Patent Application
20050048261
The present invention relates to a label for application to a housing of appliances, etc. The present invention further relates to a ventilation housing to which the label has been applied.
There are cases where the housings of appliances such as automotive electrical equipments, e.g., ECUs (electronic control units), lamps, motors, various sensors, and pressure switches, cell phones, cameras, electric razors, electric toothbrushes, and outdoor lamps have labels applied thereto which bear information about the appliance housings. For example, since an exceedingly large number of parts are handled in producing motor vehicles, each part has a label applied thereto which bears a code (e.g., a bar code or two-dimensional code) containing information about the type number, kind of the car in which the part is to be used, specification of the car, etc. The parts are managed based on such information (see, for example, JP-A-2002-40943).
On the other hand, those appliance housings have a vent filter attached thereto. These vent filters perform various functions according to the kinds of the housings. For example, the vent filter of an appliance housing not only prevents water or dust particles from coming into the housing, but also functions to transmit sound, release a gas generated in the housing, and diminish pressure changes in the housing due to temperature fluctuations.
However, the production of ventilation housings heretofore in use has been costly because the production process includes the steps of preparing a label and a vent filter as separate members and attaching these to a housing.
The present invention has been made in view of the above.
One object of the present invention is to provide a label for application to a housing of appliances, etc.
Another object of the present invention is to provide a ventilation housing to which the label has been applied.
The label according to the present invention comprises an ink-receiving layer and a pressure-sensitive adhesive layer for applying the ink-receiving layer to an adherend, wherein the ink-receiving layer is an air-permeable porous material comprising at least one resin selected from polytetrafluoroethylenes (IPTFE) and polyolefins, and the label has, formed in at least the pressure-sensitive adhesive layer, an air passage hole which extends from one to the other side of the pressure-sensitive adhesive layer in the thickness direction and enables a gas which has permeated the ink-receiving layer to pass therethrough.
The ventilation housing according to the present invention comprises a housing having an opening and the label applied to the housing such that the air passage hole is connected to the opening of the housing.
According to the present invention, a label having a vent filter function and a ventilation housing having a reduced cost can be provided.
One embodiment of the label of the present invention will be explained by reference to the drawings.
Since the label 1 also functions as a vent filter as described above, there is no need of separately producing a label and a vent filter in producing a ventilation housing, and the operation for attaching a label and a vent filter to a housing can be simplified. As a result, the cost of the ventilation housing can be reduced.
When information is imparted to the ink-receiving layer 2 by printing with, e.g., an ink, the ink infiltrates into pores and is fixed. The information printed with an ink hence has excellent wearing resistance. The at least one resin selected from PTFE and polyolefins can be easily made to have porosity with satisfactory precision. The resin can hence realize an ink-receiving layer 2 which has pores having a regulated pore diameter so as to prevent ink separation and which has excellent air permeation stability.
In particular, PTFE can be easily made microporous and can hence realize an ink-receiving layer 2 (porous PTFE) which, even when small in area, has high air permeability and is highly effective in inhibiting water or dust particles from coming into the housing. PTFE is also preferred in its high heat resistance.
On the other hand, polyolefins are preferred in that they are inexpensive and easy to recycle. Examples of monomers for the polyolefins include ethylene, propylene, 4-methylpentene-1, and 1-butene. A polyolefin obtained by the homopolymerization of one of such monomers or by copolymerizing two or more of these can be used in the ink-receiving layer 2. The ink-receiving layer 2 may be made of a blend of two or more of such polyolefins, or may have a multilayer structure in which each layer is made of one resin selected from those polyolefins. Especially preferred of those polyolefins is ultrahigh-molecular polyethylene having a viscosity-average molecular weight of 300,000-10,000,000, preferably 500,000-9,000,000, which has high strength and is excellent in handleability and heat resistance.
The average pore diameter of the ink-receiving layer 2 is generally 100 μm or smaller, and preferably 0.5-60 μm, because too large pore diameters thereof result in a decrease in film strength and a decrease in waterproofing and dust-proofing properties. Further, from the standpoints of clearness of printed information and ink infiltration, the average pore diameter of the ink-receiving layer 2 preferably is within that range.
The thickness of the ink-receiving layer 2 is generally preferably 5 μm or larger because too small thicknesses thereof result in reduced strength and hence in difficulties in processing.
That side of the ink-receiving layer 2, opposite the pressure-sensitive adhesive layer 3 is preferably subjected to any of various treatments, such as corona discharge treatment or chemical etching treatment, so as to enhance ink infiltration.
It is preferred that information 5 be printed on the ink-receiving layer 2 in an area located outside the region to be permeated by a gas which has passed through the air passage hole 4 in the ink-receiving layer 2. This is intended to secure sufficient air permeability in the region to be permeated by a gas which has passed through the air passage hole 4 in the ink-receiving layer 2.
The contents of the information 5 are not particularly limited, and may be any of a bar code or two-dimensional code which is coded information about, e.g., article name, lot number, and type number, characters, figures, and the like.
Techniques for printing on the label 1 are not particularly limited. Examples the printing technique include thermal transfer printing, ink-jet printing, and laser printing. Thermal transfer inks for thermal transfer printing can use, for example, commercial thermal-transfer ink sheets of the resin type or wax type. An ink-receiving layer 2 on which information has been printed by any of these printing techniques may be heated with, e.g., a heated roll to thereby accelerate ink infiltration into the ink-receiving layer 2.
The air permeability of the region to be permeated by a gas which has passed through the air passage hole 4 in the ink-receiving layer 2 is determined after the area of the opening of the housing (area of the plane perpendicular to the gas permeation direction), kind of the housing to which the label is to be attached, etc. are taken into account. In general, however, the air permeability thereof is preferably 0.1-300 sec/100 ml. In the present invention, values of air permeability (Gurley air permeability) are found values obtained through a measurement in accordance with JIS P 8117.
The ink-receiving layer 2 can be produced by, for example, the following manner.
Where the ink-receiving layer 2 is porous PTFE layer, the first step is to preform a pasty mixture obtained by adding a liquid lubricant to a fine PTFE powder. The liquid lubricant is not particularly limited as long as it can wet the surface of the fine PTFE powder and be removed by extraction or heating. For example, hydrocarbons such as naphtha and white oil can be used. The amount of the liquid lubricant added is desirably about 5-50 parts by weight per 100 parts by weight of the fine PTFE powder. The preforming is conducted at such a pressure that the liquid lubricant is not squeezed out. Subsequently, the preform is formed into a sheet by extrusion and/or rolling. The sheet-form molding thus obtained is stretched at least uniaxially, whereby a porous PTFE sheet can be obtained. It is preferred to conduct the stretching after the liquid lubricant is removed. Conditions for the stretching can be suitably selected. Usually, the conditions include a temperature of 20-320° C. and a stretch ratio of 2-30 for each of the machine and transverse directions. The porous PTFE sheet obtained through stretching may be burned by heating to a temperature not lower than the melting point of the PTFE, whereby the strength of the porous PTFE sheet can be heightened.
Where the ink-receiving layer 2 is a porous layer comprising a polyolefin, this ink-receiving layer 2 can be produced by, for example, (1) a method which comprises molding a resin by melt extrusion and subjecting the molded resin to low-temperature stretching and then to high-temperature stretching (dry film-forming method), (2) a method which comprises mixing a resin with an extractable material, subjecting the mixture to treatments such as molding and stretching, and removing the extractable material by extraction with a solvent or the like (wet film-forming method), or (3) a method which comprises fusion-bonding particles of a resin to one another with pressing to form a porous block and cutting the block into a desired shape.
The material of the pressure-sensitive adhesive layer 3 can use a hot-melt adhesive, a pressure-sensitive adhesive, or the like. Examples of the hot-melt adhesive that can be used include the polyester, olefin, polyurethane, polyamide, and acrylic types. Examples of the pressure-sensitive adhesive that can be used include the acrylic, silicone, rubber-based, polyurethane, and vinyl ether types. These adhesives may be used alone or in combination of two or more thereof
The pressure-sensitive adhesive layer 3 can be formed by, for example, laminating with heating, extrusion coating, or another coating technique. Where the pressure-sensitive adhesive layer 3 is formed from a pressure-sensitive adhesive, the pressure-sensitive adhesive may directly be applied to the ink-receiving layer 2 to form the pressure-sensitive adhesive layer 3. Alternatively, the pressure-sensitive adhesive may be applied to a release sheet to form a pressure-sensitive adhesive layer and this adhesive layer may be applied to the ink-receiving layer 2 to form the pressure-sensitive adhesive layer 3.
As shown in
The air-permeable support layer 6 is not particularly limited in material, structure, and form. However, a porous material having higher air permeability than the ink-receiving layer 2 can, for example, be used as the air-permeable support layer 6. Examples of the porous material include porous ultrahigh-molecular polyethylene, nonwoven fabrics, woven fabrics, nets, meshes, sponges, foams, porous metals, and metallic meshes. In particular, nonwoven fabrics are preferred because they are satisfactory in workability, fusion bondability, etc.
Bonding between the ink-receiving layer 2 and the air-permeable support layer 6 can be conducted by, for example, a technique such as ultrasonic fusion bonding, vibrational fusion bonding, adhesive laminating with a pressure-sensitive adhesive, or thermal laminating. For example, in the case of bonding by thermal laminating, part of the air-permeable support layer 6 is melted by heating to bond the ink-receiving layer 2 to the air-permeable support layer 6. It is also possible to interpose a fusion-bonding agent such as a hot-melt powder to conduct bonding.
The edges of the air-permeable support layer 6 are preferably made nonporous. By making the edges of the air-permeable support layer 6 nonporous by fusion-bonding or another technique, dust particles or water can be inhibited from coming into the label through the edges of the air-permeable support layer 6. The dust-proofing and waterproofing properties of the label can hence be enhanced.
The label 1 preferably is one which includes an air-impermeable reinforcing layer 7 disposed between the ink-receiving layer 2 and the pressure-sensitive adhesive layer 3 and in which the air passage hole 4 extends from one to the other side of the air-impermeable reinforcing layer 7, as shown in
The air-impermeable reinforcing layer 7 is not particularly limited in material, structure, and form. However, a resin film, metal foil, or the like can, for example, be used as the air-impermeable reinforcing layer 7. Examples of the material of the resin film that can be used include polyolefins, vinyl resins, polyesters, polyurethanes, polyamides, and acrylic resins.
Methods of bonding the air-impermeable reinforcing layer 7 to a layer (the air-permeable support layer 6 in
The label 1 preferably includes a surface coat layer 13 formed on the ink-receiving layer 2 on the side opposite the pressure-sensitive adhesive layer 3, as shown in
The surface coat layer 13 may be one intended to give a color or improve heat resistance. When the surface coat layer 13 contains a pigment having a high color contrast with the ink to be used for printing, e.g., when the ink to be used for printing is black and the layer 13 contains a white pigment, then information can be clearly printed. When the surface coat layer 13 contains an antioxidant, the heat resistance of the label can be improved.
The surface coat layer 13 can be formed by preparing a coating fluid comprising an appropriate solvent and, dissolved or dispersed therein, an organic binder and at least one member selected from the inorganic powdery materials, pigments, and antioxidants, applying the coating fluid to the ink-receiving layer 2 on the side opposite the pressure-sensitive adhesive layer 3 by, e.g., gravure coating, and thermally curing the coating fluid applied. The organic binder is not particularly limited, and examples thereof include polyurethanes, polyesters, epoxy resins, and acrylic resins. It is preferred that the surface coat layer 13 be formed in an area located outside the region to be permeated by a gas which has passed through the air passage hole 4 in the ink-receiving layer 2, so as to secure sufficient air permeability in that region.
The label 1 preferably is applied to a releasable sheet material 12 as shown in
The present invention will be explained below in more detail by reference to the following Examples, but it should be understood that the invention is not construed as limiting thereto.
The hydraulic test and dust-proof test conducted in the following Examples are as follows.
Hydraulic Test
A ventilation housing was placed in a water-containing pressure vessel so that the label was located in the water at a depth of 5 cm. The ventilation housing in this state was allowed to stand for 5 minutes, and then visually examined for water penetration into the ventilation housing.
Dust-Proof Test
200 g of test dust No. 8 (Kanto loam, JIS Z 8901) and a ventilation housing were introduced into a vessel having a capacity of 10 liters. This vessel was rotated at a speed of 10 rpm for 10 minutes. Thereafter, the ventilation housing was taken out of the vessel and then visually examined for dust penetration into the ventilation housing.
The label 1 shown in
A given pattern (information) was printed on the ink-receiving layer 2 using a commercial thermal transfer printer and an ink sheet. The label 1 showed satisfactory printability.
On the other hand, poly(butylene terephthalate) (“CG7640” manufactured by Teijin Ltd.) was used to produce a housing 10 of the structure shown in
The label 1 was applied to this housing 10 so that the air passage hole 4 was connected to the opening 11. Thus, a ventilation housing was obtained. The ventilation housing obtained was subjected to the hydraulic test and the dust-proof test. As a result, no penetration of water or dust into the ventilation housing occurred.
A label was produced in the same manner as in Example 1, except that a porous ultrahigh-molecular polyethylene sheet (“Sunmap” manufactured by Nitto Denko Corp.; thickness: 200 μm; average pore diameter: 20 μm; Gurley air permeability: 0.5 sec/100 ml) was used as the ink-receiving layer. A pattern (information) was printed in the same manner as in Example 1. As a result, the label showed satisfactory printability. This label was applied to the housing produced in Example 1 to obtain a ventilation housing, which was subjected to the hydraulic test and the dust-proof test. As a result, no penetration of water or dust into the ventilation housing occurred.
A porous PTFE sheet (trade name: “Microtex (Temish) NTF 1131” manufactured by Nitto Denko Corp.; thickness: 80 μm; average pore diameter: 1 μm) and a nonwoven polyester fabric (thickness: 200 μm) were prepared for use as an ink-receiving layer and an air-permeable support layer, respectively. A multilayer structure having a through-hole was prepared in the same manner as in Example 1. The release sheet disposed on one side of the multilayer structure was stripped off, and the nonwoven polyester fabric was laminated to the PTFE film (air-impermeable reinforcing layer). The porous PTFE sheet was press-bonded to the nonwoven polyester fabric with heating at 260° C. Except these, a label was produced in the same manner as in Example 1. The Gurley air permeability of a layered structure (thickness: 200 μm) consisting of the porous PTFE sheet and the nonwoven polyester fabric was examined and was found to be 10 sec/100 ml. A pattern (information) was printed in the same manner as in Example 1. As a result, the label showed satisfactory printability. This label was applied to the housing produced in Example 1 to obtain a ventilation housing, which was subjected to the hydraulic test and the dust-proof test. As a result, no penetration of water or dust into the ventilation housing occurred.
As described above, the present invention can provide a label having a vent filter function and a ventilation housing having a reduced cost. The label is hence suitable for application to the housings of appliances, etc.
It should further be apparent to those skilled in the art that various changes in form and detail of the invention as shown and described above may be made. It is intended that such changes be included within the spirit and scope of the claims appended hereto.
This application is based on Japanese Patent Application No. 2003-301616 filed Aug. 26, 2003, the disclosure of which is incorporated herein by reference in its entirety.