The present invention relates to: a lining material for a conduit; and a method for lining a conduit.
To repair an existing aging conduit such as a water supply or sewer pipe, a pipe for agricultural water, or a gas pipe, there have been conventionally known methods as follows: a tubular lining material containing a liquid curable resin with reinforced fibers is installed on an inner surface of the existing conduit, and then the liquid curable resin is cured, thereby to construct, in the conduit, a robust lining structure including a fiber reinforced resin.
In a method described in Patent Literature 1, a base material sheet is used for a lining material. The base material sheet is formed of non-woven fabrics of organic fibers and woven fabrics made of glass yarns, in which non-woven and woven fabrics are laid on one another and jointed by needlepunching, and the base material sheet is impregnated with a liquid thermosetting resin. The base material sheet is rolled into a tubular form, and overlapping both ends of the base material sheet in its circumferential direction, that is, the overlapping both circumferential ends (an overlapping portion) are jointed to each other by a hot melt adhesive, to form the lining material. An outer surface of the lining material is composed of an impermeable tubular woven fabric. In the method described in Patent Literature 1, first, the tubular lining material is installed in a conduit, while being inverted so as to be inside out by applying compressed air (installation step). Then, a heating medium such as heated air or steam is supplied to the inside of the lining material, and thereby the lining material is pressurized from the inside thereof while being heated, to expand the diameter of the lining material (diameter expansion step). That cures the liquid thermosetting resin included in the lining material which is in close contact with the conduit, to form the robust lining structure on the inner surface of the conduit.
Patent Literature 1: Japanese Unexamined Patent Publication No. 086386/2012 (Tokukai 2012-086386)
An object of the present invention is to prevent peeling at overlapping both circumferential ends (overlapping portion) of a lining material installed in a conduit.
According to a first aspect of the invention, a lining material for a conduit, the lining material being inverted to be inside out to line the conduit, includes: an impermeable layer; a lining material main body provided inside the impermeable layer, the lining material main body made into a tubular form by rolling a base material sheet, with its both circumferential ends overlapping each other; and a tubular member provided inside the lining material main body.
In this aspect, the tubular member is provided inside the lining material main body, before inversion. Therefore, when the lining material is installed in the conduit while being inverted to be inside out, that is, while the lining material main body and the tubular member are inverted, the tubular member to be positioned outside prevents the overlapping both circumferential ends of the lining material main body from contacting an inner surface of the conduit. This prevents peeling at the overlapping both circumferential ends of the lining material main body, especially in a bending portion of the conduit where the lining material tries to rotate in the circumferential direction.
According to a second aspect of the invention, the lining material of the first aspect is arranged such that a diameter of the tubular member is larger than a diameter of the lining material main body.
In this aspect, the diameter of the tubular member is larger than the diameter of the lining material main body, and therefore, it is possible to invert the lining material to be inside out, that is, to invert the lining material main body and the tubular member, and the tubular member does not interfere with diameter expansion at the both circumferential ends of the inverted lining material main body.
According to a third aspect of the invention, the lining material of the second aspect is arranged such that: the tubular member has a slack portion; and the slack portion does not contact an overlapping portion where both circumferential ends of the lining material main body overlap each other.
In this aspect, the slack portion of the tubular member does not contact the overlapping portion where the both circumferential ends of the lining material main body overlap each other. Therefore, as shown in
According to a fourth aspect of the invention, the lining material of any one of the first to third aspects is arranged such that the lining material main body and the tubular member are releasably jointed to each other.
In this aspect, the lining material main body and the tubular member are releasably jointed together into one member, and therefore, no shift occurs between the lining material main body and the tubular member when inverted. In other words, the lining material main body is not moved by a force applied to the tubular member, and this ensures prevention of peeling at the overlapping both circumferential ends of the lining material main body due to the tubular member when the tubular member is inverted.
According to a fifth aspect of the invention, the lining material of the fourth aspect is arranged such that inside the lining material main body, the tubular member is releasably jointed to an inner surface of an overlapping portion where both circumferential ends of the lining material main body overlap each other.
In this aspect, inside the lining material main body, the tubular member is releasably jointed to the inner surface of the overlapping portion where the both circumferential ends of the lining material main body overlap each other. Therefore, in the process of lining, it is possible to prevent peeling by the tubular member at the overlapping portion of the lining material main body, where the both circumferential ends thereof overlap each other, even in the case where the conduit has a complicated structure with a larger number of bending portions.
According to a sixth aspect of the invention, the lining material of any one of the first to fifth aspects is arranged such that the tubular member is a tubular woven fabric.
In this aspect, the tubular member is a tubular woven fabric, which has high permeability of the liquid thermosetting resin to be impregnated into the lining material main body, and which reduces the possibility that the tubular member is deformed. Therefore, the lining process is performed stably.
According to a seventh aspect of the invention, the lining material of the sixth aspect is arranged such that the tubular woven fabric has no seam in an axial direction of the tubular woven fabric.
In this aspect, since the tubular member has no seam in its axial direction, that is, which has no joint in the axial direction, its elongation in the circumferential direction is uniform. This facilitates smooth inside-out inversion of the lining material.
According to an eighth aspect of the invention, the lining material of any one of the first to seventh aspects is arranged such that the impermeable layer includes a tubular woven fabric which is woven from synthetic yarns, an outer surface of the tubular woven fabric being coated with a coating of a thermoplastic resin.
In this aspect, the impermeable layer is formed of: the tubular woven fabric; and the thermoplastic resin coating on the outer surface of the tubular woven fabric. That is, the tubular woven fabric is reinforced by the coating. This enables inversion of the lining material to be performed stably.
According to a ninth aspect of the invention, a method for lining a conduit having a bending portion including: impregnating the lining material described in any one of the first to eighth aspects with a curable resin; and subsequently inverting the lining material to line the conduit.
In this aspect, the lining material main body and the tubular member provided inside the lining material main body are inverted together to line the conduit. Therefore, the tubular member to be positioned outside prevents the overlapping portion of the lining material main body from contacting the inner surface of the conduit, when inverted. This prevents peeling at the overlapping portion of the lining material main body, especially in the bending portion of the conduit.
In the present invention, the tubular member is provided inside the lining material main body, before inversion. Therefore, when the lining material is installed in the conduit while being inverted to be inside out, that is, while the lining material main body and the tubular member are inverted, the tubular member to be positioned outside prevents the overlapping both circumferential ends of the lining material main body from contacting the inner surface of the conduit. This prevents peeling at the overlapping both circumferential ends of the lining material main body, especially in a bending portion of the conduit where the lining material tries to rotate in the circumferential direction.
The following describes an embodiment of the present invention.
First, the structure of the lining material 1 will be described. The lining material 1 includes a lining material main body 2.
As shown in
The both circumferential ends of the base material sheet 10 rolled into the tubular form are jointed to each other by a hot melt adhesive 6 with the both ends overlapping each other, to form the lining material main body 2.
Note that, as for the firmness of the joint, it is only required that the both circumferential ends of the lining material main body 2 are releasably jointed to prevent shifting relative to each other when the lining material main body 2 is inserted into a conduit P while being inverted. As will be described later, when the lining material main body 2 is heated in a diameter expansion step which is conducted after the lining material main body 2 (the lining material 1) is installed in the conduit P, the hot melt adhesive 6 is softened and thereby the jointed both ends are released.
The tubular woven fabric 3 shown in
The lining material main body 2 is produced through the following processes, for example. First, glass roving is woven on a plain weaving machine, into the woven glass roving fabrics 5. Then, the woven glass roving fabrics 5 and the non-woven fabrics 4 are alternately laid on one another and jointed together by needlepunching, and this lamination is cut to form the base material sheet 10 having a predetermined width.
The lining material 1 of this embodiment further includes a tubular member 8 which is provided inside the lining material main body 2 before inverted. The tubular member 8 is a tubular woven fabric which has no seam in its axial direction (its longitudinal direction). To form the tubular member 8, a yarn is circularly woven on a circular weaving machine, and this makes the tubular member 8 seamless in its circumferential direction. Then, as shown in
The specification of the tubular member 8 for a conduit having an inner diameter of 700 mm, for example, is as follows.
(Structure) Warp: polyester yarn, 1100T/3×1500
(Initial Diameter) 700 mm
(Thickness of Woven Fabric) 0.9 mm
After the tubular member 8 is disposed on the lining material main body 2, the base material sheet 10 is rolled into the tubular form. Then, the hot melt adhesive 6 is applied to a surface of one circumferential end of the base material sheet 10, and the other circumferential end of the sheet 10 is laid on the one end to joint the both ends to each other, thereby to form the lining material main body 2. In this process, the tubular member 8 is disposed so that, as shown in
The thus produced tubular lining material 1 is impregnated with a liquid thermosetting resin. In this process, the liquid resin is injected into the inside of the innermost tubular member 8, to impregnate, with the liquid thermosetting resin, the whole of the tubular woven fabric 3, the lining material main body 2, and the tubular member 8, which are positioned inside the coating 7. To impregnate these with the liquid resin, there may be adopted a general way in which the lining material 1 into which the liquid thermosetting resin has been injected is squeezed using a nip roller. However, for more uniform impregnation, it is preferable to perform the following process before squeezing on the nip roller: injecting a liquid resin having a lower viscosity than that of generally used resins (i.e., a liquid resin dripping at normal temperature); and then conveying the lining material main body 2, into which the liquid resin has been injected, to a higher position. With this, the lining material main body 2 is uniformly impregnated with the liquid resin while extra liquid resin attached to the lining material main body 2 is gravitationally removed. Further, as compared with the way in which the lining material main body 2 is squeezed using the nip roller only, the period of time required for the resin impregnation process is shortened. Further, it is effective to depressurize the inside of the lining material 1 in addition to the above.
Note that, if the lining material 1 is conveyed after impregnated with the resin, the low-viscous liquid resin may drip. Therefore, it is preferable to conduct a viscosity increasing process (e.g., heating, cooling, or the like) depending on the type of the liquid resin to increase the viscosity, before the lining material 1 is conveyed.
The following describes a process of repairing the existing conduit P using the above-described lining material 1. To repair the conduit P using the lining material 1, first, the lining material 1 is installed in the conduit P to be repaired while being inverted to be inside out (installation step). Then, the diameter of the lining material main body 2 of the lining material 1 installed in the conduit P is expanded by circumferentially sliding the both circumferential ends of the lining material main body 2, on each other (diameter expansion step). In the above diameter expansion step, the lining material main body 2 is heated and pressurized from the inside thereof, to cure the liquid resin impregnated into the lining material main body 2 and to expand the diameter of the lining material main body 2.
(Installation Step)
First, the installation step will be described.
As shown in
Under the condition shown in
In this inversion method, compressed air advances the leading end portion of the inverted lining material 1 along the conduit P, and this makes it relatively easier to install the lining material 1 in the conduit P having a bending portion. Further, as described above, in the installation step, the both circumferential ends of the lining material main body 2 are jointed (releasably jointed) to each other by the hot melt adhesive 6, and this prevents the both ends from shifting relative to each other and thereby expanding the lining material main body 2 during the inside-out inversion of the lining material 1.
(Diameter Expansion Step)
Next, description will be given for the diameter expansion step.
In this diameter expansion step, the lining material 1 is heated to the setting temperature of the thermosetting resin (for example, 80 to 100 degrees Celsius). In this process, the hot melt adhesive 6 releasably jointing the both circumferential ends of the lining material main body 2 is softened, and thereby its adhesion is decreased, which allows the both ends of the lining material main body 2 to circumferentially slide on each other. Note that the type of the hot melt adhesive 6 may be determined appropriately depending on the setting temperature of the liquid thermosetting resin. Simultaneously with this heating, the lining material main body 2 is pressurized from the inside thereof, and this causes the both circumferential ends of the lining material main body 2 to circumferentially slide on each other, to increase the diameter of the lining material main body 2. As a result, the lining material main body 2 is pressed to the inner surface of the conduit P to be brought into close contact with the inner surface, and in this state, the thermosetting resin is thermally set. Thus, on the inner surface of the conduit P, there is formed a robust lining structure in which the thermosetting resin is reinforced by the high-strength woven glass roving fabrics 5.
As described above, the lining material 1 of this embodiment includes the tubular member 8 which is provided inside the lining material main body 2 before inverted. The tubular member 8 to be positioned outside prevents the overlapping both circumferential ends (overlapping portion 2a) of the lining material main body 2 from contacting the inner surface of the conduit P when the lining material 1 is installed in the conduit P while being inverted to be inside out, that is, while the tubular woven fabric 3, the lining material main body 2, and the tubular member 8 are inverted, in the installation step. This prevents peeling at the overlapping both circumferential ends of the lining material main body 2, especially in the bending portion.
Further, the diameter of the tubular member 8 is larger than the diameter of the lining material main body 2, and therefore, it is possible to invert the lining material 1 to be inside out, that is, to invert the lining material main body 2 and the tubular member 8, and the tubular member 8 does not interfere with diameter expansion at the circumferential both ends (overlapping portion 2a) of the inverted lining material main body 2.
Moreover, the slack portion A of the tubular member 8 does not contact the overlapping portion 2a where the both circumferential ends of the lining material main body 2 overlap each other. Therefore, as shown in
In addition, the lining material main body 2 and the tubular member 8 are releasably jointed together into one member, and therefore, no shift occurs between the lining material main body 2 and the tubular member 8 when inverted. In other words, the lining material main body 2 is not moved by a force applied to the tubular member 8, and this ensures prevention of peeling at the overlapping both circumferential ends of the lining material main body 2 due to the tubular member 8 when the tubular member 8 is inverted.
Moreover, inside the lining material main body 2, the tubular member 8 is releasably jointed to the inner surface of the overlapping portion 2a where the both circumferential ends of the lining material main body 2 overlap each other. Therefore, in the process of lining, it is possible to prevent peeling by the tubular member 8 at the overlapping portion 2a of the lining material main body 2, where the both circumferential ends thereof overlap each other, even in the case where the conduit P has a complicated structure with a larger number of bending portions.
In addition, the tubular member 8 is the tubular woven fabric, which has high permeability of the liquid thermosetting resin to be impregnated into the lining material main body 2, and which reduces the possibility that the tubular member 8 is deformed. Therefore, the lining process is performed stably. Further, when an open weave fabric is used as the tubular member 8, the permeability of the liquid thermosetting resin into the tubular member 8 is further increased. Furthermore, since the tubular member 8 is the tubular woven fabric which has no seam in its axial direction, that is, which has no joint in the axial direction, its elongation in the circumferential direction is uniform. This facilitates smooth inversion of the lining material 1 to be inside out, that is, smooth inversion of the lining material main body 2 and the tubular member 8.
In addition, the base material sheet 10 includes the woven fabrics made of the glass yarns (the woven glass roving fabrics 5), and thus includes high-strength fibers. Therefore, the base material sheet 10 has a high strength, and this makes it possible to decrease the overall thickness of the lining material main body 2 (base material sheet 10). In addition, each woven fabric made of the glass yarns, which are the high-strength fibers, is particularly the woven glass roving fabric 5, and this further enhances the strength of the lining material main body 2. Now, because of high elasticity of the lining material main body 2, it is impossible to expand the periphery of the lining material main body 2 installed in the conduit P to bring it to be in close contact with the inner surface of the conduit P. In this embodiment, the diameter of the lining material main body 2 is expanded in the diameter expansion step by sliding the both circumferential ends of the lining material main body 2 (the ends at the overlapping portion 2a), and thereby the lining material main body 2 is brought into close contact with the inner surface of the conduit P.
The base material sheet 10 is formed of: woven fabrics each made of glass yarns which are high-strength fibers (the woven glass roving fabrics 5); and non-woven fabrics 4 of organic fibers, the woven fabrics and the non-woven fabrics being laid on one another and jointed together by needlepunching. Each non-woven fabric 4 has a structure in which long fibers are entangled. Therefore, if an external force is applied to any of the woven glass roving fabrics 5, the non-woven fabric 4 laid on and jointed to that woven glass roving fabric 5 by needlepunching applies resistance to its glass yarns. This suppresses yarn slippage of the woven glass roving fabric 5. The non-woven fabrics 4 also prevent raveling out of the woven glass roving fabrics 5 made of the glass yarns at its edge. Thus, a uniform and high-strength lining structure is constructed inside the conduit P.
Further, in the above diameter expansion step, the lining material main body 2 is heated and pressurized from the inside thereof, to set the liquid thermosetting resin with which the lining material main body 2 has been impregnated while expanding the diameter of the lining material main body 2. With this, a robust lining structure is constructed on the inner surface of the conduit P.
Further, the both circumferential ends of the lining material main body 2 in the rolled tubular form (the both ends at the overlapping portion 2a) are jointed to each other by the hot melt adhesive 6 with the both ends overlapping each other. This further prevents peeling at the overlapping ends. Further, this prevents the both ends from shifting relative to each other and thereby expanding the lining material main body 2 when the lining material 1 is inserted into the conduit P in the installation step. Furthermore, when the lining material main body 2 is heated and pressurized after installed in the conduit P, the hot melt adhesive 6 is softened, and thereby its adhesion is decreased. As a result, the both circumferential ends move and slide on each other to expand the diameter of the lining material main body 2, to bring it into close contact with the inner surface of the conduit P, and the thermosetting resin is set in this state.
Hereinbefore, the embodiment of the present invention has been described. Application of the present invention is not limited to the above embodiment, and various modifications and variations are possible within the scope of the spirit of the invention, as described below, for example.
In the above-described embodiment, the diameter of the tubular member 8 is larger than the diameter of the lining material main body 2, and the slack portion A of the tubular member 8 is on its inner side (inner surface) which does not contact the overlapping portion 2a of the lining material main body 2. The present invention is not limited to this, and as shown in
In the above-described embodiment, the both circumferential ends of the single base material sheet 10 rolled into the tubular form are jointed to each other by the hot melt adhesive 6 with the both ends overlapping each other, to form the lining material main body 2. The present invention is not limited to this, and two or more base material sheets may be used to form a larger-diameter lining material main body, for a conduit having a large diameter.
In the above-described embodiment, the tubular member 8 is the tubular woven fabric; however, the tubular member 8 may be made from other material, for example, by a non-woven fabric. Further, the tubular member 8 is the woven fabric which has no seam in its axial direction; however, the tubular member 8 may have a seam in the axial direction, i.e., does not have to be seamless.
In the above-described embodiment, the liquid curable resin with which the lining material 1 is impregnated is a thermosetting resin. However, the liquid curable resin is not limited to this, and a UV curing resin or a cold setting resin may be used. However, in the case where lining is performed through the two steps of the installation step and the diameter expansion step as is in the above-described embodiment, it is preferable to use a liquid thermosetting resin so that curing of the liquid curable resin and softening of the hot melt adhesive 6 (release of the joint) can be conducted at the same time.
In the above-described embodiment, the both circumferential ends of the tubular lining material main body 2 are jointed to each other by the hot melt adhesive 6. However, the both ends may be jointed in another way, for example, by sewing. It should be noted that, if the both ends are jointed by sewing, the both ends have to be jointed relatively loosely so that a sewed portion can be torn when pressure is applied to the lining material main body 2 from inside in the diameter expansion step.
Further, it is not particularly necessary to joint the both circumferential ends of the lining material main body 2 to each other when there is no possibility that, due to high friction between the overlapping both circumferential ends, for example, the tubular lining material main body 2 significantly expands when the lining material 1 is installed in the conduit P.
In addition, inversion and diameter expansion may be performed at the same time, for example, in repairing of a water pipe or the like. In this case, the both circumferential ends of the tubular lining material main body 2 (the ends at the overlapping portion 2a) are jointed to each other by the hot melt adhesive 6 relatively weakly (for example, the usage of the hot melt adhesive 6 is reduced). Then, the joint is released by pressure applied for inversion, and thereby the overlapping ends are slid on each other. Thus, inversion and diameter expansion are performed simultaneously, and the lining material main body 2 is brought into close contact with the inner surface of the conduit P. With this simultaneous performance of inversion and diameter expansion to bring the lining material 1 into close contact with the conduit P, it is possible to prevent, for example, water entry from the outside of the existing pipe, which can cause the thermosetting resin to be insufficiently heated and thereby to be uncured. In addition, it is possible to expel forward water stagnant in the conduit P, in parallel with inversion and diameter expansion.
In the above-described embodiment, the tubular woven fabric 3 coated with the coating 7 is used as the impermeable layer. The impermeable layer is not limited to this, and a plastic tube with a relatively large thickness (on the order of 100 μm) may be alternatively used as the impermeable layer. In this case, it is possible to remove the impermeable layer after the conduit is lined.
The above-described embodiment deals with a case where the present invention is used to repair an existing conduit. However, the lining material may be installed to reinforce a conduit, irrespective of whether the conduit is existing or new.
The base material sheet 10 constituting the lining material main body 2 is not limited to that described in the above embodiment. The base material sheet 10 may be structured as follows.
In the base material sheet 10 of the above-described embodiment, the non-woven fabrics 4 are respectively laid on the both sides of each woven glass roving fabric 5, and each woven glass roving fabric 5 is sandwiched by two non-woven fabrics 4. However, the non-woven fabric 4 may be laid on only one of the both sides of each woven glass roving fabric 5. This structure also provides the effect of preventing yarn slippage in the woven glass roving fabric 5, or preventing raveling out at an edge.
Further, the woven fabric made of glass yarns is not limited to the woven glass roving fabric formed of the glass roving made of paralleled glass yarns. There may be used a glass fabric made by weaving twisted glass yarns.
The base material sheet does not have to have the lamination structure in which the woven fabric(s) made of glass yarns and the non-woven fabric(s) are laid on one another. For example, one or more of the non-woven fabrics 4 may be omitted. For instance, the non-woven fabrics 4 and the woven glass roving fabrics 5 do not have to be alternately laid on one another. The non-woven fabrics 4 may be respectively laid only on upper and lower sides of a stack of the woven glass roving fabrics 5. Alternatively, no non-woven fabric 4 may be provided. Further, the reinforced fiber layer of the lining material does not have to be the woven fabric of the glass yarns. For example, the base material sheet may be sheet molding compound (SMC) in which high-strength short fibers are dispersed in a liquid thermosetting resin.
Furthermore, the base material sheet includes the glass yarns which are high-strength fibers; however, the base material sheet may include high-strength fibers other than the glass yarns, such as aramid fibers, high-strength polyethylene fibers and high-strength polyallylate fibers.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2012-268647 | Dec 2012 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2013/082659 | 12/5/2013 | WO | 00 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2014/088053 | 6/12/2014 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 3927164 | Shimabukuro | Dec 1975 | A |
| 4009063 | Wood | Feb 1977 | A |
| 4064211 | Wood | Dec 1977 | A |
| 4334943 | Zenbayashi | Jun 1982 | A |
| 4368091 | Ontsuga | Jan 1983 | A |
| 4427480 | Kamuro | Jan 1984 | A |
| 4439469 | Wood | Mar 1984 | A |
| 4576205 | Morinaga | Mar 1986 | A |
| 4681783 | Hyodo | Jul 1987 | A |
| 4686126 | Hyodo | Aug 1987 | A |
| 4723579 | Hyodo | Feb 1988 | A |
| 4768562 | Strand | Sep 1988 | A |
| 4883557 | Morinaga | Nov 1989 | A |
| 4972880 | Strand | Nov 1990 | A |
| 4976290 | Gelin | Dec 1990 | A |
| 5164237 | Kaneda | Nov 1992 | A |
| 5186215 | Gilleland | Feb 1993 | A |
| 5186987 | Imoto | Feb 1993 | A |
| 5223204 | Endoh | Jun 1993 | A |
| 5334429 | Imoto | Aug 1994 | A |
| 5411060 | Chandler | May 1995 | A |
| 5439033 | Kamiyama | Aug 1995 | A |
| 5454401 | Kamiyama | Oct 1995 | A |
| 5566719 | Kamiyama | Oct 1996 | A |
| 5598873 | Kamiyama | Feb 1997 | A |
| 5653555 | Catallo | Aug 1997 | A |
| 5993581 | Toyoda | Nov 1999 | A |
| 6050300 | Schwert | Apr 2000 | A |
| 6152184 | Kamiyama | Nov 2000 | A |
| 6227764 | Einhaus | May 2001 | B1 |
| 6837273 | Woolstencroft | Jan 2005 | B2 |
| 6899832 | Wood | May 2005 | B2 |
| 7096890 | Woolstencroft | Aug 2006 | B2 |
| 7311121 | Kamiyama et al. | Dec 2007 | B2 |
| 7476348 | Waring | Jan 2009 | B2 |
| 7478650 | Pleydon | Jan 2009 | B2 |
| 7845372 | Kiest, Jr. | Dec 2010 | B2 |
| 8580364 | Quitter | Nov 2013 | B2 |
| 8757215 | Burdy | Jun 2014 | B2 |
| 20060159791 | Kamiyama | Jul 2006 | A1 |
| 20070001330 | Driver | Jan 2007 | A1 |
| 20080277012 | Anders | Nov 2008 | A1 |
| 20090218002 | Kashihara | Sep 2009 | A1 |
| 20100012214 | Kamiyama | Jan 2010 | A1 |
| 20150068632 | Onishi | Mar 2015 | A1 |
| 20150328857 | Ueda | Nov 2015 | A1 |
| Number | Date | Country |
|---|---|---|
| 1765613 | May 2006 | CN |
| 61 143129 | Jun 1986 | JP |
| 2001-116165 | Apr 2001 | JP |
| 2011-25456 | Feb 2011 | JP |
| 2012 006334 | Jan 2012 | JP |
| 2012 086386 | May 2012 | JP |
| 2012 121264 | Jun 2012 | JP |
| 2012 126129 | Jul 2012 | JP |
| 10 2006 0012367 | Feb 2006 | KR |
| 10-0956077 | May 2010 | KR |
| Entry |
|---|
| Decision of Rejection dated May 7, 2014 in Korean Patent Application No. 10-2013-0151427 (with English language translation). |
| Extended European Search Report dated Aug. 19, 2016 in Patent Application No. 13860295.8. |
| Combined Office Action and Search Report dated May 12, 2016 in the corresponding Chinese Patent Application No. 201380063633.0 (with English translation and English translation of Category of Cited Documents). |
| Office Action dated Jun. 28, 2016 in the corresponding Japanese Patent Application No. 2012-268647 (with English translation). |
| Singaporean Office Action dated Nov. 9, 2016 in Singapore Patent Application No. 11201504412Q. |
| Office Action dated Jan. 13, 2016 in Singaporean Patent application No. 11201504412Q. |
| International Search Report dated Mar. 18, 2014 in PCT/JP13/082659 filed Dec. 5, 2013. |
| Korean office action dated Jan. 23, 2014, in Korean Patent Application No. 10-2013-0151427. (with English translation). |
| International Preliminary Report on Patentability and Written Opinion dated Jun. 9, 2015 in PCT/JP2013/082659 filed Dec. 5, 2013 (with English language translation). |
| Office Action dated Jun. 1, 2017 in Singaporean Patent Application No. 11201504412Q. |
| Office Action dated May 11, 2017 in Australian Patent Application No. 2013355697. |
| Office Action dated Sep. 22, 2017 in Australian Patent Application No. 2013355697. |
| Russian Office Action issued in RU2015127036, dated Oct. 3, 2017, 7pgs. |
| Number | Date | Country | |
|---|---|---|---|
| 20150328857 A1 | Nov 2015 | US |