This invention relates generally to Li recovery processes and the onsite production of chemicals used in Li recovery processes. The invention can be used to improve Li extraction from various sources, including brine sources or lithium ore sources where hydrochloric acid, sodium hydroxide, and/or sulfuric acid may be required. The invention can eliminate the need to outsource the acid and base feed materials by utilizing the already available brine onsite, whether derived from salar brine or a brine solution that is produced in the lithium ore refining process or a brine produced during a lithium ion battery recycling process. The invention can also be used to directly convert lithium containing salts, e.g. lithium chloride or lithium sulfate, to higher value lithium hydroxide product. The invention can also provide a gas diffusion electrode configured for use in a membrane electrolysis cell and a method of producing the gas diffusion electrode. Additionally, the invention can provide a membrane electrolysis cell for processing a salt-containing solution. The invention can also provide a process for purifying or concentrating or producing LiOH using a membrane electrolysis cell.
Lithium has found an ever-increasing attention over the past few decades due to the advent of lithium ion batteries (LIBs) as the main source of energy storage for automobile and electronic application. The electric vehicle (EV) market, which is heavily depending on LIBs, is also expanding at record pace over the last decade and is expected to share 20% of the transportation market with internal combustion engines. Renewable energy generation including solar and wind applications are also expected to rely on LIBs for load leveling purposes. Recovering, such as by recycling Li from LIBs, is considered to be a secondary resource for lithium. Beside batteries, Li also has applications in glass and ceramics, chemicals and pharmaceuticals, metallurgicals and greases. Accordingly, there remains a growing need for improved Li recovery processes and related equipment.
Disclosed herein as an aspect of this invention is a gas diffusion electrode for use in a membrane electrolysis cell. The gas diffusion electrode comprises a diffusion layer configured to diffuse a gas; a hydrophilic catalyst layer disposed on a surface of the diffusion layer, the hydrophilic catalyst layer having a hydrophilicity greater than that of the diffusion layer and being capable of transporting negative ions; and an ion exchange membrane disposed on a surface of the hydrophilic catalyst layer, the ion exchange membrane being configured to exchange ions from the hydrophilic catalyst layer to an opposed surface of the ion exchange membrane.
Also disclosed according to another aspect of this invention is a method of producing a gas diffusion electrode for use in a membrane electrolysis cell. The method comprises disposing a hydrophilic catalyst layer on a surface of a diffusion layer, the hydrophilic catalyst layer having a hydrophilicity greater than that of the diffusion layer; and disposing an ion exchange membrane on a surface of the catalyst layer, the ion exchange membrane being configured to exchange ions from the catalyst layer to an opposed surface of the ion exchange membrane and to prevent flooding of the catalyst layer.
A membrane electrolysis cell for processing a salt-containing solution is also disclosed according to another aspect of this invention. The membrane electrolysis cell comprises an inlet through which the salt-containing solution is introduced into an interior of the membrane electrolysis cell; an anode positioned to extend within the interior of the membrane electrolysis cell and positioned in an anode compartment; a cathode comprising a gas diffusion electrode positioned to extend within the interior of the membrane electrolysis cell and positioned in a cathode compartment, the gas diffusion electrode including a diffusion layer configured to diffuse gas and a hydrophilic catalyst layer disposed on a surface of the diffusion layer, the hydrophilic catalyst layer having a hydrophilicity greater than that of the diffusion layer and the hydrophilic catalyst layer being configured to transport negative ions; a gas inlet through which a gas comprising O2 is introduced into contact with the gas diffusion electrode; a first ion exchange membrane interposed between the anode compartment and the hydrophilic catalyst layer of the gas diffusion electrode, the first ion exchange membrane being configured to exchange ions received from the anode to an opposed surface of the first ion exchange membrane; and at least one outlet through which a product of the salt solution is removed from an interior of the membrane electrolysis cell.
Finally, a process for purifying or concentrating LiOH using a membrane electrochemical cell is disclosed according to yet another aspect of this invention.
Although the invention is illustrated and described herein with reference to specific embodiments, the invention is not intended to be limited to the details shown. Rather, various modifications may be made in the details within the scope and range of equivalents of the claims and without departing from the invention.
The invention, according to one aspect, makes it possible to provide a unique gas diffusion electrode that can use ambient undried, humid air as a source of oxygen. This gas diffusion electrode, according to one embodiment, is used only at the cathode of the membrane electrolysis cells as disclosed herein.
According to additional aspects of this invention, the invention makes it possible to improve Li extraction from various sources, including brine sources or lithium ore sources where hydrochloric acid, sodium hydroxide, and/or sulfuric acid may be required; eliminate the need to outsource the acid and base feed materials by utilizing the already available brine onsite, whether derived from salar brine or a brine solution that is produced in the lithium ore refining process or a brine produced during a lithium ion battery recycling process; directly convert lithium containing salts, e.g. lithium chloride or lithium sulfate, to higher value lithium hydroxide product; provide a gas diffusion electrode configured for use in a membrane electrolysis cell and a method of producing the gas diffusion electrode; provide a membrane electrolysis cell for processing a salt-containing solution; and/or provide a process for purifying or concentrating or producing LiOH using a membrane electrolysis cell.
As used herein the term, “hydrophobic” means lacking an affinity for, repelling, or failing to adsorb or absorb water. In particular, a hydrophobic substance is one which has a contact angle greater than 90° when a droplet of water is placed on it.
As used herein the term, “hydrophilic” means having an affinity for and being capable of adsorbing or absorbing water. In particular, a hydrophilic material is one where the contact angle between a droplet of water and the material is less than 90°.
As used herein, the terms “oxygen depolarized cathode” or “ODC,” and “gas diffusion cathode” or “GDC,” may be used interchangeably and/or refer to the same structure, which is used for example, as the cathode in a membrane electrolysis cell.
Lithium Extraction from Brines
An increasing demand for the lithium requires matching production levels. In its free metallic form, lithium is extremely reactive. Hence, it is usually found in the form of mineral compounds comprising about 0.007% of the earth's crust as the primary source of lithium. Natural sources of lithium include igneous rocks, springs, sea and ocean water, as well as salar brines, which are underground reservoirs that contain high concentrations of dissolved salts, such as lithium, potassium, and sodium. These are generally found below the surface of dried lakebeds, known as salars.
Most lithium products are from brine sources, and most lithium is recovered from the salar brines or salt lake brines that occur in the Earth's crust and which contain lithium. The concentration of lithium in sea water is about 0.17 mg/L. Geothermal water and oil-well brines are also another source of recoverable lithium. Lithium salt-containing brines that may be produced during lithium ion battery recycling processes are also a source of recoverable lithium. Lithium recovery from these brines can be less expensive than mining the lithium from the mineral rocks.
While the following disclosure presents embodiments directed to recovering lithium from salar brines, or from lithium brines produced during processes to recover lithium from lithium ores, lithium salt solutions, also referred to herein as “brine,” may also be sourced from lithium ion battery recycling processes.
The first attempt at commercial extraction of lithium from salt lake was reported in 1936 at the Searles Lake in the US. An ever-increasing growth in the extraction of lithium from the salt lakes has occurred since then. The brine concentration, pond accessibility and locality for solar evaporation, ratio of alkaline earth and alkali metal to lithium and the complexity of the chemistry are important factors when considering a brine as a Li recovery source.
The recovery of lithium from brine on an industrial scale can commence with a series of multiple stages of continuous solar pond evaporation of water from the brine. The lithium concentration of major brine extraction operations in the world ranges from 0.06 to 0.15 wt. % of the element lithium. This concentration reaches about 6 wt. % at the end of the evaporation cycle when it is ready for lithium carbonate (Li2CO3) production, or the production of LiOH as the desired end product. During the evaporation stage, salts with a lower solubility limit than the lithium salts precipitate out of the brine. Halite salts such as (NaCl) is the first to precipitate followed by sylvite (KCl), sylvanite (NaCl·KCl) and other salts. KCl is the main by-product in most brine recovery operations.
Some salar brines which contain higher Mg, Ca, and B content, require additional processing steps to remove these elements. Magnesium and calcium are preferably removed in order for the final product to be utilized in battery applications. Boron contamination is also harmful to the quality of the end product and has to be removed during the extraction process to achieve LIB quality requirement. During the evaporation stage, some compounds of Mg such as carnallite (KCl·MgCl2·6H2O) and bischoffite (MgCl2·6H2O) precipitate at around 4.4 wt. % elemental Li concentration in the brine. After further evaporation to reach 5-6 wt. % Li, the co-precipitation of compounds such as lithium carnallite (LiCl·MgCl2·6H2O) along with lithium carbonate or lithium chloride results leaves the final product with Mg contamination. To obtain a pure lithium carbonate or chloride product, these contaminants are preferably removed.
The removal process of Ca, Mg and B from the brine involves solvent extraction and precipitation stages. For example, boron can be removed by a solvent extraction process or the precipitation of boric acid. In the solvent extraction method, extractants such as high aliphatic alcohols or other organic solvents are used in an acidic environment to remove boron from the brine. Under acidic conditions, boron compounds form boric acid which precipitates out of the brine.
Numerous systems have been reported on development of boron removal process from lithium-containing brine. For instance, U.S. Pat. No. 3,855,392 describes the use of high aliphatic alcohol for extraction of boron from magnesium brine. Similarly, U.S. Pat. No. 4,980,136 describes the use of high aliphatic alcohol with 6 to 16 carbon atoms dissolved in kerosene at pH levels of 1 to 2 for extracting the boron from brine. U.S. Pat. Nos. 3,424,563 and 5,939,038 describe the use of diols which are organic molecules containing two OH groups in their structures as extractants for boron removal. U.S. Pat. No. 4,261,960 discloses a boron, magnesium and calcium removal process involving the use of slaked lime (Ca(OH)2) and calcium chloride solution to precipitate calcium borate hydrate as well as magnesium hydroxide and calcium sulfate dihydrate from the brine.
Magnesium and calcium can be removed from the brine through several precipitation processes. Converting the dissolved magnesium salt into magnesium hydroxide removes magnesium from the brine. Calcium hydroxide, lime (CaO) or slaked lime (Ca(OH)2) is added to the brine to increase the pH and form Mg(OH)2 which has limited solubility in water. During this process, sulfate ions also precipitate in the form of CaSO4 and boron precipitates in the form of calcium borate hydrate. The precipitation of Mg(OH)2 is also beneficial in further removal of boron though surface adsorption mechanism.
The adjustment of pH can be effected through different mediums. U.S. Pat. Nos. 4,036,713 and 4,207,297, disclose using the lithium hydroxide product form the recovery product to raise the pH of the initial brine and thereby precipitating the magnesium hydroxide. These patents also disclose the use of other basic solutions including sodium hydroxide or calcium hydroxide. U.S. Pat. No. 6,143,260 discloses the use of limed mother liquor from a previous lithium precipitation stage to remove Mg by precipitating the Mg(OH)2. U.S. Pat. No. 6,048,507 discloses a bicarbonation process comprising mixing the impure lithium carbonate brine with CO2 gas under pressure to precipitate unwanted species of iron, magnesium and calcium. Further removal of Fe, Mg and Ca ions is carried out by selective ion exchange process.
U.S. Pat. No. 5,993,759 describes a multistage process for purifying the lithium carbonate brine of high Mg content using soda ash, slaked lime and organic extractant. The process starts with an acidification step using hydrochloric acid (HCl) to maintain a pH level of 0 to 4 in order to produce boric acid (H3BO3) and which is removed through crystallization. The resulting boron-depleted brine is further purified using organic solvent extractant to achieve boron-free brine. The resulting brine diluted by a mother liquor is then treated by addition of sodium carbonate (soda ash) yielding magnesium carbonate as the solid precipitate. The rest of magnesium in the brine is further precipitated using calcium hydroxide and so forms Mg(OH)2. During this stage, any calcium introduced to the brine also precipitates in the form of calcium carbonate due to the presence of sodium carbonate in the brine. The addition of soda ash at the last step results in the precipitation of lithium carbonate.
U.S. Pat. No. 8,691,169 discloses that the sequence of adding these compounds to the brine plays an important role in producing high purity lithium carbonate. The disclosure shows that the addition of calcium hydroxide before the brine removal step can remove all soluble magnesium as well as some boron and surface ions in the post-evaporation brine. The rest of boron in the brine is removed via solvent extraction. The resulting magnesium and boron-free brine is then carbonized by soda ash to obtain high purity lithium carbonate precipitates. The obtained Li2CO3 was further purified by adding carbonic acid, forming lithium bicarbonate and then precipitation of pure lithium carbonate is effected by heating the bicarbonate-containing brine. The last stage is disclosed to remove all sodium and calcium impurities from the final precipitate product.
The final lithium product is produced from the resulting brine from which most of Mg, B, Ca, and other species have been removed. Soda ash (sodium carbonate, i.e. Na2CO3) is a reagent for converting the solute Li ions into Li2CO3 precipitate. This precipitate can be used in technical or high purity grade. Depending on the nature of the process, the initial composition of the brine and the customer demand, the Li recovery process can be designed and modified. For technical grade lithium carbonate, the common recovery process of pond evaporation and concentration, selective removal of contaminants and carbonation is sufficient.
For high purity and battery grade product, several extra processing stages have been proposed. For instance, U.S. Pat. No. 9,169,125 B2 discloses the use of spray drying, washing and carbonation after the contaminant removal to obtain purified lithium carbonate product. Bicarbonation of the lithium carbonate can be used for purifying the final product.
U.S. Pat. No. 8,691,169 B2 discloses the use of carbonic acid to form lithium bicarbonate from the lithium carbonate. The resulting bicarbonate is then decomposed to purified carbonate upon exposure to heat at 50 to 95° C. Another method for further purification of the brine prior to lithium carbonate precipitation is the implementation of ion exchange resins. Lithium carbonate products with purity as high as 99.9% can be achieved by using this method in the process.
WO Pat. Appln. Publ. No. 2013/036983 discloses the use of ion exchange resins throughout the recovery process. Also disclosed therein is an ion exchange resin for boron removal, which replaces the solvent extraction method. An ion exchange resin to remove the trace soluble divalent and trivalent species containing Mg, Ca and Fe from the brine during the final stages of the recovery is also disclosed. U.S. Pat. No. 8,641,992 discloses ion exchange resin by which Mg ions are selectively removed from the brine.
Generally, a process for the recovery of lithium from brine can be illustrated as shown in
Some of the magnesium in the form of precipitated MgCl2 is also removed during this evaporative stage. Next stages involve the removal of boron, calcium, magnesium as the main sources of impurity in the brine. Removal of the B, Ca and Mg ions is carried out using repeated pH adjustment, solvent extraction and precipitation steps to ensure maximum ion removal. Ion exchange removal of leftover trace monovalent, divalent and trivalent ionic species other than the lithium further purifies the brine. Introduction of soda ash, Na2CO3, to convert the dissolved lithium salts to lithium carbonate, Li2CO3, is the last major step to produce technical and high purity lithium carbonate.
As expected, almost every brine recovery operation, no matter the source of the brine heavily relies on the use of reagents throughout the process stages. Generally, more than 50% of the overall operating costs in lithium production usually stems from the cost of these reagents. The major reagents contributing to the recovery cost are soda ash (Na2CO3), lime (primarily CaCO3) and slaked lime (Ca(OH)2), caustic soda (NaOH), hydrochloric acid (HCl), extractants such as high aliphatic alcohols or other organic solvents, and sulfuric acid (H2SO4).
Soda ash or sodium carbonate (Na2CO3) is the major component of a lithium recovery process due to its importance for various lithium recovery stages. It is used to remove calcium from the brine through precipitation of CaCO3. It is also the sole reagent used for producing lithium carbonate.
Slaked lime or calcium hydroxide (Ca(OH)2) produced from heating and then hydrating the lime (primarily CaCO3), can be used for the removal of magnesium and some sulfate ions. Different grades of lime could be used based in the use of lime in the initial evaporation pond or the lithium carbonate processing plant. For instance, the removal of magnesium chloride and sulfate and other sulfate ions from the brine using the slaked lime occurs according to the following reactions:
MgCl2(aq.)+Ca(OH)2(aq.)⇔Mg(OH)2(s)+CaCl2)(aq.) 1)
MgSO4(aq.)+Ca(OH)2(aq.)⇔Mg(OH)2(s)+CaSO4(s) 2)
Na2SO4(aq.)+Ca(OH)2(aq.)⇔CaSO4(s)+NaOH(aq.) 3)
Caustic soda or sodium hydroxide (NaOH) is another chemical reagent that can be used in different stages of the processing plant. It can be used as the stripping agent to regenerate the solvent after the boron removal using the organic solvent extraction. It is also the most suitable alkali metal hydroxide for the removal of magnesium because it produces very high purity Mg(OH)2 as a by-product. Another important use of the NaOH is during the water treatment process for pH adjustment, as well as for ion exchange resin regeneration.
Similar to caustic, hydrochloric acid (HCl) can be used as a reagent in a variety of the process steps throughout the recovery process. It can be used as a pH modifier during the boron solvent extraction step since the initial stage of solvent extraction normally requires an acidic environment. Another use of hydrochloric acid is in the concentration ponds (also called evaporation ponds) where adding it prevents the unwanted precipitation of lithium carbonate. HCl is also the main reagent for transformation of lithium carbonate into lithium chloride when needed. Hydrochloric acid is also used to regenerate the acid exchange resins which are used for selective ion removal from brine. Sulfuric acid (H2SO4) can be stored in the concentrated 98% form and can be used for de-scaling and cleaning of the lithium carbonate processing plant.
The major constituents of the reagent costs are soda ash, contributing to almost 50%, lime with around 15%, caustic soda (NaOH) with about 7% and hydrochloric acid with 1% of the total reagents costs. In some cases where the ratio of Mg:Li is high, this contribution of the soda ash can be as much as 80% of the total reagent costs. The on-site production of these chemicals can be very beneficial toward reducing operating costs.
Disclosed herein, as an aspect of this invention, is an electrodialysis multi-compartment system which allows for the on-site production of caustic soda (NaOH) and hydrochloric acid (HCL) from the existing brine in the evaporation ponds. The caustic soda is then transformed into sodium carbonate (soda ash) and sodium bicarbonate (NaHCO3) using the readily available carbon dioxide (CO2) that is used on-site. The system is fully controllable and allows for the desired concentration of product. The capability to tune the concentration of NaOH and HCl mitigates the operating costs associated with shipping and storing concentrated solutions.
Lithium Extraction from Rock Mining
Several minerals contain Li in their structure. For example, at least four minerals have found interest as viable Li sources. These are Lepidolite (K(Li,Al,Rb)2(Al,Si)4O10(F,OH)2), Spodumene (LiAl(SiO3)2), Petalite (LiAlSi4O10), and Amblygonite ((Li,Na)AlPO4(F,OH)). Among these, Spodumene is usually the most important ore for commercial Li production. (Helvaci, C., 2003. Presence and distribution of lithium in borate deposits and some recent lake waters of West-Central Turkey. Int. Geol. Rev. 45 (2), 1-14.). Expected growth in demand over the coming century for lithium batteries used in power hybrid and fully electric automobiles has raised interest in lithium production (Tahil, 2007, 2008; Bradbury, 2008).
Various methods have been developed to obtain lithium from lithium ores (Victor, K. A., 1953. Method of recovering lithium compounds from lithium minerals. U.S. Pat. No. 2,793,933; Walter, R., Bichowsky, Francis R., 1935. Method of recovering lithium from its ores. U.S. Pat. No. 2,020,854.; Robinson, G. P., 1961. Recovery of lithium from ore. U.S. Pat. No. 2,983,576; Moon, K. S., Fuerstenau, D. W., 2003. Surface crystal chemistry in selective flotation of spodumene (LiAl[SiO3]2) from other aluminosilicates. Int. J. Miner. Process. 72 (1-4), 11-24; Saeki, S., Lee, J., Zhang, Q., Saito, F., 2004. Co-grinding LiCoO2 with PVC and water leaching of metal chlorides formed in ground product. Int. J. Miner. Process. 74 (Supplement 1), S373-S378; Buyükburç, A., Maras, I., Ioglu, D., Bilici, M. S. U., Köksal, G., 2006. Extraction of lithium from boron clays by using natural and waste materials and statistical modelling to achieve cost reduction. Miner. Eng. 19 (5), 515-517; Jandová, J., Dvorák, P., Vu, H. N., 2010. Processing of zinnwaldite waste to obtain Li2CO3. Hydrometallurgy 103 (1-4), 12-18; Brandt, F., Haus, R., 2010. New concepts for lithium minerals processing. Miner. Eng. 23 (8), 659-661; Chen, Y., Tian, Q., Chen, B., Shi, X., Liao, T., 2011. Preparation of lithium carbonate from spodumene by a sodium carbonate autoclave process. Hydrometallurgy 109 (1-2), 43-46). Lithium can be extracted from lepidolite using the sulfate acid and the lime methods (Distin, P. A., Phillips, C. V., 1982. The acid extraction of lithium from the granites of South West England. Hydrometallurgy 9 (1), 1-14). However, the extraction of lithium by the sulfate acid method often uses high concentration acid and the purification procedure can be complex. The lime process uses limestone and can require a large amount of energy.
Wadman and von Girsewalt (Ellestad, Reuben B., Clarke, Fremont F., 1955. Extraction of lithium from its ores. Min. Eng. 7, 1045) ground lithium silicate ore (Lepidolite (K(Li,Al,Rb)2(Al,Si)4O10(F,OH)2), Spodumene (LiAl(SiO3)2)) with an excess of alkali sulfate (usually K2SO4) in at least a 1 to 1 proportion and heated the mixture to a relatively high temperature. At elevated temperature ion exchange occurred forming lithium sulfate which, together with the excess potassium sulfate, was dissolved by leaching with water. Successful operation of this process required thorough mixing and careful temperature control. In addition, high consumption of K2SO4 may add cost. A mixture of alkali sulfates and alkali oxide was used as reactant and the results demonstrated that an advantageous effect was obtained when the lepidolite was roasted with a mixture of Na2SO4, K2SO4 and CaO.
In order to process spodumene as described in U.S. Pat. No. 2,516,109, α-spodumene raw material is first converted to β-phase by roasting at 1100-1300° C. A typical lithium extraction from spodumene mineral is shown in
Li2O·Al2O3·4SiO2(s)+H2SO4(conc.)→Li2SO4(s)+Al2O3·4SiO2(s) 4)
Lithium carbonate can be recovered by the addition of sodium carbonate to the solution after pH adjustment, purification and evaporation, shown in reaction 5.
Li2SO4(aq.)+Na2CO3(s)→Li2CO3(s)+Na2SO4(aq.) 5)
The world's first continuous plant to convert spodumene concentrate to lithium carbonate by calcination, roasting of calcine with H2SO4 and subsequent water leaching, was commissioned in 2012 by Galaxy Resources in China (Clarke, G. M., 2013. Lithium-ion batteries: raw material considerations. Am. Inst. Chem. Eng. 44-52). One of the drawbacks of the sulfuric acid method to treat lepidolite, petalite and zinnwaldite is the requirement of a high concentration of acid and complex purification processes, whereas spodumene needs to be converted to the more leachable β-phase at higher temperature.
Overall, the cost of reagents during the rock mining process also contributes to 45% of the overall operation costs. Implementing methods to reduce such costs is the next big step in lithium recovery process. Due to the intense use of chemical reagents during these processes, the most logical approach is to recycle them after the process. Electrochemical techniques provide flexible solutions for recycling chemicals.
Electrochemical Processes for Onsite Reagent Recovery
The use of membrane electrolysis cells (also referred to as electrodialysis cells) have been successfully implemented as described herein to generate chemicals from a brackish water or brine stream. The process involves the use of a series of ion exchange membranes stacked in an order specific to the components of the brine stream being processed as well as the desired outputs. The membranes are designed to allow specific charged ionic species permeate through. Cation exchange membranes transfer cationic species while anion exchange membrane only allow anions transport through the membrane structure. Bipolar membranes are another type which split water molecules into the H+ and OH− components. The movement of ions is enabled by applying an external voltage using a cathode and anode electrode. Under applied voltage, anions travels toward the positively charged anode while cations travel towards the negatively charged cathode. Through careful placement of membranes, desired chemicals such acids, bases, and salts can be produced. During an electrolytic process with aqueous catholyte and anolyte, gaseous species such as H2 and O2 may be generated on the electrodes, due to the electrolysis of water.
Electrochemical desalination techniques rely on the above-mentioned principles of membrane electrolysis. A stream of concentrated brine or salt passes through the separation device. An electrical current (DC) applied between anode and cathode generates ionic species. The anions from the input salt solution migrate through anion exchange membrane(s) and combine with H+ ions generated on the anode and produce acid. Cations from the input salt solution likewise migrate through cation exchange membrane(s) and combine with OH− ions generated on the cathode and produce base.
An example of salt splitting process is disclosed in U.S. Pat. No. 2,829,095, where a combination of anion and cation exchange membrane was used to dissociate NaCl salt into Na+ and Cl− ions. Sodium ions were then combined with OH− from the cathode and produced NaOH. On the other hand, chloride ions combined with H+ generated on the anode and produce HCl. The overall voltage required to achieve the splitting include the potential for water decomposition and potential drop across the membranes and electrolyte solutions.
Another example of this process is the conversion of brine (NaCl) into NaOH and chlorine gas during the chlor-alkali process described in U.S. Pat. No. 4,217,186. During this process, the NaCl brine is fed into the anolyte compartment while water (or NaOH) is fed into the catholyte compartment. Upon the application of voltage, sodium ions migrate through a cation exchange membrane toward the cathode where they combine with OH− ions produced by the electrolytic splitting of water on the cathode which forms NaOH. Chlorine gas is evolved in the anode compartment according to reaction 6) while hydrogen gas is produced on the cathode.
4Cl−→2Cl2+4e−E0=1.36V 6)
The chlor-alkali process can be modified to reduce the overall cell voltage and thereby reduce energy consumption. With the purpose of eliminating the H2 generation on the cathode and reducing overall cell energy consumption, an oxygen depolarized cathode (ODC) has shown reduction in the required cell voltage in the chlor-alkali process. An example of such an application is disclosed in U.S. Pat. No. 4,191,618. The depolarization of the cathode by oxygen gas results in the formation of only hydroxyl ions thereby preventing the formation of hydrogen gas. In a hydrogen evolving scenario, the cathodic reaction in the chlor-alkali process is as follows:
4H2O+4e−→2H2+4OH−E0=−0.83V 7)
Using the oxygen depolarized cathode, where O2 gas is applied to the cathode, the cathodic reaction changes to a hydroxyl formation reaction according to the reaction:
2H2O+O2+4e−→4OH−E0=0.401 V 8)
Overall, the use of ODC and the application of pure oxygen at the cathode in the chlor-alkali process means that the overall cell voltage is approximately 1V less out of 3.3V in chlor-alkali cell. In most cases of ODCs, pure O2 is required to operate the cell.
As will be described in detail below, the novel gas diffusion electrode disclosed herein, permits the operation of a five-compartment membrane electrolysis cell with an air stream, rather than pure oxygen applied at the cathode. In the instant case, the anode reaction is not the chlorine evolution because there is no chloride solution there. Instead oxygen is evolved in the water oxidation reaction:
2H2O(l)→O2(g)+4H+(aq.)+4e− 9)
WIPO Pat. Appln. Publ. No. WO 2015/149185 A1 describes a membrane electrolysis cell assembled using a combination of anion and cation exchange membranes. The cell was utilized to convert carbon dioxide gas and a saline brine stream into carbonate salt, hydrochloric acid and desalinated water.
The present disclosure is related to the in situ process of generating reagent chemicals useful during the regular lithium extraction processes from salar brines or other lithium-containing brines such as those arising from lithium ion battery recycling operations, and from rock minerals. The process describes an electrochemical method for converting waste chemical streams into valuable reagent chemicals required during the lithium extraction operation. The disclosed electrochemical method involves a multi-compartment membrane electrolysis cell which may be incorporated into current lithium extraction processes from salar brine and from lithium-containing ore without disturbing the process flow of either type of recovery process. The disclosed process is unique in that it allows the attachment of the unique membrane electrolysis cell feed and product streams onto the commonly practiced lithium extraction processes, as well as the particular design of the gas diffusion electrode (GDE) which is used as the cathode and optionally may also be used as the anode of the cell.
In the following description of the embodiments of the invention, the membrane electrolysis cell will be described, and then the details of the gas diffusion electrode that is used as the oxygen depolarized cathode will be discussed in detail. Finally, particular uses of the membrane electrolysis cell that comprises the GDE as the cathode in the production of lithium will be described.
Membrane Electrolysis Cell
A schematic diagram of feed and product streams for a generalized inventive membrane electrolysis cell is illustrated in
A solution being treated, also referred to herein as the brine feed, is fed into the depletion (also referred to as the salt depletion chamber or compartment) chamber and cations and anions migrate from the solution in the depletion chamber to adjacent product chambers (which may be referred to herein also as acid build up compartment or base build up compartment), thereby reducing the ion concentration of the solution. The solution may be any saltwater solution such as brine, seawater or wastewater, or any solution being treated to reduce the concentration of ions therein, for example industrial waste solutions from oil and gas, mining, forestry, lithium ion battery recycling processes, etc. Any type of aqueous or non-aqueous stream consisting of ions or non-ionic species that could be made into ions by the addition of other chemicals or by processing could potentially be utilized as the brine feed.
As alluded to above, in electrodialysis, an electric potential gradient may be generated between an anode and cathode. In an aqueous setting, the anode and the cathode generally undergo the following half-cell reactions respectively:
H2O(l)→2H+(aq.)+½O2(g)+2e−(anodic reaction) 10)
2H+(aq.)+2e−→H2(g)(cathodic reaction) 11)
The dialysis cell, also referred to as the membrane electrolysis cell of the disclosed embodiments includes a plurality of compartments, creating a “stack” of compartments, and the walls of the compartments comprise ion exchange barriers separating the chambers. Ion exchange barriers (also referred to herein as membranes) in the membrane electrolysis cell generally do not require regeneration, thereby reducing the need for chemical inputs over ion exchange processes. Inorganic scaling of ion exchange barriers and ion exchange barrier fouling can be managed through polarity reversal, periodic flushes and/or acid washes, as necessary.
The ion exchange barriers of the membrane electrolysis cell include cation exchange barriers which selectively allow migration of cations, and anion exchange barriers which selectively allow migration of anions. The ion exchange barriers may be water permeable. The ion exchange barriers may be ion exchange membranes and may include, but are not limited to, commercially available bi-polar membranes and membranes with chemical modifications. Non-limiting examples of such modifications are: (i) perfluorinated films with fixed pyridine or sulfonic groups; (ii) polyetherketones; (iii) polysulfonones; (iv) polyphenylene oxides; (v) polystyrene; (vi) styrene-divinyl benzene; (vii) polystyrene/acrylic based fabrics with sulfonate and quaternary ammonium cations; (viii) polyfluorinated sulfuric acid polymers; or (ix) resin-polyvinylidenedifluoride fabrics. In alternative embodiments, other ion exchange barriers such as are known in the art may be utilized.
The membrane electrolysis cells (also referred to as electrodialysis cells) of the described embodiments generally include a cathode and anode, which may be constructed of conductive porous or non-porous substrates, and coated with a catalyst or catalysts. The ion exchange barrier (such as an ion exchange membrane) may alternatively or additionally be coated with a catalyst or catalyst. These catalysts may enhance the rate of reactions in the electrolysis cell. Suitable catalysts include, but are not limited to, precious or non-precious transition metals and their compounds (e.g. oxides, nitrides, etc.). The catalysts could be supported onto for example metal, metal oxides, metal nitrides, etc. or unsupported. A mixture of one or more catalysts, optional binder and other optional additives (for example hydrophilic and/or hydrophobic additives to control liquid and gas bubble removal), may be applied to the either or both of the cathode and anode electrodes and/or ion exchange barrier by a variety of techniques known in the art, such as spraying, sputtering, screen printing and the like. Fluids can flow in the cell via flow fields (open channels like serpentine, inter-digitated, etc.), porous closed channels, or open pocket. The cell could be operated under pressure or pressure differentials.
In operation, an electric potential may be applied between the cathode and anode to facilitate the occurrence of electrochemical reactions at the electrodes and migration of ions across the ion exchange membranes. In a membrane electrolysis cell (also referred to as a dialysis cell), an electric potential may be applied between conductors to create an electric field to enhance migration of ions across the ion exchange membranes and chambers without any electrochemical reactions occurring. However, the application of an electric potential between the conductors is not necessary for operation as ions may diffuse through the ion exchange membranes under the influence of other transport mechanisms such as a concentration gradient.
In the described embodiments of the membrane electrolysis cell, solutions may be conveyed into and away from chambers of the membrane electrolysis cell using a manifolding assembly which may include conduits, optional valves and other equipment known in the art to convey solutions to and away from chambers of a membrane electrolysis cell.
As the
A first embodiment membrane electrolysis single cell consists of five compartments as depicted in
The electrochemical processes involved in the first membrane electrolysis cell are cathodic reaction on an ODC, anodic reaction on a DSA, acid formation in the acid build up compartment, base formation in the base build up compartment and salt splitting in the salt depletion compartment. The use of a first anion exchange membrane near the cathode compartment allows for transport of the hydroxyl ions generated by the cathode into the base compartment. Another important use of this membrane is to avoid the flooding of gas diffusion electrode cathode (i.e., the ODC) in contact with the base solution. A first cation exchange membrane between the salt depletion compartment and the base build up compartment enables the transport of salt cations (Na+ in the case of NaCl or Na2SO4 as the feed brine or Li in the case of LiCl or Li2SO4) from the salt depletion compartment into the base build up compartment. The combination of sodium ions with hydroxyl ions results in the formation of sodium hydroxide in the base build up compartment. The anodic reaction results in generation of protons (H+) which are then transported through a second cation exchange membrane into the acid build up compartment. The protons then combine with anions transported through a second anion exchange membrane from the salt depletion compartment to form acid. Depending on the nature of salt, anions (Cl− in the case of NaCl and SO42− (sulfate) in the case of Na2SO4), hydrochloric acid (HCl) or sulfuric (H2SO4) acid is formed. Further, if LiCl is fed to the salt depletion compartment, HCl will build up in the acid build up compartment and LiOH will be formed in the base build up compartment. Finally, if Li2SO4 is utilized as the brine feed stream, sulfuric (H2SO4) acid and LiOH will be formed in the acid build up compartment and the base build up compartment, respectively.
A second embodiment of the membrane electrolysis cell is shown in
In the membrane electrolysis cell first embodiment shown in
Importantly, a person having skill in the art can appreciate that if LiCl in an aqueous solution is used as the brine feed stream rather than the exemplary NaCl, LiOH will be produced in the base build up compartment. In the case of LiCl, chlorine gas will still be produced at the anode. Analogous to the first embodiment membrane electrolysis cell, Na2SO4 or Li2SO4 can also be used as the brine feed streams in the second embodiment membrane electrolysis cell, and will therefore produce NaOH and LiOH, respectively in the base build up compartment and will produce H2SO4 at the anode.
A third embodiment membrane electrolysis cell is shown in
Therefore, as shown in
As shown in
A fourth embodiment membrane electrolysis cell is shown in
Any of the membrane electrolysis cells described herein may optionally incorporate any of the following of features:
Gas Diffusion Electrodes
As mentioned briefly above, an important component of the membrane electrolysis cells disclosed herein is the unique gas diffusion electrode that is used as the oxygen depolarized cathode. This gas diffusion electrode allows the membrane electrolysis cell to operate using air as the oxygen source at the cathode. This is a significant economic and safety advance in the ability to incorporate these cells into lithium recovery processes.
A gas diffusion electrode is shown schematically in
As shown in
The implementation of the ODC in the membrane electrolysis cell requires significant changes to cell design. A porous gas diffusion electrode (GDE) is usually used as the cathode electrode. This is because of the requirement of a three-phase boundary where the three reactants (oxygen gas, liquid water and electrons) must be present all at the same time. The most crucial factor is the ease of oxygen gas access to the active area where the reaction takes place.
It should be understood that the terms, “upper,” middle,” “lower,” etc. in the following discussion relate only to the relative placement of the layers in the FIG. under discussion and are not necessarily applicable to the structure while it is in use.
A key feature of the inventive gas diffusion electrode (GDE), also referred to herein as an oxygen depolarized cathode (ODC) or a gas diffusion cathode (GDC) is that the catalyst layer is deposited directly on the anion exchange membrane, as shown in
The gas diffusion layer may be made of for example, carbon fiber paper, carbon felt, carbon cloth, porous metal structures, or other porous materials which can conduct electrons and provide ability for a gas to diffuse. The reduction reaction of water to produce hydrogen can occur on many different materials depending on the voltage applied to the electrode. Without wishing to be bound by theory, the gas diffusion electrode as disclosed herein may ensure that any hydrogen that is produced due to reduction of water may react with oxygen to produce water. This water is then available to take part in the reduction of oxygen at the cathode to produce OH−.
Finally, disposed directly on the second gas diffusion layer is an optional hydrophobic catalyst layer. Importantly, if this optional second catalyst layer is present, it is a hydrophobic catalyst layer. If the optional second gas diffusion layer is not present, the optional hydrophobic catalyst layer may be disposed directly on the opposite side of the first gas diffusion layer from the required hydrophilic catalyst layer. Both the hydrophobic catalyst layer and the hydrophilic catalyst layer comprise a commercially available platinum/carbon powder, as is known in the art. The Pt/C catalyst, also referred to as an electrocatalyst, is mixed with an anion conducting ionomer. The addition of an anion conducting ionomer allows for better transport of OH− ions from the reaction site toward the catalyst layer/membrane interface. It also serves as the binder for the platinum/carbon powder or another electrocatalyst. The binders may be polymers that have both hydrophilic and hydrophobic nature. The binders may be polymers that are exclusively hydrophobic or exclusively hydrophilic. For example, Nafion® (DuPont) ionomer is hydrophobic with hydrophilic pores while Teflon® (DuPont) may be used as a binder as well but is only hydrophobic. The specific nature of the binder should allow gas diffusion, electrical conductivity and ionic conductivity. In most cases, this is a balance of the amount of binder and catalyst. If there is too much polymer, the electrons will not be conducted but if there is too little binder, the catalyst layer will not be stable. The catalyst layer which comprises this mixture is hydrophilic. The anion exchange ionomer may be an ionomer, i.e, a polymer having some amount of ionizable copolymerized monomers. The ionomer may be a dispersed solution in a liquid which is mixed with the catalyst and applied on the gas diffusion layer. An exemplary method of creating the ionomer binder may be to provide the ion exchange membrane is a solvent. This solution may be combined with the catalyst and applied to the gas diffusion layer to produce the catalyst layer and thereby produce the gas diffusion electrode. Some ion exchange membranes may be available as ionomers and do not need to be dissolved. Some such anion exchange membranes are available commercially. Non-limiting examples of such materials are the Fumion® FAA-3 ionomer from FuMA-Tech, which comprises a polyaromatic polymer, quaternary ammonium group(s) and has bromide (Br−) as the counterion, or the anion exchange ionomer from Ionomr (Vancouver, BC, Canada) are suitable, for example.
The hydrophilic/hydrophobic character of the gas diffusion electrode used as the oxygen depolarized cathode as described herein is shown schematically in
The benefits of the bilayer GDE (i.e., having the hydrophilic catalyst layer deposited directly under the anion exchange membrane and on top of the gas diffusion layer) stem from two distinct functionalities of its structure. First, the unique structure promotes the reaction of oxygen reduction to hydroxyl ions, reaction 12) rather than the undesirable hydrogen gas formation through reaction 13).
O2+2H2O+4e−→4OH− 12)
2H2O+2e−→2OH−+H2 13)
Hydrogen gas formation is undesirable because: (a) there is about 1V for the overall cell voltage (i.e. extra energy consumption) when reaction 13) occurs and (b) the hydrogen gas will make the operation of such cells unsafe due to the presence of oxygen gas, hydrogen gas and platinum catalyst at the same time in the cathode compartment.
Second, the specific configuration of hydrophilic and hydrophobic layers in this bilayer gas diffusion electrode allows for two simultaneous processes. First, and importantly, the hydrophobic diffusion layer support and the optional hydrophobic bottom catalyst layer (if present) ensure that the humidified gaseous stream (oxygen or air) has easy access to the hydrophilic catalyst layer facing the anion exchange membrane at all times which results in greatly improved mass transport, increasing the output capacity of the membrane electrolysis cell. The hydrophobic catalyst layer (if present) at the bottom of the bilayer gas diffusion electrode also ensures that any possible hydrogen gas formed at the hydrophilic catalyst layer facing the anion exchange membrane is immediately combined with the incoming oxygen to form water. The hydrophobic nature improves the reaction by pushing the water away from the electrode and preventing the catalyst sites from becoming flooded. If the catalyst sites are flooded with water, the oxygen will not be able to reach the cathode and the desired oxygen reduction reaction with water to produce anions will not occur. This is shown schematically in
The top gas diffusion layer is coated with a catalyst ink to provide the hydrophilic catalyst layer. The ink is a mixture of Pt/C catalyst powder and an anion exchange ionomer (serves as a binder and anion transferring agent) as described above. The bottom gas diffusion layer is likewise coated with a catalyst ink containing a hydrophobic agent, e.g. a polytetrafluoroethylene (PTFE) dispersion. The ink is a therefore a mixture of Pt/C catalyst powder, an anion exchange ionomer, which permits that catalyst layer to transport anion and, a PTFE dispersion (Teflon® is an example of such a material), which serves to render the catalyst layer hydrophobic. Next, the two coated gas diffusion layers are placed together such that the uncoated sides are facing each other. The anion exchange membrane is disposed on the hydrophilic catalyst layer. In operation, it should be understood that completed oxygen depolarization cathode is oriented such that the hydrophilic catalyst layer is facing the anion exchange membrane which may face the base build up compartment, and hydrophobic catalyst layer is therefore facing the incoming gas stream, which comprises O2 and preferably is air and more preferably is humid air. Regarding the process as shown in
The oxygen diffusion cathode as described above may optionally comprise a flow channel at the back side of the bilayer ODC. The flow channel serves two purposes. The first is that it provides improved distribution of the gas (air or oxygen). The flow channel can be serpentine, multiple serpentine, parallel flow, or interdigitated. Secondly, the “landing” parts of the flow field also act as pressure points, thereby providing uniform and sufficient contact through the overall cell. An example of a serpentine flow field in cathode compartment is shown in
Thus, the inventive bilayer gas diffusion electrode which preferably is used as the oxygen depolarized cathode in all of the embodiments of the membrane electrolysis cell described here has as part of its inventive feature two layers, unlike the single layer gas diffusion electrode. It is this unique geometry that allows these ODC's to use air, rather than pure oxygen. In addition, the air may be humid or humidified, i.e., ambient undried air may be fed directly to the gas diffusion electrode. The ODC also may use waste gas streams comprising oxygen as the oxygen source, for example an enriched oxygen stream resulting from a nitrogen production process.
Regarding all embodiments of the ODC, it may have the following attributes:
Regarding the dimensionally stable anode (DSA) it may have the following attributes:
If hydrogen gas is applied to the anode, the reaction is shown as reaction 14).
H2→2H++2e− 14)
Incorporation of Membrane Electrolysis Cell Comprising Gas Diffusion Electrodes into Lithium Recovery Processes
A salar brine lithium recovery process which utilizes the membrane electrolysis cell to is shown in
The ions that migrate out of the salt depletion chamber depend on what ionic species are in the feed brine that is fed to the membrane electrolysis cell. Hence, the desalinated water removed from the salt depletion compartment can be re-concentrated and therefore recycled as feed brine using the readily available salt (NaCl) stockpile from the salts that are precipitated from the salar lake evaporation ponds. The concentration of feed brine plays an important role in providing the mass transfer of the feed brine as well as supplying ions for acid and base generation. Although the membrane cell can be operated at feed brine concentrations as low as 0.1 wt. % of salt, it is beneficial to operate at the maximum available feed brine concentrations.
The concentration of product acid and base that are removed from the acid and base build up chambers, respectively, may be adjusted according to the requirements of each particular process. Caustic soda (NaOH) concentrations in the range of 5-20 wt. % may be achieved using the membrane electrolysis cell disclosed herein. As shown in
All of the above-mentioned processes require caustic (NaOH) concentrations in the range of 5-20 wt. % which is within the range achievable by the membrane electrolysis cell.
Non-limiting examples of typical uses of the hydrochloric acid that can be produced by the membrane electrolysis cell during a lithium brine recovery process is as follows:
A concentration of hydrochloric acid for the above-mentioned applications is in the range of 4-12 wt. % which is achievable by the membrane electrolysis cell.
A lithium rock mining operation process which incorporates the membrane electrolysis cell is shown in
Sulfuric acid (H2SO4) is the main reagent necessary for extracting the lithium from the ore during the acid roasting process. As shown in
Likewise, the sodium hydroxide that is produced can be used in a variety of ways in the overall lithium production process. Non-limiting examples of uses of sodium hydroxide during a lithium rock mining operation are as follows:
All above mentioned processes require NaOH concentrations in the range of 5-20 wt. % which is within the range achievable by the membrane electrolysis cell.
In an analogous manner, water may optionally be fed to the cell, rather than being removed. Whether or not water is fed to the cell depends on the concentration of the feed brine, i.e. the aqueous LiCl solution, as well as the desired concentration of LiOH and HCl that are produced. As shown in
As a point of reference, based on a test using 6% LiCl stream used as a brine feed, it takes about 150-250 kWh/m3 of LiCl brine to reduce the total salt content to 3% when air is used at the ODC.
Whether or not desalinated water is removed from the cell depends on the concentration of the feed brine, i.e. the aqueous LiCl solution, as well as the desired concentration of LiOH and HCl that are produced. In an analogous manner, water may optionally be fed to the cell, rather than being removed. Whether or not water is fed to the cell depends on the concentration of the feed brine, i.e. the aqueous LiCl solution, as well as the desired concentration of LiOH and HCl that are produced. In this embodiment, all of the LiOH that is produced is removed, i.e. there is not a recycle stream comprising LiOH.
However, the HCl stream as in the first embodiment may be recycled and used in the lithium recovery process. As shown in
The steps are thus:
Taken together, these steps result in a closed or nearly closed loop for sodium hydroxide, sodium carbonate and lithium carbonate by the incorporation of the electrochemical cell (membrane electrolysis cell) into the overall process to recover LiOH from salar brine.
Turning next to
In certain brine recovery processes it is desirable to convert a Li2SO4 solution to a LiOH, and so the membrane electrolysis cell could be used in such a process as well. As shown in
As in the first embodiment and the second embodiment, desalinated water may be optionally removed from the cell, although this stream is not shown in
In this embodiment, both the LiOH and the H2SO4 are recycled back into the lithium recovery process, which mitigates at least some of the need to buy additional reagents. Importantly, only a portion of the LiOH is recycled, since of course the LiOH is a desirable end product. The H2SO4 is used in the acid roasting step of ore production, in order to produce the Li2SO4 brine solution after the water leaching step. A portion of the LiOH that is produced can be used to precipitate out Ca and Mg from the Li2SO4 brine solution after the water leaching step, as shown in
As shown in the following three exemplary embodiments (
As discussed above, lithium hydroxide is produced by processing lithium rich brines, such as salar brines, through an extensive process. The water in the brine is allowed to evaporate over a period of 6 to 18 months to concentrate the lithium chloride in the solution to 5 wt. % LiCl or higher and to precipitate out significant sodium, calcium and magnesium salt species, since these are in general less soluble than the LiCl.
The lithium chloride-rich brine must then be subjected to a variety of purification steps. These purification steps may include for example: boron removal through a solvent or other means, calcium and magnesium removal through the addition of lime (calcium oxide and/or calcium hydroxide) and caustic soda, soda ash and/or sodium bicarbonate or other species, further calcium and magnesium removal through the addition of soda ash, i.e., sodium carbonate Na2CO3. These processes produce a mixed lithium chloride and sodium chloride stream to which additional soda ash is added resulting in the precipitation of lithium carbonate. The lithium carbonate may then be crystallized. Currently, this crystallized lithium carbonate is often transported to a lithium hydroxide plant where it is converted to lithium hydroxide by adding calcium hydroxide. The lithium hydroxide is then crystallized for sale. There are several process units associated with all these steps and clearly, procuring and maintaining these process units represents significant capital investment as well as on-going operational costs.
An ion exchange resin selective to adsorption or binding of lithium can be used to eliminate many of these steps to selectively adsorb lithium from the salar brine (or other source) without the need for time-consuming evaporation or removal of boron, calcium, magnesium, etc. For instance, an ion exchange resin for selectively binding lithium and producing lithium chloride by desorbing the lithium from the resin with HCl could be utilized. A membrane electrolysis cell as disclosed herein can convert the lithium chloride to lithium hydroxide and the hydrochloric acid, which would be recycled back to the ion exchange resin, which the desirable lithium hydroxide is collected.
In another embodiment, an ion exchange resin for selective adsorption of lithium could also be used to produce lithium sulfate by regeneration of the resin with sulfuric acid. Analogously, the lithium sulfate would be fed to the electrolysis cell to produce lithium hydroxide and sulfuric acid. The sulfuric acid would be recycled back to the ion exchange resin to produce more lithium sulfate, while the desirable lithium hydroxide is collected.
The ion exchange resin would eliminate significant capital and operating expenditures and costs associated with the lithium evaporation ponds and associated downstream transportation.
Eliminating the evaporation ponds would also conserve water which is lost to the atmosphere during the evaporation step. Producers would be able to pump the lithium-depleted brine back to the salar brine reservoir, which conserves the water which would be evaporated. This feature is critical from both environmental and legal viewpoints. Chile, for example, where most of the world's lithium brines are located, has strict limits on water usage and the amount of brine lithium producers can pump. The purpose of the regulations is to conserve the scarce water in the Salar desert region of Chile. Therefore, these limits effectively mean that the producers' production of lithium is limited. However, if the lithium-depleted brine from the ion exchange process is pumped back to the reservoirs, much less net brine is pumped, and the producers can increase their production of lithium without exceeding the governmental limits on the amount of salar brine they can pump or amount of water used in the operation. Use of ion exchange resins in the lithium recovery process would also save time, since the evaporation step is slow. Additionally and importantly, the need to purchase reagents necessary for precipitation of calcium and magnesium would be eliminated.
The largest cost associated with direct production of lithium with ion exchange resins is with the need to procure HCl which is required to desorb or unbind the lithium ion from the active sites and regenerate the ion-exchange resin. An electrochemical cell as described herein that is capable of converting lithium chloride to lithium hydroxide and hydrochloric acid not only eliminates the need to procure the reagent required for the conversion of lithium chloride to lithium carbonate to lithium hydroxide, but these cells also produce the vital HCl required to extract the lithium from the ion exchange resin. Accordingly, the whole process starting from lithium chloride evaporation to lithium carbonate production and lithium carbonate conversion through to production of lithium hydroxide for use in batteries may be simplified to the use of only an ion exchange resin and an electrochemical cell.
In addition, another exemplary use of the membrane electrolysis cells in processes utilizing ion exchange resins to directly adsorb lithium from brine is a process where the ion exchange resin is deployed in the desert where the salar brine is pumped, while the membrane electrolysis cell is in a different location. In this exemplary process the ion exchange resin is removed, transported to the location of the membrane electrolysis cell where the ion exchange resin is regenerated with HCl thus producing LiOH. The ion-exchange resin would then be shipped back to the brine site in the desert. Thus, a used ion-exchange resin would move one way and the regenerated ion exchange resin would move the opposite way. Therefore, in any of the exemplary processes shown in
Non-limiting examples of suitable such ion exchange resins are those that selectively binds lithium or another precious metal based on the pH of the solution. For example, the resin may bind lithium in acid but not in alkali, or vice versa. This allows us to be able to regenerate the resin and extract lithium from it. This allows the producers to be able to regenerate the resin and extract lithium from it. The membrane electrolysis cell then produces the appropriate pH solution to remove the bound ion by providing HCl or NaOH. Such ion exchange resins may also include complexed metal resins such as HnMnOn where the H is hydrogen, M is a metal species, O is oxygen and n is an integer. Non-limiting examples include LiAlO2, LiCuO2, among others.
The following two embodiments thus demonstrate how the membrane electrolysis cell as disclosed herein may be incorporated into lithium recovery processes in which an ion exchange resin is used to directly produce LiOH.
Note that in the process as shown in
2H2O→O2+4H++4e− Anode:
O2+2+H2O+4e−→4OH− Cathode:
O2+2H2O+4e−→4OH− Cathode:
2H2O→4H++4e−+O2 Anode:
The lithium carbonate would react with the protons generated at the anode to liberate lithium ions, carbon dioxide and water as follows:
2Li2CO3+4H+→4Li++2CO2+2H2O
The liberated lithium ions would be transported towards the cathode to the lithium hydroxide compartment where they would combine with the hydroxide ions produced at the cathode and produce a lithium hydroxide solution.
It should be understood that in all of the foregoing Embodiments depicting the use of the inventive membrane electrolysis cell in recovery processes for lithium, that the role of GDEs essentially remain the same between the various applications: to produce OH− ions from a humidified oxygen/air gas stream. Regardless of the salt used as the feed brine (LiCl, NaCl, Na2SO4, Li2SO4), the cathode catalyst on the GDE always plays the same role.
Various non-limiting aspects of the invention may be summarized as follows:
Aspect 1: A process for recovering Li from a Li source, the process comprising the steps of:
Aspect 2: The process of Aspect 1, further comprising:
Aspect 3: The process of Aspect 1 or Aspect 2, wherein the membrane electrolysis cell comprises
Aspect 4: The process of Aspect 3, the diffusion layer having a bi-layer construction formed from a plurality of diffusion sublayers, wherein the diffusion sublayers are hydrophobic and wherein water is transported away from the diffusion sublayers.
Aspect 5: The process of Aspect 3, the gas diffusion electrode further comprising a hydrophobic catalyst layer disposed on a surface of the diffusion layer that is opposite from the hydrophilic catalyst layer, the hydrophobic catalyst layer having a hydrophilicity less than that of the diffusion layer and being capable of transporting negative ions, wherein the OH− ions are transported through the hydrophobic catalyst layer.
Aspect 6: The process of Aspect 5, the membrane electrolysis cell further comprising:
Aspect 7: The process of Aspect 6, the membrane electrolysis cell further comprising:
Aspect 8: The process of Aspect 7, the membrane electrolysis cell further comprising:
Aspect 9: The process of Aspect 8, wherein the first and fourth ion exchange membranes comprise cation exchange membranes and the second and third ion exchange membranes comprise anion exchange membranes.
Aspect 10: The process of any of Aspects 1-9, wherein the gas comprising O2 is air.
Aspect 11: The process of any of Aspects 1-9, wherein the gas comprising oxygen is a waste stream from a nitrogen producing operation.
Aspect 12: The process of any of Aspects 1-11, wherein the Li source comprises a salar brine and the recovered Li comprises at least one of LiOH, Li2CO3, and/or LiCl.
Aspect 13: The process of any of Aspects 1-12, wherein in the receiving step the byproducts of the process for recovering Li comprise NaCl precipitated from the salar brine; and in the delivering step the reagent materials used in the process for recovering Li comprise HCl and NaOH.
Aspect 14: The process of any of Aspects 1-13 wherein the reagent materials are used to regenerate and/or desorb ions from an ion exchange resin used in the process for recovering lithium.
Aspect 15: The process of Aspect 13 wherein at least one of the HCl and the NaOH are used to regenerate and/or desorb ions from an ion exchange resin used in the process for recovering lithium.
Aspect 16: The process of any of Aspects 1-14, wherein the lithium source comprises lithium ore and the recovered lithium comprises at least one of LiOH, Li2CO3, and/or Li2SO4.
Aspect 17: The process of Aspect 16, wherein the recovered lithium comprises LiOH and the process further comprises a step of recycling a portion of the LiOH into the process for recovering lithium.
Aspect 18: The process of Aspect 17, further comprising a step of precipitating at least one of calcium and magnesium with the portion of the LiOH.
Aspect 19: The process of Aspect 17, further comprising a step of reacting the portion of the LiOH with CO2 to produce Li2CO3, and further comprising a step of precipitating at least one of calcium and magnesium with the Li2CO3.
Aspect 20: The process of any of Aspects 1-16, wherein in the receiving step the byproducts of the process for recovering Li comprise Na2SO4 and in the delivering step the reagent materials used in the process for recovering lithium comprise H2SO4 and NaOH.
Aspect 21: The process of any of Aspects 1-14, wherein the lithium source comprises a salar brine and in the receiving step the salt-containing solution comprises LiCl and in the delivering step the recovered lithium comprises LiOH and the reagent materials used in the lithium recovery process comprise HCl.
Aspect 22: The process of Aspect 21, further comprising recycling a portion of the LiOH into the process for recovering lithium.
Aspect 23: The process of either of Aspect 21 or Aspect 22, further comprising a step of reacting the portion of the LiOH with CO2 to produce Li2CO3, and further comprising a step of precipitating at least one of calcium and magnesium with the Li2CO3.
Aspect 24: The process of any of Aspects 1-14, wherein the lithium source comprises a salar brine and in the receiving step the salt-containing solution comprises LiCl and NaCl and in the delivering step the recovered lithium comprises LiOH and the reagent materials used in the lithium recovery process comprise HCl and NaOH.
Aspect 25: The process of Aspect 20, further comprising recycling a portion of the LiOH into the lithium recovery process.
Aspect 26: The process of any of Aspects 1-16, wherein the lithium source comprises lithium ore and in the receiving step the salt-containing solution comprises Li2SO4 from the lithium ore and in the delivering step the recovered lithium comprises LiOH and the reagent materials used in the lithium recovery process comprise H2SO4.
Aspect 27: The process of Aspect 18, wherein the salt-containing solution comprising LiCl is derived by contacting salar brine with an ion exchange resin, wherein the ion exchange resin is configured to adsorb lithium from the salar brine and to desorb the adsorbed lithium in the form of the solution comprising the LiCl in the presence of the HCl.
Aspect 28: The process of Aspect 26, wherein the salt-containing solution comprising Li2SO4 is derived by contacting a lithium containing-stream derived from the lithium ore with an ion exchange resin, wherein the ion exchange resin is configured to adsorb lithium from the lithium containing-stream derived from the lithium ore and to desorb the adsorbed lithium in the form of the solution comprising the Li2SO4 in the presence of the H2SO4.
Aspect 29: The process of Aspect 22, wherein the ion exchange resin is further configured to adsorb lithium directly from the salar brine.
Aspect 30: The process of Aspect 22, wherein the process further comprises a step of removal of boron from the salar brine prior to contacting the salar brine with the ion exchange resin.
Aspect 31: The process of any of Aspects 1-16, wherein the lithium source comprises Li2CO3.
Aspect 32: The process of Aspect 31, wherein in the receiving step the salt-containing solution comprises LiCl or Li2SO4.
Aspect 33: The process of Aspect 32, wherein in the delivering step the recovered lithium comprises LiOH and the reagent materials used in the lithium recovery process comprise HCl.
Aspect 34: The process of Aspect 32, wherein in the delivering step the recovered lithium comprises LiOH and the reagent materials used in the lithium recovery process comprise H2SO4.
Aspect 35: The process of Aspect 33, wherein the process further comprises recycling the HCl to dissolve the Li2CO3 to produce the LiCl.
Aspect 36: The process of Aspect 34, wherein the process further comprises recycling the H2SO4 to dissolve the Li2CO3 to produce the Li2SO4.
Aspect 37: The process of any of Aspects 1-11, wherein the lithium source comprises a brine derived from a lithium ion battery recovery process.
Aspect 38: A gas diffusion electrode for use in a membrane electrolysis cell, the gas diffusion electrode comprising:
Aspect 39: The gas diffusion electrode of Aspect 38, the diffusion layer having a bi-layer construction formed from a plurality of diffusion sublayers.
Aspect 40: The gas diffusion electrode of either of Aspect 38 or Aspect 39, further comprising a hydrophobic catalyst layer disposed on a surface of the diffusion layer that is opposite from the hydrophilic catalyst layer, the hydrophobic catalyst layer having a hydrophilicity less than that of the diffusion layer and being capable of transporting negative ions.
Aspect 41: The gas diffusion electrode of any of Aspects 38-40, the hydrophilic catalyst layer comprising platinum and carbon and an anion exchange ionomer.
Aspect 42: The gas diffusion electrode of either of Aspect 40 or Aspect 41, the hydrophobic catalyst layer comprising platinum and carbon and an anion exchange ionomer.
Aspect 43: The gas diffusion electrode of any of Aspects 40-42, the hydrophobic catalyst layer comprising PTFE.
Aspect 44: The gas diffusion electrode of any of Aspects 40-43, at least one of the hydrophilic catalyst layer and the hydrophobic catalyst layer being configured as an oxygen depolarized cathode to catalyze the following reaction: O2+2H2O+4e−→4OH−.
Aspect 45: The gas diffusion electrode of any of Aspects 38-44, said ion exchange membrane being an anion exchange membrane, thereby forming a cathode.
Aspect 46: A method of producing a gas diffusion electrode for use in a membrane electrolysis cell, the method comprising:
Aspect 47: The method of Aspect 46, further comprising disposing a hydrophobic catalyst layer on a surface of the diffusion layer that is opposite from the hydrophilic catalyst layer, the hydrophobic catalyst layer having a hydrophilicity less than that of the diffusion layer.
Aspect 48: The method of either of Aspect 46 or Aspect 47, the diffusion layer having a bilayer construction formed from a plurality of diffusion sublayers, the hydrophilic catalyst layer disposing step including disposing the hydrophilic catalyst layer on a surface of one of the diffusion sublayers, and the hydrophobic catalyst layer disposing step including disposing the hydrophobic catalyst layer on an opposite surface of another one of the diffusion sublayers.
Aspect 49: The method of any of Aspects 46-48, further comprising combining the diffusion sublayers to form the diffusion layer.
Aspect 50: The method of any of Aspects 46-49, at least one of the hydrophilic catalyst layer and the hydrophobic catalyst layer being formed from an ink and at least one of the hydrophilic catalyst layer disposing step and the hydrophobic catalyst layer disposing step comprising applying the ink on the surface of the diffusion layer.
Aspect 51: A membrane electrolysis cell for processing a salt-containing solution, the membrane electrolysis cell comprising:
Aspect 52: The membrane electrolysis cell of Aspect 51, further comprising
Aspect 53: The membrane electrolysis cell of Aspect 52, further comprising
Aspect 54: The membrane electrolysis cell of Aspect 53, further comprising:
Aspect 55: The membrane electrolysis cell of Aspect 54 wherein the first and fourth ion exchange membranes comprise cation exchange membranes and the second and third ion exchange membranes comprise anion exchange membranes.
Aspect 56: The membrane electrolysis cell of any of Aspects 51-55 wherein the hydrophilic catalyst layer comprises platinum and carbon and an anion exchange ionomer.
Aspect 57: A process for purifying or concentrating LiOH using a membrane electrolysis cell, the steps of the process comprising the steps of:
Aspect 58: A process for producing LiOH using a membrane electrolysis cell, the steps of the process comprising the steps of:
Experiments were conducted to demonstrate the effect of the inventive bilayer gas diffusion electrodes used as the oxygen depolarized cathodes compared to the single layer ODC.
In some embodiments, the invention herein can be construed as excluding any element or process that does not materially affect the basic and novel characteristics of the composition or process. Additionally, in some embodiments, the invention can be construed as excluding any element or process not specified herein.
As noted previously, although the invention is illustrated and described herein with reference to specific embodiments, the invention is not intended to be limited to the details shown. Rather, various modifications may be made in the details within the scope and range of equivalents of the claims and without departing from the invention.
Within this specification, embodiments have been described in a way which enables a clear and concise specification to be written, but it is intended and will be appreciated that embodiments may be variously combined or separated without departing from the invention. For example, it will be appreciated that all preferred features described herein are applicable to all aspects of the invention described herein.
While preferred embodiments of the invention have been shown and described herein, it will be understood that such embodiments are provided by way of example only. Numerous variations, changes and substitutions will occur to those skilled in the art without departing from the spirit of the invention. Accordingly, it is intended that the appended claims cover all such variations as fall within the spirit and scope of the invention.
This is a continuation application of U.S. application Ser. No. 17/416,413, filed Jun. 18, 2021, which is the U.S. National Phase of International Application No. PCT/IB2019/001346, filed Dec. 19, 2019, which claims priority to U.S. Provisional Application No. 62/784,324, filed Dec. 21, 2018, and U.S. Provisional Application No. 62/907,486, filed Sep. 27, 2019, the contents each of which are incorporated herein by reference in their entireties for all purposes.
Number | Name | Date | Kind |
---|---|---|---|
2020854 | Rosett et al. | Nov 1935 | A |
2516109 | Ellestad et al. | Jul 1950 | A |
2793933 | Kroll et al. | May 1957 | A |
2829095 | Kenichi et al. | Apr 1958 | A |
2983576 | Robinson | May 1961 | A |
3424563 | Grinstead | Jan 1969 | A |
3855392 | Folkestad et al. | Dec 1974 | A |
4036713 | Brown | Jul 1977 | A |
4191618 | Coker et al. | Mar 1980 | A |
4207297 | Brown et al. | Jun 1980 | A |
4217186 | McRae | Aug 1980 | A |
4261960 | Boryta | Apr 1981 | A |
4299682 | Oda et al. | Nov 1981 | A |
4415413 | Veber | Nov 1983 | A |
4584080 | Staab et al. | Apr 1986 | A |
4877694 | Solomon et al. | Oct 1989 | A |
4980037 | Hossain et al. | Dec 1990 | A |
4980136 | Brown et al. | Dec 1990 | A |
5246551 | Pletcher et al. | Sep 1993 | A |
5567293 | Paleologou et al. | Oct 1996 | A |
5939038 | Wilkomirsky | Aug 1999 | A |
5993759 | Wilkomirsky | Nov 1999 | A |
6048507 | Amouzegar et al. | Apr 2000 | A |
6117268 | Shimamune et al. | Sep 2000 | A |
6143260 | Boryta | Nov 2000 | A |
6217728 | Lehmann et al. | Apr 2001 | B1 |
8641922 | Viloria et al. | Feb 2014 | B2 |
8691169 | Perez et al. | Apr 2014 | B2 |
9169125 | Kang et al. | Oct 2015 | B2 |
9601779 | Visco et al. | Mar 2017 | B2 |
10144990 | Bourassa et al. | Dec 2018 | B2 |
10718057 | Freiderich | Jul 2020 | B1 |
20070248885 | Bannai et al. | Oct 2007 | A1 |
20100021777 | Gottesfeld et al. | Jan 2010 | A1 |
20110044882 | Buckley et al. | Feb 2011 | A1 |
20110203929 | Buckley et al. | Aug 2011 | A1 |
20130037415 | Izawa et al. | Feb 2013 | A1 |
20130146476 | Chon et al. | Jun 2013 | A1 |
20140023940 | Zaghib et al. | Jan 2014 | A1 |
20150240368 | Iacopetti et al. | Aug 2015 | A1 |
20180147531 | Park et al. | May 2018 | A1 |
20180244531 | Magnan et al. | Aug 2018 | A1 |
20190048483 | Swonger et al. | Feb 2019 | A1 |
Number | Date | Country |
---|---|---|
1511964 | Jul 2004 | CN |
1894821 | Jan 2007 | CN |
103031568 | Apr 2013 | CN |
103415953 | Nov 2013 | CN |
104628217 | May 2015 | CN |
106011917 | Oct 2016 | CN |
108341420 | Jul 2018 | CN |
804921 | Nov 1958 | GB |
11172484 | Jun 1999 | JP |
2011031232 | Feb 2011 | JP |
2011518257 | Jun 2011 | JP |
2011258489 | Dec 2011 | JP |
1020160075679 | Jun 2016 | KR |
2015149185 | Oct 2015 | WO |
2020086000 | Apr 2020 | WO |
Entry |
---|
Non Final Office Action for U.S. Appl. No. 17/883,767, dated Nov. 25, 2022, 28 pages. |
Non Final Office Action for U.S. Appl. No. 17/883,969, dated Dec. 8, 2022, 29 pages. |
Non Final Office Action for U.S. Appl. No. 17/883,850, dated Dec. 14, 2022, 26 pages. |
Ji et al., “Preliminary Study on Recovering Lithium From High Mg2+/Li+ Ratio Brines By Electrodialysis”, Separation and Purification Technology, 2017, vol. 172, pp. 168-177. |
Korean Request for Submission of an Opinion for Korean Application No. 10-2022-7020732, dated Feb. 14, 2023 with translation, 23 pages. |
Chinese Office Action for Chinese Application No. 201980092809.2, dated Aug. 8, 2022 with translation, 33 pages. |
Australian Examination Report for Australian Application No. 2021290346, dated Mar. 19, 2022, 5 pages. |
Bradbury, Energy Storage Technology Review, 2010, 34 pages. |
Brandt et al., “New Concepts for Lithium Minerals Processing”, Minerals Engineering, 2010, vol. 23, pp. 659-661. |
Büyükburc et al., “Extraction of Lithium from Boron Clays by Using Natural and Waste Materials and Statistical Modelling to Achieve Cost Reduction”, Minerals Engineering, 2006, vol. 19, pp. 515-517. |
Canadian Examination Report for Canadian Application No. 3124281, dated Aug. 24, 2021, 4 pages. |
Canadian Office Action for Canadian Application No. 3,124,281, dated Mar. 2, 2022, 6 pages. |
Chen et al., “Preparation of Lithium Carbonate From Spodumene by A Sodium Carbonate Autoclave Process”, Hydrometallurgy, 2011, vol. 109, pp. 43-46. |
Chinese Office Action for Chinese Application No. 201980092809.2, dated Jan. 30, 2022, with translation, 13 pages. |
Clarke et al., “Lithium-Ion Batteries”, American Institute of Chemical Engineers, 2015, 32 pages. |
Distin et al., “The Acid Extraction of Lithium From the Granites of South West England”, Hydrometallurgy, 1982, vol. 9, pp. 1-14. |
Ellestad et al., “Extraction of Lithium from Its Ores”, Mining Engineering, 1955, pp. 1045-1047. |
European Partial Supplementary Search Report for European Application No. 19900554.7 dated Jun. 24, 2022, 23 pages. |
Helvaci et al., “Presence and Distribution of Lithium in Borate Deposits and Some Recent Lake Waters of West-Central Turkey”, International Geology Review, 2004, vol. 46, pp. 177-190. |
International Preliminary Report on Patentability for International Application No. PCT/IB2019/001346, dated Jun. 16, 2021, 6 pages. |
International Search Report and Written Opinion for International Application No. PCT/IB2019/001346, dated May 28, 2020, 9 pages. |
Jandová et al., “Processing of Zinnwaldite Waste to Obtain Li2CO3”, Hydrometallurgy, 2010, vol. 103, pp. 12-18. |
Korean Notification of Reason for Refusal for Korean Application No. 10-2021-7022179, dated Dec. 8, 2021 with translation, 10 pages. |
McKetta, “Lithium and Lithium Compounds”, Encyclopedia of Chemical Processing and Design, vol. 28, pp. 324-344. |
Moon et al., “Surface Crystal Chemistry in Selective Flotation of Spodumene (liA1[SiO3]2) From Other Aluminosilicates”, Int. J. Miner. Process., 2003, vol. 72, pp. 11-24. |
Saeki et al., “Co-Grinding LiCoO2 with PVC and Water Leaching of Metal Chlorides Formed in Ground Product”, Int. J. Miner Process., 2004, vol. 74S, pp. S373-S378. |
Tahil, W., “How much lithium does a Li ion EV battery really need?”, Meridian Int. Res., Mar. 5, 2010, 11 pages. |
Technical Data Sheet—fumion FAA-3 Solution in NMP (10%), 1 page. |
Entire patent prosecution history of U.S. Appl. No. 17/416,413, filed Jun. 18, 2021, entitled, “Li Recovery Processes and Onsite Chemical Production for Li Recovery Processes”. |
“The Trouble with Lithium 2 Under the Microscope”, Meridian International Research, 2008, 58 pages. |
Moore, “Lithium Supply May Not Be Sufficient for Electric Car Battery Production Study Finds”, 2007, downloaded from the internet at https://www.prweb.com/releases/2007/01/prweb500533.htm, 3 pages. |
Extended European Search Report for European Application No. 23 167 855.8, dated Jul. 14, 2023, 11 pages. |
Extended European Search Report for European Application No. 23 167 858.2, dated Jul. 14, 2023, 11 pages. |
Notice of Allowance for U.S. Appl. No. 18/130,190, dated Dec. 22, 2023, 10 pages. |
Number | Date | Country | |
---|---|---|---|
20220380912 A1 | Dec 2022 | US |
Number | Date | Country | |
---|---|---|---|
62907486 | Sep 2019 | US | |
62784324 | Dec 2018 | US |
Number | Date | Country | |
---|---|---|---|
Parent | 17416413 | US | |
Child | 17883983 | US |