Landfillable composition from iron chloride waste treatment in molten salt

Abstract

A solid, water impervious landfillable composition of a process for treating iron chloride wastes such as those obtained when chlorinating titanium ore is disclosed. The process involves reacting the iron chlorides with limestone in molten CaCl.sub.2.xH.sub.2 O, where x equals 3-6. The composition comprises CaCl.sub.2.xH.sub.2 O where x is from 3-6 and FeO.sub.Y where Y is from 1.0-1.5 and the weight ratio of CaCl.sub.2.xH.sub.2 O (calculated as CaCl.sub.2.2H.sub.2 O)/FeO.sub.Y is from 1/9-4/1.

Description

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a solid, water impervious composition of a process of treating iron chloride wastes such as those generated when chlorinating titanium ores or chlorinating aluminum ores to make them suitable for disposal, such as landfill.

2. Prior Art

U.S. Pat. No. 4,229,399 discloses mixing the iron chloride waste stream from a titanium ore chlorinator with an alkaline material and thereafter adding water and granulating the resulting mixture.

SUMMARY OF THE INVENTION

The present invention relates to a solid, water impervious composition of a process of treating iron chloride wastes such as those generated in the chlorination of titanium ores to form titanium dioxide or chlorinating bauxite in the production of aluminum chloride and electrolytic aluminum. The process involves contacting the iron chloride wastes with limestone, dolomitic limestone, dolomite, or MgCO.sub.3 in a bath of molten CaCl.sub.2.xH.sub.2 O, where x is from 3-6, at from 50.degree.-200.degree. C., and preferably between 100.degree.-150.degree. C.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic flowsheet of a first method of performing the process by which the composition of the present invention is made.

FIG. 2 is a schematic flowsheet of a second method of performing the process by which the composition of the present invention is made.

FIG. 3 is a plot of % conversion vs. reaction time as described in Examples 5-10.

FIG. 4 is a plot of % conversion vs. reaction time as described in Examples 11-13.

DETAILED DESCRIPTION OF THE DRAWINGS

Referring now to FIG. 1, iron chloride wastes from a titanium ore chlorinator in line 11 are fed to mixer 12. Pulverized limestone in line 13 is also fed to mixer 12. From mixer 12 the iron chloride wastes and limestone are fed via line 14 to molten salt reactor 15 containing CaCl.sub.2.xH.sub.2 O wherein the iron chloride is converted to iron oxide and the limestone to calcium chloride. Air is fed to molten salt reactor 15 via line 16 and defoamer via line 17. Carbon dioxide and water vapor are removed from molten salt reactor 15 via line 18. The surface of the molten salt in reactor 15 is skimmed and the resulting impurities such as coke and a small amount of CaCl.sub.2.xH.sub.2 O are removed via line 19 and sent to unit 20 where defoaming action is performed. The CaCl.sub.2.xH.sub.2 O-impregnated coke is removed from unit 20 via line 21 and disposed of. The reaction products from molten salt reactor 15 are removed via line 23 and sent to sedimentation or centrifuging separation unit 26. The titanium ore which settles to the bottom of sedimentation or centrifuging separation unit 26 is removed via line 27 and sent to washing unit 28. Wash water is fed to washing unit 28 via line 29. Washed titanium ore is removed from washing unit 28 via line 31 and sent to drier 32. Water vapor is removed from drier 32 via line 33 and titanium ore via line 34. Water is removed from washing unit 28 and sent to molten salt reactor 15 as make-up water via line 35. Recycle CaCl.sub.2.xH.sub.2 O is removed from sedimentation or centrifuging separation unit 26 via line 36 and recycled to molten salt reactor 15. A mixture of CaCl.sub.2.xH.sub.2 O and iron oxide composed of approximately 70-80% CaCl.sub.2.xH.sub.2 O and 20-30% FeO.sub.Y where Y is 1-1.5, is removed from sedimentation or centrifuging separation unit 26 via line 37 and disposed of.

Referring now to FIG. 2, iron chloride wastes from a titanium ore chlorinator are fed to molten salt bath 41 containing CaCl.sub.2.xH.sub.2 O at 50.degree.-200.degree. C. via line 42. The molten salt and iron chloride wastes are fed from molten salt bath 41 to sedimentation unit 43 via line 44. Titanium ore settles in sedimentation unit 43 and is removed in line 45 and sent to washer 46. Wash water is fed to washer 46 via line 47. Washed titanium ore is removed from washer 46 via line 48 and sent to drier 49. Water vapor is removed from drier 49 via line 51 and washed and dried titanium ore is recovered via line 52 and returned to a chlorination unit (not shown). Molten salt and entrained and/or dissolved iron chloride is removed from sedimentation unit 43 via 53 and sent to molten salt reactor 54 via line 55. Water is removed from washer 46 via line 56 and sent to molten salt bath 41 via line 57 and to molten salt reactor 54 via line 58 as make-up water. Limestone is fed to molten salt reactor 54 via line 59. Defoamer is fed to molten salt reactor 54 via line 61. Air is fed to molten salt reactor via line 62. Carbon dioxide and water vapor are removed from molten salt reactor via line 63. Molten salt reactor is fitted with a skimmer which feeds line 64 with coke and molten salt. The molten salt and coke are defoamed and condensed in unit 65. Molten salt and iron oxide are sent from molten salt reactor 54 to sedimentation unit 71 via line 72. Molten CaCl.sub.2.xH.sub.2 O and entrained iron oxide are removed from the bottom of sedimentation unit 71 via line 73 and disposed of. Molten salt is removed from sedimentation unit 71 via 74 and recycled to molten salt reactor 54 via line 55 and to molten salt bath 41 via line 75.

DETAILED DESCRIPTION

The present invention involves the discovery that the composition produced in a process for treating iron chloride wastes such as those obtained when chlorinating titanium ore is surprisingly a stable nonleaching material which is less water permeable than clay when handled properly. The composition of the present invention sets up when placed in a landfill and is impermeable to water even if some ferrous chloride is present. The fact that the product is nonleaching and impermeable to water is surprising, because of the presence of a large amount of calcium chloride which is very soluble in water. The material appears to set up in a manner somewhat analogous to cement setting up, but the set up material is not strong enough to use as a structural substitute for cement.

The self-sealing product is obtained when the molten, melt-neutralized material is poured into a test tube or landfill providing:

1. That the starting material FeCl.sub.3 /FeCl.sub.2, contains at least about 10% by weight FeCl.sub.3, and

2. The FeO.sub.Y, where Y equals 1.0-1.5, in admixture with CaCl.sub.2, has been concentrated to a weight ratio of CaCl.sub.2.xH.sub.2 O (calculated as CaCl.sub.2 2H.sub.2 O)/FeO.sub.Y of from 1/9 to 4/1 preferably about 2/1.

The samples produced from pure FeCl.sub.2 starting material never sealed under any circumstances.

The concentration of FeO.sub.Y in the molten salt can be achieved by either settling or centrifuging.

The self-sealing property can also be achieved by first dehydrating the melt-neutralized product from CaCl.sub.2 4.H.sub.2 O to CaCl.sub.2.2H.sub.2 O by heating at about 200.degree. C. followed by wetting with water shortly before packing or landfilling.

The process that produces the composition of the present invention involves the treatment or neutralization with limestone of iron chloride wastes from a titanium dioxide ore chlorinator at a modest temperature in a molten salt reactor. The reaction is fast and generates a great deal of carbon dioxide. This generation of carbon dioxide combined with elevated temperature serves to strip water from the system and thus maintain the desired water content in the system as well as to agitate the reaction mixture. Any water deficiency in the system is corrected with make-up water. Generally the temperature is in the range of from about 50.degree.-200.degree. C. with 100.degree.-150.degree. C. being preferred. The molten salt used in the process is CaCl.sub.2.xH.sub.2 O where x is between 3 and 6 and more preferably between 4 and 5. The case, where x=3 is in reality a mixture of CaCl.2H.sub.2 O and CaCl.sub.2.4H.sub.2 O. The amount of water of hydration is important because it controls the melting range (without boiling) of the salt which, in turn affects the reaction rate and the viscosity of the melt. The process minimizes the pressure needed to prevent boiling, at the required reaction temperature, but does not exclude pressurization if still higher temperatures are desired.

The low pressure afforded by the process facilitates removal of the gaseous CO.sub.2 which is generated by the reaction and thus avoids suppression of the reaction which can be caused by the use of pressure required when using an aqueous system at near and/or beyond the boiling point of water.

The reactions are generally fast with over half the reactions being sufficiently complete in less than 10 minutes for the ferric system for the composition of this invention to be landfilled. In the process that produces the composition of the present invention, ferric chloride reacts fast even at temperatures as low as 110.degree. C. Ferrous chloride reacts slower and requires a temperature of about 150.degree. C. to reach a significant rate but is rendered landfillable rapidly at lower temperatures when reacted with calcium carbonate in admixture with ferric chloride. Most of the other trace metal chlorides commonly associated with the iron chlorides waste from a titanium ore chlorinator will also be neutralized along with the iron chlorides. The iron chlorides and the other trace metal chlorides appear to first dissolve in the molten salt followed by adsorption, CaCO.sub.3 dissociation, and finally neutralization. Representative reactions which occur can be summarized as follows:

CaCO.sub.3 +FeCl.sub.2 .fwdarw.FeO+CaCl.sub.2 +CO.sub.2 .uparw. 3FeO+1/2O.sub.2 .fwdarw.Fe.sub.3 O.sub.4 (if O.sub.2 is present) 3CaCO.sub.3 +2FeCl.sub.3 .fwdarw.Fe.sub.2 O.sub.3 +3CaCl.sub.2 +3CO.sub.2 .uparw.

The process offers numerous advantages over the dry lime (CaO) neutralization process. First the low-temperature and atmospheric-pressure operation simplifies material handling, storage and reactor design. The process allows recovery of blowover coke and titanium ore, which are entrained in the chlorination gases, either before or after the neutralization reaction. The process allows 100% use of limestone which would otherwise require an energy intensive calcination temperature in excess of 500.degree. C. to produce CaO which has to be handled and stored dry. Further, the high temperatures promote the production of more soluble forms of some impurities such as chromium and manganese. The limestone neutralization also avoids the danger of any high-temperature runaway reaction, such as the reaction between FeCl.sub.3 and CaO as well as any hydrogen gas hazard which is characteristically associated with the lime-neutralization at high temperatures. The CaCl.sub.2.xH.sub.2 O molten salt is nonhazardous. Another advantage of the process is that no external source of molten salt is needed because the molten salt is also one of the major reaction products, which is recycled to the reactor.

EXAMPLES

Example 1

Calcium chloride hydrate containing two molecules of hydration (147 g) is mixed with 36 g of water in a three-necked 1000 ml flask equipped with a stirrer, thermometer and gas connections. After hardening, the contents of the flask are heated to 125.degree. C. with stirring. Fifteen grams of calcium carbonate are mixed with 21.35 g of FeCl.sub.3 and added to the flask. After 2 minutes 10 ml of water containing 0.5 ml antifoam agent are added to the flask. Nitrogen gas is passed through the flask at a rate of 750 ml/minute as measured at standard temperature and pressure. Samples of off-gas from the flask are taken at 130.degree. C. and analyzed for carbon dioxide with the results reported in Table I. The production of CO.sub.2 is an indication of the rate of reaction, thus in 15 minutes the reaction was essentially complete.

TABLE I______________________________________ Time CO.sub.2 Minutes %______________________________________ 1 27.57 3 22.06 6 8.30 10 3.13 15 0.45 20 0.12 30 0.02______________________________________

EXAMPLE 2

Example 1 is repeated except the flask is heated to 150.degree. C. before adding the calcium carbonate and ferric chloride and 22.5 g of calcium carbonate are added to the flask. Twenty-six minutes into the sampling time the material in the flask has thickened to a paste and 10 ml of water are added. The results of the off-gas sampling are reported in Table II.

TABLE II______________________________________ Temperature CO.sub.2Time .degree.C. %______________________________________35 sec 140 42.781 min, 45 sec 140 28.974 min 145 17.277 min 148 9.7010 min 146 3.7421 min 155 2.2530 min 1.29______________________________________

EXAMPLE 3

Example 1 is repeated except that the flask is heated to 110.degree. C. before the ferric chloride and calcium carbonate are added to the flask and that 40.14 g of calcium carbonate was added to the flask. The analyses of the off-gas from the flask are separated in Table III.

TABLE III______________________________________ Temperature CO.sub.2Time .degree.C. %______________________________________55 sec 111 42.941 min, 55 sec 112 29.545 min. -- 21.9210 min 115 3.9915 min 114 2.4120 min 113 1.1930 min 110 0.68______________________________________

EXAMPLE 4

Example 3 is repeated except the contents of the flask are heated to 130.degree. C. before adding the ferric chloride and calcium carbonate. The analyses of the off-gas from the flask are reported in Table IV.

TABLE IV______________________________________ Temperature CO.sub.2Time .degree.C. %______________________________________50 sec 125 40.232 min 125 26.075 min 127 21.1210 min 131 5.6815 min 130 3.4920 min 127 1.5530 min 130 0.69______________________________________

EXAMPLE 5

Calcium chloride hydrate containing two molecules of hydration (147.0 g) is mixed with 36.0 g of water in a three-necked, 1000 ml flask equipped with a stirrer, thermometer and gas connections. The water reacts with the CaCl.sub.2.2H.sub.2 O to form CaCl.sub.2.4H.sub.2 O which forms as a hard solid. The contents of the flask are heated to 145.degree. C. with continuous stirring until the molten CaCl.sub.2.4H.sub.2 O salt is water-like. A stoichiometric mixture of FeCl.sub.2 and CaCO.sub.3 powder is added to the melt in the flask. The initial mole ratio of CaCl.sub.2.4H.sub.2 O/(FeCl.sub.2 +CaCO.sub.3) is 1.0/0.4. After about two minutes, 10 ml of water containing 0.5 ml antifoam agent are added to the flask. Air is bubbled through the flask at a rate of 750 ml/minute as measured at standard temperature and pressure. A reflux condenser is fitted to the exit neck of the flask, thereby minimizing the loss of H.sub.2 O from the flask. Samples of the off-gas from the flask are taken periodically and analyzed for carbon dioxide content at selected intervals of time, the results of which are reported as broken line curve (2) in FIG. 3.

EXAMPLE 6

Example 5 is repeated except that an equimolar amount of magnesium carbonate is substituted for the calcium carbonate. The results are reported as broken line curve (1) in FIG. 3. As can be seen from FIG. 3, magnesium carbonate exhibits a faster reaction role than calcium carbonate.

EXAMPLE 7

Example 5 is repeated except that an equimolar amount of sodium carbonate is substituted for the calcium carbonate. The results are reported as broken line curve (3) in FIG. 3. As can be seen, the sodium carbonate is less reactive than the calcium carbonate.

EXAMPLE 8

Example 5 is repeated except that an equimolar amount of ferric chloride is substituted for the ferrous chloride. The results are reported as solid line curve (2) in FIG. 3.

EXAMPLE 9

Example 5 is repeated except an equimolar amount of magnesium carbonate is substituted for the calcium carbonate and an equimolar amount of ferric chloride is substituted for the ferrous chloride. The results are reported as solid line curve (1) in FIG. 3. As can be seen the magnesium carbonate is more reactive than the calcium carbonate.

EXAMPLE 10

Example 5 is repeated except an equimolar amount of sodium carbonate is substituted for the calcium carbonate and an equimolar amount of ferric chloride is substituted for the ferrous chloride. The results are reported as solid line curve (3) in FIG. 3. As can be seen the sodium carbonate is less reactive than the calcium carbonate.

EXAMPLE 11

Example 5 is repeated except an equimolar amount of an equimolar mixture of ferric chloride and ferrous chloride is substituted for the ferrous chloride. The results are reported as line (1) in FIG. 4.

EXAMPLE 12

Example 5 is repeated except an equimolar amount of an equimolar mixture of ferric chloride and ferrous chloride is substituted for the ferrous chloride and an equimolar amount of magnesium carbonate is substituted for the calcium carbonate. The results are reported as line (2) in FIG. 4. Again the magnesium carbonate is more reactive than the calcium carbonate.

EXAMPLE 13

Example 5 is repeated except that an equimolar amount of an equimolar mixture of ferric chloride and ferrous chloride is substituted for the ferrous chloride and an equimolar amount of sodium carbonate is substituted for the calcium carbonate. The results are reported as curve (3) in FIG. 4. Again the sodium carbonate is less reactive than the calcium carbonate.

EXAMPLES 14-16

Example 5 is repeated except 40.0 g of a mixture of solid chloride waste from a titanium ore chlorinator is added to the molten CaCl.sub.2.4H.sub.2 O in the flask. After one hour of reaction, the molten mass is centrifuged at 1,840 rpm in a laboratory bench-top centrifuge heated to 150.degree. C. After ten minutes of centrifuging, the supernatant molten salt is poured out of the centrifuge tubes. The solidified reddish mass in the bottom layer comprises approximately 30 weight percent iron oxides and 70 weight percent CaCl.sub.2.xH.sub.2 O. This solid mass is pulverized and subjected to the Environment Protection Agency's E.P. Toxicity leaching test and analysis as reported in the Federal Register V. 45 No. 98, May 18, 1980 pp. 33122, 33127-33128. Although chromium and especially chromium in the hexavalent state are of major concern in the titanium ore chlorinator solid waste materials tested, due to their being one of the eight elements listed by E.P.A. for the regulation of hazardous waste solids, Fe, Mn and V are also analyzed to determine the extent of insolubilization of each element as a result of the treatment. Titanium ore chlorinator solid waste from two plants A and B are tested. The data are summarized in Table V. In Table V mg stands for milligrams, and ND stands for not detectable.

EXAMPLE 17

Example 17 reports the result of dry-lime neutralizing the wastes from plant B using CaO which reacts spontaneously with iron chloride when a small amount of water is sprayed onto the solid mixture.

TABLE V__________________________________________________________________________Fe Mn V Cr--Total Cr.sup.VI Waste Insolu- Insolu- Insolu- Insolu- Insolu- From bilized bilized bilized bilized bilizedEx Plant mg/l % mg/l % mg/l % mg/l % mg/l %__________________________________________________________________________14 A 159 98.1 88.1 50.0 0.986 99.2 0.366 99.4 ND 10015 A 229 97.2 65.0 50.0 -- -- 0.53 99.1 0.1 10016 B 678 95.1 36.8 90.1 0.841 99.2 0.224 99.5 ND 10017 B 771 94.8 109.0 70.5 -- -- 8.40 82.3 2.1 --__________________________________________________________________________ As can be seen in Table V, chromium, chromium in the hexavalent state, vanadium and iron are all nearly completely reacted and insolublized. Manganese is the only one which is only partially (50-90%) insolubilized.

EXAMPLE 18

Numerous CaCO.sub.3 melt-neutralized iron chloride samples are tested in the laboratory for permeability under a two foot head of water. A sample of the permeability test data is presented in Table VI. Table VI also serves as a summary of the experimental findings for achieving water impermeability of the neutralized products. The following are the conclusions based on the test data. The method of dampening the product before packing it into a permeability test tube does not produce impermeability with the melt-neutralized product. Charging the molten, melt-neutalized sample into the permeability test tube can produce a self sealing product under the conditions as follows:

The starting material has to contain 10% by weight FeCl.sub.3. Samples produced with pure FeCl.sub.2 never did seal under any circumstances. Samples produced from either pure FeCl.sub.3 or FeCl.sub.3 /FeCl.sub.2 mixture sealed very well so long as the FeO.sub.y had been concentrated to about 20-90%, preferably 30% by weight. The concentration of FeO.sub.y can be achieved by either settling or centrifuging. Both A and B plant samples, after neutralization and centrifuging, yielded self-sealing products.

Self-sealing property can also be achieved by first dehydrating the melt-neutalized product from tetra- to di-hydrate at 200.degree. C. followed by wetting with H.sub.2 O shortly before packing.

TABLE VI______________________________________Permeability Test of the CaCO.sub.3 Melt-Neutralized FeCl(Samples Packed When Still Molten)ReactantsRun Com- Product Time PermeationNo. pound Gr-Mole Centrifuge* (Days) (lbs/ft.sup.2 -day)______________________________________36 Fe.sub.2 O.sub.3 -- -- 250 0 CaCl.sub.2 -- -- 0 2H.sub.2 O42 FeCl.sub.2 0.15 No 128 38.4 CaCO.sub.3 0.1540 FeCl.sub.2 0.15 Yes 134 31.2 CaCO.sub.3 0.1543 FeCl.sub.3 0.15 No (CaCl.sub.2 was washed out of CaCO.sub.3 0.225 the 6" column in 20 days)44 FeCl.sub.3 0.15 Yes 127 0 CaCO.sub.3 0.225 12735 FeCl.sub.3 0.075 No 250 2.1 FeCl.sub.2 0.075 250 CaCO.sub.3 0.188 25045 FeCl.sub.3 0.075 Yes 126 0 FeCl.sub.2 0.075 CaCO.sub.3 0.18848 A** 25.0 gr Yes 119 0 CaCO.sub.3 15.0 gr49 B** 25.0 gr Yes 119 0 CaCO.sub.3 15.0 gr______________________________________ Reaction conditions: 150.degree. C., 60 min., 750 ml/min. O.sub.2 flow, CaCl.sub.2 4H.sub.2 O, melt100 grmole. *After 10 minutes of centrifuging and the removal of supernatant molten salt, the remaining solids comprise approximately 20-40% iron oxides and 60-80% CaCl.sub.2.XH.sub.2 O

Claims

1. A solid, water impervious, landfillable composition consisting essentially of CaCl.sub.2.xH.sub.2 O where x is an average of from 3-6 and FeO.sub.y where y is from 1.0-1.5 and the weight ratio of CaCl.sub.2.xH.sub.2 O (calculated as CaCl.sub.2.2H.sub.2 O)/FeO.sub.y is from 1/9-4/1.

2. The composition of claim 1 wherein the weight ratio of CaCl.sub.3.xH.sub.2 O/FeO.sub.y is about 2/1.