The present invention relates to laminated fabrics and protective covers and, in particular, to laminated fabrics and protective covers that include post-industrial (“PI”) and/or post-consumer (“PC”) content and methods of making them.
Laminated and shrinkable protective covers have been widely used for industrial shipping and storage applications for more than twenty five years. Examples of such covers are discussed in U.S. Pat. Nos. 5,491,017, 5,623,812, 5,705,566, 5,712,008, 6,562,740 and 8,637,139.
Known laminated protective covers are often constructed from laminated fabric having layers made from multiple polymers. These polymers often have different melting temperatures (“Tm”), which may vary significantly from polymer to polymer. It is advantageous when recycling plastics to process materials that have similar properties, such as melting temperatures, together. This is one reason why recyclable plastic products typically include ASTM International Resin Identification Codes indicating the type of plastic from which the product is made. The current ASTM coding system is as follows:
Recycling facilities may only accept items for recycling that are made from particular materials, due to the equipment capabilities of the facility.
Laminated fabrics that are designed for use as protective covers are often constructed from a film, an adhesive material and a nonwoven material. The film often includes polyethylene (“PE”), including branched and/or linear PE polymers, such as low density polyethylene (“LDPE”) or its branched or unbranched copolymers, such as ethylene vinyl acrylate (“EVA”), ethylene methyl acrylate (“EMA”), ethylene butyl acrylate (“EBA”) or linear low density polyethylene (“LLDPE”). The film may or may not be shrinkable. The film often includes UV and antioxidant additives as well as pigments for color.
The adhesive used in these laminated fabrics are often hot melt adhesives designed for outdoor use, so they tend to include saturated block-co-polymers.
The nonwoven layer is typically the layer with the highest melting temperature polymer. In many instances, the nonwoven is a PET. Other polymers, such as nylons, are also used for the nonwoven layer.
Laminated fabrics and covers that have a film made from PE, such as, for example, LDPE (a Code 4 plastic), and a nonwoven layer made from PET (a Code 1 plastic) are often not accepted by recycling facilities because of the significantly different melting temperatures of these materials. For example, LDPE and its copolymers have a melting temperature range of about 85-110 degrees Celsius, whereas PET has a melting temperature as low as about 245 degrees Celsius. The presence of hot melt adhesive between the film layer and nonwoven layer adds another level of complexity to most recycling operations.
The present invention includes methods of recycling products, such as laminated fabrics and protective covers, that include plastic/polymer materials having significantly different melting temperatures, such as protective covers that include a film having a polyethylene polymer, such as, for example, LDPE, and a nonwoven layer having PET. In one embodiment of the invention, the melting temperature difference is greater than 100 degrees Celsius. In other embodiments, the melting temperature difference is between about 10% and about 225%. The processed recycled material can be used to produce other products, such as new protective covers. For example, according to one embodiment of the present invention, a method of recycling laminated fabrics and laminated fabric products and producing new laminated fabrics includes the steps of shredding the scrap or used laminated fabric, melt separating the polymers, pelletizing the melt separated polymers, extruding the pelletized material with at least one virgin material to form a film, and laminating the film to a nonwoven material to form a new laminated fabric. According to embodiments of the invention, the polymers do not have to be completely separated, either before or after pelletizing.
In one embodiment of the present invention, a method of protecting an object with a cover includes the steps of obtaining a laminated fabric including material from a recycled laminated fabric product, the recycled laminated fabric product having a first component having a melting point and a second component having a melting point different from the melting point of the first component, the laminated fabric further including (a) a film layer including at least some of the first component from the recycled laminated fabric product and at least one virgin polymer resin, (b) a nonwoven layer, and (c) an adhesive between the film layer and the nonwoven layer; forming the laminated fabric into a cover; and placing the cover over the object to be protected.
In one embodiment, the recycled laminated fabric product is heat shrinkable.
In another embodiment, the content of material from the recycled laminated fabric product is less than 90% by weight of the laminated fabric. In certain embodiments, the content of material from the recycled laminated fabric product is greater than 1% by weight of the laminated fabric.
In one embodiment, the first component of the recycled laminated fabric product is a polyethylene polymer.
In some embodiments, the second component of the recycled laminated fabric product is PET.
In other embodiments, the film layer includes at least some of the second component from the recycled laminated fabric product.
In another embodiment, the laminated fabric is heat sealable.
In one embodiment, the first component of the recycled laminated fabric product and the at least one virgin resin are the same material.
In certain embodiments, the nonwoven layer is constructed at least in part from recycled material.
In other embodiments, the nonwoven layer is constructed entirely from recycled material.
In one embodiment, forming the laminated fabric into a cover includes cutting the laminated fabric to a desired size. In other embodiments, forming the laminated fabric into a cover includes cutting the laminated fabric to a desired shape. In yet another embodiment, forming the laminated fabric into a cover includes forming the laminated fabric into a desired shape.
In some embodiments, the method further includes applying heat to the cover after the cover is placed over the item to be protected.
In one embodiment of the present invention, a method of protecting an object with a cover includes the steps of making a laminated fabric by a process that includes the steps of (a) obtaining an existing laminated fabric product, the existing laminated fabric product having a first component having a first melting point and a second component having a second melting point different from the melting point of the first component, (b) separating the first component of the existing laminated fabric product from the second component of the existing laminated fabric product, (c) forming the first component of the existing laminated fabric product into pellets, (d) providing at least one virgin polymer resin, (e) forming the pellets and the at least one virgin polymer resin into a film, (f) providing a nonwoven material, and (g) laminating the film to the nonwoven material; forming the laminated fabric into a cover; and placing the cover over the item to be protected.
In one embodiment, the step of separating the first component of the existing laminated fabric product from the second component of the existing laminated fabric product is performed by melt separation.
In another embodiment, the first component of the existing laminated fabric product and the at least one virgin polymer resin are the same material.
In some embodiments, the pellets and the at least one virgin polymer resin are extruded to form a cast film. In certain embodiments, the pellets and the at least one virgin polymer resin are extruded to form a blown film.
In one embodiment, the laminated fabric is heat shrinkable.
In another embodiment, the first component of the existing laminated fabric product is a polyethylene polymer.
In certain embodiments, the second component of the existing laminated fabric product is PET.
In some embodiments, the laminated fabric is heat sealable.
In one embodiment, the method further includes providing a second film and coextruding the film with the second film to form a multilayer film that is laminated to the nonwoven material.
In another embodiment, forming the laminated fabric into a cover includes cutting the laminated fabric to a desired size. In some embodiments, forming the laminated fabric into a cover includes cutting the laminated fabric to a desired shape. In one embodiment, forming the laminated fabric into a cover includes forming the laminated fabric into a desired shape.
In another embodiment, the method further includes applying heat to the cover after the cover is placed over the item to be protected.
Other features of the present invention will be apparent from the following Detailed Description of Embodiments of the Invention and the accompanying drawings.
Certain embodiments of the invention described below are illustrated in the context of laminated fabrics including a film constructed at least in part from LDPE. However, it is to be understood that reference to LDPE is for purposes of example only. The invention is equally applicable to, and embodiments of the invention encompass, processing and manufacturing laminated fabrics and products that include laminated fabrics having films constructed in whole or in part from PE and/or one or more PE copolymers other than, instead of, or in addition to LDPE.
Referring to
In other embodiments of the invention, film 100 is coextruded with virgin film to form a multilayer film that can be laminated to nonwoven material 110 utilizing adhesive 140. For example, as shown in
In other embodiments of the invention, the layers of film 100 are coextruded with the layers of virgin film 180 to form multilayer film 170, which is then laminated to nonwoven material 110 in a single step process like that shown in
In one embodiment of the invention, the equipment and operating parameters that may be utilized for Step 2 above are indicated in the following table:
It has been found that use of methods according to the present invention permits the successful manufacture of laminated fabrics and protective covers even if there is not complete separation of the LDPE from the PET. For example, in one embodiment of the invention, pelletized material that included 10% PET content, less than 2% styrene-ethylene butylene-styrene (“SEBS”) hot melt adhesive and the remainder LDPE was able to be extruded and blown to produce a film that has acceptable physical properties for use in the production of protective covers. In one embodiment of the invention, up to 50% virgin LDPE resin is used in the film. Use of 20% recycled pelletized material in the film results in a final laminated fabric that includes about 15%-16% postindustrial/postconsumer plastic by weight. The percentage can be increased further if the nonwoven utilized to make the new laminated fabric is manufactured from recycled polymers as well. For example, nonwoven material 110 could be manufactured from recycled PET. Doing so would bring the total recycled content of the final laminated fabric to about 35% by weight.
Product by weight before and after recycling is described on the following table:
16%
The example above shows that by use of melt-separation and pelletizing, two different polymer systems can be recycled together and used to produce a film that can further be laminated to form laminated fabrics and cut and sewn into covers for shipping and storage applications. In the non-limiting example provided above, the recycled content is between 10% and 35% by weight.
In another embodiment of the invention, the nonwoven material utilized for the newly made laminated fabric is made from PLA polymers, which makes the laminated fabric partially biodegradable. Furthermore, because PLA can be produced from renewable plant-based resources (as opposed to fossil fuels) it can provide additional environmental benefits.
Tables 4-6 disclose and describe properties of a film (Formula 1) produced without the use of recycled materials according to the present invention and two films (Formulas 2-3) according to embodiments of the present invention produced according to methods of the present invention. In the embodiments disclosed and discussed below, the films were produced on a blown film line utilizing pellets 70 according to embodiments of the present invention that contain 88% LDPE/LLDPE and 12% PET, virgin EXCEED® 1012 LLDPE (available from Exxon Mobile Corporation), and a color and additive masterbatch.
Extruder and blown film line parameters for the above formulas are shown below:
These film had the following properties:
Although the present invention has been described in detail, the same is for purposes of illustration only and is not to be taken as a limitation on the scope of the invention. Numerous modifications can be made to the embodiments described above without departing from the scope of the invention. For example, product containing polymers and materials other than those specifically discussed can be processed according to methods of the present invention to produce laminated fabrics according to embodiments of the present invention. New products other than protective coves can be produced from laminated fabrics according to the present invention. Other variations are also within the scope of the present invention.
This application is a divisional application claiming priority from U.S. patent application Ser. No. 17/190,805, filed Mar. 3, 2021, now U.S. Pat. No. 11,230,083, which is a divisional application claiming priority from U.S. patent application Ser. No. 17/074,766, filed Oct. 20, 2020, now U.S. Pat. No. 11,155,058 which claims priority from U.S. Provisional Patent Application Ser. No. 62/923,739, filed Oct. 21, 2019. The disclosures of all of the above-referenced applications are hereby incorporated in their entireties by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5077556 | Aisslinger | Dec 1991 | A |
| 5491017 | Todt | Feb 1996 | A |
| 5565158 | Sullivan et al. | Oct 1996 | A |
| 5623812 | Todt | Apr 1997 | A |
| 5662978 | Brown | Sep 1997 | A |
| 5705566 | Todt | Jan 1998 | A |
| 5712008 | Todt | Jan 1998 | A |
| 5840773 | Booij | Nov 1998 | A |
| 5888616 | Ang | Mar 1999 | A |
| 6045900 | Haffner | Apr 2000 | A |
| 6444595 | Elkouh et al. | Sep 2002 | B1 |
| 6562740 | Todt | May 2003 | B1 |
| 6638589 | Jarvenkyla | Oct 2003 | B1 |
| 6794317 | Elkouh et al. | Sep 2004 | B2 |
| 6875712 | Todt | Apr 2005 | B2 |
| 7183230 | Elkouh et al. | Feb 2007 | B2 |
| 7344765 | Hayakawa et al. | Mar 2008 | B2 |
| 8012572 | Ramli et al. | Sep 2011 | B2 |
| 8465684 | Tsai | Jun 2013 | B1 |
| 8637139 | Todt et al. | Jan 2014 | B2 |
| 8828487 | Todt et al. | Sep 2014 | B2 |
| 8871319 | Stanley et al. | Oct 2014 | B2 |
| 8883284 | Todt et al. | Nov 2014 | B2 |
| 11230083 | Ozol | Jan 2022 | B2 |
| 20030218367 | Parker | Nov 2003 | A1 |
| 20130040092 | Moore | Feb 2013 | A1 |
| 20150018461 | Todt | Jan 2015 | A1 |
| 20150123304 | Ashraf et al. | May 2015 | A1 |
| 20210023815 | Venugopal | Jan 2021 | A1 |
| Number | Date | Country |
|---|---|---|
| 2008056123 | May 2008 | WO |
| Entry |
|---|
| Wikipedia page for “polyethylene terephthalate”, 15 pages, accessed Dec. 31, 2022. |
| Wikipedia page for “polyethylene”, 11 pages, accessed Dec. 31, 2022. |
| CHEMbaseNET (Polyethylene, Polyethylene Terephthalate) (Year: 2023). |
| Number | Date | Country | |
|---|---|---|---|
| 20220111614 A1 | Apr 2022 | US |
| Number | Date | Country | |
|---|---|---|---|
| 62923739 | Oct 2019 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17190805 | Mar 2021 | US |
| Child | 17555576 | US | |
| Parent | 17074766 | Oct 2020 | US |
| Child | 17190805 | US |