In building construction, different types of claddings are used as panels for forming interior and exterior wall and ceiling surfaces. For simplicity, as used herein, it will be understood that the term “wall” also encompasses ceilings. Typically, the claddings are in the form of boards (also referred to as panels) affixed to framing members such as in balloon framing arrangements known in the art. Examples of claddings include gypsum board faced with paper, fibrous mats (e.g., fiberglass), and the like. These and other types of boards are typically cut to appropriate dimensions and then fastened to framing members, e.g., with screws, nails, or the like to form wall sections formed from multiple boards.
Such wall sections are normally finished to provide aesthetically pleasing, uniform, and protected surfaces. For example, two side-by-side boards disposed in the same plane will form a joint seam between them on vertical walls and horizontal ceilings. To finish the seam, joint reinforcement tape is embedded in the seam, along with a layer of joint compound under the tape, and multiple coats of joint compound applied over the tape. Some boards meet at an angle such as when forming a corner. Reinforcement bead can be utilized to hide the corner seam and to protect the corner. Reinforcement bead can be directly attached to the board using fasteners, or a layer of joint compound is applied under the trim to adhere the reinforcement bead to the board. The installed reinforcement is then concealed with multiple layers of joint compound applied over the trim. Fasteners used to affix the board to framing members must also be concealed with multiple layers of joint compound applied over them. After the various joint compound applications are dried, the resulting wall surfaces can be sanded and painted to form the desired uniform and aesthetically pleasing appearance.
The level of finishing as described above can vary. For example, with respect to gypsum wallboard, six (6) levels of gypsum board finish are understood in the art, ranging from zero (no treatment at all) to level five (the highest level of finish), as set forth in Gypsum Association document GA-214 and American Society for Testing and Materials (“ASTM”) C840. The level of finish generally corresponds with the number of applications of joint compound to seams, trims, and fasteners. Levels three, four, and five are typically used for occupied spaces within buildings. For single family homes, level 4 is the most common level that is implemented. Level five is less frequently used and usually requires application of a skim coat of joint compound across the entire wall surface.
Conventional approaches for finishing wall assemblies as described above have not been fully satisfactory. The materials conventionally used to finish wall assemblies create significant inefficiencies in the process and also require an advanced level of skill to use effectively. For example, existing joint compounds require three separate coats to be applied to fasteners as well as multiple coats applied to flat seams between boards in the same plane and to corner seams. Each coat must separately dry which introduces significant downtime in the construction process, particularly since the other construction trades ordinarily cannot work inside the building while the wall finishing occurs. Each layer of joint compound can require about a day to dry, and it typically can take about a week to install the gypsum board and finish the flat joints, fasteners, and corner trims for a typical new construction of a home of 2,400 square feet of living space (corresponding to about 10,000 square feet of board).
In addition, the need for applying multiple coats of joint compound requires that the user manipulate the joint compound significantly above the plane of the board. To allow the board to appear flat to the naked eye (even though it is not), significant skill and workmanship is required to achieve the proper visual appearance when the user is functioning above the plane of the board. The additional layers of joint compound must be feathered out wider and wider from the seam in a graduated manner to make the seam appear aesthetically flat. If the user is not significantly skilled, the visual appearance will not be satisfactory.
It will be appreciated that this background description has been created by the inventors to aid the reader and is neither to be taken as a reference to prior art nor as an indication that any of the indicated problems were themselves appreciated in the art. While the described principles can, in some regards and embodiments, alleviate the problems inherent in other systems, it will be appreciated that the scope of the protected innovation is defined by the attached claims and not by the ability of the claimed invention to solve any specific problem noted herein.
One embodiment provides a kit for assembling a wall, which comprises gypsum boards having at least one tapered edge with a recess depth at the deepest point from about 0.005 inch to about 0.125 inch. The kit also comprises a drying-type joint compound with shrinkage of less than 15% by volume as measured by ASTM C474-05. The drying-type joint compound comprises a plurality of hollow spheres and a binder selected from the group consisting of acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof. The hollow spheres have an average isostatic crush strength of at least about 250 psi as measured according to ASTM D3102-78. The density of the spheres is from about 0.0015 lb/in3 (about 0.04 g/cm3) to about 0.04 lb/in3 (about 1.1 g/cm3).
Further embodiments include kits in which the joint compound exhibits shrinkage of about 2% or less by volume, as measured by ASTM C474-05.
In some embodiments, the joint compound is substantially free of at least one of the following: setting minerals, bulk filler, clays, starch, mica, calcium carbonate, expanded perlite, calcium magnesium carbonate, limestone, calcium sulfate dihydrate, attapulgite clay, kaolin clay, talcs and diatomaceous earth.
At least some kits are formulated with a joint compound in which the binder has a glass transition temperature (Tg) from about 32° F. to about 70° F.
The hollow spheres can be made of various materials, including lime boro-silicate, polystyrene, ceramic, recycled glass, expanded glass, lightweight polyolefin, and any combination thereof. Some joint compounds may further comprise a nonionic surfactant having a hydrophilic-lipophilic balance (HLB) from about 3 to about 20.
Further embodiments include methods for assembling a wall, which utilize a first gypsum board and a second gypsum board, each of the boards having at least one tapered edge with a recess depth at the deepest point from about 0.005 inch to about 0.125 inch, and a drying-type joint compound with shrinkage of less than 15% by volume as measured by ASTM C474-05, the drying-type joint compound comprising a plurality of hollow spheres and a binder selected from the group consisting of acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof; wherein the hollow spheres have an average isostatic crush strength of at least about 250 psi as measured according to ASTM D3102-78; and wherein the density of the spheres is from about 0.0015 lb/in3 (about 0.04 g/cm3) to about 0.04 lb/in3 (about 1.1 g/cm3). In the methods, the two gypsum boards are joined together such that the tapered edges of the two boards create a seam; and the drying-type joint compound is then applied over the seam. Some advantageous methods include those in which the drying-type joint compound is applied in one coat only. In some embodiments, the seam between the first gypsum board and the second gypsum board is further reinforced with a joint tape.
In some embodiments, the first gypsum board and the second gypsum board have a face surface and a back surface. The face surface of the first gypsum board and the face surface of the second gypsum board have at least one tapered edge, while the back surfaces are not tapered. In the methods, the two gypsum boards may be joined at the tapered edges to create a seam such that the two face surfaces stay on the same side and create a combined face surface, and the joint compound is applied over the seam on the combined face surface only.
Embodiments include installation methods performed in less than 72, 48 or 24 hours. Some embodiments contemplate methods by which installation is completed in two days.
The joint compound composition comprises, consists, or consists essentially of binder selected from acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof. The composition also comprises a plurality of hollow spheres. The spheres desirably have an average isostatic crush strength of at least about 100 psi as measured according to ASTM D3102-78.
In another aspect, the invention provides a joint compound composition consisting essentially of (a) latex emulsion binder in an amount from about 3% to about 90% by weight of the wet composition; (b) a plurality of hollow spheres having an average isostatic crush strength of at least about 100 psi as measured according to ASTM D3102-78, wherein the spheres are present in an amount from about 5% to about 25% by weight of the wet composition; (c) nonionic surfactant in an amount from about 0.001% to about 5% by weight of the wet composition; and (d) humectant in an amount from about 0.001% to about 3% by weight of the wet composition; and, optionally, (e) defoamer in an amount from about 0.05% to about 5% by weight of the wet composition; (f) rheological modifier in an amount from about 0.1% to about 5% by weight of the wet composition; (g) biocide, in an amount from about 0.1% to about 1.5% by weight of the wet composition; (h) bulk filler, such as calcium carbonate or limestone in an amount from about 1% to about 40% by weight of the wet composition; and (i) delaminated clay, such as kaolin clay, in an amount from about 0.1% to about 5% by weight of the wet composition.
In another aspect, the invention provides a wall assembly comprising, consisting of, or consisting essentially of two adjacent boards, joined by a seam. Only one-coat of the joint compound is applied over the seam to provide a uniform aesthetic appearance. The joint compound composition comprises binder selected from acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof. The composition also comprises a plurality of hollow spheres. The spheres desirably have an average isostatic crush strength of at least about 100 psi as measured according to ASTM D3102-78. The wall assembly further comprises dimensionally stable, non-swelling flat joint tape embedded in the seam.
In another aspect, the invention provides a method of treating a wallboard assembly of two adjacent boards joined by a seam. The method comprises, consists of, or consists essentially of applying joint tape and one coat of the joint compound composition to the seam. The joint compound composition comprises binder selected from acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof. The composition also comprises a plurality of hollow spheres. The spheres desirably have an average isostatic crush strength of at least about 100 psi as measured according to ASTM D3102-78. The method further comprises drying the composition.
In another aspect, the invention provides a reinforcement trim for protecting a seam of two adjacent boards having opposing face and back surfaces, the faces being disposed with respect to each other at an angle between the board faces. The trim comprises, consists of, or consists essentially of paper face comprising non-swelling synthetic paper facing material and a backing. For example, the facing material can be laminated to a sturdy, rust-resistant material designed to impart superior long term corner angle joint reinforcement that exceeds the minimum performance requirements established in ASTM C1047-10a (Standard Specification for Accessories for Gypsum Wallboard and Gypsum Veneer Base) for crack resistance and chipping, resulting in corner vertex that remains straight during normal building movement and/or displacement and daily wear-and-tear. In some embodiments, the backing comprises metal such as galvanized steel and/or other backing material having the aforesaid desired properties, including, for example, composite laminate structure, layered paper, thermoplastic, thermoset, carbon fiber, polyester, polycarbonate, spun polyolefin, natural or synthetic fiber, woven material, and the like.
Disclosed are aspects of board finishing systems. For example, in various aspects, disclosed are kits, gypsum boards, joint compound compositions, wall assemblies, methods of treating walls, and products related to any of the foregoing, including reinforcement trim, e.g., for protecting corners where boards meet, fasteners, and joint tape. The joint compound preferably is a drying type composition with reduced shrinkage property, and includes binder and hollow spheres, resulting in an ultra lightweight formulation in some embodiments. The joint compound composition can be applied in a one-coat treatment in preferred embodiments. Other aspects of board finishing system accommodate such a one-coat treatment to allow a user to manipulate the compound closer to the plane of board as compared with conventional formulations.
In various embodiments, the present invention relates to joint compound compositions, board finishing systems, wall assemblies, methods of treating walls, and products related to any of the foregoing, including reinforcement trim, e.g., for protecting corners where boards meet, fastener, and joint tape. Various aspects of the invention advantageously impart considerable efficiencies in the finishing of wall assemblies comprising cladding, such as gypsum drywall, mat-faced board (e.g., having fiberglass facing), and the like. For example, the present invention allows for wall finishing to take place with significantly fewer steps required for any given desired finish level, e.g., a level 4 finish in accordance with Gypsum Association document GA-214 and/or ASTM C840 (“level 4”). As a result, wall finishing can occur more rapidly with less downtime. In addition, wall finishing in accordance with aspects of the invention requires less skill by users during cladding installation.
One aspect of the invention is predicated, at least in part, on the surprising and unexpected discovery of joint compound composition that exhibits low shrinkage. As a result, the joint compound advantageously can be applied in fewer coats than conventional joint compounds. In some embodiments, only one coat of joint compound is used over fasteners, joint tape, or reinforcement trims. However, if desired, more than one coat (e.g., two or three coats) may be applied depending on the level of finish desired. For example, conventional systems suffer from significant shrinkage, such as, for example, exceeding 15%, e.g., about 18% or greater. Embodiments of the invention provide considerably less shrinkage. Embodiments of joint compound also exhibit desirable flexibility properties and can be sanded readily and, desirably, do not crack.
Because the joint compound composition can be applied in fewer coats, advantageously, a user can manipulate the joint compound closer to the plane of the board. Conventionally, in multi-coat (e.g., 3 coats or more) systems, the user must broadly feather the joint compound across a wide radius from the seam to provide a visual illusion of a flat surface. Significant skill is required for the user to achieve such appearance when the joint compound thickness elevates significantly above the plane of board and board seams. By using a one-coat joint compound in accordance with embodiments of the invention, a user will not need to feather the joint compound as widely, and less skill is necessary to achieve a flat visual appearance. In some embodiments, board is specially designed to have a smaller taper than conventional board or no taper at all (i.e., squared edge) in the machine direction edges as described herein.
In other aspects, the invention provides for a special non-swellable material that can be used in joint tape as well as for a face layer in reinforcement trim composite used to conceal and protect wall corners where two boards meet at an angle (e.g., an “inside” corner or “outside” corner as understood in the art). The trim can also include a backing (e.g., comprising metal or other material) to provide rigidity and support.
Adhesive can be used in various aspects of the invention. In some embodiments, the adhesive is an aqueous quick-drying adhesive such as an aqueous wall covering adhesive (e.g., such as those marketed by Roman Adhesives), an aqueous bonding agent (e.g., such as those marketed by United States Gypsum Company), or an aqueous latex emulsion glue (e.g., such as those marketing by OSI). For example, such adhesive can be applied to framing members to minimize the number of fasteners used to hang board. Adhesive can also be used to facilitate application of joint tape and reinforcement trim in accordance with embodiments of the invention.
A fastener, in accordance with embodiments of the invention, can be used to accommodate a single coat of joint compound. For example, the fastener can include a concave head design to create a dimpled effect although other fasteners are possible, including staples or other drywall screws. One or more of these various aspects can be combined in a board finishing system in accordance with embodiments of the invention.
Reference is now made to the figures to depict advantageous illustrative embodiments of the invention.
The framing members 116 are desirably provided with adhesive 120 to promote adhesion to the boards 110, 112, and 114 and to allow the use of fewer fasteners 118 than are used in conventional systems. Since fasteners need to be covered by joint compound, reducing the number of fasteners is thereby advantageous in terms of efficiency, ease, and quality of installation.
Board edges are generally identified as being in the machine direction or cross direction based on how the board is made on the manufacturing line. Edges along the machine direction are normally the longer edges and are usually wrapped with cover sheet (e.g., made of paper) during board manufacture in which a cementitious slurry is deposited on a moving cover sheet (e.g., on a conveyor) to initially form a long, continuous ribbon of board precursor, which is eventually cut in the cross direction to desired dimensions as known in the art (e.g., 4′×8′; 4′×10′; 4′×12′; etc., although different widths and lengths are possible, including 36 inch wide board, or 54 inch wide board). For example, board 110 has machine direction edges 122 and 124 and cross-machine edges 126 and 128. Similarly, board 112 has machine direction edges 130 and 132 and cross-machine edges 134 and 136, while board 114 has machine direction edges 138 and 140 and cross-machine edges 142 and 144. As discussed in
Two boards can meet in various configurations to form a seam, often referred to as a joint. Since machine edges are tapered while cross machine joints are not tapered, the nature of the joints will vary depending on which edges of the boards meet. When a machine direction edge of one board meets a machine direction board of another board, a machine direction joint is formed where two tapers meet to form a recess. When a cross direction edge of one board meets a cross direction edge of another board, a butt joint, without tapers, is formed. As seen in
To illustrate the tapered edges in the machine direction of board, reference is made to
As seen in
In
Conventional systems, as shown in
The inventive embodiments illustrated in
As seen in exploded view of
To illustrate an inside corner,
As seen in exploded view of
The trim face 430 or 468 desirably comprises non-swelling paper (natural or synthetic) in some embodiments. The non-swelling paper is particularly desirable in one coat systems since less compound will go over the paper and disguise any unwanted swelling that might lead to bulging or other unsightly results. For example, in some embodiments, the face 430 or 468 has a dimensional stability of less than about 0.4% machine direction (MD) expansion and less than about 2.5% cross machine direction (CD) expansion (e.g., less than about 0.3% MD expansion, and less than about 1.5% CD expansion, such as less than about 0.2% MD expansion, and less than about 1% CD expansion after 30 minute immersion in water, ASTM C474-05, Section 12. It will be understood that embodiments that pass testing relative to ASTM C474-05 can also exceed the minimum performance specifications established in ASTM C475/C475M-12 Standard Specification for Joint Compound and Joint Tape for Finishing Gypsum Board.
In some embodiments, the face 430 or 468 has a thickness from about 0.01 inches (≈0.0254 cm) to about 0.125 inches (≈0.318 cm), such as from about 0.05 inches (≈0.127 cm) to about 0.0625 (≈159 cm). It will be understood that the joint tape can be composed of the same materials, characteristics, and properties as the reinforcement trim face.
The backing 432 or 470 for the reinforcement trim 428 or 466 can comprise any suitable material that provides strength to the trim composite. The backing material is useful to reduce, control, or eliminate seam cracking in the wall angles when new construction framing shifts and minor wall displacement occurs. The backing material also, in conjunction with the facing material, serves the function of forming a true and straight angle line along the vertex where two walls join or intersect at an angle. For example, the trim backing 432 or 470 can comprise a composite laminated structure, layered paper (synthetic or natural), thermoplastic, thermoset, natural or synthetic fiber, carbon fiber, polyester, polycarbonate, fiberglass, non-woven natural or synthetic materials, woven natural or synthetic materials, spun polyolefin, or metals such as steel, e.g., electro-galvanized and/or hot dipped galvanized, zinc phosphate treated and/or dried in place chromate sealer, and/or other treated or coated metal and the like. For example, in one illustrative embodiment, the backing 432 or 470 is formed of galvanized steel. The trim backing 432 or 470 desirably has any suitable thickness, e.g., a thickness of at least about 0.010, e.g., about 0.012 inches (≈0.030 cm) to about 0.0625 inches (≈0.159 cm), such as from about 0.012 inches to about 0.030 inches (≈0.0762 cm). In some embodiments of backing material, such as when galvanized steel is used, the backing typically imparts a Rockwell hardness scale B from about 45 to about 85, such as from about 55 to about 65, when measured according to ASTM E18-03.
Preparation of trims is illustrated in embodiments with non-swellable paper face with galvanized steel backing. The trims are prepared by running flat steel (on a spool) through a series of progressive dies and the facing material and metal backing are introduced just after the last set of dies. The facing and backing can be hot-melt glued together in some embodiments. Other techniques for forming reinforcement trims formed from a variety of materials will be apparent to one of skill in the art.
With respect to inside and outside corner installation,
In these and other embodiments, joint compound composition in accordance with the present invention comprising (a) binder, (b) hollow spheres (sometimes referred to as bubbles) having an average isostatic crush strength of at least about 100 psi (e.g., at least about 250 psi) as measured according to ASTM D 3102-78, and optionally other ingredients. Preferably, the joint compound composition exhibits low shrinkage. For example, in some embodiments, the joint compound composition exhibits a shrinkage of about 10% or less by volume, e.g., about 7% or less, such as about 5% or less, about 2% or less, about 1% or less, about 0.1% or less, or about zero (no shrinkage) as measured by ASTM C474-05, Section 6.
The joint compound can have any suitable density, but preferably is an ultra lightweight composition having a density of about 10 lb/gal or less, such as about 8 lb/gal or less. For example, in some embodiments, the joint compound has a density from about 2 lb/gal (≈240 kg/m3) to about 8 lb/gal (≈960 kg/m3) (preferably from about 2 lb/gal to about 6 lb/gal (≈720 kg/m3), more preferably about 3 lb/gal (≈360 kg/m3) to about 4 lb/gal (≈480 kg/m3)).
Generally, the composition is a drying type joint compound, wherein the compound hardens by evaporation of water. Thus, in some embodiments, the joint compound composition is substantially free of setting-type materials such as calcined gypsum, cement, or other hydraulically setting materials. Furthermore, in some embodiments, the joint compound composition can desirably be substantially free of raw materials such as bulk filler, clays, starch, or mica; including such examples as calcium carbonate, expanded perlite, calcium magnesium carbonate, limestone, calcium sulfate dihydrate, a gelling clay such as attapulgite clay, a delaminated clay, such as kaolin clay, talcs, and diatomaceous earth. Furthermore, the joint compound composition can desirably be substantially free of any combination of the aforementioned raw materials.
As used herein, “substantially free” of such setting minerals, bulk filler, clays, starch, mica, or a combination thereof means that the joint compound composition contains either (i) 0 wt. % based on the weight of the composition, or no such setting minerals, bulk filler, clays, starch, mica, or a combination thereof, or (ii) an ineffective or (iii) an immaterial amount of such setting minerals, bulk filler, clays, starch, mica, or a combination thereof. An example of an ineffective amount is an amount below the threshold amount to achieve the intended purpose of using such setting minerals, bulk filler, clays, starch, mica, or a combination thereof as one of ordinary skill in the art will appreciate. An immaterial amount may be, e.g., below about 5 wt. %, such as below about 2 wt. %, below about 1 wt. %, below about 0.5 wt. %, below about 0.2 wt. %, below about 0.1 wt. %, or below about 0.01 wt. % as one of ordinary skill in the art will appreciate. However, if desired in alternative embodiments, such ingredients can be included in the joint compound composition.
In alternative embodiments, bulk filler (e.g., calcium carbonate or limestone) or delaminated clay, such as kaolin clay may be present. These raw materials can be added, in some embodiments, to tailor the joint compound for the subjective feel desired by the end user during the application process. These raw materials, as used herein, do not otherwise change the physical properties of the joint compound. In such embodiments, up to about 40 wt. % of bulk filler, such as calcium carbonate or limestone, can be included. If included, in some embodiments, the bulk filler can be present, for example, in an amount of up to about 35 wt. %, up to about 30 wt. %, up to about 25 wt. %, up to about 20 wt. %, up to about 15 wt. %, up to about 10 wt. %, up to about 5 wt. %, or up to about 1 wt. % added based on the weight of the wet composition. Each of the aforementioned endpoints can have a lower limit, e.g., ranging from 1 wt. %, 5 wt. %, 10 wt. %, 15 wt. %, 20 wt. %, 25 wt. %, 30 wt. %, or 35 wt. %, as numerically appropriate.
For example, in various embodiments, the bulk filler can be present from about 1 wt. % to about 40 wt. %, e.g., from about 1 wt. % to about 30 wt. %, from about 1 wt. % to about 25 wt. %, from about 1 wt. % to about 20 wt. %, from about 1 wt. % to about 15 wt. %, from about 1 wt. % to about 10 wt. %, from about 5 wt. % to about 30 wt. %, from about 5 wt. % to about 25 wt. %, from about 5 wt. % to about 20 wt. %, from about 5 wt. % to about 15 wt. %, from about 5 wt. % to about 10 wt. %, from about 10 wt. % to about 30 wt. %, from about 10 wt. % to about 25 wt. %, from about 10 wt. % to about 20 wt. %, from about 15 wt. % to about 30 wt. %, from about 15 wt. % to about 25 wt. %, or from about 20 wt. % to about 30 wt. %.
If included, delaminated clay, such as kaolin clay, may be present in some embodiments, for example, in an amount up to about 5 wt. %, up to about 4.5 wt. %, up to about 4 wt. %, up to about 3.5 wt. %, up to about 3 wt. %, up to about 2.5 wt. %, up to about 2 wt. %, up to about 1.5 wt. %, up to about 1 wt. %, up to about 0.5 wt. %, or up to about 0.1 wt. % added based on the weight of the wet composition. Each of the aforementioned endpoints can have a lower limit, e.g., ranging from 0.1 wt. %, 0.5 wt. %, 1 wt. %, 1.5 wt. %, 2 wt. %, 2.5 wt. %, 3 wt. %, 3.5 wt. %, 4 wt. %, or 4.5 wt. %, as numerically appropriate.
For example, in various embodiments, delaminated clay, such as kaolin clay, can be present from about 0.1 wt. % to about 5 wt. %, e.g., from about 0.1 wt. % to about 4 wt. %, from about 0.1 wt. % to about 3 wt. %, from about 0.1 wt. % to about 2 wt. %, from about 0.1 wt. % to about 1 wt. %, from about 0.1 wt. % to about 0.5 wt. %, from about 0.5 wt. % to about 5 wt. %, from about 0.5 wt. % to about 4 wt. %, from about 0.5 wt. % to about 3 wt. %, from about 0.5 wt. % to about 2 wt. %, from about 0.5 wt. % to about 1 wt. %, from about 1 wt. % to about 5 wt. %, from about 1 wt. % to about 4 wt. %, from about 1 wt. % to about 3 wt. %, from about 1 wt. % to about 2 wt. %, from about 2 wt. % to about 5 wt. %, from about 2 wt. % to about 4 wt. %, from about 2 wt. % to about 3 wt. %, from about 3 wt. % to about 5 wt. %, from about 3 wt. % to about 4 wt. %, or from about 4 wt. % to about 5 wt. %.
Any suitable binder can be used to achieve desired joint compound in accordance with aspects of the invention. Desired binders hold particles in composition together and form a film. In some embodiments, the binder is selected from acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof. The binder in some embodiments has a glass transition temperature (Tg) from about 32° F. (≈0° C.) to about 70° F. (≈21° C.), e.g., about 32° F. to about 66° F. (≈18° C.), such as from about 40° F. (≈5° C.) to about 60° F. (≈15° C.), e.g., about 55° F. (≈13° C.). In some embodiments, the binder has a minimum film forming temperature (MMFT) from about 32° F. to about 90° F. (≈32° C.), e.g., from about 32° F. to about 86° F. (≈30° C.), such as from about 40° F. (≈5° C.) to about 60° F. (≈15° C.), e.g., about 52° F. (≈11° C.).
In some embodiments, the binder generally can be any suitable film-forming resin (or combinations thereof) capable of forming a solid film and binding solid materials to the surface to which the joint compound composition is applied. For example, the binder can be an acrylic acid polymer and/or acrylic acid copolymer in some embodiments. The binder is in the form of an aqueous emulsion in some embodiments, with suitable latex emulsion media including, but not limited to, acrylics, such as, for example, vinyl acrylics and styrenated acrylics. In some embodiments, suitable binder materials include acrylic latex, vinyl-acrylic, vinyl acetate, polyurethane, and/or combinations thereof.
Useful latex emulsion media include polyacrylate ester polymers marketed under the RHOPLEX® trade names (Rohm & Haas), acrylic polymers, vinyl acrylic polymers, for example, vinyl acetate-butyl acrylate copolymers, styrene acrylic polymers, and vinyl acetate polymers marketed under the UCAR™ and NEOCAR™ trade names (The Dow Chemical Company, Michigan) such as UCAR™ 367; emulsion polymers products marketed under the VINREZ® trade name (Halltech, Inc., Ontario); vinyl acrylic polymers marketed under the Plioway® trade name (Eliokem, Ohio); acrylic, vinyl acrylic, and styrene acrylic latex polymers marketed under the AQUAMAC™ trade name (Resolution Specialty Materials, LLC, Illinois); and vinyl acrylic resin marketed under the trade name VINREZ® 663 V15 (Halltech, Inc., Ontario), which has a glass temperature of about 18° C. Another vinyl acrylic copolymer binder is marketed under product identification no. HP-31-496 (Halltech, Inc., Ontario), and has a glass temperature of about 0° C.
Suitable functionalized acrylics, alkyds, polyurethanes, polyesters, and epoxies can be obtained from a number of commercial sources. Useful acrylics are sold under the ACRYLOID™ trade name (Rohm & Haas, Co., Pennsylvania); useful epoxy resins are sold under the EPON™ trade name (Resolution Specialty Materials, LLC, Illinois); useful polyester resins are sold under the CYPLEX® trade name (Cytec Industries, New Jersey); and useful vinyl resins are sold under the UCAR™ trade name (The Dow Chemical Company, Michigan).
The binder can be included in the joint compound composition in any suitable amount. For example, the binder can be included in an amount from about 5 wt. % to about 100 wt. % by weight (on a solids basis) of the wet composition, such as from about 20 wt. % to about 80 wt. %, from about 30 wt. % to about 70 wt. %, from about 40 wt. % to about 60 wt. %, etc.
The hollow spheres contain self contained air bound by a solid barrier. Since the air is contained within a solid shell, the air does not coalesce such that, overall, the air can be distributed throughout the compound and maintain a substantially uniform density. The hollow spheres facilitate a lower density but desirably have good strength properties, such that the hollow spheres impart crush resistance, such that the dried joint compound, after application, is substantially non-friable, in some embodiments, unlike conventional joint compound, which is friable and brittle.
The spheres in some embodiments facilitate an ultra lightweight joint compound, which results in desired properties and creates less strain on a user in lifting compound in pails, etc. during a work day. The spheres can have any suitable density, such as a density from about 0.0015 lb/in3 to about 0.04 lb/in3, e.g., from about 0.0018 lb/in3 (≈0.05 g/cm3) to about 0.036 lb/in3 (≈1 g/cm3), such as from about 0.0036 lb/in3 (≈0.1 g/cm3) to about 0.0253 lb/in3 (≈0.7 g/cm3). With respect to strength, for example, the spheres can have an average isostatic crush strength of at least about 50 psi (≈340 kPa) as measured according to ASTM D 3102-78, such as an isostatic crush strength of at least about 100 psi (≈690 kPa). For example, the isostatic strength of the spheres can be from about 50 psi to about 50,000 psi (≈344,740 kPa), from about 50 psi to about 25,000 psi (≈172,000 kPa), from about 50 psi to about 10,000 psi, from about 50 psi to about 5,000 psi (≈34,000 kPa), from about 50 psi to about 1,000 psi, from about 50 psi to about 500 psi (≈3,450 kPa), from about 100 psi to about 50,000 psi, from about 100 psi to about 25,000 psi, from about 100 psi to about 10,000 psi, from about 100 psi to about 5,000 psi, from about 100 psi to about 1,000 psi, from about 100 psi to about 500 psi, from about 250 psi (≈1,720 kPa) to about 50,000 psi, from about 250 psi to about 25,000 psi, from about 250 psi to about 10,000 psi, from about 250 psi to about 5,000 psi, from about 250 psi to about 1,000 psi, from about 250 psi to about 500 psi, from about 500 psi to about 50,000 psi, from about 500 psi to about 25,000 psi, from about 500 psi to about 10,000 psi, from about 500 psi to about 5,000 psi, from about 500 psi to about 1,000 psi, from about 1,000 psi to about 50,000 psi, from about 1,000 psi to about 25,000 psi, from about 1,000 psi to about 10,000 psi, from about 1,000 psi to about 5,000 psi, from about 2,500 psi (≈17200 kPa) to about 50,000 psi, from about 2,500 psi to about 25,000 psi, from about 2,500 psi to about 10,000 psi, from about 2,500 psi to about 5,000 psi, etc.
Examples of types of spheres in accordance with embodiments of the invention include lime boro-silicate, polystyrene, ceramic, recycled-glass, expanded glass, and lightweight polyolefin beads, and/or any other chemical form of plastic. For example, in some embodiments, spheres for use in the joint compound include but are not limited to soda lime boro-silicate glass bubbles (e.g., as marketed under the Scotchlite™ (3M) trade name), multi-cellular hollow glass microspheres (e.g., as marketed under the Omega-Bubbles™ (Omega Minerals) trade name), expandable polymeric microspheres (e.g., as marketed under the DUALITE® (Henkel) trade name), polyolefin micro beads and polystyrene microspheres (e.g., as marketed under the Spex•Lite® (Schabel Polymer Technology, LLC) trade name), expanded glass spheres (e.g., as marketed under the Poraver® North America trade name), and combinations thereof. As illustrative embodiments, suitable spheres can comprise Scotchlite™ (3M) K1 and/or K15.
The spheres can have any suitable diameter and can be provided in any suitable concentration. It will be understood that the term spheres is known in the art and does not imply a perfectly geometric sphere, inasmuch as the spheres can have irregular shapes. Thus, the diameter as used herein refers to the diameter of the smallest geometric sphere that encompasses the actual sphere. In some embodiments, the spheres can have a diameter from about 10 microns to about 100 microns, such as from about 40 microns to about 80 microns, or from about 50 microns to about 70 microns. With respect to amounts, in some embodiments, the spheres are present in an amount from about 2% to about 50% by weight of the wet composition, such as, for example, from about 5% to about 35%, from about 7% to about 25%, or from about 10% to about 20%.
In some embodiments, the joint compound composition, optionally, also includes surfactant. Desirably, the surfactant can facilitate stabilizing binder so the binder does not flocculate. Surfactant also desirably can provide a wetting or dispersing action. In this respect, when dry raw materials are added to water, the dry materials can compete for water and form unwanted agglomerations. Thus, in some embodiments, the surfactant is included to increase the ease of mixing when incorporating dry materials in liquid and further assists in pumping joint compound from fill stations and into pails during manufacture. The surfactant is also beneficial during use, when applying the joint compound, e.g., with dispensing tools known in the art.
For example, in some embodiments, the surfactant can be a nonionic surfactant having a hydrophilic-lipophilic balance (HLB) from about 3 to about 20, such as from about 4 to about 15 or from about 5 to about 10. It will be understood that surfactants with HLB values below 9 are generally considered to be lipophilic, those with values between 11 and 20 are generally considered to be hydrophilic, and those with values between 9 and 11 are generally considered to be intermediate. Suitable non-ionic surfactants having an HLB value below about 9 include, but are not limited to, octylphenol ethoxylates and nonylphenol ethoxylates, including non-ionic surfactants having HLB values below about 9 marketed under the TRITON™ and TERGITOL™ trade names (The Dow Chemical Company, Michigan). Suitable non-ionic surfactants having a HLB value greater than about 11 include octylphenol ethoxylates and nonylphenol ethoxylates which have more ethylene oxide units than the non-ionic surfactants having a HLB value below about 9. Useful surfactants having HLB values greater than about 11 are also marketed under the TRITON™ trade name (The Dow Chemical Company, Michigan). Other surfactants may also be used provided that the HLB value for the (blend of) surfactant(s) is as previously described for joint compound compositions and combinations thereof. If included, the nonionic surfactant can be present in any suitable amount, such as from about 0.001% to about 15% by weight of the wet composition, such as from about 0.001% to about 10%, from about 0.001% to about 5%, or from about 0.01% to about 0.5%.
One or more defoamer, such as, for example, petroleum distillate or the like, as known in the art, is optionally included in some embodiments of the joint compound composition. If included, the defoamer can be present in an amount from about 0.01% to about 15% by weight of the wet composition, such as from about 0.05% to about 5%, or from about 0.3% to about 1%.
Humectant is optionally included in some embodiments. For example, humectants can be used to help keep the joint compound wetter by facilitating retention of moisture and can also aid with use of mechanical dispensing tools. In particular, one or more humectants is included in embodiments of aqueous joint compound composition in order to slow the drying of the joint compound composition and provide a more consistent finish. Humectants can also advantageously provide freeze thaw tolerance and/or stability in the joint compound composition. Any suitable humectants can be included, such as, for example, sorbitol derivatives, polyhydric alcohols, including but not limited to glycols such as ethylene glycol, diethylene glycol (DEG), triethylene glycol, propylene glycol, di-propylene glycol, and/or tri-propylene glycol, or any combination thereof. If included, the humectants can be included in an amount from about 0.001% to about 15% by weight of the wet composition, such as from about 0.001% to about 10%, from about 0.01% to about 5%, or from about 0.001% to about 3%.
Optionally, the joint compound composition comprises a rheological modifier in some embodiments. If included, the rheological modifier is generally provided to enhance certain rheological properties such as the flow, viscosity, application properties, and other performance attributes associated with joint compounds. For example, in some embodiments, rheological modifiers are often added to provide the coating compositions with desired viscosity values as described herein, e.g., using C.W. Brabender visco-corder equipment for measuring the viscosity of the joint compound composition.
Suitable rheological modifiers for optional use in the joint compound composition include, but are not limited to, cellulosic and associative thickeners, including but limited to, hydrophobically modified ethoxylated urethanes (HEUR), hydrophobically modified alkali-swellable emulsions (HASE), and styrene-maleic anhydride terpolymers (SMAT), and/or combinations thereof. Exemplary cellulosic rheological modifiers include, but are not limited to, cellulose ethers such as hydroxyethyl cellulose (HEC), ethylhydroxyethyl cellulose (EHEC), methylhydroxyethyl cellulose (MHEC), carboxymethyl cellulose (CMC), hydroxypropylmethyl cellulose (HPMC), and/or other cellulose ethers having a molecular weight between about 1000 and 500,000 daltons, e.g., alkyl hydroxypropyl cellulose ethers, hydroxypropyl methyl celluloses, as well as xanthan gums, sodium alginates and other salts of alginic acid, carrageenans, gum arabic (mixed salts of arabic acid), gum karaya (an acetylated polysaccharide), gum tragacanth (a complex mixture of acidic polysaccharides), gum ghatti (the calcium and magnesium salt of a complex polysaccharide), guar gum (a straight chain galactomannan) and its derivatives, locust bean gum (a branched galactomannan), tamarind gum, psyllium seed gum, quince seed gum, larch gum, pectin and its derivatives, dextrans, and hydroxypropylcelluloses, or any combination thereof.
If included, the rheological modifier can be included in any suitable amount, e.g., to achieve a desired viscosity as will be appreciated by one of ordinary skill in the art. For example, in some embodiments, the rheological modifier is included in an amount from about 0.01% to about 15%, by weight of the wet composition, such as from about 0.01% to about 10%, from about 0.1% to about 5%, from about 0.1% to about 3%, from about 0.1% to about 2%, or from about 0.1% to about 1%. The joint compound typically comprises from about 0.01 wt. % to about 10 wt. %, about 0.1 wt. % to about 5.0 wt. %, and/or about 0.10 wt. % to about 3.0 wt. % of the cellulosic thickener. The alkyl group of useful alkyl hydroxypropyl celluloses may contain up to 9 carbon atoms, but usually the alkyl group contains from one to three atoms. Hydroxypropyl methyl celluloses having an average of about two hydroxypropyl and/or methoxypropyl groups per anhydroglucose unit are often used. The viscosity of an aqueous solution containing about 2 wt. % of a suitable alkyl hydroxypropyl cellulose ether at 20° C. is about 60,000 centipoises (cps) to about 90,000 cps as measured with an Ubbelohde tube capillary viscometer. Alternatively, similar measurements can be made with a Brookfield rotational viscometer at a speed between about 2.5 rpm and 5 rpm. In one refinement, the initially solid-colored coating composition contains about 0.25 wt. % of an alkyl hydroxypropyl cellulose ether. Of course, other types of cellulosic thickeners may also be used, and a greater quantity may be needed if a lower viscosity thickener is used (or vice versa). Exemplary alkyl hydroxypropyl cellulose ethers are marketed under the Methocel® trade name (The Dow Chemical Company, Michigan).
Suitable associative thickeners for optional use in the joint compound compositions include hydrophobically modified ethoxylated urethanes (HEUR), hydrophobically modified alkali-swellable emulsions (HASE), and styrene-maleic anhydride terpolymers (SMAT). HEUR thickeners (also generally known as polyurethane or PUR associative thickeners) can be included in aqueous, latex-based joint compound and other yield stress fluid/solid like compositions. Acidic acrylate copolymers (cross-linked) of ethyl acrylate and methacrylic acid, and acrylic terpolymers (cross-linked) of ethyl acrylate, methacrylic acid, and nonionic urethane surfactant monomer may also optionally be used as associative thickeners. When one or more suitable associative thickeners are used, the thickening reaction is caused in part by either association between the associative thickener and at least one other particle of the joint compound composition (e.g., a pigment particle or resin particle) or another associative thickener molecule. In various embodiments, if included, the joint compound composition can comprise from about 0.01 wt. % to about 10 wt. %, about 0.1 wt. % to about 5.0 wt. %, and/or about 0.1 wt. % to about 3 wt. % of the associative thickener. Useful associative thickeners include those marketed under the Alcogum® trade name (Alco Chemical Company, TN), the Acrysol® trade name (Rohm & Haas, PA), and the Viscalex® trade name (Ciba Specialty Chemicals, NY).
In one illustrative embodiment, the rheological modifier comprises a HEUR and a cellulose ether, e.g., an alkyl hydroxypropyl cellulose ether. Without intending to be bound by any particular theory, it is believed that the combination of an associative thickener and a cellulose ether provides improved application and storage properties. For example, the lubricity and flow characteristic of the joint compound compositions (when applied to a substrate) can be improved by using such a combination of associative thickener and cellulose ether. Additionally, such a combination can help prevent the spheres of the joint compound compositions from settling out (when the joint compound compositions are stored in bulk).
The rheologically modified associative thickener system generally performs best under alkaline conditions. Thus, it is generally advisable to include a basic material in the joint compound composition in order to give the final joint compound composition a pH of at least about 8.0. A variety of basic materials may be used to increase the pH including but not limited to ammonia, caustic soda (sodium hydroxide), tri-ethylamine (TEA), and 2-amino-2-methyl-1 propanol (AMP). In various embodiments, the joint compound composition comprises about 0.001 wt. % to about 10 wt. %, about 0.01 wt. % to about 0.5 wt. %, and/or about 0.01 wt. % to about 0.50 wt. % of the alkaline/basic material.
In some embodiments, joint compound composition optionally comprises biocide in any suitable amount, e.g., from about 0% to about 3% by weight of the wet composition, such as from about 0.05% to about 2%, from about 0.1% to about 1.5%, or from about 0.1% to about 1%. If included, in some embodiments of joint compound composition, the biocide comprises a bactericide and/or a fungicide. An illustrative useful bactericide is marketed under the MERGAL 174® trade name (TROY Chemical Corporation). An illustrative useful fungicide is marketed under the FUNGITROL® trade name (International Specialty Products, New Jersey), or any combination thereof.
The joint compound composition can be formulated to have any suitable viscosity to allow for workability as will be understood in the art. For example, the viscosity of the joint compound composition when wet can have a viscosity from about 100 Brabender units (BU) to about 700 BU, such as from about 100 BU to about 600 BU, about 100 BU to about 500 BU, about 100 BU to about 400 BU, about 100 BU to about 300 BU, about 100 BU to about 200 BU, about 130 BU to about 700 BU, about 130 BU to about 600 BU, about 130 BU to about 500 BU, about 130 BU to about 400 BU, about 130 BU to about 300 BU, about 130 BU to about 200 BU, about 150 BU to about 700 BU, about 150 BU to about 600 BU, about 150 BU to about 500 BU, about 150 BU to about 400 BU, about 150 BU to about 300 BU, or about 150 BU to about 200 BU. One of ordinary skill in the art will readily recognize Brabender units. The viscosity is measured according to ASTM C474-05, Section 5 using a CW Brabender viscometer with a Type-A Pin, sample cup size of ½ pint with a 250 cm-gm cartridge Brabender Torque-Head and an RPM of 75.
Desirably, in some embodiments, to enhance the anti-shrinkage property of the joint compound composition, water content is desirably reduced compared with conventional formulations. It will be understood that some raw materials (e.g., latex emulsions and the like) are provided in an aqueous form. However, additional water (e.g., gauging water) is desirably kept low in some embodiments, e.g., in an amount of about 60% or less by weight of the wet composition, e.g., from about 0% to about 50%, such from about 0% to about 30%, from about 0% to about 15%, or from about 0% to about 10%, etc. In some embodiments, the total water content of the joint compound, including water from other raw material including latex emulsion binder, and any gauging water, could range, e.g., from about 5% to about 60% by weight of the wet composition, such as from about 10% to about 45% by weight, or from about 25% to about 45% by weight, or over.
In some embodiments, the invention provides a joint compound composition consisting essentially of (a) latex emulsion binder in an amount from about 3% to about 90% by weight of the wet composition; (b) a plurality of hollow spheres having an average isostatic crush strength of at least about 100 psi, as measured according to ASTM D3102-78, wherein the spheres are present in an amount from about 5% to about 25% by weight of the wet composition; (c) nonionic surfactant in an amount from about 0.001% to about 5% by weight of the wet composition; and (d) humectant in an amount from about 0.001% to about 3% by weight of the wet composition; and, optionally, (e) defoamer in an amount from about 0.05% to about 5% by weight of the wet composition; (f) rheological modifier in an amount from about 0.1% to about 5% by weight of the wet composition; (g) biocide, in an amount from about 0.1% to about 1.5% by weight of the wet composition; (h) bulk filler, such as calcium carbonate or limestone in an amount from about 1% to about 40% by weight of the wet composition; and (i) delaminated clay, such as kaolin clay, in an amount from about 0.1% to about 5% by weight of the wet composition. In such embodiments, the composition precludes any raw material other than the aforesaid ingredients that materially affects the inventive joint compound composition.
Embodiments of the invention also provide a wall assembly in accordance with the various aspects described herein. The wall assembly comprises two adjacent boards, joined by a seam. In some embodiments, only one-coat of the joint compound is applied over the seam to provide a uniform aesthetic appearance. However, if desired, more than one coat (e.g., two or three coats) may be applied depending on the level of finish desired. The joint compound composition comprises binder selected from acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof. The composition also comprises a plurality of hollow spheres. The spheres desirably have an average isostatic crush strength of at least about 100 psi as measured according to ASTM D3102-78. The wall assembly further comprises dimensionally stable, non-swelling flat joint tape embedded in the seam.
Embodiments of the invention also provide a method of treating a wallboard assembly of two adjacent boards joined by a seam in accordance with the various aspects described herein. In some embodiments, the method comprises applying joint tape and one coat of the joint compound composition to the seam. The joint compound composition comprises binder selected from acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof. The composition also comprises a plurality of hollow spheres. The spheres desirably have an average isostatic crush strength of at least about 100 psi as measured according to ASTM D3102-78. The method further comprises drying the composition. In some embodiments, after the joint compound is applied and dried, the wallboard assembly can be sanded and/or painted to give a desired visual appearance.
The following embodiments further illustrate aspects of the invention but, of course, should not be construed as in any way limiting its scope.
In an embodiment, a drying-type joint compound composition comprises, a binder selected from acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof; and a plurality of hollow spheres, wherein the spheres have an average isostatic crush strength of at least about 100 psi as measured according to ASTM D3102-78.
In another embodiment of the joint compound composition, the binder is an acrylic acid polymer or acrylic acid copolymer.
In another embodiment of the joint compound composition, the binder is in the form of an aqueous emulsion.
In another embodiment of the joint compound composition, the composition has a density from about 2 lb/gal to about 8 lb/gal.
In another embodiment of the joint compound composition, the composition exhibits a shrinkage of about 2% or less as measured by ASTM C474-05.
In another embodiment of the joint compound composition, the composition is substantially free of setting minerals, bulk filler, clays, starch, mica, or a combination thereof.
In another embodiment of the joint compound composition, the composition is substantially free of calcium carbonate, expanded perlite, calcium magnesium carbonate, limestone, calcium sulfate dihydrate, delaminated clay, such as kaolin clay, talcs, diatomaceous earth, or a combination thereof.
In one embodiment of the joint compound composition, the composition is substantially free of gelling clays. Such gelling clays include attapulgites, sepiolites, bentonites, laponites, nontronites, beidellites, laponites, yakhontovites, zincsilites, volkonskoites, hectorites, saponites, ferrosaponites, sauconites, swinefordites, pimelites, sobockites, stevensites, svinfordites, vermiculites, water-swellable synthetic clays, smectites, e.g., montmorillonites, particularly sodium montmorillonite, magnesium montmorillonite, and calcium montmorillonite, illites, mixed layered illite/smectite minerals such as rectorites, tarosovites, and ledikites, magnesium aluminum silicates, and admixtures of the clays named above. Palygorskite attapulgite clays are one type of illustrative gelling clay that are excluded in this embodiment.
In another embodiment of the joint compound composition, the binder has a glass transition temperature (Tg) from about 32° F. to about 70° F.
In another embodiment of the compound composition, the binder has a minimum film forming temperature (MMFT) from about 32° F. to about 90° F.
In another embodiment of the joint compound composition, the spheres have an isostatic crush strength of at least about 250 psi.
In another embodiment of the joint compound composition, the spheres have a density from about 0.0015 lb/in3 to about 0.04 lb/in3.
In another embodiment of the joint compound composition, the spheres comprise lime boro-silicate, polystyrene, ceramic, recycled-glass, expanded glass, and lightweight polyolefin beads, thermoplastic, thermoset, or any combination thereof.
In another embodiment of the joint compound composition, the composition further comprises a nonionic surfactant having a hydrophilic-lipophilic balance (HLB) from about 3 to about 20.
In another embodiment of a joint compound composition consisting essentially of: (a) latex emulsion binder in an amount from about 3% to about 90% by weight of the wet composition; (b) a plurality of hollow spheres having an average isostatic crush strength of at least about 100 psi as measured according to ASTM D3102-78, wherein the spheres are present in an amount from about 5% to about 25% by weight of the wet composition; (c) nonionic surfactant in an amount from about 0.001% to about 5% by weight of the wet composition; and (d) humectant in an amount from about 0.001% to about 3% by weight of the wet composition; and, optionally: (e) defoamer in an amount from about 0.05% to about 5% by weight of the wet composition; (f) rheological modifier in an amount from about 0.1% to about 5% by weight of the wet composition; (g) biocide, in an amount from about 0.1% to about 1.5% by weight of the wet composition; (h) bulk filler, such as calcium carbonate or limestone in an amount from about 1% to about 40% by weight of the wet composition; and (i) delaminated clay, such as kaolin clay, in an amount from about 0.1% to about 5% by weight of the wet composition.
In another embodiment, a wall assembly comprises: (a) two adjacent boards, joined by a seam; (b) only one-coat of the joint compound composition in the seam to provide a uniform aesthetic appearance; and (c) dimensionally stable non-swelling flat joint tape embedded in the seam.
In another embodiment of the wall assembly, at least one board has a tapered edge adjacent to the seam, the taper edge having a maximum depth of about 0.125 inch (about 0.3 cm) or less.
In another embodiment of the wall assembly, the boards comprise opposing face and back surfaces, wherein the faces of two adjacent boards are disposed with respect to each other to define an inside corner with a corner angle between the board faces from about 30° to about 180°.
In another embodiment of the wall assembly, the boards comprise opposing face and back surfaces, the faces of two adjacent boards are disposed with respect to each other to define an outside corner with an angle between the board faces from about 180° to about 300°.
In another embodiment of the wall assembly, the assembly further comprises reinforcement trim disposed over the seam, wherein the trim comprises (i) a facing material comprising paper having a dimensional stability of less than about 0.4% machine direction expansion and less than about 2.5% cross direction expansion after 30 minute immersion in water as measured according to ASTM C474-05, Section 12, and (ii) a reinforcement backing comprising paper, plastic, natural or synthetic fiber, carbon fiber, polyester, polycarbonate, fiberglass, non-woven natural or synthetic materials, woven natural or synthetic materials, spun polyolefin, or metal, wherein the backing has a thickness from about 0.012 inches (about 0.03 cm) to about 0.0625 inches (about 0.2 cm).
In another embodiment of the wall assembly, the assembly comprises adhesive for at least partially affixing the reinforcement trim to the edges of the board.
In another embodiment of the wall assembly, the assembly further comprises at least one framing member and adhesive, wherein the adhesive at least partially affixes at least one board to the framing member.
In another embodiment presented a method of treating a wallboard assembly of two adjacent boards joined by a seam, the method comprises (a) applying joint tape and one coat of the joint compound composition of claim 1 to the seam; and (b) drying the composition.
In another embodiment is presented, a reinforcement trim for protecting a seam of two adjacent boards having opposing face and back surfaces, the faces being disposed with respect to each other at an angle between the board faces, the trim comprising: a paper face characterized by a non-swelling synthetic paper facing material; and a reinforcement backing comprising paper, thermoplastic, thermoset, natural or synthetic fiber, carbon fiber, polyester, polycarbonate, fiberglass, non-woven natural or synthetic materials, woven natural or synthetic materials, spun polyolefin, or metal, wherein the backing has a thickness from about 0.012 inches (about 0.03 cm) to about 0.0625 inches (about 0.2 cm).
In another embodiment of the drying-type joint compound composition comprises, a binder selected from acrylic acid polymers, acrylic acid copolymers, alkyds, polyurethanes, polyesters, epoxies, and combinations thereof; and a plurality of hollow spheres, wherein the spheres have an average isostatic crush strength of at least about 250 psi as measured according to ASTM D3102-78; and wherein the density of the spheres are from about 0.0015 lb/in3 (about 0.04 g/cm3) to about 0.04 lb/in3 (about 1.1 g/cm3).
In another embodiment of the joint compound composition, the spheres have an isostatic crush strength of at least about 500 psi.
In another embodiment of the joint compound composition, the spheres have a density from about 0.0018 lb/in3 (≈0.05 g/cm3) to about 0.036 lb/in3 (≈1 g/cm3).
In another embodiment of the joint compound composition, in a 3/16 inch (about 0.5 cm) stripe, at least 60% of the water content is removed by drying within about 1.5 to 4.5 hours in a moderate environment of about 75° F. (about 24° C.) and about 50% relative humidity.
In another embodiment of the joint compound composition, in a 3/16 inch (about 0.5 cm) stripe, at least 60% of the water content is removed within about 1 to about 3 hours in a hot and dry environment of about 95° F. (about 35° C.) and about 10% relative humidity.
In another embodiment of the joint compound composition, in a 3/16 inch (about 0.5 cm) stripe, at least 60% of the water content is removed within about 5 to about 12.5 hours in a cold and damp environment of about 40° F. (about 4° C.) and about 80% relative humidity.
In another embodiment of the joint compound composition, in a 1/16 (about 0.2 cm) inch stripe, at least 60% of the water content is removed by drying within about 0.5 to 2 hours in a moderate environment of about 75° F. (about 24° C.) and about 50% relative humidity.
In another embodiment of the joint compound composition, in a 1/16 inch (about 0.2 cm) stripe, at least 60% of the water content is removed within about 1 hour in a hot and dry environment of about 95° F. (about 35° C.) and about 10% relative humidity.
In another embodiment of the joint compound composition, in a 1/16 inch (about 0.2 cm) stripe, at least 60% of the water content is removed within about 0.5 to about 3 hours in a cold and damp environment of about 40° F. (about 4° C.) and about 80% relative humidity.
Conventional joint compounds are applied in three separate coats to fasteners as well as in multiple coats to flat seams between boards in the same plane. Each conventional coat must separately dry before applying a new coat. While, the existing coat created by a conventional joint compound does not need to dry completely, about 75% of the water content must evaporate from the compound before the coat becomes firm enough to receive a second layer. This creates a significant period of downtime during which the other construction trades ordinarily cannot work inside the building while the wall finishing occurs.
The joint compounds of the present invention can be applied in a single coat over the seam and yet provide a uniform aesthetic appearance. If a second coat is required, the joint compounds of the present invention become firm enough to receive the second coat when about 60% of the water evaporates from the compound. Accordingly, the installation of walls and ceilings can be completed much sooner than by conventional methods. In some embodiments, the installation is completed in two days. In further embodiments, the installation is completed in less than 72 hours. In yet further embodiments, the installation is completed in less than 48 hours or in less than 24 hours.
A thick coat ( 3/16 inch; about 0.5 cm) is representative of various applications, e.g., 1st or 2nd coat over corner reinforcement trim; 1st or 2nd coat over panel/wall offsets; 1st or 2nd coat over square edge butt joints; and 2nd fill coat over tapered edge joints. As seen in
The following examples further illustrate the invention but, of course, should not be construed as in any way limiting its scope.
This example sets forth three sample formulations (1A, 1B, and 1C) illustrating joint compound in accordance with embodiments of the invention.
As an illustrative method of preparation, all of the liquid ingredients were added to a Hobart Model N50 mixer. In this respect, it is to be noted that the functional filler (Scotchlite K1) and rheological polymer (Cellosize DSC) were the only dry materials with the remainder considered to be in liquid form for purposes of addition to the mixer. Since the functional filler was in bulk form and the rheological polymer was in a small quantity, the rheological polymer was added to the functional filler, and the combined dry material was added to the mixer with the liquids already included. The resulting composition was mixed for approximately two minutes until uniform.
However, it will be understood that the formulations can be prepared in any suitable manner. For example, the composition can be prepared on a plant scale in horizontal shafted mixer with helical blade configuration or the like to promote suitable mixing dynamics as will be understood by one of ordinary skill in the art.
Formulation 1A is set forth in Table 1 below. It will be understood “added water” refers to additional water not already present in any of the ingredients (e.g., RHOPLEX is in the form of a 47/53 solids/water emulsion by weight).
Formulation 1B is set forth in Table 2 below.
Formulation 1C is set forth in Table 3 below.
The formulations set forth in Table 1 include relatively low amounts of water and result in low shrinkage levels while also exhibiting good compressive strength and flexural strength. They can readily be applied with fewer coats than applied in conventional systems (e.g., desirably in a one-coat application system) to seams, trim, and fasteners in wall assemblies in accordance with some embodiments of the invention. As a result, Formulations 1A-1C permit efficient application without considerable delays requiring downtime as each separate coat dries. The Formulations 1A-1C also allow for easy application, requiring less skill on the part of the user, since the formulations can be applied closer to the plane of wall assemblies. The Formulations 1A-1C exhibited shrinkage from about zero to about 3% as measured in accordance with ASTM C474-05, Section 6. In addition, Formulations 1A-1C were crack resistant when measured in accordance with ASTM C474-05, Section 7.
This Example illustrates the superior strength properties exhibited by joint compound in accordance with embodiments of the invention as compared with two different conventional joint compounds.
A total of three specimens were tested for flexural strength. Each joint compound specimen was formed and dried into a strip having a length of 10 inches, a width of 2 inches (about 5 cm), and a thickness of 0.0625 inches (about 0.2 cm). Each specimen was placed on a table with its ends seated on 0.125 (⅛) inch (about 0.3 cm) thick spacers in order to demonstrate that, with the slightest displacement, the brittle nature and friability associated with representative samples of commercially available joint compound product formulations used in the industry. A down force of about 200 gm was applied to the center of each joint compound strip with a metal probe.
For comparative purposes, the first specimen, Formulation 2A, was a conventional joint compound commercially available as SHEETROCK® Brand Lightweight All Purpose Joint Compound from USG that has a density of approximately 14 lb/gal. The progression of the test is shown in
For further comparative purposes, the second specimen, Formulation 2B, was another conventional joint compound commercially available as SHEETROCK® Brand All Purpose Joint Compound from USG that has a density of approximately 8 lb/gal. The progression of the test is shown in
The third Formulation, 2C, was prepared in accordance with Formulation 1A, as set forth in Table 1, in accordance with embodiments of the invention Formulation 2C had a density of 3 lb/gal. The progression of the test is shown in
It will be understood that Formulation 2C imparted the most desirable finishing attributes of a drywall joint compound. For example, Formulation 2C did not shrink when dry. In addition, Formulation 2C remained flexible enough to resist cracking (as opposed to conventional brittle compounds shown in Formulations 2A and 2B) yet was sufficiently rigid to enable easy sanding and smoothing over the surface. Formulation 2C could also be easily painted.
This example sets forth five sample sets of formulations (2D-F, 3A-C, 4A-C, 5A-C, and 6A-C) illustrating a joint compound in accordance with embodiments of the invention.
It will be understood that the formulations can be prepared in any suitable manner, e.g., as described in Example 1. For example, the composition can be prepared on a plant scale in a horizontal shafted mixer with helical blade configuration or the like to promote suitable mixing dynamics as will be understood by one of ordinary skill in the art.
It will be understood “added water” refers to additional water not already present in any of the ingredients.
The Example below Illustrates the superior flexibility, crack resistance, and strength over commercially available joint compounds when used in the novel joint system and tested using ASTM C474.
Formulations 1A and 2E, as described above, were prepared. Also, a conventional weight all-purpose joint compound (Formulation AP) and a lightweight all purpose joint compound (Formulation LW) were used for comparative purposes. Formulation AP was SHEETROCK® Brand All-Purpose Joint Compound, and Formulation LW was SHEETROCK® Brand Lightweight All Purpose Joint Compound. Each sample was prepared in triplicate.
Each Formulation was prepared and tested according to the ASTM C474 conducted in the following manner. The joint compounds were applied over a gap created at the gypsum board seam with a waxed spacer. A synthetic joint tape was affixed over the gypsum panel joint. The samples were layered on top of the tape and conditioned for 24 hours at 70° F. (about 21° C.) and 50% relative humidity. The waxed spacers were removed, and the samples were mounted into test fixtures. The fixture was loaded into the Universal Test Machine (UTM).
Each joint system was challenged under a load at 0.4 inches/min. (about 1 cm/min.) at a constant rate of displacement until the sample failed. The load and the displacement were recorded twice—first when a visual first crack was observed, and second when the system failed.
The results of this Example illustrate that when the joint system was placed into tension, Formulations 1A and 2E both demonstrated a superior elongation and physical displacement before failure while Formulations AP and LW were brittle and did not impart similar performance under the same testing condition of the joint system of the present invention. Also, these commercially available joint compounds did not perform any better in the conventional joint systems.
When the joint system of the present invention was challenged under shear forces, the differences between the joint compounds of the present invention and conventional joint compounds became even more apparent. The joint compounds of this example exhibited high superior displacements and higher displacement ratios than the commercially available joint compounds. Thus, the joint compounds of the present invention demonstrated a high strength and crack resistance.
This Example illustrates the superior flexibility and elastomeric properties or flexibility/degree of embrittlement when used in the novel joint system and tested using ASTM C711.
Each Formulation was prepared and tested according to the ASTM C711 conducted in the following manner. Samples of Formulations 1A and 2E were prepared, and representative commercially available joint compounds Formulation AP-SHEETROCK® Brand All-Purpose Joint Compound and Formulation LW-SHEETROCK® Brand Lightweight All Purpose Joint Compound were used for comparative purposes. Each sample was prepared in triplicate.
A ⅛-inch (about 0.3 cm) thick strip of joint compound (2″×10″) (about 5 cm×about 25 cm) was laid over a bond breaker film, i.e., the joint compound does not adhere to film after drying. The samples were prepared in triplicate for each environmental condition. The samples were then dried under four different environmental test conditions for 24 hours. A second set of tests was conducted after conditioning for 28 days. The samples were removed from the bond breaker film and were subjected to a bending condition around a 1 inch (about 2.5 cm) diameter cylindrical mandrel to assess elastomeric and flexibility properties of the joint compounds. The samples were then visually graded on a 3 rating scale to determine the degree of elastomeric flexibility properties illustrated by ASTM C711.
It is to be noted that ASTM C711 published 2009 illustrates with photographs the differences between a satisfactory joint compound and unsatisfactory joint compounds when mounted and bent around a mandrel in accordance with the test. One provides a depiction of a satisfactory joint compound that would receive the pass rating due to a lack of cracking or any visible failure. Another depicts an unsatisfactory joint compound that would receive the Fail-A rating due to severe cracking. A third shows an unsatisfactory joint compound that would receive the Fail-B rating due to complete cracking and adhesive failure.
Table 9 demonstrates the results of the visual test after conditioning the samples in four different conditions of ASTM C711 for 24 hours. The specimens Formulations 1A and 2E performed significantly better than the conventional joint compounds represented by Formulations AP and LW. While Formulations 1A and 2E received a pass rating on each of the standard condition tests, Formulations AP and LW received a Fail-B rating.
Table 10 demonstrates the results of the visual test after conditioning the samples in four different conditions of ASTM C711 for 28 days. The specimens Formulations 1A and 2E performed significantly better than the conventional joint compounds represented by Formulations AP and LW. While Formulations 1A and 2E received a pass rating on each of the standard condition tests, Formulations AP and LW received a Fail-B rating.
The conventional joint compounds were so brittle under these testing conditions that they failed when even bent less than ⅛-inch deflection and could not be bent around cylindrical mandrel without catastrophic failure. The performance of the joint compound under these test conditions helps ensure the structural adequacy and service life of the joint compounds.
This Example Illustrates the superior properties of the joint compounds and joint system under the real world conditions that are representative of those encountered in service. The performance criteria based on data from these tests ensure structural adequacy of the joint compound and joint systems during their service life.
The joint system of the present invention and conventional joint system were tested using modified ASTM E72 in the following manner. The wall assembly joint system of the present invention was prepared using Formulations 1A and 2E compounds and compared against Formulations AP and LW. Samples of Formulations 1A and 2E were prepared, and representative commercially available joint compounds Formulation AP-SHEETROCK® Brand All-Purpose Joint Compound and Formulation LW-SHEETROCK® Brand Lightweight All Purpose Joint Compound were used for comparative purposes. Formulation AP represents a conventional weight all-purpose joint compound. Formulation LW represents a lightweight all purpose joint compound.
Formulations 1A and 2E were used to prepare a test under the Flat Joint Treatment (square edge/butt and tapered edge joints). In this system, the joint seams were taped using the synthetic joint reinforcement tape to affix the joint boards with an adhesive. A single coat of Formulation 1A or 2E was applied over the taped joint seams. The fasteners were prepared by applying one coat of the present invention joint compound Formulation 1A or 2E over the fasteners.
For comparison, the conventional joint systems are generally prepared by taping the all flat joint seams using paper joint reinforcement tape affixed to joint board with Formulation AP or LW joint compound. Three (3) separate coats of Formulation AP or LW joint compound were applied over the taped joint seams. The fasteners were prepared by three (3) separate coats of Formulation AP or LW joint compound applied over the fasteners.
During this test, plane of the board in these racking assembly systems was permitted to move only in the same plane as the face of the wall. The computer controlled hydraulic ram was programmed to run a sinusoidal waveform with amplitude of 0.025″ (about 0.06 cm) at a frequency 0.5 Hz (2 seconds per cycle) for a cycle count of 500 and hammer the upper left hand corner of the assembly. After the completion of this cycle, the amplitude was increased to 0.050″ (about 0.12 cm) for a cycle count of 500 cycles. After the second cycle was completed, again the amplitude was increased to 0.075″ (about 0.18 cm) for a cycle count of 500 cycles. This was repeated until the amplitude reached 0.400″ (about 1 cm). During this rigorous testing, the assembly was monitored continuously, and when a failure was observed, the cycle count was noted along with the location of the failure.
The results show a significant advantage of the elastic membrane effect of Formulations 1A and 2E. Even in areas where the fasteners had failed in the wall assembly, the joint compounds had not been breached or punctured. Whereas in the comparative conventional system prepared by conventional joint compounds, e.g., Formulations AP and LW, a brittle fractured effect was observed including loss of bond over the fasteners.
This Example illustrates the superior drying properties of the joint system of the present invention.
As discussed in the specification, the existing joint compounds require three separate coats to be applied to fasteners as well as multiple coats applied to flat seams between boards in the same plane. Each coat must separately dry before applying a new coat. While, the existing coat does not need to dry completely, it is found that about 75% of the water content must evaporate from the compound before the coat becomes firm enough to receive a second layer. This creates a significant period of downtime during which the other construction trades ordinarily cannot work inside the building while the wall finishing occurs.
On the other hand, the joint compounds of the present invention only require a single coat over the seam to provide a uniform aesthetic appearance. In case a second layer is required to account for imperfect workmanship and the like, the joint compounds of the present invention become firm enough to receive the second coat when about 60% of the water evaporates from the compound.
Samples of Formulations 1A, 2E, 3A, and 4B were prepared. Also a conventional weight all-purpose joint compound (Formulation AP) as well as a lightweight all purpose joint compound (Formulation LW) were used for comparative purposes. Formulation AP was SHEETROCK® Brand All-Purpose Joint Compound, and Formulation LW was SHEETROCK® Brand Lightweight All Purpose Joint Compound.
A thick coat ( 3/16 inch; about 0.5 cm) is representative of various applications, e.g., 1st or 2nd coat over corner reinforcement trim; 1st or 2nd coat over panel/wall offsets; 1st or 2nd coat over square edge butt joints; and 2nd fill coat over tapered edge joints.
As seen in
As seen in
As seen in
A thin coat ( 1/16 inch; about 0.2 cm) is representative of various applications, e.g., 1st or 2nd coat over inside corner finishing; 1st, 2nd, or 3rd finishing coat over flat joints; 3rd coat over square edge butt joints; and 1st, 2nd, or 3rd coat over fasteners.
As seen in
As seen in
As seen in
Thus, this Example shows that the joint compounds of the present invention had a faster drying profile in each of the different test environment than the conventional joint compound.
The use of the terms “a” and “an” and “the” and “at least one” and similar referents in the context of describing the invention (especially in the context of the following claims) are to be construed to cover both the singular and the plural unless otherwise indicated herein or clearly contradicted by context. The use of the term “at least one” followed by a list of one or more items (for example, “at least one of A and B”) is to be construed to mean one item selected from the listed items (A or B) or any combination of two or more of the listed items (A and B) unless otherwise indicated herein or clearly contradicted by context. The terms “comprising,” “having,” “including,” and “containing” are to be construed as open-ended terms (i.e., meaning “including, but not limited to,”) unless otherwise noted. Recitation of ranges of values herein are merely intended to serve as a shorthand method of referring individually to each separate value falling within the range, unless otherwise indicated herein, and each separate value is incorporated into the specification as if it were individually recited herein. All methods described herein can be performed in any suitable order unless otherwise indicated herein or otherwise clearly contradicted by context. The use of any and all examples, or exemplary language (e.g., “such as”) provided herein, is intended merely to better illuminate the invention and does not pose a limitation on the scope of the invention unless otherwise claimed. No language in the specification should be construed as indicating any non-claimed element as essential to the practice of the invention.
Preferred embodiments of this invention are described herein, including the best mode known to the inventors for carrying out the invention. Variations of those preferred embodiments may become apparent to those of ordinary skill in the art upon reading the foregoing description. The inventors expect skilled artisans to employ such variations as appropriate, and the inventors intend for the invention to be practiced otherwise than as specifically described herein. Accordingly, this invention includes all modifications and equivalents of the subject matter recited in the claims appended hereto as permitted by applicable law. Moreover, any combination of the above-described elements in all possible variations thereof is encompassed by the invention unless otherwise indicated herein or otherwise clearly contradicted by context.
This patent application is a continuation-in-part patent application of U.S. patent application Ser. No. 13/842,342, filed Mar. 15, 2013, which claims the benefit of U.S. Provisional Patent Application No. 61/705,551, filed Sep. 25, 2012. All of the preceding patent applications are incorporated herein by reference in their entireties.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4587173 | Lat et al. | May 1986 | A |
| 4657594 | Struss | Apr 1987 | A |
| 4686253 | Struss et al. | Aug 1987 | A |
| 4885203 | Wakat | Dec 1989 | A |
| 5277712 | McInnis | Jan 1994 | A |
| 5746822 | Espinoza et al. | May 1998 | A |
| 6238476 | Sprinkle | May 2001 | B1 |
| 6295776 | Kunz et al. | Oct 2001 | B1 |
| 6461691 | Taylor et al. | Oct 2002 | B1 |
| 6476099 | Cimaglio et al. | Nov 2002 | B1 |
| 6531528 | Kurp | Mar 2003 | B1 |
| 6545066 | Immordino, Jr. et al. | Apr 2003 | B1 |
| 6722092 | Kunz et al. | Apr 2004 | B2 |
| 6858260 | Taylor et al. | Feb 2005 | B2 |
| 6884830 | Hornaman | Apr 2005 | B1 |
| 7314898 | Downing, Jr. et al. | Jan 2008 | B2 |
| 7513963 | Frank et al. | Apr 2009 | B2 |
| 8642346 | Immordino, Jr. et al. | Feb 2014 | B2 |
| 8691046 | Jorgenson et al. | Apr 2014 | B2 |
| 8931230 | Negri et al. | Jan 2015 | B2 |
| 20020073638 | Kunz et al. | Jun 2002 | A1 |
| 20020129744 | Immordino, Jr. et al. | Sep 2002 | A1 |
| 20030089058 | Kunz et al. | May 2003 | A1 |
| 20030136072 | Peng | Jul 2003 | A1 |
| 20040182287 | Ayambem | Sep 2004 | A1 |
| 20050235878 | Podlas | Oct 2005 | A1 |
| 20060159908 | Houck et al. | Jul 2006 | A1 |
| 20080141909 | Immordino et al. | Jun 2008 | A1 |
| 20080245026 | Hamilton | Oct 2008 | A1 |
| 20100175590 | Stevens et al. | Jul 2010 | A1 |
| 20100294430 | Hyman et al. | Nov 2010 | A1 |
| 20120031555 | Thompson et al. | Feb 2012 | A1 |
| 20130143980 | Fasula et al. | Jun 2013 | A1 |
| 20130156961 | Heulings, IV et al. | Jun 2013 | A1 |
| 20140083035 | Negri et al. | Mar 2014 | A1 |
| 20140083038 | Negri et al. | Mar 2014 | A1 |
| 20140100309 | Rosenthal et al. | Apr 2014 | A1 |
| 20150007519 | Negri et al. | Jan 2015 | A1 |
| 20150083303 | Negri et al. | Mar 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 60-223848 | Nov 1985 | JP |
| WO 03040243 | May 2003 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20150007519 A1 | Jan 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61705551 | Sep 2012 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13842342 | Mar 2013 | US |
| Child | 14492905 | US |