The present invention relates to multijunction solar cells, and in particular to high efficiency solar cells comprised of III-V semiconductor alloys.
Multijunction solar cells made primarily of III-V semiconductor alloys are known to produce solar cell efficiencies exceeding efficiencies of other types of photovoltaic materials. Such alloys are combinations of elements drawn from columns III and V of the standard Periodic Table, identified hereinafter by their standard chemical symbols, names and abbreviation. (Those of skill in the art can identify their class of semiconductor properties by class without specific reference to their column.) The high efficiencies of these solar cells make them attractive for terrestrial concentrating photovoltaic systems and systems designed to operate in outer space. Multijunction solar cells with efficiencies above 40% under concentrations equivalent to several hundred suns have been reported. The known highest efficiency devices have three subcells with each subcell consisting of a functional p-n junction and other layers, such as front and back surface field layers. These subcells are connected through tunnel junctions, and the dominant layers are either lattice matched to the underlying substrate or are grown over metamorphic layers. Lattice-matched devices and designs are desirable because they have proven reliability and because they use less semiconductor material than metamorphic solar cells, which require relatively thick buffer layers to accommodate differences in the lattice constants of the various materials. As set forth more fully in U.S. patent application Ser. No. 12/217,818, entitled “GaInNAsSb Solar Cells Grown by Molecular Beam Epitaxy,” which application is incorporated herein by reference, a layer made of GaInNAsSb material to create a third junction having a band gap of approximately 1.0 eV offers a promising approach to improving the efficiency of multijunction cells. Improvements are nevertheless to be considered on the cell described in that application.
The known highest efficiency, lattice-matched solar cells typically include a monolithic stack of three functional p-n junctions, or subcells, grown epitaxially on a germanium (Ge) substrate. The top subcell has been made of (Al)GaInP, the middle one of (In)GaAs, and the bottom junction included the Ge substrate. (The foregoing nomenclature for a III-V alloy, wherein a constituent element is shown parenthetically, denotes a condition of variability in which that particular element can be zero.) This structure is not optimal for efficiency, in that the bottom junction can generate roughly twice the short circuit current of the upper two junctions, as reported by J. F. Geisz et al., “Inverted GaInP/(In)GaAs/InGaAs triple junction solar cells with low-stress metamorphic bottom junctions,” Proceedings of the 33rd IEEE PVSC Photovoltaics Specialists Conference, 2008. This extra current capability is wasted, since the net current must be uniform through the entire stack, a design feature known as current matching.
In the disclosure of above noted U.S. patent application Ser. No. 12/217,818, it was shown that a material that is substantially lattice matched to Ge or GaAs with a band gap near 1.0 eV might be used to create a triple junction solar cell with efficiencies higher than the structure described above by replacing the bottom Ge junction with a junction made of a different material that produces a higher voltage.
In addition, it has been suggested that the use of this 1 eV material might be considered as a fourth junction to take advantage of the entire portion of the spectrum lying between 0.7 eV (the band gap for germanium) and 1.1 eV (the upper end of the range of bandgaps for the ˜1 eV layer). See for example, S. R. Kurtz, D. Myers, and J. M. Olson, “Projected Performance of Three and Four-Junction Devices Using GaAs and GaInP,” 26th IEEE Photovoltaics Specialists Conference, 1997, pp. 875-878. Ga1-xInxNyAs1-y has been identified as such a 1 eV material, but currents high enough to match the other subcells have not been achieved, see, e.g., A. J. Ptak et al., Journal of Applied Physics 98 (2005) 094501. This has been attributed to low minority carrier diffusion lengths that prevent effective photocarrier collection. Solar subcell design composed of gallium, indium, nitrogen, arsenic and various concentrations of antimony (GaInNAsSb) has been investigated with the reported outcome that antimony is helpful in decreasing surface roughness and allowing growth at higher substrate temperatures where annealing is not necessary, but the investigators reported that antimony, even in small concentrations is critical to be avoided as detrimental to adequate device performance. See Ptak et al., “Effects of temperature, nitrogen ion, and antimony on wide depletion width GaInNAs,” Journal of Vacuum Science Technology B 25(3) May/June 2007 pp. 955-959. Devices reported in that paper have short circuit currents far too low for integration into multijunction solar cells. Nevertheless, it is known that Ga1-xInxNyAs1-y-zSbz with 0.05≦x≦0.07, 0.01≦y≦0.02 and 0.02≦z≦0.06 can be used to produce a lattice-matched material with a band gap of approximately 1 eV that can provide sufficient current for integration into a multijunction solar cell. However, the voltages generated by subcells containing this material have not exceeded 0.30 V under 1 sun of illumination. See D. B. Jackrel et al., Journal of Applied Physics 101 (114916) 2007. Thus, a triple-junction solar cell with this material as the bottom subcell has been expected to be only a small improvement upon an analogous triple junction solar cell with a bottom subcell of Ge, which produces an open circuit voltage of approximately 0.25 V. See H. Cotal et al., Energy and Environmental Science 2 (174) 2009. What is needed is a material that is lattice-matched to Ge and GaAs with a band gap near 1 eV that produces an open circuit voltage greater than 0.30 V and sufficient current to match (Al)InGaP and (In)GaAs subcells. Such a material would also be advantageous as a subcell in high efficiency solar cells with 4 or more junctions.
According to the invention, an alloy composition is provided that has a bandgap of at least 0.9 eV, namely, Ga1-xInxNyAs1-y-zSbz with a low antimony (Sb) content and with enhanced indium (In) content and enhanced nitrogen (N) content as compared with known alloys of GaInNAsSb, achieving substantial lattice matching to GaAs and Ge substrates and providing both high short circuit currents and high open circuit voltages in GaInNAsSb subcells suitable for use in multijunction solar cells. The composition ranges for Ga1-xInxNyAs1-y-zSbz are 0.07≦x≦0.18, 0.025≦y≦0.04 and 0.001≦z≦0.03. These composition ranges employ greater fractions of In and N in GaInNAsSb than previously taught and allow the creation of subcells with bandgaps that are design-tunable in the range of 0.9-1.1 eV, which is the range of interest for GaInNAsSb subcells. This composition range alloy will hereinafter be denoted “low-antimony, enhanced indium-and-nitrogen GaInNAsSb” alloy. Subcells of such an alloy can be grown by molecular beam epitaxy (MBE) and should be able to be grown by metallorganic chemical vapor deposition (MOCVD), using techniques known to one skilled in the art.
The invention described herein reflects a further refinement of work described in U.S. patent application Ser. No. 12/217,818, including the discovery and identification of specific ranges of elements, i.e., a specific alloy mix of the various elements in GaInNAsSb that improve significantly the performance of the disclosed solar cells.
The invention will be better understood by reference to the following detailed description in connection with the accompanying drawings.
Low Sb, enhanced In and N GaInNAsSb subcells may also be incorporated into multijunction solar cells with four or more junctions without departing from the spirit and scope of the invention.
By way of further illustration,
To determine the effect of Sb on enhanced In and N GaInNAsSb subcell performance, various subcells of the type (12) of the structure shown in
Compressive strain improves the open circuit voltage of low Sb, enhanced In and N GaInNAsSb subcells 10, 100. More specifically, low Sb, enhanced In and N GaInNAsSb layers 220 that have a lattice constant larger than that of a GaAs or Ge substrate when fully relaxed (≦0.5% larger), and are thus under compressive strain when grown pseudomorphically on those substrates. They also give better device performance than layers with a smaller, fully relaxed lattice constant (under tensile strain).
Low Sb, enhanced In and N, compressively-strained GaInNAsSb subcells have been successfully integrated into high efficiency multijunction solar cells.
The invention has been explained with reference to specific embodiments. Other embodiments will be evident to those of ordinary skill in the art. It is therefore not intended for the invention to be limited, except as indicated by the appended claims.
This application is a continuation of U.S. application Ser. No. 14/597,621, filed on Jan. 15, 2015, which is a continuation of U.S. application Ser. No. 14/512,224, now allowed, filed on Oct. 10, 2014, which is a continuation of U.S. application Ser. No. 13/739,989, filed on Jan. 11, 2013, issued as U.S. Pat. No. 8,912,433, which is a divisional of U.S. application Ser. No. 12/749,076, filed on Mar. 29, 2010, each of which is incorporated by reference herein in its entirety.
Number | Name | Date | Kind |
---|---|---|---|
4404421 | Fraas | Sep 1983 | A |
4881979 | Lewis | Nov 1989 | A |
4935384 | Wanlass | Jun 1990 | A |
5009719 | Yoshida | Apr 1991 | A |
5016562 | Madan et al. | May 1991 | A |
5166761 | Olson et al. | Nov 1992 | A |
5223043 | Olson et al. | Jun 1993 | A |
5316593 | Olson et al. | May 1994 | A |
5342453 | Olson et al. | Aug 1994 | A |
5376185 | Wanlass | Dec 1994 | A |
5405453 | Ho et al. | Apr 1995 | A |
5689123 | Major et al. | Nov 1997 | A |
5800630 | Vilela et al. | Sep 1998 | A |
5911839 | Tsai et al. | Jun 1999 | A |
5935345 | Kuznicki | Aug 1999 | A |
5944913 | Hou et al. | Aug 1999 | A |
6150603 | Karam et al. | Nov 2000 | A |
6252287 | Kurtz et al. | Jun 2001 | B1 |
6281426 | Olson et al. | Aug 2001 | B1 |
6340788 | King et al. | Jan 2002 | B1 |
6504091 | Hisamatsu et al. | Jan 2003 | B2 |
6617618 | Sato | Sep 2003 | B2 |
6660928 | Patton et al. | Dec 2003 | B1 |
6756325 | Bour et al. | Jun 2004 | B2 |
6764926 | Takeuchi et al. | Jul 2004 | B2 |
6765238 | Chang et al. | Jul 2004 | B2 |
6787385 | Barber et al. | Sep 2004 | B2 |
6815736 | Mascarenhas | Nov 2004 | B2 |
6951819 | Iles et al. | Oct 2005 | B2 |
7071407 | Faterni et al. | Jul 2006 | B2 |
7119271 | King et al. | Oct 2006 | B2 |
7122733 | Narayanan et al. | Oct 2006 | B2 |
7122734 | Fetzer et al. | Oct 2006 | B2 |
7123638 | Leary et al. | Oct 2006 | B2 |
7126052 | Fetzer et al. | Oct 2006 | B2 |
7255746 | Johnson et al. | Aug 2007 | B2 |
7279732 | Meng et al. | Oct 2007 | B2 |
7709287 | Fatemi et al. | May 2010 | B2 |
7727795 | Stan et al. | Jun 2010 | B2 |
7807921 | Fetzer et al. | Oct 2010 | B2 |
7842881 | Comfeld et al. | Nov 2010 | B2 |
8067687 | Wanlass | Nov 2011 | B2 |
8575473 | Jones et al. | Nov 2013 | B2 |
20020000546 | Sato | Jan 2002 | A1 |
20020195137 | King et al. | Dec 2002 | A1 |
20030070707 | King et al. | Apr 2003 | A1 |
20030145884 | King et al. | Aug 2003 | A1 |
20040045598 | Narayanan et al. | Mar 2004 | A1 |
20040130002 | Weeks et al. | Jul 2004 | A1 |
20040200523 | King et al. | Oct 2004 | A1 |
20050155641 | Fafard | Jul 2005 | A1 |
20050274409 | Fetzer et al. | Dec 2005 | A1 |
20060144435 | Wanlass | Jul 2006 | A1 |
20060162768 | Wanlass et al. | Jul 2006 | A1 |
20070034853 | Robbins et al. | Feb 2007 | A1 |
20070131275 | Kinsey et al. | Jun 2007 | A1 |
20070227588 | Gossard et al. | Oct 2007 | A1 |
20080035939 | Puetz et al. | Feb 2008 | A1 |
20080149173 | Sharps | Jun 2008 | A1 |
20080245400 | Li | Oct 2008 | A1 |
20080257405 | Sharps | Oct 2008 | A1 |
20090001412 | Nagai et al. | Jan 2009 | A1 |
20090014061 | Harris et al. | Jan 2009 | A1 |
20090057721 | Miura et al. | Mar 2009 | A1 |
20090078310 | Stan et al. | Mar 2009 | A1 |
20090145476 | Fetzer et al. | Jun 2009 | A1 |
20090155952 | Stan et al. | Jun 2009 | A1 |
20090229659 | Wanlass et al. | Sep 2009 | A1 |
20090255575 | Tischler | Oct 2009 | A1 |
20090255576 | Tischler | Oct 2009 | A1 |
20090272438 | Cornfeld | Nov 2009 | A1 |
20090288703 | Stan et al. | Nov 2009 | A1 |
20100087028 | Porthouse et al. | Apr 2010 | A1 |
20100096001 | Sivananthan et al. | Apr 2010 | A1 |
20100180936 | Kim | Jul 2010 | A1 |
20100218819 | Farmer et al. | Sep 2010 | A1 |
20100282305 | Sharps et al. | Nov 2010 | A1 |
20100282306 | Sharps et al. | Nov 2010 | A1 |
20100319764 | Wiemer et al. | Dec 2010 | A1 |
20110023958 | Masson et al. | Feb 2011 | A1 |
20110114163 | Wiemer et al. | May 2011 | A1 |
20110210313 | Fuji et al. | Sep 2011 | A1 |
20110232730 | Jones et al. | Sep 2011 | A1 |
20110303268 | Tan et al. | Dec 2011 | A1 |
20120031478 | Boisvert et al. | Feb 2012 | A1 |
20120103403 | Misra et al. | May 2012 | A1 |
20120211071 | Newman et al. | Aug 2012 | A1 |
20120216858 | Jones-Albertus et al. | Aug 2012 | A1 |
20120216862 | Abou-Kandil et al. | Aug 2012 | A1 |
20120227797 | Stan et al. | Sep 2012 | A1 |
20120285526 | Jones-Albertus et al. | Nov 2012 | A1 |
20130014815 | Jones-Albertus et al. | Jan 2013 | A1 |
20130118546 | Jones-Albertus et al. | May 2013 | A1 |
20130118566 | Jones-Albertus et al. | May 2013 | A1 |
20130220409 | Jones-Albertus et al. | Aug 2013 | A1 |
Number | Date | Country |
---|---|---|
63100781 | May 1988 | JP |
06061513 | Mar 1994 | JP |
06061516 | Mar 1994 | JP |
10012905 | Jan 1998 | JP |
2010151553 | Dec 2010 | WO |
2011062886 | May 2011 | WO |
2011123164 | Oct 2011 | WO |
2012057874 | May 2012 | WO |
2012115838 | Aug 2012 | WO |
2012154455 | Nov 2012 | WO |
Entry |
---|
Bank, et al., “Molecular-beam epitaxy growth of low-threshold cw GainNAsSb lasers at 1.5 μm,” J. Vac. Sci. Technol. B 23(3), May/Jun. 2005, pp. 1337-1340. |
Bertness et al., “29.5%-Efficient GaInP/GaAs Tandem Solar Cells,” Applied Physics Letters, vol. 65, Aug. 22, 1994, pp. 989-991. |
Bhuiyan et al., InGaN Solar Cells: Present State of the Art and Important Challenges, IEEE Journal of Photovoltaics, vol. 2, No. 3, Jul. 2012, pp. 246-293. |
Cornfeld et al., “Evolution of a 2.05 eV AlGaInP Top Sub-cell for 5 and 6J-IMM Applications”, Photovoltaic Specialists Conference (PVSC), 38th IEEE, Jun. 3, 2012, p. 2788-2791. |
Cotal et al., “III-V multijunction solar cells for concentrating photovoltaics” pp. 174-192, www.rsc.org/ees, Energy and Environmental Science 2, (2009). |
Denton et al., Vergard's Law, Physics Review A, The American Physical Society, 1991, vol. 43, No. 6, p. 3161-3164. |
Ferguson et al., Nonradiative Recombination in 1.56 μm GaInNAsSb/GaNAs Quantum-Well Lasers, pp. 1-3, published online Dec. 8, 2009, Applied Physics Letters 95, 231104 (2009). |
Fewster P.F., “X-Ray Scattering From Semiconductors” Second Edition, Imperial College Press, London, 2003, Ch. 1, pp. 1-22. |
Friedman et al., “Analysis of the GaInP/GaAs/1-eV/Ge Cell and Related Structures for Terrestrial Concentration Application,” pp. 856-859, Conference Record of the Twenty-ninth IEEE Photovoltaic Specialists Conference, New Orleans, LA., May 19-24, 2002. |
Friedman et al., “Breakeven Criteria for the GaInNAs Junction in GaInP/GaAs/GaInNAs/Ge Four-junction Solar Cells”, pp. 331-344, Progress in Photovoltaics: Research and Applications. (2002). |
Friedman et al., “Analysis of Depletion-Region Collection in GaInNAs Solar Cells,” pp. 691-694, Conference Record of the Thirty-first IEEE Photovoltaic Specialists Conference, Lake Buena Vista, Florida, Jan. 3-7, 2005. |
Friedman et al., “1-eV Solar cells with GaInNAs active layer”, Journal of Crystal Growth, vol. 195, 1998, p. 409-415. |
Garcia et al., Analysis Of Tellurium As N-Type Dopant in GaInP: Doping, Diffusion, Memory Effect And Surfactant Properties, pp. 794-799, Journal of Crystal Growth 298 (2007). |
Geelen et al., Epitaxial Lift-Off GaAs Solar Cell From A Reusable GaAs Substrate, pp. 162-171, Materials Science and Engineering B45 (1997). |
Geisz et al., “Inverted GaInP / (In)GaAs / InGaAs triple-junction solar cells with low-stress metamorphic bottom junctions,” Proceedings of the 33rd IEEE PVSC Photovoltaics Specialists Conference, (2008). |
Green et al., Progress in Photovoltaics: Research and Applications 19 (2011) pp. 565-572. |
Green et al., Progress in Photovoltaics: Research and Applications 20 (2012) pp. 12-20. |
Green, “Third Generation Photovoltaics: Advanced Solar Energy Conversion,” pp. 95-109, Springer Publishing, Berlin, Germany (2003). |
Green, Do Built-in Fields Improve Solar Cell Performance? pp. 57-66, Progress in Photovoltaics: Research and Applications (2009), Published online in Wiley InterScience (www.interscience.wiley.com) on Oct. 1, 2008. |
Gu et al., “Gas Source Growth and Doping Characteristics of A1InP on GaAs” Materials Science and Engineering B 131 (2006), pp. 49-53. |
Harris Jr. et al., “Development of GainNAsSballoys: Growth, band structure, optical properties and applications,” 2007, Physics Status Solidi(b), vol. 244, Issue 8, pp. 2707-2729, Jul. 6, 2007. |
Hovel H.J., “Semiconductors and Semimetals”, Academic Press, New York, 1975, Ch. 2, pp. 8-47. |
Jackrel et al., “GaInNAsSb Solar Cells Grown by Molecular Beam Epitaxy,” pp. 1-16, IEEE 4th World Conference on Photovoltaic Energy Conversion, Waikoloa, HI, 2006. |
Jackrel et al., “GaInNAsSb Solar Cells Grown by Molecular Beam Epitaxy,” 2006. Photovoltaic Energy Conversion, Conference Record of the 2006 IEEE 4th World Conference, vol. 1, p. 783-786, May 2006. |
Jackrel et al., “Dilute nitride GainNAs and GainNAsSb solar cells by molecular beam epitaxy”, pp. 1-8, Journal of Applied Physics 101 (114916), Jun. 14, 2007. |
Janotti et. al., Mutual Passivation of Electrically Active and Isovalent Impurities in Dilute Nitrides, Physical Review Letters 100, 045505 (2008). |
King et al., “High-Voltage, Low-Current GaInP/GaInP/GaAs/GaInNAs/Ge Solar Cells” Spectrolab Inc., 2002, pp. 852-855. |
King et al., “40% Efficient Metamorphic GaInP/GaInAs/Ge Multijunction Solar Cells,” J. of Applied Physics Letters, May 4, 2007. |
Kudrawiec, “Contactless electroreflectance of GaInNAsSb/GaAs single quantum wells with indium content of 8%-32%”, Jan. 2007, Journal of Applied Physics, vol. 101, pp. 013504-1-013504-9. |
Kurtz et al., “Projected Performance of Three and Four-Junction Devices Using GaAs and GaInP,” pp. 875-878, 26th IEEE Photovoltaics Specialists Conference, (1997). |
Kurtz et al., “Understanding the potential and limitations of dilute nitride alloys for solar cells”, Paper No. NREL/CP-520-38998, DOE Solar Energy Technologies Conference, Denver, CO, Nov. 7-10, 2005, 5 pages. |
Law et al., “Future technology pathways of terrestrial III-V multijunction solar cells for concentrator photovoltaic systems”, Solar Energy Materials & Solar Cells, 2010, 94, p. 1314-1318. |
Merrill et al., Directions and Materials Challenges in High Performance Photovoltaics, Dec. 2007, JOM Energetic Thin Films, 59, 12, p. 26-30. |
Miller et al., GaAs-AlGaAs tunnel junctions for multigap cascade solar cells, Journal of Applied Physics, vol. 53, No. 1, Jan. 1982, pp. 744-748. |
Miyashita et al., Effect of Indium Composition on GaInNAsSb Solar Cells Grown by Atomic Hydrogen-Assisted Molecular Beam Epitaxy, pp. 632-635, 978-1-4244-2950@ 2009 IEEE. |
Miyashita et al., “Improvement of GaInNAsSb films fabricated by atomic hydrogen-assisted molecular beam epitaxy”, pp. 3249-3251, Journal of Crystal Growth 311, 2009. |
Ng et al., 1EV GANXAS1-X-YSBY Material For Lattice-Matched III-V Solar Cell Implementation On GaAs and Ge, pp. 76-80, (2009). |
Olson J.M. et al., “High-Efficiency III-V Multijunction Solar Cells” Handbook of Photovoltaic Science and Engineering, 1st ed.; Luque, A., Hegedus, S., Eds.; Wiley: New York, NY, USA, 2003; Chapter 9, pp. 359-411. |
Patton et al., “Development of a High Efficiency Metamorphic Triple-junction 2.1 eV/1.6 eV/1.2 eV AlGaInP/InGaAsP/InGaAs Space Solar Cell”, Conference Record of the IEEE Photovoltaic Specialists Conference, Institute of Electrical and Electronics Engineers Inc., May 19, 2002, vol. 29, p. 1027-1030. |
Ptak et al., “Effects of Temperature, Nitrogen Ions and Antimony on Wide Depletion Width GaInNAs,” pp. 955-959.J. Vac. Sci. Tech. B25(3), May/Jun. 2007 (published May 31, 2007). |
Ptak et al., “Low-acceptor-Concentration GaInNAs grown by Molecular-beam Epitaxy for High-current p-i-n solar cell applications.” J. of Applied Physics, 98.094501 (2005). |
Ptak et al., “Defects in GaInNAs: What We've Learned so Far” National Renewable Energy Laboratory NREL/CP-520-33555, May 2003, 7 pages. |
Sabnis et al., A new roadmap for space solar cells, Industry Photovoltaics, www.compoundsemiconductor.net/csc/features-details/19735471, Aug./Sep. 2012, 5 pages. |
Solar Junction Inc, “Sharp Develops Solar Cell with Word's Highest Conversion Efficiency of 35.8%” Press Release, dated Oct. 22, 2009, 3 pages. |
Volz et al., Optimization Of Annealing Conditions of (GaIn)(NAs) For Solar Cell Applications, pp. 2222-2228, Journal of Crystal Growth 310 (2008). |
Volz et al., MOVPE growth of dilute nitride III/V semiconductors using all liquid metalorganic precursors, Journal of Crystal Growth 311 (2009), pp. 2418-2526. |
E. Wesoff, “Update: Solar Junction breaking CPV efficiency records, raising $30M”, Greentech Media, Apr. 15, 2011, 4 pages. |
E. Wesoff, “CPV Roundup: SolFocus funding, 5MW order for Solar Junction, GreenVolts, Amonix”, Greentech Media, May 22, 2012, 3 pages. |
E. Wesoff, “Record 44 percent CPV efficiency from startup Solar Junction”, Greentech Media, Oct. 15, 2012, 3 pages. |
Weyers et al., “Red shift of photoluminescence and absorption in dilute GaAsN alloy layers”, Japan Journal of Applied Physics, vol. 31, Issue 7A, 1992, p. L853-L855. |
Wiemer et al., “43.5% Efficient Lattice Matched Solar Cells” Proc. SPIE 810804 (2011), 5 pages. |
Wistey et al., Nitrogen Plasma Optimization For High-Quality Dilute Nitrides, pp. 229-233, Journal of Crystal Growth, available online on Feb. 1, 2005 at http://www.sciencedirect.com. |
Wu et al., Band Anticrossing In Highly Mismatched III-V Semiconductor Alloys, pp. 860-869, Semiconductor Science and Technology 17 (2002). |
Yamaguchi et al., “Multi-junction III-V solar cells: current status and future potential”, in: Solar Energy, vol. 79, issue 1, Jul. 2005. |
Yu et. al., Mutual Passivation Of Group IV Donors And Nitrogen In Diluted GaNxAs1-x Alloys, pp. 2844-2846, Applied Physics Letters, vol. 83, No. 14 (Oct. 6, 2003). |
Yuen, “The role of antimony on properties of widely varying GaInNAsSb compositions”, Journal of Applied Physics, May 2006, vol. 99, p. 093504-1 to 093804-8. |
International Search Report and Written Opinion for PCT/US2008/008495, mailed on Apr. 6, 2009, 5 pages. |
International Preliminary Report on Patentability for PCT/US2008/008495, mailed on Jan. 12, 2010, 5 pages. |
International Search Report and Written Opinion for PCT/US2010/039534, mailed on Sep. 8, 2010, 8 pages. |
International Search Report and Written Opinion for PCT/US2010/056800, mailed on Jan. 26, 2011, 8 pages. |
International Search Report and Written Opinion for PCT/US2010/061635, mailed on Mar. 1, 2011, 7 pages. |
International Search Report and Written Opinion for PCT/US2011/036486, mailed on Aug. 25, 2011, 12 pages. |
International Preliminary Report on Patentability for PCT/US2010/056800, mailed on May 31, 2012, 6 pages. |
International Search Report and Written Opinion for PCT/US2012/036020, mailed on Aug. 14, 2012, 11 pages. |
International Search Report and Written Opinion for PCT/US2012/025307, mailed on Aug. 16, 2012, 13 pages. |
International Search Report and Written Opinion for PCT/US2013/033567, mailed on Mar. 4, 2014, 12 pages. |
Amendment, Affidavits under 37 C.F.R. §132, and Information Disclosure Statement filed Nov. 2013 for U.S. Appl. No. 13/739,989, 51 pages. |
Non-Final Office Action dated Feb. 20, 2014, for U.S. Appl. No. 13/678,389, 13 pages. |
Non-Final Office Action dated Dec. 31, 2013, for U.S. Appl. No. 13/370,500, 7 pages. |
Non-Final Office Action dated Dec. 14, 2012, for U.S. Appl. No. 13/618,496, 16 pages. |
Non-Final Office Action dated Jun. 10, 2010, for U.S. Appl. No. 12/217,818, 15 pages. |
Final Office Action dated Jan. 1, 2011, for U.S. Appl. No. 12/217,818, 15 pages. |
Non-Final Office Action dated Oct. 5, 2012, for U.S. Appl. No. 12/944,439, 15 pages. |
Final Office Action dated May 29, 2013, for U.S. Appl. No. 12/944,439, 11 pages. |
Non-Final Office Action dated Aug. 13, 2014, for U.S. Appl. No. 12/944,439, 11 pages. |
Non-Final Office Action dated Oct. 24, 2012, for U.S. Appl. No. 12/749,076, 17 pages. |
Final Office Action dated Feb. 6, 2013, for U.S. Appl. No. 13/618,496, 8 pages. |
Non-Final Office Action dated Feb. 13, 2013, for U.S. Appl. No. 12/819,534, 8 pages. |
Final Office Action dated Sep. 9, 2013, for U.S. Appl. No. 12/819,534, 13 pages. |
Non-Final Office Action dated Feb. 15, 2013, for U.S. Appl. No. 12/914,710, 14 pages. |
Final Office Action dated Sep. 6, 2013, for U.S. Appl. No. 12/914,710, 17 pages. |
Notice of Allowance dated Mar. 22, 2013, for U.S. Appl. No. 13/618,496, 8 pages. |
Non-Final Office Action dated Feb. 15, 2013, for U.S. Appl. No. 13/708,763, 23 pages. |
Notice of Allowance dated Feb. 20, 2014, for U.S. Appl. No. 13/708,763, 9 pages. |
Non-Final Office Action dated Feb. 25, 2013, for U.S. Appl. No. 13/708,791, 16 pages. |
Final Office Action dated Oct. 1, 2013, for U.S. Appl. No. 13/708,791, 15 pages. |
Final Office Action dated Feb. 26, 2014, for U.S. Appl. No. 13/739,989, 16 pages. |
Non-Final Office Action dated May 24, 2013, for U.S. Appl. No. 13/739,989, 7 pages. |
Non-Final Office Action dated Nov. 8, 2012, for U.S. Appl. No. 13/104,913, 12 pages. |
Final Office Action dated Oct. 2, 2013, for U.S. Appl. No. 13/104,913, 12 pages. |
Notice of Allowance dated Feb. 21, 2014, for U.S. Appl. No. 13/104,913, 8 pages. |
Notice of Allowance for U.S. Appl. No. 13/708,791, mailed on Oct. 31, 2014, 8 pages. |
Notice of Allowance for U.S. Appl. No. 13/370,500, mailed on Sep. 22, 2014, 10 pages. |
Notice of Allowance for U.S. Appl. No. 13/739,989, mailed on Sep. 30, 2014, 9 pages. |
Non-Final Office Action dated Mar. 21, 2014, for U.S. Appl. No. 13/442,146, 6 pages. |
Declaration Under 37 C.F.R. § 1.132 of Homan Yuen filed for U.S. Appl. No. 13/739,989 on Nov. 15, 2013, pp. 1-10. |
Declaration Under 37 C.F.R. § 1.132 of Jerry Olson filed for U.S. Appl. No. 13/739,989 on Nov. 15, 2013, pp. 1-5. |
Declaration Under 37 C.F.R. § 1.132 of Minjoo Lee filed for U.S. Appl. No. 13/739,989 on Nov. 15, 2013, pp. 1-6. |
Japanese Application No. 2012-517662, Office Action mailed on Apr. 30, 2013, 5 pages. (English translation). |
Japanese Application No. 2013-502560, Office Action mailed on May 7, 2014, 5 pages. (English translation). |
Japanese Application No. 2013-536607, Office Action mailed on Mar. 18, 2014, 6 pages. (English translation). |
Number | Date | Country | |
---|---|---|---|
20150214412 A1 | Jul 2015 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 12749076 | Mar 2010 | US |
Child | 13739989 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 14597621 | Jan 2015 | US |
Child | 14678737 | US | |
Parent | 14512224 | Oct 2014 | US |
Child | 14597621 | US | |
Parent | 13739989 | Jan 2013 | US |
Child | 14512224 | US |