This application is based upon and claims the benefit of priority of the prior Japanese Patent Application No. 2022-168344, filed on Oct. 20, 2022, the entire contents of which are incorporated herein by reference.
The embodiments discussed herein are related to a light receiving element and an infrared imaging device.
An infrared detector includes a light receiving element and a readout circuit. The light receiving element generates an amount of current corresponding to the intensity of an incident infrared ray. The readout circuit includes a capacitor and an amplifier, accumulates a current generated by the light receiving element in the capacitor as a charge, converts the accumulated charge into a voltage by the amplifier, amplifies the voltage, and outputs the voltage.
Dark current flows through the light receiving element even when there is no incident infrared ray. Dark current serves as a noise source, and as dark current increases, a ratio between a signal and noise (S/N ratio) decreases. When one light receiving element is processed and formed into a mesa type, dark current is roughly divided into in-plane components and peripheral (side wall) components. As a light receiving element is miniaturized due to an increase in the number of pixels of the light receiving element, the influence of peripheral components becomes relatively large. Accordingly, in order to obtain a good S/N ratio in the miniaturized light receiving element, it is important to reduce the peripheral components of dark current.
Japanese Laid-open Patent Publication No. 2017-011168, Japanese Laid-open Patent Publication No. 2016-111294, U.S. Patent Application Publication No. 2008/0073743, and U.S. Patent Application Publication No. 2013-0213462 are disclosed as related art.
According to an aspect of the embodiments, a light receiving element including: a light receiving layer that includes a superlattice of an InAs layer and a GaSb layer; and an amorphous layer that covers a side wall surface of the light receiving layer, wherein the amorphous layer contains In and As, and an amount of Ga and an amount of Sb contained in the amorphous layer are smaller than an amount of In and an amount of As contained in the amorphous layer.
The object and advantages of the invention will be realized and attained by means of the elements and combinations particularly pointed out in the claims.
It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory and are not restrictive of the invention.
As a material for an infrared absorption layer included in a light receiving element, a type II superlattice (T2SL) has been attracting attention. For example, a superlattice of InAs layers and GaSb layers is promising in terms of sensitivity, wavelength controllability, increasing the number of pixels, and the like. However, it is difficult to reduce the peripheral components of dark current flowing through the side wall surfaces of an infrared absorption layer including a superlattice of InAs layers and GaSb layers.
An object of the present disclosure is to provide a light receiving element and an infrared imaging device capable of reducing the peripheral components of dark current.
The inventors of the present application have made intensive studies to investigate the cause of the difficulty of reducing the peripheral components of dark current flowing through the side wall surfaces of an infrared absorption layer including a superlattice of InAs layers and GaSb layers. As a result, it has become clear that, in the process of manufacturing a light receiving element, Ga oxide and Sb oxide are generated on the side walls of the infrared absorption layer at the time of cleaning in deionized water or the like after etching, and the Sb oxide having relatively low thermal stability is deprived of oxygen by another element, thereby exhibiting metal-like properties. Based on such findings, the inventors of the present application have devised the following embodiments.
Hereinafter, embodiments of the present disclosure will be described in detail with reference to accompanying drawings. In the present specification and drawings, constituent elements having substantially the same functional configuration may be described with the same reference signs and redundant description thereof may be omitted.
A first embodiment will be described. The first embodiment relates to a light receiving element.
As illustrated in
For example, the lower contact layer 13 is an InAs0.91Sb0.09 layer. The lower contact layer 13 is doped with Si or Te as an n-type impurity at a concentration of 1×1018 cm−3, and the lower contact layer 13 has n-type conductivity. For example, the thickness of the lower contact layer 13 is 2 μm.
The electron barrier layer 14 is provided over the lower contact layer 13. For example, the electron barrier layer 14 includes a type II superlattice in which InAs layers and GaSb layers are alternately laminated. For example, the thickness of the InAs layers is 2.2 nm and the thickness of the GaSb layers is 2.1 nm. For example, the electron barrier layer 14 is doped with Be or Zn as a p-type impurity at a concentration of 5×1017 cm−3, and the electron barrier layer 14 has p-type conductivity. For example, the thickness of the electron barrier layer 14 is equivalent to 50 cycles when a laminate of an InAs layer and a GaSb layer is set as one cycle of the superlattice.
The infrared absorption layer 15 is provided over the electron barrier layer 14. As illustrated in
The hole barrier layer 16 is provided over the infrared absorption layer 15. For example, the hole barrier layer 16 includes a type II superlattice in which InAs layers and AlSb layers are alternately laminated. For example, the thickness of the InAs layers is 4.6 nm and the thickness of the AlSb layers is 1.2 nm. For example, the hole barrier layer 16 is doped with Si or Te as an n-type impurity at a concentration of 5×1017 cm−3, and the hole barrier layer 16 has n-type conductivity. For example, the thickness of the hole barrier layer 16 is equivalent to 50 cycles when a laminate of an InAs layer and an AlSb layer is set as one cycle of the superlattice.
The upper contact layer 17 is provided over the hole barrier layer 16. For example, the upper contact layer 17 is an InAs layer. The upper contact layer 17 is doped with Si or Te as an n-type impurity at a concentration of 1×1018 cm−3, and the upper contact layer 17 has n-type conductivity. For example, the thickness of the upper contact layer 17 is 20 nm.
The electron barrier layer 14, the infrared absorption layer 15, the hole barrier layer 16, and the upper contact layer 17 are etched into a mesa shape. For example, the light receiving element 1 includes a mesa 19 including the electron barrier layer 14, the infrared absorption layer 15, the hole barrier layer 16, and the upper contact layer 17.
The amorphous layer 20 covers the side wall surfaces of the electron barrier layer 14 and the infrared absorption layer 15. The amorphous layer contains In and As. The amorphous layer 20 may further contain oxygen (O). The main components of the amorphous layer are In, As, and O. Ga, Sb, or both of Ga and Sb may be contained in the amorphous layer 20, but an amount of Ga (atomic %) and an amount of Sb (atomic %) contained in the amorphous layer 20 are smaller than an amount of In (atomic %) and an amount of As (atomic %) contained in the amorphous layer 20. Each of the amount of Ga (atomic %) and the amount of Sb (atomic %) contained in the amorphous layer 20 is preferably 10 atomic % or less, more preferably 8 atomic % or less, and still more preferably 5 atomic % or less.
Although the amorphous layer 20 mainly covers the side wall surfaces of the electron barrier layer 14 and the infrared absorption layer 15, the amorphous layer 20 may include a portion covering the side wall surfaces of the hole barrier layer 16. However, the portion covering the side wall surfaces of the hole barrier layer 16 is thin. For example, the thickness from an end portion of an InAs layer included in the hole barrier layer 16 is at most 3 nm. Accordingly, the distance between the hole barrier layer 16 and the protective layer 21 is 3 nm or less. The portion of the amorphous layer 20 covering the side wall surfaces of the hole barrier layer 16 does not contain Ga, but contains Al.
The protective layer 21 covers the side surfaces of the upper contact layer 17 and the hole barrier layer 16, the upper surface of the upper contact layer 17, and the upper surface of the lower contact layer 13. The protective layer 21 further covers the amorphous layer 20. For example, the protective layer 21 is a silicon dioxide (SiO2) layer, a silicon oxynitride (SiON) layer, or a silicon nitride (SiN) layer. For example, the thickness of the protective layer 21 is about 500 nm.
An opening 22 that exposes a part of the upper surface of the lower contact layer 13 and an opening 23 that exposes a part of the upper surface of the upper contact layer 17 are formed in the protective layer 21. The lower electrode 24 is provided inside the opening 22, and the upper electrode 25 is provided inside the opening 23. For example, the lower electrode 24 includes a Ti film in contact with the lower contact layer 13, a Pt film over the Ti film, and an Au film over the Pt film. The lower electrode 24 is in ohmic junction with the lower contact layer 13. For example, the upper electrode 25 includes a Ti film in contact with the upper contact layer 17, a Pt film over the Ti film, and an Au film over the Pt film. The upper electrode 25 is in ohmic junction with the upper contact layer 17.
Next, a method of manufacturing the light receiving element 1 according to the first embodiment will be described.
First, as illustrated in
Next, an SiON layer 31 is formed over the upper contact layer 17. For example, the SiON layer 31 is formed by a plasma CVD method. For example, the thickness of the SiON layer 31 is about 500 nm. After that, a resist mask 32 is formed over the SiON layer 31 by lithography. The resist mask 32 is formed so as to cover a region where the mesa 19 is to be formed.
Subsequently, as illustrated in
After that, as illustrated in
Subsequently, the side walls of the mesa 19 are processed by using a citric acid-based aqueous solution. As a result, as illustrated in
Next, as illustrated in
After that, by removing the substrate 11 and the buffer layer 12, the light receiving element 1 according to the first embodiment may be manufactured.
In the first embodiment, the side wall surfaces of the infrared absorption layer 15 are covered with the amorphous layer 20. The amorphous layer 20 contains In and As, and the amount of Ga (atomic %) and the amount of Sb (atomic %) contained in the amorphous layer 20 are smaller than the amount of In (atomic %) and the amount of As (atomic %) contained in the amorphous layer 20. For this reason, both during the process of manufacturing the light receiving element 1 and after the completion of the light receiving element 1, arrival of oxygen at the side wall surfaces of the electron barrier layer 14 and the infrared absorption layer 15 is suppressed, and generation of Ga oxide and Sb oxide is suppressed. Accordingly, a leakage current caused by the generation of Sb oxide may be suppressed, and the peripheral components of dark current for which the side wall surfaces of the electron barrier layer 14 and the infrared absorption layer 15 serve as the leakage paths may be reduced. Accordingly, even when the light receiving element 1 is miniaturized, a good S/N ratio may be obtained.
A reference example will be described for comparison with the first embodiment.
A light receiving element 1X according to the reference example is manufactured by a method substantially similar to that in the first embodiment. The main difference from the first embodiment is that, in the manufacturing, cleaning in deionized water is performed immediately after removal of a damaged layer, and formation of the protective layer 21 and subsequent processing are performed without forming the amorphous layer 20. As illustrated in
As described above, in the light receiving element 1X, the oxide film 20X includes a portion where the thermal stability of the Sb oxide contained in the oxide film 20X is low and the Sb oxide is decomposed to exhibit properties close to metals. Since the oxide film 20X is thick, dark current easily flows in the vicinity of the side walls of the infrared absorption layer 15. By contrast, since the present embodiment has a configuration in which Sb oxide is unlikely to be included, it is possible to reduce dark current due to Sb oxide.
An analysis result of a laminated structure manufactured in accordance with the first embodiment will be described. This laminated structure has a structure illustrated in
As illustrated in
Oxygen contained in a mixed solution used for removing a damaged layer or oxygen contained in a gas used for forming the protective layer 21 may be contained in the amorphous layer 20.
The thickness of the amorphous layer 20 (thickness in a direction parallel to the upper surface of the substrate 11) is preferably 5 nm or more and 50 nm or less, more preferably 10 nm or more and 45 nm or less, and still more preferably 15 nm or more and 40 nm or less. In a case where the amorphous layer 20 is too thin, there is a possibility that, when the protective layer 21 is formed or the like, the infrared absorption layer 15 and the electron barrier layer 14 covered with the amorphous layer 20 are oxidized and Sb oxide is easily generated. In a case where the amorphous layer 20 is too thick, there is a possibility that the amount of reduction of crystalline GaSb layers constituting a superlattice is large and the surface flatness is deteriorated, formation of the protective layer 21 is insufficient, and dark current due to process damage increases.
The infrared absorption layer 15 may include an InSb layer as a strain compensation layer between the InAs layer 15A and the GaSb layer 15B. For example, the thickness of an InSb layer is 0.2 nm. An InSb layer may relieve strain caused by the difference in lattice constant between the substrate 11 and the InAs layer 15A. An InSb layer may be provided between all of the InAs layers 15A and the GaSb layers 15B, or may be provided for each cycle (set) of the InAs layers 15A and the GaSb layers 15B. Similarly, the electron barrier layer 14 and the hole barrier layer 16 may include an InSb layer as a strain compensation layer.
A second embodiment will be described. The second embodiment relates to an infrared imaging device including a light receiving element 1.
An infrared imaging device 2 according to the second embodiment includes a pixel array 50 and a readout circuit (ROIC) 60. The pixel array 50 includes a plurality of light receiving elements 1 arranged in an array. Each light receiving element 1 constitutes one pixel 51. The pixel array 50 and the readout circuit 60 are flip-chip bonded. Each pixel 51 is electrically coupled to a corresponding unit cell 61 formed in the readout circuit 60 by a bonding electrode 27 (see
Next, a method of manufacturing the infrared imaging device 2 according to the second embodiment will be described.
First, processing up to the formation of the lower electrode 24 and the upper electrode 25 is performed in accordance with the first embodiment. At this time, a plurality of mesas 19 is formed in an array over one substrate 11. A mesa for dummy pixel is formed around the pixel 51 in addition to the mesa 19 constituting the pixel 51. Lead wiring is formed on the side wall of the mesa for dummy pixel, and the lower electrode 24 is coupled to an upper electrode included in the mesa for dummy pixel. The lower electrode 24 is used as a common electrode for the plurality of pixels 51 forming a corresponding column or row of the pixel array 50.
After the formation of the lower electrode 24 and the upper electrode 25, as illustrated in
Next, as illustrated in
Subsequently, the rear surface of the substrate 11 is ground until the thickness of the substrate 11 is, for example, 50 μm. Next, as illustrated in
After that, an anti-reflection film is formed on the rear surface of the lower contact layer 13 serving as an infrared ray incidence surface, and the device is mounted in a container. In this manner, the infrared imaging device 2 may be manufactured.
According to the second embodiment, since the light receiving element 1 according to the first embodiment is included, the peripheral components of dark current are reduced, an excellent S/N ratio is obtained, and a clear image having high temperature resolution may be obtained with a fine and high-definition configuration.
The wavelength of an infrared ray to be a light receiving target is not particularly limited. For example, an infrared ray with a wavelength of 1.4 μm to 30 μm may be a light receiving target, for example, an infrared ray with a wavelength of 1.4 μm to 15 μm may be a light receiving target. The thickness of the InAs layers 15A and the GaSb layers 15B may be adjusted according to the wavelength of an infrared ray to be a light receiving target. Also for the electron barrier layer 14 and the hole barrier layer 16, the thickness of the compound semiconductor layers constituting a superlattice may be adjusted according to the wavelength of an infrared ray to be a light receiving target. The configuration of the superlattice included in the electron barrier layer 14 and the hole barrier layer 16 is not particularly limited. For example, the superlattice included in the hole barrier layer 16 may have a configuration in which an InAs layer, a GaSb layer, an AlSb layer, and a GaSb layer are laminated in this order. The conductivity type of the light receiving layer may be an n-type. In this case, an AlGaSb layer or the like may be used as the electron barrier layer.
For example, the light receiving element, the infrared imaging device, and the like may be used for nighttime navigation in a ship or may be used for nondestructive inspection of concrete.
Although the preferred embodiments and the like have been described in detail above, the present disclosure is not limited to the above-described embodiments and the like. Various modifications and replacements may be made to the above-described embodiments and the like without departing from the scope of the claims.
All examples and conditional language provided herein are intended for the pedagogical purposes of aiding the reader in understanding the invention and the concepts contributed by the inventor to further the art, and are not to be construed as limitations to such specifically recited examples and conditions, nor does the organization of such examples in the specification relate to a showing of the superiority and inferiority of the invention. Although one or more embodiments of the present invention have been described in detail, it should be understood that the various changes, substitutions, and alterations could be made hereto without departing from the spirit and scope of the invention.
Number | Date | Country | Kind |
---|---|---|---|
2022-168344 | Oct 2022 | JP | national |
Number | Date | Country | |
---|---|---|---|
20240136452 A1 | Apr 2024 | US |