethyl acetate, propyl acetate, ethanol, isopropanol, benzyl alcohol, butanol, dimethylsulfoxide, and sulfolane.
In some embodiments, a polymer solution in accordance with the present disclosure comprises at least about 33% of one solvent or a combination of solvents and at least about 18% by weight of one nonsolvent or a combination of nonsolvents. In some embodiments of the materials or methods, the polymer solution comprises at least 33% of one solvent or a combination of solvents and about 18% to about 64% by weight of one nonsolvent or a combination of nonsolvents. In some embodiments, a polymer solution in accordance with the present disclosure comprises about 33% to about 79% of one solvent or a combination of solvents and about 18% by weight of one nonsolvent or a combination of nonsolvents. In some embodiments, a polymer solution in accordance with the present disclosure comprises at least about 50% of one solvent or a combination of solvents and at least about 20% by weight of one nonsolvent or a combination of nonsolvents. In some embodiments, a polymer solution in accordance with the present disclosure comprises at least about 50% of one solvent or a combination of solvents and at least about 18% by weight of one nonsolvent or a combination of nonsolvents.
The solvent/nonsolvent percentages totaling 100% can be called “solution composition” and are by weight and include only the solvents'/nonsolvents' weight (that is, the prior to addition of the polymer to the solution to form the polymer solution). In some embodiments, a solution composition in accordance with the present disclosure comprises about 60% of one solvent or a combination of solvents and about 40% by weight of one nonsolvent or a combination of nonsolvents. In some embodiments, a solution composition in accordance with the present disclosure comprises about 70% of a solvent or a combination of solvents and about 30% by weight of one nonsolvent or a combination of nonsolvents. In some embodiments, a solution composition in accordance with the present disclosure comprises about 80% of one solvent or a combination of solvents and about 20% by weight of a nonsolvent or a combination of nonsolvents. In some embodiments of the above methods and materials, at least one diblock copolymer or multiblock copolymer is dissolved in step 1 of one of the above embodiments. In some embodiments of the above methods and materials, the polymer solution or material comprises more than one diblock or multiblock copolymer.
The radius of curvature to fracture can be measured on freestanding materials in the wet state. More specifically, to measure the radius of curvature to fracture, the wet material is curved around a steel rod or other comparable rod or tube of known diameter, forming a “C” shape around the rod. The material is then uncurled and observed for macroscopic cracking along the fold. This test may be performed with the skin facing either towards or away from the rod. The contact length of the material to the rod is approximately 1 cm. In at least one embodiment, a material in accordance with various aspects of the present disclosure can be folded and unfolded according to the above procedure around a rod of diameter down to about 0.020 inches without cracking. In at least one embodiment, a material in accordance with various aspects of the present disclosure can be folded and unfolded according to the above procedure around a rod of diameter down to about 0.028 inches without cracking. In at least one embodiment, a material in accordance with various aspects of the present disclosure can be folded and unfolded according to the above procedure around a rod of diameter down to about 0.030″ without cracking. In at least one embodiment, a material in accordance with various aspects of the present disclosure can be folded and unfolded according to the above procedure around a rod of diameter down to about 0.032 inches without cracking. In at least one embodiment, a material in accordance with various aspects of the present disclosure can be folded and unfolded according to the above procedure around a rod of diameter down to about 0.035 inches without cracking. In at least one embodiment, a material in accordance with various aspects of the present disclosure can be folded and unfolded according to the above procedure around a rod of diameter down to about 0.05 inches without cracking. In at least one embodiment, a material in accordance with various aspects of the present disclosure can be folded and unfolded according to the above procedure around a rod of diameter down to about 0.1 inches without cracking.
In some instances, isoporous mesoporous materials in accordance with various aspects of the present disclosure are freestanding. In some instances, isoporous mesoporous materials in accordance with various aspects of the present disclosure also comprise a porous support or are placed on a porous support. In some instances, isoporous mesoporous materials in accordance with various aspects of the present disclosure also comprise multiple porous supports or are placed on multiple porous supports or some combination of the above. The porous support material(s) may act as a mechanical substrate and provide additional mechanical properties such as stability or biocompatibility or other additional functionalities. The porous support material(s) can include various materials or physical properties for the various layers, thicknesses of the various layers, as well as variations in the pore size and structures. Suitable materials could include knitted, woven, or nonwoven materials, such as gauze, cotton, cellulose-based fabrics, rayon, polyesters, polyethylenes, graphene, graphene oxide, carbon foams, open cell foams such as polyurethane base, polystyrene, rayon, metal, metal oxide, or semiconductor mesh-like support structures. It may be desirable to integrate the mesoporous isoporous materials with aforementioned porous supports. For example, one or more mesoporous isoporous materials may be integrated with one or more porous support materials, preventing delamination or breakage of the material, whereas comparable mesoporous isoporous materials without a transition layer delaminate and break easily. While it is acknowledged that different modes of action are at work within the scope of the invention, in many embodiments, a mechanism of integration of the materials with porous supports is that the macrovoids mitigate stresses at the interface of the porous support, preventing delamination and cracking.
In some embodiments, at least one of said copolymers comprises an A block and a B block, wherein the A block is hydrophilic and/or hydrogen bonding and the B block is hydrophobic. In some embodiments, the block structure is a combination of A and B blocks, for example, A-B, B-A, B-A-B, A-B-A, B-A-B-A, A-B-A-B, etc. In at least one embodiment, at least one copolymer comprises an A block and a B block, wherein the A block is hydrophilic and/or hydrogen bonding and the B block is hydrophobic and the A block is a poly(vinylpyridine). In a least one embodiment, at least one copolymer comprises an A block and a B block, wherein the A block is hydrophilic and/or hydrogen bonding and the B block is hydrophobic and the A block is a poly(vinylpyridine) and the B block is poly(styrene). In at least one embodiment, at least one copolymer comprises an A block and a B block, wherein the A block is hydrophilic and/or hydrogen bonding and the B block is hydrophobic and the A block is poly(4-vinylpyridine) and the B block is poly(styrene). In at least one embodiment, at least one copolymer comprises an A block and a B block, wherein the A block is hydrophilic and/or hydrogen bonding and the B block is hydrophobic and the A block is poly(2-vinylpyridine) and the B block is poly(styrene). In at least one embodiment, at least one copolymer comprises an A block and a B block, wherein the A block is hydrophilic and/or hydrogen bonding and the B block is and the B block is a modified/or substituted poly(styrene), such as poly(hydroxystyrene) or poly(tert-butylstyrene). In at least one embodiment, at least one copolymer comprises an A block and a B block, wherein the A block is hydrophilic and/or hydrogen bonding and the B block is hydrophobic and the A block is poly(ethylene oxide). Further embodiments are conceivable from suitable blocks listed throughout this disclosure.
If the materials are to be used in biological-related applications, it is desirable to have low protein fouling properties. A typical method to measure the protein adsorption of a membrane material is by exposing the membrane to a protein solution with the pH near the protein isoelectric point (IEP). The overall charges of the proteins are neutral at around the IEP, so electrostatic interactions between the protein and membrane can be excluded in the measurement. In the context of the disclosure, “low protein fouling” is defined as adsorbing less than 100 μg/cm2 lysozyme (Lys) and/or less than 375 μg/cm2 immunoglobulin G (IgG), as measured using the procedure below. In some embodiments, the mesoporous isoporous materials are low protein fouling materials. In at least one embodiment, the low protein fouling mesoporous isoporous materials according to the present disclosure have a Lys adsorption of less than about 80 μg/cm2. In at least one embodiment, the low protein fouling mesoporous isoporous materials according to the present disclosure have an IgG adsorption of less than about 300 μg/cm2. In at least one embodiment, the low protein fouling mesoporous isoporous materials according to the present disclosure have a Lys adsorption of less than about 70 μg/cm2. In at least one embodiment, the low protein fouling mesoporous isoporous materials according to the present disclosure have an IgG adsorption of less than about 200 μg/cm2.
A procedure for determining if a material is low protein fouling is as follows: Lys (Lysozyme, IEP around 11.4, Lysozyme from chicken egg white, lyophilized powder, protein ≥90%, ≥40,000 units/mg protein, Sigma-Aldrich) and IgG (Immunoglobulin G, IEP around 7.4 γ-Globulins from bovine blood, ≥99% (agarose gel electrophoresis), Sigma-Aldrich) are prepared at 1.0 mg/mL concentration in phosphate-buffered saline (Phosphate Buffered Saline (PBS), 1×, PH=7.4, Quality Biological, VWR) at room temperature with pH around the IEP of the proteins (pH was adjusted by slowly adding sodium hydroxide for Lys). 4 mL of a given protein solution is placed on each material with 4.9 cm2 area in a small closed dish. A separate 4 mL of a given protein solution is placed in a small closed dish without material (“control”). The dishes are shaken at 80 rpm for 16 hours at 23° C. The materials are soaked with 4 mL of the aforementioned PBS buffer solution for 20 min. The dish contains the original protein solution is marked “Ads”, and the rinsed solution is marked “Wash”. The protein concentration is measured by UV-Vis at 280 nm and a standard curve for each protein solution is used to correlate the UV-Vis adsorption and the protein concentration. The protein adsorption on the materials can be calculated as follows: Protein adsorption=m(ads,protein)/material area=([“Control” concentration g/mL]−[“Ads” concentration g/mL]−[“Wash” Concentration g/mL])*(4.0 mL)/4.9 cm2.
The testing procedure may be scaled according to material area if the aforementioned dimension is not appropriate (e.g. not enough area is available to use 4.9 cm2). The adsorption test is performed on different swatches of material, one for each protein measured.
The material may be used as separation media, wherein a solute is separated from a liquid. For example, the material may be used as a membrane for separating solutes by a filtration mechanism.
The block copolymers poly(styrene-block-4-vinylpyridine) (SV), are synthesized by anionic polymerization with the polymer characteristics in Table 1 below:
Example of the Disclosure. The polymer SV168 is dissolved at 10 wt % polymer concentration in 1,4-dioxane (DOX)/acetone (ACE) (80 wt %/20 wt % solution composition) and DOX/ACE (60 wt %/40 wt % solution composition) to provide a polymer solution. The polymer solutions are spread on a porous PET woven support with thickness about 60 μm, on top of a glass slide. The films are evaporated for 45 seconds at room temperature and the films are immersed in a water bath. The membrane precipitates in water. The membrane's isoporous mesoporous structures (
SV168 is dissolved at 10 wt % polymer concentration in DOX/ACE (70 wt %/30 wt % solution composition), SV221 is dissolved at 10 wt % polymer concentration in DOX/ACE (60 wt %/40 wt % solution composition), SV273 is dissolved at 10 wt % polymer concentration in DOX/ACE (60 wt %/40 wt % solution composition). The polymer solutions are spread on a glass plate with gate height about 260 μm, on top of the glass slide, there is a PET woven support with thickness of about 60 μm. The films are evaporated for 60, 45 and 45 seconds, respectively at room temperature and the films are immersed in a water bath. The membranes precipitate in water. The isoporous mesoporous structures (
Comparative Example. The polymer SV168 is dissolved at 17 wt % polymer concentration in dimethylformamide (DMF)/tetrahydrofuran (THF)/1,4-dioxane (DOX) (33.3 wt %/33.3 wt %/33.3 wt % solution composition), and 20 wt % polymer concentration in DMF/THF (40 wt %/60 wt % solution composition) to provide polymer solutions. These conditions are in line with typically reported casting conditions. The polymer solution is spread on a glass plate with gate height about 260 μm, on top of the glass slide, there is an PET woven support with thickness about 60 μm. The films are evaporated for 40 and 30 seconds, respectively at room temperature and the films are immersed in a water bath. Some of the surface structures are not isoporous for the materials, and both lack both macrovoids and a transition layer, as shown in
Example the Disclosure. The SV168 is dissolved at 10 wt % polymer concentration in 1,4-dioxane (DOX)/acetone (ACE) (70 wt %/30 wt % solution composition), and at 17 wt % polymer concentration in dimethylformamide (DMF)/tetrahydrofuran (THF)/1,4-dioxane (DOX) (33.3 wt/33.3 wt %/33.3 wt % solution composition) to provide polymer solutions. The polymer solutions are spread on a glass plate with gate height about 210 μm. There is no porous support material on the glass plate. The films are evaporated for 20 and 40 seconds at room temperature and the films are immersed in a water bath. Upon immersion, the films peel off the glass slide and form freestanding polymer films. The films in Example 3 are cast under the same conditions.
The thickness of the films are measured and recorded. The films are punched into circles with area of 4.9 cm2, and dried in oven of 60° C. for more than 24 hours. The dried film masses are recorded and the density is calculated (density=mass/volume). Three identical film sets are cast and the averages and standard deviations are reported.
Example of the Disclosure. The same set of materials as Example 2 are used in the protein adsorption experiment. The protein adsorption experiment is a modified known procedure (Abetz 2014b) with two different proteins. The protein adsorption test is described in detail above.
The results are summarized in
Example of the Disclosure. A mixture of SV block copolymers is also used for making the disclosed films. SV142 and SV221 are dissolved at total 10 wt % polymer concentration in 1,4-dioxane (DOX)/acetone (ACE) (70 wt % I/30 wt % solution composition), at various SV ratios. The polymer solutions are spread on a glass plate with gate height about 210 μm. There is no porous support material on the glass plate. The films were evaporated for 40 seconds at room temperature and the films are immersed in a water bath. The IgG adsorption test and density measurements are conducted similarly to Examples above. The results are summarized in Table 3.
This application claims the benefit of U.S. Provisional Application No. 62/641,637 filed Mar. 12, 2018, the entire contents of which are incorporated by reference herein.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2019/021780 | 3/12/2019 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62641637 | Mar 2018 | US |