The present invention relates to a leading edge structure for aircraft wings and empennages.
Wings and empennages (vertical and horizontal) are primary structures sized in a way such as to have a rigidity and robustness suitable for the aerodynamic loads to which it can be subjected during flight, landing and takeoff. The leading edge structure of a wing and of an empennage must also be sized so as to withstand the impact with a flying object.
The so called “bird strike” test is regulated by FAR 25.631 which states that: if an aircraft suffers an impact with a bird, having a defined weight and at a predetermined speed, after such condition there must be no damage on the primary structures that could prevent the aircraft from safely landing at the nearest available airport. Since whilst flying in cruise conditions the first structural element which can potentially undergo such types of impact is the leading edge, this structure must fully comply with the aforementioned standard. In addition to the aforementioned requirement, it is necessary for the leading edge to be suitably sized so as to withstand aerodynamic loads applied to it.
The aforementioned structures are commonly designed and manufactured in a manner such as to prevent the leading edge from being pierced, and thus to avoid possible damage to the structure behind it, or, in the case in which piercing is foreseen, they are designed so that the damage is locally limited.
Conventionally, wing structures are made from aluminium (shell thicknesses generally of only a few millimetres) reinforced by transverse elements which have the main task of giving the profile its shape. In these types of structures the task of absorbing energy is carried out, apart from by the—generally curved—shape of the leading edge, it is especially carried out by its thickness. The greater the thickness, the higher the amount of energy absorbed.
Other wing structures use hybrid material such as Glare® (fibreglass and aluminium laminate) also for the leading edge. In these other structures, the energy is absorbed as well as by the curved shape of the leading edge, particularly by the coupling between fibre-glass and aluminium. Fibre-glass contributes in an important way to absorbing a substantial fraction of the elasto-plastic deformation energy due to impact; this effect is called “bridging” in the field of the materials applied to aircrafts.
The present invention has the purpose of making an improved structure for the leading edge of a wing or of an empennage, mainly tackling the problem of optimizing the rigidity of the structure, minimizing the damage caused by impact with flying objects and at the same time reducing the overall weight of the wing or of the empennage.
Now we shall describe some preferred embodiments which should not be taken to limit the invention; we refer to the attached drawings, in which:
Firstly, referring to
The leading edge structure 10 constitutes the front portion of a wing profile. The structure 10 is formed by an overlapping of a plurality of multilayer panels 20 suitably curved with concavities facing towards a direction defined as “rear” with respect to the forward direction of an aircraft.
Each multilayer panel has at least the following layers:
The intermediate layer of fibreglass 22 is connected to the adjacent layers through respective structural adhesive film layers 25. Alternatively, a self-adhesive fibreglass can be chosen.
The succession of the layers 21, 22 and 23 forming the modular panel 20 can be repeated many times depending on the design requirements. Indeed, the third honeycomb layer is securely fixed, by means of adhesives, to a subsequent aluminium foil which, in the embodiment illustrated in
Z-shaped fibreglass closing cross pieces are indicated with reference numeral 12, said cross pieces being suitable for sealing the peripheral edges of the multilayer panels 20. It is preferable to choose multilayer panels of the type having a further aluminium foil 24 for the innermost panels, so as to uninterruptedly cover the honeycomb layers 23 of the panels located in this position.
Men skilled in the art should understand that the number of overlapping curved panels 20, and thus the overall thickness of the leading edge, is variable according to the structural requirements of the wing or of the empennage to be constructed.
The aluminium foils are fundamentally used as elements for fastening the fibreglass layers. The structural characteristics of high mechanical resistance and resilience of fibreglass, intimately and securely fixed together with the metal honeycomb and with the aluminium foil, provide a bridging effect which contributes to absorbing a substantial fraction of the elasto-plastic energy of deformation caused by impact. At the same time, the invention exploits the ability of the metal honeycomb layer for absorbing another large amount of energy caused by impact. Indeed, the honeycomb layer crushes only in the area in which the impact occurs. Therefore, the damage does not propagate to other parts of the wing or of the empennage. The honeycomb layer mainly has a structural function, since it determines the overall rigidity of the leading edge with the advantage of significantly reducing the overall weight of the wing with respect to conventional structures. The honeycomb layers illustrated, as an example, in
Experiments carried out by the Applicants have demonstrated that a wing structure constructed according to the present invention allows weight to be saved, having equal overall deformation of the leading edge at the impact zone, of the order of 30% with respect to a structure having comparable rigidity constructed with Glare® technology.
It should be understood that the invention is not limited to the embodiments described and illustrated hereby, said embodiments should be considered example embodiments of the leading edge; the invention can, however, undergo modifications relative to its shape, size, and the arrangement of its constructive details, as defined by the appended claims. For example, the order of the single layers forming the panels can be inverted with respect to what has been illustrated in the present examples, by arranging the first metal foil layer 21 further inside, and the third honeycomb layer (or the fourth metal foil layer 24, if it is foreseen) further outside with respect to the wing or empennage structure. Furthermore, although the foregoing specification refers to aluminum and its alloys for the construction of the metal layers 21, 23 and 24, those skilled in the art will recognize that also other metals (for example titanium) and alloys thereof may be used for implementing the invention in addition to or in replacement of aluminum.