Patent Application
20060292328
1. Field of the Invention
The invention relates to a laminate material web having elastic and non-elastic regions, which has non-woven fabric on both surfaces. In between these surface there are sections of film strips of an elastic film. One surface is present in the form of a planar non-woven fabric layer, and the non-woven fabric layer, between the film strips, is connected with non-woven fabric that is disposed on the opposite surface of the laminate material web. The invention also relates to a method for producing the laminate material web. Sections of such a laminate material web are suitable, for example, for the production of hygiene products, on which they can be used as elastic end regions or elastic closure strips.
2. The Prior Art
A laminate material web and a method for its production is described in German Patent NO. DE 102 02 333 A1. This patent describes a procedure where thermoplastic elastomer is introduced between two non-woven fabric webs in the melted, viscous state, in the form of strips. The non-woven fabric webs are glued together over the area between the strips of the thermoplastic elastomer. The laminate material web is elastic in the region of the film strips, in the crosswise direction, and non-elastic between the film strips, where the non-woven fabric webs have been glued together over their area. With this known method, the extrusion of the thermoplastic elastomer must be coordinated with the lamination procedure, and the width of the elastic film strips is predetermined by the use of special extrusion dies. The material of the non-woven fabric webs must be selected so that high tear strength and great elasticity can be achieved.
It is therefore an object of the invention to provide a laminate material web, as well as a method for its production, which has an improved tear resistance, at greater elasticity, and is also flexible to produce.
This task is accomplished, according to the invention by providing a film strip glued to a non-woven fabric layer, to form a laminate strip. Several laminate strips are glued to a planar non-woven fabric layer on their film side. A non-woven fabric is connected with the planar non-woven fabric layer between the laminate strips. This non-woven fabric is present in the form of non-woven fabric strips that run parallel to the laminate strips and overlap the non-woven fabric layer of the laminate strips in edge regions of the laminate strips. The laminate material web according to the invention is elastic in the regions of the laminate strips, crosswise to their longitudinal direction, and non-elastic between the laminate strips. The elastic properties and the tear strength of the laminate material web can be changed, in targeted manner, both by means of the structure of the laminate strips and by means of the structure of the non-woven fabric strips.
Preferably, the non-woven fabric strips between the laminate strips are glued to the planar non-woven fabric layer over their entire area. However, the invention also comprises other methods of connection, such as a connection by means of ultrasound bonding or thermal bonding, for example.
The film strip of a laminate strip preferably consists of a mono-film of a thermoplastic elastomer. In particular, film strips of a polymer from the group of styrene-butadiene-styrene copolymers (SBS), styrene-isoprene-styrene block copolymers (SIS), styrene-ethene/butene-styrene copolymers (SEBS), elastic polyethylene copolymers, elastic polypropylene copolymers, elastic polyurethane copolymers, elastic polyamide copolymers, or a mixture of these polymers are suitable. Other polymers could also be used. In addition to the use of mono-films, co-extruded films can also be used, whereby co-extruded films having several identical layers are particularly preferred. Film strips having a thickness between 5 and 150 μm, preferably more than 10 μm and less than 130 μm, are particularly preferred.
The laminate strips consisting of an elastic film and a non-woven fabric laminated onto it are a pre-product that can be processed from a roll. The non-woven fabric of the laminate strips is glued to the elastic film. Hot-melt glues are particularly preferred. Particularly good elastic properties of the laminate material web can be achieved if the two layers of the laminate strip are connected with straight-line or wave-shaped strips of adhesive, which run along the direction of the laminate strip. In a preferred embodiment of the invention, the non-woven fabric of the laminate strips is an elastic-spunbonded fabric, but carded non-woven fabrics or non-elastic spunbonded fabrics made of polypropylene, polyethylene, polyamide, or polyethylene terephthalate can also be used. Elastic spunbonded fabrics on the basis of core/mantle multi-filaments having elastic core polymers such as elastic polypropylene copolymers or polyurethanes are particularly suitable, whereby polypropylene or polyethylene is used as the mantle polymer, for example. Aside from laminate strips in which the film strips are glued to the non-woven fabric layer, laminate strips in which the film strips are connected with the non-woven fabric layer without glue, by means of extrusion lamination or other means, can also be used within the scope of the invention. Although thermoplastic elastomers typically demonstrate great tackiness, the laminates used can be rolled onto rolls, stored, transported, and processed, as a pre-product, since the laminate is effectively prevented from sticking together by means of the non-woven fabric layer, and the tensile strength of the laminate is increased.
The planar non-woven fabric layer typically has a weight per unit area of between 5 g/m2 and 50 g/m2, preferably between 20 g/m2 and 40 g/m2. Preferably, a carded fiber non-woven fabric is used. Aside from carded fiber non-woven fabrics, spunbonded non-woven fabrics can also be used, for example, which typically have a weight per area unit between 10 g/m2 and 30 g/m2. The planar non-woven fabric layer consists, for example, of fibers made from polyethylene terephthalate, polyamide, polyethylene, preferably from polypropylene. Other materials could also be used.
The laminate strips are connected with the planar non-woven fabric layer by means of an adhesive, preferably a hot-melt glue, on their film side. The adhesive is preferably present in the form of straight-line or wave-shaped strips of adhesive that run along the direction of the laminate strips. Between the laminate strips, the non-woven fabric layer is connected with non-woven fabric strips. In a preferred embodiment of the invention, the adhesive is applied to the planar non-woven fabric layer at a weight per area unit between 2 g/m2 and 20 g/m2, preferably between 5 g/m2 and 10 g/m2, before the non-woven fabric layer is connected with the laminate strips and the non-woven fabric strips. Non-woven fabric strips made of a light-weight spunbonded non-woven fabric having a weight per area unit between 10 g/m2 and 30 g/m2, preferably more than 10 g/m2 and less than 20 g/m2, are advantageous. For example, a spunbonded non-woven fabric made of polypropylene, having a great tear resistance, is suitable.
Alternatively, carded fiber non-woven fabrics made of polypropylene, polyethylene, polyamide, or polyethylene terephthalate can also be used. The edge regions, in which the non-woven fabric strips overlap the non-woven fabric layer of the laminate strips, can have a width of 2 to 7 mm, preferably more than 4 and less than 5 mm. It is practical if the non-woven fabric strips are firmly connected with the non-woven fabric layer of the laminate strips, for example by means of adhesive or by means of connecting them by means of ultrasound bonding. When adhesive is used, in a preferred embodiment of the invention, the non-woven fabric strips and the non-woven fabric layer of the laminate strips are not glued to one another in the edge regions, proceeding from the edge of the non-woven fabric strip, over a width of maximally 5 mm, preferably over a width between 1 and 4 mm. In the case of an alternative use of an ultrasound method, the connection preferably extends up to the edge of the non-woven fabric strip, thereby increasing the tear resistance of the connection.
In the method according to the invention, laminate strips that are spaced apart and run parallel, consisting of a film strip of an elastic film and a non-woven fabric layer, in each instance, are glued to a planar non-woven fabric layer at their film side. Non-woven fabric strips are applied to the planar non-woven fabric layer between the laminate strips, and the non-woven fabric strips overlap the non-woven fabric layer of the laminate strips in an edge region of the laminate strips.
In a preferred embodiment of the method according to the invention, a laminate of an elastic film, preferably an elastic, extruded mono-film made of a thermoplastic elastomer, and a non-woven fabric layer is drawn off from a roll and cut into laminate strips. It is practical if the film and the non-woven of the laminate are connected by means of adhesive applied in strips, with the strips of adhesive extending in the longitudinal direction of the laminate strips. In a preferred embodiment, an adhesive, for example a hot-melt glue, is applied to the non-woven fabric layer in the form of strips, in the regions in which the laminate strips are laminated on. The adhesive is preferably also applied to the regions between the laminated strips over the entire area. However, the invention is not limited to a connection by means of adhesive. Thus, the connection can also be produced in an ultrasound bonding unit or by other means.
The non-woven fabric strips, in turn, are preferably also provided with an adhesive, for example a hot-melt glue, that is applied, for example, in the form of two strips on the side of the non-woven fabric strips that is laminated onto the non-woven fabric layer and the edge regions of the laminate strips. The laminate strips and the non-woven fabric strips are applied to the non-woven fabric layer in such a manner that they overlap in an edge region having a width between 2 and 7 mm, preferably more than 4 mm and less than 5 mm. If the adhesive is applied to the non-woven fabric layers at a distance of maximally 5 mm, preferably between 1 and 4 mm relative to the edge of the non-woven fabric strips, it can be prevented that adhesive exits at the surface of the laminate material web during the lamination process. If, alternatively, the non-woven fabric strips are connected with the non-woven fabric layer by means of an ultrasound bonding station, the connection preferably extends all the way to the edge of the non-woven fabric strips. If the non-woven fabric strips are connected with the laminate strips and the planar non-woven fabric layer without the use of adhesive, by means of an ultrasound bonding station, contamination of the subsequent rollers will not occur in the case of a tear or a loss of the non-woven fabric strips during the production process.
In order to improve the elastic properties of the laminate material web, or to adapt it to certain requirements, the laminate material web can be over-stretched crosswise to the orientation of the laminate strips after lamination, preferably in a stretching roller arrangement.
Other objects and features of the present invention will become apparent from the following detailed description considered in connection with the accompanying drawings. It is to be understood, however, that the drawings are designed as an illustration only and not as a definition of the limits of the invention.
In the drawings, wherein similar reference characters denote similar elements throughout the several views:
Referring now in detail to the drawings, the components of the laminate material web 1 are shown in
The method according to the invention, for the production of a laminate material web 1, is shown schematically in
Accordingly, while only a few embodiments of the present invention have been shown and described, it is obvious that many changes and modifications may be made thereunto without departing from the spirit and scope of the invention.