Patent Application
20220024184
The disclosure relates generally to hurricane resistant laminated panes having two sheets of glass and a polymer interlayer, where one sheet of glass is untempered meaning that it is not thermally or chemically strengthened but is essentially in strength condition “as produced”, and to windows employing one or more such laminated panes for combined impact and pressure cycling resistance such as in hurricane windows, or for other purposes such as for increased intrusion resistance.
So-called hurricane windows typically employ reinforced frame and spacer components as well as an inner laminated pane comprising two sheets of glass and a polymer interlayer having a high elastic modulus (or a high elastic modulus under sufficiently fast deformation).
As seen in
During a hurricane, if a wind-driven projectile strikes surface S1 with sufficient force, then sheet 50, first sheet 20, and second sheet 70 can all be broken by the impact, but if the window 200 operates as intended, the polymer interlayer 40 remains intact and remains sealed within the window frame, preventing wind and wind-borne water from passing through the window 200 and entering the dwelling even after sheet 50, first sheet 20, and second sheet 70 are broken. To enable the polymer interlayer 40 to survive such an impact, the first sheet 20 and the second sheet 70 of the laminated pane 12 are heat strengthened, meaning they are thermally tempered to produce a surface compression generally in the range of from about 24 to 52 MPa (3,500 to 7,500 psi). (The sheet 50 is also generally heat strengthened.)
If the first sheet 20 and the second sheet 70 are not thermally strengthened, they tend to break upon impact into large, sharp-edged fragments that can tear, puncture or otherwise damage the interlayer 40, causing it to fail to maintain the desired seal. It would be desirable to provide a hurricane resistant window having lower manufacturing process costs, such as by avoiding unneeded thermal strengthening, while still preserving or even improving other window properties.
According to aspects of the disclosure, a light weight hurricane-resistant laminated pane is provided, comprising a first sheet of thermally strengthened glass having a thickness in the range of from 2 to 24 mm, a second sheet of untempered glass having a thickness in the range of from 0.3 to 1 mm, and a polymer interlayer between the first sheet and the second sheet and adhered to the first sheet and the second sheet. The use of a thin second sheet allows the second sheet to be used in untempered form, saving both weight (by thinness) and processing cost (by lack of need for tempering).
According to aspects, the first sheet is a sheet of a soda lime silicate glass.
According to aspects, the second sheet is a sheet of a soda lime silicate glass.
According to other aspects of the disclosure, the second sheet is a sheet of a boro-aluminosilicate glass, or a sheet of an alkaline earth boro-aluminosilicate glass or an alkali-free boro-aluminosilicate glass.
According to aspects, the second sheet has a thickness in the range of from 0.85 to 0.4 mm, or of from 0.8 to 0.45 mm.
Also disclosed as another aspect is a window comprising a laminated pane according to any of the above aspects.
According to aspects of the present disclosure, a process for forming a hurricane resistant laminated pane comprises thermally strengthening a first sheet of glass having a thickness in the range of from 2 to 24 mm and, using a polymer interlayer, laminating the first sheet of glass to a second sheet of untempered glass having a thickness in the range of from 0.3 to 1 mm.
According to aspects, a hurricane resistant window comprises an outer pane having a thickness in the range of from 2 to 24 mm, an inner laminated pane comprising a first sheet of thermally strengthened glass having a thickness in the range of from 2 to 24 mm and a second sheet of untempered glass having a thickness in the range of from 0.3 to 1 mm and a polymer interlayer between the first sheet and the second sheet and adhered to the first sheet and the second sheet.
According to aspects, the first sheet of the laminated pane faces of the hurricane resistant window faces the outer pane.
According to aspects, the second sheet of the laminated pane faces of the hurricane resistant window faces the outer pane.
Additional features and advantages of the disclosure will be set forth in the detailed description which follows, and in part will be readily apparent to those skilled in the art from that description or recognized by practicing the methods as described herein, including the detailed description which follows, the claims, as well as the appended drawings.
It is to be understood that both the foregoing general description and the following detailed description present various embodiments of the disclosure, and are intended to provide an overview or framework for understanding the nature and character of the claims. The accompanying drawings are included to provide a further understanding of the disclosure, and are incorporated into and constitute a part of this specification. The drawings illustrate various embodiments of the disclosure and, together with the description, serve to explain the principles and operations of the disclosure.
The following detailed description can be further understood when read in conjunction with the following drawings in which:
Various aspects of the disclosure will now be discussed with reference to
With reference to
The first sheet 20 can be a sheet of a soda lime silicate glass.
The second sheet 30 can also be a sheet of a soda lime silicate glass. Alternatively, the second sheet 30 can be a sheet of a boro-aluminosilicate glass, or a sheet of an alkaline earth boro-aluminosilicate glass or an alkali-free boro-aluminosilicate glass. The thickness of the second sheet can be in the range of from 0.85 to 0.4 mm, or of from 0.8 to 0.45 mm.
An improved process of forming a hurricane resistant window comprises thermally strengthening a first sheet of glass 20 having a thickness in the range of from 2 to 24 mm and, using a polymer interlayer 40, laminating the first sheet of glass 20 to a second sheet of untempered glass 30 having a thickness in the range of from 0.3 to 1 mm.
As shown in
It will be appreciated that the various disclosed embodiments can involve particular features, elements or steps that are described in connection with that particular embodiment. It will also be appreciated that a particular feature, element or step, although described in relation to one particular embodiment, can be interchanged or combined with alternate embodiments in various non-illustrated combinations or permutations.
It is also to be understood that, as used herein the terms “the,” “a,” or “an,” mean “at least one,” and should not be limited to “only one” unless explicitly indicated to the contrary. Thus, for example, reference to “a component” includes examples having one such “component” or two or more such “components” unless the context clearly indicates otherwise. Similarly, a “plurality” or an “array” is intended to denote two or more, such that an “array of components” or a “plurality of components” denotes two or more such components.
Ranges can be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, examples include from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another aspect. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint.
All numerical values expressed herein are to be interpreted as including “about,” whether or not so stated, unless expressly indicated otherwise. It is further understood, however, that each numerical value recited is precisely contemplated as well, regardless of whether it is expressed as “about” that value. Thus, “a dimension less than 100 nm” and “a dimension less than about 100 nm” both include embodiments of “a dimension less than about 100 nm” as well as “a dimension less than 100 nm.”
Unless otherwise expressly stated, it is in no way intended that any method set forth herein be construed as requiring that its steps be performed in a specific order. Accordingly, where a method claim does not actually recite an order to be followed by its steps or it is not otherwise specifically stated in the claims or descriptions that the steps are to be limited to a specific order, it is no way intended that any particular order be inferred.
While various features, elements or steps of particular embodiments can be disclosed using the transitional phrase “comprising,” it is to be understood that alternative embodiments, including those that can be described using the transitional phrases “consisting” or “consisting essentially of,” are implied. Thus, for example, implied alternative embodiments to a device comprising A+B+C include embodiments where a device consists of A+B+C, and embodiments where a device consists essentially of A+B+C.
It will be apparent to those skilled in the art that various modifications and variations can be made to the present disclosure without departing from the spirit and scope of the disclosure. Since modifications combinations, sub-combinations and variations of the disclosed embodiments incorporating the spirit and substance of the disclosure can occur to persons skilled in the art, the disclosure should be construed to include everything within the scope of the appended claims and their equivalents.
This application claims the benefit of priority under 35 U.S.C. § 119 of U.S. Provisional Application No. 62/772,727, filed Nov. 29, 2018, the content of which is incorporated herein by reference in its entirety.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2019/062893 | 11/24/2019 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62772727 | Nov 2018 | US |