This invention relates generally to lightweight porous fiber reinforced thermoplastic polymer sheets, and more particularly to lightweight porous fiber reinforced thermoplastic polymer sheets that include reinforcing skins.
Lightweight porous fiber reinforced thermoplastic sheets have been described in U.S. Pat. Nos. 4,978,489 and 4,670,331 and are used in numerous and varied applications in the product manufacturing industry because of the ease of molding the fiber reinforced thermoplastic sheets into articles. Known techniques, for example, thermo-stamping, compression molding, vacuum forming, and thermoforming have been used to successfully form articles from fiber reinforced thermoplastic sheets.
Tougher automotive fuel economy standards are requiring an overall vehicle weight reduction to meet these standards Traditional vehicle seat back systems are made from stamped steel or blow molded plastics. Steel stamping dies are a huge capital investment. Although a steel seat back is thin, the steel material is very dense compared with polymers. Steel seat back can range from about 3 lbs to 6 lbs. The steel seat back is spot welded to the seat frame and structural reinforcements are attached to the comers of the steel seat back to prevent and bending of the steel when a load is applied. Blow molded seat backs are lighter than steel seat backs, but are bulky and can be 50 mm or greater in thickness. Blow molded plastic seat backs are attached mechanically to the seat frame.
In one aspect, a multi-layered fiber reinforced sheet for automotive vehicle interior structural components is provided. The multi-layered fiber reinforced sheet includes a permeable fiber reinforced thermoplastic core layer having a first surface and a second surface. The core layer includes a plurality of reinforcing fibers bonded together with a thermoplastic resin, and has a density of about 0.1 gm/cc to about 1.8 gm/cc. The multi-layered fiber reinforced sheet also includes at least one first reinforcing skin applied to the first surface of the core layer, and at least one second reinforcing skin applied to the second surface of the core layer. Each first and second reinforcing skin includes a matrix of reinforcing fibers and a thermoplastic resin wherein the matrix of reinforcing fibers applied to the first surface are arranged in a bi-directional orientation and the matrix of reinforcing fibers applied to the second surface are arranged in a bi-directional orientation.
In another aspect, an automotive vehicle interior structural component formed from a multi-layered fiber reinforced material is provided. The multi-layered fiber reinforced sheet includes a permeable fiber reinforced thermoplastic core layer having a first surface and a second surface. The core layer includes a plurality of reinforcing fibers bonded together with a thermoplastic resin, and has a density of about 0.1 gm/cc to about 1.8 gm/cc. The multi-layered fiber reinforced sheet also includes at least one first reinforcing skin applied to the first surface of the core layer, and at least one second reinforcing skin applied to the second surface of the core layer. Each first and second reinforcing skin includes a matrix of reinforcing fibers and a thermoplastic resin wherein the matrix of reinforcing fibers applied to the first surface are arranged in a bi-directional orientation and the matrix of reinforcing fibers applied to the second surface are arranged in a bi-directional orientation.
In another aspect, a method of making an automotive vehicle interior structural component is provided. The method includes forming a permeable fiber reinforced thermoplastic core layer having a first surface and a second surface. The core layer includes a plurality of reinforcing fibers bonded together with a thermoplastic resin, and has a density of about 0.1 gm/cc to about 1.8 gm/cc. The method also includes positioning at least one first reinforcing skin on the first surface, positioning at least one second reinforcing skin on the second surface, attaching the at least one first reinforcing skin to the first surface, attaching the at least one second reinforcing layer to the second surface to form a multi-layered fiber reinforced sheet, and molding the multi-layered fiber reinforced sheet into a predetermined shape. Each first and second reinforcing skin includes a matrix of reinforcing fibers and a thermoplastic resin wherein the matrix of reinforcing fibers applied to the first surface are arranged in a bi-directional orientation and the matrix of reinforcing fibers applied to the second surface are arranged in a bi-directional orientation.
A formable lightweight composite thermoplastic sheet having reinforcing skins for making automotive vehicle interior structural components, for example, seat backs, is described below in detail. The composite thermoplastic sheet can be used to reduce the weight of load bearing interior components up to about 60% without sacrificing strength over known steel designs. The composite sheet can be thermoformed at low pressures which permit cycle times of about 60 seconds or less and mild temperatures of about 160° F. A low pressure forming process utilizes, for example, match mold aluminum tooling instead of a steel stamping press used for known steel designs. The thickness of the composite thermoplastic sheet in one embodiment is about 2 mm to about 10 mm, and in another embodiment about 2 m to about 4 mm, which permits decreased packaging space to a seatback which increases leg room and/or storage space in an automotive vehicle.
Referring to the drawings,
Core 12 is formed from a web made up of open cell structures formed by random crossing over of reinforcing fibers held together, at least in part, by one or more thermoplastic resins, where the void content of porous core 12 ranges in general between about 1% and about 95% and in particular between about 30% and about 80% of the total volume of core 12. In another embodiment, porous core 12 is made up of open cell structures formed by random crossing over of reinforcing fibers held together, at least in part, by one or more thermoplastic resins, where about 40% to about 100% of the cell structure are open and allow the flow of air and gases through. Core 12 has a density in one embodiment of about 0.1 gm/cc to about 1.8 gm/cc and in another embodiment about 0.3 gm/cc to about 1.0 gm/cc. Core 12 is formed using known manufacturing process, for example, a wet laid process, an air laid process, a dry blend process, a carding and needle process, and other known process that are employed for making non-woven products. Combinations of such manufacturing processes are also useful.
Core 12 includes about 20% to about 80% by weight of reinforcing fibers having an average length of between about 5 mm and about 50 mm, and about 20% to about 80% by weight of a wholly or substantially unconsolidated fibrous or particulate thermoplastic materials, where the weight percentages are based on the total weight of core 12 In another embodiment, core 12 includes about 30% to about 55% by weight of reinforcing fibers. In another embodiment, core 12 includes reinforcing fibers having an average length of between about 5 mm and about 25 mm. Suitable fibers include, but are not limited to metal fibers, metalized inorganic fibers, metalized synthetic fibers, glass fibers, graphite fibers, carbon fibers, ceramic fibers, mineral fibers, basalt fibers, inorganic fibers, aramid fibers, kenaf fibers, jute fibers, flax fibers, hemp fibers, cellulosic fibers, sisal fibers, coir fibers, and mixtures thereof
In the exemplary embodiment, reinforcing fibers having an average length of about 5 mm to about 50 mm is added with thermoplastic powder particles, for example polypropylene powder, to an agitated aqueous foam which can contain a surfactant. The components are agitated for a sufficient time to form a dispersed mixture of the reinforcing fibers and thermoplastic powder in the aqueous foam. The dispersed mixture is then laid down on any suitable support structure, for example, a wire mesh, and then the water is evacuated through the support structure forming a web. The web is dried and heated above the softening temperature of the thermoplastic powder. The web is then cooled and pressed to a predetermined thickness to produce composite core 12 having a void content of between about 1 percent to about 95 percent.
The web is heated above the softening temperature of the thermoplastic resins in core 12 to substantially soften the plastic materials and is passed through one or more consolidation devices, for example calendaring rolls, double belt laminators, indexing presses, multiple daylight presses, autoclaves, and other such devices used for lamination and consolidation of sheets and fabrics so that the plastic material can flow and wet out the fibers. The gap between the consolidating elements in the consolidation devices are set to a dimension less than that of the unconsolidated web and greater than that of the web if it were to be fully consolidated, thus allowing the web to expand and remain substantially permeable after passing through the rollers. In one embodiment, the gap is set to a dimension about 5% to about 10% greater than that of the web if it were to be fully consolidated. A fully consolidated web means a web that is fully compressed and substantially void free. A fully consolidated web would have less than 5% void content and have negligible open cell structure.
Particulate plastic materials include short plastics fibers which can be included to enhance the cohesion of the web structure during manufacture. Bonding is affected by utilizing the thermal characteristics of the plastic materials within the web structure. The web structure is heated sufficiently to cause the thermoplastic component to fuse at its surfaces to adjacent particles and fibers.
In one embodiment, individual reinforcing fibers should not on the average be shorter than about 5 millimeters, because shorter fibers do not generally provide adequate reinforcement in the ultimate molded article. Also, reinforcing fibers should not on average be longer than about 50 millimeters since such fibers are difficult to handle in the manufacturing process.
In one embodiment, in order to confer structural strength the reinforcing fibers have an average diameter between about 7 and about 22 microns. Fibers of diameter less than about 7 microns can easily become airborne and can cause environmental health and safety issues. Fibers of diameter greater than about 22 microns are difficult to handle in manufacturing processes and do not efficiently reinforce the plastics matrix after molding.
In one embodiment, the thermoplastics material used to form core 12 is, at least in part, in a particulate form. Suitable thermoplastics include, but are not limited to, polyolefins, including polymethylene, polyethylene, and polypropylene, polystyrene, acrylonitrylstyrene, butadiene, polyesters, including polyethyleneterephthalate, polybutyleneterephthalate, and polypropyleneterephthalate, polybutyleneterachlorate, and polyvinyl chloride, both plasticised and unplasticised, acrylics, including polymethyl methacrylate, and blends of these materials with each other or other polymeric materials. Other suitable thermoplastics include, but are not limited to, polyarylene ethers, acrylonitrile-butylacrylate-styrene polymers, amorphous nylon, as well as alloys and blends of these materials with each other or other polymeric materials. It is anticipated that any thermoplastics resin can be used which is not chemically attacked by water and which can be sufficiently softened by heat to permit fusing and/or molding without being chemically or thermally decomposed.
The thermoplastic particles need not be excessively fine, but particles coarser than about 1.5 millimeters are unsatisfactory in that they do not flow sufficiently during the molding process to produce a homogenous structure. The use of larger particles can result in a reduction in the flexural modulus of the material when consolidated.
Referring also to
The reinforcing fibers described above that are suitable for use in making core layer 12 are also suitable in reinforcing skins 18 and 20. Similarly, the thermoplastic resins described above that are suitable for core layer 12 are also suitable in reinforcing skins 18 and 20. Reinforcing skins 18 and 20 can be attached to core layer 12 during the manufacturing process of core layer 12 or reinforcing skins 18 and 20 an be attached prior to forming a automotive vehicle structural component, for example, a seat back. Reinforcing skins 18 and 20 can be laminated to core 12, sonic welded to core 12, or simply laid across core 12 before the structural component forming process.
In one exemplary embodiment, to form a vehicle structural component, composite thermoplastic sheet 10 is heated to a temperature sufficient to melt the thermoplastic resin. Heated composite thermoplastic sheet 10 is positioned in a mold, for example a matched aluminum mold, heated to about 160° F. and stamped into the desired shape using a low pressure press. In other embodiments, composite thermoplastic sheet 10 can be molded into various automotive vehicle interior structural components using any method known in the art including, for example, thermal forming, thermal stamping, vacuum forming, compression forming, and autoclaving.
In another embodiment, decorative layer 22 is applied to second reinforcing skin 20 by any known technique, for example, lamination, adhesive bonding, and the like. Decorative layer 22 is formed from a thermoplastic film of, for example, polyvinyl chloride, polyolefin, thermoplastic polyester, thermoplastic elastomer, or the like. In another embodiment, decorative layer 22 is a multilayered structure that includes a foam core formed from, for example, polypropylene, polyethylene, polyvinyl chloride, polyurethane, and the like. A fabric is bonded to the foam core, for example, woven fabrics made from natural and synthetic fibers, organic fiber nonwoven fabric after needle punching or the like, raised fabric, knitted goods, flocked fabric and the like. In another embodiment the fabric is bonded to the foam core with a thermoplastic adhesive, including pressure sensitive adhesives and hot melt adhesives, for example, polyamides, modified polyolefins, urethanes and polyolefins.
While the invention has been described in terms of various specific embodiments, those skilled in the art will recognize that the invention can be practiced with modification within the spirit and scope of the claims.