Composite parts of aircrafts or other vehicles are made from several layers, or plies, of fibers and resin, which are hardened or cured to maintain rigidity. These composite parts are relatively lightweight as compared to traditional metallic parts, while exhibiting similar or even improved strength and longevity properties. Thus, many aircraft components such as fuselages, wings, and other parts that traditionally were made of steel, aluminum, or other metal are now produced as composite parts. These composite parts may be formed using a thermoplastic polymer, which turns to liquid when heated and turns solid when cooled, or else using a thermoset polymer, which is a polymer that is pliable at room temperatures and thereafter cures when heated to elevated temperatures.
Unlike metal components, however, composite parts are not electrically conductive, and thus do not inherently provide adequate lighting strike protection. When fuselages or wings are made from aluminum, steel, or other metallic substances, the outer surface provides a highly conductive path such that, if the part is subject to a lightning strike during flight, the current passes from the entry point across the surface to an exit point without structurally damaging the aircraft. On the other hand, the materials used to form composite aircraft components such as, for example, carbon or graphite fibers combined with a thermoplastic or thermoset resin, are not electrically conductive and thus cannot, on their own, sufficiently pass current across the outer skin of the component.
Composite parts of aircraft in lightning strike zones are therefore provided with a lightning strike protection layer, which increases the conductivity of the outer surface of the composite part and enables the composite part to sufficiently absorb and pass current from a lightning strike across the outer surface of the part without structural damage to the part similar to the more traditional aluminum, steel, or other metallic components. The lightning strike protection layer may be a conductive metallic mesh or foil that is affixed to the outer surface of the composite part. If the part is thereafter subjected to a lightning strike, the current passes from the entry point to an exit point via the conductive mesh or foil eliminating structural damage to the aircraft part.
Often, composite parts are created using a thermoset resin, which is relatively pliable at normal manufacturing temperatures and which cures and hardens when heated to elevated temperatures. For such thermoset parts, adding lightning strike protection may include adding an outermost layer comprised of a thermoset resin and wire mesh or foil, and then heating the part to cure the thermoset resin thus bonding the wire mesh or foil to the component part and holding the mesh or foil in place. Because the thermoset resin is pliable at normal manufacturing temperatures, the lightning strike protection layer can relatively easily conform to the outer contour of the wing, fuselage, or other aircraft part being produced.
Recently, however, there has been a push to produce aircraft components from thermoplastic polymers because thermoplastic components exhibit certain advantages over thermoset components. For example, thermoplastic components may be more easily recycled than thermoset components, may exhibit increased strength as compared to thermoset components, and are less expensive and easier to produce because the parts can be heated and cooled repeatedly and produced rapidly without the need for autoclaves or other expensive equipment.
Thermoplastic component parts have certain drawbacks, however. For one, semi-crystalline thermoplastic composites have a very low surface energy and thus can be difficult to bond with primer or paint. Thus, in order to achieve sufficient paint adhesion for thermoplastic component parts, the outermost layer must be subjected to slow and expensive surface treatment such as plasma or corona etching to achieve a sufficient surface roughness or surface energy increase for paint adhesion. Similarly, to repair surface defects in thermoplastic parts, additional surface treatment (such as etching or similar) is necessary so that the filler may adequately bond to the defect.
Moreover, the low surface energy of the semi-crystalline thermoplastic parts makes it difficult for the secondary application of lightning strike protection to a thermoplastic skin in a durable fashion. That is, thermoplastic processing resins that are compatible for simultaneous melt processing with the composite parts are in the form of a film, which at ordinary manufacturing temperatures are not pliable and thus not drapable. In this regard, the film must be applied to the compound contours of the part being formed (fuselage, wing, etc.) in narrow strips. When applying a lightning strike protection in the form of a metallic mesh or foil or the like, each strip must form sufficient contact with the neighboring strip in order to ensure sufficient conductivity across the outer surface of the composite part. Any because such films do not have any tack at normal manufacturing temperatures, it is challenging to keep the narrow strips in place during application and processing.
Still more, the high processing (melt) temperature and crystalline content of advanced thermoplastic resins results in substantial shrinkage when they cool, especially for a resin rich area. This results in substantial residual tensile stress in the resin when processed with a low coefficient of thermal expansion (CTE) carbon fiber laminate that shrinks very little during cool-down. These stresses can result in cracking of the resin, especially when exposed to low temperatures. Furthermore, when complex thermoplastics structures are processed in production surface porosity and pitting often occur. Repairing these defects can be expensive, especially when they occur in lightning strike protected areas.
Thus, although it would be desirable to form certain composite parts from thermoplastic polymers, the difficulty in applying a sufficient surfacer, particularly in lightning strike protected areas, has limited the use of thermoplastic component parts in practice. Thus, there exists a need exists for an improved surfacer to be implemented on thermoplastic composite parts.
At a high level, the present invention is directed to an improved surfacer to be used with thermoplastic component parts, and methods of producing the same. More particularly, embodiments of the invention are directed to a paintable surfacer for thermoplastic composite laminates with integral lightning strike protection mesh or foil that has drape and reinforced surface healing capability, and methods of producing the same.
For example, some embodiments of the invention are directed to a thermoplastic surfacer for providing lightning strike protection to a composite component of an aircraft. The thermoplastic surfacer includes a broadgood having a thermoplastic resin, one or more fillers embedded into the broadgood, and a lightning strike protection mesh or foil embedded into the broadgood.
Other embodiments of the invention are directed to a method of manufacturing a thermoplastic surfacer for providing lightning strike protection to a composite component of an aircraft. The method includes conveying a matrix resin fleece along one or more conveyor tables, with the matrix resin fleece including a broadgood having a thermoplastic resin embedded therein. The method also includes embedding one or more fillers into the matrix resin fleece and heating the matrix resin fleece until at least a portion of the thermoplastic resin reaches a melt temperature of the thermoplastic resin. Finally, the method includes embedding a lightning strike protection mesh or foil into the matrix resin fleece.
Still other embodiments of the invention are directed to a method of applying a thermoplastic surfacer to a composite part of an aircraft. The method includes draping a thermoplastic surfacer on an at least partially unconsolidated composite part, such as the thermoplastic surfacer discussed above or the thermoplastic surfacer produced by the method discussed above. The method further includes consolidating the at least partially unconsolidated composite part thereby forming a consolidated composite part by heating the at least partially unconsolidated composite part to a temperature at or above a melt temperature of a resin used in the at least partially unconsolidated composite part and at or above a melt temperature of the thermoplastic polymer resin of the thermoplastic surfacer. Finally, the method includes filling at least one surface defect in the consolidated part using the thermoplastic polymer resin and milled fibers provided in the thermoplastic surfacer.
These and other features will be discussed in more detail below in connection with the accompanying drawings.
The present invention is described in detail below with reference to the attached drawing figures, wherein:
The following detailed description of the invention references the accompanying drawings that illustrate specific embodiments in which the invention can be practiced. The embodiments are intended to describe aspects of the invention in sufficient detail to enable those skilled in the art to practice the invention. Other embodiments can be utilized, and changes can be made, without departing from the scope of the current invention. The following detailed description is, therefore, not to be taken in a limiting sense. The scope of the current invention is defined only by the appended claims, along with the full scope of equivalents to which such claims are entitled.
In this description, references to “one embodiment,” “an embodiment,” or “embodiments” mean that the feature or features being referred to are included in at least one embodiment of the technology. Separate references to “one embodiment,” “an embodiment,” or “embodiments” in this description do not necessarily refer to the same embodiment and are also not mutually exclusive unless so stated and/or except as will be readily apparent to those skilled in the art from the description. For example, a feature, structure, act, etc., described in one embodiment may also be included in other embodiments, but is not necessarily included. Thus, the current technology can include a variety of combinations and/or integrations of the embodiments described herein.
Generally, aspects of the invention are directed to a thermoplastic surfacer that overcomes problems associated with using thermoplastic laminates as primary composite part structures, especially in areas where lightning strike protection is required. These and other features will be readily understood with reference to the figures.
First,
At a high level, the matrix resin fleece 112 is an amorphous polymer fleece that is similar in terms of drapability and pliability to a conventional blanket or coat-liner type material. More particularly, the matrix resin fleece 112 is an amorphous polymer filament felt made by distributing and entangling thermoplastic filaments into a wide broadgood—that is, a non-woven fabric made of thermoplastic filaments. Any suitable thermoplastic that exhibits amorphous behavior (as opposed to crystalline or semi-crystalline behavior) can be used as the thermoplastic filaments. These amorphous polymers include, without limitation, acrylonitrile butadiene styrene (ABS), polystyrene (PS), polycarbonate (PC), polysulfone (PSU), polyethersulfone (PES), polyphenylene sulfone (PPSU), and polyetherimide (PEI).
For example, one non-limiting example of a suitable matrix resin fleece is the backing material used by the Mitsubishi Chemical Corporation is its commercial PEI thermoplastic fleece product marketed under the trade name Kyron®Tex. The Kyron®Tex PEI product generally includes a matrix resin fleece material combined with various reinforcement fibers. Thus, in some embodiments the matrix resin fleece 112 may be the matrix resin fleece portion of the Kyron®Tex PEI product; that is, the matrix resin fleece 112 may be Kyron®Tex PEI without some or all of the reinforcement fibers. In other embodiments the matrix resin fleece 112 may be the Kyron®Tex PEI product in its entirety; that is the matrix resin fleece 112 could already have glass fibers embedded as is currently available from Mitsubishi.
In some embodiments, the matrix resin fleece 112 will have a melt or handling temperature similar to the melt or handling temperature of the thermoplastic component part to which the surfacer 132 is ultimately be applied to assist with adhesion during processing steps such as during laminate consolidation, as will be discussed in more detail below in connection with
The tooling 110 shown in
The matrix resin fleece 112 is guided along the tables 114, 122 and impregnated with or otherwise combined with the milled fibers 118 and/or other fillers 120. More particularly, in the depicted embodiment the milled fibers 118 and fillers 120 are applied to a top surface of the matrix resin fleece 112 and embedded into the fleece 112 via a vacuum provided by the air table 114 drawing the fibers 118 and fillers 120 into the fleece. As the matrix resin fleece 112 (now impregnated with the fibers 118 and fillers 120) moves along the tooling 110, a vibration table 122 may further embed the fibers 118 and fillers 120 therein by vibrating the impregnated fleece 112, causing the fibers 118 and fillers 120 to more compactly settle therein. The tooling may also include a binder spray 124 either at one of the tables 114, 122 or else downstream thereof, which helps to adhere the fibers 118 and fillers 120 to the fleece 112 and ensures the fibers 118 and/or fillers 120 stay in place.
After the fleece 112 is provided with any milled fibers 118, other fillers 120, and binder spray 124—referred to herein as the “filler-laden” fleece 112—the filler-laden fleece 112 passes through heaters 126. The heaters 126 heat at least a portion of the resin in the filler-laden fleece 112 to a melting or softening point, such that the thermoplastic resin begins to melt and becomes more pliable. In some embodiments only a top surface of the resin (that is, a surface to which a lightning strike protection mesh or foil 128 is to be applied) in the filler-laden fleece 112 is heated to the melting point. In other embodiments, the resin is heated completely through its thickness (that is, the vertical dimension shown in
A lightning strike protection mesh or foil 128 is then applied to an exposed (and melted) upward-facing side of the filler-laden fleece 112. The lightning strike protection mesh or foil 128 can be any metallic, and thus electrically conductive, mesh or foil known in the art. In embodiments in which the mesh or foil is aluminum and the fibers used in the laminate of the composite part to which the surfacer 132 is to be applied are carbon, it may be necessary to electrically isolate the mesh or foil 128 from the carbon fibers using the milled fibers 118, the other fillers 120, and/or a veil to reduce corrosion due to the galvanic reaction, which will be discussed in more detail below.
Finally, the filler-laden fleece 112 and lightning strike protection mesh or foil 128 combination is provided to a pair of calendaring rolls 130 which compress the lightning strike protection mesh or foil 128 into the heated, filler-laden fleece 112 forming the novel thermoplastic surfacer 132. At this point the matrix resin fleece 112 will be partially consolidated such that the mesh or foil 128 will be attached, but the resin will not be completely melted so that the right amount of drape remains while providing enough support so that the mesh or foil 128 is protected from handling damage.
Optionally, once cooled the thermoplastic surfacer 112 can be spooled onto a takeup roll 134 or similar for storage and/or transportation. In such embodiments, when ultimately applied to a composite part or the like, the surfacer 132 is simply spooled off of the takeup roll 134 and draped onto the composite part.
The thermoplastic surfacer 132 exhibits several advantages as compared to known surfacers and lightning strike protection processes. Because the lightning strike protection mesh or foil 128 is embedded into the matrix resin fleece 112, the mesh or foil 128 is protected during handling and when applying to a composite part. Put another way, the combination of the partially consolidated filled fleece 112 and lightning strike protection mesh or foil 128 (i.e., conductive foil) can provide drapability and prevents damaging the very fragile foil during handling. This prevents damage to the mesh or foil 128 that may otherwise occur using known manufacturing processes and thus increases the integrity of the lightning strike protection features.
Moreover, the thermoplastic surfacer 132 is drapable and thus can more readily conform to the complex outer contours of the composite part to which the surfacer 132 is being adjoined. Because known films are not drapable, they must be applied in strips when accommodating complex contours with each strip being adjoined to neighboring strips. This may result in gaps in the conductive mesh or foil and thus reduced lightning strike protection performance, defects formed at the intersection of adjoining strips, and time-consuming and expensive manufacturing processes.
Still more, because the resin of the thermoplastic surfacer 132 may have a melt temperature substantially similar to the thermoplastic composite part to which it is applied, the surfacer 132 may be easily melded with the composite part during manufacture by simply heating the components to the melt range and subsequently cooling. More particularly, the method of manufacturing the thermoplastic surfacer 132 would begin with a felt or fleece composed of an amorphous resin with a similar process temperature to that of composite laminate matrix being covered. Ideally the surfacer and the laminate would have substantial overlap in recommended process temperatures. For example, the recommended process temperature for Toray TC 1225 polyaryletherketone (PAEK) carbon prepreg is 608 to 720° F. and the Mitsubishi Chemical Kyron®Tex PEI has a recommended process temperature of 680 to 716° F. This overlap of processing temperatures allows the two to melt and diffuse together during laminate consolidation.
Still more, because the thermoplastic surfacer 132 is formed using an amorphous rather than semi-crystalline resin, the outer surface of the thermoplastic surface 132 exhibits increased paint adhesion characteristics as compared to the outer surface of thermoplastic component parts made from semi-crystalline resins. Paint, primer, and other substances used to fill surface pitting or defects adheres more readily to this amorphous resin as compared to semi-crystalline resins. Thus, primer, paint, and other finishing or defect-filling materials can be easily applied to a composite part outfitted with the thermoplastic surfacer 132 without necessitating additional processing steps such as etching or the like.
Although
In this embodiment, rather than implementing a vacuum assist table 114 to embed the milled fibers 218 and/or other fillers 220 into the matrix resin fleece 212, the tooling 210 uses an electrostatic table 214. The electrostatic table 214 includes an electricity source 213 having a positive lead 215 electrically connected to the powder applicators 216 in order to make the fillers 218, 220 positively charged and a negative lead 217 attached to a working surface of the table 214 to make the table 214 negatively charged. In this regard, the positively charged fillers 218, 220 will be attracted to the negatively charged table 214 and become embedded in the matrix resin fleece 212 passing therebetween. The tooling 210 may also include a vibration table 222 in order to more fully embed the fillers 218, 220 into the matrix resin fleece 212, which is substantially similar to the vibration table 122 discussed in connection with the tooling 110.
Similar to the filler-laden fleece 112 discussed above, the filler-laden fleece 212 (i.e., the matrix resin fleece 212 embedded with the milled fibers 218, other fillers 220, and/or binder spray 224) passes through heaters 226 in order to raise the temperature of the thermoplastic resin to a workability or melting point, and then combined with a lightning strike protection mesh or foil 228, which is substantially similar to the lightning strike protection mesh or foil 128 discussed above. In this embodiment, however, the lightning strike protection mesh or foil 228 is combined with the filler-laden fleece 212 prior to the fleece 212 entering the heaters 226. This in turn raises the temperature of both the fleece 212 and the mesh or foil 128 prior to the components being pressed together via calendaring rolls 230, which are substantially similar to calendaring rolls 130 discussed above. Heating the mesh or foil 128 in addition to the filler-laden fleece 212 may reduce stresses and thus defects that may otherwise be caused during cooling of the thermoplastic resin because the heated mesh or foil 228 also cools and thus contracts as the thermoplastic resin cools and contracts. Moreover, the elevated temperature of the mesh or foil 128 may provide for a better bond between the mesh or foil 128 and the fleece 112 during the calendaring process. However, in other embodiments the lightning strike protection mesh or foil 228 may be applied to the filler-laden fleece 212 after the fleece 212 passes through the heaters 226, in a similar manner as described in connection with tooling 110.
Once the calendaring rolls 230 press the lightning strike protection mesh or foil 228 into the filler-laden fleece 212 and the thermoplastic resin thereof cools, the thermoplastic surfacer 232 is fully formed. Optionally, the thermoplastic surfacer 232 may thereafter be taken up on a takeup roll 234 or similar for later application to a composite part such as a fuselage, wing, or similar component.
In this embodiment, the thermoplastic surfacer 332 includes a veil 327 between the lightning strike protection mesh or foil 328 and filler-laden fleece 312. The veil 327 may be a layer of glass or light fabric or the like used for galvanic isolation when the lightning strike protection mesh or foil 328 is comprised of aluminum in order to reduce or eliminate corrosion of the mesh or foil 328 that might otherwise occur due to a galvanic reaction between the mesh or foil 328 and the carbon fibers provided in the thermoplastic composite part to which the thermoplastic surfacer 332 is ultimately applied. In embodiments in which the veil 327 is utilized the milled fibers 118, 218 may be eliminated, as shown in
The veil 327 is spooled onto the matrix resin fleece 312 prior to the lightning strike protection mesh or foil 328 in order to provide an ultimate electric barrier between the mesh or foil 328 and the carbon fibers. Although in the depicted embodiment the veil 327 and the mesh or foil 328 are spooled onto the filler-laden fleece 312 prior to the heaters 326, in other embodiments one or both of the veil 327 and the lightning strike protection mesh or foil 328 may be spooled onto the filler-laden fleece 312 after the fleece 312 has passed through the heaters 326. Finally, the veil 327 and mesh or foil 328 are thereafter compressed into the heated fleece 312 via the calendaring rolls 330 forming the thermoplastic surfacer 332, and optionally spooled onto a takeup roll 334 for later use, as discussed.
In some embodiments, the width of the lightning strike protection mesh or foil 128, 228, 328 being applied to the filler-laden fleece 112, 212, 312 may be smaller than or equal to the width of the filler-laden fleece 112, 212, 312. As used herein, “length” refers to the substantially continuous dimension of the fleece 112, 212, 312 as is comes off the roll (corresponding to the horizontal direction as viewed in
This may be more readily understood with reference to
The thermoplastic surfacers 132a, 132b each include a filler-laden fleece 112a, 112b having a first width, w1, and a lightning strike protection mesh or foil 128a, 128b having a second width, w2, which is greater than w1. Because w2 is greater than w1, the mesh or foil 128 overhangs the fleece 112 forming a mesh or foil overhang 410a, 410b. When the thermoplastic surfacers 132a, 132b are applied to a composite part or the like such that the adjacent passes of the fleece 112a, 112b abut each other, the mesh or foil overhang 410a of the first surfacer 132a overlaps the second surfacer 132b forming an overlapping region 412. Put another way, the protruding mesh or foil 128a on one edge of the first surfacer 132a can be covered by the next pass of the second surfacer 132b, creating direct electrical contact between the rows of the thermoplastic surfacer 132a, 132b. In this regard, there is no threat of a residual gap being formed in the mesh or foil 128 when the surfacer 132 is applied to a composite part in strips. More particularly, the lightning strike protection mesh or foil 128a of the first surfacer 132a forms a electric bond with the lightning strike protection mesh or foil 128b of the second surfacer 132b due to the overlap 412, ensuring electrical continuity between the surfacers 132a, 132b. Thus, when present in a potential lightning strike zone on an aircraft of the like, the overlapping mesh or foils 128a, 128b ensure that any lightning strike is effectively routed across the surface of the aircraft from an entry point to an exit point without damaging the composite skin of the aircraft that may otherwise occur if there is a break between successive mesh or foils.
Applying a thermoplastic surfacer made in accordance with aspects of the invention such as the surfacers 132, 232, or 332 or similar may beneficially provide automatic defect filling during consolidation of a lightning strike protected part. This may be more readily understood with reference to
During consolidation, the composite part 511 is heated while a negative pressure (i.e., vacuum) is applied to the vacuum bag 517 via a vacuum 516. As the air is removed from the vacuum bag 517, the vacuum bag 517 exerts pressure on the unconsolidated laminate 514 forcing it to compress, or consolidate, after which the composite part 511 is ready for painting and/or assembly into the aircraft. Because the stiffener 512 is preconsolidated, however, it does not further compress during the consolidation process. And because the laminate portion 514, 515 thus shrinks during consolidation while the stiffener does not, sometimes defects can form in the composite part 511 during the consolidation process, such as a vacuum bag induced defect 524 shown in
Traditionally, these defects must be filled or otherwise repaired following the consolidation process, which can be time-consuming. However, the surfacer 522 made according to aspects of the invention may serve to self-fill these defects, resulting in a smooth outer surface of the composite part 511 without further finishing and defect repair. More particularly, during the consolidation process resin from the surfacer 522 flows from an area of high pressure to any areas of low pressure and thus into any defects such as the vacuum bag induced defect 524, forming a resin pocket 526 that fills the void and otherwise prevents a noticeable defect on the outer surface of the consolidated laminate 515. Moreover, the resin pocket 526 will include fillers and fibers 528 (such as, e.g., the milled fibers 118, 218 or other fillers 120, 220, 320) thereby reducing shrinkage of the resin pocket 526, reducing residual tensile stresses in the resin pocket 526, and otherwise providing increased tensile strength and crack resistance to the resin pocket 526. Still more, because the resin and any fillers and fibers 528 included therein fills the defect 524, the lightning strike protection mesh or foil 530 of the surfacer 522 does not get pulled into the defect. This eliminates possible damage to the mesh or foil 530 that may otherwise occur if the resin did not fill the defect 524.
At step 620 the matrix resin fleece is embedded with any desired fillers such as milled fibers or the like via one more powder applicators such as applicators 116, 216, 316. These fillers can include, but are not limited to, nano clay, talc, calcium carbonate, Kaolin, Wollastonite, mica, other fillers widely used with polymers, nanotubes, nanonickel strands, highly conductive fillers, and milled fibers such as glass, carbon, or other suitable fibers. Moreover, optionally a vacuum assist table, electrostatic table, vibration table, and/or other electronically or mechanically controlled tooling can be used at step 620 to assist embedding the fibers into the matrix resin fleece.
At step 630 a binder spray is applied to the matrix resin fleece. As should be appreciated from the above discussion in connection with
At step 640 a lightning strike protection mesh or foil is applied to the filler-laden matrix resin fleece. This may be any lightning strike protection mesh or foil typically used in lightning strike zones on an aircraft fuselage or wings or the like. In embodiment in which carbon fibers are used in the composite part to which the surfacer is to be applied, a veil may also be applied at step 640. In such embodiments the veil is placed between the lightning strike protection mesh or foil and the filler-laden fleece in order to mitigate corrosion due to the galvanic reaction between the metallic mesh or foil and the carbon fibers. Moreover, and as discussed in connection with
At step 650 the filler-laden mesh or foil is heated so that at least the surface of fleece reaches the melt temperature. Optionally, the matrix resin fleece can be heated throughout such that all of the thermoplastic resin reaches the melt temperature. Moreover, in some embodiments the filler-laden fleece is heated prior to the addition of the lightning strike protection mesh or foil and optional veil (that is, in some embodiments step 650 is performed prior to step 640), while in other embodiments the lightning strike protection mesh or foil and optional veil are applied to the filler-laden mesh or foil and optional mesh or foil prior to the heating step such that the mesh or foil, optional veil, and filler-laden fleece are all heated at step 650.
At step 660 the lightning strike protection mesh or foil and optional veil are compressed into the filler-laden fleece such as by, without limitation, calendaring the lightning strike protection mesh or foil and optional veil into the filler-laden fleece as discussed above. Once fully cooled, the surfacer is complete and ready for applying to a composite thermoplastic part. Optionally, the completed thermoplastic surfacer can be spooled onto a takeup spool such as spool 134, 234, 334 for storage or transportation.
At step 720 a thermoplastic surfacer such as the thermoplastic surfacer 132, 232, 332 discussed above is applied to an outer-facing surface of the composite part. Again, the thermoplastic surfacer is drapable and thus can seamlessly be applied to the thermoplastic composite part notwithstanding any complex contours of the part. In some embodiments the thermoplastic surfacer is applied piecewise to a large composite part, with each length of surfacer abutting a neighboring surfacer. In embodiments in which the lightning strike protection mesh or foil overhangs the edge of the matrix resin fleece such as the embodiments shown in
At step 730 the composite part with surfacer applied thereto is placed in a consolidation tool. In some embodiments, this may include placing the outward-facing surface of the part (that is, the surface of the part containing the surfacer) against a similarly contoured consolidation tool and placing a vacuum bag around the part. In some embodiments, open edges of the vacuum bag may be sealed to the consolidation tool using a sealant tape or the like forming an airtight seal.
At step 740 the unconsolidated portion of the composite part is consolidated by applying heat and/or a negative pressure to the composite part. For example, a vacuum may be used to remove the air from the inside of the bag and thus apply a pressure to the unconsolidated part while the part is heated to a melting temperature of the thermoplastic resin used in the composite part and/or the surfacer. As discussed in connection with
At step 750, any defects that are formed in the outer-facing surface of the composite part can be self-filled during the consolidation process by the thermoplastic surfacer. More particularly, resin from the surfacer flows into the defect forming a resin pocket such as surfacer resin pocket 526 discussed above, thereby filling and repairing the defect. Moreover, in embodiments in which the surfacer includes milled fibers or other fillers, the milled fibers and/or fillers flow into the resin pocket with the thermoplastic resin thus providing increased strength to the otherwise resin-rich area.
Finally, at step 760 the composite part is cooled and is then ready for assembly onto an aircraft of the like. Optionally, the composite part with the surfacer thereon is painted at step 760. As discussed, because the surfacers created according to aspects of the invention include increased paint adhesion properties as compared to known thermoplastic component parts due to the use of an amorphous thermoplastic resin, the finished composite part can be primed and painted at step 760 without requiring the slow and expensive surface treatment processed such as plasma or corona etching to achieve a sufficient surface roughness for paint adhesion.
Although the invention has been described with reference to the embodiments illustrated in the attached drawings, it is noted that equivalents may be employed without departing from the scope of the invention as recited in the claims.
This application is a continuation of and claims priority to U.S. application Ser. No. 16/905,318 filed on Jun. 18, 2020, now U.S. Pat. No. 11,504,925, and entitled “Lightning Strike Protection Surfacer and Method of Manufacturing the Same,” which is incorporated by reference herein in its entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5370921 | Cedarleaf | Dec 1994 | A |
| 6485589 | Johnson et al. | Nov 2002 | B1 |
| 8709189 | Schaaf | Apr 2014 | B2 |
| 8962130 | Kruckenberg et al. | Feb 2015 | B2 |
| 9550330 | Pratte et al. | Jan 2017 | B2 |
| 9623984 | Steinwandel | Apr 2017 | B2 |
| 9676961 | Sang | Jun 2017 | B2 |
| 11027856 | Sang | Jun 2021 | B2 |
| 11504925 | Wadsworth | Nov 2022 | B2 |
| 20200307162 | Remy | Oct 2020 | A1 |
| 20210367416 | Hebert | Nov 2021 | A1 |
| Number | Date | Country |
|---|---|---|
| 2018063970 | Apr 2018 | WO |
| 2019018754 | Jan 2019 | WO |
| Number | Date | Country | |
|---|---|---|---|
| 20230086362 A1 | Mar 2023 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16905318 | Jun 2020 | US |
| Child | 17989931 | US |