20200329920
The present invention relates to shower curtains having water repellency and mildew resistance.
The shower curtain industry has struggled and failed to produce a fabric liner that combines the needed water repellency and passes standard testing for mildew resistance. Conventionally, the problem faced by the industry was that two different chemical treatments previously used to accomplish a water impermeable and mildew resistant fabric fought each other. Accordingly, a need exists for shower curtains having an improved combination of water repellency and mildew resistance.
The present invention provides laminated shower curtains having an antimicrobial pre-treated fabric layer comprising a first antimicrobial agent, and an antimicrobial liquid impermeable film layer bonded to the antimicrobial pre-treated fabric layer comprising a polymeric material and a second antimicrobial agent. The antimicrobial pre-treated fabric layer and the antimicrobial pre-treated fabric layer of the laminated shower curtains may be individually produced before being bonded together.
An aspect of the present invention is to provide a laminated shower curtain comprising an antimicrobial pre-treated fabric layer comprising a first antimicrobial agent, and an antimicrobial liquid impermeable film layer bonded to and in contact with the antimicrobial pre-treated fabric layer comprising a polymeric material and a second antimicrobial agent, wherein the antimicrobial liquid impermeable film layer comprises a composite layer including a polymeric matrix with molecules or particles of the second antimicrobial agent dispersed therein, and the laminated shower curtain is impermeable to water vapor.
Another aspect of the present invention is to provide a method of making a laminated water vapor-impermeable shower curtain material comprising laminating an antimicrobial pre-treated fabric layer comprising a first antimicrobial agent with an antimicrobial liquid impermeable film layer comprising a polymeric material and a second antimicrobial agent to produce a laminated shower curtain material that is impermeable to water vapor, wherein the antimicrobial liquid impermeable film layer is produced by co-extruding a molten mixture of the polymer material and the second antimicrobial agent to thereby form a polymeric matrix with molecules or particles of the second antimicrobial agent dispersed therein.
These and other aspects of the present invention will be more apparent from the following description.
The present invention provides laminated shower curtains that combine water repellency and mildew resistance. Instead of obtaining water repellency of a fabric layer with chemicals, the laminated shower curtains of the present invention comprise a fabric layer laminated with a liquid impermeable film layer. Before lamination, the fabric layer of the laminated shower curtain is pre-treated with an antimicrobial agent. The liquid impermeable film layer may include a co-extrusion of polymer material and a second antimicrobial agent.
As used herein, the term “shower curtain” includes curtains for use with a shower, a bath, or the like. The term “curtain” may refer to a single curtain that is used by itself in a shower or bath, or is used as a liner for an additional curtain.
As used herein, the term “antimicrobial” means substances, such as bactericidal, fungicidal, antiviral and the like, that kill or inhibit the growth of microorganisms.
As used herein, the term “liquid impermeable” means impermeable or substantially impermeable to liquids, such as water. For example, a liquid impermeable film layer of the present invention prevents liquid water from flowing through the thickness of the film.
As used herein, the term “liquid permeable” means permeable or substantially permeable to liquids, such as water. For example, a liquid permeable fabric layer of the present invention, prior to lamination with the film layer, allows at least some liquid water to flow through the thickness of the fabric.
As used herein, the term “gas impermeable” means impermeable or substantially impermeable to gas or vapor, such as water vapor, air and the like. For example, a gas impermeable film layer of the present invention prevents water vapor and/or air from passing through the thickness of the film.
As used herein, the term “gas permeable” means permeable or substantially permeable to gas or vapor, such as water vapor, air and the like. For example, a gas permeable fabric layer of the present invention, prior to lamination with the film layer, allows at least some passage of water vapor and/or air through the thickness of the fabric.
The laminated shower curtain 10 may have any suitable dimensions and features, e.g., as found in conventional standard shower curtains. The dimensions of the laminated shower curtain 10 may be varied depending on the size of the shower or bath. For example, the width of the laminated shower curtain 10 may typically range from 3 to 7 feet, or from 4 to 6.5 feet. The height of the laminated shower curtain 10 may typically range from 5 to 9 feet, or from 6 to 8 feet. The laminated shower curtain 10 may comprise a top edge including standard openings or attachment points for conventional shower curtain rings or hooks (not shown). The top, bottom and/or side edges of the laminated shower curtain 10 may include standard edge treatments as found in conventional shower curtains, such as hemming and the like (not shown).
In an embodiment of the invention, the fabric of the antimicrobial pre-treated fabric layer 12 may have a material weight ranging from 10 to 500 grams per square meter (gsm), for example, from 20 to 200 gsm, or from 50 to 100 gsm. In a particular embodiment, the fabric of the antimicrobial pre-treated fabric layer 12 may have a material weight of 70 gsm. As shown in
In accordance with an embodiment of the present invention, the antimicrobial pre-treated fabric layer 12 may be made from a liquid permeable and gas permeable fabric material, e.g., the fabric may be permeable to liquid water and to water vapor and/or air. The antimicrobial pre-treated fabric layer 12 may be made from knitted or woven fabric material. In accordance with an embodiment of the invention, the antimicrobial pre-treated fabric layer 12 may comprise any suitable synthetic or natural material, such as polyester, nylon, cotton, or the like. In a particular embodiment, the fabric material of the antimicrobial pre-treated fabric layer 12 may comprise polyester.
The first antimicrobial agent of the antimicrobial pre-treated fabric layer 12 may comprise agents that kill microorganisms or inhibit their growth. For example, the first antimicrobial agent may contain at least one metal such as silver, gold, platinum, palladium, iridium, zinc, copper, nickel, tin, titanium, zirconium, molybdenum, iron, antimony, bismuth and the like, or mixtures of these metals with the same or other metals. In certain embodiments, the first antimicrobial agent can comprise at least one such metal in combination with at least one of oxygen, nitrogen, carbon, boron, sulfur, a halogen (e.g., fluorine, chlorine, bromine, iodine) and/or hydrogen. In certain embodiments, the first antimicrobial agent may comprise one or more metal oxide, carbide, hydroxide, nitride, nitrate, chloride, boride, sulfide, sulfate, halide, hydride, or metal salts containing metals as described above. In certain embodiments, the first antimicrobial agent may comprise metal-containing compounds, such as coordination complexes or metal complexes, metal pyrithiones, metal trialkyls, organometallics, microcomposites and the like. The metal(s) components of such compounds may be selected from those listed above.
Examples of suitable coordination complexes or metal complexes may include dehydroabietyl amine, 8-hydroxyquinolinium 2-ethylhexoate, copper naphthenate, copper oleate, silver pyrithione, gold pyrithione, zinc pyrithione, copper pyrithione, palladium (II) complexes, silver acetate, silver (I) carbene, zinc ammonium carbonate, copper ammonium carbonate, zinc borate, and the like. Examples of suitable metal trialkyls may include tributyl tin oxide, tributyl tin acetate, and the like. Examples of suitable organometallics may include copper 8-quinolinolate, and the like. Examples of suitable microcomposites may include silver chloride nanoparticles attached to titanium dioxide as a carrier material and the like.
In accordance with certain embodiments, the first antimicrobial agent may comprise organic compounds such as phenolics, polybiguanides, quarternary ammonium compounds, isothiazolinones, and N-halamine compounds. Examples of suitable phenolics may include triclosan, dalbergin (I) and the like. Examples of suitable polybiguanides may include polyhexamethylene biguanides and the like. Examples of suitable quarternary ammonium compounds may include domiphen bromid, 3-(trihydroxysilyl) propyldimethyl-octadecyl ammonium chloride, benzalkonium chloride, methylbenzethonium chloride, cetalkonium chloride, cetylpyridinium chloride, cetrimide, dofanium chloride, cetrimonium, benzethonium chloride, tetraethylammonium bromide, didecyldimethylammonium chloride, and the like. Examples of suitable isothiazolinones may include methylisothiazolinone, methylchloroisothiazolinone, benzisothiazolinone, octylisothiazolinone, dichlorooctyli sothiazolinone, butylbenzisothiazolinone, 5-chloro-2-methyl-4-isothiazolin-3-one, 2-Butyl-1,2-benzisothiazolin-3-one, 2-methyl-4-isothiazolin-3-one, and the like. Examples of N-halamine compounds may include hydantoins, isocyanurates,1,3-Dichloro-2,2,5,5-tetramethyl-4-imidazolidinone, 1,3-Dibromo-2,2,5,5-tetramethyl-4-imidazolidinone, I-Bromo-3-chloro-2,2,5,5-tetramethyl-4-imidazolidinone, and the like.
In accordance with certain embodiments, the amount of the first antimicrobial agent contained in or on the antimicrobial pre-treated fabric layer 12 may typically be from 0.1 to 30 weight percent based on the total weight of the fabric of the antimicrobial pre-treated fabric layer 12 and the dry weight of the first antimicrobial agent. For example, the first antimicrobial agent may comprise from 1 to 20 weight percent, or from 2 to 10 weight percent.
In accordance with an embodiment of the present invention, the antimicrobial liquid impermeable film layer 14 may be both a liquid impermeable and a gas impermeable polymeric material, e.g., the film layer 14 is substantially impermeable to liquid water and to water vapor. The antimicrobial liquid impermeable film layer 14 may comprise a continuous film of any suitable polymeric material, such as polyethylene, polypropylene, polyvinyl chloride, polystyrene, nylon, polycarbonate, polytetrafluoroethylene, polyurethane, and the like. In a particular embodiment, the polymeric material of the antimicrobial liquid impermeable film layer 14 may be a polyethylene material.
In an embodiment, the antimicrobial liquid impermeable film layer 14 may have a thickness Tr ranging from 0.02 to 2 mm, for example, from 0.05 to 1 mm, or from 0.1 to 0.5 mm. In a particular embodiment, the antimicrobial liquid impermeable film layer 14 may have a thickness Tr of about 0.2 mm. In an embodiment of the present invention, the thickness TF of the antimicrobial pre-treated fabric layer 12 may be greater than the thickness Tr of the impermeable antimicrobial liquid impermeable film layer 14. In another embodiment, the thicknesses may be the same.
In accordance with an embodiment of the present invention, the antimicrobial liquid impermeable film layer 14 may comprise the second antimicrobial agent dispersed throughout a polymeric matrix of the antimicrobial liquid impermeable film layer 14. In accordance with an embodiment of the invention, the antimicrobial liquid impermeable film layer 14 may be coextruded to form a coextrusion. As used herein, the term “coextrusion”, when referring to the antimicrobial liquid impermeable film layer, means that the polymer and the second antimicrobial agent are extruded together into a film comprising a polymeric matrix and the second antimicrobial agent dispersed therein. The antimicrobial liquid impermeable film layer 14 may be a composite layer comprising a polymeric matrix with molecules or particles of the second antimicrobial agent dispersed therein. In accordance with certain embodiments, the second antimicrobial agent may be uniformly dispersed throughout the thickness of the antimicrobial liquid impermeable film layer 14. In other embodiments, the second antimicrobial agent may be non-uniformly dispersed, for example, there may be a greater concentration of the second antimicrobial agent on one or both of the exterior surfaces than in the center of the antimicrobial liquid impermeable film layer 14.
The second antimicrobial agent may comprise agents that kill microorganisms or inhibit their growth. For example, the second antimicrobial agent may contain at least one metal such as silver, gold, platinum, palladium, iridium, zinc, copper, nickel, tin, titanium, zirconium, molybdenum, iron, antimony, bismuth and the like, or mixtures of these metals with the same or other metals. In certain embodiments, the second antimicrobial agent can comprise at least one such metal in combination with at least one of oxygen, nitrogen, carbon, boron, sulfur, a halogen (e.g., fluorine, chlorine, bromine, iodine) and/or hydrogen. In certain embodiments, the second antimicrobial agent may comprise one or more metal oxide, carbide, hydroxide, nitride, nitrate, chloride, boride, sulfide, sulfate, halide, hydride, or metal salts containing metals as described above. In certain embodiments, the second antimicrobial agent may comprise metal-containing compounds, such as coordination complexes or metal complexes, metal pyrithiones, metal trialkyls, organometallics, microcomposites and the like. The metal(s) components of such compounds may be selected from those listed above.
Examples of suitable coordination complexes or metal complexes may include dehydroabietyl amine, 8-hydroxyquinolinium 2-ethylhexoate, copper naphthenate, copper oleate, silver pyrithione, gold pyrithione, zinc pyrithione, copper pyrithione, palladium (II) complexes, silver acetate, silver (I) carbene, zinc ammonium carbonate, copper ammonium carbonate, zinc borate, and the like. Examples of suitable metal trialkyls may include tributyl tin oxide, tributyl tin acetate, and the like. Examples of suitable organometallics may include copper 8-quinolinolate, and the like. Examples of suitable microcomposites may include silver chloride nanoparticles attached to titanium dioxide as a carrier material and the like.
In accordance with certain embodiments, the second antimicrobial agent may comprise organic compounds such as phenolics, polybiguanides, quarternary ammonium compounds, isothiazolinones, and N-halamine compounds. Examples of suitable phenolics may include triclosan, dalbergin (I) and the like. Examples of suitable polybiguanides include polyhexamethylene biguanides and the like. Examples of suitable quarternary ammonium compounds may include domiphen bromid, 3-(trihydroxysilyl) propyldimethyl-octadecyl ammonium chloride, benzalkonium chloride, methylbenzethonium chloride, cetalkonium chloride, cetylpyridinium chloride, cetrimide, dofanium chloride, cetrimonium, benzethonium chloride, tetraethylammonium bromide, didecyldimethylammonium chloride, and the like. Examples of suitable isothiazolinones may include methylisothiazolinone, methylchloroisothiazolinone, benzisothiazolinone, octylisothiazolinone, dichlorooctyli sothiazolinone, butylbenzisothiazolinone, 5-chloro-2-methyl-4-isothiazolin-3-one, 2-Butyl-1,2-benzisothiazolin-3-one, 2-methyl-4-isothiazolin-3-one, and the like. Examples of suitable N-halamine compounds may include hydantoins, isocyanurates,1,3-Dichloro-2,2,5,5-tetramethyl-4-imidazolidinone,1,3-Dibromo-2,2,5,5-tetramethyl-4-imidazolidinone, l-Bromo-3-chloro-2,2,5,5-tetramethyl-4-imidazolidinone, and the like.
In certain embodiments, the amount of the second antimicrobial agent contained in or on the antimicrobial liquid impermeable film layer 14 coextrusion may be from 0.1 to 30 weight percent based on the total weight of the polymeric material of the antimicrobial liquid impermeable film layer 14 and the weight of the second antimicrobial agent. For example, the second antimicrobial agent may comprise from 1 to 20 weight percent, or from 2 to 10 weight percent.
In accordance with certain embodiments, the second antimicrobial agent may be provided in the form of particles having an average particle size ranging from 5 nanometers up to the thickness Tr of the antimicrobial liquid impermeable film layer 14, for example, from 10 nanometers to 1,000 microns, or from 0.1 to 10 microns, or from 0.5 to 5 microns.
As schematically shown in
As schematically shown in
In accordance with certain embodiments, after the antimicrobial pre-treated fabric layer 12 and the antimicrobial liquid impermeable film layer 14 are produced, the antimicrobial liquid impermeable film layer 14 can be deposited on the surface of the antimicrobial pre-treated fabric layer 12 through a lamination process 51. The lamination process 51 may use heat and/or pressure to combine the antimicrobial pre-treated fabric layer 12 and the antimicrobial liquid impermeable film layer 14 into a laminated structure. For example, the antimicrobial liquid impermeable film layer 14, or both the antimicrobial liquid impermeable film layer 14 and antimicrobial pre-treated fabric layer 12, may be heated and passed through a upper nip-roller 71 and a lower nip-roller 72 to thereby bond the antimicrobial pre-treated fabric layer 12 and the antimicrobial liquid impermeable film layer 14 together. In other embodiments, other types of pressure-applying machines may be used. During the lamination process, the antimicrobial liquid impermeable film layer 14 may not significantly infiltrate the antimicrobial pre-treated fabric layer 12, but is sufficiently bonded thereto to prevent delamination during use. In an embodiment of the present invention, no other adhesive is used to combine the antimicrobial pre-treated fabric layer 12 and the antimicrobial liquid impermeable film layer 14. However, an adhesive may be used in other embodiments. When the antimicrobial liquid impermeable film layer 14 is laminated 51 to the antimicrobial pre-treated fabric layer 12, the antimicrobial liquid impermeable film layer 14 provides a continuous film that allows the laminated shower curtains 10 to be both liquid impermeable and gas impermeable. After lamination, the laminated material of the shower curtain 10 may then be rolled 52.
In accordance with the certain embodiments, the roll 52 of the laminated material may be formed into a laminated shower curtain 10 by conventional techniques known to those skilled in the art. For example, the laminated material may be cut to the desired dimensions and conventional edge treatment such as hemming may be applied to the top, bottom and side edges. In addition, the top edge of the laminated shower curtain 10 may be provided with standard holes or attachment points for shower curtain rings or hooks by conventional techniques.
Samples of laminated shower curtain materials of the present invention were tested for mildew resistance against sterilized control samples comprising sterilized filter paper. The tests were conducted in accordance with AATCC Test Method 30-2013 Antifungal activity, Assessment on Textile Materials: Mildew and Rot Resistance of Textile Materials—Test III: Agar Plate: Aspergillus Niger ATCC 6275. Three laminated shower curtain materials of the present invention were cut into multiple disc-shaped samples. For each type of laminated shower curtain material tested, one of the test discs was tested on its “Face” side and one of the test discs was tested on its “Back” side. The combined test results are listed in Table 1 below. All of the laminated shower curtain test disc samples corresponding to the present invention exhibited no growth (no test organisms visible by the naked eye or under a microscope; 0% of the surface area of the test disc covered with the test organism), while all of the sterilized control samples exhibited macroscopic growth (visible to the naked eye; 100% of the surface area of the test disc covered with the test organism).
Aspergillus Niger: 0%
Aspergillus Niger: 100%
Aspergillus Niger: 0%
Aspergillus Niger: 100%
Whereas particular embodiments of this invention have been described above for purposes of illustration, it will be evident to those skilled in the art that numerous variations of the details of the present invention may be made without departing from the invention as defined in the appended claims.
This application is a continuation of U.S. patent application Ser. No. 15/197,213 filed Jun. 29, 2016, which claims the benefit of U.S. Provisional Patent Application Ser. No. 62/185,996, filed on Jun. 29, 2015, which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62185996 | Jun 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15197213 | Jun 2016 | US |
| Child | 16917250 | US |