The present invention relates to a porous surface and a method for forming the same, which uses a directed energy beam to selectively remelt a powder to produce a part. In particular, this invention relates to a computer-aided laser apparatus, which sequentially remelts a plurality of powder layers to build the designed part in a layer-by-layer fashion. The present application is particularly directed toward a method of forming a porous and partially porous metallic structure.
The field of free-form fabrication has seen many important recent advances in the fabrication of articles directly from computer controlled databases. These advances, many of which are in the field of rapid prototyping of articles such as prototype parts and mold dies, have greatly reduced the time and expense required to fabricate articles, particularly in contrast to conventional machining processes in which a block of material, such as a metal, is machined according to engineering drawings.
One example of a modern rapid prototyping technology is the selective laser sintering process practiced by systems available from DTM Corporation of Austin, Tex. According to this technology, articles are produced in layer-wise fashion from a laser-fusible powder that is dispensed one layer at a time. The powder is fused, remelted or sintered, by the application of laser energy that is directed in raster-scan fashion to portions of the powder layer corresponding to a cross section of the article. After the fusing of the powder in each layer, an additional layer of powder is dispensed, and the process repeated, with fused portions or lateral layers fusing so as to fuse portions of previous laid layers until the article is complete. Detailed descriptions of the selective laser sintering technology may be found in U.S. Pat. Nos. 4,863,538, 5,017,753, 5,076,869 and 4,944,817, all assigned to Board of Regents, the University of Texas. Quasi-porous structures have also been developed in the form of regular and irregular lattice arrangements in which individual elements (column and connecting cross-members) are constructed singularly from a pre-defined computer-aided design model of the external geometry and lattice structure. The selective laser remelting and sintering technologies have enabled the direct manufacture of solid or dense three-dimensional articles of high resolution and dimensional accuracy from a variety of materials including wax, metal powders with binders, polycarbonate, nylon, other plastics and composite materials, such as polymer-coated metals and ceramics.
The field of the rapid prototyping of parts has, in recent years, made large improvements in broadening high strain, high density, parts for use in the design and pilot production of many useful articles, including metal parts. These advances have permitted the selective laser remelting and sintering processes to now also be used in fabricating prototype tooling for injection molding, with expected tool life in access of ten thousand mold cycles. The technologies have also been applied to the direct fabrication of articles, such as molds, from metal powders without a binder. Examples of metal powder reportedly used in such direct fabrication include two-phase metal powders of the copper-tins, copper-solder (the solder being 70% led and 30% tin), and bronze-nickel systems. The metal articles formed in these ways have been quite dense, for example, having densities of up to 70% to 80% of fully dense (prior to any infiltration). Prior applications of this technology have strived to increase the density of the metal structures formed by the remelting or sintering processes. The field of rapid prototyping of parts has focused on providing high strength, high density, parts for use and design in production of many useful articles, including metal parts.
However, while the field of rapid prototyping has focused on increasing density of such three-dimensional structures, the field has not focused its attention on reducing the density of three-dimensional structures. Consequently, applications where porous and partially porous metallic structures, and more particularly metal porous structures with interconnected porosity, are advantageous for use have been ignored. It is an object of this invention to use a laser and powder metal to form pores in structures in which pores are irregular in size and have a controlled total porosity. It is a further object to produce porous tissue in growth surfaces with interconnected porosity with uniform pores and porosity.
The present invention relates to a method for producing a three-dimensional porous structure particularly for use with tissue ingrowth. In one embodiment of the present invention, a layer of metallic powder is deposited onto a substrate or a build platform. Preferred metals for the powder include titanium, titanium alloys, stainless steel, cobalt chrome alloys, tantalum or niobium. A laser beam with predetermined settings scans the powder layer causing the powder to preferentially remelt and consequently solidify with a decreased density, resulting from an increase in porosity as compared to a solid metal. The range of the laser's power may be between 5 W and 1000 W. After the first layer of powder has been completed, successive offset layering and remelting are continued until the porous part has been successfully completed. In this embodiment, the benefit of the part formed is that that decreased density increases porosity thus enabling the part to be used for, among other things, tissue ingrowth.
In a second embodiment, the first layer of metallic powder is deposited onto a solid base or core and fused thereto. Preferred metals used for the core include titanium, titanium alloys, stainless steel, cobalt chrome alloys, tantalum and niobium. Successive powder layers of the same or different materials are once again added in a layer-by-layer fashion until the part is completed. This embodiment has the desired effect of providing a structure in which the porosity may be increased as the structure is built, resulting in a graded profile in which the mechanical properties will also be reduced outwards from the core. This will allow the formed part to be used for, among other things, medical implants and prosthesis, but yet still include a surface for tissue ingrowth.
The method of producing a three-dimensional porous tissue ingrowth structure may include depositing a first layer of a powder made from a metal selected from the group consisting of titanium, titanium alloys, stainless steel, cobalt chrome alloys, tantalum and niobium, onto a substrate. Followed by scanning a laser beam at least once over the first layer of powder. The laser beam having a power (P) in Joule per seconds with a scanning speed (v) in millimeters per second with a range between 80 and 400 mms. and a beam overlap (b) in millimeters of between 50% and −1200%. Such that the number calculated by the formula P/(b×v) lies between the range 0.3-8 J/mm2.
At least one additional layer of powder is deposited and then the laser scanning steps for each successive layer are repeated until a desired web height is reached. In a second embodiment, during the step of repeating the laser scanning steps, at least one laser scan is carried out angled relative to another laser scan in order to develop an interconnecting or non-interconnecting porosity.
The thickness of the first layer and said successive layers of powder is between 5 μm-2000 μm. The laser can be applied either continuously or in a pulse manner, with the frequency of the pulse being in the range of approximately 1 KHz to 50 KHz. Preferably, the method is carried out under an inert atmosphere, more preferably specifically an Argon inert atmosphere.
In order to achieve a greater mechanical strength between the base or core and the first layer of powder a third metal may be used to act as an intermediate. The third metal would act as a bond coat between the core and first layer of powder. Additionally the core may be integral with the resultant porous ingrowth structure and impart additional physical properties to the overall construct. The core may also be detachable from the resultant porous surface buildup.
It is the object of the present invention to provide a method of fabricating porous and partially porous metallic structures with a known porosity for use in particularly but not exclusively hard or soft tissue interlock structures or medical prosthesis.
These and other objects are accomplished by a process of fabricating an article in which laser-directed techniques are used to produce a porous three-dimensional structure with interconnected porosity and predetermined pore density, pore size and pore-size distribution. The article is fabricated, in the example of remelting, by using a laser and varying either the power of the laser, the layer thickness of the powder, laser beam diameter, scanning speed of the laser or overlap of the beam. In fabricating a three-dimensional structure, the powder can be either applied to a solid base or not. The article is formed in layer-wise fashion until completion.
Methods of forming the porous surface of the present invention can be performed in many ways and some embodiments will now be described by way of example and with reference to the accompanying drawings in which:
a-f are examples of typical waffle structures.
The present invention relates to a method of forming porous and partially porous metallic structures which are particularly but not exclusively applicable for use in hard or soft tissue interlock structures for medical implants and prosthesis. The method makes use of laser technology by employing a variety of scanning strategies. Typical metal and metal alloys employed include stainless steel, cobalt chromium alloys, titanium and its alloys, tantalum and niobium, all of which have been used in medical device applications. The present invention can be used for such medical device applications where bone and soft tissue interlock with a component is required, or where a controlled structure is required to more closely match the mechanical properties of the device with surrounding tissue. Additionally, the present invention may be employed to enhance the biocompatibility of a porous structure with animal tissue. With these advantages in mind, a structure may be created using specific dimensions required to accommodate a particular patient.
One particular intention of the present invention is to produce a three-dimensional structure using a direct laser remelt process, for example, for building structures with or without a solid base or core. When applied to an orthopedic prosthesis, the three-dimensional structure could be used to provide a porous outer layer to form a bone in-growth structure. Alternatively, the porous structure, when applied to a core, could be used to form a prosthesis with a defined stiffness to both fulfill the requirement of a modulus match with surrounding tissue and provide interconnected porosity for tissue interlock. A further use could be to form an all-porous structure with grade pore size to interact with more than one type of tissue. Again, the process can be used to build on a solid base or core with an outer porous surface, the porosity of which is constant or which varies. The base or core materials to which the process is applied is either titanium and its alloys, stainless steel, cobalt chrome alloys, tantalum or niobium. The preferred surface coatings are titanium, cobalt chrome and tantalum but both stainless steel and niobium can also be used. Fully porous structures may be built from any of the materials tested, with the preferred material being titanium. One intention of the present invention is to produce a method which can be exploited on a commercial basis for the production of, for example, bone interlock surfaces on a device although it has many other uses.
According to the present invention, a method of forming a three-dimensional structure includes building the shape by laser melting powdered titanium and titanium alloys, stainless steel, cobalt chrome alloys, tantalum or niobium. The laser may be a continuous wave or pulsed laser beam.
The method can be performed so that the structure is porous and if desired, the pores can be interconnecting to provide an interconnected porosity.
If desired, the method can include using a base or core of cobalt chrome alloy, titanium or alloy, stainless steel, niobium and tantalum, on which to build a porous layer of any one of the aforementioned metals and alloys by laser melting using a continuous or pulsed laser beam. Thus, a mixture of desired mixed materials may be employed.
Thus, the method can be applied to an existing article made from cobalt chrome, titanium or titanium alloys, stainless steel, tantalum or niobium, such as an orthopedic implant, to produce a porous outer layer from any of the aforementioned metals or alloys to provide a bone in-growth structure.
Preferably, prior to the deposition of any powder onto a substrate, a cleaning operation to ensure a contaminant-free surface may be employed. Typically, this process may include a solvent wash followed by a cleaning scan of the laser beam without the presence of particles.
In order to increase the mechanical bond between a substrate i.e., core or base, and a first layer of deposited powder a coating process may be employed. The coating process includes applying a third metal directly to the substrate, which has a higher bond strength to the substrate then does the first layer of powder. This process is particularly useful when the substrate and first powder layer are of different materials. The process of coating the substrate may be accomplished using known processes including laser deposition, plasma coating, cold gas dynamic spraying or similar techniques. One example of the coating process includes using either niobium or tantalum as an interface between a cobalt chrome alloy substrate and a first layer of titanium powder.
The present invention can also include a laser melting process, which precludes the requirement for subsequent heat treatment of the structure, thereby preserving the initial mechanical properties of the core or base metal.
The present invention may be applied to produce an all-porous structure using any of the aforementioned metal or metal alloys. Such structures can be used as finished product or further processed to form a useful device for either bone or soft tissue in-growth. Additionally, the structure may be used to serve some other function such as that of a lattice to carry cells.
The pore density, pore size and pore size distribution can be controlled from one location on the structure to another. It is important to note that successive powder layers can differ in porosity by varying factors used for laser scanning powder layers. As for example, a first layer of powder is placed and subsequently scanned. Next a second layer of powder is placed and scanned. In order to control porosity the second scan may be angled relative to the first scan. Additionally, the angling of the scanning as compared to previous and post scans may be maneuvered and changed many times during the process of building a porous structure. If a structure was built without alternating the angling of any subsequent scans you would produce a structure having a plurality of walls rather than one with an interconnecting or non-interconnecting porosity.
In one such method, the laser melting process includes scanning the laser beam onto the powder in parallel scan lines with a beam overlap i.e., scan spacing, followed by similar additional scans or subsequent scans at 90°. The type of scan chosen may depend on the initial layer thickness as well as the web height required. Web height refers to the height of a single stage of the porous structure. The web height may be increased by deposited additional layers of powder of a structure and scanning the laser at the same angle of the previous scan.
Further, the additional scan lines may be at any angle to the first scan, to form a structure with the formation of a defined porosity, which may be regular or random. The scan device may be programmed to proceed in a random generated manner to produce an irregular porous construct but with a defined level of porosity. Furthermore, the scan can be pre-programmed using digitized images of various structures, such as a trabecular bone, to produce a similar structure. Contrastingly, the scan may be pre-programmed using the inverse of digitized images, such as the inverse of a digitized trabecular bone to produce trabecular shaped voids. Many other scanning strategies are possible, such as a waffle scan, all of which can have interconnecting porosity if required.
The beam overlap or layer overlap may be achieved by rotation of the laser beam, the part being produced, or a combination of both.
A first method according to the present invention is intended to produce a porous structure for bone in-growth on the outer surface layer of a prosthesis.
To produce a porous surface structure, the nature of the material formed as a result of laser melting of powdered beads is principally dependent on the thermal profile involved (heating rate, soaking time, cooling rate); the condition of the raw material (size and size distribution of powder particles); atmospheric conditions (reducing, inert or oxidizing chamber gas); and accurate control of the deposited layer thickness.
There have been a number of studies to determine the optimum pore structure for maximization of bone in-growth on prostheses. The general findings suggest that optimum porosity is between approximately 20% and 40%, and aim to mid value with a mean volume percent of voids of about 70%. The preferred pore structure is irregular and interconnected, with a minimum pore size between about 80 μm and 100 μm and a maximum pore size between 80 μm and 800 μm. The structured thickness for in-growth is 1.4-1.6 mm, but can be larger or smaller depending on the application. As for example, it may be necessary to produce even smaller pore sizes for other types of tissue interaction or specific cellular interaction.
The first phase of development of the present invention involved an investigation, designed to characterize the material transformation process and to identify the optimum parameters for processing using three substrate materials CoCr and Ti stainless steel alloys, with five powder types Ti, CoCr, Ta and Nb, stainless steel.
The initial Direct Laser Remelting trials explored a comprehensive range of process parameters during the production of a number of coated base substrates. Results from this task were evaluated using laser scanning and white light interferometry in order to define the range of process parameters that produced the optimum pore structure.
Referring to
The build chamber 24 illustrated in
Preliminary experiments were performed on CoCr alloy to determine the efficacy of in-situ laser cleaning of the substrate. Typical processing conditions were: Laser power of 82 W, pulse frequency of 30 KHz, and a laser scan speed of 160 mm/sec.
Preliminary experiments were performed on CoCr to assess the environment conditions within the chamber. In these examples, Co212-e Cobalt Chrome alloy was used. The CoCr was configured into square structures, called coupons. Arrays of CoCr coupons were built onto a stainless steel substrate. The Co212-e Cobalt Chrome alloy had a particle size distribution of 90<22 um, i.e., 90% of the particles are less than 22 μm, the composition of which is shown in the table below.
An array of nine sample coupons were produced as shown in
The incremental changes in scanning speed and the size of the speed range were modified as the experiments progressed. To begin with, a large range of speeds was used to provide an initial indication of the material's performance and the propensity to melt. As the experiments progressed, the range was reduced to more closely define the process window. Speed and beam overlap variations were used to modify the specific energy density being applied to the powder bed and change the characteristics of the final structure. The complete series of parameters are given in
CoCr was the first of four powders to be examined and, therefore, a wide range of process parameters was used. In each case, laser power and the pulse repetition rate were kept constant, i.e., continuous laser pulse, to allow the two remaining parameters to be compared. Layer thickness was maintained at 100 μm throughout all the experiments described here. Layer thickness can, however, vary between 5 μm to 2000 μm.
On completion of the initial series of experiments using CoCr powder on 2.5 mm thick stainless steel substrates, basic optical analysis was conducted of the surface of the coupons to ascertain the size of the pores and degree of porosity being obtained. Once a desired pore size was obtained and the coupons had suitable cohesion, the two experiments closest to the optimum desired pore size were repeated using first CoCr and then Ti substrates. The same structure could be obtained by other parameters.
Following the conclusion of the CoCr experiments, the remaining three powders; Niobium, Tantalum and Titanium were investigated in turn. The procedure followed a simple course although fewer parameter sets were explored as the higher melting points of these materials forced the reduction in speeds compared to CoCr powder.
For Niobium, the particle size description was 80%<75 μm at a purity of 99.85%. Due to its higher melting temperature compared to that of CoCr (Nb being at about 2468° C., and CoCr being at about 1383° C.), the laser parameters used included a reduced scanning speed range and increased beam overlap providing increased specific energy density at the powder bed. In addition, the pulse repetition rate was varied from 20 kHz to 50 kHz.
On completion of a small number (four in total) of preliminary experiments of Nb on stainless steel substrate, the experiment with the most ideal parameters was repeated on both the CoCr and Ti substrates.
The Tantalum used in this study had a particular size distribution of 80%<75 μm with a purity of 99.85%. Ta has a melting point of about 2996° C. and was processed using the same laser parameters as Nb. Now confident of the atmospheric inertness, the Ta powder was melted directly onto the CoCr and Ti substrates.
Bio-medical alloys of Titanium were not readily available in powder form and so pure Ti was chosen. The particle size distribution for the Ti powder was 80%<45 μm with a purity of 99.58%. The same parameters used for Nb and Ta were also used for the Ti powder. Ti has a lower melting point than Ta or Nb, Ti being at about 1660° C., but has a higher thermal conductivity than Ta or Nb. This implies that although the powder should require less energy before melting, the improved heat transfer means a larger portion of the energy is conducted away from the melt pool.
Following the completion of samples with all four powders on the required substrates, surface analysis was conducted using optical analysis and a scanning electron microscope to obtain images of the resultant pores. Porosity was calculated using a simple image processing technique involving the setting of contrast thresholds and pixel counting. While this technique is not the most accurate method, it allows the rapid analysis of small samples produced. Techniques such as Xylene impregnation would yield more accurate results but they are time consuming and require larger samples than those produced here.
Following an extended series of experimentation, two sets of laser processing parameters were selected for the laser melting of CoCr powder. From analysis of the stainless steel substrates, it was seen that a large portion of the results fell within the pore size required for these materials, stated as being in the range of 80 μm to 400 μm.
Optical analysis of the surface structure of each of the coupons produced with CoCr on CoCr and Ti alloy substrates were initially viewed but due to problems with the depth of field associated with an optical microscope, little information could be extracted. In addition to the coupons that were produced to satisfy the project requirements, two experiments were conducted using a relatively large negative beam overlap of −250 and −500%. Optical images of the coupon's surface and in section are shown in
To provide a clearer indication of the pore size and pore density, the optical analysis was repeated using images obtained from the scanning electron microscope.
a) to 7(c) are scanning election microscope images of the surface structure of Ta on Ti alloy substrates produced using the same parameters used in the Nb or Ti alloy substrates except:
a) to 8(e) are scanning electron microscope images taken from the Ti coupons on the CoCr alloy substrates. The laser processing parameters used were the same as those for the Nb and Ta powders, with once again only the speed varying. The scanning speed was varied from 160 mms−1 (
a) to 9(e) are scanning electron microscope images of surface structures of Ti on Ti alloy substrates produced with the same parameters used in
Following the completion of the multi-layer coupons, a series of 20 mm×20 mm structures were produced from Ti that utilized an X and Y-direction “waffle” scanning format using the optimum Ti operating parameters with the two scans being orthogonal to one another. The intention behind these experiments was to demonstrate the ability of the Direct Laser Remelting process to produce parts with a controlled porosity, e.g. internal channels of dimensions equal to the required pore size, e.g. 80 μm to 400 μm. To do this, a relatively large beam overlap of between −400% and −600% was used. Scanning electron microscope images of the surfaces of these structures are shown in
To illustrate more clearly the interaction between the substrate/structure metallurgical interaction, the Ti on Ti substrate was sectioned, hot mounted and polished using a process of 1200 and 2500 grade SiC, 6 μm diamond paste and 70/30 mixture of OPS and 30% H2O2. The polished sample was then etched with 100 ml H2O, 5 ml NH.FHF and 2 cm3 HCl for 30 seconds to bring out the microstructure. Optical images of this sample in section are shown in
From the optical and scanning election microscope analysis conducted, it is apparent that the Direct Laser Remelting process is capable of satisfying the requirements for pore characteristics, concerning maximum and minimum pore size, interconnectivity and pore density. From the initial visual analysis of the CoCr coupons, it was apparent from these and other examples, that subtle variations in pore structure and coverage could be controlled by scanning velocity and line spacing.
The key laser parameters varied for forming the three-dimensional metallic porous structures are: (a) Laser scanning speed (v.) in (mms−1), which controls the rate at which the laser traverses the powder bed; (b) Laser power, P(W), which in conjunction with the laser spot size controls the intensity of the laser beam. The spot size was kept constant throughout the experiment; (c) Frequency, (Hz) or pulse repetition rate. This variable controls the number of laser pulses per second. A lower frequency delivers a higher peak power and vice versa.
The line width can be related to the laser scanning speed and the laser power to provide a measure of specific density, known as the “Andrew Number”, where:
Where P denotes the power of the laser, v is the laser scanning speed and b denotes beam width of the laser. The Andrew number is the basis for the calculation of the present invention. The Andrew number may also be calculated by substituting the line separation (d) for beam width (b). The two methods of calculating the Andrew number will result in different values being obtained. When using line separation (d) as a factor only on track of fused powder is considered, whereas when using the beam width (b) as a factor, two tracks of fused powder are considered as well as the relative influence of one track to the next. For this reason we have chosen to concern ourselves with the Andrew number using scan spacing as a calculating factor. It can thus be appreciated, that the closer these tracks are together the greater the influence they have on one another.
Additionally, the laser power may be varied between 5 W and 1000 W. Utilizing lower power may be necessary for small and intricate parts but would be economically inefficient for such coatings and structures described herein. It should be noted that the upper limit of laser power is restricted because of the availability of current laser technology. However, if a laser was produced having a power in excess of 1000 W, the scanning speed of the laser could be increased in order that an acceptable Andrew number is achieved. A spot size having a range between 5 um(fix) to 500 um(fix) is also possible. For the spot size to increase while still maintaining an acceptable Andrew number, either the laser power must be increased or the scanning speed decreased.
The above formula gives an indication of how the physical parameters can vary the quantity of energy absorbed by the powder bed. That is, if the melted powder has limited cohesion, e.g. insufficient melting, the parameters can be varied to concentrate the energy supply to the powder. High Andrew numbers result in reduced pore coverage and an increase in pore size due to the effects of increased melt volume and flow. Low Andrew numbers result in low melt volume, high pore density and small pores. Current satisfactory Andrew numbers are approximately 0.3 J/mm−2 to 8 J/mm−2 and are applicable to many alternative laser sources. It is possible to use a higher powered laser with increased scanning speed and obtain an Andrew number within the working range stated above.
Line spacing or beam overlap can also be varied to allow for a gap between successive scan lines. It is, therefore, possible to heat selected areas. This gap would allow for a smaller or larger pore size to result. The best illustration of this is shown in
The use of an optical inspection method to determine this approximate porosity is appropriate given the sample size. This method, although not accurate due to the filter selection process, can, if used carefully, provide an indication of porosity. An average porosity level of around 25% was predicted. This porosity level falls within the range of the desired porosity for bone in-growth structures. The mechanical characteristics of the porous structures are determined by the extent of porosity and the interconnecting webs. A balance of these variables is necessary to achieve the mechanical properties required by the intended application.
Increased fusion may, if required, be obtained by heating the substrate, powder or both prior to scanning. Such heating sources are commonly included in standard selective laser sintering/melting machines to permit this operation.
Following trials on the titanium build on the cobalt chromium substrate, it was determined that the interface strength was insufficient to serve the intended application. Trials were made by providing a bond coat of either tantalum or niobium on the cobalt chromium substrate prior to the deposition of the titanium layers to for the porous build. The typical protocol involved:
A typical waffle build of titanium on a titanium substrate was constructed as a way of regulating the porous structure. Scanning sequences of 0° 0°0°, 90° 90° 90°, 45° 45° 45°, 135°, 135°, 135°, of layer thickness 0, 1 mm were developed to form a waffle. Three layers of each were necessary to obtain sufficient web thickness in the “z” direction to give a structure of adequate strength. Typical parameters employed were: Laser power was 82 watts, operating frequency between 0 (cw) and 40 KHz, scan speed of between 160 and 240 mm/sec with a beam overlap of −700%.
Trabecular structures of titanium on a titanium substrate were constructed as a way of randomising the porous structures. An STL (sterolithography) file representing trabecular structure was produced from a micro CT scan of trabecular bone. This file was sliced and the slice data sent digitally to the scanning control. This allowed the layer-by-layer building of a metallic facsimile to be realised.
A method for making lattice-type constructs was referred to in the relevant art. A typical example of this type of structure is shown in
‘First
The second and preferred approach uses a continuous scanning strategy whereby the pores are developed by the planar deposition of laser melted powder tracks superimposed over each other. This superimposition combined with the melt flow produces random and pseudorandom porous structures. The properties of the final structure, randomness, interconnectivity, mechanical strength and thermal response are controlled by the process parameters employed. One set of scanning parameters used was: Scanning sequences of 0° 0°0°, 90° 90° 90°, 45° 45° 45°, 135°, 135°, 135°, of layer thickness 0.1 mm were developed to form a waffle. Three layers of each were necessary to obtain sufficient web thickness in the “z” direction. The array of sequences was repeated many times to give a construct of the desired height. Laser power was 82 watts, operating frequency between 0 (cw) and 40 KHz, scan speed of between 160 and 240 mm/sec with a beam overlap of −700%.
The use of an optical inspection method to determine this approximate porosity is appropriate given the sample size. This method, although not accurate due to the filter selection process, can, if used carefully, provide an indication of porosity. An average porosity level of around 25% was predicted. This porosity level falls within the range of the desired porosity for bone in-growth structures.
In consideration of the potential application, it is important to minimize loose surface contamination and demonstrate the ability to fully clean the surface. Laser cleaning or acid etching technique may be effective. Additionally, a rigorous cleaning protocol to remove all loose powder may entail blowing the porous structure with clean dry compressed gas, followed by a period of ultrasonic agitation in a treatment fluid. Once dried, a laser scan may be used to seal any remaining loose particles.
On examination, all candidate materials and substrates were selectively fused to produce a complex interconnected pore structure. There were small differences in certain process parameters such as speed and beam overlap percentage. From
The non-contact surface profilimeotry (OSP) images shown in
a) shows Ti on CoCr (Single Layer; SEM Micrograph) v=160 mms−1;
b) shows Ti on CoCr (Single Layer; SEM Micrograph) v=160 mms−1;
a) shows Ti on CoCr (Single Layer; SEM Micrograph) v=170 mms−1;
b) shows Ti on CoCr (Single Layer; SEM Micrograph) v=180 mms−1;
a) shows Ti on CoCr (Single Layer; SEM Micrograph) v=190 mms−1;
b) shows Ti on CoCr (Single Layer; SEM Micrograph) v=200 mms−1;
a) shows Ti on CoCr (Single Layer; SEM Micrograph) v=210 mms−1;
b) shows Ti on CoCr (Single Layer; SEM Micrograph) v=220 mms−1;
a) shows Ti on CoCr (Single Layer; SEM Micrograph) v=230 mms−1;
b) shows Ti on CoCr (Single Layer; SEM Micrograph) v=240 mms−1;
a) shows Ti on Ti (Single Layer; SEM Micrograph) v=160 mms−1;
b) shows Ti on Ti (Single Layer; SEM Micrograph) v=170 mms−1;
a) shows Ti on Ti (Single Layer; SEM Micrograph) v=190 mms−1;
b) shows Ti on Ti (Single Layer; SEM Micrograph) v=200 mms−1;
a) shows Ti on Ti (Single Layer; SEM Micrograph) v=220 mms−1;
b) shows Ti on Ti (Single Layer; SEM Micrograph) v=230 mms−1;
a) shows Ti on Ti (Single Layer; SEM Micrograph) v=240 mms−1;
b) shows Ti on Ti (Single Layer; SEM Micrograph) v=240 mms−1;
The method according to the present invention can produce surface structures on all powder/baseplate combinations with careful selection of process parameters.
As described above, the process is carried out on flat baseplates that provide for easy powder delivery in successive layers of around 100 μm thickness. Control of powder layer thickness is very important if consistent surface properties are required. The application of this technology can also be applied to curved surfaces such as those found in modern prosthetic devices; with refinements being made to the powder layer technique.
The structures have all received ultrasonic and aqueous cleaning. On close examination, the resultant porous surfaces produced by the Direct Laser Remelting process exhibit small particulates that are scattered throughout the structure. It is unclear at this stage whether these particulates are bonded to the surface or loosely attached but there are means to remove the particulates if required.
The Direct Laser Remelting process has the ability to produce porous structures that are suitable for bone in-growth applications. The powdered surfaces have undergone considerable thermal cycling culminating in rapid cooling rates that have produced very fine dendritic structures (e.g.
The Direct Laser Remelting process can produce effective bone in-growth surfaces and the manufacturing costs are reasonable.
In the preceding examples, the object has been to provide a porous structure on a base but the present invention can also be used to provide a non-porous structure on such a base to form a three-dimensional structure. The same techniques can be utilized for the materials concerned but the laser processing parameters can be appropriately selected so that a substantially solid non-porous structure is achieved.
Again, a technique can be used to deposit the powder onto a suitable carrier, for example a mold, and to carry out the process without the use of a base so that a three-dimensional structure is achieved which can be either porous, as described above, or non-porous if required.
It will be appreciated that this method can, therefore, be used to produce article from the metals referred to which can be created to a desired shape and which may or may not require subsequent machining. Yet again, such an article can be produced so that it has a graded porosity of, e.g., non-porous through various degrees of porosity to the outer surface layer. Such articles could be surgical prostheses, parts or any other article to which this method of production would be advantageous.
This application claims the benefit of U.S. Provisional Application No. 60/424,923 filed on Nov. 8, 2002, and U.S. Provisional Application No. 60/425,657 filed on Nov. 12, 2002, the disclosures of which are incorporated by reference herein.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3520099 | Mattes | Jul 1970 | A |
| 3556918 | Lemelson | Jan 1971 | A |
| 3605123 | Hahn | Sep 1971 | A |
| 3806961 | Muller | Apr 1974 | A |
| 3816855 | Saleh | Jun 1974 | A |
| 3826054 | Culpepper, Jr. | Jul 1974 | A |
| 4047349 | Aguilar, Jr. | Sep 1977 | A |
| 4085466 | Goodfellow et al. | Apr 1978 | A |
| 4154040 | Pace | May 1979 | A |
| 4164794 | Spector et al. | Aug 1979 | A |
| 4202055 | Reiner et al. | May 1980 | A |
| 4218494 | Belmondo et al. | Aug 1980 | A |
| 4344193 | Kenny | Aug 1982 | A |
| 4385404 | Sully et al. | May 1983 | A |
| 4444818 | Tominaga et al. | Apr 1984 | A |
| 4502161 | Wall | Mar 1985 | A |
| 4513045 | Bondoc et al. | Apr 1985 | A |
| 4543158 | Bondoc et al. | Sep 1985 | A |
| 4636219 | Pratt et al. | Jan 1987 | A |
| 4644942 | Sump | Feb 1987 | A |
| 4673408 | Grobbelaar | Jun 1987 | A |
| 4719908 | Averill et al. | Jan 1988 | A |
| 4766029 | Brock et al. | Aug 1988 | A |
| 4863538 | Deckard | Sep 1989 | A |
| 4944817 | Bourell et al. | Jul 1990 | A |
| 4961154 | Pomerantz et al. | Oct 1990 | A |
| 4969302 | Coggan et al. | Nov 1990 | A |
| 4969907 | Koch et al. | Nov 1990 | A |
| 4990163 | Ducheyne et al. | Feb 1991 | A |
| 5004476 | Cook | Apr 1991 | A |
| 5017753 | Deckard | May 1991 | A |
| 5031120 | Pomerantz et al. | Jul 1991 | A |
| 5034186 | Shimamune et al. | Jul 1991 | A |
| 5053090 | Beaman et al. | Oct 1991 | A |
| 5067964 | Richmond et al. | Nov 1991 | A |
| 5076869 | Bourell et al. | Dec 1991 | A |
| 5090174 | Fragale | Feb 1992 | A |
| 5147402 | Bohler et al. | Sep 1992 | A |
| 5155324 | Deckard et al. | Oct 1992 | A |
| 5158574 | Stone | Oct 1992 | A |
| 5176710 | Hahn et al. | Jan 1993 | A |
| 5192328 | Winters | Mar 1993 | A |
| 5219362 | Tuke et al. | Jun 1993 | A |
| 5282870 | Moser et al. | Feb 1994 | A |
| 5287435 | Cohen et al. | Feb 1994 | A |
| 5314478 | Oka et al. | May 1994 | A |
| 5358529 | Davidson | Oct 1994 | A |
| 5368602 | de la Torre | Nov 1994 | A |
| 5386500 | Pomerantz et al. | Jan 1995 | A |
| 5425210 | Zafir et al | Jun 1995 | A |
| 5443510 | Shetty et al. | Aug 1995 | A |
| 5443518 | Insall | Aug 1995 | A |
| 5461839 | Beck | Oct 1995 | A |
| 5490962 | Cima et al. | Feb 1996 | A |
| 5496372 | Hamamoto et al. | Mar 1996 | A |
| 5514183 | Epstein et al. | May 1996 | A |
| 5526627 | Beck | Jun 1996 | A |
| 5571185 | Schug et al | Nov 1996 | A |
| 5571196 | Stein | Nov 1996 | A |
| 5609646 | Field et al. | Mar 1997 | A |
| 5616294 | Deckard | Apr 1997 | A |
| 5640667 | Freitag et al. | Jun 1997 | A |
| 5681354 | Eckhoff | Oct 1997 | A |
| 5702448 | Buechel et al. | Dec 1997 | A |
| 5728162 | Eckhoff | Mar 1998 | A |
| 5729946 | Beck | Mar 1998 | A |
| 5735903 | Li et al. | Apr 1998 | A |
| 5776201 | Colleran et al. | Jul 1998 | A |
| 5782908 | Cahalan et al. | Jul 1998 | A |
| 5795353 | Felt | Aug 1998 | A |
| 5824098 | Stein | Oct 1998 | A |
| 5824102 | Buscayret et al. | Oct 1998 | A |
| 5839247 | Beck | Nov 1998 | A |
| 5857303 | Beck et al. | Jan 1999 | A |
| 5879387 | Jones et al. | Mar 1999 | A |
| 5928285 | Bigliani et al. | Jul 1999 | A |
| 5987838 | Beck | Nov 1999 | A |
| 5989472 | Ashby et al. | Nov 1999 | A |
| 6046426 | Jeantette et al. | Apr 2000 | A |
| 6087553 | Cohen et al. | Jul 2000 | A |
| 6096043 | Techiera et al. | Aug 2000 | A |
| 6128866 | Wearne | Oct 2000 | A |
| 6132468 | Mansmann | Oct 2000 | A |
| 6139585 | Li | Oct 2000 | A |
| 6164032 | Beck | Dec 2000 | A |
| 6190407 | Ogle et al. | Feb 2001 | B1 |
| 6206924 | Timm | Mar 2001 | B1 |
| 6206927 | Fell et al. | Mar 2001 | B1 |
| 6215093 | Meiners et al. | Apr 2001 | B1 |
| 6248131 | Felt et al. | Jun 2001 | B1 |
| 6251143 | Schwartz et al. | Jun 2001 | B1 |
| 6280478 | Richter et al. | Aug 2001 | B1 |
| 6283997 | Garg et al. | Sep 2001 | B1 |
| 6299645 | Ogden | Oct 2001 | B1 |
| 6355086 | Brown et al. | Mar 2002 | B2 |
| 6370382 | Kang et al. | Apr 2002 | B1 |
| 6371958 | Overaker | Apr 2002 | B1 |
| 6385585 | Jonsson et al. | May 2002 | B1 |
| 6395327 | Shetty | May 2002 | B1 |
| 6406497 | Takei | Jun 2002 | B2 |
| 6415574 | Beck | Jul 2002 | B2 |
| 6476343 | Keicher et al. | Nov 2002 | B2 |
| 6482209 | Engh et al. | Nov 2002 | B1 |
| 6494914 | Brown et al. | Dec 2002 | B2 |
| 6520996 | Manasas et al. | Feb 2003 | B1 |
| 6530951 | Bates et al. | Mar 2003 | B1 |
| 6558421 | Fell et al. | May 2003 | B1 |
| 6599301 | Vibe-Hansen et al. | Jul 2003 | B2 |
| 6632246 | Simon et al. | Oct 2003 | B1 |
| 6652246 | Lin et al. | Nov 2003 | B1 |
| 6652587 | Felt et al. | Nov 2003 | B2 |
| 6686437 | Buchman et al. | Feb 2004 | B2 |
| 6699252 | Farr et al. | Mar 2004 | B2 |
| 6709462 | Hanssen | Mar 2004 | B2 |
| 6712822 | Re et al. | Mar 2004 | B2 |
| 6712856 | Carignan et al. | Mar 2004 | B1 |
| 6716957 | Tunc | Apr 2004 | B2 |
| 6770099 | Andriacchi et al. | Aug 2004 | B2 |
| 6846329 | McMinn et al. | Jan 2005 | B2 |
| 6850125 | Norman et al. | Feb 2005 | B2 |
| 6855165 | Fell et al. | Feb 2005 | B2 |
| 6866684 | Fell et al. | Mar 2005 | B2 |
| 6893463 | Fell et al. | May 2005 | B2 |
| 6911044 | Fell et al. | Jun 2005 | B2 |
| 6916341 | Rolston | Jul 2005 | B2 |
| 6921264 | Mayer et al. | Jul 2005 | B2 |
| 6923831 | Fell et al. | Aug 2005 | B2 |
| 20020010512 | Takei | Jan 2002 | A1 |
| 20020015654 | Das et al. | Feb 2002 | A1 |
| 20020016635 | Despres et al. | Feb 2002 | A1 |
| 20020127328 | Shetty | Sep 2002 | A1 |
| 20020130112 | Manases et al. | Sep 2002 | A1 |
| 20020151983 | Shetty | Oct 2002 | A1 |
| 20020173855 | Mansmann | Nov 2002 | A1 |
| 20020198528 | Engh et al. | Dec 2002 | A1 |
| 20030032351 | Horner et al. | Feb 2003 | A1 |
| 20030033018 | Merchant | Feb 2003 | A1 |
| 20030045941 | Lewallen | Mar 2003 | A1 |
| 20030055500 | Fell et al. | Mar 2003 | A1 |
| 20030055501 | Fell et al. | Mar 2003 | A1 |
| 20030060882 | Fell et al. | Mar 2003 | A1 |
| 20030060883 | Fell et al. | Mar 2003 | A1 |
| 20030060884 | Fell et al. | Mar 2003 | A1 |
| 20030060885 | Fell et al. | Mar 2003 | A1 |
| 20030060888 | Fell et al. | Mar 2003 | A1 |
| 20030069718 | Hollister et al. | Apr 2003 | A1 |
| 20030153977 | Suguro et al. | Aug 2003 | A1 |
| 20030153981 | Wang et al. | Aug 2003 | A1 |
| 20030155686 | Hawkins et al. | Aug 2003 | A1 |
| 20030158606 | Coon et al. | Aug 2003 | A1 |
| 20030209305 | Smith et al. | Nov 2003 | A1 |
| 20030220696 | Levine et al. | Nov 2003 | A1 |
| 20040006393 | Burkinshaw | Jan 2004 | A1 |
| 20040023586 | Tilton | Feb 2004 | A1 |
| 20040044414 | Nowakowski | Mar 2004 | A1 |
| 20040054416 | Wyss et al. | Mar 2004 | A1 |
| 20040059356 | Gingras | Mar 2004 | A1 |
| 20040098132 | Andriacchi et al. | May 2004 | A1 |
| 20040121110 | Schmidt et al. | Jun 2004 | A1 |
| 20040143339 | Axelson et al. | Jul 2004 | A1 |
| 20040153163 | Posner | Aug 2004 | A1 |
| 20040162622 | Simon et al. | Aug 2004 | A1 |
| 20040167633 | Wen et al. | Aug 2004 | A1 |
| 20040191106 | O'Neill et al. | Sep 2004 | A1 |
| 20040199249 | Fell | Oct 2004 | A1 |
| 20040199250 | Fell | Oct 2004 | A1 |
| 20040204766 | Siebel | Oct 2004 | A1 |
| 20040243237 | Unwin et al. | Dec 2004 | A1 |
| 20040267363 | Fell et al. | Dec 2004 | A1 |
| 20050033424 | Fell | Feb 2005 | A1 |
| 20050043816 | Datta et al. | Feb 2005 | A1 |
| 20050085918 | Soffiati et al. | Apr 2005 | A1 |
| 20050100578 | Schmid et al. | May 2005 | A1 |
| 20050154471 | Aram et al. | Jul 2005 | A1 |
| 20050171604 | Michalow | Aug 2005 | A1 |
| 20050177169 | Fisher et al. | Aug 2005 | A1 |
| 20050192672 | Wyss et al. | Sep 2005 | A1 |
| 20060147332 | Jones et al. | Jul 2006 | A1 |
| 20070142914 | Jones et al. | Jun 2007 | A1 |
| 20070156249 | Lawrynowicz et al. | Jul 2007 | A1 |
| 20080004709 | O'Neill et al. | Jan 2008 | A1 |
| 20080050412 | Jones et al. | Feb 2008 | A1 |
| Number | Date | Country |
|---|---|---|
| 2 295 896 | Jul 2000 | CA |
| 2295896 | Jul 2000 | CA |
| 0 178 650 | Oct 1985 | EP |
| 0 178 650 | Apr 1986 | EP |
| 0 528 800 | Mar 1993 | EP |
| 0761242 | Mar 1997 | EP |
| 2218242 | Dec 2003 | RU |
| WO-2005087982 | Sep 2005 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20040191106 A1 | Sep 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60425657 | Nov 2002 | US | |
| 60424923 | Nov 2002 | US |