The present invention relates to a method of manufacturing a component comprising liquid crystal, a component comprising liquid crystal manufactured according to the method, and devices including such components. The method is particularly suitable for, but not limited to, manufacturing liquid crystal lenses for use in optical scanning devices.
Optical pickup units for use in optical scanning devices are known. The optical pickup units are mounted on a movable support for scanning across the tracks of the optical disk. The size and complexity of the optical pickup unit is preferably reduced as much as practicable, in order to reduce the manufacturing cost and to allow additional space for other components being mounted in the scanning device.
Modern optical pickup units are generally compatible with at least two different formats of optical disk, such as the Compact Disc (CD) and the Digital Versatile Disc (DVD) format. Recently proposed has been the Blu-ray Disk (BD) format, offering a data storage capacity of around 25 GB (compared with a 650 MB capacity of a CD, and a 4.7 GB capacity of a DVD).
Larger capacity storage is enabled by using small scanning wavelengths and large numerical apertures (NA), to provide small focal spots, (the size of the focal spot is approximately λ/NA), so as to allow the readout of smaller sized marks in the information layer of the disk. For instance, a typical CD format utilizes a wavelength of 785 nm and an objective lens with a numerical aperture of 0.45, a DVD uses a wavelength of 650 nm and a numerical aperture of 0.65, and a BD system uses a wavelength of 405 nm and a numerical aperture of 0.85.
Typically, the refractive index of materials vary as a function of wavelength. Consequently, a lens will provide different focal points and different performance for different incident wavelengths. Further, the discs may have different thickness transparent layers, thus requiring a different focal point for different types of discs.
In some instances, storage capacity is further increased by increasing the number of information layers per disc. For example, a dual layer BD-disc has two information layers separated by a 25 μm thick spacer layer. Thus, the light from the optical pickup unit has to travel through the spacer layer when focusing on the second information layer. This introduces 255 mλ rms (0.255λ root mean square) spherical aberration, the phenomenon that rays close to the axis of the converging cone of light have a different focal point compared to the rays on the outside of the cone. This results in a blurring of the focal spot, and a subsequent loss of fidelity in the read-out of the disc.
To enable dual layer readout and backward compatibility (i.e. the same optical system being used for different disc formats), polarization sensitive lenses (PS-Lenses) have been proposed to compensate for spherical aberration. Such lenses can be formed of a birefringent material, such as a liquid crystal. Birefringence denotes the presence of different refractive indices for the two polarization components of a beam of light. Birefringent materials have an extraordinary refractive index (ne) and an ordinary refractive index (no), with the difference between the refractive indices being Δne−no. PS lenses can be used to provide different focal points for a single or different wavelength(s) by ensuring that the same or different wavelengths are incident upon the lens with different polarisations.
In order to form the lens with the desired optical properties, the liquid crystal molecules need to be directed in a specific orientation. Well known materials to induce this orientation are polyimides. These polyimides are usually applied via spincoating, and subsequently rubbed with a non-fluff cloth to induce a specific orientation of the polyimide alignment layer, which subsequently determines the orientation of the liquid crystal molecules placed upon the layer.
However, if a substrate on which the liquid crystal molecules have to be oriented is curved (or otherwise shaped e.g. with a step structure) rubbing of the substrates is often irreproducible. Further, creating suitably shaped substrates with a specific desired curvature is relatively expensive.
JP 031578616A describes a method of manufacturing a liquid crystal lens by laminating transparent polycarbonate sheets via adhesive agent on both surfaces of a flat plate of variable focus liquid crystal, and subsequently pressing the sheet by moulds, so as to obtain the desired shape of liquid crystal lens. Such a process requires that the flat plate liquid crystal layer has been previously aligned prior to lamination. Further, it is likely that the subsequent molding of the liquid crystal will act to alter the alignment of the liquid crystal within the lens body. In some instances, it may also be desirable to subsequently remove the transparent polycarbonate sheets, requiring an additional processing step and potentially resulting in the lens surface being damaged.
It is an aim of embodiments of the present invention to provide an improved manufacturing process which addresses one or more of the problems of the prior art, whether referred to herein or otherwise.
It is an aim of embodiments of the present invention to provide a manufacturing process that allows the formation of a component comprising liquid crystal having a predetermined shape that can be relatively cheaply manufactured, as well as liquid crystal components formed by such a method.
In a first aspect, the present invention provides a method of manufacturing a component comprising liquid crystal, the method comprising: placing a liquid crystal between a substrate and a mould, the mould having a shaped surface, at least a portion of the shaped surface having an alignment layer formed thereon, and the substrate having a first surface on which is formed a bonding layer; bringing the mould and the substrate together so as to sandwich the liquid crystal between the first surface of the substrate and the shaped surface of the mould; polymerising the liquid crystal; adhering the liquid crystal to the bonding layer; and removing the substrate with the adhered polymerised liquid crystal from the mould.
Such a manufacturing method allows the predetermined shaped mould to be reused. This decreases the cost of the manufacturing process. Further, as the alignment layer within the mould can also be reused, reproducibility of the orientation and shape of components formed by the process is improved.
In another aspect, the present invention provides an optical component comprising a liquid crystal, at least a portion of the optical component being formed according to the method as described above.
In a further aspect, the present invention provides an optical scanning device for scanning an information layer of an optical record carrier, the device comprising a radiation source for generating a radiation beam and an objective system for converging the radiation beam on the information layer, wherein the device comprises an optical component formed according to the method as described above.
For a better understanding of the invention, and to show how embodiments of the same may be carried into effect, reference will now be made, by way of example, to the accompanying diagrammatic drawings in which:
In the first step, shown in
An alignment layer 110 is arranged on the curved surface 102, so as to induce a predetermined orientation (indicated by the arrow direction 110) in the liquid crystal subsequently placed upon the alignment layer.
In this particular example, the alignment layer is a layer of polyimide (PI). The polyimide may be applied using spincoating from a solution. The polyimide may then be aligned so as to induce a specific orientation (this orientation determining the resulting orientation of the liquid crystal molecules). For instance, a known process is to rub the polyimide layer with a non-fluff cloth repeatedly in a single direction so as to induce this orientation (110).
A substrate 150, which in this particular embodiment will form part of the optical component, has a bonding layer 120 applied to a first surface 152. The bonding layer is arranged to form a bond with the liquid crystal. In this particular instance, the bonding layer is also an alignment (or orientation) layer comprising polyimide. The bonding layer contains reactive groups arranged to form a chemical bond with the liquid crystal molecules, and in this instance has the same type of reactive group as the liquid crystal molecules, such that when photopolymerising the liquid crystal molecules, chemical bonds with the bonding layer on the substrate are also created. This results in very good adhesion between substrate and the liquid crystal layer. The bonding layer may be deposited on the substrate using the same type of process used to deposit and align the alignment layer on the mould 100. The bonding layer, which in this instance also functions as an alignment layer, is oriented in a predetermined orientation (arrow 120) depending upon the desired properties of the resulting liquid crystal components.
In this particular example, a PS lens is being formed, so the bonding layer is aligned so as to be parallel to the direction 110 of the alignment layer on the mould. Preferably, the rotation of the bonding layer is parallel but in the opposite direction to the orientation of the alignment layer.
As illustrated in
In this particular example, as illustrated in
A droplet of the liquid crystals 200 is placed on the first surface 152 of the substrate. The compound 200 has been degassed, so as to avoid the inclusion of air bubbles within the resulting optical component. It also avoids the formation of air bubbles from dissolved gases coming out of the solidifying liquid during (isochorous) polymerization, as the driving force from shrinkage during isochorous (i.e. constant volume) polymerization leads to a large pressure drop inside the polymerizing liquid.
The glass mould is then heated so that the liquid crystal is in the isotropic phase (typically to about 80° C.-120° C.), so as to facilitate the subsequent flow of the liquid crystal into the desired shape.
The substrate and the mould are subsequently brought together, so as to define the shape of the liquid crystal portion 201 of the final resulting optical component (
The substrate/mould/liquid crystal may then be cooled, for instance down to room temperature for 30 minutes, so as to ensure that the liquid crystal enters the nematic phase, coming from the isotropic phase.
When entering the nematic stage, multi domains may appear in the liquid crystal mixture. Consequently, the mixture can be heated to above the clearing point to destroy the multidomain orientation (e.g. the mixture may be heated for 3 minutes to 105° C.). Subsequently, the mixture may be cooled to obtain a homogenous orientation 202 (
The homogenous liquid crystal mixture may then be photopolymerised using light 302 from an ultra violet radiation source 300 (
Subsequently, the optical component (150, 203) can be released from the mould 100 (
The mould can be reused to produce subsequent components, by repeating steps illustrated in
If desired, a further processing step can be performed to remove the liquid crystal 203 from the substrate 150. However, in most instances it is assumed that the substrate 150 will form part of the final optical component.
In experiments to characterize the influence of the mould parameters on the optical properties of the lenses, three different shaped moulds were utilized.
A suitable polyimide for use in the alignment layer is OPTMER AL-1051 supplied by Japan Synthetic Rubber Co., whilst Merck ZLI2650, spincoated from a solution in γ-butyrolactone can be used as an appropriate reactive polyimide with methacrylate groups as the bonding layer.
As mentioned above, in the preferred embodiment a mixture of two liquid crystals was utilized to obtain the desired ne and no. The two liquid crystals utilized were 1,4-di(4-(3-acryloyloxypropyloxy)benzoyloxy)-2-methylbenzene (RM 257) and E7 (a cyanobiphenyl mixture with a small portion of cyanotriphenyl compound) both from Merck, Darmstadt, Germany. The photoinitiator used to ensure the photo polymerization of the liquid crystals was Irgacure 651, obtainable from Ciba Geigy, Basel.
Resulting measurements illustrated that the lenses made from the mould with the radius of 49 mm had the best optical properties, with a very homogenous liquid crystal orientation even in the region near the pupil boarders where the mould surface is steeper. The total root mean square wavefront aberration was generally less than 0.015 wavelengths, using a laser wavelength of 430 nm.
In some instances, a surfactant was mixed with the liquid crystal to promote the lens release from the mould. The surfactants utilized were FC171 a perfluorinated surfactant (3M) and 2-(N-ethylperfluorooctane sulfonamido-ethylacrylate (Acros). The use of the surfactant was seen to influence the orientation of the liquid crystal (a lower Δn was seen when a surfactant was utilised).
In general, the optical aberrations of the liquid crystal lenses were very small, and generally the root mean square wavefront aberration was less than 0.02 wavelengths.
Alternatively, the transparent layer may have the sole function of protecting the information layer, while the mechanical support is provided by a layer on the other side of the information layer, for instance by the protection layer 5 or by a further information layer and a transparent layer connected to the information layer 4. Information may be stored in the information layer 4 of the record carrier in the form of optically detectable marks arranged in substantially parallel, concentric or spiral tracks, not indicated in the Figure. The marks may be in any optically readable form, e.g. in the form of pits, or areas with a reflection coefficient or a direction of magnetization different from their surroundings, or a combination of these forms.
The scanning device 1 comprises a radiation source 11 that can emit a radiation beam 12. The radiation source may be a semiconductor laser. A beam splitter 13 reflects the diverging radiation beam 12 towards a collimator lens 14, which converts the diverging beam 12 into a collimated beam 15. The collimated beam 15 is incident on an objective system 18.
The objective system may comprise one or more lenses and/or a grating. The objective system 18 has an optical axis 19. The objective system 18 changes the beam 17 to a converging beam 20, incident on the entrance face 6 of the record carrier 2. The objective system has a spherical aberration correction adapted for passage of the radiation beam through the thickness of the transparent layer 3. The converging beam 20 forms a spot 21 on the information layer 4. Radiation reflected by the information layer 4 forms a diverging beam 22, transformed into a substantially collimated beam 23 by the objective system 18 and subsequently into a converging beam 24 by the collimator lens 14. The beam splitter 13 separates the forward and reflected beams by transmitting at least part of the converging beam 24 towards a detection system 25. The detection system captures the radiation and converts it into electrical output signals 26. A signal processor 27 converts these output signals to various other signals.
One of the signals is an information signal 28, the value of which represents information read from the information layer 4. The information signal is processed by an information processing unit for error correction 29. Other signals from the signal processor 27 are the focus error signal and radial error signal 30. The focus error signal represents the axial difference in height between the spot 21 and the information layer 4. The radial error signal represents the distance in the plane of the information layer 4 between the spot 21 and the center of a track in the information layer to be followed by the spot.
The focus error signal and the radial error signal are fed into a servo circuit 31, which converts these signals to servo control signals 32 for controlling a focus actuator and a radial actuator respectively. The actuators are not shown in the Figure. The focus actuator controls the position of the objective system 18 in the focus direction 33, thereby controlling the actual position of the spot 21 such that it coincides substantially with the plane of the information layer 4. The radial actuator controls the position of the objective lens 18 in a radial direction 34, thereby controlling the radial position of the spot 21 such that it coincides substantially with the central line of track to be followed in the information layer 4. The tracks in the Figure run in a direction perpendicular to the plane of the Figure.
The device of
In the embodiment shown in
The focal point of the objective system can be altered by using the bifocal nature of the liquid crystal lens 181. In this particular instance, the substrate 150 used in the lens manufacture is glass. Further, the substrate is a planar sheet, and as such does not effect the focusing power of the lens. The focal length of the lens 181 is thus fe=r/(ne−na) and f0=r/(no−na) for the extraordinary and ordinary modes respectively, where na is the refractive index of air, and r is the curvature radius of the lens.
Consequently, it will be seen that by providing an optical signal with polarization parallel to the liquid crystal orientation, such that the extraordinary mode of the lens 181 is utilised, the objective system 18 will focus the collimated beam 15 on the nearer information layer 4. However, when the collimated beam is incident on to the objective system 18 with polarisation perpendicular to the liquid crystal orientation, in the resulting ordinary mode the focal point of the objective system 18 is further away i.e. on the second information layer 4′.
It will be appreciated that the above embodiments are described by way of example only, and that various alternatives will be apparent to the skilled person. For instance, whilst a method has been described suitable for producing polarisation sensitive lenses, it will be appreciated that any optical component can be manufactured from liquid crystal as desired, particularly if the resulting optical component has a shaped surface such as that might be defined by a curved surface or a step surface on a mould.
For instance, the method could be used to form components having large surfaces, such as compensation foils that can be used in or on the surface of visual displays for viewing angle optimization. In such a compensation foil, the display screen itself could be used as the substrate in the manufacturing method.
The mould may be formed of any material, including rigid materials such as glass.
Further, the shaped surface of the mould may be dimensioned so as to allow for any change in shape or volume of the liquid crystal material during the method. For instance, typically liquid crystal monomers shrink slightly upon polymerization, due to double bonds within the liquid crystal being reformed as single bonds. By appropriately making the optical component shaped defined by the substrate and the mould slightly oversize, an appropriately sized and shaped optical component can be produced.
Whilst the substrate has been seen in this particular example as comprising a single sheet of glass, with two flat, substantially parallel sides, it will be appreciated that the substrate can in fact be any desired shape.
An extra adhesion layer may be applied to the mould and/or substrate (prior to deposition of the bonding layer onto the substrate and the orientation layer to the mould), so as to make sure that the applied layers are well attached to the mould and the substrate. For instance, organosilanes may be used to provide this adhesion layer. For the substrate an organosilane comprising a methacrylate group may be used and for the mould an organosilane comprising an amine end group may be used.
Equally, the alignment layers used may have any desired orientation. For instance, by placing the orientation of the alignment layer on the substrate perpendicular to the orientation of the alignment layer on the mould, a twisted nematic device can be formed.
By using the above method, the predetermined shaped mould can be reused, decreasing the cost of the manufacturing process, and allowing consistently sized optical components to be produced.
| Number | Date | Country | Kind |
|---|---|---|---|
| 02080550.3 | Dec 2002 | EP | regional |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/IB03/06040 | 12/16/2003 | WO | 6/24/2005 |