In recent years, various methods have been studied to improve luminance of AlGaInP-series light-emitting diodes (LEDs). With great breakthroughs in this area, the application of AlGaInP-series light-emitting diodes extends widely to display system, lighting system, automatic system, etc. For example, according to Chinese patent 201210341574.6, at least two Bragg reflector layers with different corresponding reflecting wavelength are provided to expand bandwidth of the reflection wavelength of LED and to improve internal quantum efficiency.
The inventors of the present disclosure have recognized that, to respond to fierce market competition, chip size is increasingly narrowed to cut cost, coming up with new performance problems. When the chip size is narrowed, for example, at 7.0 mil×7.0 mil, in conventional LED structures, the resistance to aging caused by high current is dramatically reduced, which cannot meet market requirements. Therefore, it is necessary to study and improve anti-aging performance of small-size chips driven by high current.
Various embodiments of the present disclosure provide an AlGaInP light-emitting diode to improve the resistance to aging caused by high current.
The technical scheme of the present disclosure is: an AlGaInP light-emitting diode with improving resistance to aging caused by high current includes from bottom to up a substrate, a distributed Bragg reflector (DBR) reflecting layer, an N-type semiconductor layer, a quantum well light-emitting layer, a P-type semiconductor layer, a transient layer and a P-type current spreading layer. The DBR reflecting layer is multispectral-doping. The P-type semiconductor layer includes a first P-type semiconductor layer adjacent to the quantum well light-emitting layer and a second P-type semiconductor layer adjacent to the transient layer; wherein, doping concentration of the second P-type semiconductor layer is lower than that of the first P-type semiconductor layer. By using a segmented-doping multispectral DBR reflecting layer, DBR doping concentration is improved; and by lowering concentration of the P-type semiconductor doping layer at the adjacent segmentation of the transient layer, a segmented P-type semiconductor layer with certain thickness ratio and concentration ratio is formed.
According to studies, in small-sized chip, degrading current spreading of the DBR layer is a key point to affect aging. Through segmented-doping multispectral DBR, DBR spreading effect can be improved under same current density. Meanwhile, without influencing voltage process window, improvement of the DBR doping concentration facilitates current spreading and dramatically improves anti-aging performance. In addition, doping concentration of the transient layer is the key affecting aging. In conventional method, aging is improved by lowering doping concentration of the transient layer. However, decreased doping concentration may cause increase of voltage VFavg of LED. In the present disclosure, by lowering doping concentration of the P-type semiconductor doping layer at the segmentation adjacent to the transient layer, a concentration difference is formed with that of the transient layer to balance doping of the transient layer; this avoids increasing non-radiation composition from high doping of the transient layer during long-time aging, which may cause light attenuation; in addition, voltage is controlled by keeping doping concentration of the P-type semiconductor layer at the segmentation adjacent to the quantum well, thus dramatically improving reliability.
In some embodiments, the substrate can be GaAs, GaP or Ge substrate that is suitable for epitaxial growth.
In some embodiments, the DBR reflecting layer adopts multi-spectral DBR, with preferred material of AlxGa1-xAs/AlyGa1-yAs, where, 0<x≤1, 0<y<1.
In some embodiments, in the multispectral DBR, the reflection wave band is divided into three bands; wherein, reflection wave bands of the first DBR reflecting layer, the second DBR reflecting layer and the third DBR reflecting layer are 700-750 nm, 650-700 nm, and 600-650 nm respectively.
In some embodiments, for the multispectral DBR, there are 2-7 pairs of the first DBR reflecting layers, 6-12 pairs of the second DBR reflecting layers, and 13-20 pairs of the third DBR reflecting layers.
In some embodiments, doping impurity of the multispectral DBR is any of Si, Sn, S, Se or Te.
In some embodiments, in the multispectral DBR, doping concentration of the first DBR reflecting layer is 7×1018-1×1020 cm−3; doping concentration of the second DBR reflecting layer is 5×1018-1×1020 cm−3, which is lower than that of the first DBR reflecting layer; and doping concentration of the third DBR reflecting layer is 2×1018-1×1020 cm−3, which is lower than that of the second DBR reflecting layer.
In some embodiments, the N-type semiconductor layer is GaAs, AlxGayIn1-xP and AlxIn(1-x)P, and preferably AlxIn(1-x)P, where, 0<x<1.
In some embodiments, doping impurity of the N-type doping is any of Si, Sn, S, Se or Te.
In some embodiments, N-type doping concentration is 0.5×1018-3.0×1018 cm−3.
In some embodiments, material of the quantum well light-emitting layer is AlxGayIn1-x-yP, where, 0<x<1, 0<y<1.
In some embodiments, material of P-type semiconductor is the same as that of the N-type semiconductor, preferably AlxIn(1-x)P, wherein 0<x<1.
In some embodiments, doping impurity of the P-type doping is any of Be, Mg, Zn, Cd or C.
In some embodiments, the segmented P-type semiconductor layer includes a first P-type semiconductor layer at the segmentation adjacent to the quantum well and a second P-type semiconductor layer at the segmentation adjacent to the transient layer.
In some embodiments, doping concentration of the first P-type semiconductor layer at the segmentation adjacent to the quantum well is 0.7×1018-1.5×1018 cm−3.
In some embodiments, thickness of the first P-type semiconductor layer at the segmentation adjacent to the quantum well is 0.3-1.0 μm.
In some embodiments, doping concentration of the second P-type semiconductor layer at the adjacent segmentation of the transient layer is 0.28×1018-1.2×1018 cm−3.
In some embodiments, thickness of the second P-type semiconductor layer at the segmentation adjacent to the transient layer is 0.03-0.3 μm.
In some embodiments, thickness of the second P-type semiconductor layer is 10%-30% that of the first P-type semiconductor layer.
In some embodiments, doping concentration of the second P-type semiconductor layer is 40%-80% that of the first P-type semiconductor layer.
In some embodiments, the transient layer adopts AlxGayIn1-x-yP material for gradient growth of each component, where, 0<x<1, 0<y<1, x+y<1.
In some embodiments, doping concentration of the transient layer is 1.5×1018-4.0×1018 cm−3.
In some embodiments, the P-type current spreading layer is GaP with Mg doping.
In some embodiments, thickness of the P-type current spreading layer is 2-10 μm.
Compared with existing technologies, some embodiments of the present disclosure can have one or more of the following technical effects. In the LED structure, the segmented-doping multispectral DBR can effectively improve current spreading and anti-aging performance; improved doping concentration of the DBR can further improve anti-aging performance without influencing the voltage process window. In addition, by lowering doping concentration of the P-type semiconductor doping layer at the segmentation adjacent to the transient layer, a concentration difference is formed with that of the transient layer to balance doping of the transient layer; this avoids increasing non-radiation composition from high doping of the transient layer during long-time aging, which may cause light attenuation; in addition, voltage is controlled by keeping doping concentration of the P-type semiconductor layer at the segmentation adjacent to the quantum well, thus dramatically improving reliability. This disclosure, in particular, improves anti-aging performance dramatically when the light-emitting diode is smaller than 50 mil2 and drive current is higher than or equal to 100 mA.
The accompanying drawings, which are included to provide a further understanding of the disclosure and constitute a part of this specification, together with the embodiments, are therefore to be considered in all respects as illustrative and not restrictive. In addition, the drawings are merely illustrative, which are not drawn to scale.
In the drawings: 100: substrate, 110: DBR reflecting layer, 120: N-type semiconductor layer, 130: quantum well light-emitting layer, 140: P-type semiconductor layer, 150: transient layer, 160: P-type current spreading layer; 200: substrate, 210: DBR reflecting layer, 211: first DBR reflecting layer, 212: second DBR reflecting layer, 213: third DBR reflecting layer, 220: N-type semiconductor layer, 230: quantum well light-emitting layer, 240: P-type semiconductor layer, 241: first P-type semiconductor layer, 242: second P-type semiconductor layer, 250: transient layer, 260: P-type current spreading layer, 270: P electrode, 280: N electrode.
Various embodiments of the present disclosure will be explained in details with reference to the accompanying drawings. Before further description, it should be understood, however, that various modifications and changes may be made to these embodiments. Therefore, the present disclosure is not limited to the embodiments below. It should also be noted that the scope of the present disclosure should still be subjected to the scope defined in the claims and the embodiments are merely for purposes of illustration, rather than restricting. Unless otherwise specified, all technical and scientific words shall have the same meanings as understood by persons skilled in the art.
As shown in
In the fabrication process of the AlGaInP light-emitting diode according to the present disclosure, the carrier gas is high-purity H2, and Ga, Al, In, As, P sources are TMGa, TMAl, TMIn, AsH3 and PH3, respectively. N-type and P-type doping agents are Si2H6 and Cp2Mg, respectively. Details are as follows:
First, providing a GaAs substrate.
Second, deoxidizing the surface of the GaAs substrate under temperature of 650-750° C., preferably 700° C. and then inputing AsH3.
Third, growing a multispectral DBR reflecting layer over the substrate, with material of AlxGa1-xAs/AlyGa1-yAs, where, 0<x≤1, 0<y<1, x=0, y=0.5, which includes:
growing a first DBR reflecting layer 211, with reflecting wavelength of 720 nm and doping concentration of 2.0×1019 cm−3, wherein, preferred number of pairs is 6; next, growing a second DBR reflecting layer 212 with reflecting wavelength of 670 nm and doping concentration of 1.0×1019 cm−3, wherein, preferred number of pairs is 10; at last, growing a third DBR reflecting layer 213 with reflecting wavelength of 630 nm and doping concentration of 6.0×1018 cm−3, wherein, preferred number of pairs is 14.
Forth, growing an N-type semiconductor layer 220 over the third DBR reflecting layer 213, with preferred material of AlxIn(1-x)P, where, 0<x<1 and the doping material is Si.
Fifth, growing a quantum well light-emitting layer 230 over the N-type semiconductor layer 220, wherein, the light-emitting layer material is AlxGayIn1-x-yP, where, 0<x<1, 0<y<1.
Sixed, growing a P-type semiconductor layer 240 over the quantum well light-emitting layer 230 with doping concentration of 1.0×1018 cm−3 and preferred thickness of 0.65 μm.
Seventh, growing a transient layer 250 over the P-type semiconductor layer 240, wherein, the transient layer is AlxGayIn1-x-yP, where 0<x<1, 0<y<1, x+y<1. Each component is under gradient growth.
Eighth, growing a P-type current spreading layer 260 over the transient layer 250 with thickness between 2-10 μm, and preferably 5 μm, wherein, the material is GaP.
In this new-type AlGaInP structure LED, after fabrication of the P-type electrode 270 and the N-type electrode 280, a small-size chip of 5.8 mil×5.8 mil is used for evaluation. Under 100 mA and 50° C., long-term aging light attenuation value can be controlled within −8%. The performance is improved compared with that of the conventional structure (above −20%).
As shown in
In this new-type AlGaInP structure LED, after fabrication of the P-type electrode 270 and the N-type electrode 280, a small-size chip of 5.8 mil×5.8 mil is used for evaluation. Under 100 mA and 50° C., long-term aging light attenuation value can be controlled within −5%. It can be seen that with improvement of DBR doping concentration, resistance to high current of small-size chip can be dramatically improved. However, this is not to say that the higher is the DBR doping, the better. Higher doping may produce impurities, thus increasing series resistance and voltage VFavg. Therefore, DBR doping concentration is controlled within 1×1020 cm−3.
Differences between Embodiment 3 and Embodiment 2 may include: on the basis of Embodiment 2, doping concentration of the second P-type semiconductor layer adjacent to the transient layer is lowered to fabricate a segmented doping P-type semiconductor layer. As shown in
In this new-type AlGaInP structure LED, after fabrication of the P-type electrode 270 and the N-type electrode 280, a small-size chip of 5.8 mil×5.8 mil is used for evaluation. Under 100 mA and 50° C., long-term aging light attenuation value can be controlled within −3%. This indicates that the resistance to aging caused by high current can be effectively improved by lowering doping concentration of the P-type semiconductor layer adjacent to the transient layer.
Differences between Embodiment 4 and Embodiment 3 may include: extend growth time of the first P-type semiconductor layer adjacent to the quantum well, and shorten growth time of the second P-type semiconductor layer adjacent to the transient layer to optimize thickness ratio. Reduce the doping flow set value of the second P-type semiconductor layer to about 0.5×1018 cm−3, which is 50% of that of the first P-type semiconductor layer to optimize doping ratio.
The P-type semiconductor is over the quantum well light-emitting layer.
Set growth temperature to 670° C., and reaction chamber pressure to 60 Torr. The doping material is Mg. During growth of the first P-type semiconductor layer, input Cp2Mg, and continue inputting for 12 min when flow setting remains unchanged. The doping concentration is 1.0×1018 cm−3 and growth thickness is about 0.6 μm. During growth of the second P-type semiconductor layer, reduce Mg flow to 50% with 1 min gradient method, and keep stable growth for 1.8 min. Maintain doping concentration at 0.5×1018 cm−3. The thickness is about 0.09 μm, which is 15% of that of the first P-type semiconductor layer. A segmented P-type semiconductor structure with preferred performance is therefore fabricated.
On the basis of Embodiment 3, Embodiment 4 further improves the segmented P-type doping layer structure with further optimized doping concentration ratio and thickness ratio. In Embodiment 4, doping of the second P-type semiconductor layer adjacent to the transient layer is further lowered to optimize anti-aging performance. Moreover, voltage VFavg is kept stable by increasing thickness of the first P-type semiconductor layer and reducing thickness of the second P-type semiconductor layer. Through this optimization scheme of thickness ratio and doping ratio, the resistance to aging caused by high current can be further improved to improve LED reliability.
In this new-type AlGaInP structure LED, after fabrication of the P-type electrode 270 and the N-type electrode 280, a small-size chip of 5.8 mil×5.8 mil is used for evaluation. Under 100 mA and 50° C., long-term aging light attenuation value can be controlled within −1.5% under 100 mA and 50° C.
Although specific embodiments have been described above in detail, the description is merely for purposes of illustration. It should be appreciated, therefore, that many aspects described above are not intended as required or essential elements unless explicitly stated otherwise. Various modifications of, and equivalent acts corresponding to, the disclosed aspects of the exemplary embodiments, in addition to those described above, can be made by a person of ordinary skill in the art, having the benefit of the present disclosure, without departing from the spirit and scope of the disclosure defined in the following claims, the scope of which is to be accorded the broadest interpretation so as to encompass such modifications and equivalent structures.
Number | Date | Country | Kind |
---|---|---|---|
2016 1 0276669 | Apr 2016 | CN | national |
The present application is a continuation of, and claims priority to, PCT/CN2016/111672 filed on Dec. 23, 2016, which claims priority to Chinese Patent Application No. 201610276669.2 filed on Apr. 29, 2016. The disclosures of these applications are hereby incorporated by reference in their entirety.
Number | Name | Date | Kind |
---|---|---|---|
5237581 | Asada | Aug 1993 | A |
6229834 | Nisitani | May 2001 | B1 |
6346719 | Udagawa | Feb 2002 | B1 |
7622745 | Suzuki | Nov 2009 | B2 |
7759148 | Hanamaki | Jul 2010 | B2 |
20020036296 | Akaike | Mar 2002 | A1 |
20020104997 | Kuo | Aug 2002 | A1 |
20090140273 | Takeuchi | Jun 2009 | A1 |
20120319080 | Fudeta | Dec 2012 | A1 |
20140291612 | Aihara | Oct 2014 | A1 |
Number | Date | Country | |
---|---|---|---|
20180145210 A1 | May 2018 | US |
Number | Date | Country | |
---|---|---|---|
Parent | PCT/CN2016/011672 | Dec 2016 | US |
Child | 15859555 | US |