This invention relates to a storage battery in which the positive electrode is fabricated from a lead-based material, the negative electrode comprises palladium, and the electrolyte is an aqueous solution of a sulfate salt.
The most common type of storage battery, found in almost every vehicle, is the lead-acid battery. This battery comprises a lead dioxide positive electrode, a lead metal negative electrode, and sulfuric acid for the electrolyte. The advantages of the lead-acid battery are numerous. It is low cost, maintenance-free, and provides dependable service over a wide temperature range.
Unfortunately, the lead-acid battery also has its drawbacks; The electrolyte, sulfuric acid, is highly corrosive. The energy density of the battery is low, thus limiting its use in mobile equipment. Finally, its operation is handicapped by the evolution of hydrogen at the negative electrode when the battery is overcharged.
Pursuant to the invention, a rechargeable battery is provided in which the positive electrode comprises lead-based material, the negative electrode comprises palladium metal, and the electrolyte is an aqueous solution of a soluble sulfate salt. Upon charging, the lead-based material is converted to lead dioxide while atomic hydrogen is absorbed by the palladium. When the battery is discharged, lead dioxide is reduced to lead monoxide or a lead (II) salt, and hydrogen from the palladium electrode is oxidized to hydrogen ions.
The soluble sulfate salt may be a salt of one of the following metals: lithium, sodium, potassium, rubidium, cesium, magnesium and aluminum. This group is not meant to be exhaustive, there being any number of additional soluble sulfates that may qualify. These salts may be used individually or in combination. For example, alum, sodium aluminum sulfate, may be used.
The description herein makes reference to the accompanying drawings wherein like reference numerals refer to like parts throughout the several views, and wherein:
The electrochemistry of the present invention is best explained by the reactions that occur at the electrodes during cycling of the cell. In the special case where the electrolyte consists of an aqueous solution of sodium sulfate, the following reactions take plate upon discharge.
At the positive electrode:
PbO2+Na2SO4+2H2O+2e−→PbSO4+2OH− (1)
and at the negative electrode:
2PdH→2Pd+2H++2e− (2)
where PbO2 is lead dioxide, Na2SO4 is sodium sulfate, H2O is water, e− is an electron, PbSO4 is lead sulfate, NaOH is sodium hydroxide, OH− is the hydroxyl ion, PdH is palladium hydride, Pd is palladium, and H+ is the hydrogen ion.
Upon charging the cell, the above reactions are reversed. Atomic hydrogen that is formed at the negative electrode is absorbed by the palladium. This metal has the unique capability of absorbing up to 900 times its own volume of hydrogen at room temperature. Whether the absorbed hydrogen is chemisorbed or forms a palladium hydride compound is not known for sure. In any case, the absorption is reversible so that on discharge, the palladium releases the hydrogen as shown in equation 2.
Any soluble sulfate can be used in the battery of the present invention. Thus, instead of the sodium salt shown by the above equations, salts of other alkali metals might be used. Although the reactions are similar for all of these salts, slight differences, as measured by cell potentials, might be observed. In addition, the solubility of the selected salt is a factor. For example, 167 gm. of cesium sulfate is dissolved in 100 ml. of water at 0° C. This result compares with a value of 7.35 gm. for potassium sulfate.
The palladium electrode can be used in pure form or alloyed with other metals. One consideration is the cost of palladium. If less expensive materials can be partially substituted for palladium, this approach will be of interest. In any case, the electrochemistry must be favorable.
Candidates for palladium alloys include the platinum group metals (PGM). Platinum, in particular, has shown catalytic properties similar to those of palladium, and it is frequently used in palladium alloys. Other than PGM, nickel is especially noteworthy. This metal shares notable properties with palladium. It is a catalyst for hydrogen oxidation, and it exhibits good resistance to corrosion.
A prototype of a functional battery is shown in
An example would be as follows: An experimental cell was fashioned from a glass jar 2½ in. diameter by 4 in. high. The positive electrode was a strip of lead 1½ in. wide by 4 in. long. The negative electrode was a rod of palladium of 99.95% purity ¼ in. diameter by 4 in. long. The electrolyte was prepared by dissolving 72.2 gm. of lithium sulfate monohydrate ACS in 200 ml. water. After charging the cell at 2.8 volts for ten minutes, an open circuit potential of 2.35 volts was realized. The cell was discharged, briefly lighting a flashlight bulb with a current of 70 milliamps.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3964927 | Villarreal-Dominguez | Jun 1976 | A |
| 4467020 | Puglisi | Aug 1984 | A |
| 7550231 | Stauffer | Jun 2009 | B2 |
| 7608361 | Stauffer | Oct 2009 | B2 |
| 7682737 | Stauffer | Mar 2010 | B2 |
| 20050233216 | Stauffer | Oct 2005 | A1 |
| 20080187830 | Stauffer | Aug 2008 | A1 |
| 20100047697 | Stauffer | Feb 2010 | A1 |
| Number | Date | Country | |
|---|---|---|---|
| 20100261053 A1 | Oct 2010 | US |