The present disclosure relates to a light-diffusing sheet, a backlight unit, a liquid crystal display device, an information apparatus, and a method of manufacturing a light-diffusing sheet.
In recent years, liquid crystal display devices (hereinafter, also referred to as liquid crystal displays) are widely used as display devices of various information apparatuses including smartphones and tablet terminals. As backlights of liquid crystal displays, direct-type systems in which a light source is arranged on a rear surface of a liquid crystal panel or edge light systems in which a light source is arranged in a vicinity of a side surface of a liquid crystal panel are predominantly used.
When adopting a direct-type backlight, a light-diffusing member (a light-diffusing plate, a light-diffusing sheet, or a light-diffusing film) is used in order to erase an image of a light source such as an LED (Light Emitting Diode) and increase uniformity of in-plane brightness on a light-emitting surface.
In a direct-type backlight disclosed in Japanese Patent Application Publication No. 2010-117707, a light-diffusing plate provided with a plurality of depressed portions with an inverted polygonal pyramid shape (inverted pyramid shape) or an inverted truncated polygonal pyramid shape is used in order to improve brightness uniformity. Japanese Patent Application Publication No. 2010-117707 discloses, in a stacked structure of a light-diffusing plate and another optical film, making an inside surface of each depressed portion of the light-diffusing plate into a curved surface of which a center of curvature is positioned on a side of a depth direction of the depressed portion in an opening edge part in order to prevent the light-diffusing plate and the other optical film from becoming worn and damaged due to vibration during transportation.
However, with the direct-type backlight disclosed in Japanese Patent Application Publication No. 2010-117707, damage to the light-diffusing plate and the other optical film cannot be sufficiently suppressed.
In consideration thereof, an object of the present disclosure is to provide a light-diffusing sheet that is less susceptible to damage even when stacked while improving brightness uniformity.
In order to achieve the object described above, a light-diffusing sheet according to the present disclosure includes a plurality of depressed portions formed in an approximately inverted polygonal pyramid on at least a first surface. Ridgelines that partition the plurality of depressed portions have a depressed shape between intersections of the ridgelines with respect to straight lines that connect the intersections. When an array pitch of the plurality of depressed portions is denoted by P and a dimension occupied by a curved portion of a vertex of each of the ridgelines in an array direction of the plurality of depressed portions is denoted by Wr, a ratio Wr/P is 0.3 or lower. A maximum height difference d between the straight line and the ridgelines is 1 μm or more and 10 μm or less. The plurality of depressed portions include a depressed portion of which a vertex of the approximately inverted polygonal pyramid is formed in a linear shape.
With the light-diffusing sheet according to the present disclosure, since the light-diffusing sheet includes a plurality of depressed portions formed in an approximately inverted polygonal pyramid on at least a first surface, brightness uniformity can be improved. In addition, while the ridgelines (an opening edge of the depressed portions) that partition the depressed portions cause abrasion and damage, the ridgelines have a depressed shape between the intersections of the ridgelines. Therefore, abrasion and damage are less likely to occur even when the light-diffusing sheet is used by being stacked with other optical sheets or other light-diffusing sheets. In addition, the dimension Wr occupied by the curved portion of a vertex of each of the ridgelines in the array direction of the depressed portions is kept to or under 30% of the array pitch P of the depressed portions. Therefore, since the vertex of the ridgelines can maintain a steep shape, brightness uniformity does not readily decline even when the ridgelines are depressed between the intersections of the ridgelines. Furthermore, since the maximum height difference d between a straight line connecting the intersections of the ridgelines and the ridgelines is set to 1 μm or more, scratch resistance is improved and, at the same time, since the maximum height difference d is set to 10 μm or less, a decline in brightness uniformity can be suppressed. Moreover, since the vertex of the approximately inverted polygonal pyramid (in other words, a bottom part of the depressed portions) is formed in a linear shape, mass production of the light-diffusing sheet of which brightness uniformity is prevented from declining can be readily performed.
While the expression “approximately inverted polygonal pyramid” is used in consideration of the fact that it is difficult to form depressed portions of a geometrically-strict inverted polygonal pyramid using ordinary shape transfer techniques in the light-diffusing sheet according to the present disclosure, it is needless to say that the expression includes a true inverted polygonal pyramid and shapes that are substantially an inverted polygonal pyramid.
In addition, while the ridgelines preferably have a depressed shape between all intersections of the ridgelines in the light-diffusing sheet according to the present disclosure, it is not essential for the ridgelines to have a depressed shape between all intersections. In other words, the ridgelines need not have a depressed shape between parts of the intersections.
Furthermore, in the present disclosure, a “light-diffusing sheet” is to include a “light-diffusing plate” with a plate shape and a “light-diffusing film” with a film shape.
Moreover, in the present disclosure, an “optical sheet” means a sheet that has various optical functions such as diffusion, condensing, refraction, and reflection and a “light-diffusing sheet” is one of such “optical sheets”.
In the light-diffusing sheet according to the present disclosure, when the maximum height difference d is 1.5 μm or more and 7 μm or less, both scratch resistance and brightness uniformity can be further improved. In this case, when the maximum height difference d is 2.5 μm or more and 5 μm or less, both scratch resistance and brightness uniformity can be even further improved.
In the light-diffusing sheet according to the present disclosure, when the ratio Wr/P is 0.2 or lower, brightness uniformity can be further improved. In this case, when the ratio Wr/P is 0.1 or lower, brightness uniformity can be even further improved.
In the light-diffusing sheet according to the present disclosure, when the array pitch P is 50 μm or more and 500 μm or less and an angle formed between a wall surface of the plurality of depressed portions (in other words, inclined surfaces of the approximately inverted polygonal pyramids) and a sheet surface of the light-diffusing sheet is 40 degrees or more and 65 degrees or less, brightness uniformity can be improved.
In the light-diffusing sheet according to the present disclosure, when the ridgeline is depressed in an approximately parabolic shape, an approximately arc shape, an approximately triangular shape, or an approximately trapezoidal shape between the intersections, scratch resistance can be improved.
In the light-diffusing sheet according to the present disclosure, the plurality of depressed portions may be formed in an approximately inverted square pyramid. In this case, the ridgelines may extend in a first direction and a second direction. In addition, the maximum height difference d may be an average value of a maximum height difference dx between the straight lines and the ridgelines in the first direction and a maximum height difference dy between the straight lines and the ridgelines in the second direction. Furthermore, the array pitch P may be an average value of an array pitch Px of the plurality of depressed portions in the first direction and an array pitch Py of the plurality of depressed portions in the second direction. Moreover, the dimension Wr may be an average value of a dimension Wrx occupied by a curved portion of a vertex of each of the ridgelines in the first direction and a dimension Wry occupied by a curved portion of a vertex of each of the ridgelines in the second direction. Accordingly, a light-diffusing sheet with superior scratch resistance and brightness uniformity can be readily manufactured.
In the light-diffusing sheet according to the present disclosure, when the plurality of depressed portions are only provided on the first surface and a second surface is a matte surface, brightness uniformity can be further improved while suppressing abrasion and damage on the second surface.
In the light-diffusing sheet according to the present disclosure, a ratio of depressed portions of which the vertex is formed in a linear shape among the plurality of depressed portions may be 10% or more. Alternatively, the ratio may be 20% or more, 30% or more, 40% or more, 50% or more, 60% or more, 70% or more, 80% or more, 90% or more, or 100%.
A backlight unit according to the present disclosure is a backlight unit which is built into a liquid crystal display device and which guides light emitted by a light source toward a display screen and includes the light-diffusing sheet according to the present disclosure described earlier between the display screen and the light source.
Since the backlight unit according to the present disclosure includes the light-diffusing sheet according to the present disclosure described earlier, brightness uniformity can be improved and, at the same time, damage can be suppressed even when the light-diffusing sheet and other optical sheets are stacked.
In the backlight unit according to the present disclosure, when the light source is arranged on a reflecting sheet provided on an opposite side to the display screen as viewed from the light-diffusing sheet, brightness uniformity is even further improved.
In the backlight unit according to the present disclosure, the light-diffusing sheet may be stacked in plurality (for example, three or more sheets) and arranged between the display screen and the light source. Accordingly, brightness uniformity is further improved. In a case where three or more sheets of the light-diffusing sheet are stacked, when the light-diffusing sheet closest to the display screen contains a diffusing agent but the other light-diffusing sheets substantially do not contain the diffusing agent, brightness uniformity is even further improved.
A liquid crystal display device according to the present disclosure includes the backlight unit according to the present disclosure described earlier and a liquid crystal display panel.
Since the liquid crystal display device according to the present disclosure includes the backlight unit according to the present disclosure described earlier, brightness uniformity can be improved and, at the same time, damage can be suppressed even when the light-diffusing sheet and other optical sheets are stacked.
An information apparatus according to the present disclosure includes the liquid crystal display device according to the present disclosure described earlier.
Since the information apparatus according to the present disclosure includes the liquid crystal display device according to the present disclosure described earlier, brightness uniformity can be improved and, at the same time, damage can be suppressed even when the light-diffusing sheet and other optical sheets are stacked.
A method of manufacturing a light-diffusing sheet according to the present disclosure is a method of manufacturing the light-diffusing sheet according to the present disclosure described earlier, wherein the light-diffusing sheet is subjected to extrusion molding at a line rate of 10 m/minute or more and 30 m/minute or less and compressible linear pressure of 100 kgf/cm or more and 500 kgf/cm or less.
With the method of manufacturing a light-diffusing sheet according to the present disclosure, since the dimension Wr occupied by the curved portion of the vertex of the ridgelines in the array direction of the depressed portions can be kept to or under 30% of the array pitch P of the depressed portions, a light-diffusing sheet of which a shape of the vertex of the ridgelines is steep and which has superior brightness uniformity can be manufactured.
In addition, with the method of manufacturing a light-diffusing sheet according to the present disclosure, the maximum height difference d between the straight lines that connects intersections of the ridgelines and the ridgelines can be set to 1 μm or more and 10 μm or less. In other words, a light-diffusing sheet in which the ridgelines are depressed between the intersections of the ridgelines and elevated at portions of the intersections of the ridgelines is obtained. Therefore, even when the light-diffusing sheet and other optical sheets are stacked, since the ridgelines are less likely to come into contact with the other optical sheets between the intersections of the ridgelines, abrasion and damage are less likely to occur, and since the ridgelines come into point contact with the other optical sheets at the intersections of the ridgelines, slippage is created and reduces abrasion and damage. As a result, a light-diffusing sheet with superior scratch resistance can be manufactured.
Furthermore, with the method of manufacturing a light-diffusing sheet according to the present disclosure, since extrusion molding is used, the light-diffusing sheet according to the present disclosure described earlier can be manufactured at low cost.
In order to achieve the object described above, a light-diffusing sheet according to another aspect of the present disclosure includes a plurality of depressed portions formed in an approximately inverted polygonal pyramid on at least a first surface. Ridgelines that partition the plurality of depressed portions have a depressed shape between intersections of the ridgelines with respect to the straight lines that connect the intersections. When an array pitch of the plurality of depressed portions is denoted by P and a dimension occupied by a curved portion of a vertex of each of the ridgelines in an array direction of the plurality of depressed portions is denoted by Wr, a ratio Wr/P is 0.3 or lower. A maximum height difference d between the straight lines and the ridgelines is 1 μm or more and 10 μm or less. The plurality of depressed portions include a depressed portion of which a vertex of the approximately inverted polygonal pyramid is formed in a rectangular shape.
With the light-diffusing sheet according to the other aspect of the present disclosure, since the light-diffusing sheet includes a plurality of depressed portions formed in an approximately inverted polygonal pyramid on at least a first surface, brightness uniformity can be improved. In addition, while the ridgelines (an opening edge of the depressed portions) that partition the depressed portions cause abrasion and damage, the ridgelines have a depressed shape between the intersections of the ridgelines. Therefore, abrasion and damage are less likely to occur even when the light-diffusing sheet is used by being stacked with other optical sheets or other light-diffusing sheets. In addition, the dimension Wr occupied by the curved portion of a vertex of each of the ridgelines in the array direction of the depressed portions is kept to or under 30% of the array pitch P of the depressed portions. Therefore, since the vertex of the ridgelines can maintain a steep shape, brightness uniformity does not readily decline even when the ridgelines are depressed between the intersections of the ridgelines. Furthermore, since the maximum height difference d between the straight lines connecting the intersections of the ridgelines and the ridgelines is set to 1 μm or more, scratch resistance is improved and, at the same time, since the maximum height difference d is set to 10 μm or less, a decline in brightness uniformity can be suppressed. Moreover, since the vertex of the approximately inverted polygonal pyramid (in other words, a bottom part of the depressed portions) is formed in a rectangular shape, mass production of the light-diffusing sheet of which brightness uniformity is prevented from declining can be readily performed.
According to the present disclosure, a light-diffusing sheet that is less susceptible to damage even when stacked with other optical sheets while improving brightness uniformity can be provided.
Hereinafter, an embodiment of the present disclosure will be described with reference to the drawings. It should be noted that the scope of the present disclosure is not limited to the embodiment described below and any modifications can be made without departing from the scope of technical ideas of the present disclosure.
As shown in
While a shape of a display screen 50a of the liquid crystal display device 50 as viewed from front (above in
In the liquid crystal display device 50, an image is displayed by applying a voltage of a predetermined magnitude to the liquid crystal layer 3 to change a state of alignment of the liquid crystal layer 3, adjusting transmittance of light incident via the first polarizing plate 6 from the backlight unit 40, and emitting the light via the second polarizing plate 7 in each sub-pixel corresponding to each pixel electrode.
The liquid crystal display device 50 according to the present embodiment is used as a display device to be built into various information apparatuses (for example, a vehicle-mounted device for car navigation or the like, a personal computer, a mobile phone, a portable information terminal, a portable game machine, a copy machine, a ticket vending machine, and an automated teller machine).
For example, the TFT substrate 1 includes a plurality of TFTs provided in a matrix pattern on a glass substrate, an interlayer insulating film provided so as to cover each TFT, a plurality of pixel electrodes provided in a matrix pattern on the interlayer insulating film and respectively connected to the plurality of TFTs, and an alignment film provided so as to cover each pixel electrode. For example, the CF substrate 2 includes a black matrix provided in a grid pattern on a glass substrate, a color filter including a red layer, a green layer, and a blue layer respectively provided between the respective grids of the black matrix, a common electrode provided so as to cover the black matrix and the color filter, and an alignment film provided so as to cover the common electrode. The liquid crystal layer 3 is constituted of a nematic liquid crystal material or the like containing liquid crystal molecules with electro-optic characteristics. For example, the first polarizing plate 6 and the second polarizing plate 7 include a polarizer layer with a polarizing axis in one direction and a pair of protection layers provided so as to sandwich the polarizer layer.
As shown in
For example, the reflecting sheet 41 is constituted of a film made of white polyethylene terephthalate resin, a sliver-deposited film, or the like.
While a type of the small light sources 42 is not particularly limited, for example, the small light sources 42 may be LED elements, laser elements, or the like and LED elements may be used from the perspectives of cost, productivity, and the like. A lens may be mounted to the LED elements to be used as the small light sources 42 in order to adjust emission angle characteristics of the LED elements. For example, as shown in
In addition, while the number of arranged small light sources 42 is also not particularly limited, when the plurality of small light sources 42 are to be arranged in a distributed manner, the small light sources 42 are preferably regularly arranged on the reflecting sheet 41. Regularly arranged means arranged with certain regularity and, for example, arranging the small light sources 42 at equal intervals constitutes arranging regularly. When the small light sources 42 are to be arranged at equal intervals, a center-to-center distance between two adjacent small light sources 42 may be 0.5 mm or more (preferably, 2 mm or more) and 20 mm or less.
Each first light-diffusing sheet 43 includes a base material layer 21. A plurality of depressed portions 22 are provided on a first surface (a surface opposing the small light sources 42) 43a of the first light-diffusing sheet 43. The plurality of depressed portions 22 are formed in an approximately inverted polygonal pyramid. In the present example, the plurality of depressed portions 22 are formed in an approximately inverted right square pyramid. Depressed portions 22 that are adjacent to each other are partitioned by ridgelines 23. An array pitch of the plurality of depressed portions 22 is, for example, around 50 μm or more and around 500 μm or less. An angle formed between a wall surface of the depressed portions 22 (an inclined surface of the approximately inverted polygonal pyramid) and a sheet surface (a virtual mirror surface without the depressed portions 22) of the first light-diffusing sheet 43 is set to, for example, 40 degrees or more and 65 degrees or less. In other words, a vertex angle of the depressed portions 22 is set to, for example, 50 degrees or more and 100 degrees or less. While a second surface 43b of the first light-diffusing sheet 43 may be a mirror surface, the second surface 43b is preferably a matte surface in order to improve diffusivity.
While the base material layer 21 is constructed using, for example, a polycarbonate as a base material (matrix resin) and preferably does not contain a diffusing agent, the base material layer 21 may contain up to, for example, around 0.1 to 4 percent by mass of the diffusing agent per 100 percent by mass of the base material. Known materials can be appropriately used as the diffusing agent. While the first light-diffusing sheet 43 has a one-layer structure of the base material layer 21 in the present example, alternatively, the first light-diffusing sheet 43 may have a structure of two layers or more including a layer on which the depressed portions 22 are formed.
The second light-diffusing sheet 44 may include a matte surface on a first surface (a surface that opposes the first prism sheet 45) 44a and a mirror surface or depressed portions formed in an approximately inverted right square pyramid on a second surface 44b. The second light-diffusing sheet 44 is constructed using, for example, a polycarbonate as a base material (matrix resin) and preferably contains a diffusing agent and, for example, the second light-diffusing sheet 44 may contain around 0.5 to 4 percent by mass of the diffusing agent per 100 percent by mass of the base material. The second light-diffusing sheet 44 is constructed by, for example, mixing 1 part by mass of a silicone composite powder (average particle size 2.0 μm) as a diffusing agent per 99 parts by mass of an aromatic polycarbonate resin.
The first prism sheet 45 and the second prism sheet 46 are, for example, films formed such that a plurality of groove lines with an isosceles triangular cross-section are adjacent to each other and a vertex angle of a prism sandwiched between a pair of adjacent groove lines is around 90 degrees. In this case, each groove line formed on the first prism sheet 45 and each groove line formed on the second prism sheet 46 are arranged so as to be orthogonal to each other. The first prism sheet 45 and the second prism sheet 46 may be integrally formed. For example, a PET (polyethylene terephthalate) film given prism shapes using a UV-curable acrylic resin may be used as the first prism sheet 45 and the second prism sheet 46.
Although not illustrated, when a polarizing sheet is provided above the second prism sheet 46, for example, the DBEF series manufactured by 3M may be used as the polarizing sheet. The polarizing sheet improves brightness of the display screen 50a by preventing light emitted from the backlight unit 40 from being absorbed by the first polarizing plate 6 of the liquid crystal display device 50.
While the plurality of depressed portions 22 are formed on the first surface (the surface opposing the small light sources 42) 43a of the first light-diffusing sheet 43 in the example shown in
The plurality of depressed portions 22 may be formed in an approximately inverted polygonal pyramid. The plurality of depressed portions 22 may be regularly two-dimensionally arrayed. As an “inverted polygonal pyramid”, a triangular pyramid, a square pyramid, or a hexagonal pyramid that can be two-dimensionally arranged in a seamless manner is preferable. While a die (metal roll) is used in manufacturing steps such as extrusion molding and injection molding when providing the depressed portions 22, an inverted square pyramid may be selected as the “inverted polygonal pyramid” in consideration of accuracy of cutting operations of a surface of the die (metal roll).
While the expression “approximately inverted polygonal pyramid” is used in consideration of the fact that it is difficult to form depressed portions of a geometrically-strict inverted polygonal pyramid using ordinary shape transfer techniques, it is needless to say that the expression includes a true inverted polygonal pyramid and shapes that are substantially an inverted polygonal pyramid. In addition, “approximately” means “can be approximated” and, for example, an “approximate square pyramid” refers to a shape that can be approximated to a square pyramid. Furthermore, shapes having deformed from an “inverted polygonal pyramid” within a range of inevitable variability of shapes attributable to machining accuracy in industrial production are also included in an “approximately inverted polygonal pyramid”.
When a plurality of depressed portions 22 are regularly two-dimensionally arrayed, the plurality of depressed portions 22 may be seamlessly provided over an entire surface of the first light-diffusing sheet 43 or may be provided at constant intervals (pitch).
The first light-diffusing sheet 43 may be constituted of the base material layer 21 not including a diffusing agent such as the base material layer 21 made of a clear polycarbonate. When the base material layer 21 is to contain a diffusing agent, while a material of the diffusing agent is not particularly limited, inorganic particles of silica, titanium oxide, aluminum hydroxide, barium sulfate, or the like or organic particles of acrylic, acrylonitrile, silicone, polystyrene, polyamide, or the like may be used. A particle size of the diffusing agent may be set to, for example, 0.1 μm or more (preferably, 1 μm or more) and 10 μm or less (preferably, 8 μm or less) from the perspective of a light-diffusing effect. While the first light-diffusing sheet 43 preferably does not include a diffusing agent from the perspectives of an effect of reflection and refraction by the approximately inverted polygonal pyramid shape and a light-diffusing effect by the diffusing agent, a content of the diffusing agent may be set to, for example, 0.1 percent by mass or more (preferably, 0.3 percent by mass or more) and 10 percent by mass or less (preferably, 8 percent by mass or less) with a material (matrix) constituting the base material layer 21 being 100 percent by mass. A difference between the refractive index of the diffusing agent and the refractive index of the matrix of the base material layer 21 may be 0.01 or more, preferably 0.03 or more, more preferably 0.05 or more, even more preferably 0.1 or more, and most preferably 0.15 or more. The diffusing effect by the diffusing agent becomes insufficient when the difference between the refractive index of the diffusing agent and the refractive index of the matrix of the base material layer 21 is less than 0.01.
While a resin that constitutes the matrix of the base material layer 21 is not particularly limited as long as a material that transmits light is used, for example, acrylic, polystyrene, polycarbonate, MS (methyl methacrylate-styrene copolymer) resin, polyethylene terephthalate, polyethylene naphthalate, cellulole acetate, or polyimide may be used.
While a thickness of the first light-diffusing sheet 43 is not particularly limited, for example, the thickness may be 3 mm or less (preferably 2 mm or less, more preferably 1.5 mm or less, even more preferably 1 mm or less) and 0.1 mm or more. Achieving a thinner liquid crystal display becomes difficult when the thickness of the first light-diffusing sheet 43 exceeds 3 mm. On the other hand, producing an effect of improving brightness uniformity becomes difficult when the thickness of the first light-diffusing sheet 43 falls below 0.1 mm.
When the first light-diffusing sheet 43 has a multilayer structure (for example, a base material layer constituting a first layer and a depressed portion formation layer constituting a second layer), a thickness of the depressed portion formation layer is greater than a maximum depth of the depressed portions 22. For example, in a case of a layer provided with depressed portions with a depth of 20 μm, the thickness of the layer is set greater than 20 μm. The first light-diffusing sheet 43 may be configured to have a structure of three layers or more including the base material layer and the depressed portion formation layer. Alternatively, the base material layer and the depressed portion formation layer may be respectively configured as independent sheets and the sheets may either be stacked or separately arranged.
Hereinafter, a method of manufacturing the first light-diffusing sheet 43 will be described. While the method of manufacturing the first light-diffusing sheet 43 is not particularly limited, for example, an extrusion molding method or an injection molding method may be used. When subjecting the first light-diffusing sheet 43 to extrusion molding, for example, a line rate may be set to 10 m/minute or more and 30 m/minute or less and compressible linear pressure may be set to 100 kgf/cm or more and 500 kgf/cm or less.
Procedures of manufacturing a single-layer light-diffusing sheet with uneven shapes on a surface thereof using an extrusion molding method are as follows. First, plastic particles with a pellet shape to which a diffusing agent has been added (plastic particles with a pellet shape to which a diffusing agent has not been added may be mixed therewith) are fed into a single-screw extruder and melted and kneaded while applying heat. Subsequently, after sandwiching molten resin extruded by T-dies with two metal rolls and cooling the molten resin, a diffusing sheet is fabricated by conveying the resin using a guide roll and cutting the resin into flat sheets with a sheet cutter. In this case, since sandwiching the molten resin using metal rolls of which surfaces have an inverted shape of a desired uneven shape causes the inverted shape on the roll surfaces to be transferred to the resin, the desired uneven shape can be formed on the surface of the diffusing sheet. In addition, since the shape transferred to the resin does not necessarily represent a 100% transfer of the shape of the roll surfaces, the shape of the roll surfaces may be designed backward from a degree of transfer.
When manufacturing a light-diffusing sheet with a two-layer structure having an uneven shape on a surface thereof using an extrusion molding method, for example, after feeding plastic particles with a pellet shape necessary for forming each layer into each of two single-screw extruders, procedures similar to those described earlier may be executed for each layer and the respective fabricated sheets may be stacked.
Alternatively, a light-diffusing sheet with a two-layer structure having an uneven shape on a surface thereof may be fabricated as described below. First, plastic particles with a pellet shape necessary for forming each layer are fed into each of two single-screw extruders and melted and kneaded while applying heat. Subsequently, molten resin to become each layer is fed into one T-die and stacked molten resin having been stacked in the T-die and extruded from the T-die is sandwiched between two metal rolls and cooled. Subsequently, a diffusing sheet with a two-layer structure having an uneven shape on a surface thereof may be fabricated by conveying the stacked molten resin using a guide roll and cutting the resin into flat sheets with a sheet cutter.
In addition, a light-diffusing sheet may be manufactured as described below by shape-transfer using UV (ultraviolet light). First, a roll having an inverted shape of an uneven shape to be transferred is filled with an uncured ultraviolet-curing resin and a base material is pressed against the resin. Next, ultraviolet light is radiated to cure the ultraviolet-curing resin in a state where the roll filled with the resin and the base material are integrated. Next, a sheet to which the uneven shape has been shape-transferred by the resin is separated from the roll. Finally, the sheet is once again irradiated with ultraviolet light to completely cure the resin and a diffusing sheet with an uneven shape on a surface thereof is fabricated.
Hereinafter, features of the first light-diffusing sheet 43 according to the present embodiment will be described in detail with reference to
As shown in
As a feature of the first light-diffusing sheet 43, with respect to straight lines Lx and Ly connecting intersections 23a of the ridgelines 23, the ridgelines 23 have a depressed shape between the intersections 23a. In this case, a maximum height difference d between the straight lines Lx and Ly that connect the intersections 23a and the ridgelines 23 shall be 1 μm or more and 10 μm or less, may preferably be 1.5 μm or more and 7 μm or less, and may more preferably be 2.5 μm or more and 5 μm or less.
While the ridgelines preferably have a depressed shape between all intersections 23a of the ridgelines in the first light-diffusing sheet 43, it is not essential for the ridgelines 23 to have a depressed shape between all of the intersections 23a. In other words, the ridgelines 23 need not have a depressed shape between parts of the intersections 23a.
When the depressed portions 22 are formed in an inverted right square pyramid, the array pitch Px of the depressed portions 22 in the X-direction is equal to intervals (horizontal distances) between the intersections 23a in the X-direction and the array pitch Py of the depressed portions 22 in the Y-direction is equal to intervals (horizontal distances) between the intersections 23a in the Y-direction.
In addition, when a maximum height difference d represents an average value of the maximum height difference dx in the X-direction and the maximum height difference dy in the Y-direction, the maximum height difference d shall be set to 1 μm or more and 10 μm or less, may preferably be set to 1.5 μm or more and 7 μm or less, and may more preferably be set to 2.5 μm or more and 5 μm or less.
Furthermore, while a depressed shape of the ridgelines 23 between the intersections 23a is not particularly limited, for example, as shown in
As another feature of the first light-diffusing sheet 43, when the array pitch of the depressed portions 22 is denoted by P and a dimension occupied by a curved portion of a vertex of each of the ridgelines 23 in the array direction of the depressed portions 22 is denoted by Wr, a ratio Wr/P shall be 0.3 or lower, may more preferably be 0.2 or lower, and may even more preferably be 0.1 or lower.
In the sectional structure shown in
In the sectional structure shown in
When the depressed portions 22 are formed in an inverted square pyramid, and an average value of the array pitch Px and the array pitch Py is denoted by P and an average value of the dimension Wrx and the dimension Wry is denoted by Wr, a ratio Wr/P shall be set to 0.3 or lower, may preferably be set to 0.2 or lower, and may more preferably be set to 0.1 or lower.
In addition, in a measurement of the array pitches Px and Py, a “horizontal distance between the intersections 23a” in each of the X-direction and the Y-direction is obtained as Px and Py. In this manner, the array pitches Px and Py can be readily and accurately obtained even in the method of measuring a “horizontal distance between the intersections 23a”.
A further feature of the first light-diffusing sheet 43 is that, for example, as shown in
As described above, the first light-diffusing sheet 43 according to the present embodiment includes the plurality of depressed portions 22 formed in an approximately inverted polygonal pyramid on at least the first surface 43a. The ridgelines 23 that partition the plurality of depressed portions 22 have a depressed shape between intersections 23a of the ridgelines 23 with respect to a straight line that connects the intersections 23a. When the array pitch of the plurality of depressed portions 22 is denoted by P and the dimension occupied by a curved portion of a vertex of each of the ridgelines 23 in the array direction of the plurality of depressed portions 22 is denoted by Wr, the ratio Wr/P is 0.3 or lower. The maximum height difference d between connecting the intersections 23a of the ridgelines 23 and the ridgelines 23 is 1 μm or more and 10 μm or less. The plurality of depressed portions 22 includes the depressed portion 22 which is formed in an approximately inverted polygonal pyramid and which has the vertex 22b with a linear shape.
With the first light-diffusing sheet 43 according to the present embodiment, since the first light-diffusing sheet 43 includes the plurality of depressed portions 22 formed in an approximately inverted polygonal pyramid on at least the first surface 43a, brightness uniformity can be improved. In addition, while the ridgelines 23 (an opening edge of the depressed portions 22) that partition the depressed portions 22 cause abrasion and damage, the ridgelines 23 have a depressed shape between the intersections 23a of the ridgelines 23. Therefore, abrasion and damage are less likely to occur even when the light-diffusing sheet is used by being stacked with other optical sheets or other light-diffusing sheets. In addition, the dimension Wr occupied by the curved portion of a vertex of each of the ridgelines 23 in the array direction of the depressed portions 22 is kept to or under 30% of the array pitch P of the depressed portions. Therefore, since the vertex of the ridgelines 23 can maintain a steep shape, brightness uniformity does not readily decline even when the ridgelines 23 are depressed between the intersections 23a. Furthermore, since the maximum height difference d between a straight line connecting the intersections 23a and the ridgelines 23 is set to 1 μm or more, scratch resistance is improved and, at the same time, since the maximum height difference d is set to 10 μm or less, a decline in brightness uniformity can be suppressed. Moreover, since the vertex 22b of the depressed portions 22 (approximately inverted polygonal pyramids) is formed in a linear shape, mass production of the first light-diffusing sheet 43 of which brightness uniformity is prevented from declining can be readily performed.
In the first light-diffusing sheet 43 according to the present embodiment, when the maximum height difference d between a straight line that connects the intersections 23a and the ridgelines 23 is 1.5 μm or more and 7 μm or less, both scratch resistance and brightness uniformity can be further improved. In this case, when the maximum height difference d is 2.5 μm or more and 5 μm or less, both scratch resistance and brightness uniformity can be even further improved.
In the first light-diffusing sheet 43 according to the present embodiment, in a case where the array pitch of the plurality of depressed portions 22 is denoted by P and a dimension occupied by a curved portion of a vertex of each of the ridgelines 23 in the array direction of the plurality of depressed portions 22 is denoted by Wr, when the ratio Wr/P is 0.2 or lower, brightness uniformity can be further improved. In this case, when the ratio Wr/P is 0.1 or lower, brightness uniformity can be even further improved.
In the first light-diffusing sheet 43 according to the present embodiment, when the array pitch P of the plurality of depressed portions 22 is 50 μm or more and 500 μm or less and an angle formed between the wall surface of the plurality of depressed portions 22 (in other words, inclined surfaces of the approximately inverted polygonal pyramids) and the sheet surface is 40 degrees or more and 65 degrees or less, brightness uniformity can be improved.
In the first light-diffusing sheet 43 according to the present embodiment, when the ridgeline 23 is depressed in an approximately parabolic shape, an approximately arc shape, an approximately triangular shape, or an approximately trapezoidal shape between the intersections 23a, scratch resistance can be improved.
In the first light-diffusing sheet 43 according to the present embodiment, the plurality of depressed portions 22 may be formed in an approximately inverted square pyramid. In this case, the ridgelines 23 may extend in the X-direction (first direction) and the Y-direction (second direction). In addition, the maximum height difference d between a straight line that connects the intersections 23a and the ridgelines 23 may be an average value of the maximum height difference dx between the straight line and the ridgelines 23 in the X-direction and a maximum height difference dy between the straight line and the ridgelines 23 in the Y-direction. Furthermore, the array pitch P of the plurality of depressed portions 22 may be an average value of the array pitch Px of the depressed portions 22 in the X-direction and an array pitch Py of the depressed portions 22 in the Y-direction. Moreover, the dimension Wr occupied by a curved portion of a vertex of each of the ridgelines 23 in the array direction of the depressed portions 22 may be an average value of the dimension Wrx occupied by a curved portion of a vertex of each of the ridgelines 23 in the X-direction and the dimension Wry occupied by a curved portion of a vertex of each of the ridgelines 23 in the Y-direction. Accordingly, a light-diffusing sheet with superior scratch resistance and brightness uniformity can be readily manufactured.
In the first light-diffusing sheet 43 according to the present embodiment, when the plurality of depressed portions 22 are only provided on the first surface 43 a and the second surface 43b is a matte surface, brightness uniformity can be further improved while suppressing abrasion and damage on the second surface 43b.
In the first light-diffusing sheet 43 according to the present embodiment, a ratio of depressed portions 22 of which the vertex 22b is formed in a linear shape among the plurality of depressed portions 22 may be 10% or more. Alternatively, the ratio may be 20% or more, 30% or more, 40% or more, 50% or more, 60% or more, 70% or more, 80% or more, 90% or more, or 100%.
The backlight unit 40 according to the present embodiment is the backlight unit 40 which is built into the liquid crystal display device 50 and which guides light emitted by the light source 42 toward the display screen 50a and includes the first light-diffusing sheet 43 according to the present embodiment between the display screen 50a and the light source 42.
Since the backlight unit 40 according to the present embodiment includes the first light-diffusing sheet 43 according to the present embodiment, brightness uniformity can be improved and, at the same time, damage can be suppressed even when sheets of the first light-diffusing sheet 43 are stacked or the first light-diffusing sheet 43 and other optical sheets are stacked.
In the backlight unit 40 according to the present embodiment, when the light source 42 is arranged on the reflecting sheet 41 provided on an opposite side to the display screen 50a as viewed from the first light-diffusing sheet 43, brightness uniformity is further improved.
The liquid crystal display device 50 according to the present embodiment includes the backlight unit 40 according to the present embodiment and the liquid crystal display panel 5.
Since the liquid crystal display device 50 according to the present embodiment and an information apparatus including the liquid crystal display device 50 include the backlight unit 40 according to the present embodiment, brightness uniformity can be improved and, at the same time, damage can be suppressed even when sheets of the first light-diffusing sheet 43 are stacked or the first light-diffusing sheet 43 and other optical sheets are stacked.
The method of manufacturing a light-diffusing sheet according to the present embodiment is a method of manufacturing the first light-diffusing sheet 43 according to the present embodiment, wherein the first light-diffusing sheet 43 is subjected to extrusion molding at a line rate of 10 m/minute or more and 30 m/minute or less and compressible linear pressure of 100 kgf/cm or more and 500 kgf/cm or less.
With the method of manufacturing a light-diffusing sheet according to the present embodiment, since the dimension Wr occupied by the curved portion of the vertex of the ridgelines 23 in the array direction of the depressed portions 22 can be kept to or under 30% of the array pitch P of the depressed portions 22, the first light-diffusing sheet 43 of which a shape of the vertex of the ridgelines 23 is steep and which has superior brightness uniformity can be manufactured.
In addition, with the method of manufacturing a light-diffusing sheet according to the present embodiment, the maximum height difference d between a straight line that connects intersections 23a and the ridgelines 23 can be set to 1 μm or more and 10 μm or less. In other words, the first light-diffusing sheet 43 in which the ridgelines 23 are depressed between the intersections 23a and elevated at portions of the intersections 23a is obtained. Therefore, even when sheets of the first light-diffusing sheet 43 are stacked or the first light-diffusing sheet 43 and other optical sheets are stacked, since the ridgelines 23 are less likely to come into contact with the other optical sheets between the intersections 23a, abrasion and damage are less likely to occur, and since the ridgelines 23 come into point contact with, for example, the other optical sheets at the intersections 23a, slippage is created and reduces abrasion and damage. As a result, the first light-diffusing sheet 43 with superior scratch resistance can be manufactured.
Furthermore, with the method of manufacturing a light-diffusing sheet according to the present embodiment, since extrusion molding is used, the first light-diffusing sheet 43 according to the present embodiment can be manufactured at low cost.
While the vertex 22b of the depressed portions 22 (approximately inverted polygonal pyramids) is formed in a linear shape in the first light-diffusing sheet 43 according to the present embodiment, even when a planar shape of the vertex 22b is formed in a rectangular shape instead of a linear shape, similar advantageous effects to the present embodiment can be produced.
Hereinafter, the first light-diffusing sheet 43 according to examples will be described by comparing the examples with comparative examples.
A shape observation of the depressed portions 22 formed on the first light-diffusing sheet 43 according to each example described below was performed using the laser microscope VK-100 manufactured by KEYENCE CORPORATION. Specifically, performed were measurements of: a cross-sectional shape of the ridgelines 23 of the depressed portions 22 formed in an inverted right square pyramid (cross-sectional shapes shown in
As optical properties of the first light-diffusing sheet 43 according to each example described below, a Haze and light transmittance at a wavelength of 450 nm were measured. Haze was measured using HZ-2 manufactured by Suga Test Instruments Co., Ltd. in conformity with JIS K-7105 by causing light to be incident to the surface (first surface 43a) with the depressed portions 22 formed in an inverted right square pyramid. In addition, light transmittance at the wavelength of 450 nm was measured using V-670 manufactured by JASCO Corporation by causing light to be incident to the surface (first surface 43a) with the depressed portions 22 formed in an inverted right square pyramid.
A device shown in
Assessments in the inspection and the determination were performed based on the following criteria.
AA: Light-diffusing sheet with exceptionally high scratch resistance with absolutely no visible scratches.
A: Light-diffusing sheet with high scratch resistance with hardly any visible scratches.
B: Light-diffusing sheet with somewhat high scratch resistance with a minimal amount of visible scratches.
C: Light-diffusing sheet of which scratch resistance is near an acceptable lower limit with some visible scratches.
X: Light-diffusing sheet with poor scratch resistance with a large amount of visible scratches.
A measurement of brightness and brightness uniformity of the first light-diffusing sheet 43 according to each example described below was performed with the configuration of the backlight unit 40 shown in
In the measurement of brightness uniformity, firstly, in the LED array (6×6) shown in
brightness uniformity=(average value of cross-sectional brightness)/(standard deviation of cross-sectional brightness).
The brightness uniformity obtained in this manner show that, the higher a numerical value of the brightness uniformity, the more uniform the brightness.
Assessment criteria of brightness uniformity are as follows.
AA: Light-diffusing sheet with brightness uniformity of 210 or higher and exhibiting highest uniformity at a level where there is absolutely no visible brightness non-uniformities.
A: Light-diffusing sheet with brightness uniformity of 200 or higher and lower than 210 and exhibiting high uniformity at a level where brightness spots are hardly visible.
B: Light-diffusing sheet with brightness uniformity of 190 or higher and lower than 200 and exhibiting an acceptable level of uniformity with a minimal amount of visible brightness spots.
C: Light-diffusing sheet with brightness uniformity of 180 or higher and lower than 190 and exhibiting the lowest acceptable level of uniformity with visible brightness spots.
X: Light-diffusing sheet with brightness uniformity of lower than 180 and exhibiting poor uniformity with clearly visible brightness spots.
In addition, assessment criteria of brightness are as follows.
A: Light-diffusing sheet with average value of cross-sectional brightness of 3150 cd/m2 or higher.
B: Light-diffusing sheet with average value of cross-sectional brightness of 3100 cd/m2 or higher and lower than 3150 cd/m2.
C: Light-diffusing sheet with average value of cross-sectional brightness of 3050 cd/m2 or higher and lower than 3100 cd/m2.
An overall assessment of the first light-diffusing sheet 43 according to each example to be described later was performed according to the following criteria based on a result of the scratch resistance test and an assessment result of brightness uniformity.
AA: Best overall light-diffusing sheet which scored A or higher in all of the assessment results of the scratch resistance test of both the inverted right square pyramid surface and the matte surface and the assessment result of brightness uniformity and which scored two or more AA's.
A: Best overall light-diffusing sheet (excluding AA-assessed items) which scored A or higher in all of the assessment results of the scratch resistance test of both the inverted right square pyramid surface and the matte surface and the assessment result of brightness uniformity.
B: High overall light-diffusing sheet (excluding AA-assessed and A-assessed items) which scored B or higher in all of the assessment results of the scratch resistance test of both the inverted right square pyramid surface and the matte surface and the assessment result of brightness uniformity.
C: Usable light-diffusing sheet (excluding AA-assessed, A-assessed, and B-assessed items) with lowest overall acceptable level of performance which scored C or higher in all of the assessment results of the scratch resistance test of both the inverted right square pyramid surface and the matte surface and the assessment result of brightness uniformity.
X: Poor overall light-diffusing sheet with an assessment of X in any one of the assessment results of the scratch resistance test of both the inverted right square pyramid surface and the matte surface and the assessment result of brightness uniformity.
A method of manufacturing the first light-diffusing sheet 43 according to example 1 is as follows. First, an aromatic polycarbonate resin of which a melt mass-flow rate as measured in conformity with ISO 1133 is 15 g/10 minutes is fed into an extruder, melted and kneaded, and extruded by a T-die. Subsequently, using a roll having, on a surface thereof, a shape (a shape of a right square pyramid with a height of 50 μm, a pitch of 100 μm, and a vertex angle of 90 degrees) shown in (A) and (B) ((B) is a shape diagram representing a view from a direction of a cross section taken along line X-Y in (A)) in
A shape observation of the depressed portions (inverted right square pyramids) 22 formed on the first light-diffusing sheet 43 according to example 1 fabricated as described above was performed using the laser microscope VK-100 manufactured by KEYENCE CORPORATION. Specifically, performed were measurements of: a cross-sectional shape of the ridgelines 23 of the depressed portions 22 formed in an inverted right square pyramid (cross-sectional shapes shown in
In a method of manufacturing the first light-diffusing sheet 43 according to example 2, as shown in Table 1, the same conditions as example 1 were used with the exception of using a roll having, on a surface thereof, a shape of a right square pyramid with a height of 54.6 μm, a pitch of 100 μm, and a vertex angle of 85 degrees as the roll with a right square pyramid shape among the two metal rolls.
In a method of manufacturing the first light-diffusing sheet 43 according to example 3, as shown in Table 1, the same conditions as example 1 were used with the exception of using a roll having, on a surface thereof, a shape of a right square pyramid with a height of 59.6 μm, a pitch of 100 μm, and a vertex angle of 80 degrees as the roll with a right square pyramid shape among the two metal rolls.
In comparative example 1, first, a press original plate with a thickness of 1 mm was created using the same aromatic polycarbonate resin as example 1. Next, using a flat metal mold having, on a surface thereof, a shape (a shape created by rounding a valley portion of a pyramid of a same shape of the right square pyramid as example 1 into a curved surface shape with a radius of curvature of 4.2 μm) shown in (A) and (B) ((B) is a shape diagram representing a view from a direction of a cross section taken along line X-Y in (A)) in
In comparative example 2, after creating a press original plate in a similar manner to comparative example 1, the 180 μm-thick light-diffusing sheet shown in Table 1 was created by the compression molding method by performing heating, pressing, and cooling under the same conditions as comparative example 1 with the exception of using a flat metal mold having, on a surface thereof, a shape created by rounding, in a similar manner to comparative example 1, a valley portion of a pyramid of a same shape of the right square pyramid as example 2 into a curved surface shape with a radius of curvature of 4.2 μm.
In comparative example 3, after creating a press original plate in a similar manner to comparative example 1, the 180 μm-thick light-diffusing sheet shown in Table 1 was created by the compression molding method by performing heating, pressing, and cooling under the same conditions as comparative examples 1 and 2 with the exception of using a flat metal mold having, on a surface thereof, a shape created by rounding, in a similar manner to comparative examples 1 and 2, a valley portion of a pyramid of a same shape of the right square pyramid as example 3 into a curved surface shape with a radius of curvature of 4.2 μm.
With respect to the first light-diffusing sheet 43 obtained by examples 1 to 3, a shape, dimensions, an angle, and the like of each element obtained by measurement are shown in Table 2 together with comparative examples 1 to 3, and a measurement result of optical properties, a result of the scratch resistance test, assessment results of brightness and brightness uniformity, and an overall assessment result are shown in Table 3 together with comparative examples 1 to 3.
From the results shown in Table 2 and Table 3, in the first light-diffusing sheet 43 obtained in examples 1 to 3 on which the depressed portions 22 with inverted right square pyramid shapes are formed, the maximum height difference d between a straight line connecting the intersections 23a and the ridgelines 23 is 1.0 μm or more and the ridgelines 23 have a shape that is depressed in a roughly parabolic shape between the intersections 23a. Therefore, since abrasion and damage attributable to the ridgelines 23 are less likely to occur even when used stacked, the scratch resistance tests produced favorable results.
On the other hand, in comparative examples 1 to 3, while a curved surface shape with a radius of curvature of around 4.2 μm is imparted near the vertex of the ridgelines 23, the maximum height difference d is 0 μm, the ridgelines 23 have no depression whatsoever, and the ridgelines 23 between the intersections 23a have a horizontal shape. Therefore, as a result of damage attributable to the ridgelines 23 occurring during the scratch resistance tests, results were poor with respect to scratch resistance.
In addition, in all of example 1 and comparative example 1, example 2 and comparative example 2, and example 3 and comparative example 3, the ratio Wr/P was 10% or lower and since a steep shape of the vertex of the ridgelines 23 is maintained, favorable assessment results comparable to each other were produced with respect to brightness uniformity.
From the above, the overall assessments of examples 1 to 3 were “C” and the overall assessments of comparative examples 1 to 3 were “X”.
In examples 4 to 7, as shown in Table 4, the light-diffusing sheet was fabricated by the same method as example 1 with the exception of changing the line rate among the molding conditions so as to range from 15 m/minute to 4 m/minute.
In examples 8 to 10 and comparative example 4, as shown in Table 4, the light-diffusing sheet was fabricated by the same method as example 1 with the exception of changing the compressible linear pressure between the two rolls among the molding conditions so as to range from 180 kgf/cm to 40 kgf/cm.
With respect to the first light-diffusing sheet 43 obtained by examples 4 to 10, a shape, dimensions, an angle, and the like of each element obtained by measurement are shown in Table 5 together with comparative example 4, and a measurement result of optical properties, a result of the scratch resistance test, assessment results of brightness and brightness uniformity, and an overall assessment result are shown in Table 6 together with comparative example 4.
From the results shown in Table 5 and Table 6, in the first light-diffusing sheet 43 obtained in examples 4 to 10 and comparative example 4 on which the depressed portions 22 with inverted right square pyramid shapes are formed, the maximum height difference d between a straight line connecting the intersections 23a and the ridgelines 23 is 1.0 μm or more and the ridgelines 23 have a shape that is depressed in a roughly parabolic shape between the intersections 23a. Therefore, since abrasion and damage attributable to the ridgelines 23 are less likely to occur even when used stacked, the scratch resistance tests produced favorable results.
In addition, in examples 4 to 10, the ratio Wr/P was 30% or lower in all of the examples and since a steep shape of the vertex of the ridgelines 23 is maintained, favorable assessment results comparable to each other were produced with respect to brightness uniformity.
However, in comparative example 4, since the ratio Wr/P exceeded 30%, a steep shape of the vertex of the ridgelines 23 is not maintained and a poor result was produced with respect to brightness uniformity.
From the above, the overall assessments of examples 4 to 10 were “C” and the overall assessment of comparative example 4 was “X”.
In a method of manufacturing the first light-diffusing sheet 43 according to example 11, a 200 μm-thick light-diffusing sheet shown in Table 7 was fabricated using more or less the same conditions as example 1 with the exception of using a roll having, on a surface thereof, a shape of a right square pyramid with a height of 90.0 μm, a pitch of 180 μm, and a vertex angle of 90 degrees as the roll with a right square pyramid shape among the two metal rolls.
In a method of manufacturing the first light-diffusing sheet 43 according to example 12, a 200 μm-thick light-diffusing sheet shown in Table 7 was fabricated using more or less the same conditions as example 1 with the exception of using a roll having, on a surface thereof, a shape of a right square pyramid with a height of 98.2 μm, a pitch of 180 μm, and a vertex angle of 85 degrees as the roll with a right square pyramid shape among the two metal rolls.
In a method of manufacturing the first light-diffusing sheet 43 according to example 13, a 200 μm-thick light-diffusing sheet shown in Table 7 was fabricated using more or less the same conditions as example 1 with the exception of using a roll having, on a surface thereof, a shape of a right square pyramid with a height of 107.3 μm, a pitch of 180 μm, and a vertex angle of 80 degrees as the roll with a right square pyramid shape among the two metal rolls.
In a method of manufacturing the first light-diffusing sheet 43 according to example 14, a 200 μm-thick light-diffusing sheet shown in Table 7 was fabricated using more or less the same conditions as example 1 with the exception of using a roll having, on a surface thereof, a shape of a right square pyramid with a height of 117.3 μm, a pitch of 180 μm, and a vertex angle of 75 degrees as the roll with a right square pyramid shape among the two metal rolls.
In examples 15 to 17, a 200 μm-thick light-diffusing sheet was fabricated using the same rolls as in example 13 but by changing the line rate among the molding conditions so as to range from 15 m/minute to 11 m/minute as shown in Table 7.
In comparative example 5, after creating a press original plate in a similar manner to comparative example 1, a 200 μm-thick light-diffusing sheet shown in Table 7 was created by the compression molding method by performing heating, pressing, and cooling under the same conditions as comparative example 1 with the exception of using a flat metal mold having, on a surface thereof, a shape created by rounding, in a similar manner to comparative example 1, a valley portion of a pyramid of a same shape of the right square pyramid as example 11 into a curved surface shape with a radius of curvature of 4.2 μm.
With respect to the first light-diffusing sheet 43 obtained by examples 11 to 17, a shape, dimensions, an angle, and the like of each element obtained by measurement are shown in Table 8 together with comparative example 5, and a measurement result of optical properties, a result of the scratch resistance test, assessment results of brightness and brightness uniformity, and an overall assessment result are shown in Table 9 together with comparative example 5.
From the results shown in Table 8 and Table 9, in the first light-diffusing sheet 43 obtained in examples 11 to 17 on which the depressed portions 22 with inverted right square pyramid shapes are formed, the maximum height difference d between a straight line connecting the intersections 23a and the ridgelines 23 is 2.5 μm or more and the ridgelines 23 have a shape that is depressed in a roughly parabolic shape between the intersections 23a. Therefore, since abrasion and damage attributable to the ridgelines 23 are even less likely to occur even when used stacked, the scratch resistance tests produced the most favorable results among the examples.
On the other hand, in comparative example 5, although a curved surface shape is imparted near the vertex of the ridgelines 23, the maximum height difference d is 0 μm, the ridgelines 23 have no depression whatsoever, and the ridgelines 23 between the intersections 23a have a horizontal shape. Therefore, as a result of damage attributable to the ridgelines 23 occurring during the scratch resistance tests, results were poor with respect to scratch resistance.
In addition, in examples 11 to 17 and comparative example 5, the ratio Wr/P was 10% or lower in all of the examples and the comparative example and since a steeper shape of the vertex of the ridgelines 23 is maintained, particularly favorable assessment results were produced with respect to brightness uniformity. In particular, in examples 11 to 17, since the maximum height difference d is 5.0 μm or less, a decline in brightness uniformity attributable to the ridgelines 23 having a depressed shape between the intersections 23a was not observed.
From the above, the overall assessment of example 11 was “A”, the overall assessments of examples 12 to 17 were “AA” representing highest scores, and the overall assessment of comparative example 5 was “X”.
In example 18, a 180 μm-thick light-diffusing sheet shown in Table 10 was fabricated using the same conditions as example 1 with the exception of feeding a mixture having been prepared in advance of 1 part by mass of a silicone composite powder (average particle size 2.0 μm) as a diffusing agent per 99 parts by mass of the aromatic polycarbonate resin used in example 1 into an extruder and performing melting and kneading.
In examples 19 to 23, a 180 μm-thick light-diffusing sheet was fabricated using the same method as in example 18 but by changing the line rate among the molding conditions so as to range from 15 m/minute to 9 m/minute as shown in Table 10.
With respect to the first light-diffusing sheet 43 obtained by examples 18 to 23, a shape, dimensions, an angle, and the like of each element obtained by measurement are shown in Table 11 and a measurement result of optical properties, a result of the scratch resistance test, assessment results of brightness and brightness uniformity, and an overall assessment result are shown in Table 12.
From the results shown in Table 11 and Table 12, in the first light-diffusing sheet 43 obtained in examples 18 to 23 on which the depressed portions 22 with inverted right square pyramid shapes are formed, the maximum height difference d between a straight line connecting the intersections 23a and the ridgelines 23 is 1.6 μm or more and the ridgelines 23 have a shape that is depressed in a roughly parabolic shape between the intersections 23a. Therefore, since abrasion and damage attributable to the ridgelines 23 are less likely to occur even when used stacked, the scratch resistance tests produced favorable results.
In addition, in examples 18 to 23, the ratio Wr/P was within a range of 6 to 13% and since a steep shape of the vertex of the ridgelines 23 is maintained, favorable assessment results were produced with respect to brightness uniformity.
From the above, the overall assessments of examples 18 to 23 were “C”.
In example 24, a 120 μm-thick light-diffusing sheet shown in Table 13 was fabricated using the aromatic polycarbonate resin used in example 1 and the molding conditions shown in Table 13, using a roll having, on a surface thereof, a shape (a shape of a right square pyramid with a height of 50 μm, a pitch of 100 μm, and a vertex angle of 90 degrees) shown in (A) and (B) in
In example 25, a 120 μm-thick light-diffusing sheet shown in Table 13 was fabricated using the same diffusing agent-containing aromatic polycarbonate resin as in example 18, the molding conditions shown in Table 13, and the same two metal rolls as in example 24.
In example 26, a 200 μm-thick light-diffusing sheet shown in Table 13 was fabricated using the same aromatic polycarbonate resin as in example 24, the molding conditions shown in Table 13, using the roll having, on a surface thereof, a shape of a right square pyramid with a height of 107.3 μm, a pitch of 180 μm, and a vertex angle of 80 degrees used in example 13 as one of two metal rolls, and using a roll having, on a surface thereof, a random matte shape (surface roughness Ra=2.0 μm) as the other roll.
In example 27, a 200 μm-thick light-diffusing sheet shown in Table 13 was fabricated using the same diffusing agent-containing aromatic polycarbonate resin as in example 25, the molding conditions shown in Table 13, using the same roll having, on a surface thereof, a shape of a right square pyramid as in examples 24 and 25 as one of two metal rolls, and using a roll having, on a surface thereof, a random matte shape (surface roughness Ra=2.0 μm) as the other roll.
With respect to the first light-diffusing sheet 43 obtained by examples 24 to 27, a shape, dimensions, an angle, and the like of each element obtained by measurement are shown in Table 14 and a measurement result of optical properties, a result of the scratch resistance test, assessment results of brightness and brightness uniformity, and an overall assessment result are shown in Table 15. In addition, surface photographs of samples after the scratch resistance test in each of examples 24 to 27 and comparative example 1 or, more specifically, surface photographs of the lower surface (inverted square pyramid surface) of the fixed sample and the upper surface (matte surface) of the moved sample are shown in
From the results shown in Table 14 and Table 15, in the first light-diffusing sheet 43 obtained in examples 24 to 27 on which the depressed portions 22 with inverted right square pyramid shapes are formed, the maximum height difference d between a straight line connecting the intersections 23a and the ridgelines 23 is 2.7 μm or more and the ridgelines 23 have a shape that is depressed in a roughly parabolic shape between the intersections 23a. Therefore, since abrasion and damage attributable to the ridgelines 23 are less likely to occur even when used stacked, as shown in
Note that in examples 24 and 25, relatively large depressions have occurred in the ridgelines 23 due to the thickness of the first light-diffusing sheet 43 being relatively thin and, in example 26, relatively large depressions have occurred in the ridgelines 23 due to the inverted square pyramids of the depressed portions 22 being relatively large.
In addition, in examples 24 to 27, the ratio Wr/P was within a range of around 5 to 11% and since a steep shape of the vertex of the ridgelines 23 is maintained, favorable assessment results were produced with respect to brightness uniformity.
From the above, the overall assessment of example 24 was “A”, the overall assessments of examples 25 and 27 were “C”, and the overall assessment of example 26 was “AA” representing a highest score.
Table 16 shows a result of examining a shape of a vertex of each of the inverted square pyramids with respect to five samples S1 to S5 with different inverted square pyramid shapes of the depressed portions 22 among the first light-diffusing sheets 43 according to the examples described above.
As shown in Table 16, in each of the samples S1 to S5, it was found that 50% or more of the vertexes of the inverted right square pyramids were formed in a linear shape in both the X-direction and the Y-direction (refer to
A rate at which the vertex of the inverted square pyramids is formed in a linear shape (an occurrence rate of linear vertexes) in the plurality of depressed portions 22 provided on the first light-diffusing sheet 43 was examined by a method shown in
Tables 17 to 19 show a result of examining an occurrence rate of linear vertexes with respect to the 15 samples respectively fabricated using the three pyramid rolls (hereinafter, also referred to as first to third rolls). In addition, tables 20 to 21 show a result of examining an occurrence rate by dividing the linear vertexes into those with a dimension of 1.0 μm or less and those with a dimension of more than 1.0 μm with respect to the samples fabricated using the first roll and the third roll.
Measurement of dimensions of the vertexes of the inverted square pyramids (bottom portions of the depressed portions 22) was performed using Shape Measurement Laser Microscope VK-X110 of the 3D Laser Scanning Confocal Microscope VK-X series manufactured by KEYENCE CORPORATION (and analysis application version 3.6.1.0 manufactured by the same manufacturer as analysis software). Specifically, a shape profile of a cross section which passes through a vertex of an inverted square pyramid (a bottom portion of the depressed portion 22) and which is orthogonal to the ridgelines 23 of the depressed portions 22 was measured with respect to each of the X-direction and the Y-direction (refer to
As shown in Tables 17 to 19, regardless of which pyramid roll was used, the ratio of depressed portions 22 of which the vertex 22b is formed in a linear shape among the plurality of depressed portions 22 or, in other words, the occurrence rate of linear vertexes was 10% or more.
Specifically, when using the first roll, as shown in Table 17, the occurrence rate of linear vertexes was 20% or more in all but one sample, the occurrence rate of linear vertexes was 40% or more in many samples, the occurrence rate of linear vertexes was 60% or more in a majority of the samples, and the occurrence rate of linear vertexes was 80% or more in almost half of the samples. In addition, when using the first roll, as shown in Table 20, the occurrence rate of linear vertexes with a dimension of more than 1.0 μm was 50% or more in almost half of the samples.
When using the second roll, as shown in Table 18, the occurrence rate of linear vertexes was 70% or more in all of the samples, the occurrence rate of linear vertexes was 90% or more in all but one sample, and the occurrence rate of linear vertexes was 100% in a majority of the samples.
When using the third roll, as shown in Table 19, the occurrence rate of linear vertexes was 30% or more in many samples and the occurrence rate of linear vertexes was 50% or more in a majority of the samples. In addition, when using the third roll, as shown in Table 21, the occurrence rate of linear vertexes with a dimension of more than 1.0 μm was 50% or more in one sample.
From the results described above, it was found that when the vertex 22b of the depressed portions 22 is formed in a linear shape, mass production of the first light-diffusing sheet 43 of which brightness uniformity is prevented from declining can be readily performed.
Note that the vertex 22b of the depressed portions 22 may be formed in a rectangular shape instead of being formed in a linear shape. Specifically, the “vertex 22b of the depressed portions 22 being a rectangular shape” means that the X-direction dimension and the Y-direction dimension of the vertex of the inverted square pyramid differ from each other and both dimensions are 0.1 μm or more. In this case, a dimensional difference between the X-direction dimension and the Y-direction dimension may be 10% or more of the longer dimension. Alternatively, the dimensional difference may be 20% or more, 30% or more, 40% or more, 50% or more, 60% or more, 70% or more, 80% or more, or 90% or more of the longer dimension. In addition, from the perspective of suppressing a decline in uniformity, the longer dimension of the X-direction dimension and the Y-direction dimension is preferably 10 μm or less, more preferably 5 μm or less, even more preferably 3 μm or less, and most preferably 2 μm or less.
While an embodiment (including examples: the same applies hereinafter) of the present disclosure has been described above, the present disclosure is not solely limited to the embodiment described above and various modifications can be made within the scope of the disclosure. In other words, the foregoing description of the embodiment is illustrative in nature and is not intended to limit the present disclosure, its applications, or its uses. For example, it is needless to say that a configuration (layer structure, material, and the like) of a light-diffusing sheet is not limited to the configuration of the first light-diffusing sheet 43 according to the embodiment described above. In addition, it is needless to say that a configuration of a backlight to which the light-diffusing sheet is applied and a configuration of a liquid crystal display device including the backlight are also not limited to the configurations of the backlight unit 40 and the liquid crystal display device 50 according to the embodiment described above.
For example, instead of the combination of a stack of two sheets of the first light-diffusing sheet 43 and the second light-diffusing sheet 44 in the backlight unit 40 according to the embodiment described above and shown in
| Number | Date | Country | Kind |
|---|---|---|---|
| 2022-087114 | May 2022 | JP | national |
| 2023-083829 | May 2023 | JP | national |
This application is a bypass continuation of International Application No. PCT/JP2023/019378, filed May 24, 2023, which international application claims priority to and the benefit of Japanese Application No. 2022-087114, filed May 27, 2022 and Japanese Application No. 2023-083829, filed May 22, 2023; the contents of all of which are hereby incorporated by reference herein in their respective entireties.
| Number | Date | Country | |
|---|---|---|---|
| Parent | PCT/JP2023/019378 | May 2023 | WO |
| Child | 18953812 | US |