Patent Application
20210121674
The present invention relates to a Japanese encephalitis vaccine-containing microneedle array and, in particular, to an autolytic microneedle array containing a Japanese encephalitis vaccine.
As a drug administration method of administering an appropriate amount of drug and achieving sufficient medicinal effects, a method of using a microneedle array comprising drug-containing microneedles (a needle portion) with a high aspect ratio, by which the microneedles penetrate into a stratum corneum barrier layer to inject the drug into the skin without pain, has attracted attention. For example, an autolytic microneedle array comprising a biosoluble substance as a base material has been reported. In such an autolytic microneedle array, a drug is retained in the base material, and the base material is autolyzed when the microneedles are inserted into the skin, so that the drug can be intracutaneously administered.
Patent Document 1 discloses a method for producing an array as a microstructure, comprising (a) a step of dissolving or suspending at least one therapeutic agent in a solvent to form a therapeutic agent solution or suspension, (b) a step of dissolving at least one polymer in a solvent to form a polymer solution, (c) a step of mixing the therapeutic agent solution or suspension and the polymer solution or suspension to form a polymer matrix solution or suspension, (d) a step of dispensing the polymer matrix solution or suspension into a forming die having a microstructure cavity array, (e) a step of filling the microstructure cavities in the forming die with the solution or suspension, (f) a step of removing an excessive amount of polymer matrix solution or suspension on the surface of the forming die, (g) a step of drying the solution or suspension from the below of the forming die at a temperature of approximately 5° C. to 50° C., and (h) a step of drying the microstructure under vacuum at a temperature of approximately 5° C. to 50° C.
Patent Document 2 discloses a delivery system for the transcutaneous delivery of an epoetin-based agent to a patient, wherein the delivery system comprises: a microspike member having a plurality of microspikes adapted to penetrate into the stratum corneum of the patient; and a biocompatible coating disposed on the microspike member, wherein the coating is formed from a coating preparation comprising at least one type of epoetin-based agent.
Patent Document 3 discloses a needle-shaped body surface applicable preparation having a base agent consisting of a biosoluble substance and a substance of interest retained on the base agent, wherein the preparation is used by being inserted into the body surface, and the substance of interest is absorbed into the body by dissolution of the base agent. The needle-shaped body surface applicable preparation consists of two or more divisions divided by the interfaces in the insertion direction, and the substance of interest is retained in at least one division other than the endmost division. The division retaining the substance of interest is obtained by dissolving the substance constituting the base agent in a solvent, further dissolving or dispersing the substance of interest in the solvent, and then drying and solidifying the liquid-state base agent containing the substance of interest. The division retaining the substance of interest and the division not retaining the substance of interest each consist of a different composition that has been prepared, separately.
As a result of the studies conducted by the present inventors, it has been found that, among various vaccines, in particular, a Japanese encephalitis vaccine easily loses its activity in a drying step during the production of a microneedle array. In the above-described Patent Documents 1 to 3, studies regarding suppression of a reduction in such activity have not been conducted.
It is an object of the present invention to provide a Japanese encephalitis vaccine-containing microneedle array capable of suppressing a reduction in the activity of a Japanese encephalitis vaccine.
The present inventors have conducted intensive studies directed toward achieving the aforementioned object. As a result, the present inventors have found that a reduction in the activity of a Japanese encephalitis vaccine can be suppressed by using a microneedle array having a sheet portion and a plurality of needle portions present on the upper surface of the sheet portion, wherein the needle portion comprises at least one of an electrically neutral water-soluble polymer and a disaccharide, a Japanese encephalitis vaccine, and an electrically neutral surfactant, and the sheet portion comprises at least one of an electrically neutral water-soluble polymer and a disaccharide.
Specifically, the present invention provides the following inventions.
(1) A microneedle array having a sheet portion and a plurality of needle portions present on the upper surface of the sheet portion, wherein
the needle portion comprises at least one of an electrically neutral water-soluble polymer and a disaccharide, a Japanese encephalitis vaccine, and an electrically neutral surfactant, and
the sheet portion comprises at least one of an electrically neutral water-soluble polymer and a disaccharide.
(2) The microneedle array according to (1), wherein the electrically neutral surfactant is sorbitan fatty acid ester, a polyoxyethylene/polyoxypropylene copolymer, polyoxyethylene hydrogenated castor oil, or octylphenol ethoxylate.
(3) The microneedle array according to (1) or (2), wherein the weight average molecular weight of the electrically neutral water-soluble polymer comprised in the needle portion is 5,000 or more and 100,000 or less.
(4) The microneedle array according to any one of (1) to (3), wherein the water-soluble polymer comprised in the needle portion is a polysaccharide.
(5) The microneedle array according to any one of (1) to (4), wherein the water-soluble polymer comprised in the needle portion is hydroxyethyl starch.
(6) The microneedle array according to any one of (1) to (5), wherein the weight average molecular weight of the electrically neutral water-soluble polymer comprised in the sheet portion is 5,000 or more and 100,000 or less.
(7) The microneedle array according to any one of (1) to (6), wherein the water-soluble polymer comprised in the sheet portion is a polysaccharide.
(8) The microneedle array according to any one of (1) to (7), wherein the water-soluble polymer comprised in the sheet portion is hydroxyethyl starch.
(9) The microneedle array according to any one of (1) to (8), wherein the disaccharide comprised in the needle portion is sucrose.
According to the present invention, a reduction in the activity of a Japanese encephalitis vaccine can be suppressed upon the production of a microneedle array.
Hereinafter, the embodiments of the present invention will be described in detail. In the present description, the phrase “comprise a Japanese encephalitis vaccine” means that a needle comprises a Japanese encephalitis vaccine in an amount sufficient for exhibiting the effects of the Japanese encephalitis vaccine, when the needle is punctured into the body surface. On the other hand, the phrase “not to comprise a Japanese encephalitis vaccine” means that a needle does not comprise a Japanese encephalitis vaccine in an amount sufficient for exhibiting the effects of the Japanese encephalitis vaccine, and in this case, the amount of the Japanese encephalitis vaccine ranges from a case where no Japanese encephalitis vaccine is contained, to a case where the Japanese encephalitis vaccine is contained in an amount in which the effects of the vaccine are not exhibited.
The microneedle array of the present invention is a microneedle array having a sheet portion and a plurality of needle portions present on the upper surface of the sheet portion, wherein the needle portion comprises at least one of an electrically neutral water-soluble polymer and a disaccharide, a Japanese encephalitis vaccine, and an electrically neutral surfactant, and the sheet portion comprises at least one of an electrically neutral water-soluble polymer and a disaccharide.
In the present invention, the term “a plurality of” means one or more.
In order to efficiently administer a Japanese encephalitis vaccine into the skin, the microneedle array of the present invention comprises, at least, a sheet portion and a needle portion, and the Japanese encephalitis vaccine is deposited on the needle portion.
The microneedle array of the present invention is a device in which a plurality of needle portions are arranged in an array on the upper surface side of a sheet portion. The needle portions are preferably arranged on the upper surface side of the sheet portion. The needle portions may be directly arranged on the upper surface of the sheet portion, or the needle portions may also be arranged on the upper surface of a frustum portion disposed on the upper surface of the sheet portion.
Preferably, the needle portions are arranged on the upper surface of the frustum portion disposed on the upper surface of the sheet portion. In this case, the microneedle array of the present invention has a plurality of frustum portions between a sheet portion and a plurality of needle portions. In this aspect, it is preferable that the tip region of each needle portion comprises at least one of an electrically neutral water-soluble polymer and a disaccharide, Japanese encephalitis vaccine, and an electrically neutral surfactant, and that the root region of the needle portion other than the tip region, the frustum portion, and the sheet portion comprise at least one of an electrically neutral water-soluble polymer and a disaccharide. The water-soluble polymers comprised in the needle portion and the sheet portion may be identical to or different from each other. The water-soluble polymer will be described later.
The sheet portion is a base for supporting the needle portions, and has a plane shape like a sheet portion 116 as shown in
The area of the sheet portion is not particularly limited, and it is preferably 0.005 to 1000 mm2, more preferably 0.05 to 500 mm2, and further preferably 0.1 to 400 mm2.
The thickness of the sheet portion is indicated as a distance between the surface contacted with the frustum portion or the needle portion and the surface of the opposite side. The thickness of the sheet portion is preferably 1 μm or more and 2000 μm or less, more preferably 3 μm or more and 1500 μm or less, and further preferably 5 μm or more and 1000 μm or less.
The sheet portion comprises at least one of an electrically neutral water-soluble polymer and a disaccharide. The sheet portion may also comprise additives other than the aforementioned components (for example, a water-soluble polymer having an electric charge, etc.). It is to be noted that the sheet portion preferably does not comprise a Japanese encephalitis vaccine.
The electrically neutral water-soluble polymer comprised in the sheet portion is not particularly limited. Examples of the electrically neutral water-soluble polymer may include polysaccharide, polyvinylpyrrolidone, polyoxyethylene polyoxypropylene glycol, polyethylene glycol, and polyvinyl alcohol. Examples of the above-described polysaccharide may include Pullulan, dextran, dextrin, cellulose derivatives (e.g., water-soluble cellulose derivatives in which cellulose is partially modified, such as hydroxypropyl cellulose or hydroxypropylmethyl cellulose), hydroxyethyl starch, and gum Arabic. The above-described components may be used alone as a single type, or may also be used as a mixture of two or more types.
Among the above-described components, the electrically neutral water-soluble polymer comprised in the sheet portion is preferably at least one selected from the group consisting of hydroxyethyl starch, dextran, polyvinylpyrrolidone, polyoxyethylene polyoxypropylene glycol, polyethylene glycol and polyvinyl alcohol, and the electrically neutral water-soluble polymer is particularly preferably hydroxyethyl starch.
In the present invention, the sheet portion may also comprise a non-electrically neutral water-soluble polymer, or sugars other than disaccharides. Examples of the non-electrically neutral water-soluble polymer or the sugars other than disaccharides comprised in the sheet portion may include hyaluronic acid, sodium hyaluronate, chondroitin sulfate, sodium chondroitin sulfate, and carboxymethyl cellulose.
The content percentage of the non-electrically neutral water-soluble polymer or the sugars other than disaccharides in the sheet portion is preferably 0% by mass or more and less than 50% by mass, more preferably 0% by mass or more and less than 40% by mass, further preferably 0% by mass or more and 30% by mass or less, and most preferably 0% by mass or more and 20% by mass or less, based on the total solid content of the sheet portion.
The weight average molecular weight of the electrically neutral water-soluble polymer comprised in the sheet portion is preferably 5,000 or more and 100,000 or less, more preferably 10,000 or more and 100,000 or less, and further preferably 30,000 or more and 90,000 or less.
The sheet portion may comprise a disaccharide. Examples of the disaccharide may include sucrose, lactulose, lactose, maltose, trehalose, and cellobiose. Among these, sucrose is particularly preferable.
The microneedle array is constituted with a plurality of needle portions arranged in an array on the upper surface side of the sheet portion. The needle portion is a convex structure having a tip. The needle is not limited to a needle having a sharp tip, but it may also be a needle having a blunt tip.
Examples of the shape of the needle portion may include a cone, a pyramid (a square pyramid, etc.), and a spindle. The needle portion may have, for example, a shape such as a needle portion 112 shown in
When the microneedle array of the present invention is applied to the skin, it is preferable that the needle portion is inserted into the skin, so that the upper surface of the sheet portion or a part thereof is allowed to come into contact with the skin.
The height (length) of the needle portion indicates the length of a perpendicular line dropped from the tip of the needle portion to the frustum portion or the sheet portion (in a case where such a frustum portion is absent). The height (length) of the needle portion is not particularly limited, and it is preferably 50 μm or more and 3000 μm or less, more preferably 100 μm or more and 1500 μm or less, and further preferably 100 μm or more and 1000 μm or less. When the length of the needle portion is 50 μm or more, transdermal administration of a Japanese encephalitis vaccine can be carried out. On the other hand, when the length of the needle portion is 3000 μm or less, the development of pain caused by the contact of the needle portion with a nerve can be prevented, and bleeding can be avoided. Thus, the length of the needle portion is preferably within the aforementioned range.
The interface between the frustum portion (if the frustum portion is absent, it is the needle portion,) and the sheet portion is referred to as a “base portion.” The distance between the farthest points in the base of a single needle portion is preferably 50 μm or more and 2000 μm or less, more preferably 100 μm or more and 1500 μm or less, and further preferably 200 μm or more and 1000 μm or less.
The number of the needle portions arranged on a single microneedle array is preferably 1 to 2000, more preferably 3 to 1000, and further preferably 5 to 500. When two needle portions are comprised in a single microneedle array, the interval between the two needle portions is indicated by the distance between the legs of perpendicular lines dropped from the tips of the needle portions to the frustum portion or the sheet portion (in a case where such a frustum portion is absent). When three or more needle portions are comprised in a single microneedle array, with regard to the intervals between the arranged needle portions, the distance between the legs of perpendicular lines that are dropped from the tips of the two closest needle portions out of all of the needle portions to the frustum portion or the sheet portion (in a case where such a frustum portion is absent) is obtained, and a mean value of the obtained distances is then obtained. The interval between the needle portions is preferably 0.1 mm or more and 10 mm or less, more preferably 0.2 mm or more and 5 mm or less, and further preferably 0.3 mm or more and 3 mm or less.
The needle portion contains at least one of an electrically neutral water-soluble polymer and a disaccharide, a Japanese encephalitis vaccine, and an electrically neutral surfactant.
In order for the needle portion not to affect a human body even if it remains in the skin, the electrically neutral water-soluble polymer is preferably a biosoluble substance.
The electrically neutral water-soluble polymer comprised in the needle portion is not particularly limited. Examples of the electrically neutral water-soluble polymer may include polysaccharide, polyvinylpyrrolidone, polyoxyethylene polyoxypropylene glycol, polyethylene glycol, and polyvinyl alcohol. Examples of the above-described polysaccharide may include Pullulan, dextran, dextrin, cellulose derivatives (e.g., water-soluble cellulose derivatives in which cellulose is partially modified, such as hydroxypropyl cellulose or hydroxypropylmethyl cellulose), hydroxyethyl starch, and gum Arabic. The above-described components may be used alone as a single type, or may also be used as a mixture of two or more types.
Among the above-described components, the water-soluble polymer comprised in the needle portion is preferably at least one selected from the group consisting of hydroxyethyl starch, dextran, polyvinylpyrrolidone, polyoxyethylene polyoxypropylene glycol, polyethylene glycol, and polyvinyl alcohol, and the water-soluble polymer is particularly preferably hydroxyethyl starch. Furthermore, in order to hinder agglutination of the water-soluble polymer upon the mixing with a Japanese encephalitis vaccine, in general, a polysaccharide having no electric charge is more preferable. The electrically neutral water-soluble polymer comprised in the needle portion may be identical to or different from the electrically neutral water-soluble polymer comprised in the sheet portion.
The weight average molecular weight of the electrically neutral water-soluble polymer comprised in the needle portion is preferably 5,000 or more and 100,000 or less, more preferably 10,000 or more and 100,000 or less, and further preferably 30,000 or more and 90,000 or less.
The needle portion (in particular, the tip region of the needle portion) may comprise a disaccharide. Examples of the disaccharide may include sucrose, lactulose, lactose, maltose, trehalose, and cellobiose. Among these, sucrose is particularly preferable.
In the present invention, the content percentage of the electrically neutral water-soluble polymer or the disaccharide is 50% by mass or more of the total solid content of the needle portion. The content percentage of the electrically neutral water-soluble polymer or the disaccharide is preferably 55% by mass or more, more preferably 60% by mass or more, and further preferably 65% by mass or more, based on the total solid content of the needle portion.
The upper limit of the content percentage of the electrically neutral water-soluble polymer or the disaccharide is not particularly limited. The upper limit of the content percentage of the electrically neutral water-soluble polymer or the disaccharide is preferably 99% by mass or less, more preferably 95% by mass or less, and further preferably 90% by mass or less, based on the total solid content of the needle portion.
By setting the content percentage of the electrically neutral water-soluble polymer or the disaccharide to be 50% by mass or more based on the total solid content of the needle portion, favorable puncture ability and favorable effects can be obtained.
The content percentage of the electrically neutral water-soluble polymer or the disaccharide in the total solid content of the needle portion can be measured by the following method, but the measurement method is not particularly limited thereto. As a measurement method, for example, the needle portion is cut from the produced microneedle array, the needle portion is then dissolved in a buffer solution (a buffer solution suitable for dissolving the water-soluble polymer constituting the needle portion, such as a phosphate buffered saline (PBS)), and the amount of the electrically neutral water-soluble polymer or the disaccharide in the solution can be measured according to a high performance liquid chromatographic method.
The needle portion contains a Japanese encephalitis vaccine.
As such a Japanese encephalitis vaccine, a vaccine comprising, as an active ingredient, an inactivated Japanese encephalitis virus can be used. For example, a formalin inactivated virus preparation prepared from a culture solution of Vero cells (African green monkey kidney-derived cell line) infected with a Japanese encephalitis virus, or a formalin inactivated virus preparation prepared from the mouse brain infected with a Japanese encephalitis virus, or the like can be used.
The content of the Japanese encephalitis vaccine in the needle portion is not particularly limited. It is preferably 0.001% to 10% by mass, more preferably 0.003% to 1% by mass, and particularly preferably 0.005% to 0.5% by mass, with respect to the solid content mass of the needle portion.
The content of the Japanese encephalitis vaccine in a single microneedle array is not particularly limited. It is preferably 0.05 to 5 μg, and more preferably 0.2 to 3 μg, at a protein content.
The needle portion contains an electrically neutral surfactant (nonionic surfactant).
Examples of the electrically neutral surfactant may include sugar alcohol fatty acid esters such as sucrose fatty acid ester, sorbitan fatty acid ester, glycerin fatty acid ester, polyglycerin fatty acid ester, propylene glycol fatty acid ester, polyoxyethylene sorbitan fatty acid ester, polyoxyethylene glycerin fatty acid ester, polyethylene glycol fatty acid ester, a polyoxyethylene/polyoxypropylene copolymer, polyoxyethylene castor oil, polyoxyethylene hydrogenated castor oil, and octylphenol ethoxylate. Among the above-described substances, sorbitan fatty acid ester, a polyoxyethylene/polyoxypropylene copolymer, or polyoxyethylene hydrogenated castor oil are particularly preferable. As such electrically neutral surfactants, commercially available products such as Tween (registered trademark) 80, MONTANOX (registered trademark) 80 API, Pluronic (registered trademark) F-68, NIKKOL (registered trademark) HCO-60, or Triton (registered trademark) X-100 can also be used.
The additive amount of the electrically neutral surfactant is not particularly limited, and it is preferably 0.01 μg or more, and more preferably 0.1 μg or more, for a single microneedle array (area: 1 cm2).
Hereinafter, preferred embodiments of the present invention will be described with reference to the drawings attached herewith. However, the present invention is not limited thereto.
In
The microneedle array of the present invention preferably takes the shape of the microneedle 110 of
A needle portion first layer 112A shown in
In the microneedle array of the present invention, with regard to the lateral line of the needle portion, microneedles are preferably arranged with intervals of approximately 0.1 to 10 needles per mm. The microneedle array more preferably has 1 to 10000 microneedles per cm2. The microneedles can be efficiently punctured into the skin by setting the density of the microneedles at 1 microneedle/cm2 or more. On the other hand, by setting the density of the microneedles to be 10000 microneedles/cm2 or less, it becomes possible for the microneedles to be sufficiently punctured into the skin. The density of the needle portion is preferably 10 to 5000 microneedles/cm2, more preferably 25 to 1000 microneedles/cm2, and particularly preferably 25 to 400 microneedles/cm2.
The microneedle array of the present invention can be supplied in the form in which it is hermetically preserved together with a desiccant. As such desiccants, known desiccants (e.g., silica gel, quicklime, calcium chloride, silica alumina, a sheet-shaped desiccant, etc.) can be used.
The microneedle array of the present invention can be produced by the following method, for example, in accordance with the method described in Japanese Patent Publication (Kokai) No. 2013-153866 A or International Publication No. WO 2014/077242.
According to the first method, photoresist is applied onto a Si substrate, followed by exposure and development. Thereafter, etching is carried out by RIE (reactive ion etching), etc., so that an array of conical shaped portions (protrusions) 12 is produced on the surface of an original form 11. Besides, when etching such as RIE is carried out to form conical shaped portions on the surface of the original form 11, the etching is carried out from an oblique direction, while rotating the Si substrate, so that the conical shape can be formed. The second method is a method of forming an array of shaped portions 12 such as square pyramids on the surface of an original form 11 by processing a metal substrate such as Ni using a cutting tool such as a diamond bit.
Subsequently, a mold is produced. Specifically, as shown in
The first method is a method comprising pouring a silicone resin prepared by adding a hardening agent to PDMS (polydimethylsiloxane; for example, SYLGARD 184 (registered trademark) manufactured by Dow Corning) into the original form 11, then subjecting the original form to a heat treatment at 100° C. to harden it, and then peeling the hardened resin from the original form 11. The second method is a method comprising pouring a UV (ultraviolet) curable resin hardened by ultraviolet irradiation into the original form 11, then applying ultraviolet ray to the original form in a nitrogen atmosphere, and then peeling the resin from the original form 11. The third method is a method comprising pouring a solution prepared by dissolving a plastic resin such as polystyrene or PMMA (polymethyl methacrylate) in an organic solvent into an original form 11 coated with a peeling agent, then drying the original form to volatilize the organic solvent and harden the residue, and then peeling the hardened resin from the original form 11. The fourth method is a method of producing an inverted product by Ni electroforming.
Thereby, produced is a mold 13, in which needle recess portions 15 that are inverted shapes of the conical or pyramidal shapes of the original form 11 are arranged in a two-dimensional array. The thus produced mold 13 is shown in
As shown in
By using such a mold composite 18, a solution filling into the needle recess portion 15 does not permeate, and only the air existing in the needle recess portion 15 can be discharged from the needle recess portion 15. Thereby, the transcription ability of transcribing the shape of the needle recess portion 15 into a polymer can be improved, so that a sharper needle portion can be formed.
The diameter D of the air vent hole 15C is preferably in the range of 1 to 50 μm. When the diameter D of the air vent hole 15C is less than 1 μm, it cannot sufficiently play a role as an air vent hole. On the other hand, when the diameter D of the air vent hole 15C exceeds 50 μm, the sharpness of the tip of the molded microneedle is impaired.
As a gas permeation sheet 19 formed with a material through which gas permeates but liquid does not permeate, for example, a gas permeable film (manufactured by Sumitomo Electric Industries, Ltd., Poreflon (registered trademark), FP-010) can be preferably used.
As a material used for the mold 13, an elastic material or a metallic material can be used, and an elastic material is preferable. A material having high gas permeability is more preferable. Oxygen permeability that is representative gas permeability is preferably 1×10−12 (mL/s·m2·Pa) or more, and is more preferably 1×10−10 (mL/s·m2·Pa) or more. Besides, 1 mL is 10−6 m3. By setting gas permeability within the above-described range, the air existing in the recess portion of the mold 13 can be discharged from the mold side, so that a microneedle array with few defects can be produced. Specific examples of such a material may include materials, such as silicone resins (e.g., SYLGARD 184 (registered trademark) manufactured by Dow Corning, and KE-1310ST (product number) manufactured by Shin-Etsu Chemical Co., Ltd.), UV curable resins, and plastic resins (e.g., polystyrene and PMMA (polymethyl methacrylate)), which are melted or dissolved in a solvent. Among these materials, silicone rubber-based materials are preferable because they have durability to transcription by repeated pressurization, and also have good peelability from the materials. Moreover, examples of the metallic material may include Ni, Cu, Cr, Mo, W, Ir, Tr, Fe, Co, MgO, Ti, Zr, Hf, V, Nb, Ta, α-aluminum oxide, zirconium oxide, stainless steel (e.g., STAVAX (trademark) material manufactured by Bohler-Uddeholm KK), and an alloy thereof. As a material for a frame 14, the same material as that for the mold 13 can be used.
In the present invention, it is preferable to prepare:
(i) a solution comprising at least one of an electrically neutral water-soluble polymer and a disaccharide, a Japanese encephalitis vaccine, and an electrically neutral surfactant, which is for use in forming a needle portion tip region that is a part of a needle portion, and
(ii) a solution comprising at least one of an electrically neutral water-soluble polymer and a disaccharide, which is for use in forming a needle portion root region other than the needle portion tip region in the needle portion, and a sheet portion (or a needle portion root region other than the needle portion tip region in the needle portion, a frustum portion, and a sheet portion).
The types of the electrically neutral water-soluble polymer, the disaccharide, and the electrically neutral surfactant are as described above in the present description.
The concentration of the electrically neutral water-soluble polymer or the disaccharide in the above-described solution is different depending on the types of substances used. In general, it is preferably 1% to 50% by mass. In addition, the solvent used in dissolution may also be a solvent having volatility, even other than water, and methyl ethyl ketone (MEK), alcohol or the like can be used.
As shown in
As a material used for the nozzle 34, an elastic material or a metallic material can be used. Examples of the material may include Teflon (registered trademark), stainless steel (SUS (Steel Use Stainless)), and titanium.
As shown in
When the mold 13 is formed with a material having gas permeability, the solution 22 comprising a Japanese encephalitis vaccine can be suctioned by suctioning from the back surface of the mold 13, so that the filling of the solution 22 comprising a Japanese encephalitis vaccine into the needle recess portions 15 can be promoted.
After the filling step has been carried out with reference to
Since the liquid supplying device is moved while the lip portion 34A of the nozzle 34 is contacted with the surface of the mold 13, the nozzle 34 can scrape the solution 22 comprising a Japanese encephalitis vaccine remaining on the surface of the mold 13 other than the needle recess portions 15. Thus, the solution 22 comprising a Japanese encephalitis vaccine cannot remain on the surface of the mold 13 other than the needle recess portions 15.
In order to reduce damage to the mold 13 and also in order to suppress the deformation of the mold 13 caused by compression as much as possible, the pressure of pressing the nozzle 34 to the mold 13 is preferably as small as possible, upon the moving of the liquid supplying device. In addition, in order to prevent the solution 22 comprising a Japanese encephalitis vaccine from remaining on the mold 13 other than the needle recess portions 15, at least one of the mold 13 or the nozzle 34 is desirably formed with a material that flexibly elastically deforms.
By repeating the filling step shown in
The aforementioned filling step and moving step may have an aspect (1) in which the solution 22 comprising a Japanese encephalitis vaccine is filled into the needle recess portions 15, while moving the nozzle 34, or may also have an aspect (2) in which the nozzle 34 is once allowed to stand still on the needle recess portions 15 during the moving of the nozzle 34, the solution 22 comprising a Japanese encephalitis vaccine is then filled into the needle recess portions 15, and after the filling of the solution, the nozzle is moved again. Between the filling step and the moving step, the lip portion 34A of the nozzle 34 is contacted with the surface of the mold 13.
After the filling of the solution into the 5×5 multiple needle recess portions 15 has been completed, the nozzle 34 is moved to the adjacent 5×5 multiple needle recess portions 15. Regarding solution supply, when the liquid supplying device is moved to the adjacent 5×5 multiple needle recess portions 15, it is preferable to terminate the supply of the solution 22 comprising a Japanese encephalitis vaccine. There is a certain distance from the needle recess portion 15 on the 5th line to the next first needle recess portions 15. When the nozzle 34 is moved between them, if the solution 22 comprising a Japanese encephalitis vaccine is continuously supplied, the liquid pressure in the nozzle 34 becomes excessively high in some cases. As a result, there may be a case where the solution 22 comprising a Japanese encephalitis vaccine is flown out of the nozzle 34 to the portion of the mold 13 other than the needle recess portions 15. In order to suppress this problem, the liquid pressure in the nozzle 34 is detected and if the nozzle is determined to have an excessively high liquid pressure, it is preferable to terminate the supply of the solution 22 comprising a Japanese encephalitis vaccine.
Besides, in the above description, a method of supplying a solution comprising a Japanese encephalitis vaccine by using a dispenser having a nozzle is explained, but bar coating, spin coating, coating using a spray, etc. can also be applied, as well as the coating using a dispenser.
In the present invention, it is preferable to perform a drying treatment, after a solution comprising a Japanese encephalitis vaccine has been supplied to needle recess portions.
Preferably, the microneedle array of the present invention can be produced by: a step of drying a mold for forming needle portions filled with a solution comprising a Japanese encephalitis vaccine to form parts of the needle portions; and a step of filling a solution comprising at least one of an electrically neutral water-soluble polymer and a disaccharide into the upper surfaces of the above-formed parts of the needle portions, followed by drying.
The conditions for drying the mold for forming needle portions filled with a solution comprising a Japanese encephalitis vaccine are preferably conditions in which the water content percentage of the above-described solution reaches 20% or less at 30 minutes to 300 minutes after initiation of the drying.
Particularly preferably, the above-described drying can be regulated, so that the temperature is kept to a temperature at which the activity of the Japanese encephalitis vaccine is not lost, or lower, and the water content percentage of the solution reaches 20% or less at 60 minutes after initiation of the drying.
A method of regulating the speed of the above-described drying may be, for example, any given means capable of delaying the drying, such as temperature, humidity, drying air volume, the use of a container, the volume and/or shape of the container, etc.
The drying can be carried out in a state in which the mold for forming needle portions filled with a solution comprising a Japanese encephalitis vaccine is covered with a container or is stored in a container.
The temperature applied upon the drying is preferably 1° C. to 45° C., and more preferably 1° C. to 40° C.
The relative humidity applied upon the drying is preferably 10% to 95%, more preferably 20% to 95%, and further preferably 30% to 95%.
Regarding a step of forming a sheet portion, several aspects will be described.
Regarding the step of forming a sheet portion, a first aspect is described with reference to
In the first aspect, in order to promote the filling of the solution 22 comprising a Japanese encephalitis vaccine and the solution 24 comprising at least one of an electrically neutral water-soluble polymer and a disaccharide into the needle recess portions 15, it is also preferable to carry out pressurization from the surface of the mold 13 and suction from the back surface of the mold 13 under reduced pressure.
Next, a second aspect is described with reference to
In the second aspect, in order to promote the filling of the solution 24 comprising at least one of an electrically neutral water-soluble polymer and a disaccharide into the needle recess portions 15, it is also preferable to carry out pressurization from the surface of the mold 13 and suction from the back surface of the mold 13 under reduced pressure.
The method of drying the solution 24 comprising at least one of an electrically neutral water-soluble polymer and a disaccharide may be a step of volatizing the solvent in the solution. The drying method is not particularly limited, and for example, methods such as heating, ventilation, or decompression can be used. The drying treatment can be carried out under conditions of 1° C. to 50° C. for 1 to 72 hours. In the case of ventilation, a method of blowing warm air to the solution at 0.1 to 10 m/sec is applied, for example. The drying temperature is preferably a temperature at which the Japanese encephalitis vaccine in the solution 22 comprising the Japanese encephalitis vaccine is not thermally deteriorated.
The method of peeling a microneedle array from a mold 13 is not particularly limited. Upon peeling, needle portions are preferably not bent or broken. Specifically, as shown in
The method for producing the microneedle array of the present invention is not particularly limited. The microneedle array of the present invention is preferably obtained by a production method comprising: (1) a step of producing a mold, (2) a step of preparing a solution comprising at least one of an electrically neutral water-soluble polymer and a disaccharide, a Japanese encephalitis vaccine, and an electrically neutral surfactant, (3) a step of filling the solution obtained in the step (2) into the mold to form needle portion tip regions, (4) a step of filling a solution comprising at least one of an electrically neutral water-soluble polymer and a disaccharide into the mold to form residual portions of the needle portions (frustum portions, as desired) and a sheet portion, and (5) a step of peeling a microneedle array from the mold.
The present invention will be more specifically described in the following examples. In the following examples, the material used, its amount and ratio, the details of the treatment, the treatment process, and the like may be suitably modified unless they overstep the spirit and the scope of the invention. Accordingly, the invention should not be restrictively interpreted by the specific examples mentioned below.
Abbreviations and product names used in the following Examples have the following meanings.
HES: Hydroxyethyl Starch 70000 (Fresenius Kabi) (weight average molecular weight: 70000)
DEX: Dextran70000 (Meito Sangyo Co., Ltd.) (weight average molecular weight: 70000)
CS: Sodium chondroitin sulfate (Maruha Nichiro Corporation) (weight average molecular weight: 90000)
PVP K25: Polyvinylpyrrolidone (FUJIFILM Wako Pure Chemical Corporation) (weight average molecular weight: 24000)
Tw: MONTANOX (registered trademark) 80 API (Seppic)
SDS: Sodium dodecyl sulfate (FUJIFILM Wako Pure Chemical Corporation)
Pluronic (registered trademark) F-68 (NOF CORPORATION)
NIKKOL (registered trademark) HCO-60 (Nikko Chemicals Co., Ltd.)
Triton (registered trademark) X-100 (Alfa Aesar)
100 Needles, each consisting of a shaped portion 12 having a needle structure, in which a cone 52 having a diameter D2 of 300 μm and a height H2 of 500 μm was formed on a truncated cone 50 having a diameter D1 of 500 μm (bottom surface) and a height H1 of 150 μm, as shown in
A stock solution of Japanese encephalitis vaccine (provided from BIKEN Group) was concentrated according to centrifugal ultrafiltration, and was then mixed with a water-soluble polymer, sucrose (FUJIFILM Wako Pure Chemical Corporation), sodium L-glutamate (FUJIFILM Wako Pure Chemical Corporation), and a surfactant. The amounts of individual components used are shown in Table 1.
Hydroxyethyl starch 70000 (HES, Fresenius Kabi) was dissolved in water to prepare an aqueous solution of 56% by mass of HES.
The filling device shown in
A gas permeable film with a side of 15 mm (manufactured by Sumitomo Electric Industries, Ltd., Poreflon (registered trademark), FP-010) was placed on a horizontal vacuum stand, and a mold was placed thereon so that the surface thereof came to the top. From the direction of the back surface of the mold, pressure was reduced at a suction pressure (gauge pressure) of 90 kPa, so that the gas permeable film and the mold were fixed on the vacuum stand.
A nozzle made of SUS (stainless steel) having the shape shown in
The mold filled with the solution comprising a Japanese encephalitis vaccine was stored in a lid (box) in the environment of 23° C. and 45%, and was then dried. At this time, the solution comprising a Japanese encephalitis vaccine was gradually dried, and after 180 minutes or longer had passed, the water content percentage became 20% or less. The drying means are not limited to the lid, but other means such as regulation of the temperature and the humidity or regulation of air volume may also be used.
The support used to form a sheet portion was prepared by subjecting a polyethylene terephthalate (PET) sheet (175 μm) to a hydrophilic plasma treatment using Cloud Remover (Victor jvc) under the following conditions (used gas: O2; gas pressure: 13 Pa; high frequency (RF) electric power: 100 W; irradiation time: 3 minutes; O2 flow rate: SV 250; and desired vacuum degree (CCG): 2.0×10−4 Pa). A solution used to form a sheet portion was applied onto the surface and back surface of the treated PET to result in each film thickness of 75 μm. On the other hand, the mold filled with the solution comprising a Japanese encephalitis vaccine was fixed on the vacuum stand by suction. The surface side of the PET sheet, onto which the solution used to form a sheet portion had been applied, was disposed facing with the surface of the mold, and further, the void between the PET sheet and the mold or the space existing on the side of the PET opposite to the mold was decompressed for 2 minutes. After completion of the decompression, only the space on the side of the PET opposite to the mold was exposed to the atmosphere, so that the PET sheet, onto which the solution used to form a sheet portion had been applied, was adhered to the mold. After the contacted state of the PET and the mold had been maintained for 10 minutes, an integrated body in which the PET adhered to the mold was dried under the environment of 23° C. and 45% (relative humidity).
The dried and solidified microneedle array was carefully peeled from the mold, so that a microneedle array comprising a Japanese encephalitis vaccine therein was formed. The present microneedle was composed of a frustum portion and a needle portion, and it was a truncated cone structure, in which the length L of a needle-shaped protrusion was approximately 800 μm, the width of a base portion was approximately 350 μm, the height of a frustum portion was approximately 190 μm, the diameter of the upper bottom surface was approximately 350 μm, and the diameter of the lower bottom surface was approximately 700 μm. The number of the microneedles was 109, and these microneedles were arranged with intervals of approximately 1 mm.
A microneedle array was produced in the same manner as that of Example 1, with the exception that the composition of an aqueous solution comprising a Japanese encephalitis vaccine and the composition of a solution used to form a sheet portion were changed as shown in Table 1.
The content of the Japanese encephalitis vaccine and the amount of the electrically neutral surfactant shown in Table 1 each indicate the amount thereof for a single microneedle array. The area of a single microneedle array was 1 cm2. Besides, in Example 5, the microneedle array was produced at a ratio (mass ratio) of DEX/CS that was 70/30.
(Evaluation 1: Vaccine Activity after Production of Microneedle Array)
A microneedle array as a whole was dissolved in 1 mL of a dissolving solution (a phosphate buffer supplemented with 0.1% of Tween (registered trademark) 20 and 0.5% of bovine serum albumin), and the vaccine activity was then evaluated according to ELISA (Enzyme-Linked ImmunoSorbent Assay). The expected content was calculated from (the concentration (μg/mL) of the Japanese encephalitis vaccine in the filling solution×the weight (mg) filled into the mold). The results of the above-described evaluation are shown in Table 1. The content of the vaccine detected by ELISA that was 80% or more of the expected content was evaluated as A, whereas the vaccine content that was less than 80% of the expected content was evaluated as B.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2018-098810 | May 2018 | JP | national |
This application is a Continuation of PCT International Application No. PCT/JP2019/020284 filed on May 22, 2019, which claims priority under 35 U.S.C § 119(a) to Japanese Patent Application No. 2018-098810 filed on May 23, 2018. Each of the above application(s) is hereby expressly incorporated by reference, in its entirety, into the present application.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2019/020284 | May 2019 | US |
| Child | 17100495 | US |