Patent Application
20230330774
The present disclosure relates to a laser processing method and a laser processing apparatus.
A laser processing method in which a material layer is irradiated with laser light to impart compressive residual stress to an object has been described. In a laser processing method described in Patent Literature 1, an absorbing material layer is formed such that a thickness of the absorbing material layer is a predetermined thickness in order to impart a uniform compressive residual stress to an object.
However, it is difficult to impart a uniform compressive residual stress to an object along an objective area on a surface of the object by simply forming an absorbing material layer such that a thickness of the absorbing material layer is a predetermined thickness, as in the laser processing method described in Patent Literature 1.
An object of the present disclosure is to provide a laser processing method and a laser processing apparatus capable of curbing variation in compressive residual stress imparted to an object along an objective area on a surface of the object.
According to an aspect of the present disclosure, there is provided a laser processing method for imparting compressive residual stress to an object along an objective area on a surface of the object by irradiating the objective area with laser light, the method including: a first step of expanding an area irradiated with the laser light toward a first side in the objective area; and a second step of expanding the area irradiated with the laser light toward a second side different from the first side in the objective area.
In this laser processing method, in the first step, the area irradiated with the laser light is expanded toward the first side, and in the second step, the area irradiated with the laser light is expanded toward the second side different from the first side. Accordingly, the compressive residual stress imparted to the object in the first step decreases toward the first side, and the compressive residual stress imparted to the object in the second step decreases toward the second side different from the first side. Therefore, for example, the variation in the compressive residual stress imparted to the object is curbed in the first step and the second step as compared with the case where the area irradiated with the laser light is expanded toward the first side in the first step and the area irradiated with the laser light is expanded toward the first side in the second step. Therefore, according to this laser processing method, it is possible to curb the variation in the compressive residual stress imparted to the object along the objective area on the surface of the object.
In the laser processing method according to the aspect of the present disclosure, the first side and the second side may be sides opposite each other in a first direction. Accordingly, it is possible to more reliably curb the variation in the compressive residual stress imparted to the object in the first step and the second step.
In the laser processing method according to the aspect of the present disclosure, in the first step, a first process of moving an irradiation spot of the laser light along each of a plurality of lines extending in a second direction perpendicular to the first direction and arranged in the first direction may be sequentially executed from the second side to the first side to expand the area irradiated with the laser light toward the first side, and in the second step, a second process of moving the irradiation spot of the laser light along each of a plurality of lines extending in the second direction and arranged in the first direction may be sequentially executed from the first side to the second side to expand the area irradiated with the laser light toward the second side. Accordingly, in the first step, the area irradiated with the laser light can be reliably and easily expanded toward the first side, and in the second step, the area irradiated with the laser light can be reliably and easily expanded toward the second side different from the first side.
In the laser processing method according to the aspect of the present disclosure, in the first step, as the first process, a process of moving the irradiation spot of the laser light from one side to the other side in the second direction and a process of moving the irradiation spot of the laser light from the other side to the one side in the second direction may be alternately executed, and in the second step, as the second process, a process of moving the irradiation spot of the laser light from the one side to the other side in the second direction and a process of moving the irradiation spot of the laser light from the other side to the one side in the second direction may be alternately executed. Accordingly, in the first step, the area irradiated with the laser light can be efficiently expanded toward the first side, and in the second step, the area irradiated with the laser light can be efficiently expanded toward the second side different from the first side.
The laser processing method according to the aspect of the present disclosure may further include: a third step of expanding the area irradiated with the laser light toward a third side in the objective area; and a fourth step of expanding the area irradiated with the laser light toward a fourth side different from the third side in the objective area, wherein the third side and the fourth side may be sides opposite each other in a second direction perpendicular to the first direction. Accordingly, it is possible to more reliably curb the variation in the compressive residual stress imparted to the object along the objective area on the surface of the object.
In the laser processing method according to the aspect of the present disclosure, in the third step, a third process of moving the irradiation spot of the laser light along each of a plurality of lines extending in the first direction and arranged in the second direction may be sequentially executed from the fourth side to the third side to expand the area irradiated with the laser light toward the third side, and in the fourth step, a fourth process of moving the irradiation spot of the laser light along each of a plurality of lines extending in the first direction and arranged in the second direction may be sequentially executed from the third side to the fourth side to expand the area irradiated with the laser light toward the fourth side. Accordingly, in the third step, the area irradiated with the laser light can be reliably and easily expanded toward the third side, and in the fourth step, the area irradiated with the laser light can be reliably and easily expanded toward the fourth side different from the third side.
In the laser processing method according to the aspect of the present disclosure, in the third step, as the third process, a process of moving the irradiation spot of the laser light from one side to the other side in the first direction and a process of moving the irradiation spot of the laser light from the other side to the one side in the first direction may be alternately executed, and in the fourth step, as the fourth process, a process of moving the irradiation spot of the laser light from the one side to the other side in the first direction and a process of moving the irradiation spot of the laser light from the other side to the one side in the first direction may be alternately executed. Accordingly, in the third step, the area irradiated with the laser light can be efficiently expanded toward the third side, and in the fourth step, the area irradiated with the laser light can be efficiently expanded toward the fourth side different from the third side.
According to another aspect of the present disclosure, there is provided a laser processing apparatus for imparting compressive residual stress to an object along an objective area on a surface of the object by irradiating the objective area, the apparatus including: a support part configured to support the object; an irradiation part configured to irradiate the objective area with the laser light; and a control part configured to control an operation of at least one of the support part and the irradiation part, wherein the control part controls an operation of at least one of the support part and the irradiation part such that an area irradiated with the laser light expands toward a first side in the objective area, and controls an operation of at least one of the support part and the irradiation part such that the area irradiated with the laser light expands toward a second side different from first side in the objective area.
According to this laser processing apparatus, as in the laser processing method described above, it is possible to curb the variation in the compressive residual stress imparted to the object along the objective area on the surface of the object.
According to the present disclosure, it is possible to provide a laser processing method and a laser processing apparatus capable of curbing variation in compressive residual stress imparted to an object along an objective area on a surface of the object.
Hereinafter, an embodiment of the present disclosure will be described in detail with reference to the drawings. The same or corresponding parts in the drawings are denoted with the same reference signs, and repetitive description will be omitted.
As shown in
The support part 2 supports the object 10 such that the surface 10a of the object 10 is orthogonal to the Z direction. The support part 2 includes, for example, a clamp that clamps the object 10, a robot arm, and the like. The object 10 is, for example, a plate-shaped member made of a metal material such as copper, aluminum, iron, or titanium. A protective layer P is formed on the objective area 11 when the laser peening processing is performed. A confinement layer C is formed on a surface of the protective layer P. The protective layer P is a layer that absorbs heat generated by the irradiation of the objective area 11 with the laser light L in order to protect the objective area 11 from the heat. The protective layer P is, for example, a metal or resin layer. The confinement layer C is a layer that confines plasma generated by the irradiation of the objective area 11 with the laser light L in order to give an impact of the plasma to the object 10. The confinement layer C is, for example, water supplied in order to cover the protective layer P.
The irradiation part 3 irradiates the objective area 11 on the surface 10a of the object 10 supported by the support part 2 with the laser light L. The irradiation part 3 two-dimensionally moves an irradiation spot S of the laser light L with respect to the objective area 11. The irradiation spot S of the laser light L is an irradiation region of the laser light L in the objective area 11. In the present embodiment, a convergence spot CS of the laser light L is positioned on the objective area 11. That is, in the present embodiment, the convergence spot CS of the laser light L becomes the irradiation spot S of the laser light L.
The irradiation part 3 has a light source 31, an optical axis adjusting part 32, an optical axis adjusting lens 33, an X-axis movable mirror 34, a Y-axis movable mirror 35, and an objective lens 36. The light source 31 emits the laser light L. The light source 31 is, for example, a semiconductor laser that emits the laser light L by a pulse oscillation method. The optical axis adjusting part 32 supports the optical axis adjusting lens 33. The optical axis adjusting part 32 moves the optical axis adjusting lens 33 in the Z direction to move the convergence spot CS in the Z direction. The X-axis movable mirror 34 adjusts an inclination of a mirror surface that reflects the laser light L to move the convergence spot CS in the X direction. The Y-axis movable mirror 35 adjusts an inclination of a mirror surface that reflects the laser light L to move the convergence spot CS in the Y direction. Each of the X-axis movable mirror 34 and the Y-axis movable mirror 35 is, for example, a galvanomirror. The objective lens 36 optically corrects a position of the convergence spot CS of the laser light L such that the convergence spot CS is positioned on a plane perpendicular to the Z direction. The objective lens 36 is, for example, an f·θ lens.
The control part 4 controls an operation of the irradiation part 3 such that the irradiation spot S moves in the objective area 11 along a predetermined trajectory. The control part 4 has, for example, a processing part 41, a storage part 42, and an input reception part 43. The processing part 41 is configured as a computer device including a processor, a memory, a storage, a communication device, and the like. In the processing part 41, the processor executes software (a program) read from the memory or the like and controls reading and writing of data in the memory and the storage, and communication of a communication device. The storage part 42 is a hard disk or the like and stores various types of data. The input reception part 43 is an interface that receives an input of various types of data from an operator. In the present embodiment, the input reception part 43 constitutes a graphical user interface (GUI).
A laser processing method executed in the laser processing apparatus 1 described above will be described. The laser processing method is a method in which the objective area 11 on the surface 10a of the object 10 is irradiated with the laser light L to impart the compressive residual stress to the object 10 along the objective area 11. That is, the laser processing method is a method in which the laser peening processing is performed on the objective area 11 on the surface 10a of the object 10. In the present embodiment, the control part 4 controls the irradiation part 3 to execute a first step, a second step, a third step, and a fourth step, which will be described below. As an example, in the first step, the second step, the third step, and the fourth step, an output of the laser light L and an area and a shape of the irradiation spot S are constant.
First, the object 10 is prepared. According to the present embodiment, in the laser processing apparatus 1, the object 10 is supported by the support part 2, and the objective area 11, irradiation conditions of the laser light L, and the like are set by the control part 4. In the present embodiment, as shown in (a) of
Subsequently, in the objective area 11, an area 12 irradiated with the laser light L is expanded toward the first side (the first step), and the irradiated area 12 is expanded over all the objective area 11. Specifically, in the objective area 11, a first process of moving the irradiation spot S along each of a plurality of lines L1 extending in the Y direction and arranged at regular intervals in the X direction is sequentially executed from the second side to the first side to expand the irradiated area 12 toward the first side. In the present embodiment, as the first process, a process of moving the irradiation spot S from the third side to the fourth side (from one side to the other side in the second direction) and a process of moving the irradiation spot S from the fourth side to the third side (from the other side to the one side in the second direction) are alternately executed. The interval between the adjacent lines L1 is about ½ of the width of the irradiation spot S in the X direction.
Subsequently, as shown in (b) of
Subsequently, as shown in (a) of
Subsequently, as shown in (b) of
As described above, by executing the first step, the second step, the third step, and the fourth step, the compressive residual stress is imparted to the object 10 along the objective area 11. In other words, the above laser processing method is a method for manufacturing the object to which the compressive residual stress is imparted along the objective area 11. In the above laser processing method, the irradiation with the laser light L only has to be executed such that “at least a portion of the irradiated area 12 expanded in the first step,” “at least a portion of the irradiated area 12 expanded in the second step,” “at least a portion of the irradiated area 12 expanded in the third step,” and “at least a portion of the irradiated area 12 expanded in the fourth step” overlap each other in the objective area 11. In other words, in the above laser processing method, an area in which the irradiation with the laser light L is executed such that “at least a portion of the irradiated area 12 expanded in the first step,” “at least a portion of the irradiated area 12 expanded in the second step,” “at least a portion of the irradiated area 12 expanded in the third step,” and “at least a portion of the irradiated area 12 expanded in the fourth step” overlap each other is the objective area 11.
In the above laser processing method, in the first step, the area 12 irradiated with the laser light L is expanded toward the first side, and in the second step, the area 12 irradiated with the laser light L is expanded toward the second side. Accordingly, the compressive residual stress imparted to the object 10 in the first step decreases toward the first side, and the compressive residual stress imparted to the object 10 in the second step decreases toward the second side. Furthermore, in the third step, the area 12 irradiated with the laser light L is expanded toward the third side, and in the fourth step, the area 12 irradiated with the laser light L is expanded toward the fourth side. Accordingly, the compressive residual stress imparted to the object 10 in the third step decreases toward the third side, and the compressive residual stress imparted to the object 10 in the fourth step decreases toward the fourth side. Therefore, variation in the compressive residual stress imparted to the object 10 is curbed as compared with a case where the area 12 irradiated with the laser light L is expanded toward the first side in each of the first step, the second step, the third step, and the fourth step, for example. Therefore, according to the above laser processing method, it is possible to curb the variation in the compressive residual stress imparted to the object 10 along the objective area 11 on the surface 10a of the object 10.
In the above laser processing method, the first side and the second side are sides opposite each other in the X direction, and the third side and the fourth side are sides opposite each other in the Y direction. Accordingly, it is possible to more reliably curb the variation in the compressive residual stress imparted to the object 10.
In the above laser processing method, in the first step, the first process of moving the irradiation spot S of the laser light L along each of the plurality of lines L1 extending in the Y direction and arranged in the X direction is sequentially executed from the second side to the first side to expand the area 12 irradiated with the laser light L toward the first side. Accordingly, in the first step, the area 12 irradiated with the laser light L can be reliably and easily expanded toward the first side. In the above laser processing method, in the second step, the second process of moving the irradiation spot S of the laser light L along each of the plurality of lines L2 extending in the Y direction and arranged in the X direction is sequentially executed from the first side to the second side to expand the area 12 irradiated with the laser light L toward the second side. Accordingly, in the second step, the area 12 irradiated with the laser light L can be reliably and easily expanded toward the second side different from the first side.
In the above laser processing method, in the first step, as the first process, the process of moving the irradiation spot S of the laser light L from one side to the other side in the Y direction and the process of moving the irradiation spot S of the laser light L from the other side to the one side in the Y direction are alternately executed. Accordingly, in the first step, the area 12 irradiated with the laser light L can be efficiently expanded toward the first side. In the above laser processing method, in the second step, as the second process, the process of moving the irradiation spot S of the laser light L from one side to the other side in the Y direction and the process of moving the irradiation spot S of the laser light L from the other side to the one side in the Y direction are alternately executed. Accordingly, in the second step, the area 12 irradiated with the laser light L can be efficiently expanded toward the second side different from the first side.
In the above laser processing method, in the third step, the third process of moving the irradiation spot S of the laser light L along each of the plurality of lines L3 extending in the X direction and arranged in the Y direction is sequentially executed from the fourth side to the third side to expand the area 12 irradiated with the laser light L toward the third side. Accordingly, in the third step, the area 12 irradiated with the laser light L can be reliably and easily expanded toward the third side. In the above laser processing method, in the fourth step, the fourth process of moving the irradiation spot S of the laser light L along each of the plurality of lines L4 extending in the X direction and arranged in the Y direction is sequentially executed from the third side to the fourth side to expand the area 12 irradiated with the laser light L toward the fourth side. Accordingly, in the fourth step, the area 12 irradiated with the laser light L can be reliably and easily expanded toward the fourth side different from the third side.
In the above laser processing method, in the third step, as the third process, the process of moving the irradiation spot S of the laser light L from one side to the other side in the X direction and the process of moving the irradiation spot S of the laser light L from the other side to the one side in the X direction are alternately executed. Accordingly, in the third step, the area 12 irradiated with the laser light L can be efficiently expanded toward the third side. In the above laser processing method, in the fourth step, as the fourth process, the process of moving the irradiation spot S of the laser light L from one side to the other side in the X direction and the process of moving the irradiation spot S of the laser light L from the other side to the one side in the X direction are alternately executed. Accordingly, in the fourth step, the area 12 irradiated with the laser light L can be efficiently expanded toward the fourth side different from the third side.
According to the above laser processing apparatus 1, as in the laser processing method described above, it is possible to curb the variation in the compressive residual stress imparted to the object 10 along the objective area 11 on the surface 10a of the object 10.
First, laser processing methods of Comparative Example 1, Comparative Example 2, Comparative Example 3, and Comparative Example 4 will be described. Irradiation conditions of the laser light in the laser processing methods of Comparative Example 1, Comparative Example 2, Comparative Example 3, and Comparative Example 4 are as follows.
Wavelength: 1053 nm
Pulse energy: 300 mJ
Pulse width: 10 ns (rectangular)
Converged light size: about 0.8×0 8 mm
Intensity: 4.7 GW/cm2
Repetition frequency: 2 Hz
Material: aluminum alloy (A2024)
Shape: 49×49 mm
Thickness: 3 mm
Objective area: 2×10 mm
Protective layer: resin tape (thickness: 100 μm or less)
Confinement layer: flowing water
In the laser processing method of Comparative Example 1, as shown in (a) of
In the laser processing method of Comparative Example 2, as shown in (b) of
In the laser processing method of Comparative Example 3, as shown in (a) of
In the laser processing method of Comparative Example 4, as shown in (b) of
A two-dimensional distribution of compressive residual stress imparted by the laser processing method of each of Comparative Example 1, Comparative Example 2, Comparative Example 3, and Comparative Example 4 was measured by an X-ray residual stress measurement apparatus. The conditions for measuring the two-dimensional distribution of the compressive residual stress are as follows.
X-ray size: φ 0.5 mm
Measuring range: 3×4 mm
Interval: 0.25 mm
Tube: Co
In the two-dimensional distribution of the compressive residual stress imparted by the laser processing method of Comparative Example 1, the compressive residual stress decreases from one side to the other side in the X direction, as shown in (a) of
In the two-dimensional distribution of the compressive residual stress imparted by the laser processing method of Comparative Example 2, the compressive residual stress decreases from one side to the other side in the X direction in a half area of the objective area on the one side in the X direction, as shown in (b) of
In the two-dimensional distribution of the compressive residual stress imparted by the laser processing method of Comparative Example 3, the compressive residual stress decreases from the other side to one side in the X direction in a half area of the objective area on the one side in the X direction, as shown in (a) of
In the two-dimensional distribution of the compressive residual stress imparted by the laser processing method of Comparative Example 4, the compressive residual stress decreases from one side to the other side in the X direction in a half area of the objective area on the one side in the X direction, as shown in (b) of
From the above results, it was demonstrated that the compressive residual stress imparted to the object decreases toward the side on which the area irradiated with the laser light expands in the objective area. Further, it was demonstrated that the distribution of the compressive residual stress imparted to the object varies even if the area irradiated with the laser light expands randomly from a sparse state to a dense state in the objective area.
Next, laser processing methods of Comparative Example 5, Example 1, and Example 2 will be described. Irradiation conditions of the laser light in the laser processing methods of Comparative Example 5, Example 1, and Example 2 are as follows.
Wavelength: 1064 nm
Pulse energy: 42 mJ
Pulse width: 39.4 ns (Gaussian)
Converged light size: φ 0.19 mm
Intensity: 3.8 GW/cm2
Repetition frequency: 300 Hz
Material: aluminum alloy (A2024)
Shape: 49×49 mm
Thickness: 3 mm
Objective area: 3×3 mm
Protective layer: aluminum tape (thickness: 100 μm or less)
Confinement layer: flowing water
In the laser processing method of Comparative Example 5, a step of expanding the area irradiated with the laser light from one side toward the other side in the X direction in the objective area (a step corresponding to the first step in the laser processing method of the above embodiment) was executed four times.
In the laser processing method of Example 1, a step of expanding the area irradiated with the laser light from one side toward the other side in the X direction in the objective area (a step corresponding to the first step in the laser processing method of the above embodiment) and a step of expanding the area irradiated with the laser light from the other side toward the one side in the X direction in the objective area (a step corresponding to the second step in the laser processing method of the above embodiment) were alternately executed two times.
In the laser processing method of Example 2, a step of expanding the area irradiated with the laser light from one side toward the other side in the X direction in the objective area (a step corresponding to the first step in the laser processing method of the above embodiment), a step of expanding the area irradiated with the laser light from the other side toward the one side in the X direction in the objective area (a step corresponding to the second step in the laser processing method of the above embodiment), a step of expanding the area irradiated with the laser light from one side toward the other side in the Y direction in the objective area (a step corresponding to the third step in the laser processing method of the above embodiment), and a step of expanding the area irradiated with the laser light from the other side toward the one side in the Y direction in the objective area (a step corresponding to the fourth step in the laser processing method of the above embodiment) were executed one time in that order.
A two-dimensional distribution of compressive residual stress imparted by the laser processing method of each of Comparative Example 5, Example 1, and Example 2 was measured by an X-ray residual stress measurement apparatus. The conditions for measuring the two-dimensional distribution of the compressive residual stress are as follows.
X-ray size: φ 0.5 mm
Measuring range: 5.0×2.5 mm
Interval: 0.25 mm
Tube: Co
In the two-dimensional distribution of the compressive residual stress imparted along the objective area by the laser processing method of Comparative Example 5, the compressive residual stress decreases from one side to the other side in the X direction, as shown in (a) of
The present disclosure is not limited to the embodiment and the examples described above. A laser processing method of Modification Example 1 will be described. In the laser processing method of the Modification Example 1, as shown in (a) of
A laser processing method of Modification Example 2 will be described. In the laser processing method of Modification Example 2, the objective area 11 is divided into a plurality of areas, and the laser processing method of the above embodiment is executed in each of the plurality of areas. For example, as shown in
In the laser processing apparatus 1 of the above embodiment, the control part 4 controls the operation of the irradiation part 3 such that the irradiation spot S moves in the objective area 11 along the predetermined trajectory, but the control part 4 only has to control the operation of at least one of the support part 2 and the irradiation part 3. For example, the control part 4 may control the operation of the support part 2 such that the irradiation spot S moves in the objective area 11 along the predetermined trajectory. Alternatively, the control part 4 may control the operations of the support part 2 and the irradiation part 3 such that the irradiation spot S moves in the objective area 11 along the predetermined trajectory.
In the laser processing method of the above embodiment, in the first step and the second step, the process of moving the irradiation spot S from the third side to the fourth side and the process of moving the irradiation spot S from the fourth side to the third side are alternately executed, but in the first step and the second step, the process of moving the irradiation spot S from the third side to the fourth side and the process of moving the irradiation spot S from the fourth side to the third side may be performed consecutively.
In the laser processing method of the above embodiment, in the third step and the fourth step, the process of moving the irradiation spot S from the first side to the second side and the process of moving the irradiation spot S from the second side to the first side are alternately executed, but in the third step and the fourth step, the process of moving the irradiation spot S from the second side to the first side and the process of moving the irradiation spot S from the first side to the second side may be performed consecutively.
In the laser processing method of the above embodiment, the lines L2 match the lines L1, but, if the plurality of lines L2 extend in the Y direction and are arranged in the X direction, the lines L2 may not match the lines L1. Similarly, in the laser processing method of the above embodiment, the lines L4 match the lines L3, but, if the plurality of lines L4 extend in the X direction and are arranged in the Y direction, the lines L4 may not match the lines L3.
In the laser processing method of the above embodiment, the plurality of lines L1 are arranged at regular intervals, but the plurality of lines L1 may not be arranged at regular intervals. Similarly, in the laser processing method of the above embodiment, the plurality of lines L2 are arranged at regular intervals, but the plurality of lines L2 may not be arranged at regular intervals. Similarly, in the laser processing method of the above embodiment, the plurality of lines L3 are arranged at regular intervals, but the plurality of lines L3 may not be arranged at regular intervals. Similarly, in the laser processing method of the above embodiment, the plurality of lines L4 are arranged at regular intervals, but the plurality of lines L4 may not be arranged at regular intervals.
In the laser processing method of the above embodiment, the interval between the adjacent lines L1 is about ½ of the width of the irradiation spot S in the X direction, but the interval between the adjacent lines L1 may be larger than ½ of the width of the irradiation spot S in the X direction. That is, there may be a region between the adjacent lines L1 that is not irradiated with the laser light L two times. The interval between the adjacent lines L1 is preferably smaller than ½ of the width of the irradiation spot S in the X direction. That is, a portion between the adjacent lines L1 is preferably irradiated with the laser light L two times or more. Furthermore, the interval between the adjacent lines L1 is preferably ½ of the width of the irradiation spot S in the X direction. That is, a portion between the adjacent lines L1 is preferably irradiated with the laser light L two times without overlapping. In this case, the irradiated area 12 uniformly irradiated with the laser light L can be expanded toward the first side.
Similarly, in the laser processing method of the above embodiment, the interval between the adjacent lines L2 is about ½ of the width of the irradiation spot S in the X direction, but the interval between the adjacent lines L2 may be larger than ½ of the width of the irradiation spot S in the X direction. That is, there may be a region between the adjacent lines L2 that is not irradiated with the laser light L two times. The interval between the adjacent lines L2 is preferably smaller than ½ of the width of the irradiation spot S in the X direction. That is, a portion between the adjacent lines L2 is preferably irradiated with the laser light L two times or more. Furthermore, the interval between the adjacent lines L2 is preferably ½ of the width of the irradiation spot S in the X direction. That is, a portion between the adjacent lines L2 is preferably irradiated with the laser light L two times without overlapping. In this case, the irradiated area 12 uniformly irradiated with the laser light L can be expanded toward the second side.
Similarly, in the laser processing method of the above embodiment, the interval between the adjacent lines L3 is about ½ of the width of the irradiation spot S in the Y direction, but the interval between the adjacent lines L3 may be larger than ½ of the width of the irradiation spot S in the Y direction. That is, there may be a region between the adjacent lines L3 that is not irradiated with the laser light L two times. The interval between the adjacent lines L3 is preferably smaller than ½ of the width of the irradiation spot S in the Y direction. That is, a portion between the adjacent lines L3 is preferably irradiated with the laser light L two times or more. Furthermore, the interval between the adjacent lines L3 is preferably ½ of the width of the irradiation spot S in the Y direction. That is, a portion between the adjacent lines L3 is preferably irradiated with the laser light L two times without overlapping. In this case, the irradiated area 12 uniformly irradiated with the laser light L can be expanded toward the third side.
Similarly, in the laser processing method of the above embodiment, the interval between the adjacent lines L4 is about ½ of the width of the irradiation spot S in the Y direction, but the interval between the adjacent lines L4 may be larger than ½ of the width of the irradiation spot S in the Y direction. That is, there may be a region between the adjacent lines L4 that is not irradiated with the laser light L two times. The interval between the adjacent lines L4 is preferably smaller than ½ of the width of the irradiation spot S in the Y direction. That is, a portion between the adjacent lines L4 is preferably irradiated with the laser light L two times or more. Furthermore, the interval between the adjacent lines L4 is preferably ½ of the width of the irradiation spot S in the Y direction. That is, a portion between the adjacent lines L4 is preferably irradiated with the laser light L two times without overlapping. In this case, the irradiated area 12 uniformly irradiated with the laser light L can be expanded toward the fourth side.
In the laser processing method of the above embodiment, the first process of moving the irradiation spot S of the laser light L along each of the plurality of lines L1 is sequentially executed from the second side to the first side, but the process may not be sequentially executed. For example, the first process may be executed from the second side to the first side while some lines among the plurality of lines L1 are skipped, and a process of moving the irradiation spot S of the laser light L along the skipped some lines may be executed after the first process. Similarly, in the laser processing method of the above embodiment, the second process of moving the irradiation spot S of the laser light L along each of the plurality of lines L2 is sequentially executed from the first side to the second side, but the process may not be sequentially executed. For example, the second process may be executed from the first side to the second side while some lines among the plurality of lines L2 are skipped, and a process of moving the irradiation spot S of the laser light L along the skipped some lines may be executed after the second process.
In the laser processing method of the above embodiment, the third process of moving the irradiation spot S of the laser light L along each of the plurality of lines L3 is sequentially executed from the fourth side to the third side, but the process may not be sequentially executed. For example, the third process may be executed from the fourth side to the third side while some lines among the plurality of lines L3 are skipped, and a process of moving the irradiation spot S of the laser light L along the skipped some lines may be executed after the third process. Similarly, in the laser processing method of the above embodiment, the fourth process of moving the irradiation spot S of the laser light L along each of the plurality of lines L4 is sequentially executed from the third side to the fourth side, but the process may not be sequentially executed. For example, the fourth process may be executed from the third side to the fourth side while some lines among the plurality of lines L4 are skipped, and a process of moving the irradiation spot S of the laser light L along the skipped some lines may be executed after the fourth process.
In the laser processing method of the above embodiment, the steps are executed in the order of the first step, the second step, the third step, and the fourth step, but the order of executing the steps may be changed. Specifically, the steps may be executed in the order of the first step, the third step, the second step, and the fourth step. Alternatively, the steps may be executed in the order of the first step, the third step, the fourth step, and the second step.
In the laser processing method of the above embodiment, the third step and the fourth step are executed, but at least the first step and the second step only have to be executed. Also in this case, since the area 12 irradiated with the laser light L can be expanded toward two different sides, it is possible to curb the variation in the compressive residual stress imparted to the object 10 along the objective area 11. In a case where only the first step and the second step are executed, the irradiation with the laser light L only has to be executed such that “at least a portion of the irradiated area 12 expanded in the first step” and “at least a portion of the irradiated area 12 expanded in the second step” overlap each other in the objective area 11. In other words, in a case where only the first step and the second step are executed, an area in which the irradiation with the laser light L is executed such that “at least a portion of the irradiated area 12 expanded in the first step” and “at least a portion of the irradiated area 12 expanded in the second step” overlap each other is the objective area 11.
In the laser processing method of the above embodiment, the first side and the second side are sides opposite each other in the X direction, but the first side and the second side only have to be sides opposite each other in a predetermined direction. Furthermore, the first side and the second side only have to be sides different from each other. If the first side and the second side are different from each other, it is possible to curb the variation in the compressive residual stress imparted to the object 10 in the first step and the second step as compared with the case where the area 12 irradiated with the laser light L is expanded toward the first side in the second step. In a case where each of the first side and the second side is represented by a vector having the same magnitude, an angle formed by a vector indicating the first side (that is, a vector directed to the first side) and a vector indicating the second side (that is, a vector directed to the second side) is preferably greater than 90 degrees and less than or equal to 180 degrees. That is, it is preferable that the vector indicating the first side and the vector indicating the second side have vector components opposite each other in a predetermined direction. In this case, it is possible to curb the variation in the compressive residual stress imparted to the object 10 along the objective area 11 in the predetermined direction. For reference, the case where the angle formed by the vector indicating the first side and the vector indicating the second side is 180 degrees is the case where the first side and the second side face each other.
In the laser processing method of the above embodiment, the third side and the fourth side are sides opposite each other in the Y direction, but the third side and the fourth side only have to be sides opposite each other in a predetermined direction. Furthermore, the third side and the fourth side only have to be sides different from each other. If the third side and the fourth side are different from each other, it is possible to curb the variation in the compressive residual stress imparted to the object 10 in the third step and the fourth step as compared with the case where the area 12 irradiated with the laser light L is expanded toward the third side in the fourth step. In a case where each of the third side and the fourth side is represented by a vector having the same magnitude, an angle formed by a vector indicating the third side (that is, a vector directed to the third side) and a vector indicating the fourth side (that is, a vector directed to the fourth side) is preferably greater than 90 degrees and less than or equal to 180 degrees. That is, it is preferable that the vector indicating the third side and the vector indicating the fourth side have vector components opposite each other in a predetermined direction. In this case, it is possible to curb the variation in the compressive residual stress imparted to the object 10 along the objective area 11 in the predetermined direction. For reference, the case where the angle formed by the vector indicating the third side and the vector indicating the fourth side is 180 degrees is the case where the third side and the fourth side face each other.
The objective area 11 is not limited to a flat surface and may be a curved surface. The objective area 11 is not limited to a rectangle and may have another shape such as a circle. Each of the line L1, the line L2, the line L3, and the line L4 is not limited to a straight line and may be a curved line.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2020-159829 | Sep 2020 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2021/025328 | 7/5/2021 | WO |