The present invention relates to a current-light conversion device, such as an organic light-emitting device (OLED) or an organic photovoltaic device (OPVD). The present invention relates further to a fabrication apparatus and a fabrication method for fabricating the current-light conversion device.
OLEDs are known to be extremely sensitive to moisture and oxygen, with major degradation effects occurring due to metal delamination, recrystallization of organic materials, reactions in metal and organic interfaces, and the like. An effective encapsulation to prevent the ingression of water and oxygen into the device is therefore required to achieve adequate lifetimes.
An established method for protecting non-flexible OLEDs is to make use of a conventional glass packaging with a material known as a “getter”, which easily absorbs water and can hold a large volume of it, provided on the edge of the package outside the active OLED area. This rigid approach, however, does not work for flexible OLEDs, which are provided on flexible substrates made from polymers, such as plastic, metal foils, ultrathin glass, or the like. In this case, a thin-film encapsulation (TFE) comprising (a) transparent barrier layer(s) is typically used in place of the rigid glass packaging to effectively isolate the device from moisture and oxygen.
A problem with known transparent barrier layers for TFE is that they generally have inferior barrier properties to water and oxygen ingression compared to a conventional glass packaging. In some proposals, getter particles, for instance, calcium oxide (CaO), are dispersed in the transparent barrier layer. This, however, has the disadvantage that the transparent barrier layer will scatter light due to the presence of the dispersed getter particles. This scattering is also in some cases undesired if a top-emitting device provided on a non-flexible glass substrate is fabricated.
It is an object of the present invention to provide a current-light conversion device comprising a barrier layer, wherein the barrier layer has improved transparency characteristics while providing the desired getter functionality. It is a further object of the present invention to provide a fabrication apparatus and a fabrication method for fabricating the current-light conversion device.
In a first aspect of the present invention, a current-light conversion device is presented, wherein the current-light conversion device comprises:
Since the getter material is provided in a pattern of getter dots, the light scattering effect resulting from dispersed getter particles can be avoided, resulting in improved transparency characteristics of the barrier layer while still providing the desired getter functionality. Moreover, since the getter material is provided in the transparent organic layer, that is, between the first and the second transparent inorganic barrier layer, an easier manufacture may be achieved compared to a case, where the getter material is provided directly on an electrode layer, in particular, a cathode layer, because the getter material may be reactive towards the material of the cathode layer.
The current-light conversion material can be adapted to convert a current into light or, the other way around, light into a current. In the first case, the current-light conversion device can be, for instance, an OLED, and in the second case, the current-light conversion device can be, for instance, an OPVD. In both the first and the second case, the current-light conversion material comprises an organic current-light conversion material. In other cases, however, it is also possible that the current-light conversion material comprises an inorganic current-light conversion material. Moreover, it is possible that the current-light conversion material comprises multiple organic and/or inorganic materials or combinations thereof. For instance, in some cases, the current-light conversion material may comprise a perovskite (e.g., CH3NH3PbI3).
The first electrode layer may be a transparent conductive anode layer, in particular, an indium tin oxide (ITO) anode layer, and the second electrode layer may a transparent conductive cathode layer, made, for instance, from silver (Ag). If the current-light conversion device is, for instance, an OLED, when an electrical voltage is applied to the transparent conductive anode layer and the transparent conductive cathode layer, electrons and holes are injected into the organic current-light conversion material. When these recombine, light is emitted.
The transparent organic layer can be, for instance, a transparent polymer layer, and the first and the second transparent inorganic barrier layer can be made, for instance, from silicon nitride (SiN). Alternatively, a transparent inorganic barrier layer can also comprise a stack of inorganic layers, for instance, an SiN—SiON—SiN layer stack. The transparent organic layer has a function to ensure that pinholes in the two transparent inorganic barrier layers, which could let small traces of water into the current-light conversion device, do not join up.
It is also preferred that the first transparent inorganic barrier layer is provided closer to the substrate than the second transparent inorganic barrier layer, wherein the transparent organic layer comprises a transparent organic underlayer provided between the first transparent inorganic barrier layer and the getter dots. The transparent organic underlayer can provide an advantage during fabrication of the current-light conversion device, for instance, it can function as a transparent organic protection layer for mechanically protecting the first transparent inorganic barrier layer if the getter dots are provided through a screen mask, such as by means of physical vapor deposition (PVD) or sputtering or by means of screen printing (see below), or it can function as a transparent organic printing improvement layer for improving the printing of the getter dots if the getter dots are printed by means of inkjet printing (see below).
It is preferred that the first transparent inorganic barrier layer is provided closer to the substrate than the second transparent inorganic barrier layer, wherein the transparent organic layer comprises a transparent organic planarization layer that embeds the getter dots and forms a planar surface at a side opposite the first transparent inorganic barrier layer. This has the advantage that the transparent organic planarization layer provides a smooth surface, such that the subsequent layer, in particular, the second transparent inorganic barrier layer can be of higher quality.
It is preferred that the barrier layer comprises a further transparent organic layer provided between the first and the second transparent inorganic barrier layer, wherein the getter material is also provided in the further transparent organic layer in a pattern of getter dots, wherein a further transparent inorganic barrier layer is provided between the transparent organic layer and the further transparent organic layer. With this arrangement, the barrier properties of the barrier layer to water and oxygen ingression can be further improved by means of the further transparent inorganic barrier layer, which can also be made, for instance, from silicon nitride (SiN), or can comprise a stack of inorganic layers, for instance, an SiN—SiON—SiN layer stack. In addition, this arrangement can allow to provide more getter material without substantially increasing the fill factor of the getter dots.
It is further preferred that the getter dots have a fill factor of less than 20%, preferably less than 10%, most preferred less than 5%. The fill factor characterizes the density of the pattern of getter dots; it is defined as the ratio between the area covered by the getter dots and the total area. By means of the preferred fill factors, a sufficient transparency of the barrier layer can be achieved while still providing the desired getter functionality.
It is preferred that the height of the getter dots ranges from 10 nm to 20 μm and/or that the size of the getter dots ranges from 5 μm to 200 μm. For instance, if the getter dots are provided by means of a physical vapor deposition (PVD), the height of the getter dots may be rather limited, preferably, they may range from 10 μm to 500 nm, more preferred from 200 nm to 400 nm, most preferred 300 nm, due to the increased fabrication costs resulting from longer deposition times. In contrast, if the getter dots are provided by means of screen printing or inkjet printing, larger heights can be achieved more easily. In this case, they height of the getter dots may preferably range from 5 μm to 20 μm, more preferred 8 μm to 15 μm, most preferred, 10 μm to 12 μm.
It is preferred that the barrier layer is provided at a side of the current light-conversion arrangement opposite the substrate. This can preferably be used to fabricate top-emitting current-light conversion devices, wherein the barrier layer protects the current-light conversion device, in particular, the current-light conversion arrangement, from the ingression of water and oxygen from the top side.
Additionally or alternatively, it is preferred that the barrier layer is provided between the substrate and the current light-conversion arrangement. Providing the barrier layer (also) between the substrate and the current light-conversion arrangement is particularly advantageous if the substrate is, for instance, a transparent polymer (plastic) substrate, which has an inferior barrier property to water and oxygen ingression compared to, for instance, a glass substrate. Therewith, bottom-emitting current-light conversion devices can be realized, wherein the barrier layer protects the current-light conversion device, in particular, the current-light conversion arrangement, from the ingression of water and oxygen from the bottom side.
A configuration where a barrier layer is provided both at the side of the current light-conversion arrangement opposite the substrate and between the substrate and the current light-conversion arrangement, can preferably be used for fabricating flexible fully transparent current-light conversion devices, wherein the barrier layers protect the current-light conversion device, in particular, the current-light conversion arrangement, from the ingression of water and oxygen from both the top side and the bottom side.
It is further preferred that the current-light conversion arrangement forms a structure with light-emitting regions and non-light-emitting regions of the current-light conversion material, wherein the barrier layer forms a mirror layer with non-transparent regions aligned to the light-emitting regions of the current-light conversion material and transparent regions aligned to the non-light-emitting regions of the current-light conversion material, wherein the non-transparent regions are formed by the getter dots. According to this arrangement, the current-light conversion device may at the same time be transparent (where the transparent regions are aligned with the non-light-emitting regions) and have a primary or even single direction of light emission (where the non-transparent regions block the light emission of their associated, aligned light-emitting regions). This is described in more detail in the published international patent application WO 2010/046833 A1 (“Transparent OLED Device”), the contents of which are incorporated herein by reference. Since the non-transparent regions, here, are formed by the getter dots, an additional getter functionality is achieved in a simple and efficient manner.
In a further aspect of the present invention, a fabrication apparatus for fabricating a current-light conversion device as defined in claim 1 is presented, wherein the fabrication apparatus comprises:
It is preferred that the barrier layer providing unit comprises:
Providing the getter dots through a screen mask, such as by means of physical vapor deposition (PVD) or sputtering or by means of screen printing, allows the getter dots to be provided in a simple manner. Moreover, by providing the transparent organic underlayer, a function of a transparent organic protection layer for protecting the first transparent inorganic barrier layer may be realized, such that damages, scratches and the like, which may occur on/in the first transparent inorganic barrier layer as a result of the use of the screen mask, may fully or partially be avoided.
As the getter material, a mixture of about 10% CaO dispersed in the same material that is used for the transparent organic layer is preferably used. However, other getter materials, such as barium oxide (BaO), calcium (Ca), certain salts and the like may also be employed.
Preferably, the barrier layer providing unit comprises:
The transparent organic planarization layer provides a smooth surface, such that the subsequent layer, in particular, the second transparent inorganic barrier layer can be of higher quality.
In an alternative, it is preferred that the barrier layer providing unit comprises:
Making use of inkjet printing allows the getter dots to be provided in a simple manner. Moreover, by providing the transparent organic underlayer and by processing the transparent organic underlayer to make it more hydrophobic, that is, to reduce the ability of wetting of the transparent organic underlayer, a function as a transparent organic printing improvement layer for improving the printing of the getter dots can be realized, such that a tendency of the getter material to flow apart, which may result in an undesired increase of the size of the getter dots and/or a loss of the form thereof, may be reduced.
The first processing unit may comprise suitable means for generating a plasma, for instance, a tetrafluoromethane (CF4) plasma with about 5% of oxygen (O2), wherein the transparent organic underlayer is made more hydrophobic by processing it with the CF4 plasma. Alternatively, a plasma based on, for instance, trifluoromethyl (CF3) may be used or (a) primer(s), such as hexamethyldisilazane (HMDS), trichlorophenylsilane (TCPS) and the like, may be employed.
As the getter material, a mixture of about 10% CaO dispersed in the same material that is used for the transparent organic layer is preferably used. However, other getter materials, such as barium oxide (BaO), calcium (Ca), certain salts and the like may also be employed.
Preferably, the barrier layer providing unit further comprises:
By processing the more hydrophobic transparent organic underlayer to make it more hydrophilic, the transparent organic planarization layer, which provides a smooth surface, such that the subsequent layer, in particular, the second transparent inorganic barrier layer can be of higher quality, can be provided with good quality.
The second processing unit may comprise suitable means for generating a plasma, for instance, an oxygen (O2) plasma, wherein the more hydrophobic transparent organic underlayer is made more hydrophilic by processing it with the O2 plasma. Alternatively, for instance, a UV-ozone may be employed.
It is preferred that a getter dot is printed as a stack of two or more layers of getter material. By doing so, higher getter dots having more getter capacity can be provided. This may be particularly simple due to the hydrophobic properties of the processed transparent organic underlayer (see above), which allow the getter material of the two or more layers to align itself locally.
In a further aspect of the present invention, a fabrication method for fabricating a current-light conversion device as defined in claim 1 is presented, wherein the fabrication method comprises:
It shall be understood that the current-light conversion device of claim 1, the fabrication apparatus of claim 9 and the fabrication method of claim 15 have similar and/or identical preferred embodiments, in particular, as defined in the dependent claims.
It shall be understood that a preferred embodiment of the present invention can also be any combination of the dependent claims or above embodiments with the respective independent claim.
These and other aspects of the invention will be apparent from and elucidated with reference to the embodiments described hereinafter.
In the following drawings:
In the drawings, like or corresponding reference numerals refer to like or corresponding parts and/or elements.
The OLED 1 comprises a substrate 10, in this embodiment, a glass substrate, which has a barrier property to water and oxygen ingression, and a current-light conversion arrangement 11 arranged on the glass substrate 10. The current-light conversion arrangement 11 comprises a current-light conversion material 111, here, an organic current-light conversion material, which is adapted to convert a current into light, provided between a first and a second electrode layer 110, 112. In this embodiment, the first electrode layer 110 is a transparent conductive anode layer, in particular, an indium tin oxide (ITO) anode layer, and the second electrode layer 112 is a transparent conductive cathode layer, made, for instance, from silver (Ag). When an electrical voltage is applied to the transparent conductive anode layer 110 and the transparent conductive cathode layer 112, electrons and holes are injected into the organic current-light conversion material 111. When these recombine, light is emitted.
In order to protect the OLED 1, in particular, the current-light conversion arrangement 11, from the ingression of water and oxygen, the OLED 1 further comprises a barrier layer 12 provided on the current-light conversion arrangement 11. The barrier layer 12, here, comprises a transparent organic layer 121, for instance, a transparent polymer layer, provided between a first and a second transparent inorganic barrier layer 120, 122, made from silicon nitride (SiN). The transparent organic layer 121 has a function to ensure that pinholes in the two transparent inorganic barrier layers 120, 122, which could let small traces of water into the OLED 1, do not join up.
In this embodiment, the OLED 1 further comprises a transparent topcoating 13 provided on the barrier layer 12 and a transparent protecting foil 14 provided on the transparent topcoating 13.
In order to further improve the barrier properties of the barrier layer 12 to water and oxygen ingression, a getter material is provided in the transparent organic layer 121 in a pattern of getter dots 1211.
Here, the first transparent inorganic barrier layer 120 is provided closer to the substrate 10 than the second transparent inorganic barrier layer 122. The transparent organic layer 121 comprises a transparent organic underlayer 1210 provided between the first transparent inorganic barrier layer 120 and the getter dots 1211 and a transparent organic planarization layer 1212 that embeds the getter dots 1211 and forms a planar surface at a side opposite the first transparent inorganic barrier layer 120. The transparent organic planarization layer 1212 provides a smooth surface, such that the subsequent layer, in particular, the second transparent inorganic barrier layer 122 can be of higher quality.
In this embodiment, the glass substrate 10 already provides a sufficient protection of the OLED 1, in particular, the current-light conversion arrangement 11, from the ingression of water and oxygen from the bottom side. The barrier layer 12 is therefore only provided at a side of the current light-conversion arrangement 11 opposite the glass substrate 10, such as to protect the OLED 1 from the ingression of water and oxygen from the top side, that is, through the transparent protecting foil 14 and the transparent topcoating 13.
The OLED 2 is structurally quite similar to the OLED 1 shown in
In this embodiment, the OLED 2 further comprises a transparent topcoating 23 provided on the barrier layer 22 and a transparent protecting foil 24 provided on the transparent topcoating 23.
In order to further improve the barrier properties of the barrier layer 22 to water and oxygen ingression, a getter material is provided in the transparent organic layer 221 in a pattern of getter dots 2211.
Here, the first transparent inorganic barrier layer 220 is provided closer to the substrate 20 than the second transparent inorganic barrier layer 222. The transparent organic layer 221 comprises a transparent organic underlayer 2210 provided between the first transparent inorganic barrier layer 220 and the getter dots 2211 and a transparent organic planarization layer 2212 that embeds the getter dots 2211 and forms a planar surface at a side opposite the first transparent inorganic barrier layer 220. The transparent organic planarization layer 2212 provides a smooth surface, such that the subsequent layer, in particular, the second transparent inorganic barrier layer 222 can be of higher quality.
While the OLED 2, as described so far, corresponds to the EOLD 1 shown in
The barrier layer 32 is structurally quite similar to the barrier layers 12, 22, 25. In particular, it also comprises a transparent organic layer 321, for instance, a transparent polymer layer, provided between a first and a second transparent inorganic barrier layer 320, 322, made from silicon nitride (SiN). Likewise, a getter material is provided in the transparent organic layer 321 in a pattern of getter dots 3211. In this variant, however, the barrier layer 32 comprises a further transparent organic layer 323, for instance, a further transparent polymer layer, provided between the first and the second transparent inorganic barrier layer 320, 322, and the getter material is also provided in the further transparent organic layer in a pattern of getter dots 3231. Moreover, a further transparent inorganic barrier layer 324, made from silicon nitride (SiN), is provided between the transparent organic layer 321 and the further transparent organic layer 323. With this arrangement, the barrier properties of the barrier layer 32 to water and oxygen ingression can be further improved by means of the further transparent inorganic barrier layer 324. In addition, this arrangement can allow to provide more getter material without substantially increasing the fill factor of the getter dots 3211, 3231.
The fabrication apparatus 4 comprises a substrate providing unit 41 for providing a substrate 10, here, a glass substrate, which has a barrier property to water and oxygen ingression. The fabrication apparatus 4 further comprises a current-light conversion arrangement providing unit 42 for providing a current-light conversion arrangement 11 on the glass substrate 10. The current-light conversion arrangement 11 comprises a current-light conversion material 111, here, an organic current-light conversion material, which is adapted to convert a current into light, provided between a first and a second electrode layer 110, 112 (all not shown in detail in this figure). In this embodiment, the first electrode layer 110 is a transparent conductive anode layer, in particular, an indium tin oxide (ITO) anode layer, and the second electrode layer 112 is a transparent conductive cathode layer, made, for instance, from silver (Ag). When an electrical voltage is applied to the transparent conductive anode layer 110 and the transparent conductive cathode layer 112, electrons and holes are injected into the organic current-light conversion material 111. When these recombine, light is emitted.
The fabrication apparatus 4 further comprises a barrier layer providing unit 43 for providing a barrier layer 12, here, comprising a transparent organic layer 121, for instance, a transparent polymer layer, provided between a first and a second transparent inorganic barrier layer 120, 122, made from silicon nitride (SiN). The transparent organic layer 121 has a function to ensure that pinholes in the two transparent inorganic barrier layers 120, 122, which could let small traces of water into the OLED 1, do not join up.
In this embodiment, the fabrication apparatus 4 further comprises a transparent topcoating providing unit 44 for providing a transparent topcoating 13. The fabrication apparatus 4 further comprises a transparent protecting foil providing unit 45 for providing a transparent protecting foil 14.
The fabrication apparatus 4 is adapted to provide a getter material in the transparent organic layer 121 in a pattern of getter dots 1211.
In this embodiment, the barrier layer providing unit 43 comprises a first transparent inorganic barrier layer providing unit 431 for providing the first transparent inorganic barrier layer 120. The barrier layer providing unit 43 further comprises a transparent organic underlayer providing unit 432 for providing a transparent organic underlayer 1210. The barrier layer providing unit 43 further comprises a getter dots providing unit 433 for providing the getter dots 1211 on the transparent organic underlayer 1210 through a screen mask (not shown in the figure), here, by means of screen printing. Here, a mixture of about 10% CaO dispersed in the same material that is used for the transparent organic layer 121 is preferably used as the getter material.
The barrier layer providing unit 43, here, further comprises a transparent organic planarization layer providing unit 434 for providing a transparent organic planarization layer 1212 that embeds the getter dots 1211 and forms a planar surface at a side opposite the first transparent inorganic barrier layer 120. The barrier layer providing unit 43 further comprises a second transparent inorganic barrier layer providing unit 435 for providing the second transparent inorganic barrier layer 122.
The fabrication apparatus 5 comprises a substrate providing unit 51 for providing a substrate 10, here, a glass substrate, which has a barrier property to water and oxygen ingression. The fabrication apparatus 5 further comprises a current-light conversion arrangement providing unit 52 for providing a current-light conversion arrangement 11 on the glass substrate 10. The current-light conversion arrangement 11 comprises a current-light conversion material 111, here, an organic current-light conversion material, which is adapted to convert a current into light, provided between a first and a second electrode layer 110, 112 (all not shown in detail in this figure). In this embodiment, the first electrode layer 110 is a transparent conductive anode layer, in particular, an indium tin oxide (ITO) anode layer, and the second electrode layer 112 is a transparent conductive cathode layer, made, for instance, from silver (Ag). When an electrical voltage is applied to the transparent conductive anode layer 110 and the transparent conductive cathode layer 112, electrons and holes are injected into the organic current-light conversion material 111. When these recombine, light is emitted.
The fabrication apparatus 5 further comprises a barrier layer providing unit 53 for providing a barrier layer 12, here, comprising a transparent organic layer 121, for instance, a transparent polymer layer, provided between a first and a second transparent inorganic barrier layer 120, 122, made from silicon nitride (SiN). The transparent organic layer 121 has a function to ensure that pinholes in the two transparent inorganic barrier layers 120, 122, which could let small traces of water into the OLED 1, do not join up.
In this embodiment, the fabrication apparatus 5 further comprises a transparent topcoating providing unit 54 for providing a transparent topcoating 13. The fabrication apparatus 4 further comprises a transparent protecting foil providing unit 55 for providing a transparent protecting foil 14.
The fabrication apparatus 5 is adapted to provide a getter material in the transparent organic layer 121 in a pattern of getter dots 1211.
In this embodiment, the barrier layer providing unit 53 comprises a first transparent inorganic barrier layer providing unit 531 for providing the first transparent inorganic barrier layer 120. The barrier layer providing unit 53 further comprises a transparent organic underlayer providing unit 532 for providing a transparent organic underlayer 1210. The barrier layer providing unit 53 further comprises a first processing unit for processing the transparent organic underlayer 1210 to make it more hydrophobic and a getter dots printing unit 534 for printing the getter dots 1211 on the more hydrophobic transparent organic underlayer 1210 by means of inkjet printing. In this embodiment, the first processing unit 534 comprises suitable means for generating a plasma, for instance, a tetrafluoromethane (CF4) plasma with about 5% of oxygen (O2), wherein the transparent organic underlayer 1210 is made more hydrophobic by processing it with the CF4 plasma. Here, a mixture of about 10% CaO dispersed in the same material that is used for the transparent organic layer 121 is preferably used as the getter material.
The barrier layer providing unit 53, here, further comprises a second processing unit 535 for processing the more hydrophobic transparent organic underlayer 1210 to make it more hydrophilic and a transparent organic planarization layer providing unit 536 for providing a transparent organic planarization layer 1212 that embeds the getter dots 1211 and forms a planar surface at a side opposite the first transparent inorganic barrier layer 120. In this embodiment, the second processing unit 535 comprises suitable means for generating a plasma, for instance, an oxygen (O2) plasma, wherein the more hydrophobic transparent organic underlayer 1210 is made more hydrophilic by processing it with the O2 plasma. The barrier layer providing unit 53 further comprises a second transparent inorganic barrier layer providing unit 537 for providing the second transparent inorganic barrier layer
In the following, a first embodiment of a fabrication method 6 for fabricating a current-light conversion device, here, the OLED 1 shown in
In step 61, a substrate 10, here, a glass substrate, which has a barrier property to water and oxygen ingression, is provided. In step 62, a current-light conversion arrangement 11 is provided on the glass substrate 10. The current-light conversion arrangement 11 comprises a current-light conversion material 111, here, an organic current-light conversion material, which is adapted to convert a current into light, provided between a first and a second electrode layer 110, 112 (all not shown in detail in this figure). In this embodiment, the first electrode layer 110 is a transparent conductive anode layer, in particular, an indium tin oxide (ITO) anode layer, and the second electrode layer 112 is a transparent conductive cathode layer, made, for instance, from silver (Ag). When an electrical voltage is applied to the transparent conductive anode layer 110 and the transparent conductive cathode layer 112, electrons and holes are injected into the organic current-light conversion material 111. When these recombine, light is emitted.
In step 63, a barrier layer 12, here, comprising a transparent organic layer 121, for instance, a transparent polymer layer, provided between a first and a second transparent inorganic barrier layer 120, 122, made from silicon nitride (SiN), is provided. The transparent organic layer 121 has a function to ensure that pinholes in the two transparent inorganic barrier layers 120, 122, which could let small traces of water into the OLED 1, do not join up.
In this embodiment, a transparent topcoating 13 is provided in step 64 and a transparent protecting foil 14 is provided in step 65.
The fabrication method 6 provides a getter material in the transparent organic layer 121 in a pattern of getter dots 1211. In this embodiment, the barrier layer providing step 63 comprises providing 631 the first transparent inorganic barrier layer 120. The barrier layer providing step 63 further comprises providing 632 a transparent organic underlayer 1210. The barrier layer providing step 63 further comprises providing 633 the getter dots 1211 on the transparent organic underlayer 1210 through a screen mask (not shown in the figure), here, by means of screen printing. Here, a mixture of about 10% CaO dispersed in the same material that is used for the transparent organic layer 121 is preferably used as the getter material.
The barrier layer providing step 63, here, further comprises providing 634 a transparent organic planarization layer 1212 that embeds the getter dots 1211 and forms a planar surface at a side opposite the first transparent inorganic barrier layer 120. The barrier layer providing step 63 further comprises providing 635 the second transparent inorganic barrier layer 122.
In step 71, a substrate 10, here, a glass substrate, which has a barrier property to water and oxygen ingression, is provided. In step 72, a current-light conversion arrangement 11 is provided on the glass substrate 10. The current-light conversion arrangement 11 comprises a current-light conversion material 111, here, an organic current-light conversion material, which is adapted to convert a current into light, provided between a first and a second electrode layer 110, 112 (all not shown in detail in this figure). In this embodiment, the first electrode layer 110 is a transparent conductive anode layer, in particular, an indium tin oxide (ITO) anode layer, and the second electrode layer 112 is a transparent conductive cathode layer, made, for instance, from silver (Ag). When an electrical voltage is applied to the transparent conductive anode layer 110 and the transparent conductive cathode layer 112, electrons and holes are injected into the organic current-light conversion material 111. When these recombine, light is emitted.
In step 73, a barrier layer 12, here, comprising a transparent organic layer 121, for instance, a transparent polymer layer, provided between a first and a second transparent inorganic barrier layer 120, 122, made from silicon nitride (SiN), is provided. The transparent organic layer 121 has a function to ensure that pinholes in the two transparent inorganic barrier layers 120, 122, which could let small traces of water into the OLED 1, do not join up.
In this embodiment, a transparent topcoating 13 is provided in step 74 and a transparent protecting foil 14 is provided in step 75.
The fabrication method 7 provides a getter material in the transparent organic layer 121 in a pattern of getter dots 1211.
In this embodiment, the barrier layer providing step 73 comprises providing 731 the first transparent inorganic barrier layer 120. The barrier layer providing step 73 further comprises providing 732 a transparent organic underlayer 1210. The barrier layer providing step 73 further comprises a first processing 733 of the transparent organic underlayer 1210 to make it more hydrophobic and printing 734 the getter dots 1211 on the more hydrophobic transparent organic underlayer 1210 by means of inkjet printing. In this embodiment, the first processing step 733 comprises suitably generating a plasma, for instance, a tetrafluoromethane (CF4) plasma with about 5% of oxygen (O2), wherein the transparent organic underlayer 1210 is made more hydrophobic by processing it with the CF4 plasma. Here, a mixture of about 10% CaO dispersed in the same material that is used for the transparent organic layer 121 is preferably used as the getter material.
The barrier layer providing step 73, here, further comprises a second processing 735 of the more hydrophobic transparent organic underlayer 1210 to make it more hydrophilic and providing 736 a transparent organic planarization layer 1212 that embeds the getter dots 1211 and forms a planar surface at a side opposite the first transparent inorganic barrier layer 120. In this embodiment, the second processing step 735 comprises suitable suitably generating a plasma, for instance, an oxygen (O2) plasma, wherein the more hydrophobic transparent organic underlayer 1210 is made more hydrophilic by processing it with the O2 plasma. The barrier layer providing step 73 further comprises providing the second transparent inorganic barrier layer 122.
In the first and the second embodiment of a current-light conversion device 1, 2 described with reference to
While in the first and the second embodiment of a current-light conversion device 1, 2 described with reference to
While in the first and the second embodiment of a current-light conversion device 1, 2 described with reference to
While in the first and the second embodiment of a fabrication method 6, 7 for fabricating a current-light conversion device described with reference to
The transparent organic underlayer 10, 2210, 2510, 3210, 8210 does not have to be provided in all embodiments of a current-light conversion device. For instance, if the getter dots are provided by means of a physical vapor deposition (PVD) of the getter material, preferably CaO, a mechanical protection of the first transparent inorganic barrier layer may not be necessary.
If the transparent organic layer comprises a transparent organic planarization layer, the transparent organic planarization layer may completely cover the getter dots, that is, the planar surface at the side opposite the first transparent inorganic barrier layer may completely be formed by the transparent organic planarization layer. It may, however, also be possible that the planar surface is formed by the top surfaces of the getter dots and the transparent organic planarization layer, that is, that the transparent organic planarization layer is provided up to the same height as the getter dots.
It shall be noted that in addition to the getter dots, a rim made from getter material may be provided in the transparent organic layer to surround the “active area” of the current-light conversion device. Such a getter rim can be fabricated using substantially the same methods as described above. For instance, it can be provided by means of inkjet printing.
While in the structure shown in
While the present invention has been described above with reference to embodiments in which the current-light conversion device is an organic light-emitting device (OLED), in other embodiments, the current-light conversion device can also be something else, for instance, an organic photovoltaic device (OPVD) or the like.
Other variations to the disclosed embodiments can be understood and effected by those skilled in the art in practicing the claimed invention, from a study of the drawings, the disclosure, and the appended claims.
In the claims, the word “comprising” does not exclude other elements or steps, and the indefinite article “a” or “an” does not exclude a plurality.
A single unit or device may fulfill the functions of several items recited in the claims. The mere fact that certain measures are recited in mutually different dependent claims does not indicate that a combination of these measures cannot be used to advantage.
Any reference signs in the claims should not be construed as limiting the scope.
The present invention relates to a current-light conversion device, such as an OLED or an OPVD, wherein the current-light conversion device comprises a substrate, a current-light conversion arrangement comprising a current-light conversion material provided between a first and a second electrode layer, and a barrier layer comprising a transparent organic layer provided between a first and a second transparent inorganic barrier layer. A getter material is provided in the transparent organic layer in a pattern of getter dots. Since the getter material is provided in a pattern of getter dots, the light scattering effect resulting from dispersed getter particles can be avoided, resulting in improved transparency characteristics of the barrier layer while still providing the desired getter functionality.
| Number | Date | Country | Kind |
|---|---|---|---|
| 14181891.4 | Aug 2014 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2015/068807 | 8/17/2015 | WO | 00 |