Patent Application
20220410445
For many years the consolidation of thermoplastic and thermosetting materials to form composite laminates has been accomplished through the simultaneous application of elevated pressure and temperature. This consolidation process is usually applied in a hydraulic press with thermally regulated platens, or, in an autoclave with a pressurised and thermally regulated gas.
Consolidation of laminates within a hydraulic press fitted with thermally regulated platens, commonly referred to as ‘hydraulic axial pressing’, usually allows the application of a high-magnitude of consolidation pressure directed through opposing rigid surfaces. This high-magnitude of consolidation pressure is commonly associated with the production of high-performance composite laminates. In some fields, such as the production of ballistic protection laminates, hydraulic axial pressing can fabricate composite articles with a relatively high resistance to penetration. However, hydraulic axial pressing also has limitations, such as a low-rate of production, costly tooling and a relatively high standard deviation (SD) associated with ballistic testing results.
Consolidation of laminates within an autoclave containing a pressurised and thermally regulated gas, commonly referred to as ‘autoclaving’, usually allows the application of a low-magnitude of isostatic consolidation pressure. This autoclaving process is widely employed within industry and is associated with the production of both large parts and in batches of significant part quantities. In some fields, such as the production of ballistic protection laminates, autoclaving can have limitations, such as the need for a relatively high proportion of matrix (resin) to achieve adequate laminate consolidation. Most significantly, autoclaving is associated with the production of composite articles offering relatively low resistance to penetration.
An adaption of the autoclaving process is to substitute the gaseous fluid for a liquidous fluid and subsequently the pneumatic application of consolidation pressure with the hydraulic application of consolidation pressure. In such an application, the processing volume that contains the pressurised liquidous fluid is referred to as a hydroclave, and the process referred to as ‘hydroclaving’. A form of hydroclaving is employed within a known composite consolidation process, as disclosed within U.S. Pat. No. 8,979,523 B2. This process combines the production efficiencies of autoclaving with the high-magnitude of consolidation pressure of hydraulic axial pressing.
WO2008/098771 describes a process for manufacturing a molded article that uses known isostatic pressurizing processes to consolidate a stack of laminate material under very specific conditions, comprising placing the stack of specific laminate materials and binders in an isostatic pressurizing means and consolidating under specific pressures and elevated temperatures.
It has been found that for a ballistic protection laminate, application of a high-magnitude of isostatic consolidation pressure acting on a composite laminate can have a detrimental effect on the resultant laminate's resistance to penetration.
Terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. For example, as used herein, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, steps, operations, elements, components, and/or groups thereof. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items and may be abbreviated as “/”.
Spatially relative terms, such as “under”, “below”, “lower”, “over”, “upper” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. It will be understood that the spatially relative terms are intended to encompass different orientations of the device in use or operation in addition to the orientation depicted in the figures.
The present invention has been specifically devised to provide a shielding of consolidation pressure to the sidewalls of a composite laminate of stacked material, which may or may not be pre-preg material, being synthetic fibres, such as, but not limited to, aramid material such as Kevlar®, high modulus polyethylene (HMPE) material such as Ineggra®, high modulus polypropylene (HMPP), ultra-high molecular weight polyethylene (UHMWPE) such as Dyneema® or other suitable ballistic laminate material under consolidation by isostatic pressure. Layers of resin compound may be layers in the stack if required. When the sidewalls are shielded, the pressure acting on the remaining faces of the laminate provide a compression that acts to extrude the laminate at its sidewalls in an action that subsequently tensions the reinforcing fibres. The resulting laminate, whilst maintaining the same volume, is thinner and slightly elongated in its major dimensions. This tensioning of reinforcing fibres has a beneficial effect on the resultant laminate's resistance to penetration, which, when coupled with the relatively low standard deviation (SD) associated with ballistic testing results for isostatically consolidated laminates, yields outstanding performance.
An isostatic side-pressure shielding (ISPS) composite consolidation, in accordance with an embodiment of the invention, comprises a fixture that shields the sidewalls of a laminate from pressure whilst the laminate and fixture are together exposed to isostatic pressure.
In preference, the said fixture comprises a circumferential sidewall section and that provides pressure shielding of the laminate sidewall, an enclosing profiled section that governs the curvature of the laminate and a sealing section. The circumferential sidewall section may take any such shape as required
In preference, the said sealing section contains an opening that allows direct application of isostatic pressure to all but the perimeter of the laminate surface it contacts.
In preference, the said enclosing profile section and the said sealing section both contact the said circumferential section and the non-sidewall laminate faces and form a sealed void between the said circumferential section and the sidewalls of the laminate. The said sealing section and the said enclosing profiled section are able to move towards each other under pressure and, in preference, their opposing faces are an offset of the same profile, dictated by the laminate thickness.
In various embodiments of the invention, the said circumferential section and the said enclosing profile section may be combined, or, the said circumferential section and the said sealing section may be combined.
In operation, the laminate and said fixture are typically enclosed in a reusable silicone membrane and heat-sealed in a disposable plastic bag, fused with the contents and surrounds under vacuum. The said silicone membrane can be comprised of multiple separate sections and is ideally preformed to fit the laminate and said fixture accurately. The said silicone membrane is adequately soft as to transfer the applied pressure to the exposed laminate and said fixture surfaces without significant loss of isostatic nature. The said heat-sealed disposable plastic bag containing the said silicone membrane, said fixture and laminate are cycled through the simultaneous and controlled application of elevated isostatic pressure and temperature to ISPS consolidate the laminate, ideally within XTEK Limited's XTclave™ composite consolidation process. The laminate is subsequently extracted from the said heat-sealed disposable plastic bag, said silicone membrane and said fixture and typically subjected to finishing processes.
In preference, the said circumferential section, said enclosing profiled section and said sealing section are constructed from rigid and strong materials, such as metals, metal alloys or composites. In further preference, these materials should have favourable thermal conductivity. Various successful embodiments of the invention have used steel alloy (AS 1444-1996-4140), aluminium alloy (ASTM B 209 6061-T6) and carbon fibre reinforced epoxy resin matrix (GMS Composites EP-250) designed for high temperature resistant composite tooling applications. It has been found advantageous to employ a lubricant, such as lithium grease containing molybdenum disulphide, to assist motion between the said sealing section and the said circumferential section.
In preference, the circumferential sidewall section is non-circular.
In preference, the application of pressure to the fixture acts to close the interfaces between the said circumferential section and the said sealing section and enclosing profiled section. In further preference, the said sealing section is engineered to elastically deform under pressure to maintain contact with the said circumferential section. Harnessing applied pressure to energise the sealing actions improves function and reliability.
Subject to the fluidity of the laminate undergoing ISPS composite consolidation, it may be advantageous to position a membrane between the said sealing section and the laminate. In preference, this said membrane extends over the entire surface of the laminate. This said membrane functions to minimise marking of the laminate at the perimeter of its interface with the said sealing section. Various successful embodiments of the invention have used thin (0.2 mm) brass (Alloy C26000,) and polycarbonate (0.5 mm) materials for this said membrane. Most importantly, this membrane must be adequately soft as to transfer the applied pressure to the exposed laminate and without significant loss of isostatic nature.
In a further form of the invention, there is a mold for a ballistic article by consolidating a laminate stack, the mold including;
In preference, the sealing section shields the lateral sides of the laminate stack from external pressure.
In preference, the internal dimension of the circumferential upwardly extending sidewall of the base profile section is between 0.001 mm to 25 mm greater than the outer dimension of the laminate stack to be consolidated.
In preference, the sealing section is a ring or band.
In preference, the sliding sealing section is a ring or a band having an angled profile.
In preference, the sliding sealing section is a ring or a band having a bevelled profile.
In preference, the sliding sealing section is a ring or a band having an “L”-shaped profile.
In preference, the sealing section is a hoop or band having a substantially constant profile.
In preference, the sealing section is deformable.
In preference, the base profile section is two piece.
In preference, the base profile section is two piece, including a base profile section and a circumferential sidewall section.
In preference, the mold is a molding tool.
In a further form of the invention there is provided a process for the preparation of a molded article including the steps of:
In preference, the molded article is a ballistic article.
In preference, the sealing section is deformable.
In preference, the stack of laminate material has a top surface, bottom surface and a side surface.
In preference the isostatic pressure is prevented from being applied the side surface of the laminate material.
By way of example/illustration only, an embodiment of the invention is described with reference to the accompanying figures, in which:
The term “laminate stack” as used herein refers to a stack of material, such as ballistic material or ballistic laminate sheets layered on top of each other so as to form a pile or stack.
The term “prepreg” as used herein refers to fabric material, such as ballistic material of ballistic laminate sheets, that have been pre-impregnated with a resin system or matrix.
With reference to
The sealing section (3) then fits snugly into the opening (37) of the circumferential section (1), with a sliding fit between the outer face (28) of the sealing section (3) and the inner face (36) of the circumferential section (1). This close fitting between the sealing section (3) and the circumferential section (1) can be seen in
Referring to
The sealing section (3) has an outer surface (28), an inner surface (31), a top edge (29), a bottom edge (30) and an opening (34). The inner surface (31) has bevelled sloping faces (32) and (33), to provide a substantially constant profile about the hoop or band, which in this embodiment is a bevelled or angled profile but may also be an “L”-shaped profile as shown in
The circumferential section (1) includes an outer surface (35) and an inner surface (36), both being parallel to one another. The opening (37) is of a matching shape to the outer surface (28) of the sealing section (3) so as to allow the sealing section (3) to be inserted therein.
The profile section (base section) (2) has a flange section (38) about its periphery so that the circumferential section (1) can be placed directly on the flange surface (38) so that a portion of the inner face (36) abuts, or is contiguous with, the face (40) of the profile section (2) with a tight fit. The surface (39) of the profile section (base section) (2) carries the shape of a face of the ballistic article that is to be produced. The surface (39) may be smooth or patterned as required. As shown in
A cross section of the composite consolidation apparatus or mold (100) is shown in
The sealing section (3) is then inserted into the opening (37) of the circumferential section (1) and a portion of the upper surface (54) of the laminate stack (4) is left exposed. The inner diameter of the opening (37) of the circumferential section (1) is equal to or greater than an outer diameter of the laminate stack (4). When the outer diameter of the laminate stack (4) is less than the inner diameter of the opening (37) of the circumferential section (1) a sealed void (5) is formed.
The assembled composite consolidation apparatus or mold (100) with laminate stack (4) in place is then inserted into a flexible silicone membrane (6), sealed under vacuum and into a protective plastic bag (7) and then placed into a suitable consolidation apparatus such as a high pressure autoclave, the resulting pressure applied can then exert isostatic pressure to the top surface (54) of the laminate stack (4) as well as against the bevelled sloping surface (31) of the sealing section (3) thus providing isostatic side-pressure shielding to the sides (41) of the laminate stack (4). As such, under consolidation conditions (pressure and heat) excess matrix (resin) material is forced to the sides (41) of the laminate stack (4) and into the sealed void (5), isostatic pressure thus prevented from being applied by the consolidation conditions to the sides (41) of the laminate stack (4).
Referring to
The ballistic articles formed by the present invention have been shown to have significantly improved ballistic resistance compared to similar ballistic articles produced by known isostatic pressure processes and equipment by allowing excess prepreg matrix material to be forced out of the main body of the laminate stack. In addition, the ballistic articles formed by the present invention are also thinner and lighter than those produced by other isostatic processes, thus providing a significant improvement over that which is already known.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017905053 | Dec 2017 | AU | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/AU2018/051350 | 12/18/2018 | WO |