Patent Grant
8891568
The present application claims priority to Japanese Priority Patent Application JP 2011-274256 filed in the Japan Patent Office on Dec. 15, 2011, the entire content of which is hereby incorporated by reference.
The present disclosure relates to a laser diode device and to a method of manufacturing a laser diode device. More specifically, the present disclosure relates to a hexagonal III-nitride laser diode device and to a method of manufacturing the same.
A laser diode is currently utilized in enormous numbers of technical fields. In particular, the laser diode is indispensable necessary optical device in the field of image display units such as a television and a projector. In such applications, a laser diode outputting light of red, green, and blue which are light's three primary colors is necessitated, and improvement of laser characteristics is desired.
In Japanese Unexamined Patent Application Publication No. 2009-176837, in order to effectively suppress higher-order mode light in a nitride-based laser diode device used in a short-wavelength region with a wavelength of about 400 nm, a configuration in which an insulating layer containing fine particles that absorb emitted light is formed on side surfaces of a ridge is disclosed. Red and blue laser diodes have been in practical use. Meanwhile, in recent years, a green (a wavelength from about 500 nm to about 560 nm both inclusive) laser diode has been actively developed (for example, see “The World's First True Green Laser Diodes on Novel Semi-Polar {2 0
In NPTL1 and NPTL2, a III-nitride laser diode (green laser) in which an n-type cladding layer, a light emitting layer including an active layer configured of InGaN, and a p-type cladding layer are laminated in this order on a semi-polar surface {2, 0, −2, 1} of an n-type GaN substrate is proposed. It is to be noted that, in the present specification, a plane direction of a hexagonal crystal is described as {h, k, l, m} (h, k, l, and m represent plane indices).
In NPTL1 and NPTL2, crystal growth of an epitaxial layer is made on the semi-polar surface of the GaN substrate, and thereby, a green laser with superior crystal quality is achieved while influence of piezo electric field is suppressed. In NPTL2, a configuration in the case where a green laser apparatus has a refractive index waveguide (ridge type) structure is described. In the configuration, laser light is confined by forming an insulating layer with low refractive index on side surfaces of a ridge.
As described above, in the existing laser diode devices, various configurations to prevent degradation of oscillation characteristics due to a ridge structure have been proposed. However, in the technical field of a laser diode device using a semi-polar substrate, there are many characteristics different from the characteristics of the existing nitride-based laser diode device using a polar substrate, and therefore, further development for improving the characteristics are desired.
It is desirable to provide a laser diode device with superior reliability that suppresses degradation of oscillation characteristics resulting from a ridge structure as a nitride-based laser diode device using a semi-polar substrate.
According to an embodiment of the present disclosure, there is provided a laser diode device including: a semiconductor substrate including a semi-polar surface, the semiconductor substrate being formed of a hexagonal III-nitride semiconductor; an epitaxial layer including a light emitting layer, the epitaxial layer being formed on the semi-polar surface of the semiconductor substrate, and the epitaxial layer including a ridge section; a first electrode formed on a top surface of the ridge section; an insulating layer covering the epitaxial layer in an adjacent region of the ridge section and a side surface of the ridge section, the insulating layer covering part or all of side surfaces of the first electrode continuously from the epitaxial layer; a pad electrode formed to cover a top surface of the first electrode and the insulating layer, the pad electrode being electrically connected to the first electrode; and a second electrode formed on a surface, of the semiconductor substrate, opposite to the semi-polar surface. Here, “adjacent region of the ridge section” refer to a surface, of the epitaxial layer, in a region other than the ridge section.
In the laser diode device according to the embodiment of the present disclosure, the insulating layer covers the epitaxial layer, and covers part or all of the side surfaces of the first electrode continuously from the epitaxial layer. Therefore, the pad electrode is not in direct contact with the epitaxial layer.
According to an embodiment of the present disclosure, there is provided a method of manufacturing a laser diode device, the method including: preparing a semiconductor substrate including a semi-polar surface, the semiconductor substrate being formed of a hexagonal III-nitride semiconductor; forming an epitaxial layer on the semi-polar surface of the semiconductor substrate, the epitaxial layer including a light emitting layer of the laser diode device; etching the epitaxial layer to a predetermined depth thereof through a mask, and forming a ridge section in a shape of a stripe; forming a first electrode in a region corresponding to the ridge section before the forming of the ridge section, or forming the first electrode on a top surface of the ridge section after the forming of the ridge section; forming an insulating material layer on a surface of the epitaxial layer including a top surface of the first electrode; etching the insulating material layer, and thereby forming an insulating layer, the insulating layer covering the epitaxial layer in an adjacent region of the ridge section and a side surface of the ridge section, and the insulating layer covering part or all of side surfaces of the first electrode continuously from the epitaxial layer; forming a pad electrode, the pad electrode covering a top surface of the first electrode and the insulating layer, the pad electrode being electrically connected to the first electrode; and forming a second electrode on a surface, of the semiconductor substrate, opposite to the semi-polar surface.
In the method of manufacturing a laser diode device according to the embodiment of the present disclosure, the insulating layer covers the epitaxial layer, and covers part or all of the side surfaces of the first electrode continuously from the epitaxial layer. Therefore, the pad electrode formed after forming the insulating layer is not in direct contact with the epitaxial layer.
According to the embodiments of the present invention, it is provided, a laser diode device suppressing degradation of oscillation characteristics resulting from a ridge structure and having superior reliability as a nitride-based laser diode device using a semi-polar substrate.
It is to be understood that both the foregoing general description and the following detailed description are exemplary, and are intended to provide further explanation of the technology as claimed.
Additional features and advantages are described herein, and will be apparent from the following Detailed Description and the figures.
The accompanying drawings are included to provide a further understanding of the disclosure, and are incorporated in and constitute a part of this specification. The drawings illustrate embodiments and, together with the specification, serve to explain the principles of the technology.
The first electrode 34 is formed on a top surface of the ridge section 38 of the epitaxial layer 31. The insulating layer 32 is formed on a surface of the epitaxial layer 31 to cover adjacent regions 38a of the ridge section and side surfaces 38b of the ridge section. The pad electrode 35 is formed on the whole surface including the insulating layer 32 and the first electrode 34. The second electrode 36 is formed on the other surface (rear surface) of the semiconductor substrate 37.
In the existing technology, the laser diode device 30 as illustrated in
In the step of etching the insulating layer 32 to expose the first electrode 34, the insulating layer 32 on the first electrode 34 is typically over-etched in order to securely achieve electric contact between the first electrode 34 and the pad electrode 35 formed thereon. That is, the insulating layer 32 is typically etched until part of side surfaces of the epitaxial layer 31 shaped into the ridge structure is exposed in order to prevent the insulating layer 32 from remaining on the first electrode 34.
As a result, in the existing technology, as illustrated in
However, in the existing nitride-based laser diode device emitting blue light, some minor contact between the epitaxial layer and the pad electrode does not cause a disadvantage such as degraded laser characteristics. Therefore, the configuration illustrated in
As illustrated in
As described above, in the laser diode device formed by laminating the crystal layer on the semi-polar surface of the semiconductor substrate, in the case where a portion in which no insulating layer is formed on the side surfaces of the ridge section exists, device degradation due to voltage increase is significant. Such a disadvantage of degraded characteristics is specific to a laser diode device using a semi-polar substrate, and has not been seen in the existing laser diode device using a polar substrate. For the semi-polar substrate and the polar substrate, descriptions will be given later.
Based on the foregoing finding, the proposers of the technology of the present disclosure have found a laser diode device in which voltage increase is suppressed and device degradation is decreased, as a laser diode device obtained by laminating a crystal layer on a semi-polar surface of a semiconductor substrate. A description will be hereinafter given of a laser diode device according to an embodiment of the present disclosure.
A description will be hereinafter given of the laser diode device according to the embodiment of the present disclosure and a method of manufacturing the same with reference to the drawings. The embodiment of the present disclosure will be described in the following order. It is to be noted that the present disclosure is not limited to the following examples.
[1. Configuration of Laser Diode Device]
A laser diode device according to an embodiment of the present disclosure is a laser device oscillating green light, and a refractive index waveguide type (ridge type) laser diode device having a ridge structure. A description will be hereinafter given of the laser diode device according to this embodiment.
[Whole Configuration of Laser Diode Device]
The laser diode device 1 includes a semiconductor substrate 3, an epitaxial layer 2, an insulating layer 12, a first electrode 14, a second electrode 15, and a pad electrode 13. In the laser diode device 1 according to this embodiment, the epitaxial layer 2, the insulating layer 12, the first electrode 14, and the pad electrode 13 are laminated in this order on one surface 3a of the semiconductor substrate 3 (top surface of the semiconductor substrate 3 in an example shown in
The laser diode device 1 has a shape of an approximately rectangular solid. Further, on the surface on the first electrode 14 side of the laser diode device 1, a stripe section 21 having a ridge structure extending in a predetermined direction (the Y direction in
Further, the laser diode device 1 has two side surfaces 22 and 23 (end surfaces) perpendicular to the extension direction of the stripe section 21 (Y direction in
In this embodiment, the extension direction of the stripe section 21 is a direction perpendicular to the a-axis direction. However, the extension direction of the stripe section 21 is not limited to this example, and may be set as appropriate according to, for example, applications and conditions such as necessary oscillation wavelength. Further, a width of the stripe section 21 is about several μm, and a length between the two resonance end surfaces 22 and 23 is about several hundred μm.
In the laser diode device 1 according to this embodiment, a dielectric multilayer film configured of, for example, SiO2 and Ti2 may be formed on one or both of the two resonance end surfaces 22 and 23 (end surface coating). By performing the end surface coating, reflectance is allowed to be adjusted.
[Configurations of Respective Sections]
Next, configurations of the respective sections of the laser diode device 1 according to this embodiment will be described more specifically.
[(1) Semiconductor Substrate]
The semiconductor substrate 3 is configured of a hexagonal III-nitride semiconductor such as GaN, MN, AlGaN, InGaN, and InAlGaN. Further, as the semiconductor substrate 3, a substrate in which carrier conductivity type is n-type may be used. In this embodiment, one surface of the semiconductor substrate 3 on which the epitaxial layer 2, the insulating layer 12, and the first electrode 14 are formed is not configured of the surface-plane (polar surface) but is configured of the semi-polar surface 3a.
As this embodiment, in the case where the epitaxial layer 2, the insulating layer 12, and the first electrode 14 are formed on the semi-polar surface 3a of the semiconductor substrate 3, for example, green light with a wavelength of around 500 nm is allowed to be oscillated.
As the semi-polar surface 3a, a crystal surface in which the direction of the normal to the semi-polar surface 3a is a direction obtained by tilting the c-axis in the m-axis direction at an angle from 45° to 80° both inclusive or at an angle from 100° to 135° both inclusive may be used. It is to be noted that, in the case where an angle between the direction of the normal to the semi-polar surface 3a and the c-axis is smaller than 45° or larger than 135°, a possibility that an end surface formed by cleavage process (pressing process) becomes the m-plane (nonpolar surface) is high. Further, in the case where the angle between the direction of the normal to the semi-polar surface 3a and the c-axis is larger than 80° and smaller than 135°, there is a possibility that an end surface having desired flatness and desired orthogonality is not obtained.
Further, in the foregoing angle ranges, the angle between the direction of the normal to the semi-polar surface 3a and the c-axis is preferably from 63° to 80° both inclusive or is preferably from 100° to 117° both inclusive in order to obtain light emission with long wavelength. In these angle ranges, piezo polarization in an after-mentioned light emitting layer 7 in the epitaxial layer 2 is decreased, intake of In at the time of growing (forming) an active layer becomes favorable, and the variable range of In composition in the light emitting layer 7 (active layer) is allowed to be enlarged. Therefore, by setting the angle between the direction of the normal to the semi-polar surface 3a and the c-axis to a value within the foregoing ranges, light emission with a long wavelength is easily obtained.
As the semi-polar surface 3a having the direction of the normal thereto in the foregoing angel ranges, for example, a crystal surface such as a {2, 0, −2, 1} surface, a {1, 0, −1, 1} surface, a {2, 0, −2, −1} surface, and a {1, 0, −1, −1} surface may be used. It is to be noted that a crystal surface slightly tilted from the foregoing crystal surfaces at ±4° may be also used as the semi-polar surface 3a. In this embodiment, n-type GaN is used as the semiconductor substrate 3, and its {2, 0, −2, 1} surface is used as one main surface. Since GaN is a gallium-nitride-based semiconductor as a two-dimensional compound, favorable crystal quality and a stable substrate surface (main surface) are provided.
[(2) Epitaxial Layer, Insulating Layer, First Electrode, Second Electrode, and Pad Electrode]
Next, descriptions will be given of configurations of the epitaxial layer 2, the insulating layer 12, the first electrode 14, the second electrode 15, and the pad electrode 13 of the laser diode device 1 of this embodiment with reference to
In this embodiment, the epitaxial layer 2 includes a buffer layer 4, a first cladding layer 5, a first light guide layer 6, the light emitting layer 7, a second light guide layer 8, a carrier blocking layer 9, a second cladding layer 10, and a contact layer 11. The buffer layer 4, the first cladding layer 5, the first light guide layer 6, the light emitting layer 7, the second light guide layer 8, the carrier blocking layer 9, the second cladding layer 10, and the contact layer 11 are laminated in this order on the semi-polar surface 3a of the semiconductor substrate 3.
The buffer layer 4 is formed on the semi-polar surface 3a as one main surface of the semiconductor substrate 3, and is configured of a gallium-nitride-based semiconductor layer added with n-type dopant. More specifically, for example, the buffer layer 4 may be configured of an n-type GaN layer, and Si is applicable as the n-type dopant. Further, the film thickness of the buffer layer 4 is preferably from 100 nm to 2000 nm both inclusive, for example.
The first cladding layer 5 is formed on the buffer layer 4, and is configured of one or a plurality of gallium-nitride-based semiconductor layers added with n-type dopant. More specifically, for example, the first cladding layer 5 may be configured of an n-type GaN layer, an n-type AlGaN layer, an n-type InAlGaN layer, or the like, and Si is applicable as the n-type dopant. Further, the film thickness of the first cladding layer 5 is preferably from 500 nm to 3000 nm both inclusive, for example.
The first light guide layer 6 is formed on the first cladding layer 5, and is configured of one or a plurality of gallium-nitride-based semiconductor layers. More specifically, for example, the first light guide layer 6 may be configured of an n-type GaN layer, an n-type InGaN layer, an n-type InAlGaN layer, or the like. In addition thereto, the first light guide layer 6 may be configured of a non-doped gallium-nitride-based semiconductor layer, or may have a laminated structure configured of an n-type layer and a non-doped layer. Further, the film thickness of the first light guide layer 6 is preferably from 10 nm to 500 nm both inclusive, for example.
The light emitting layer 7 is formed on the first light guide layer 6, and has a configuration in which, for example, a well layer (not illustrated) and a barrier layer (not illustrated) that are configured of non-doped gallium-nitride-based semiconductor layers not added with impurity are alternately arranged. More specifically, for example, the well layer and the barrier layer may be configured of an AlGaN layer, a GaN layer, an InGaN layer, an InAlGaN layer, or the like. Alternatively, the light emitting layer 7 (in particular, the barrier layer) may be configured of a gallium-nitride-based semiconductor layer doped with n-type dopant. In this case, a bandgap of the barrier layer is set to a larger value than that of a bandgap of the well layer. Further, the film thicknesses of the respective layers are preferably from 1 nm to 100 nm both inclusive, for example.
The light emitting layer 7 may have a single quantum well structure including a single well layer, or may have a multiquantum well structure in which a plurality of well layers and a plurality of barrier layers are alternately arranged. In this embodiment, by laminating each layer on the semi-polar surface 3a of the semiconductor substrate 3, the light emitting layer 7 is allowed to be formed to oscillate light with wavelength from 430 nm to 570 nm both inclusive. Further, the structure of the laser diode device 1 according to this embodiment is particularly suitable for oscillating light with wavelength from 480 nm to 550 nm both inclusive.
The second light guide layer 8 is formed on the light emitting layer 7, and is configured of one or a plurality of gallium-nitride-based semiconductor layers. More specifically, for example, the second light guide layer 8 may be configured of a GaN layer, an InGaN layer, or the like, and a p-type gallium-nitride-based semiconductor layer doped with Mg is applicable thereto. Further, the film thickness of the second light guide layer 8 is preferably from 10 nm to 500 nm both inclusive, for example.
The carrier blocking layer 9 (electron blocking layer) is formed on the second light guide layer 8, and is configured of a gallium-nitride-based semiconductor layer added with p-type dopant. More specifically, for example, the carrier blocking layer 9 may be configured of a p-type AlGaN layer or the like, and Mg is applicable as the p-type dopant. Further, the film thickness of the carrier blocking layer 9 is preferably from 5 nm to 100 nm both inclusive, for example. It is to be noted that the carrier blocking layer 9 may be formed between the light emitting layer 7 and the second light guide layer 8, or may be formed in the middle of the second light guide layer 8. Further, a configuration in which the carrier blocking layer 9 is not provided in the epitaxial layer 2 may be adopted. Even if the carrier blocking layer 9 is not provided, a function as a laser diode device is retained as well.
The second cladding layer 10 is formed on the carrier blocking layer 9, and is configured of one or a plurality of gallium-nitride-based semiconductor layers. More specifically, for example, the second cladding layer 10 may be configured of a p-type GaN layer, a p-type AlGaN layer, a p-type InAlGaN layer, or the like, and Mg is applicable as the p-type dopant. Further, the film thickness of the second cladding layer 10 is preferably from 100 nm to 1000 nm both inclusive, for example.
The contact layer 11 is formed on the second cladding layer 10, and is configured of a gallium-nitride-based semiconductor layer added with p-type dopant. More specifically, for example, the contact layer 11 may be configured of a p-type GaN layer, and Mg is applicable as the p-type dopant. Further, the film thickness of the contact layer 11 is preferably from 5 nm to 100 nm both inclusive, for example.
In this embodiment, a convex ridge section 18 is formed by etching, in a tapered shape, and removing a portion from the surface of the contact layer 11 to the middle of the second cladding layer 10 in opposing side surfaces in one direction of the epitaxial layer 2 laminated on the semiconductor substrate 3. The ridge section 18 configures the stripe section 21 illustrated in
As illustrated in
The first electrode 14 is configured of one or a plurality of conductive film layers, and is formed to be electrically connected to the contact layer 11 at the top of the contact layer 11. As described later, in this embodiment, the first electrode 14 is formed before forming the ridge section 18. The first electrode 14 is formed in the shape of a stripe extending in the Y direction on the top of the contact layer 11. As a conductive material of the first electrode 14, a material capable of ohmic contact with the contact layer 11 may be used. More specifically, for example, a laminated film configured of a Pd film and a Pt film that are formed in this order of closeness to the contact layer 11 is applicable.
The insulating layer 12 is formed to cover the top of the second cladding layer 10 of adjacent regions 18a of the ridge section, to cover side surfaces 18b of the ridge section configured of the second cladding layer 10 and the contact layer 11, and to reach the side surfaces of the first electrode 14. Here, the adjacent regions 18a of the ridge section refer to a surface in a region, of the epitaxial layer 2, other than the ridge section 18. As the insulating layer 12, for example, an insulating material containing one or more of SiO2, SiN, Al2O3, and ZrO2 is applicable. Film thickness thereof is preferably from 100 nm to 500 nm both inclusive, for example.
Further, in
The pad electrode 13 is formed on the insulating layer 12 and the first electrode 14 exposed from the insulating layer 12, and is formed to be electrically connected to the first electrode 14. As the pad electrode 13, for example, a laminated film configured of a Ti film, a Pt film, and an Au film that are formed on the first electrode 14 in this order of closeness to the first electrode 14 is applicable. The film thickness of the Ti film is preferably from 5 nm to 100 nm both inclusive, the film thickness of the Pt film is preferably from 10 nm to 300 nm both inclusive, and the film thickness of the Au film is preferably from 100 nm to 1000 nm both inclusive. Since the lowermost layer of the pad electrode 13 is configured of the Ti film, a metal film in contact with the insulating layer 12 is the Ti film, and therefore, adhesive characteristics of the pad electrode 13 with respect to the insulating layer 12 are improved.
The second electrode 15 is configured of a conductive film of one or a plurality of layers, and is formed on the other surface (rear surface 3b) of the semiconductor substrate 3. As a conductive material of the second electrode 15, more specifically, for example, a laminated film configured of a Ti film and an Al film that are formed in this order of closeness to the semiconductor substrate 3 is applicable. The film thickness of the Ti film is preferably from 5 nm to 50 nm both inclusive, and the film thickness of the Al film is preferably from 10 nm to 300 nm both inclusive. In this embodiment, by flowing a desired current between the first electrode 14 and the second electrode 15, green light with wavelength from 480 nm to 550 nm both inclusive is oscillated.
[2. Method of Manufacturing Laser Diode Device]
Next, a description will be given of a method of manufacturing the laser diode device 1 according to this embodiment.
First, the semiconductor substrate 3 having a semi-polar surface configured of a hexagonal III-nitride semiconductor, that is, what we call a semi-polar substrate is prepared (step S1). Further, thermal cleaning is performed on the prepared semiconductor substrate 3.
Next, the respective semiconductor layers configuring the epitaxial layer 2 are sequentially and epitaxially grown on the semi-polar surface of the semiconductor substrate 3 by using, for example, an MOVPE (organic metal vapor-phase epitaxy) method and/or the like, and thereby, the epitaxial layer 2 is formed (step S2). Specifically, the respective semiconductor layers configuring the buffer layer 4, the first cladding layer 5, the first light guide layer 6, the light emitting layer 7, the second light guide layer 8, the carrier blocking layer 9, the second cladding layer 10, and the contact layer 11 are epitaxially grown in this order on the semiconductor substrate 3.
Next, the first electrode 14 is formed on the epitaxial layer 2 (contact layer 11) (step S3). In this case, first, as illustrated in
Next, as illustrated in
Next, the ridge section 18 is formed (step S4). The ridge section 18 is formed by forming the first electrode 14, and subsequently etching the epitaxial layer 2 from the surface of the epitaxial layer 2 (contact layer 11) to a predetermined depth in the second cladding layer 10 with the use of the first electrode 14 extending in the Y direction as a mask, as illustrated in
Next, an insulating material layer 19 to become the insulating layer 12 is formed (step S5). In this case, as illustrated in
Next, a resist film 20 for etching the insulating material layer 19 is formed (step S6). In this case, first, the whole surface of the insulating material layer 19 is coated with a resist material layer. Thereafter, the resultant is exposed and developed by using a photomask in which a desired pattern is formed. Thereby, as illustrated in
Next, the insulating layer on the first electrode 14 is etched by using the resist film 20 as a mask (step S7). In this etching step, as an etching method, dry etching or wet etching may be used. In this case, as illustrated in
As described above, in this embodiment, the insulating layer 12 is formed to cover part or all of the side surfaces of the first electrode 14 continued from the side surfaces 18b of the ridge section. Therefore, in this etching step, etching is performed under conditions in which the side surfaces of the first electrode 14 are not entirely exposed. Thereafter, as illustrated in
Next, the pad electrode 13 is formed (step S8). In this case, for example, a desired conductive film is formed by using a method such as a vacuum evaporation method and a sputtering method. Thereby, as illustrated in
Thereafter, though not illustrated, the second electrode 15 is formed on the rear surface 3b of the semiconductor substrate 3 by, for example, a liftoff method to form a laser structure. It is to be noted that the laser diode device 1 is formed by cutting the laser diode device 1 from a substrate member in which a plurality of laser diode devices 1 are two-dimensionally formed. That is, a laser bar is formed by cutting the semiconductor substrate 3 to form the resonance end surfaces 22 and 23, coating is performed on the resonance end surfaces 22 and 23, and subsequently the laser bar is cut to obtain a chipped state. Accordingly, the laser diode device 1 according to this embodiment is fabricated.
[3. Experimental Result]
Next, a description will be given of characteristics difference between the laser diode device 1 fabricated in this embodiment and a laser diode device of a comparative example. The laser diode device of the comparative example is an example in which the epitaxial layer 2 is exposed from the insulating layer 12 in the laser diode device 1 according to this embodiment. That is, the laser diode device of the comparative example has the structure illustrated in
Further, the voltage increase ratio is a increase ratio of a forward voltage. The voltage increase ratio is obtained by flowing a current three times for the respective devices, and finding a ratio between a voltage value at 100 mA when a current is flown for the first time and a voltage value at 100 mA when a current is flown for the third time. That is, the voltage increase ratio represents the voltage value (the third time)/the voltage value (the first time).
It is found that, in the laser diode device of the comparative example in which part of the epitaxial layer is not covered with the insulting layer and is exposed, as the exposure width is increased, the voltage increase ratio is also increased. From the foregoing result, it has been found that exposure of the epitaxial layer causes voltage increase. One of the causes of such voltage increase in the comparative example may be drastic progression of degradation due to direct contact between the epitaxial layer formed on the semi-polar surface and the pad electrode.
Further, in the step shown in step S7 of
On the other hand, it can be seen that, in the laser diode device 1 according to this embodiment in which the coverage range with the insulating layer 12 extends to the side surfaces of the first electrode, the voltage increase ratio is approximately 1, and the third time voltage value is not changed from the first time voltage value. It has been shown that in the laser diode device 1 in which the insulating layer 12 is formed to continuously extend from the epitaxial layer 2 to the side surfaces of the first electrode 14, and the epitaxial layer 2 is not in direct contact with the pad electrode 13 as in this embodiment, voltage increase is suppressed.
As described above, in this disclosure, in the laser diode device having the ridge structure formed by crystal growth on the semi-polar surface of the semiconductor substrate, the insulting layer covering the surface of the epitaxial layer is formed to cover part or all of the first electrode from the epitaxial layer. Thereby, device degradation associated with voltage increase is allowed to be suppressed.
In this embodiment described above, as illustrated in
[Modification]
In a laser diode device 24 according to the modification, an insulating layer 25 covering the surface of the epitaxial layer 2 is formed to extend over part of the first electrode 14. That is, in the modification, part of the central region of the first electrode 14 is in contact with the pad electrode 13.
Such a laser diode device 24 may be formed by etching the insulating material layer 19 so that part of the central region of the first electrode 14 is exposed in the step of etching the insulating layer (step S7) illustrated in
As described above, as long as the first electrode 14 is electrically connected to the pad electrode 13, the insulating layer 25 may be formed to extend over part of the top surface of the first electrode 14. As illustrated in
Further, in this embodiment described above, as illustrated in the step in
Further, in this embodiment described above, the n-type semiconductor substrate is used as an example. Alternatively, a p-type semiconductor substrate may be used. In this case, for respective layers, inversed conductive type may be used in the foregoing embodiment. In this case, effects similar to those of the present disclosure are obtainable. Further, the laser diode device according to the present disclosure is not limited to the foregoing embodiment, and various modifications may be made within the spirit of the present disclosure.
It is possible to achieve at least the following configurations from the above-described exemplary embodiment and the modification of the disclosure.
It should be understood that various changes and modifications to the presently preferred embodiments described herein will be apparent to those skilled in the art. Such changes and modifications can be made without departing from the spirit and scope of the present subject matter and without diminishing its intended advantages. It is therefore intended that such changes and modifications be covered by the appended claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2011-274256 | Dec 2011 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 20090323746 | Ohmi et al. | Dec 2009 | A1 |
| 20100025657 | Nagahama et al. | Feb 2010 | A1 |
| Number | Date | Country |
|---|---|---|
| 2010-114430 | May 2010 | JP |
| 2011-049364 | Mar 2011 | JP |
| 2011-159771 | Aug 2011 | JP |
| 2011-187579 | Sep 2011 | JP |
| Entry |
|---|
| Japanese Office Action issued Jul. 2, 2013 for corresponding Japanese Appln. No. 2011-274256. |
| Number | Date | Country | |
|---|---|---|---|
| 20130156060 A1 | Jun 2013 | US |