Patent Application
20190264875
The present disclosure relates to a lighting field, and more particularly to an LED light bulb with bendable LED filament.
Incandescent bulbs have been widely used for homes or commercial lighting for decades. However, incandescent bulbs are generally with lower efficiency in terms of energy application, and about 90% of energy input can be converted into a heat form to dissipate. In addition, because the incandescent bulb has a very limited lifespan (about 1,000 hours), it needs to be frequently replaced. These traditional incandescent bulbs are gradually replaced by other more efficient lighting devices, such as fluorescent lights, high-intensity discharge lamps, light-emitting diodes (LEDs) lights and the like. In these electric lamps, the LED light lamp attracts widespread attention in its lighting technology. The LED light lamp has the advantages of long lifespan, small in size, environmental protection and the like, therefore the application of the LED light lamp continuously grows.
In recent years, LED light bulbs with LED filaments have been provided on the market. At present, LED light bulbs using LED filaments as illumination sources still have the following problems to be improved.
There is one kind of LED soft filament, which is similar to the structure of the above-mentioned LED hard filament and is employed a flexible printed circuit substrate (hereinafter referred to FPC) instead of the glass substrate to enable the LED filament having a certain degree of bending. However, by utilizing the LED soft filament made of the FPC, the FPC has a thermal expansion coefficient different from that of the silicon gel coated covering the LED soft filament, and the long-term use causes the displacement or even degumming of the LED chips. Moreover, the FPC may not beneficial to flexible adjustment of the process conditions and the like. Besides, during bending the LED soft filament it has a challenge in the stability of the metal wire bonded between LED chips. When the arrangement of the LED chips in the LED soft filament is dense, if the adjacent LED chips are connected by means of metal wire bonding, it is easy to cause the stress to be concentrated on a specific part of the LED soft filament when the LED soft filament is bent, thereby the metal wire bonding between the LED chips are damaged and even broken.
In addition, the LED filament is generally disposed inside the LED light bulb, and in order to present the aesthetic appearance and also to make the illumination of the LED filament more uniform and widespread, the LED filament is bent to exhibit a plurality of curves. Since the LED chips are arranged in the LED filaments, and the LED chips are relatively hard objects, it is difficult for the LED filaments to be bent into a desired shape. Moreover, the LED filament is also prone to cracks due to stress concentration during bending.
In order to increase the aesthetic appearance and make the illumination appearance more uniform, an LED light bulb has a plurality of LED filaments, which are disposed with different placement or angles. However, since the plurality of LED filaments need to be installed in a single LED light bulb, and these LED filaments need to be fixed individually, the assembly process will be more complicated and the production cost will be increased.
Patent No. CN202252991U discloses the light lamp employing with a flexible PCB board instead of the aluminum heat dissipation component to improve heat dissipation. Wherein, the phosphor is coated on the upper and lower sides of the LED chip or on the periphery thereof, and the LED chip is fixed on the flexible PCB board and sealed by an insulating adhesive. The insulating adhesive is epoxy resin, and the electrodes of the LED chip are connected to the circuitry on the flexible PCB board by gold wires. The flexible PCB board is transparent or translucent, and the flexible PCB board is made by printing the circuitry on a polyimide or polyester film substrate. Patent No. CN105161608A discloses an LED filament light-emitting strip and a preparation method thereof. Wherein the LED chips are disposed without overlapped, and the light-emitting surfaces of the LED chips are correspondingly arranged, so that the light emitting uniformity and heat dissipation is improved accordingly. Patent No. CN103939758A discloses that a transparent and thermally conductive heat dissipation layer is formed between the interface of the carrier and the LED chip for heat exchange with the LED chip. According to the aforementioned patents, which respectively use a PCB board, adjust the chips arrangement or form a heat dissipation layer, the heat dissipation of the filament of the lamp can be improved to a certain extent correspondingly; however, the heat is easy to accumulate due to the low efficiency in heat dissipation. The last one, Publication No. CN204289439U discloses an LED filament with omni-directional light comprising a substrate mixed with phosphors, at least one electrode disposed on the substrate, at least one LED chip mounted on the substrate, and the encapsulant coated on the LED chip. The substrate formed by the silicone resin contained with phosphors eliminates the cost of glass or sapphire as a substrate, and the LED filament equipping with this kind of substrate avoids the influence of glass or sapphire on the light emitting of the LED chip. The 360-degree light emitting is realized, and the illumination uniformity and the light efficiency are greatly improved. However, due to the fact that the substrate is formed by silicon resin, the defect of poor heat resistance is a disadvantage.
It is noted that the present disclosure includes one or more inventive solutions currently claimed or not claimed, and in order to avoid confusion between the illustration of these embodiments in the specification, a number of possible inventive aspects herein may be collectively referred to “present/the invention.”
In accordance with an embodiment of the present invention, an LED filament comprises a plurality of LED chip units, a plurality of conductors, and at least two conductive electrodes. Wherein each of the conductors is located between two adjacent LED chip units, at least two LED chip units are disposed at different heights, and the conductive electrodes are disposed corresponding to the LED chip units configuration and electrically connected to the LED chip unit by the wire. The adjacent two LED chip units are electrically connected to each other through a conductor, and the angle between the conductor and the extending direction of the length of the LED filament is in a range of about 30° to 120°.
In accordance with another embodiment of the present invention provides a composition which is suitable for use as a filament substrate or a light conversion layer, wherein the composition comprises at least a main material, a modifier and an additive. The main material is an organosilicon-modified polyimide; the modifier is a thermal curing agent; and the additives comprise microparticles added into the main material, which may comprise phosphor particles, heat dispersing particles. The additive also comprises a coupling agent.
The present disclosure provides a composition which is suitable for use as a filament substrate or a light-conversion layer, wherein the main material in the composition is an organosilicon-modified polyimide, i.e. a polyimide comprising a siloxane moiety, wherein the organosilicon-modified polyimide comprises a repeating unit represented by the general Formula (I):
In general Formula (I), Ar1 is a tetra-valent organic group having a benzene ring or an alicyclic hydrocarbon structure, Ar2 is a di-valent organic group, R is each independently methyl or phenyl, and n is 1˜5.
According to an embodiment of the present disclosure, Ar1 is a tetra-valent organic group having a monocyclic alicyclic hydrocarbon structure or a bridged-ring alicyclic hydrocarbon structure.
According to another embodiment of the present disclosure, Ar2 is a di-valent organic group having a monocyclic alicyclic hydrocarbon structure.
To make the above and other objects, features, and advantages of the present invention clearer and easier to understand, the following embodiments will be described in detail with reference to the accompanying drawings.
The present invention will become more readily apparent to those ordinarily skilled in the art after reviewing the following detailed description and accompanying drawings, in which:
The present disclosure provides a novel LED filament and its application the LED light bulb. The present disclosure will now be described in the following embodiments with reference to the drawings. The following descriptions of various implementations are presented herein for purpose of illustration and giving examples only. This invention is not intended to be exhaustive or to be limited to the precise form disclosed. These example embodiments are just that—examples—and many implementations and variations are possible that do not require the details provided herein. It should also be emphasized that the disclosure provides details of alternative examples, but such listing of alternatives is not exhaustive. Furthermore, any consistency of detail between various examples should not be interpreted as requiring such detail—it is impracticable to list every possible variation for every feature described herein. The language of the claims should be referenced in determining the requirements of the invention.
The LED chip units 102, 104, or named with the LED section 102, 104, may be composed of a single LED chip, or two LED chips. Of course, it may also include multiple LED chips, that is, equal to or greater than three LED chips.
A chip bonding design relating to an LED filament will be described.
The conductor 330a is located between the adjacent two LED chip units 302, 304, the LED chip units 302, 304 are at different positions in the Y direction, and the conductive electrodes 310, 312 are disposed corresponding to the LED chip units 302, 304 and electrically connected to the LED chip units 302 and 304 through the wires 340. The adjacent two LED chip units 302 and 304 are electrically connected to each other through the conductor 330a. The angle between the conductor 330a and the LED filament in the longitudinal direction (X direction) is 30° to 120°, preferably 60° to 120°. In the related art, the direction of the conductor 330a is parallel to the X direction, and the internal stress acting on the cross sectional area of the conductor is large when the filament is bent at the conductor. Therefore, the conductor 330a is disposed at a certain angle with the X direction and it can effectively reduce the internal stress thereof. The wire 340 is at an angle, parallel, vertical or any combination with the X direction. In the embodiment, the LED filament 300 includes two wires 340, one wire 340 is parallel to the X direction, and the other wire 340 has an angle of 30° to 120° with respect to the X direction. The LED filament 300 emits light after its conductive electrodes 310, 312 are powered with voltage source or current source.
As shown in
As shown in
The next part will describe the material of the filament of the present invention. The material suitable for manufacturing a filament substrate or a light-conversion layer for LED should have properties such as excellent light transmission, good heat resistance, excellent thermal conductivity, appropriate refraction rate, excellent mechanical properties and good warpage resistance. All the above properties can be achieved by adjusting the type and the content of the main material, the modifier and the additive contained in the organosilicon-modified polyimide composition. The present disclosure provides a filament substrate or a light-conversion layer formed from a composition comprising an organosilicon-modified polyimide. The composition can meet the requirements on the above properties. In addition, the type and the content of one or more of the main material, the modifier (thermal curing agent) and the additive in the composition can be modified to adjust the properties of the filament substrate or the light-conversion layer, so as to meet special environmental requirements. The modification of each property is described herein below.
Adjustment of the Organosilicon-Modified Polyimide
The organosilicon-modified polyimide provided herein comprises a repeating unit represented by the following general Formula (I):
In general Formula (I), Ar1 is a tetra-valent organic group. The organic group has a benzene ring or an alicyclic hydrocarbon structure. The alicyclic hydrocarbon structure may be monocyclic alicyclic hydrocarbon structure or a bridged-ring alicyclic hydrocarbon structure, which may be a dicyclic alicyclic hydrocarbon structure or a tricyclic alicyclic hydrocarbon structure. The organic group may also be a benzene ring or an alicyclic hydrocarbon structure comprising a functional group having active hydrogen, wherein the functional group having active hydrogen is one or more of hydroxyl, amino, carboxy, amido and mercapto.
Ar2 is a di-valent organic group, which organic group may have for example a monocyclic alicyclic hydrocarbon structure or a di-valent organic group comprising a functional group having active hydrogen, wherein the functional group having active hydrogen is one or more of hydroxyl, amino, carboxy, amido and mercapto.
R is each independently methyl or phenyl.
n is 1˜5, preferably 1, 2, 3 or 5.
The polymer of general Formula (I) has a number average molecular weight of 5000˜100000, preferably 10000˜60000, more preferably 20000˜40000. The number average molecular weight is determined by gel permeation chromatography (GPC) and calculated based on a calibration curve obtained by using standard polystyrene. When the number average molecular weight is below 5000, a good mechanical property is hard to be obtained after curing, especially the elongation tends to decrease. On the other hand, when it exceeds 100000, the viscosity becomes too high and the resin is hard to be formed.
Ar1 is a component derived from a dianhydride, which may be an aromatic anhydride or an aliphatic anhydride. The aromatic anhydride includes an aromatic anhydride comprising only a benzene ring, a fluorinated aromatic anhydride, an aromatic anhydride comprising amido group, an aromatic anhydride comprising ester group, an aromatic anhydride comprising ether group, an aromatic anhydride comprising sulfide group, an aromatic anhydride comprising sulfonyl group, and an aromatic anhydride comprising carbonyl group.
Examples of the aromatic anhydride comprising only a benzene ring include pyromellitic dianhydride (PMDA), 2,3,3′,4′-biphenyl tetracarboxylic dianhydride (aBPDA), 3,3′,4,4′-biphenyl tetracarboxylic dianhydride (sBPDA), and 4-(2,5-dioxotetrahydrofuran-3-yl)-1,2,3,4-tetrahydro naphthalene-1,2-dicarboxylic anhydride (TDA). Examples of the fluorinated aromatic anhydride include 4,4′-(hexafluoroisopropylidene)diphthalic anhydride which is referred to as 6FDA. Examples of the aromatic anhydride comprising amido group include N,N′-(5,5′-(perfluoropropane-2,2-diyl)bis(2-hydroxy-5,1-phenylene))bis(1,3-dioxo-1,3-dihydroisobenzofuran)-5-arboxamide) (6FAP-ATA), and N,N′-(9H-fluoren-9-ylidenedi-4,1-phenylene)bis[1,3-dihydro-1,3-dioxo-5-isobenzofuran carboxamide] (FDA-ATA). Examples of the aromatic anhydride comprising ester group include p-phenylene bis(trimellitate) dianhydride (TAHQ). Examples of the aromatic anhydride comprising ether group include 4,4′-(4,4′-isopropylidenediphenoxy)bis(phthalic anhydride) (BPADA), 4,4′-oxydiphthalic dianhydride (sODPA), 2,3,3′,4′-diphenyl ether tetracarboxylic dianhydride (aODPA), and 4,4′-(4,4′-isopropylidenediphenoxy)bis(phthalic anhydride)(BPADA). Examples of the aromatic anhydride comprising sulfide group include 4,4′-bis(phthalic anhydride)sulfide (TPDA). Examples of the aromatic anhydride comprising sulfonyl group include 3,3′,4,4′-diphenylsulfonetetracarboxylic dianhydride (DSDA). Examples of the aromatic anhydride comprising carbonyl group include 3,3′,4,4′-benzophenonetetracarboxylic dianhydride(BTDA).
The alicyclic anhydride includes 1,2,4,5-cyclohexanetetracarboxylic acid dianhydride which is referred to as HPMDA, 1,2,3,4-butanetetracarboxylic dianhydride (BDA), tetrahydro-1H-5,9-methanopyrano[3,4-d]oxepine-1,3,6,8(4H)-tetrone (TCA), hexahydro-4,8-ethano-1H,3H-benzo[1,2-C:4,5-C′]difuran-1,3,5,7-tetrone (BODA), cyclobutane-1,2,3,4-tetracarboxylic dianhydride(CBDA), and 1,2,3,4-cyclopentanetetracarboxylic dianhydride (CpDA); or alicyclic anhydride comprising an olefin structure, such as bicyclo[2.2.2]oct-7-ene-2,3,5,6-tetracarboxylic dianhydride (COeDA). When an anhydride comprising ethynyl such as 4,4′-(ethyne-1,2-diyl)diphthalic anhydride (EBPA) is used, the mechanical strength of the light-conversion layer can be further ensured by post-curing.
Considering the solubility, 4,4′-oxydiphthalic anhydride (sODPA), 3,3′,4,4′-benzophenonetetracarboxylic dianhydride (BTDA), cyclobutanetetracarboxylic dianhydride (CBDA) and 4,4′-(hexafluoroisopropylidene)diphthalic anhydride (6FDA) are preferred. The above dianhydride can be used alone or in combination.
Ar2 is derived from diamine which may be an aromatic diamine or an aliphatic diamine. The aromatic diamine includes an aromatic diamine comprising only a benzene ring, a fluorinated aromatic diamine, an aromatic diamine comprising ester group, an aromatic diamine comprising ether group, an aromatic diamine comprising amido group, an aromatic diamine comprising carbonyl group, an aromatic diamine comprising hydroxyl group, an aromatic diamine comprising carboxy group, an aromatic diamine comprising sulfonyl group, and an aromatic diamine comprising sulfide group.
The aromatic diamine comprising only a benzene ring includes m-phenylenediamine, p-phenylenediamine, 2,4-diaminotoluene, 2,6-diamino-3,5-diethyltoluene, 3,3′-dimethylbiphenyl-4,4′-diamine 9,9-bis(4-aminophenyl)fluorene (FDA), 9,9-bis(4-amino-3-methylphenyl)fluorene, 2,2-bis(4-aminophenyl)propane, 2,2-bis(3-methyl-4-aminophenyl)propane, 4,4′-diamino-2,2′-dimethylbiphenyl(APB). The fluorinated aromatic diamine includes 2,2′-bis(trifluoromethyl)benzidine (TFMB), 2,2-bis(4-aminophenyl)hexafluoropropane (6FDAM), 2,2-bis[4-(4-aminophenoxy)phenyl]hexafluoropropane (HFBAPP), and 2,2-bis(3-amino-4-methylphenyl)hexafluoropropane (BIS-AF-AF). The aromatic diamine comprising ester group includes [4-(4-aminobenzoyl)oxyphenyl]4-aminobenzoate (ABHQ), bis(4-aminophenyl)terephthalate(BPTP), and 4-aminophenyl 4-aminobenzoate (APAB). The aromatic diamine comprising ether group includes 2,2-bis[4-(4-aminophenoxy)phenyl]propane)(BAPP), 2,2′-bis[4-(4-aminophenoxy)phenyl]propane (ET-BDM), 2,7-bis(4-aminophenoxy)-naphthalene (ET-2,7-Na), 1,3-bis(3-aminophenoxy)benzene (TPE-M),[1,4-phenyldi(oxy)]bis[3-(trifluoromethyl)aniline] (p-6FAPB), 3,4′-diaminodiphenyl ether, 4, 4′-diaminodiphenyl ether (ODA), 1,3-bis(4-aminophenoxy)benzene (TPE-R), 1,4-bis(4-aminophenoxy)benzene (TPE-Q), and 4,4′-bis(4-aminophenoxy)biphenyl(BAPB). The aromatic diamine comprising amido group includes N,N′-bis(4-aminophenyl)benzene-1,4-dicarboxamide (BPTPA), 3,4′-diamino benzanilide (m-APABA), and 4,4′-diaminobenzanilide (DABA). The aromatic diamine comprising carbonyl group includes 4,4′-diaminobenzophenone (4,4′-DABP), and bis(4-amino-3-carboxyphenyl) methane (or referred to as 6,6′-diamino-3,3′-methylanediyl-dibenzoic acid). The aromatic diamine comprising hydroxyl group includes 3,3′-dihydroxybenzidine (HAB), and 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane (6FAP). The aromatic diamine comprising carboxy group includes 6,6′-diamino-3,3′-methylanediyl-dibenzoic acid (MBAA), and 3,5-diaminobenzoic acid (DBA). The aromatic diamine comprising sulfonyl group includes 3,3′-diaminodiphenyl sulfone (DDS),4,4′-diaminodiphenyl sulfone, bis[4-(4-aminophenoxy)phenyl]sulfone (BAPS) (or referred to as 4,4′-bis(4-aminophenoxy)diphenylsulfone), and 3,3′-diamino-4,4′-dihydroxydiphenyl sulfone (ABPS). The aromatic diamine comprising sulfide group includes 4,4′-diaminodiphenyl sulfide.
The aliphatic diamine is a diamine which does not comprise any aromatic structure (e.g., benzene ring). The aliphatic diamine includes monocyclic alicyclic amine and straight chain aliphatic diamine, wherein the straight chain aliphatic diamine include siloxane diamine, straight chain alkyl diamine and straight chain aliphatic diamine comprising ether group. The monocyclic alicyclic diamine includes 4,4′-diaminodicyclohexylmethane (PACM), and 3,3′-dimethyl-4,4-diaminodicyclohexylmethane (DMDC). The siloxane diamine (or referred to as amino-modified silicone) includes α,ω-(3-aminopropyl)polysiloxane (KF8010), X22-161A, X22-161B, NH15D, and 1,3-bis(3-aminopropyl)-1,1,3,3-tetramethyldisiloxane (PAME). The straight chain alkyl diamine has 6-12 carbon atoms, and is preferably un-substituted straight chain alkyl diamine. The straight chain aliphatic diamine comprising ether group includes ethylene glycol di(3-aminopropyl) ether.
The diamine can also be a diamine comprising fluorenyl group. The fluorenyl group has a bulky free volume and rigid fused-ring structure, which renders the polyimide good heat resistance, thermal and oxidation stabilities, mechanical properties, optical transparency and good solubility in organic solvents. The diamine comprising fluorenyl group, such as 9,9-bis(3,5-difluoro-4-aminophenyl)fluorene, may be obtained through a reaction between 9-fluorenone and 2,6-dichloroaniline. The fluorinated diamine can be 1,4-bis(3′-amino-5′-trifluoromethylphenoxy)biphenyl, which is a meta-substituted fluorine-containing diamine having a rigid biphenyl structure. The meta-substituted structure can hinder the charge flow along the molecular chain and reduce the intermolecular conjugation, thereby reducing the absorption of visible lights. Using asymmetric diamine or anhydride can increase to some extent the transparency of the organosilicon-modified polyimide resin composition. The above diamines can be used alone or in combination.
Examples of diamines having active hydrogen include diamines comprising hydroxyl group, such as 3,3′-diamino-4,4′-dihydroxybiphenyl, 4,4′-diamino-3,3′-dihydroxy-1,1′-biphenyl (or referred to as 3,3′-dihydroxybenzidine) (HAB), 2,2-bis(3-amino-4-hydroxyphenyl)propane(BAP), 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane(6FAP), 1,3-bis(3-hydro-4-aminophenoxy) benzene, 1,4-bis(3-hydroxy-4-aminophenyl)benzene and 3,3′-diamino-4,4′-dihydroxydiphenyl sulfone (ABPS). Examples of diamines comprising carboxy group include 3,5-diaminobenzoic acid, bis(4-amino-3-carboxyphenyl)methane (or referred to as 6,6′-diamino-3,3′-methylenedibenzoic acid), 3,5-bis(4-aminophenoxy)benzoic acid, and 1,3-bis(4-amino-2-carboxyphenoxy)benzene. Examples of diamines comprising amino group include 4,4′-diaminobenzanilide (DABA), 2-(4-aminophenyl)-5-aminobenzoimidazole, diethylenetriamine, 3,3′-diaminod ipropylamine, triethylenetetramine, and N,N′-bis(3-aminopropyl)ethylenediamine (or referred to as N,N-di(3-aminopropyl)ethylethylamine). Examples of diamines comprising thiol group include 3,4-diaminobenzenethiol. The above diamines can be used alone or in combination.
The organosilicon-modified polyimide can be synthesized by well-known synthesis methods. For example, it can be prepared from a dianhydride and a diamine which are dissolved in an organic solvent and subjected to imidation in the presence of a catalyst. Examples of the catalyst include acetic anhydride/triethylamine, and valerolactone/pyridine. Preferably, removal of water produced in the azeotropic process in the imidation is promoted by using a dehydrant such as toluene.
Polyimide can also be obtained by carrying out an equilibrium reaction to give a poly (amic acid) which is heated to dehydrate. In other embodiments, the polyimide backbone may have a small amount of amic acid. For example, the ratio of amic acid to imide in the polyimide molecule may be 1˜3:100. Due to the interaction between amic acid and the epoxy resin, the substrate has superior properties. In other embodiments, a solid state material such as a thermal curing agent, inorganic heat dispersing particles and phosphor can also be added at the state of poly (amic acid) to give the substrate. In addition, solubilized polyimide can also be obtained by direct heating and dehydration after mixing of alicylic anhydride and diamine. Such solubilized polyimide, as an adhesive material, has a good light transmittance. In addition, it is liquid state; therefore, other solid materials (such as the inorganic heat dispersing particles and the phosphor) can be dispersed in the adhesive material more sufficiently.
In one embodiment for preparing the organosilicon-modified polyimide, the organosilicon-modified polyimide can be produced by dissolving the polyimide obtained by heating and dehydration after mixing a diamine and an anhydride and a siloxane diamine in a solvent. In another embodiment, the amidic acid, before converting to polyimide, is reacted with the siloxane diamine.
In addition, the polyimide compound may be obtained by dehydration and ring-closing and condensation polymerization from an anhydride and a diamine, such as an anhydride and a diamine in a molar ratio of 1:1. In one embodiment, 200 micromole (mmol) of 4,4′-(hexafluoroisopropylidene) diphthalic anhydride(6FDA), 20 micromole (mmol) of 2,2-bis(3-amino-4-hydroxyphenyl)hexafluoropropane(6FAP), 50 micromole (mmol) of 2,2′-di(trifluoromethyl)diaminobiphenyl(TFMB) and 130 micromole (mmol) of aminopropyl-terminated poly(dimethylsiloxane) are used to give the PI synthesis solution.
The above methods can be used to produce amino-terminated polyimide compounds. However, other methods can be used to produce carboxy-terminated polyimide compounds. In addition, in the above reaction between anhydride and diamine, where the backbone of the anhydride comprises a carbon-carbon triple bond, the affinity of the carbon-carbon triple bond can promote the molecular structure. Alternatively, a diamine comprising vinyl siloxane structure can be used.
The molar ratio of dianhydride to diamine may be 1:1. The molar percentage of the diamine comprising a functional group having active hydrogen may be 5˜25% of the total amount of diamine. The temperature under which the polyimide is synthesized is preferably 80˜250° C., more preferably 100˜200° C. The reaction time may vary depending on the size of the batch. For example, the reaction time for obtaining 10˜30 g polyimide is 6-10 hours.
The organosilicon-modified polyimide can be classified as fluorinated aromatic organosilicon-modified polyimides and aliphatic organosilicon-modified polyimides. The fluorinated aromatic organosilicon-modified polyimides are synthesized from siloxane-type diamine, aromatic diamine comprising fluoro (F) group (or referred to as fluorinated aromatic diamine) and aromatic dianhydride comprising fluoro (F) group (or referred to as fluorinated aromatic anhydride). The aliphatic organosilicon-modified polyimides are synthesized from dianhydride, siloxane-type diamine and at least one diamine not comprising aromatic structure (e.g., benzene ring) (or referred to as aliphatic diamine), or from diamine (one of which is siloxane-type diamine) and at least one dianhydride not comprising aromatic structure (e.g., benzene ring) (or referred to as aliphatic anhydride). The aliphatic organosilicon-modified polyimide includes semi-aliphatic organosilicon-modified polyimide and fully aliphatic organosilicon-modified polyimide. The fully aliphatic organosilicon-modified polyimide is synthesized from at least one aliphatic dianhydride, siloxane-type diamine and at least one aliphatic diamine. The raw materials for synthesizing the semi-aliphatic organosilicon-modified polyimide include at least one aliphatic dianhydride or aliphatic diamine. The raw materials required for synthesizing the organosilicon-modified polyimide and the siloxane content in the organosilicon-modified polyimide would have certain effects on transparency, chromism, mechanical property, warpage extent and refractivity of the substrate.
The organosilicon-modified polyimide of the present disclosure has a siloxane content of 20-75 wt %, preferably 30-70 wt %, and a glass transition temperature of below 150° C. The glass transition temperature (Tg) is determined on TMA-60 manufactured by Shimadzu Corporation after adding a thermal curing agent to the organosilicon-modified polyimide. The determination conditions include: load: 5 gram; heating rate: 10° C./min; determination environment: nitrogen atmosphere; nitrogen flow rate: 20 ml/min; temperature range: −40 to 300° C. When the siloxane content is below 20%, the film prepared from the organosilicon-modified polyimide resin composition may become very hard and brittle due to the filling of the phosphor and thermal conductive fillers, and tend to warp after drying and curing, and therefore has a low processability. In addition, its resistance to thermochromism becomes lower. On the other hand, when the siloxane content is above 75%, the film prepared from the organosilicon-modified polyimide resin composition becomes opaque, and has reduced transparency and tensile strength. Here, the siloxane content is the weight ratio of siloxane-type diamine(having a structure shown in Formula (A)) to the organosilicon-modified polyimide, wherein the weight of the organosilicon-modified polyimide is the total weight of the diamine and the dianhydride used for synthesizing the organosilicon-modified polyimide subtracted by the weight of water produced during the synthesis.
Wherein R is methyl or phenyl, preferably methyl, n is 1˜5, preferably 1, 2, 3 or 5.
The only requirements on the organic solvent used for synthesizing the organosilicon-modified polyimide are to dissolve the organosilicon-modified polyimide and to ensure the affinity (wettability) to the phosphor or the fillers to be added. However, excessive residue of the solvent in the product should be avoided. Normally, the number of moles of the solvent is equal to that of water produced by the reaction between diamine and anhydride. For example, 1 mol diamine reacts with 1 mol anhydride to give 1 mol water; then the amount of solvent is 1 mol. In addition, the organic solvent used has a boiling point of above 80° C. and below 300° C., more preferably above 120° C. and below 250° C., under standard atmospheric pressure. Since drying and curing under a lower temperature are needed after coating, if the temperature is lower than 120° C., good coating cannot be achieved due to high drying speed during the coating process. If the boiling point of the organic solvent is higher than 250° C., the drying under a lower temperature may be deferred. Specifically, the organic solvent may be an ether-type organic solvent, an ester-type organic solvent, a dimethyl ether-type organic solvent, a ketone-type organic solvent, an alcohol-type organic solvent, an aromatic hydrocarbon solvent or other solvents. The ether-type organic solvent includes ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, propylene glycol monomethyl ether, propylene glycol monoethyl ether, ethylene glycol dimethyl ether, ethylene glycol diethyl ether, ethylene glycol dibutyl ether, diethylene glycol dimethyl ether, diethylene glycol diethyl ether, diethylene glycol methyl ethyl ether, dipropylene glycol dimethyl ether or diethylene glycol dibutyl ether, and diethylene glycol butyl methyl ether. The ester-type organic solvent includes acetates, including ethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether acetate, propylene glycol monomethyl ether acetate, propyl acetate, propylene glycol diacetate, butyl acetate, isobutyl acetate, 3-methoxybutyl acetate, 3-methyl-3-methoxybutyl acetate, benzyl acetate and 2-(2-butoxyethoxy)ethyl acetate; and methyl lactate, ethyl lactate, n-butyl acetate, methyl benzoate and ethyl benzoate. The dimethyl ether-type solvent includes triethylene glycol dimethyl ether and tetraethylene glycol dimethyl ether. The ketone-type solvent includes acetylacetone, methyl propyl ketone, methyl butyl ketone, methyl isobutyl ketone, cyclopentanone, and 2-heptanone. The alcohol-type solvent includes butanol, isobutanol, isopentanol, 4-methyl-2-pentanol, 3-methyl-2-butanol, 3-methyl-3-methoxybutanol, and diacetone alcohol. The aromatic hydrocarbon solvent includes toluene and xylene. Other solvents include γ-butyrolactone, N-methylpyrrolidone, N,N-dimethylformamide, N,N-dimethylacetamide and dimethyl sulfoxide.
The present disclosure provides an organosilicon-modified polyimide resin composition comprising the above organosilicon-modified polyimide and a thermal curing agent, which may be epoxy resin, hydrogen isocyanate or bisoxazoline compound. In one embodiment, based on the weight of the organosilicon-modified polyimide, the amount of the thermal curing agent is 5˜12% of the weight of the organosilicon-modified polyimide. The organosilicon-modified polyimide resin composition may further comprise heat dispersing particles and phosphor.
Light Transmittance
The factors affecting the light transmittance of the organosilicon-modified polyimide resin composition at least include the type of the main material, the type of the modifier(thermal curing agent), the type and content of the heat dispersing particles, and the siloxane content. Light transmittance refers to the transmittance of the light near the main light-emitting wavelength range of the LED chip. For example, blue LED chip has a main light-emitting wavelength of around 450 nm, then the composition or the polyimide should have low enough or even no absorption to the light having a wavelength around 450 nm, so as to ensure that most or even all the light can pass through the composition or the polyimide. In addition, when the light emitted by the LED chip passes through the interface of two materials, the closer the refractive indexes of the two materials, the higher the light output efficiency. In order to be close to the refractive index of the material (such as die bonding glue) contacting with the filament substrate (or base layer), the organosilicon-modified polyimide composition has a refractive index of 1.4˜1.7, preferably 1.4˜1.55. In order to use the organosilicon-modified polyimide resin composition as substrate in the filament, the organosilicon-modified polyimide resin composition is required to have good light transmittance at the peak wavelength of InGaN of the blue-excited white LED. In order to obtain a good transmittance, the raw materials for synthesizing the organosilicon-modified polyimide, the thermal curing agent and the heat dispersing particles can be adjusted. Because the phosphor in the organosilicon-modified polyimide resin composition may have certain effect on the transmittance test, the organosilicon-modified polyimide resin composition used for the transmittance test does not comprise phosphor. Such an organosilicon-modified polyimide resin composition has a transmittance of 86-93%, preferably 88-91%, or preferably 89-92%, or preferably 90-93%.
In the reaction of anhydride and diamine to produce polyimide, the anhydride and the diamine may vary. In other words, the polyimides produced from different anhydrides and different diamines may have different light transmittances. The aliphatic organosilicon-modified polyimide resin composition comprises the aliphatic organosilicon-modified polyimide and the thermal curing agent, while the fluorinated aromatic organosilicon-modified polyimide resin composition comprises the fluorinated aromatic organosilicon-modified polyimide and the thermal curing agent. Since the aliphatic organosilicon-modified polyimide has an alicyclic structure, the aliphatic organosilicon-modified polyimide resin composition has a relatively high light transmittance. In addition, the fluorinated aromatic, semi-aliphatic and full aliphatic polyimides all have good light transmittance in respect of the blue LED chips. The fluorinated aromatic organosilicon-modified polyimide is synthesized from a siloxane-type diamine, an aromatic diamine comprising a fluoro (F) group (or referred to as fluorinated aromatic diamine) and an aromatic dianhydride comprising a fluoro (F) group (or referred to as fluorinated aromatic anhydride). In other words, both Ar1 and Ar2 comprise a fluoro (F) group. The semi-aliphatic and full aliphatic organosilicon-modified polyimides are synthesized from a dianhydride, a siloxane-type diamine and at least one diamine not comprising an aromatic structure (e.g. a benzene ring) (or referred to as aliphatic diamine), or from a diamine (one of the diamine is siloxane-type diamine) and at least one dianhydride not comprising an aromatic structure (e.g. a benzene ring) (or referred to as aliphatic anhydride). In other words, at least one of Ar1 and Ar2 has an alicyclic hydrocarbon structure.
Although blue LED chips have a main light-emitting wavelength of 450 nm, they may still emit a minor light having a shorter wavelength of around 400 nm, due to the difference in the conditions during the manufacture of the chips and the effect of the environment. The fluorinated aromatic, semi-aliphatic and full aliphatic polyimides have different absorptions to the light having a shorter wavelength of 400 nm. The fluorinated aromatic polyimide has an absorbance of about 20% to the light having a shorter wavelength of around 400 nm, i.e. the light transmittance of the light having a wavelength of 400 nm is about 80% after passing through the fluorinated aromatic polyimide. The semi-aliphatic and full aliphatic polyimides have even lower absorbance to the light having a shorter wavelength of 400 nm than the fluorinated aromatic polyimide, which is only 12%. Accordingly, in an embodiment, if the LED chips used in the LED filament have a uniform quality, and emit less blue light having a shorter wavelength, the fluorinated aromatic organosilicon-modified polyimide may be used to produce the filament substrate or the light-conversion layer. In another embodiment, if the LED chips used in the LED filament have different qualities, and emit more blue light having a shorter wavelength, the semi-aliphatic or full aliphatic organosilicon-modified polyimides may be used to produce the filament substrate or the light-conversion layer.
Adding different thermal curing agents imposes different effects on the light transmittance of the organosilicon-modified polyimide. Table 1-1 shows the effect of the addition of different thermal curing agents on the light transmittance of the full aliphatic organosilicon-modified polyimide. At the main light-emitting wavelength of 450 nm for the blue LED chip, the addition of different thermal curing agents renders no significant difference to the light transmittance of the full aliphatic organosilicon-modified polyimide; while at a short wavelength of 380 nm, the addition of different thermal curing agents does affect the light transmittance of the full aliphatic organosilicon-modified polyimide. The organosilicon-modified polyimide itself has a poorer transmittance to the light having a short wavelength (380 nm) than to the light having a long wavelength (450 nm). However, the extent of the difference varies with the addition of different thermal curing agents. For example, when the thermal curing agent KF105 is added to the full aliphatic organosilicon-modified polyimide, the extent of the reduction in the light transmittance is less. In comparison, when the thermal curing agent 2021p is added to the full aliphatic organosilicon-modified polyimide, the extent of the reduction in the light transmittance is more. Accordingly, in an embodiment, if the LED chips used in the LED filament have a uniform quality, and emit less blue light having a short wavelength, the thermal curing agent BPA or the thermal curing agent 2021p may be added. In comparison, in an embodiment, if the LED chips used in the LED filament have different qualities, and emit more blue light having a short wavelength, the thermal curing agent KF105 may be used. Both Table 1-1 and Table 1-2 show the results obtained in the transmittance test using Shimadzu UV-V is Spectrometer UV-1800. The light transmittances at wavelengths 380 nm, 410 nm and 450 nm are tested based on the light emission of white LEDs.
Even when the same thermal curing agent is added, different added amount thereof will have different effects on the light transmittance. Table 1-2 shows that when the added amount of the thermal curing agent BPA to the full aliphatic organosilicon-modified polyimide is increased from 4% to 8%, the light transmittance increases. However, when the added amount is further increased to 12%, the light transmittance keeps almost constant. It is shown that the light transmittance increases with the increase of the added amount of the thermal curing agent, but after the light transmittance increases to certain degree, adding more thermal curing agent will have limited effect on the light transmittance.
Different heat dispersing particles would have different transmittances. If heat dispersing particles with low light transmittance or low light reflection are used, the light transmittance of the organosilicon-modified polyimide resin composition will be lower. The heat dispersing particles in the organosilicon-modified polyimide resin composition of the present disclosure are preferably selected to be transparent powders or particles with high light transmittance or high light reflection. Since the soft filament for the LED is mainly for the light emission, the filament substrate should have good light transmittance. In addition, when two or more types of heat dispersing particles are mixed, particles with high light transmittance and those with low light transmittance can be used in combination, wherein the proportion of particles with high light transmittance is higher than that of particles with low light transmittance. In an embodiment, for example, the weight ratio of particles with high light transmittance to particles with low light transmittance is 3˜5:1.
Different siloxane content also affects the light transmittance. As can be seen from Table 2, when the siloxane content is only 37 wt %, the light transmittance is only 85%. When the siloxane content is increased to above 45%, the light transmittance exceeds 94%.
Heat Resistance
The factors affecting the heat resistance of the organosilicon-modified polyimide resin composition include at least the type of the main material, the siloxane content, and the type and content of the modifier (thermal curing agent).
All the organosilicon-modified polyimide resin composition synthesized from fluorinated aromatic, semi-aliphatic and, full aliphatic organosilicon-modified polyimide have superior heat resistance, and are suitable for producing the filament substrate or the light-conversion layer. Detailed results from the accelerated heat resistance and aging tests (300° C.×1 hr) show that the fluorinated aromatic organosilicon-modified polyimide has better heat resistance than the aliphatic organosilicon-modified polyimide. Accordingly, in an embodiment, if a high power, high brightness LED chip is used as the LED filament, the fluorinated aromatic organosilicon-modified polyimide may be used to produce the filament substrate or the light-conversion layer.
The siloxane content in the organosilicon-modified polyimide will affect the resistance to thermochromism of the organosilicon-modified polyimide resin composition. The resistance to thermochromism refers to the transmittance determined at 460 nm after placing the sample at 200° C. for 24 hours. As can be seen from Table 2, when the siloxane content is only 37 wt %, the light transmittance after 24 hours at 200° C. is only 83%. As the siloxane content is increased, the light transmittance after 24 hours at 200° C. increases gradually. When the siloxane content is 73 wt %, the light transmittance after 24 hours at 200° C. is still as high as 95%. Accordingly, increasing the siloxane content can effectively increase the resistance to thermochromism of the organosilicon-modified polyimide.
In the cross-linking reaction between the organosilicon-modified polyimide and the thermal curing agent, the thermal curing agent should have an organic group which is capable of reacting with the functional group having active hydrogen in the polyimide. The amount and the type of the thermal curing agent have certain effects on chromism, mechanical property and refractive index of the substrate. Accordingly, a thermal curing agent with good heat resistance and transmittance can be selected. Examples of the thermal curing agent include epoxy resin, isocyanate, bismaleimide, and bisoxazoline compounds. The epoxy resin may be bisphenol A epoxy resin, such as BPA; or siloxane-type epoxy resin, such as KF105, X22-163, and X22-163A; or alicylic epoxy resin, such as 3,4-epoxycyclohexylmethyl3,4-epoxycyclohexanecarboxylate (2021P), EHPE3150, and EHPE3150CE. Through the bridging reaction by the epoxy resin, a three dimensional bridge structure is formed between the organosilicon-modified polyimide and the epoxy resin, increasing the structural strength of the adhesive itself. In an embodiment, the amount of the thermal curing agent may be determined according to the molar amount of the thermal curing agent reacting with the functional group having active hydrogen in the organosilicon-modified polyimide. In an embodiment, the molar amount of the functional group having active hydrogen reacting with the thermal curing agent is equal to that of the thermal curing agent. For example, when the molar amount of the functional group having active hydrogen reacting with the thermal curing agent is 1 mol, the molar amount of the thermal curing agent is 1 mol.
Thermal Conductivity
The factors affecting the thermal conductivity of the organosilicon-modified polyimide resin composition include at least the type and content of the phosphor, the type and content of the heat dispersing particles and the addition and the type of the coupling agent. In addition, the particle size and the particle size distribution of the heat dispersing particles would also affect the thermal conductivity.
The organosilicon-modified polyimide resin composition may also comprise phosphor for obtaining the desired light-emitting properties. The phosphor can convert the wavelength of the light emitted from the light-emitting semiconductor. For example, yellow phosphor can convert blue light to yellow light, and red phosphor can convert blue light to red light. Examples of yellow phosphor include transparent phosphor such as (Ba,Sr,Ca)2SiO4:Eu, and (Sr,Ba)2 SiO4:Eu(barium orthosilicate (BOS)); silicate-type phosphor having a silicate structure such as Y3Al5O12:Ce(YAG(yttrium-aluminum-garnet):Ce), and Tb3Al3O12:Ce(YAG(terbium-aluminum-garnet):Ce); and oxynitride phosphor such as Ca-α-SiAlON. Examples of red phosphor include nitride phosphor, such as CaAlSiN3:Eu, and CaSiN2:Eu. Examples of green phosphor include rare earth-halide phosphor, and silicate phosphor. The ratio of the phosphor in the organosilicon-modified polyimide resin composition may be determined arbitrarily according to the desired light-emitting property. In addition, since the phosphor have a thermal conductivity which is significantly higher than that of the organosilicon-modified polyimide resin, the thermal conductivity of the organosilicon-modified polyimide resin composition as a whole will increase as the ratio of the phosphor in the organosilicon-modified polyimide resin composition increases. Accordingly, in an embodiment, as long as the light-emitting property is fulfilled, the content of the phosphor can be suitably increased to increase the thermal conductivity of the organosilicon-modified polyimide resin composition, which is beneficial to the heat dissipation of the filament substrate or the light-conversion layer. Furthermore, when the organosilicon-modified polyimide resin composition is used as the filament substrate, the content, shape and particle size of the phosphor in the organosilicon-modified polyimide resin composition also have certain effect on the mechanical property (such as the elastic modulus, elongation, tensile strength) and the warpage extent of the substrate. In order to render superior mechanical property and thermal conductivity as well as small warpage extent to the substrate, the phosphor included in the organosilicon-modified polyimide resin composition are particulate, and the shape thereof may be sphere, plate or needle, preferably sphere. The maximum average length of the phosphor (the average particle size when they are spherical) is above 0.1 μm, preferably over 1 μm, further preferably 1˜100 μm, and more preferably 1˜50 μm. The content of phosphor is no less than 0.05 times, preferably no less than 0.1 times, and no more than 8 times, preferably no more than 7 times, the weight of the organosilicon-modified polyimide. For example, when the weight of the organosilicon-modified polyimide is 100 parts in weight, the content of the phosphor is no less than 5 parts in weight, preferably no less than 10 parts in weight, and no more than 800 parts in weight, preferably no more than 700 parts in weight. When the content of the phosphor in the organosilicon-modified polyimide resin composition exceeds 800 parts in weight, the mechanical property of the organosilicon-modified polyimide resin composition may not achieve the strength as required for a filament substrate, resulting in the increase of the defective rate of the product. In an embodiment, two kinds of phosphor are added at the same time. For example, when red phosphor and green phosphor are added at the same time, the added ratio of red phosphor to green phosphor is 1:5˜8, preferably 1:6˜7. In another embodiment, red phosphor and yellow phosphor are added at the same time, wherein the added ratio of red phosphor to yellow phosphor is 1:5˜8, preferably 1:6˜7. In another embodiment, three or more kinds of phosphor are added at the same time.
The main purposes of adding the heat dispersing particles are to increase the thermal conductivity of the organosilicon-modified polyimide resin composition, to maintain the color temperature of the light emission of the LED chip, and to prolong the service life of the LED chip. Examples of the heat dispersing particles include silica, alumina, magnesia, magnesium carbonate, aluminum nitride, boron nitride and diamond. Considering the dispersity, silica, alumina or the combination thereof are some preferable choices. The shape of the heat dispersing particles may be sphere, block, etc., where the sphere shape encompasses shapes which are similar to sphere. In an embodiment, heat dispersing particles may be in a shape of sphere or non-sphere, to ensure the dispersity of the heat dispersing particles and the thermal conductivity of the substrate, wherein the added weight ratio of the spherical and non-spherical heat dispersing particles is 1:0.15˜0.35.
Table 3-1 shows the relationship between the content of the heat dispersing particles and the thermal conductivity of the organosilicon-modified polyimide resin composition. As the content of the heat dispersing particles increases, the thermal conductivity of the organosilicon-modified polyimide resin composition increases. However, when the content of the heat dispersing particles in the organosilicon-modified polyimide resin composition exceeds 1200 parts in weight, the mechanical property of the organosilicon-modified polyimide resin composition may not achieve the strength as required for a filament substrate, resulting in the increase of the defective rate of the product. In an embodiment, high content of heat dispersing particles with high light transmittance or high reflectivity (such as SiO2, Al2O3) may be added, which, in addition to maintaining the transmittance of the organosilicon-modified polyimide resin composition, increases the heat dissipation of the organosilicon-modified polyimide resin composition. The heat conductivities shown in Tables 3-1 and 3-2 were measured by a thermal conductivity meter DRL-III manufactured by Xiangtan city instruments Co., Ltd. under the following test conditions: heating temperature: 90° C.; cooling temperature: 20° C.; load: 350N, after cutting the resultant organosilicon-modified polyimide resin composition into test pieces having a film thickness of 300 μm and a diameter of 30 mm.
For the effects of the particle size and the particle size distribution of the heat dispersing particles on the thermal conductivity of the organosilicon-modified polyimide resin composition, see both Table 3-2 and
Comparing specifications 1, 2 and 3, wherein only heat dispersing particles with medium particle size but different average particle sizes are added, when only heat dispersing particles with medium particle size are added, the average particle size of the heat dispersing particles does not significantly affect the thermal conductivity of the organosilicon-modified polyimide resin composition. Comparing specifications 3 and 4, wherein the average particle sizes are similar, the specification 4 comprising small particle size and medium particle size obviously exhibits higher thermal conductivity than specification 3 comprising only medium particle size. Comparing specifications 4 and 6, which comprise heat dispersing particles with both small particle size and medium particle size, although the average particle sizes of the heat dispersing particles are different, they have no significant effect on the thermal conductivity of the organosilicon-modified polyimide resin composition. Comparing specifications 4 and 7, specification 7, which comprises heat dispersing particles with large particle size in addition to small particle size and medium particle size, exhibits the most excellent thermal conductivity. Comparing specifications 5 and 7, which both comprise heat dispersing particles with large, medium and small particle sizes and have similar average particle sizes, the thermal conductivity of specification 7 is significantly superior to that of specification 5 due to the difference in the particle size distribution. See
Accordingly, the extent of the particle size distribution of the heat dispersing particles affecting the thermal conductivity is greater than that of the average particle size of the heat dispersing particles. When large, medium and small particle sizes of the heat dispersing particles are added, and the small particle size represents about 5-20%, the medium particle size represents about 50-70%, and large particle size represents about 20-40%, the organosilicon-modified polyimide resin will have optimum thermal conductivity. That is because when large, medium and small particle sizes are present, there would be denser packing and contacting each other of heat dispersing particles in a same volume, so as to form an effective heat dissipating route.
In an embodiment, for example, alumina with a particle size distribution of 0.1˜100 μm and an average particle size of 12 μm or with a particle size distribution of 0.1˜20 μm and an average particle size of 4.1 μm is used, wherein the particle size distribution is the range of the particle size of alumina. In another embodiment, considering the smoothness of the substrate, the average particle size may be selected as ⅕˜⅖, preferably ⅕˜⅓ of the thickness of the substrate. The amount of the heat dispersing particles may be 1˜12 times the weight (amount) of the organosilicon-modified polyimide. For example, if the amount of the organosilicon-modified polyimide is 100 parts in weight, the amount of the heat dispersing particles may be 100˜1200 parts in weight, preferably 400˜900 parts in weight. Two different heat dispersing particles such as silica and alumina may be added at the same time, wherein the weight ratio of alumina to silica may be 0.4˜25:1, preferably 1˜10:1.
In the synthesis of the organosilicon-modified polyimide resin composition, a coupling agent such as a silicone coupling agent may be added to improve the adhesion between the solid material (such as the phosphor and/or the heat dispersing particles) and the adhesive material (such as the organosilicon-modified polyimide), and to improve the dispersion uniformity of the whole solid materials, and to further improve the heat dissipation and the mechanical strength of the light-conversion layer. The coupling agent may also be titanate coupling agent, preferably epoxy titanate coupling agent. The amount of the coupling agent is related to the amount of the heat dispersing particles and the specific surface area thereof. The amount of the coupling agent=(the amount of the heat dispersing particles*the specific surface area of the heat dispersing particles)/the minimum coating area of the coupling agent. For example, when an epoxy titanate coupling agent is used, the amount of the coupling agent=(the amount of the heat dispersing particles*the specific surface area of the heat dispersing particles)/331.5.
In other specific embodiments of the present invention, in order to further improve the properties of the organosilicon-modified polyimide resin composition in the synthesis process, an additive such as a defoaming agent, a leveling agent or an adhesive may be selectively added in the process of synthesizing the organosilicon-modified polyimide resin composition, as long as it does not affect light resistance, mechanical strength, heat resistance and chromism of the product. The defoaming agent is used to eliminate the foams produced in printing, coating and curing. For example, acrylic acid or silicone surfactants may be used as the defoaming agent. The leveling agent is used to eliminate the bumps in the film surface produced in printing and coating. Specifically, adding preferably 0.01-2 wt % of a surfactant component can inhibit foams. The coating film can be smoothened by using acrylic acid or silicone leveling agents, preferably non-ionic surfactants free of ionic impurities. Examples of the adhesive include imidazole compounds, thiazole compounds, triazole compounds, organoaluminum compounds, organotitanium compounds and silane coupling agents. Preferably, the amount of these additives is no more than 10% of the weight of the organosilicon-modified polyimide. When the mixed amount of the additive exceeds 10 wt %, the physical properties of the resultant coating film tend to decline, and it even leads to deterioration of the light resistance due to the presence of the volatile components.
Mechanical Strength
The factors affecting the mechanical strength of the organosilicon-modified polyimide resin composition include at least the type of the main material, the siloxane content, the type of the modifier (thermal curing agent), the phosphor and the content of the heat dispersing particles.
Different organosilicon-modified polyimide resins have different properties. Table 4 lists the main properties of the fluorinated aromatic, semi-aliphatic and full aliphatic organosilicon-modified polyimide, respectively, with a siloxane content of about 45% (wt %). The fluorinated aromatic has the best resistance to thermo chromism. The full aliphatic has the best light transmittance. The fluorinated aromatic has both high tensile strength and high elastic modulus. The conditions for testing the mechanical strengths shown in Table 4˜6: the organosilicon-modified polyimide resin composition has a thickness of 50 μm and a width of 10 mm, and the tensile strength of the film is determined according to IS0527-3:1995 standard with a drawing speed of 10 mm/min.
In the manufacture of the filament, the LED chip and the electrodes are first fixed on the filament substrate formed by the organosilicon-modified polyimide resin composition with a die bonding glue, followed by a wiring procedure, in which electric connections are established between adjacent LED chips and between the LED chip and the electrode with wires. To ensure the quality of die bonding and wiring, and to improve the product quality, the filament substrate should have a certain level of elastic modulus to resist the pressing force in the die bonding and wiring processes. Accordingly, the filament substrate should have an elastic modulus more than 2.0 GPa, preferably 2˜6 GPa, more preferably 4˜6 GPa. Table 5 shows the effects of different siloxane contents and the presence of particles (phosphor and alumina) on the elastic modulus of the organosilicon-modified polyimide resin composition. Where no fluorescent powder or alumina particle is added, the elastic modulus of the organosilicon-modified polyimide resin composition is always less than 2.0 GPa, and as the siloxane content increases, the elastic modulus tends to decline, i.e. the organosilicon-modified polyimide resin composition tends to soften. However, where phosphor and alumina particles are added, the elastic modulus of the organosilicon-modified polyimide resin composition may be significantly increased, and is always higher than 2.0 GPa. Accordingly, the increase in the siloxane content may lead to softening of the organosilicon-modified polyimide resin composition, which is advantageous for adding more fillers, such as more phosphor or heat dispersing particles. In order for the substrate to have superior elastic modulus and thermal conductivity, appropriate particle size distribution and mixing ratio may be selected so that the average particle size is within the range from 0.1 μm to 100 μm or from 1 μm to 50 μm.
In order for the LED filament to have good bending properties, the filament substrate should have an elongation at break of more than 0.5%, preferably 1˜5%, most preferably 1.5˜5%. As shown in Table 5, where no fluorescent powder or alumina particle is added, the organosilicon-modified polyimide resin composition has excellent elongation at break, and as the siloxane content increases, the elongation at break increases and the elastic modulus decreases, thereby reducing the occurrence of warpage. In contrast, where phosphor and alumina particles are added, the organosilicon-modified polyimide resin composition exhibits decreased elongation at break and increased elastic modulus, thereby increasing the occurrence of warpage.
By adding a thermal curing agent, not only the heat resistance and the glass transition temperature of the organosilicon-modified polyimide resin are increased, the mechanical properties, such as tensile strength, elastic modulus and elongation at break, of the organosilicon-modified polyimide are also increased. Adding different thermal curing agents may lead to different levels of improvement. Table 6 shows the tensile strength and the elongation at break of the organosilicon-modified polyimide resin composition after the addition of different thermal curing agents. For the full aliphatic organosilicon-modified polyimide, the addition of the thermal curing agent EHPE3150 leads to good tensile strength, while the addition of the thermal curing agent KF105 leads to good elongation.
The organosilicon-modified polyimide resin composition of the present embodiment may be used in a form of film or as a substrate together with a support to which it adheres. The film forming process comprises three steps: (a) coating step: spreading the above organosilicon-modified polyimide resin composition on a peelable body by coating to form a film; (b) heating and drying step: heating and drying the film together with the peelable body to remove the solvent from the film; and (c) peeling step: peeling the film from the peelable body after the drying is completed to give the organosilicon-modified polyimide resin composition in a form of film. The above peelable body may be a centrifugal film or other materials which do not undergo chemical reaction with the organosilicon-modified polyimide resin composition, e.g., PET centrifugal film.
The organosilicon-modified polyimide resin composition may be adhered to a support to give an assembly film, which may be used as the substrate. The process of forming the assembly film comprises two steps: (a) coating step: spreading the above organosilicon-modified polyimide resin composition on a support by coating to from an assembly film; and (b) heating and drying step: heating and drying the assembly film to remove the solvent from the film.
In the coating step, roll-to-roll coating devices such as roller coater, mold coating machine and blade coating machine, or simple coating means such as printing, inkjeting, dispensing and spraying may be used.
The drying method in the above heating and drying step may be drying in vacuum, drying by heating, or the like. The heating may be achieved by a heat source such as an electric heater or a heating media to produce heat energy and indirect convection, or by infrared heat radiation emitted from a heat source.
A film (composite film) with high thermal conductivity can be obtained from the above organosilicon-modified polyimide resin composition by coating and then drying and curing, so as to achieve any one or combination of the following properties: superior light transmittance, chemical resistance, heat resistance, thermal conductivity, film mechanical property and light resistance. The temperature and time in the drying and curing step may be suitably selected according to the solvent and the coated film thickness of the organosilicon-modified polyimide resin composition. The weight change of the organosilicon-modified polyimide resin composition before and after the drying and curing as well as the change in the peaks in the IR spectrum representing the functional groups in the thermal curing agent can be used to determine whether the drying and curing are completed. For example, when an epoxy resin is used as the thermal curing agent, whether the difference in the weight of the organosilicon-modified polyimide resin composition before and after the drying and curing is equal to the weight of the added solvent as well as the increase or decrease of the epoxy peak before and after the drying and curing are used to determine whether the drying and curing are completed.
In an embodiment, the amidation is carried out in a nitrogen atmosphere, or vacuum defoaming is employed in the synthesis of the organosilicon-modified polyimide resin composition, or both, so that the volume percentage of the cells in the organosilicon-modified polyimide resin composition composite film is 5˜20%, preferably 5˜10%. As shown in
When the organosilicon-modified polyimide resin composition is prepared by vacuum defoaming, the vacuum used in the vacuum defoaming may be −0.5˜−0.09 MPa, preferably −0.2˜−0.09 MPa. When the total weight of the raw materials used in the preparation of the organosilicon-modified polyimide resin composition is less than or equal to 250 g, the revolution speed is 1200˜2000 rpm, the rotation speed is 1200˜2000 rpm, and time for vacuum defoaming is 3˜8 min. This not only maintains certain amount of cells in the film to improve the uniformity of light emission, but also keeps good mechanical properties. The vacuum may be suitably adjusted according to the total weight of the raw materials used in the preparation of the organosilicon-modified polyimide resin composition. Normally, when the total weight is higher, the vacuum may be reduced, while the stirring time and the stirring speed may be suitably increased.
According to the present disclosure, a resin having superior transmittance, chemical resistance, resistance to thermochromism, thermal conductivity, film mechanical property and light resistance as required for a LED soft filament substrate can be obtained. In addition, a resin film having a high thermal conductivity can be formed by simple coating methods such as printing, inkjeting, and dispensing.
When the organosilicon-modified polyimide resin composition composite film is used as the filament substrate (or base layer), the LED chip is a hexahedral luminous body. In the production of the LED filament, at least two sides of the LED chip are coated by a top layer. When the prior art LED filament is lit up, non-uniform color temperatures in the top layer and the base layer would occur, or the base layer would give a granular sense. Accordingly, as a filament substrate, the composite film is required to have superior transparency. In other embodiments, sulfonyl group, non-coplanar structure, meta-substituted diamine, or the like may be introduced into the backbone of the organosilicon-modified polyimide to improve the transparency of the organosilicon-modified polyimide resin composition. In addition, in order for the bulb employing said filament to achieve omnidirectional illumination, the composite film as the substrate should have certain flexibility. Therefore, flexible structures such as ether (such as (4,4′-bis(4-amino-2-trifluoromethylphenoxy)diphenyl ether), carbonyl, methylene may be introduced into the backbone of the organosilicon-modified polyimide. In other embodiments, a diamine or dianhydride comprising a pyridine ring may be employed, in which the rigid structure of the pyridine ring can improve the mechanical properties of the composite film. Meanwhile, by using it together with a strong polar group such as —F, the composite film may have superior light transmittance. Examples of the anhydride comprising a pyridine ring include 2,6-bis(3′,4′-dicarboxyphenyl)-4-(3″,5″-bistrifluoromethylphenyl)pyridine dianhydride.
The LED filament structure in the aforementioned embodiments is mainly applicable to the LED light bulb product, so that the LED light bulb can achieve the omni-directional light illuminating effect through the flexible bending characteristics of the single LED filament. The specific embodiment in which the aforementioned LED filament applied to the LED light bulb is further explained below.
Please refer to
The lamp housing 12 is a material which is preferably light transmissive or thermally conductive, such as, glass or plastic, but not limited thereto. In implementation, the lamp housing 12 may be doped with a golden yellow material or its surface coated with a yellow film to absorb a portion of the blue light emitted by the LED chip to reduce the color temperature of the light emitted by the LED light bulb 20c. In other embodiments of the present invention, the lamp housing 12 includes a layer of luminescent material (not shown), which may be formed on the inner surface or the outer surface of the lamp housing 12 according to design requirements or process feasibility, or even integrated in the material of the lamp housing 12. The luminescent material layer comprises low reabsorption semiconductor nanocrystals (hereinafter referred to as quantum dots), the quantum dots comprises a core, a protective shell and a light absorbing shell, and the light absorbing shell is disposed between the core and the protective shell. The core emits the emissive light with emission wavelength, and the light absorbing shell emits the excited light with excitation wavelength. The emission wavelength is longer than the excitation wavelength, and the protective shell provides the stability of the light.
The LED filament 100 shown in
The stem 19 has a stand 19a extending to the center of the lamp housing 12. The stand 19a supports the supporting arms 15. The first end of each of the supporting arms 15 is connected with the stand 19a while the second end of each of the supporting arms 15 is connected with the LED filament 100.
Please refer to
The supporting arms 15 may be, but not limited to, made of carbon steel spring to provide with adequate rigidity and flexibility so that the shock to the LED light bulb caused by external vibrations is absorbed and the LED filament 100 is not easily to be deformed. Since the stand 19a extending to the center of the lamp housing 12 and the supporting arms 15 are connected to a portion of the stand 19a near the top thereof, the position of the LED filaments 100 is at the level close to the center of the lamp housing 12. Accordingly, the illumination characteristics of the LED light bulb 20c are close to that of the traditional light bulb including illumination brightness. The illumination uniformity of LED light bulb 20c is better. In the embodiment, at least a half of the LED filaments 100 is around a center axle of the LED light bulb 20c. The center axle is coaxial with the axle of the stand 19a.
In the embodiment, the first end of the supporting arm 15 is connected with the stand 19a of the stem 19. The clamping portion of the second end of the supporting arm 15 is connected with the outer insulation surface of the LED filaments 100 such that the supporting arms 15 are not used as connections for electrical power transmission. In an embodiment where the stem 19 is made of glass, the stem 19 would not be cracked or exploded because of the thermal expansion of the supporting arms 15 of the LED light bulb 20c. Additionally, there may be no stand in an LED light bulb. The supporting arm 15 may be fixed to the stem or the lamp housing directly to eliminate the negative effect to illumination caused by the stand.
The supporting arm 15 is thus non-conductive to avoid a risk that the glass stem 19 may crack due to the thermal expansion and contraction of the metal filament in the supporting arm 15 under the circumstances that the supporting arm 15 is conductive and generates heat when current passes through the supporting arm 15.
In different embodiments, the second end of the supporting arm 15 may be directly inserted inside the LED filament 100 and become an auxiliary piece in the LED filament 100, which can enhance the mechanical strength of the LED filament 100. Relative embodiments are described later.
The LED filament 100 shown in
Please refer to
As shown in
In an embodiment, the LED light bulb 20c shown in
As shown in
The two conductive electrodes (i.e., the welding points, the joint points, the contacting points, or the fusing points) are symmetrically disposed at two sides of a y-axis of the xyz coordinates. A z-axis of the xyz coordinates is coaxial with stem 19 (or is coaxial with a central axis passing through a horizontal plane of the LED light bulb 20c). The shape of the LED filament 100 varies along an x-direction, a y-direction, and a z-direction according to t, and t is a variable between 0 and 1. A position of points of the LED filament 100 in the xyz coordinates is defined as X, Y, and Z and satisfies the curve equation. Herein, the term “points of the LED filament” means “most of points of the LED filament”, or “more than 60% of points of the LED filament.” The curve equation is:
X=m1*cos(t*360),
Y=m2*sin(t*360),
Z=n*cos(t*360*k),
The LED filament 100 varies along the x-direction, the y-direction, and the z-direction according to t. When X=0, |Y|max=m2 (a max value of |Y| is m2), and |Z|max=n (a max value of |Z| is n). When Y=0, |X|max=ml (a max value of |X| is m1), and |Z|max=n (the max value of |Z| is n). When Z=0, |X|max=ml (the max value of |X| is m1), and |Y|max=m2 (the max value of |Y| is m2). m1 is a length (projection length) in the x-direction, and 24≤m1≤27 (mm). m2 is a length (projection length) in the y-direction, and 24≤m≤2≤27 (mm). Based upon the above configuration, the LED filament 100 in the lamp housing 12 may provide good luminous flux. n is a height of the highest point of the LED filament 100 from the x-y plane in the z-direction, and 0<n≤14 (mm). Based upon the above condition, wires in turning points of the LED filament 100 may hard to break. k is a number of the highest point(s). The more the supporting arms (or supporting bars), the hard the manufacture is; therefore, k is configured as: 2≤k≤8. A curve line drawn by the above curve equation may be deemed as a reference for the LED filament 100 being distributed in space. According to conditions of different arts and equipment, the configuration of the LED filament 100 in practice may have about 0 to 25% in spatial difference different from the reference based upon the curve equation. Certain region(s) on the filament with supporting point(s) may be relatively highest point(s) and lowest point(s). The spatial difference of the certain region(s) may be less, e.g., 0 to 20%. In an embodiment, r is the radius of a cross section of the lamp housing on the horizontal plane. Cross sections of the lamp housing on the horizontal plane from the bottom to the top of the lamp housing along the height direction may have varied radii, and the radius r is the one with the largest value. In such case, the values of m1, m2, and n may be set as: 0.8*r≤m1≤0.9*r; 0.8*r≤m2≤0.9*r; 0<n≤0.47*r. Additionally, p is the radius of an interface of the bulb base utilized for being connected to the lamp housing, G is the length of the LED filament, and, in such case, the values of G may be set as: 1.2*p≤G≤5.6*r. Based upon the above setting, the LED filament may not only achieve the aforementioned effect, but may also need the least length and the least number of the LED chips. As a result, the cost of materials for the manufacture of the LED light bulb may reduce, and the temperature of the LED light bulb during operation can be suppressed.
The meaning of the term “a single LED filament” and “a single strip LED filament” as used in the present invention is mainly composed of the aforementioned conductive section, the LED section, the connection between thereof, the light conversion layer (including the consecutive top layer or the bottom layer, with continuous formation to cover or support all the components), and two conductive electrodes electrically connected to the conductive brackets of the LED light bulb disposing at both ends of the LED filament, which is the single LED filament structure referred to in the present invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201410510593.6 | Sep 2014 | CN | national |
| 201510053077.X | Feb 2015 | CN | national |
| 201510316656.9 | Jun 2015 | CN | national |
| 201510347410.8 | Jun 2015 | CN | national |
| 201510489363.0 | Aug 2015 | CN | national |
| 201510502630.3 | Aug 2015 | CN | national |
| 201510555889.4 | Sep 2015 | CN | national |
| 201510966906.3 | Dec 2015 | CN | national |
| 201610041667.5 | Jan 2016 | CN | national |
| 201610272153.0 | Apr 2016 | CN | national |
| 201610281600.9 | Apr 2016 | CN | national |
| 201610394610.3 | Jun 2016 | CN | national |
| 201610544049.2 | Jul 2016 | CN | national |
| 201610586388.7 | Jul 2016 | CN | national |
| 201610936171.4 | Nov 2016 | CN | national |
| 201611108722.4 | Dec 2016 | CN | national |
| 201710024877.8 | Jan 2017 | CN | national |
| 201710079423.0 | Feb 2017 | CN | national |
| 201710138009.2 | Mar 2017 | CN | national |
| 201710180574.5 | Mar 2017 | CN | national |
| 201710234618.8 | Apr 2017 | CN | national |
| 201710316641.1 | May 2017 | CN | national |
| 201710839083.7 | Sep 2017 | CN | national |
| 201730450712.8 | Sep 2017 | CN | national |
| 201730453237.X | Sep 2017 | CN | national |
| 201730453239.9 | Sep 2017 | CN | national |
| 201710883625.0 | Sep 2017 | CN | national |
| 201730489929.X | Oct 2017 | CN | national |
| 201730517887.6 | Oct 2017 | CN | national |
| 201730520672.X | Oct 2017 | CN | national |
| 201730537542.7 | Nov 2017 | CN | national |
| 201730537544.6 | Nov 2017 | CN | national |
| 201711434993.3 | Dec 2017 | CN | national |
| 201711477767.3 | Dec 2017 | CN | national |
| 201810031786.1 | Jan 2018 | CN | national |
| 201810065369.9 | Jan 2018 | CN | national |
| 201810343825.1 | Apr 2018 | CN | national |
| 201810344630.9 | Apr 2018 | CN | national |
| 201810498980.0 | May 2018 | CN | national |
| 201810501350.4 | May 2018 | CN | national |
| 201810573314.9 | Jun 2018 | CN | national |
| 201810836433.9 | Jul 2018 | CN | national |
| 201810943054.X | Aug 2018 | CN | national |
| 201811005145.5 | Aug 2018 | CN | national |
| 201811005536.7 | Aug 2018 | CN | national |
| 201811079889.1 | Sep 2018 | CN | national |
| 201811277980.4 | Oct 2018 | CN | national |
| 201811285657.1 | Oct 2018 | CN | national |
| 201811378173.1 | Nov 2018 | CN | national |
| 201811378189.2 | Nov 2018 | CN | national |
| 201811549205.X | Dec 2018 | CN | national |
This application is a continuation application of U.S. application Ser. No. 16/234,124 filed on Dec. 27, 2018, which claims priority to Chinese Patent Applications No. 201510502630.3 filed on Aug. 17, 2015; No. 201510966906.3 filed on Dec. 19, 2015; No. 201610041667.5 filed on Jan. 22, 2016; No. 201610272153.0 filed on Apr. 27, 2016; No. 201610394610.3 filed on Jun. 3, 2016; No. 201610586388.7 filed on Jul. 22, 2016; No. 201610544049.2 filed on Jul. 7, 2016; No. 201610936171.4 filed on Nov. 1, 2016; No. 201611108722.4 filed on Dec. 6, 2016; No. 201610281600.9 filed on Apr. 29, 2016; No. 201710024877.8 filed on Jan. 13, 2017; No. 201710079423.0 filed on Feb. 14, 2017; No. 201710138009.2 filed on Mar. 9, 2017; No. 201710180574.5 filed on Mar. 23, 2017; No. 201710234618.8 filed on Apr. 11, 2017; No. 201410510593.6 filed on Sep. 28, 2014; No. 201510053077.X filed on Feb. 2, 2015; No. 201510316656.9 filed on Jun. 10, 2015; No. 201510347410.8 filed on Jun. 19, 2015; No. 201510489363.0 filed on Aug. 7, 2015; No. 201510555889.4 filed on Sep. 2, 2015; No. 201710316641.1 filed on May 8, 2017; No. 201710839083.7 filed on Sep. 18, 2017; No. 201710883625.0 filed on Sep. 26, 2017; No. 201730450712.8 filed on Sep. 21, 2017; No. 201730453239.9 filed on Sep. 22, 2017; No. 201730453237.X filed on Sep. 22, 2017; No. 201730537542.7 filed on Nov. 3, 2017; No. 201730537544.6 filed on Nov. 3, 2017; No. 201730520672.X filed on Oct. 30, 2017; No. 201730517887.6 filed on Oct. 27, 2017; No. 201730489929.X filed on Oct. 16, 2017; No. 201711434993.3 filed on Dec. 26, 2017; No. 201711477767.3 filed on Dec. 29, 2017; No. 201810031786.1 filed on Jan. 12, 2018; No. 201810065369.9 filed on Jan. 23, 2018; No. 201810343825.1 filed on Apr. 17, 2018; No. 201810344630.9 filed on Apr. 17, 2018; No. 201810501350.4 filed on May 23, 2018; No. 201810498980.0 filed on May 23, 2018; No. 201810573314.9 filed on Jun. 6, 2018; No. 201810836433.9 filed on Jul. 26, 2018; No. 201810943054.X filed on Aug. 17, 2018; No. 201811005536.7 filed on Aug. 30, 2018; No. 201811005145.5 filed on Aug. 30, 2018; No. 201811079889.1 filed on Sep. 17, 2018; No. 201811277980.4 filed on Oct. 30, 2018; No. 201811285657.1 filed on Oct. 31, 2018; No. 201811378173.1 filed on Nov. 19, 2018; No. 201811378189.2 filed on Nov. 19, 2018; No. 201811549205.X filed on Dec. 18, 2018, each of which is hereby incorporated by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16234124 | Dec 2018 | US |
| Child | 16408484 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 15858036 | Dec 2017 | US |
| Child | 16234124 | US | |
| Parent | 29627379 | Nov 2017 | US |
| Child | 15858036 | US | |
| Parent | 29619287 | Sep 2017 | US |
| Child | 29627379 | US | |
| Parent | 15723297 | Oct 2017 | US |
| Child | 29619287 | US | |
| Parent | 15168541 | May 2016 | US |
| Child | 15723297 | US | |
| Parent | 15308995 | Nov 2016 | US |
| Child | 15168541 | US | |
| Parent | 15499143 | Apr 2017 | US |
| Child | 15308995 | US | |
| Parent | 15384311 | Dec 2016 | US |
| Child | 15499143 | US | |
| Parent | 15366535 | Dec 2016 | US |
| Child | 15384311 | US | |
| Parent | 15237983 | Aug 2016 | US |
| Child | 15366535 | US |