Patent Application
20180358519
The present application claims priority under 35 U.S.C. § 119 to Japanese Patent Application No. 2018-071079, filed on Apr. 2, 2018, which claims priority to Japanese Patent Application No. 2017-114961, filed on Jun. 12, 2017, all of which are hereby incorporated by reference in their entireties.
The present disclosure relates to a light-emitting device and a method for manufacturing the light-emitting device.
Conventionally, a light-emitting device includes a sealing member made of a resin material such as an epoxy resin or a silicone resin, in order to protect a light-emitting element mounted in the light-emitting device. Recently, silicone-based resins, which have good resistance to heat, have been mainly used for sealing members for protecting high-output and high-luminosity light-emitting elements mounted in a lighting device or a backlight of a liquid crystal panel for example.
The silicone-based resins have good resistance to heat, but they have adhesiveness (tackiness). For example, Japanese patent publication No. 2009-141051 proposes attaching microparticles of SiO2 or the like on a surface of a silicone resin included in a light-emitting device after curing the silicone resin, in order to prevent delays in operations caused by the light-emitting device sticking to a tool or the like.
A light-emitting device according to certain embodiments in the present disclosure includes: a light-emitting element; a light-transmissive member that covers the light-emitting element; and light-diffusing particles contained in the light-emitting element. The light-diffusing particles are hollow and have a particle size not smaller than 50 μm. The light-transmissive member has a surface having irregularities associated with the light-diffusing particles.
A method for manufacturing a light-emitting device according to certain embodiments in the present disclosure includes steps of: mounting a light-emitting element in a recess of a base member; injecting a silicone resin containing light-diffusing particles into the recess, the light-diffusing particles having a particle size not smaller than 50 μm; causing the light-diffusing particles to float up to a surface of the injected silicone resin; and curing the injected silicone resin.
A more complete appreciation of embodiments of the invention and many of the attendant advantages thereof will be readily obtained by reference to the following detailed description when considered in connection with the accompanying drawings.
Hereinafter, a description will be given of a light-emitting device and a method for manufacturing the light-emitting device according to an embodiment. Drawings referenced in the following description schematically shows embodiments. Thus, scales of members, distances between members, and positional relation between members or the like may have been presented in an exaggerated manner, and illustration of a portion of a member may have been omitted. Furthermore, the scale and distances between members may not match between a plan view and its corresponding cross-sectional view. In the following description, members that are the same or analogous will be given the same name or number in principle, and duplicative descriptions will be appropriately omitted. It should be noted that tackiness means adhesiveness.
Light-Emitting Device
First, a description will be given of a light-emitting device 100 according to the present embodiment with reference to
The light-emitting device 100 includes a base member 2, a light-emitting element 1 disposed on the base member 2, and a light-transmissive member 3 containing a light-diffusing material 4 and covering the light-emitting element 1. The light-emitting element 1 is mounted on a base member 2. The light-diffusing material 4 is in the form of hollow particles having a particle size not smaller than 50 μm. The light-transmissive member 3 has a surface having irregularities associated with the light-diffusing material 4.
The light-emitting element 1 is mounted on the base member 2 by, for example, wire bonding with gold wires, or flip chip bonding with solder or silver paste. A single or a plurality of light-emitting elements 1 may be mounted on the base member 2. A known light-emitting element can be used as the light-emitting element 1. For example, a light-emitting diode or a laser diode may be preferably used. The base member 2 has a recess 23a and includes wiring 5 (wiring members 5a and 5b) exposed at a bottom surface 23b of the recess 23a. The light-emitting element 1 is electrically connected to the wiring members 5a and 5b and emits light having wavelengths in a wavelength range from ultraviolet to red. To emit blue or green light, a nitride-based semiconductor (InXAlYGa1-X-YN, 0≤X, 0≤Y, X+Y≤1) or GaP or the like may be used in the light-emitting element 1. To emit red light, in addition to a nitride-based semiconductor, GaAlAs or AlInGaP or the like may be used in the light-emitting element 1. The light-emitting element 1 may have a polygonal shape, such as square, rectangular, triangular, or hexagonal, or a round shape such as circular or oval, in plan view.
At least one light-emitting element 1 is mounted on the base member 2. The base member 2 allows the light-emitting device 100 to be electrically connected to external circuitry. The base member 2 includes: a support member having a flat-plate shape; and the wiring members 5a and 5b disposed on a surface of the support member or disposed on the surface of the support member and partially embedded therein. The base member 2 has a substantially square external shape in plan view, and has an inner wall defining an inner surface of the recess 23a and having a substantially square shape in plan view. The inner surface of the recess 23a is inclined such that the recess 23a has an upwardly increasing width. The inner surface efficiently guides light from the light-emitting element 1 upward, by reflecting the light in an upward direction, i.e., light-extracting direction, in accordance with the inclination of the inner surface. The base member 2 may include at a lower surface thereof a heat dissipation terminal electrically independent of the light-emitting element 1. Preferably, the heat dissipation terminal has an area greater than the sum of the areas of the upper surfaces of all the light-emitting element(s) 1 included in the light-emitting device 100, and is disposed so as to overlap a region directly below the light-emitting element(s) 1. With such an arrangement of the heat dissipation terminal, the light-emitting device 100 has good heat dissipation properties.
Preferably, the support member of the base member 2 is made of an insulative material, which is preferably less-transmissive to light emitted from the light-emitting element 1 and outside light or the like. Preferably, the support member of the base member 2 is made of a material having a predetermined strength. Specifically, examples of the material for the support member include: ceramic materials such as alumina, aluminum nitride, mullite and the like, and resin materials such as phenolic resins, epoxy resins, polyimide resins, bismaleimide-triazine resins (BT resins), polyphthalamides (PPA), polyamides (PA), and unsaturated polyesters.
The wiring members 5a and 5b correspond to positive and negative polarities. The wiring members 5a and 5b are supported by the support member of the base member 2, and are disposed such that the wiring members 5a and 5b are spaced apart from each other and the upper surfaces of the wiring members 5a and 5b are exposed at the bottom surface 23b of the recess 23a. The wiring members 5a and 5b are, for example, each constituted by a metal plate, which may have a uniform thickness or may have a partially thick or thin portion. Preferably, the wiring members 5a and 5b are made of a material having a large thermal conductivity, a material having a large mechanical strength, and/or a material easy to punch or etch. Examples of such a material include metals such as copper, aluminum, gold, silver, tungsten, iron, and nickel and alloys such as iron-nickel alloys, alloys of phosphor bronze and the like. The wiring members 5a and 5b can be formed by, for example, electroplating, electroless plating, vapor deposition, or sputtering.
The light-transmissive member 3 is disposed in the recess 23a to cover the light-emitting element 1. The light-transmissive member 3 contains the light-diffusing material 4 and has a surface with irregularities associated with the light-diffusing material 4. Comparing a surface with irregularities and a surface without irregularities, i.e., a flat surface, the former has a smaller contact area than the latter. Therefore, the surface of the light-transmissive member 3 is less tacky by having irregularities at the surface. Preferably, the irregularities are formed across over the entire area of the surface of the light-transmissive member 3, but may be formed in a partial region of the surface. Preferably, the irregularities formed on the surface of the light-transmissive member 3 have predetermined roughness. A rough surface with irregularities can be formed on the light-transmissive member 3 when a light-diffusing material 4 is added to the light-transmissive member 3. Preferably, the surface of the light-transmissive member 3 has a surface roughness of 0.3 μm to 0.6 μm, as a numerical measure of the irregularities of the surface. The light-transmissive member 3 having a surface roughness of that range reduces the tackiness and increases the luminous flux. Note that, herein, the surface of the light-transmissive member 3 basically refers to a surface opposite the bottom surface 23b of the recess 23a, i.e., an upper surface of the light-transmissive member 3, but may include a portion of a lateral surface of the light-transmissive member 3 which is contiguous to the upper surface.
As shown in
Preferably, the light-transmissive member 3 is made of a material having good light-transmissivity, such as a thermosetting resin or a thermoplastic resin. Examples of the thermosetting resin include: silicone resins, modified silicone resins, silicone hybrid resins, epoxy resins, modified epoxy resins, urea resins, diallyl phthalate resins, phenolic resins, unsaturated polyester resins, and hybrid resins containing at least one type of the foregoing resins. In particular, silicone resins, modified silicone resins, and silicone hybrid resins are preferable due to their good resistance to heat and light. The light transmittance of the light-transmissive member 3 is preferably 50% or more, more preferably 70% or more, or still more preferably 85% or more.
The light-diffusing material 4 is in the form of hollow microparticles. In
The bulk density (or specific gravity) of the light-diffusing material 4 with respect to the light-transmissive member 3 is preferably 0.1 g/cm3 to 0.7 g/cm3, and more preferably 0.1 g/cm3 to 0.2 g/cm3. The smaller the bulk density of the light-diffusing material 4 with respect to the light-transmissive member 3, the more likely the light-diffusing material 4 floats up. If the light-diffusing material 4 has too small bulk density, the light-diffusing material 4 may float up while being dispersed into the light-transmissive member 3 or may be unevenly distributed in a dispenser. These sorts of problems may impair workability. Accordingly, configuring the light-diffusing material 4 to have a bulk density within the above-described range allows the light-diffusing material 4 to float up to the surface of the light-transmissive member 3 after having been dispersed in the light-transmissive member 3, thus facilitating forming irregularities on the surface of the light-transmissive member 3.
Preferably, the particles of the light-diffusing material 4 have a spherical shape. The particles of the light-diffusing material 4 having a spherical shape facilitate forming uniformly distributed irregularities on the surface of the light-transmissive member 3. The light-diffusing material 4 may be hollow white microparticles or transparent hollow microparticles that are seen as white due to diffusion caused by a difference in the refractive indices between the surrounding material and the light-diffusing material 4. The light-diffusing material 4 causes light emitted by the light-emitting element 1 to diffuse and thereby improves the light extraction efficiency of the light-emitting device 100. Therefore, the light-diffusing material 4 is preferably made of a material having a refractive index largely different from that of the light-transmissive member 3. The material for the light-diffusing material 4 may, for example, be fine powder (hollow filler) containing hollow silica particles, hollow glass particles, hollow ceramic particles, fly ash particles, shirasu balloons, hollow polymer particles, porous silica particles, porous polymer particles, or the like. The light-diffusing material 4 may be fine powder (hollow filler) made of a mixture of these materials. For example, use of a mixture of a light-transmissive member 3 made of a silicone resin having a refractive index of 1.50 to 1.55 and a light-diffusing material 4 made of hollow silica particles having a refractive index of 1.35 to 1.45 may increase the efficiency of extracting light from the light-emitting element 1 and the like to the outside.
The amount of the light-diffusing material 4 added to the light-transmissive member 3 is preferably 0.2 parts to 3 parts, or more preferably 0.2 parts to 1.5 parts, with respect to the amount of the light-transmissive member 3. A more additive amount of light-diffusing material 4 can decrease the tackiness of the light-transmissive member 3. An excessive amount of light-diffusing material 4, however, may cause problems such as: a decrease in the luminous intensity of the light-emitting device due to a decrease in the transmissivity; and a decrease in the workability due to an increase in the tackiness of the light-transmissive member 3. The above-described amount of light-diffusing material 4 added to the light-transmissive member 3 can create moderate irregularities on the surface of the light-transmissive member 3 and thereby decrease the tackiness thereof without causing a decrease in the luminous intensity of the light-emitting device. Note the unit “part” of the additive amount of the light-diffusing material 4 corresponds to the weight of the light-diffusing material 4 with respect to a 100 g of the light-transmissive member 3. For example, 50 parts of additive amount of the light-diffusing material 4 means that a 50 g of the light-diffusing material 4 is added to a 100 g of the light-transmissive member 3.
In the light-emitting device 100 according to the present embodiment, the light-diffusing material 4, which is originally added to the light-transmissive member 3 for the purpose of controlling light distribution, is utilized to create irregularities on the surface of the light-transmissive member 3 by appropriately selecting the particle size, bulk density, and amount of the light-diffusing material 4 added to the light-transmissive member 3. In this way, the tackiness of the light-transmissive member 3 of the light-emitting device 100 is reduced. In addition, in the light-emitting device 100, the surface of the light-transmissive member 3 on which irregularities are formed provides a light-emitting plane with uniform color due to effective diffusion by the irregularities.
Light-Emitting Device Manufacturing Method
Next, a description will be given of a method for manufacturing the light-emitting device according to the present embodiment with reference to
As illustrated in
As shown in
As illustrated in
As shown in
As illustrated in
Carrying out the above-described steps produces the light-emitting device 100.
It should be noted that, the above description is given as to one light-emitting device 100. In practice, a plurality of the light-emitting devices 100 are formed on a contiguous series of the base members 2 and then they are singulated into individual light-emitting devices 100.
In the method for manufacturing a light-emitting device according to the present embodiment, the light-diffusing material 4 is made to float up to near the surface of the silicone resin to form irregularities associated with the light-diffusing material 4, by selecting the particle size, bulk density, and additive amount of the light-diffusing material 4. In this way, the method produces a light-emitting device with silicone resin having reduced tackiness. It should be noted that, according to the method, as at least a portion of each particle of the light-diffusing material 4 is embedded in the silicone resin, the light-diffusing material 4 is unlikely to detach from the light-emitting device due to an impact or the like.
The method for manufacturing a light-emitting device according to the present embodiment offers simplified, reduced number of steps compared to a conventional method that attempts to reduce tackiness by, for example, hard coating a low-viscosity, elastic material or spraying a coating material for demolding on a surface of cured resin. In addition, the method for manufacturing a light-emitting device according to the present embodiment forms irregularities on a surface of a silicone resin into which the light-diffusing material has been integrated. This allows reducing the tackiness of the silicone resin while minimizing occurrences of problems such as a low light extraction efficiency due to an interface formed between a coating layer and a resin layer.
The light-transmissive member 3 of a light-emitting device according to the present embodiment may contain a phosphor in addition to the light-diffusing material 4. Hereinafter, a description will be given of a light-emitting device 100A, which is another light-emitting device according to the present embodiment, with reference to
Phosphor
The phosphor 6 only has to absorb light from the light-emitting element 1 and thereby emit light having a different wavelength. Examples of the phosphor 6 include: a cerium-activated yttrium-aluminum-garnet-based fluorescent material (YAG:Ce); a cerium-activated lutetium-aluminum-garnet-based fluorescent material (LAG:Ce); an europium- and/or chromium-activated nitrogen-containing calcium-aluminosilicate-based fluorescent material (CaO—Al2O3—SiO2:Eu,Cr); an europium-activated silicate-based fluorescent material ((Sr,Ba)2SiO4:Eu); a nitride-based fluorescent material such as a β-sialon fluorescent material, a CASN-based fluorescent material (CaAlSiN3:Eu), a SCASN-based fluorescent material ((Sr,Ca)AlSiN3:Eu); a KSF-based fluorescent material (K2SiF6:Mn); and a sulfide-based fluorescent material. With the phosphor 6, the light-emitting device 100A can emit a mixture of first light and second light both having a visible wavelength, e.g., white light, or emit second light having a visible wavelength produced by excitation of the phosphor 6 with first light having an ultraviolet wavelength. The phosphor 6 may be a combination of a plurality types of phosphors. The color rendering properties and/or the color reproducibility can be controlled by combining phosphors with a ratio depending on the desired color tone. Preferably, the phosphor 6 has a higher particle number density in a portion of the light-transmissive member 3A near the light-emitting element 1 than in a portion of the light-transmissive member 3A near the upper surface thereof. By increasing the particle number density of the phosphor 6 in a portion of the light-transmissive member 3A near the light-emitting element 1, the wavelength conversion efficiency is increased and thus the amount of the phosphor 6 necessary for achieving desired chromaticity can be reduced.
The phosphor 6 and the light-transmissive member 3A preferably have a specific gravity difference of 0.5 g/cm3 to 10 g/cm3, or more preferably 1 g/cm3 to 6 g/cm3. The phosphor 6 is dispersed in the light-transmissive member 3A. Then, the light-transmissive member 3A is filled into the recess 23a of the base member 2. The phosphor 6 then settles down in the light-transmissive member 3A. By selecting the specific gravity of the phosphor 6 within the above-described range, the phosphor 6 is well dispersed and settles down in a short time. This increases the particle number density of the phosphor 6 in a portion of the light-transmissive member 3A near the light-emitting element 1 and thus increases the wavelength conversion efficiency.
A description will be given of relationship between the settling down of the phosphor 6 and the floating up of the light-diffusing material (hollow filler) 4, with reference to
The light-transmissive member 3A has a specific gravity of 1.1 g/cm3 to 1.5 g/cm3. The phosphor 6 and the light-transmissive member 3A preferably have a specific gravity difference of 0.5 g/cm3 to 10 g/cm3, or more preferably 1 g/cm3 to 6 g/cm3. In addition, the light-diffusing material 4 has a bulk density (or specific gravity) of 0.1 g/cm3 to 0.7 g/cm3, or more preferably 0.1 g/cm3 to 0.2 g/cm3, with respect to the light-transmissive member 3A. Preferably, the particle number density of the light-diffusing material 4 on the surface of the light-transmissive member 3A is higher than the particle number density of the phosphor 6 on the surface of the light-transmissive member 3A.
Hereinafter, a description will be given of examples of the light-emitting device according to the present disclosure. It should be noted that the light-emitting device according to the present disclosure is not limited to the examples described below.
Light-emitting devices 100 were fabricated in accordance with the method for manufacturing a light-emitting device according to the above-described embodiment. The light-emitting device 100 of Example 1 was fabricated such that the amount of the light-diffusing material 4 added to the light-transmissive member 3 was 0.2 parts with respect to the amount of the light-transmissive member 3. The light-emitting device 100 of Example 2 was fabricated such that the amount of the light-diffusing material 4 added to the light-transmissive member 3 was 1.5 parts with respect to the amount of the light-transmissive member 3.
Details of Examples 1 and 2 were as follows:
Light-Emitting Element 1
Number of pieces: 1
Type: Emits blue light having an emission peak wavelength of 455 nm
External dimensions in plan view: 0.65 mm square
Height: 200 μm
Base member 2
Material: Epoxy resin; product number: LUEL-300ME
Outer dimensions in plan view: 3.0 mm square
Inner dimensions in plan view: 2.6 mm square
Height: 0.7 mm
Shape: Substantially cuboid
Light-Transmissive Member 3
Material: Methyl silicone resin (manufactured by DOW CORNING TORAY (TM); product name: OE-6351)
External dimensions in plan view: 2.6 mm square
Thickness: 41 μm
Curing condition: 12 hrs at 40° C.+4 hrs at 150° C.
Light-Diffusing Material 4
Type: Hollow filler
Average particle size: 65 μm
Specific gravity: 0.13
Shape: Sphere
We fabricated light-emitting devices of Comparative Examples 1 and 2 for comparison with the light-emitting devices of Examples 1 and 2. The light-emitting device of Comparative Example 1 was fabricated such that the amount of the light-diffusing material added to the light-transmissive member was 0.1 parts with respect to the amount of the light-transmissive member. The light-emitting device of Comparative Example 2 was fabricated such that no light-diffusing material was added to the light-transmissive member. The light-emitting devices of Comparative Examples 1 and 2 were fabricated in the same manner as Example 1, except the amount of the light-diffusing material added to the light-transmissive member. Other details of constituent elements of the Comparative Examples 1 and 2 are the same as those described above for Examples 1 and 2. Incidentally, as the light-emitting device of Comparative Example 2 has the light-transmissive member to which no light-diffusing material has been added, the particle size of Comparative Example 2 indicated in the later-presented Table 1 is left blank.
The following experiments were conducted on the light-emitting devices of Examples 1 and 2 and Comparative Examples 1 and 2.
Sticking Test
For each of the light-emitting devices of Examples 1 and 2 and Comparative Examples 1 and 2, the following steps were performed in order: putting a plurality of the light-emitting devices in an IC pack; putting the IC pack in a cylindrical vessel to be rotated on a ball mill; eliminating static electricity of the plurality of the light emitting elements; rotating the cylindrical vessel on the ball mil, the cylindrical vessel storing the IC pack containing the plurality of the light-emitting devices whose static electricity has been removed; taking out the IC pack from the cylindrical vessel; taking out the plurality of the light-emitting devices from the IC pack; and counting the number of light-emitting devices sticking to each other.
Static electricity elimination: Two minutes
Rotation by ball mill: Five minutes
Measurement of Emission Flux
The light-emitting devices of Examples 1 and 2 and Comparative Examples 1 and 2 were measured as to their emission flux, using a spectrometer.
Rolling Ball Tack Test
A ball was rolled on an inclined resin plate, and a distance (stopping distance) from the location where the ball started rolling to the location where the ball stopped was measured. The stopping distance is small for a resin plate with great tackiness, and is large for a resin plate with small tackiness. Thus, measured stopping distances were used to determine the tackiness of resin plates. The resin plates were respectively formed in the same manner as the materials of the light-transmissive members of Examples 1 and 2 and Comparative Examples 1 and 2.
Material of ball: Polyamide 66 (PA66)
Inclination angle of resin plates: 5°
Run-up distance: 2 cm
Size of resin plate: 140 mm×70 mm×3 mm
Table 1 indicates results of evaluations. Table 1 shows the additive amount [phr (part)], particle size [μm], specific gravity [g/cm3], occurrence rate of sticking [%], emission flux [W] of each of the light-emitting devices of Examples 1 and 2 and Comparative Examples 1 and 2. The occurrence rate of sticking is a number obtained by: dividing the number of light-emitting devices sticking to another light emitting device when they are taken out from the IC pack by the total number of the light-emitting devices; and multiplying the result of the division by 100. Note that the number of light-emitting devices sticking to another light emitting device indicates the number of light-emitting devices that are sticking to another light-emitting device immediately after rotating the cylindrical vessel by the ball mill, and includes the number of light-emitting devices that have separated as time elapses. The emission flux is a value of emission energy passing through a predetermined plane per unit time.
The result shows that the occurrence rate of sticking was 80% or less in Examples 1 and 2, and 90% or more in Comparative Examples 1 and 2. In particular, the occurrence rate of sticking was 0% in Example 2. Although there was no significant difference in the emission flux between Examples 1 and 2 and Comparative Examples 1 and 2, the emission flux of Example 1 was greater than that of Comparative Example 2.
These result shows that it is possible to reduce the tackiness of the light-emitting device by adding 0.2 parts or more of light-diffusing material having a particle size of 50 μm or more to the silicone resin of the light-emitting device. It also shows that adding 1.5 parts of light-diffusing material to the silicone resin can completely eliminate the tackiness of the light-emitting device. It is preferable that the bulk density of the light-diffusing material with respect to the silicone resin be a value in the range from 0.1 g/cm3 to 0.2 g/cm3. It should be noted that the irregularities of the surface of the light-transmissive member 3 had a surface roughness Ra of 0.37 μm when using the light-diffusing material 4 having a particle size effective to reduction of the tackiness. In view of this, taking into consideration the effectiveness for reduction of the tackiness and the buoyancy of the light-diffusing material 4, the surface roughness of the light-transmissive member 3 is preferably 0.3 μm to 0.6 μm.
It further shows that the light-emitting device in which 0.2 parts of light-diffusing material is added to the silicone resin has an improved light extraction efficiency compared to the light-emitting device in which no light-diffusing material has been added to the silicone resin. It also shows that the light extraction efficiency of a light-emitting device can be substantially maintained even when up to 1.5 parts of light-diffusing material has been added to the silicone resin. It also shows that, the amount of the light-diffusing material added to the silicone resin is preferably from 0.2 parts to 1.5 parts with respect to the amount of the silicone resin.
In
According to the measurement result, the stopping distance was 14 cm or larger in Examples 1 and 2; 8.8 cm in Comparative Example 1; and 3.8 cm in Comparative Example 2. That is, the stopping distances of Examples 1 and 2 were greater than the value of transportability threshold line, whereas the stopping distances of Comparative Examples 1 and 2 were smaller than the value of the transportability threshold line. The occurrence rate of sticking of Example 1 was 80% in Example 1; 0% in Example 2; 90% in Comparative Example 1; and 98% Comparative Example 2. Thus, the occurrence rates of sticking of Examples 1 and 2 were smaller than the value of transportability threshold line, whereas the occurrence rates of sticking of Comparative Examples 1 and 2 were greater than the value of transportability line.
This result shows that it is possible to reduce the tackiness of the light-emitting device by adding 0.2 parts or more of light-diffusing material having a particle size of 50 μm to the silicone resin of the light-emitting device, and suggests that delays or the like of operations due to the tackiness of the silicone resin would not occur. It also shows that the more the additive amount of the light-diffusing material, the more the tackiness of the light-emitting device can be reduced. It further shows that the particle size of the light-diffusing material is preferably from 65 μm to 70 μm.
As Example 3, we fabricated a light-emitting device in accordance with the method for manufacturing the another light-emitting device according to the present embodiment. In the light-emitting device of Example 3, 3 parts of light-diffusing material was added to a 100 parts of the light-transmissive member, and phosphor was further added to the light-transmissive member so as to obtain light having a color temperature of 5000K, which corresponds to chromaticity coordinates of (0.347, 0.371). The light-emitting device of Example 3 was fabricated in the same manner as Example 1 except the additive amount of the light-diffusing material and the addition of the phosphor to the light-transmissive member.
In the light-emitting device of Comparative Example 3, the light-transmissive member was not added with any light-diffusing material but added with a phosphor so as to obtain light having a color temperature of 5000K, which corresponds to chromaticity coordinates of (0.347, 0.371). The light-emitting device of Comparative Example 3 was fabricated in the same manner as Example 1 except the addition of the phosphor to the light-transmissive member.
The following experiment was conducted on the light-emitting devices of Example 3 and Comparative Example 3.
The non-self-luminous colors of the light-emitting devices of Example 3 and Comparative Example 3 were measured using a high speed colorimetric spectrophotometer (manufactured by MURAKAMI COLOR RESEARCH LABORATORY CO., Ltd; product name: CMS-35PS).
The chromaticity coordinates of the non-self-luminous color of the light-emitting device of Example 3 was (0.356, 0.361), whereas the chromaticity coordinates of the non-self-luminous color of the light-emitting device of Comparative Example 3 was (0.456, 0.489). That is, as to the light-emitting device of Comparative Example 3, the emission color was white, whereas the non-self-luminous color was yellow. The yellow color of the latter is the color of the phosphor itself. In contrast, both the emission color and the non-self-luminous color of the light-emitting device of Example 3 were white.
That is, comparing the light-emitting device in which the light-diffusing material has been added to the light-transmissive member and the light-emitting device in which the light-diffusing material has not been added to the light-transmissive member, they differ from each other in the color of their appearances despite of their same emission color. This is because of the diffusion of light by the irregularities associated with the light-diffusing material formed on the surface of the light-transmissive member and having a particle size not smaller than 50 μm.
It should be noted that, in the light-emitting device in which the light-diffusing material has not been added to the light-transmissive member, portions of the light-transmissive member where phosphor is present are seen as having a noticeable dark color. In contrast, in the light-emitting device in which the light-diffusing material has been added to the light-transmissive member, the emission plane was whitened such that portions of the light-transmissive member where phosphor is present are not noticeable. This means the irregularities formed on the surface of the light-transmissive member whitens the appearance of the light-emitting device, so that the emission plane presents a uniform color.
The embodiments for carrying out the invention have been specifically described. It should be noted, however, that the spirit of the present invention is not limited thereto and should be construed broadly based on the scope of claims. It goes without saying that the spirit of the present invention also includes variations and modifications based on the foregoing descriptions. It also should be noted that the light-diffusing material 4 described in the embodiments generally takes the form of hollow filler, micropowder, or microparticles.
The light-emitting devices of the embodiments according to the present disclosure are applicable to lighting devices, backlights of liquid crystal panels and the like.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2017-114961 | Jun 2017 | JP | national |
| 2018-071079 | Apr 2018 | JP | national |