Patent Grant
7402955
The present invention is directed to a lamp that has a phosphor coating and more particularly to a fluorescent lamp having a phosphor coating on an alumina layer.
Some lamps, notably fluorescent lamps, use a coating of phosphors on the interior surface of the lamp envelope that converts ultraviolet radiation to visible light suitable for the intended purpose. Many of these phosphors are activated by rare earth ions. The coatings are typically blends that include amounts of particular phosphors and their respective rare earth activators that achieve the desired lamp brightness and color rendering index (CRI). For example, the CRI of some fluorescent lamps is desirably in excess of 82 and the 100 hour brightness is at least 3000 lumens.
Examples of the phosphors used in fluorescent lamps include one or more of a europium-activated yttrium oxide (YOE, Y2O3:Eu) red phosphor with a primary emission at 612 nm, a cerium and terbium-activated lanthanum phosphate (LAP, (La,Ce,Tb)PO4) green phosphor with a primary emission at 544 nm, a europium-activated barium magnesium aluminate (BAM, BaMgAl10O17:Eu) blue phosphor with a primary emission at 455 nm, and a europium-activated strontium borophosphate (SBP, Sr6P5BO20:Eu) blue-green phosphor with a primary emission at 480 nm. The specific rare earth activators for these phosphors include europium, terbium and cerium.
The cost of the rare earth activators is relatively high and various attempts have been made to reduce their use. In fluorescent lamps, the amount of ultraviolet radiation converted to visible light by the phosphor coating is a function of coating thickness, activator levels, and phosphor particle reflectivity. One attempt to reduce the cost of the rare earth activators in a lamp was to reduce a thickness of the coating, thereby reducing the amount of rare earth activators in the lamp. However, as the thickness of the coating was reduced more of the ultraviolet radiation passed through the coating and did not produce visible light.
To compensate for this loss of visible light, a less expensive halophosphate phosphor layer was placed under the coating (between the envelope interior surface and the coating) to convert the ultraviolet radiation that passed through the coating to visible light. However, the quality of the light emitted by the lamp was reduced due to the broad band emission spectra and low quantum efficiency of halophosphate phosphors. Specifically, the halophosphate phosphor layer reduced the lamp CRI to unacceptable levels. In addition, the halophosphate phosphor layer did not maintain consistent light output over the life of the lamp resulting in poor lamp lumen maintenance.
In a further attempt to reduce the amount of rare earth activators, the thickness of the phosphor coating was reduced and a layer of alumina was added between the phosphor coating and the lamp interior surface (instead of the halophosphate phosphor layer). The alumina layer provided some ultraviolet reflectivity so that some of the ultraviolet radiation that passed through the coating was reflected back into the phosphor coating for conversion to visible light. The alumina layer included mixed phase alumina particles that reflected the unused ultraviolet radiation back into the phosphor coating to provide higher ultraviolet conversion at lower coating weights. Nevertheless, the phosphor coating on the alumina layer still had to be relatively thick in order to achieve the desired lamp brightness.
Accordingly, an object of the present invention is to provide a novel lamp that contains a smaller amount of rare earth activators and that avoids the problems of the prior art.
A further object of the present invention is to provide a novel lamp that includes a laminate on an interior surface of the lamp envelope, where the laminate includes an alumina layer and a multilayer phosphor coating on the alumina layer. The phosphor coating includes a top layer with a first weight percent of rare earth activators and a middle layer with a second weight percent of the rare earth activators, where the second weight percent is less than the first weight percent so that a total amount of the rare earth activators in the coating is reduced while maintaining a required lamp brightness and color rendering index (CRI).
A yet further object of the present invention is to provide a novel lamp where the second weight percent is about 50-60% of the first weight percent of the rare earth activators and the middle layer is about 30-50% of a total weight of the phosphor coating so that a total weight of the activators in the phosphor coating is no more than about 80% of a weight of the activators in the coating if the first and second weight percents were the same.
These and other objects and advantages of the invention will be apparent to those of skill in the art of the present invention after consideration of the following drawings and description of preferred embodiments.
The present invention reduces the amount of rare earth activators in the phosphor coating on an alumina layer on an interior surface of a lamp by separating the phosphor coating into two phosphor layers; a top phosphor layer (nearest the source of ultraviolet radiation) that includes a normal amount of rare earth activators, and a middle phosphor layer that is between the alumina layer and the top phosphor layer and that has a reduced amount of rare earth activators. Rare earth activators preferably comprise one or more of the lanthanides (atomic nos. 57-71) and more preferably one or more of Ce, Tb, and Eu.
The primary reason this operates successfully is that a large percentage of the 254 nm ultraviolet radiation is converted to visible light by the normal rare earth amount phosphor layer 16. The exact amount of ultraviolet radiation that is converted is a function of the thickness of layer 16, activator amounts, and the phosphor particle reflectivity. The reduced rare earth amount phosphor layer 14 converts a much smaller amount of ultraviolet radiation to visible light so that the slight reduction in brightness and CRI that may result from the reduced level of rare earth activators in layer 14 does not substantially diminish the overall lamp brightness and CRI.
The phosphors and activators may be any of the above-mentioned types or other phosphors and activators suitable for lamp coatings.
The phosphor layers 14, 16 may have thicknesses that are the same or different, depending on the particular mix of phosphors and activators and their respective weights. Since the geometry of a particular envelope is known, the amounts of phosphors and activators are typically expressed as weights of the substance per lamp, rather than defining a particular thickness, i.e., total grams per lamp or coating weight.
The layers 16 and 14 preferably are comprised of substantially the same phosphors but contain different amounts of the activators. In particular, the phosphor layer 16 has a first weight percent of the rare earth activators and phosphor layer 14 has a second weight percent of the rare earth activators. The second weight percent is less than the first weight percent so that a total amount of the activators in the coating is reduced while maintaining a required lamp brightness and CRI.
Preferably the second weight percent is about 50-60% of the first weight percent and the weight of phosphor layer 14 is about 30-50% of a total weight of the layers 14 and 16 so that a total weight of the activators in the coating is no more than about 80% of a weight of the activators in the phosphor layers 14 and 16 if the first and second weight percents were the same.
Tests were conducted on a particular embodiment to demonstrate the invention. One type of conventional fluorescent lamp (OSRAM SYLVANIA FO32T8/XP) has a tubular soda lime glass envelope, a mixed phase alumina coating (0.6 grams/lamp after lehring), a phosphor coating (YOE/LAP/BAM) on the alumina (2.1 grams/lamp after lehring), an argon gas fill at 2.5 torr, lamp electrodes with a mixed-oxide emitter coating, and a bi-pin metal base. The alumina layer contains a mixture of: (1) 95% of an alumina (CR30 from Baikowski) that is 65% alpha phase and 35% gamma phase and that has a particle size of about 100 nm; and (2) 5% of a gamma phase alumina (Aluminum Oxide C from Degussa AG) that has a particle size of about 20 nm. More information about the alumina layer is provided in U.S. Pat. No. 5,726,528 that is incorporated by reference. This lamp has a brightness at 100 hours of at least about 3000 lumens and a CRI of greater than about 83.
In a test of the application of the present invention to this lamp, the phosphor coating was replaced with a multilayer coating. Initially, the glass tube was coated with a water-based suspension of the mixed phase alumina, an organic water-soluble polymer, and water-compatible surfactants. The alumina-coated tube was then heated in a lehr to remove the organic binder in order to allow further coating applications. This coating was applied so that the weight of the alumina layer remaining in the lamp after removal of the organic materials was about 0.6 grams/lamp.
The middle layer (e.g., reduced rare earth amount phosphor layer 14) included a YOE/LAP/BAM phosphor containing about 50-60% of the normal rare earth activator levels as follows (median particle size about 6-9 microns):
The blend of YOE/LAP/BAM for the middle layer was adjusted to provide light with a nominal color temperature of 4100K, a CIE x color coordinate value of 0.382, and a CIE y color coordinate value of 0.384. In particular, the phosphor blend in this layer was: reduced activator YOE—59.3 wt %, reduced activator LAP—33.3 wt %, and reduced activator BAM—7.4 wt %. The reduced-activator coating was applied to the alumina coated tube. The alumina and middle layer coated tube was then heated again to permit application of the top phosphor layer.
The top phosphor layer (e.g., normal rare earth amount phosphor layer 16) was then prepared and applied. The YOE/LAP/BAM phosphors in this layer included the above-mentioned normal weight percents of activators and a SBP phosphor. The final phosphor blend in this layer was: normal activator YOE—49.0 wt %, normal activator LAP—35.3 wt %, normal activator BAM—7.4 wt %, and normal activator SBP—8.3 wt %. The total weight of the top and middle layers was 2.1 grams/lamp.
This procedure was repeated on a set of lamps that were provided with varying amounts of the middle and top layers while keeping the total weight of the top and middle layers the same (2.1 grams/lamp in this test). The lamps were tested for brightness and CRI and the results are shown in
The percentages and phosphors given above for this test are generally representative but are not considered limiting as other percentages and phosphors are also suitable for application of the present invention in order to reduce the amount of rare earth activators in the lamp.
While embodiments of the present invention have been described in the foregoing specification and drawings, it is to be understood that the present invention is defined by the following claims when read in light of the specification and drawings.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4079288 | Maloney et al. | Mar 1978 | A |
| 4088923 | Manders | May 1978 | A |
| 4305019 | Graff et al. | Dec 1981 | A |
| 4431941 | Roy et al. | Feb 1984 | A |
| 4623816 | Hoffman et al. | Nov 1986 | A |
| 4806824 | Paynter et al. | Feb 1989 | A |
| 4879492 | Latassa et al. | Nov 1989 | A |
| 4924141 | Taubner et al. | May 1990 | A |
| 5008789 | Arai et al. | Apr 1991 | A |
| 5726528 | Jansma et al. | Mar 1998 | A |
| Number | Date | Country | |
|---|---|---|---|
| 20060267500 A1 | Nov 2006 | US |