The present disclosure relates generally to a premix barrel of a gas turbine fuel injector, and methods of making the premix barrel by laser cladding.
In a typical gas turbine engine, one or more fuel injectors direct a fuel to a combustion chamber (called a combustor) for combustion. The fuel burns in the combustor producing heat. In some applications, the temperature in the combustor can reach as high as about 1800° F. The components of the fuel injector that are coupled to (or proximate to) the combustor are exposed to these high temperatures. To minimize temperature related damage, such components are typically made of alloys that have high creep resistance and mechanical strength. However, such alloys are expensive, and can increase the cost of these components.
U.S. Pat. No. 6,056,507 describes a gas turbine engine turbine blade assembly with a nickel based superalloy blade tip attached to a steel body by brazing. In the '507 patent, the cost of the assembly is reduced by using the more expensive superalloy only at regions where they are needed.
In one aspect, a fuel injector for a gas turbine engine is disclosed. The fuel injector may include a center body disposed about a longitudinal axis, and a premix barrel positioned radially outwardly from the center body to define an annular passageway between the center body and the premix barrel. The annular passageway may extend from an upstream end that is configured to be fluidly coupled to a compressor to a downstream end that is configured to be fluidly coupled to a combustor. The premix barrel may include a first portion at the upstream end and a second portion at the downstream end. The first portion may include a stainless steel material, and the second portion may include a nickel based superalloy material. The second portion may be coupled to the first portion by a laser clad coupling.
In another aspect, a method of fabricating a premix barrel of a gas turbine fuel injector is disclosed. The method may include machining an annular groove on a tubular component extending along a longitudinal axis, and depositing a cladding on the groove using laser cladding. The method may also include machining the cladded tubular component to a form the premix barrel. The premix barrel may include the cladding extending as a hollow tube along the longitudinal axis from one end of the tubular component.
In another aspect, a method of fabricating a premix barrel of a gas turbine fuel injector is disclosed. The method may include creating an annular groove along a length of a tubular component, and depositing a cladding on the groove using laser cladding. The method may also include machining the cladded tubular component to form the premix barrel. The machining may include removing at least a portion of the tubular component below the deposited cladding to expose a bottom surface of the cladding.
In yet another aspect, a premix barrel for a fuel injector of a gas turbine engine is disclosed. The premix barrel may include a substantially tubular body extending along a longitudinal axis from a first end to a second end. The tubular body may include a first portion made of a first material proximate the first end, and a second portion made of a second material proximate the second end. The first portion may have a first inner diameter and a first outer diameter, and the second portion may have a second inner diameter and second outer diameter. The second portion may be coupled to the first portion by a laser clad coupling.
Fuel injector 12 may include a center body 36 located radially inwards of premix barrel 26 to define an annular duct 16 therebetween. The premix barrel 26 may direct the fuel-air mixture to the combustor 14 through the annular duct 16. The fuel-air mixture may be directed into the premix barrel 26 through an air swirler 34 positioned upstream of the premix barrel 26. In some embodiments, an upstream end (or a rear portion 24) of the premix barrel 26 may be connected to the air swirler 34 using a brazed joint 32. The air swirler 34 may include an annulus with a plurality of vanes connected thereto. The vanes may be configured to induce a rotational component of velocity to the fuel-air mixture passing therethrough. In some embodiments, the air swirler 34 may include fuel outlets (orifices, nozzles, spokes, etc.) that inject the fuel (any liquid or gaseous fuel) into a compressed air stream passing through the vanes to create a swirled fuel-air mixture. In some applications, the center body 36 may house a pilot assembly configured to direct a separate stream of fuel and air to the combustor 14. The fuel-air mixture entering the combustor 14 through the annular duct 16, and the fuel stream entering the combustor 14 through the center body 36 ignite and burn in the combustor 14.
The combustion in combustor 14 heats the front portion 22 of the premix barrel 26. In some embodiments, the premix barrel 26 may expand in response to the heating and scrape against the combustor wall. This scraping may induce mechanical wear on the outer surface of the front portion 22. To withstand the high temperatures in the combustor 14 and the mechanical wear, the front portion 22 may be made from a material capable of withstanding these environmental conditions. In some embodiments, an alloy such as, for example, a nickel based superalloy, may be selected for the front portion 22. In some embodiments, the nickel based superalloy may include Alloy-X (Alloy-230, Alloy-118, etc.). The rear portion 24 of the premix barrel 26, that is in contact with relative cooler fuel-air mixture, may be cooler than, and subject to less adverse conditions than, the front portion 22. Therefore, the rear portion 24 may be made of a different material, such as stainless steel (for example, AMS 5653, ASTM A-479, etc.). For increased strength of the premix barrel 26 (and therefore, increased reliability of the fuel injector 12), the front portion 22 of the premix barrel 26 may be laser clad on, or grown on, the rear portion 24.
The front portion 22 may have a length 222 and thickness 322. The length 222 and thickness 322 may depend upon the application (for example, the operating conditions and size of the gas turbine engine 10). In general, the length 222 of the front portion 22 may vary from about 0.5-2.5 inches (12.7-63.5 mm), and the thickness 322 may vary from about 0.15-0.5 inches (3.81-12.7 mm). In some embodiments, length 222 may vary from about 0.75-1.5 inches (19.05-38.1 mm), and the thickness 322 may vary from about 0.2-0.5 inches (5.08-12.7 mm). In this specification, the term “about” is used to indicate a variation of 10% of a value. For instance, a length of about 0.2 inches, indicates a length between 0.18-0.22 inches (4.57-5.59 mm).
Laser cladding the front portion 22 on the rear portion 24 creates a premix barrel 26 in which the front portion 22 is coupled to the rear portion 24 by laser clad coupling. In such a coupling, the front portion 22 may be coupled to the rear portion 24 without an adhesive material (or another interfacial material) between them. Laser cladding the front portion 22 on the rear portion 24 involves only localized heating at the interface 28, therefore, dilution of the materials (of the front and rear portions 22, 24) and alloy formation at the interface 28 will be minimal. Laser cladding the front portion 22 on the rear portion 24 (that is, laser clad coupling) is characterized by an interface 28 where material properties change relatively abruptly across the interface 28. For example, hardness measurements along a horizontal line across interface 28 will indicate a relatively sharp change in hardness across interface 28.
It should be noted that although a premix barrel 26 of a gas turbine engine fuel injector 12 is described herein, this is only exemplary. In general, a front portion 22 of one material may be laser clad on a rear portion 24 of a different material, and used as a component in any application. For example, in an application where a front portion 22 of a bearing is subject to increased wear as compared to its rear portion 24, a front portion 22 of a wear resistant material may be laser clad on a rear portion 24 of a different material in the bearing.
An exemplary method of laser cladding the front portion 22 on the rear portion 24 is described in the following section.
The disclosed laser clad premix barrel may be applied to any fuel injector to increase the temperature resistance of the premix barrel without increasing its cost. Since a heat resistant material is laser clad to the premix barrel, the strength and reliability of the premix barrel may be high. An exemplary method of laser cladding a heat resistant front portion on a stainless steel rear portion is described below.
Laser cladding is a process in which a feed stock of cladding material (in the form of a wire, powder, etc.) is applied to the groove 204. And, a concentrated laser beam is used to melt the applied feed stock and a thin layer of material at the base of the groove 204, to form a cladding 212 that is metallurgically bonded to the base of the groove 204. Since the blank 126 is rotated during laser cladding, the cladding 212 is formed evenly around the groove 204. Laser cladding is similar to thermal spraying in that an energy source is used to melt the feed stock that is being applied to a substrate. However, unlike thermal spraying, laser cladding also melts a thin layer of the substrate that the feed stock is being applied to. This melting results in a strong metallurgical bond between the cladding 212 and the base 206. Typically, laser cladding results in an interface with a superior bond strength over thermal spraying. Since a concentrated laser beam is used as the heat source, the heat affected zone in the base 206 will be a minimum. Since laser cladding processes are known in the art, the steps involved in laser cladding are not described herein. Any known laser cladding process may be used to deposit the cladding 212. The cladding 212 may be of any shape and thickness that will produce a front portion 22 having the desired dimensions (for example, length 222 and thickness 322, see
After cladding, the cladded blank 226 is machined to form the premix barrel 26 having the desired final shape and size (step 140). The machining operation may remove the base 206 at the base of the cladding 212, to form a free standing front portion 22 made of the cladding 212 material connected to the rear portion 24 at interface 28. The inclined interface 28 may increase the area of contact between the front portion 22 and the rear portion 24, and therefore, increase the strength of the interface 28. In some embodiments, the interface 28 may have other shapes. For example, in some embodiments, the interface 28 may be stepped, and in some embodiments the interface 28 may be vertical. Since the base 206 on which the cladding 216 is deposited is removed by machining after deposition, any detrimental effects of the laser cladding process on the premix barrel 26 will be minimized. The machining operation may also form other desired features of the premix barrel 26. For example, an outer diameter of the front portion 22 may be machined to be greater than an outer diameter of the rear portion 24, an inner diameter of the front portion 22 may be machined to be substantially the same as an inner diameter of the rear portion 24, and the free end of the front portion 22 may be machined to include a chamfer.
Since the laser clad portion is metallurgically bonded to the underlying substrate, the interface between them may be strong. Additionally since the laser cladding process minimizes the heat affected zone in the underlying substrate, and since the base 206 is removed after cladding, any negative effect of the laser cladding process on the underlying substrate may be minimal. Although a cladded premix barrel 26 of a fuel injector 12, and an exemplary method of cladding the premix barrel 26 are described herein, this is only exemplary. In general, the described methods may be applied to laser clad a portion of any component used in any application.
It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed laser clad premix barrel for a fuel injector. Other embodiments will be apparent to those skilled in the art from consideration of the specification and practice of the disclosed premix barrel. It is intended that the specification and examples be considered as exemplary only, with a true scope being indicated by the following claims and their equivalents.
This is a divisional of application Ser. No. 13/409,103, filed Mar. 1, 2012, which is incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 4234119 | Masaoka | Nov 1980 | A |
| 20050132569 | Clark | Jun 2005 | A1 |
| 20090032310 | Stevens | Feb 2009 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20160033137 A1 | Feb 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 13409103 | Mar 2012 | US |
| Child | 14879182 | US |