Claims
- 1. An aqueous polymer composition comprising 10 to 40 wt % of a polymer in water, the polymer consisting of 20-90 wt % .alpha.,.beta.-ethylenically unsaturated carboxylic acid monomer and at least one softening monomer selected from the group consisting of vinyl alkanoates, monoesters or diesters of maleic acid or fumaric acid with a C.sub.1 -C.sub.16 alkanol, esters of acrylic or methacrylic acid with a C.sub.2 -C.sub.8 alkanol and mixtures thereof in a sufficient amount so that the polymer has a Tg of <140.degree. C., the softening monomer having a homopolymer that exhibits a Tg.+-.35.degree. C., the aqueous polymer composition being adjusted to pH 4-6 with alkali metal hydroxide or an alkaline earth metal hydroxide and a divalent or trivalent metal crosslinking compound post-added to the aqueous polymer composition in an amount effective to yield a superabsorbing polymer.
- 2. The aqueous polymer composition of claim 1 in which the .alpha.,.beta.-ethylenically unsaturated carboxylic acid monomer is selected from the group consisting of acrylic acid, methacrylic acid, crotonic acid, maleic acid, itaconic acid, fumaric acid and mixtures thereof.
- 3. The aqueous polymer composition of claim 1 in which the softening monomers are selected from the group consisting of C.sub.1 -C.sub.12 esters of vinyl alcohol, diesters of maleic acid or fumaric acid with a C.sub.1 -C.sub.16 alkanol, esters of acrylic or methacrylic acid with a C.sub.2 -C.sub.8 alkanol and mixtures thereof.
- 4. The aqueous polymer composition of claim 1 in which the polymer consists essentially of 40 to 80 wt % .alpha.,.beta.-ethylenically unsaturated carboxylic acid monomer and has a Tg from -20.degree. to +120.degree. C.
- 5. The aqueous polymer composition of claim 1 in which the divalent or trivalent metal crosslinking compound is a salt of zirconium, zinc or chromium.
- 6. An aqueous polymer composition comprising 10 to 40 wt % of a polymer in water, the polymer consisting of 20-90 wt % .alpha.,.beta.-ethylenically unsaturated carboxylic acid monomer selected from the group consisting of acrylic acid, methacrylic acid, crotonic acid, maleic acid, itaconic acid and fumaric acid and mixtures thereof, and one or more softening monomers selected from the group consisting of C.sub.1 -C.sub.12 esters of vinyl alcohol, diesters of maleic acid or fumaric acid with a C.sub.1 -C.sub.16 alkanol and esters of acrylic or methacrylic acid with a C.sub.2 -C.sub.8 alkanol in a sufficient amount so that the polymer has a Tg<140.degree. C., the softening monomer having a homopolymer that exhibits a Tg .+-.35.degree. C., the aqueous polymer composition being adjusted to pH 4-6 with alkali metal hydroxide or alkaline earth metal hydroxide and 0.1 to 3 wt % zirconium crosslinking salt post-added to the aqueous polymer composition to yield a superabsorbing polymer.
- 7. The aqueous polymer composition of claim 6 in which the polymer consists essentially of 40 to 80 wt % .alpha.,.beta.-ethylenically unsaturated carboxylic acid monomer and has a Tg from -20.degree. to +120.degree. C.
- 8. The aqueous polymer composition of claim 7 in which the zirconium salt is selected from the group consisting of zirconium acetate, zirconium carbonate, potassium zirconium carbonate and ammonium zirconium carbonate.
- 9. An aqueous polymer composition comprising 10 to 40 wt % of a polymer in water, the polymer consisting of 20-90 wt % acrylic acid and one or more softening monomers selected from the group consisting of vinyl acetate, diesters of maleic acid with a C.sub.4 -C.sub.8 alkanol and esters of acrylic or methacrylic acid with a C.sub.2 -C.sub.8 alkanol in a sufficient amount so that the polymer has a Tg<140.degree. C., the softening monomer having a homopolymer that exhibits a Tg.+-.35.degree. C., the aqueous polymer composition being adjusted to pH 4-6 with alkali metal hydroxide and 0.1 to 3 wt % zirconium crosslinking salt selected from the group consisting of zirconium acetate, zirconium carbonate, potassium zirconium carbonate and ammonium zirconium carbonate post-added to the aqueous polymer composition to yield a superabsorbing polymer.
- 10. The aqueous polymer composition of claim 9 in which the polymer has a Tg of -20.degree. to +120.degree. C.
- 11. The aqueous polymer composition of claim 10 in which the softening monomers are selected from the group consisting of vinyl acetate, dioctyl maleate, 2-ethylhexyl acrylate and mixtures thereof.
- 12. The aqueous polymer composition of claim 5 in which the pH is subsequently adjusted to 8.5 to 10 with a fugitive base.
- 13. The aqueous polymer composition of claim 6 in which the pH is subsequently adjusted to 8.5 to 10 with a fugitive base.
- 14. The aqueous polymer composition of claim 7 in which the pH is subsequently adjusted to 8.5 to 10 with a fugitive base.
- 15. The aqueous polymer composition of claim 8 in which the pH is subsequently adjusted to 8.5 to 10 with a fugitive base.
- 16. The aqueous polymer composition of claim 9 in which the pH is subsequently adjusted to 8.5 to 10 with a fugitive base.
- 17. The aqueous polymer composition of claim 10 in which the pH is subsequently adjusted to 8.5 to 10 with a fugitive base.
- 18. The aqueous polymer composition of claim 11 in which the pH is subsequently adjusted to 8.5 to 10 with a fugitive base.
- 19. A nonwoven product comprising a nonwoven web of fibers bonded together with a polymer binder characterized in that the web is bonded with a sufficient amount of a polymer to both bond the fibers and afford enhanced absorbent properties to the web, the polymer deposited on the web from the aqueous composition of claim 1.
- 20. A nonwoven product comprising a nonwoven web of fibers bonded together with a polymer binder characterized in that the web also contains a sufficient amount of an absorbent polymer to afford enhanced absorbent properties to the web, the absorbent polymer deposited on the web from the aqueous composition of claim 1.
- 21. A superabsorbent product comprising cellulosic fibers containing a sufficient amount of an absorbent polymer to provide the fibers with enhanced absorbent properties, the absorbent polymer deposited on the fibers from the aqueous composition of claim 1.
- 22. A superabsorbent product comprising cellulosic fibers containing a sufficient amount of an absorbent polymer to provide the fibers with enhanced absorbent properties, the absorbent polymer deposited on the fibers from the aqueous composition of claim 6.
- 23. A superabsorbent product comprising cellulosic fibers containing a sufficient amount of an absorbent polymer to provide the fibers with enhanced absorbent properties, the absorbent polymer deposited on the fibers from the aqueous composition of claim 9.
CROSS-REFERENCE TO RELATED APPLICATIONS
This application is continuation-in-part of application Ser. No. 08/308,027 filed on 16 Sep. 1994, now abandoned which is incorporated by reference.
US Referenced Citations (12)
Foreign Referenced Citations (2)
Number |
Date |
Country |
0031628 |
Jul 1981 |
EPX |
0133779 |
Mar 1985 |
EPX |
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
308027 |
Sep 1994 |
|