LIQUID CRYSTAL COMPOSITION AND LIQUID CRYSTAL DISPLAY ELEMENT

Abstract
The present invention provides a liquid crystal composition, containing: one kind or two or more kinds of a first monomer having a first mesogenic skeleton, at least one polymerizable group represented by the general formula (PG1) linked to the first mesogenic skeleton, and at least one polar group linked to the mesogenic skeleton or the polymerizable group; and one kind or two or more kinds of a second monomer having a second mesogenic skeleton and a polymerizable group represented by the general formula (PG2) linked to the second mesogenic skeleton, and having a chemical structure different from that of the first monomer, in an amount of more than 0.4% by mass, which is excellent in vertical alignment, burn-in characteristics (change with time of pretilt angle), and compatibility, and provides a liquid crystal display element using the liquid crystal composition.
Description
TECHNICAL FIELD

The present invention relates to a liquid crystal composition containing a spontaneous orientation monomer and a liquid crystal display element using the same.


BACKGROUND ART

In general, liquid crystal display elements such as liquid crystal panels and liquid crystal displays change the alignment state of liquid crystal molecules by an external stimulus such as an electric field, and utilize changes in the optical characteristics associated therewith for display. Such a liquid crystal display element has a structure in which liquid crystal molecules are filled in a gap between two transparent substrates, and in general, an alignment film for aligning liquid crystal molecules in a specific direction in advance is formed on the surface of the substrate which comes into contact with the liquid crystal molecules.


However, there is a problem in that alignment defects are generated due to scratches or dust generated in the surface of the alignment film in the manufacturing process of the liquid crystal display element, and that as the size of the substrate increases, the design and management of an alignment film for obtaining uniform alignment over the entire surface of the substrate and for a long period of time becomes difficult.


Therefore, in recent years, there has been a demand for the development of a liquid crystal display element which does not require an alignment film by using a liquid crystal composition containing a spontaneous orientation material for controlling the alignment of liquid crystal molecules in a liquid crystal layer.


For example, PTL 1 describes a liquid crystal composition containing a spontaneous orientation material for suppressing a decrease in voltage holding ratio by a liquid crystal composition containing a monofunctional biphenyl monomer having an octyl group and showing a high linearity and a bifunctional biphenyl monomer having a stearyl group and showing a low linearity, instead of lauryl acrylate having a relatively weak interaction with the liquid crystal molecule. Further, PTL 2 discloses various liquid crystal compositions containing a self-alignment additive for controlling alignment of liquid crystal molecules in place of an alignment layer, and states that when a liquid crystal composition containing a nematic LC medium, a self-alignment additive and, if necessary, a polymerizable compound is filled into a test cell without a pre-alignment layer, a spontaneous homeotropic (vertical) alignment with respect to the substrate surface and the vertical alignment are stable to a clearing point, and that the formed VA cell can be reversibly switched by application of a voltage.


CITATION LIST
Patent Literature

PTL 1: US Patent Publication No. 2017/0123275


PTL 2: JP-A-2016-501938


SUMMARY OF INVENTION
Technical Problem

However, a composition containing two kinds of hydrophobic monomers having a long alkyl chain and a biphenyl skeleton as shown in PTL 1 described above is considered to have a stronger interaction, than lauryl acrylate, with liquid crystal molecules of a liquid crystal layer filled between a pair of substrates, but there is a problem that the alignment direction of liquid crystal molecules cannot be regulated due to low suction force applied to the substrate.


In PTL 2, the initial pretilt angle (pretilt) is taken into consideration, but in the case of a liquid crystal display element in which the voltage is repeatedly turned on and off, the change with time of the pretilt angle is not taken into consideration. Therefore, even if a passivation layer is constructed by the self-alignment additive having a hydroxyl group as the polar group of PTL 2 and the initial pretilt angle (pretilt) can be controlled to a desired value, there arises a new problem that the display unevenness occurs due to the change in the pretilt angle with time. In particular, the relationship between the combination of the self-alignment additive and the polymerizable compound to be added and the content thereof and the relationship between the content of the self-alignment additive and the polymerizable compound and the change with time of the pretilt angle are not studied.


Accordingly, the problem to be solved by the present invention is to provide a liquid crystal composition which is excellent in vertical alignment, burn-in characteristics (change with time of pretilt angle), and compatibility, and to provide a liquid crystal display element using the liquid crystal composition.


Solution to Problem

As a result of intensive studies by the present inventors, it has been found that the above problems can be solved by a liquid crystal composition including one kind or two or more kinds of self-alignment polymerizable compounds and one kind or two or more kinds of polymerizable compounds in a specific amount and a liquid crystal display element using the same, and the present invention has been completed.


Advantageous Effects of Invention

The liquid crystal composition according to the present invention exhibits high compatibility and excellent vertical alignment with respect to liquid crystal molecules.


The liquid crystal composition according to the present invention has one kind or two or more kinds of self-alignment polymerizable compounds and a specific amount of one kind or two or more kinds of polymerizable compounds, and thus exhibits no or little change with time in the pretilt angle.


The liquid crystal composition according to the present invention has one kind or two or more kinds of self-alignment polymerizable compounds (first monomer) and a specific amount of one kind or two or more kinds of polymerizable compounds, so that alignment unevenness can be prevented or alignment unevenness can be reduced.


The liquid crystal display element according to the present invention exhibits no alignment unevenness or reduced alignment unevenness.


The liquid crystal composition according to the present invention and the liquid crystal display element provided with the liquid crystal composition exhibit high reliability.







DESCRIPTION OF EMBODIMENTS

According to the first aspect of the present invention, provided is a liquid crystal composition, including:


one kind or two or more kinds of a first monomer having a first mesogenic skeleton, at least one polymerizable group represented by the general formula (PG1) linked to the first mesogenic skeleton, and at least one polar group linked to the mesogenic skeleton or the polymerizable group; and


one kind or two or more kinds of a second monomer having a second mesogenic skeleton and a polymerizable group represented by the general formula (PG2) linked to the second mesogenic skeleton, and having a chemical structure different from that of the first monomer, in an amount of more than 0.4% by mass:





[Chem. 1]





*—S11—P11  (PG1)





*—S21—P21  (PG2)


wherein P11 and P21 each independently represent a group represented by any of the following formulae (R-I) to (R-IX):




embedded image


wherein R21, R31, R41, R51, and R61 each independently represent a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms; W1 is a single bond, —O—, or a methylene group; T1 is a single bond or —COO—; p1, t1, and q1 are each independently 0, 1, or 2; and one or more hydrogen atoms of the polymerizable group p11 may be substituted with the polar group, or the polar group may have a polymerizable group represented by the general formula (PG1) as a substituent; * in the above chemical formulae represents a bonding site; and S11 and S21 each independently represent a single bond or an alkylene group having 1 to 15 carbon atoms, and one —CH2— or two or more —CH2— that are not adjacent to each other in the alkylene group each may be substituted with the polar group, —O—, —COO—, or —COO— so long as oxygen atoms are not directly adjacent to each other.


As a result, a liquid crystal composition having excellent vertical alignment, burn-in characteristics (pretilt angle change with time), and compatibility can be obtained.


The alkyl group in the present specification may be either linear or branched, and is preferably a linear alkyl group, and specific examples thereof include, a methyl group, an ethyl group, a propyl group, a butyl group, a pentyl group, a hexyl group, a heptyl group, an octyl group, a nonyl group, a decyl group, an isopropyl group, and an isobutyl group.


The alkylene group in the present specification may be either linear or branched, and is preferably a linear alkylene group, and specific examples thereof include a methylene group, an ethylene group, a propylene group, a butylene group, a hexylene group, and an octylene group. The alkoxy group in the present specification may be either linear or branched, and is preferably a linear alkoxy group, and examples thereof include a methoxy group, an ethoxy group, a propoxy group, a butoxy group, and a pentoxy group.


The first mesogenic skeleton according to the present invention preferably has the general formula (Me1):




embedded image


wherein in the general formula (Me1), ZMe1 represents a single bond, —CH═CH—, —CF═CF—, —C≡C—, —COO—, —OCO—, —OCOO—, —OOCO—, —CF2O—, —OCF2—, —CH═CHCOO—, —OCOCH═CH—, —CH2—CH2COO—, —OCOCH2—CH2—, —CH═C(CH3)OCO—, —OCOC(CH3)═CH—, —CH2—CH(CH3)OCO—, —OCOCH(CH3)—CH2—, —OCH2CH2O—, or an alkylene group having 2 to 20 carbon atoms, and one —CH2— or two or more —CH2— that are not adjacent to each other in the alkylene group may be substituted with —O—, —COO—, or —OCO—; AMe1 represents a divalent 6-membered ring aromatic group, a divalent 6-membered ring heteroaromatic group, a divalent 6-membered ring aliphatic group, or a divalent 6-membered heteroaliphatic group, and the hydrogen atom in these cyclic structures may be substituted with a halogen atom or P11-Sp11- and a polar group, and in the case where a plurality of each of ZMe1 and AMe1 are present, these may be the same as or different from each other,


mMe1 represents an integer of 1 to 5, and in the formula (Me1), the black dot at the left end and the black dot at the right end represent a bonding site.


The mesogenic skeleton represented by the formula (Me1) according to the present invention is preferably any one of the following formulae (Me1-1) to (Me1-16).




embedded image


embedded image


embedded image


embedded image


The polymerizable group represented by the general formula (PG 1) according to the present invention is any one of the following formulae (R-I) to (R-IX).




embedded image


In the formulae (R-I) to (R-IX), R21, R31, R41, R51, and R61 are each independently a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms, W1 is a single bond, —O—, or a methylene group, T1 is a single bond or —COO—, and p1, t1, and q1 are each independently 0, 1, or 2, and one or more hydrogen atoms of the above formulae (R-I) to (R-IX) may be substituted with the polar group, * in the above chemical formulae represents a bonding site.


Among these, in the above (PG1) and (PG2), each of P11 is independently preferably formula (R-I), formula (R-II), formula (R-III), formula (R-IV), formula (R-V), or formula (R-VII), more preferably formula (R-I), formula (R-II), formula (R-III), or formula (R-IV), and still more preferably formula (RI), and yet still more preferably an acryl group or a methacryl group, further still more preferably a methacryl group, and one or more hydrogen atoms may be substituted with the polar group.


In the above general formula (PG1), S11 is preferably an alkylene group having 1 to 5 carbon atoms which may be substituted with a single bond or a polar group, and more preferably an alkylene group having 2 to 5 carbon atoms which may be substituted with a polar group, and it is preferable that at least one hydrogen atom of S11 is substituted with a polar group represented by the following general formula (K).


The number of polymerizable groups represented by the general formula (PG1) according to the present invention is preferably 1 to 5, more preferably 1 to 4, and still more preferably 1 to 3.


The polar group according to the present invention preferably has a role of an interaction site interacting with (for example, suction) a substrate, a film, an electrode, or the like, and is more preferably a group that has a non-covalent interaction with a member (including a substrate (including a glass or a metal oxide), a film, or an electrode) that is different from the first monomer. It is preferable that the polar group is an atomic group of a polar element having a hetero atom selected from the group consisting of N, O, S, P and Si, and it is more preferable that the polar group is an atomic group of a polar element having a hetero atom selected from the group consisting of N, O, S, P and Si, and that it exhibits an interaction with a member other than the first monomer, and is preferably represented by the following formula (K). The polar group according to the present invention may be linked to the polymerizable group represented by the general formula (PG1) (the polar group may include a polymerizable group represented by the general formula (PG1) as a substituent).





[Chem. 8]





*—Sik—Kik  (K)


In the above general formula (K), Sik represents a single bond or an alkylene group having 1 to 15 carbon atoms, and one —CH2— or two or more —CH2— that are not adjacent to each other in the alkylene group may be substituted with —O—, —OCO—, or —COO— so long as oxygen atoms are not directly adjacent to each other, and


Kik is represented by the following formulae (K-1) to (K-28).




embedded image


embedded image


embedded image


In the above formulae (K-1) to (K-23), RK1 and RK2 each independently represent a hydrogen atom or a linear or branched alkyl group or alkyloxy group having 1 to 5 carbon atoms; RK3 represents a hydrogen atom or a linear or branched alkyl group having 1 to 20 carbon atoms and one —CH2— or two or more —CH2— that are not adjacent to each other in the alkyl group may be substituted with —O—, —COO—, or —OCO—; RK4 and RK5 each independently represent a hydrogen atom or an alkyl group having 1 to 8 carbon atoms;


WK1 represents a methine group, ≡C—CH3, ≡C—C2H5, ≡C—C3H7, ≡C—C4H9, ≡C—C5H11, ≡C—C6H13, or a nitrogen atom;


XK1 and XK2 each independently represent —CH2—, an oxygen atom, —C(═O)—, or a sulfur atom;


YK1 YK2 and YK3 each independently represent a methine group or a nitrogen atom;


ZK1 represents an oxygen atom or a sulfur atom; ZK2 represents a carbon atom, a sulfur atom, or a silicon atom; ZK3 represents an oxygen atom; ZK4 represents a single bond or a double bond.


One or more hydrogen atoms of the above-mentioned Sik or the above-mentioned Kik may be substituted with a polymerizable group represented by the general formula (PG1); * in the above chemical formulae represents a bonding site.




embedded image


In the formula, Yi1 represents a linear or branched alkyl group having 3 to 20 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and at least two or more secondary carbon atoms in these alkyl groups are substituted with —(C═Xi1)— and/or —(CH—CN)—, and the secondary carbon atom in the alkyl group may be substituted with —CH═CH—, —C≡C—, —O—, —NH—, —COO—, or —OCO— so long as oxygen atoms are not directly adjacent to each other; Xi1 represents an oxygen atom, a sulfur atom, NH, or NRi1;


Si1 and Si3 each independently represent an alkylene group having 1 to 6 carbon atoms or a single bond, and —CH2— in the alkylene group may be substituted with —CH═CH—, —C≡C—, —C (═CH2)—, —C(═CHRi3)—, —C(═CRi32)—, —O—, —NH—, —C═O—, —COO—, or —OCO— so long as oxygen atoms are not directly adjacent to each other;


Si2 represents a carbon atom, a nitrogen atom, or a silicon atom;


Ri2 represents a hydrogen atom, a linear or branched alkyl group having 1 to 20 carbon atoms, and the secondary carbon atom in these groups may be substituted with —O—, —CH═CH—, or —C≡C— so long as oxygen atoms are not directly adjacent to each other;


Pi1 represents a polymerizable group;


Spi1 represents a spacer group or a single bond;


ni1 represents an integer of 1 to 3; ni2 and ni3 each independently represent an integer of 0 to 2, but when Si2 represents a carbon atom or a silicon atom, ni1+ni2+ni3 is 3, and when Si2 represents a nitrogen atom, ni1+ni2+ni3 is 2. Ri3 has the same meaning as Ri3 in the general formula (i), and in the case where a plurality of each of Ri2, Xi1, Yi1, Si1, Si3, Pi1, and Spi1 are present in the general formula (K-1), these may be the same as or different from each other.




embedded image


In the formulae, Si1, Pi1 and Spi1 have the same meaning as Si1, Pi1 and Spi1 in the general formula (K-1), respectively; RK21 represents a linear or branched alkyl group having 1 to 10 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and at least two or more secondary carbon atoms in these alkyl groups may be substituted with —CH═CH—, —C≡C—, —O—, or —NH— so long as oxygen atoms are not directly adjacent to each other; and ni4 and n1K21 each independently represent 0 or 1.


The spontaneous orientation monomer according to the present invention has at least one polar group, a mesogenic group, and at least one polymerizable group, and has a chemical structure different from that of the second monomer according to the present invention. The polar group may be bonded to a mesogenic group or a polymerizable group via a spacer.


The first monomer according to the present invention has a first mesogenic skeleton, at least one polymerizable group represented by the general formula (PG1) linked to the first mesogenic skeleton, and at least one polar group linked to the mesogenic skeleton or the polymerizable group, and preferably has a first mesogenic skeleton, at least one polymerizable group represented by the general formula (PG1) linked to the first mesogenic skeleton, and at least one of the polar groups represented by the general formula (K) linked to the mesogenic skeleton or the polymerizable group. The polar group may be bonded to a mesogenic group or a polymerizable group via the spacer Sik.


Sik preferably represents a single bond or an alkylene group having 1 to 8 carbon atoms, and one or two or more —CH2— in the alkylene group may be substituted with —O—, —OCO—, or —COO— so long as oxygen atoms are not directly adjacent to each other. Moreover, the —CH2— may be substituted with the polymerizable group represented by the general formula (PG1).


In the polar group according to the present invention, Kik is preferably at least one selected from the group consisting of compounds represented by the following formulae (K-1-1) to (K-23-1)




embedded image


embedded image


embedded image


In the above formulae, RK4′ and RK5′ each independently represent an alkyl group having 1 to 5 carbon atoms.


The group may be substituted with a polymerizable group represented by the general formula (PG1). * in the above chemical formulae represents a bonding site.


Among the above, the polar group according to the present invention is preferably the formula (K-1-1), (K-2-1), (K-7-1), (K-20-1), or (K-22-1).


In the first monomer according to the present invention, the polar group may be directly linked to the first mesogenic skeleton or may be linked to a polymerizable group represented by the general formula (PG1). As a preferable form in a case in which the polar group is linked to a polymerizable group represented by the general formula (PG1) (the polar group has a polymerizable group represented by the general formula (PG1) as a substituent), when the polar group is represented by the general formula (K), one or more hydrogen atoms of the above Sik or the above Kik may be substituted with a polymerizable group represented by the general formula (PG1).


In the first monomer according to the present invention, one or more hydrogen atoms of the polymerizable group represented by the general formula (PG1) may be substituted with a polar group. A preferable form in this case includes a form in which one or more hydrogen atoms in the polymerizable group p11 or S11 are substituted with a polar group, and a more preferable form includes a form in which one or more hydrogen atoms in the polymerizable group p11 or S11 are substituted with the polar group represented by the general formula (K). For example, the form in which the polar group is directly linked to the polymerizable group represented by the general formula (PG1) includes the structure such as the following formula (P-K-1), (P-K-2), (P-K-3), or (P-K-4).




embedded image


In the above formulae, Rnk1 represents a hydrogen atom or an alkyl group having 1 to 5 carbon atoms, and nk1 and nk2 each independently represent an integer of 0 to 8.


The first monomer according to the present invention is preferably a monomer that exhibits spontaneous orientation property for controlling the alignment of liquid crystal molecules, and more preferably one kind or two or more kinds of compounds selected from the group consisting of compounds represented by the general formula (i), the general formula (ii) the general formula (iii) and the general formula (iv).




embedded image


In the above general formula (i), Ral1, Ral2, Zal1, Zal2, Lal1, Lal2, Lal3, Spal1, Spal2, Spal3, Xal1, Xal2, Xal3, mal1, mal2, mal3, nal1, nal2, nal3, pal1, and pal2 are independent of each other;


Ral1 represents a hydrogen atom, a halogen atom, a linear, branched or cyclic alkyl group having 1 to 20 carbon atoms, wherein in the alkyl group, one or two or more non-adjacent CH2 groups may be substituted with —O—, —S—, —CO—, —CO—O—, —O—CO—, or —O—CO—O— so that the 0 and/or S atoms are not directly bonded to each other, and in addition, one or two or more hydrogen atoms may be replaced by F or Cl;


Ral2 represents a polar group having any of the following partial structures:




embedded image


embedded image


Spal1, Spal2, and Spal3 each independently represent an alkyl group having 1 to 12 carbon atoms or a single bond;


Xal1, Xal2, and Xal3 each independently represent an alkyl group, an acrylic group, a methacryl group, or a vinyl group;


Zal1 represents —O—, —S—, —CO—, —CO—O—, —OCO—, —O—CO—O—, —OCH2—, —CH2O—, —SCH2—, —CH2S—, —CF2O—, —OCF2—, —CF2S—, —SCF2—, —(CH2)nal—, —CF2CH2—, —CH2CF2—, —(CF2)nal—, —CH═CH—, —CF═CF—, —C≡C—, —CH═CH—COO—, —OCO—CH═CH—, —(CRal3Ral4)nal—, —CH(-Spal1-Xal1)—, —CH2CH(-Spal1-Xal1)—, or —CH(-Spal1-Xal1)CH(-Spal1-Xal1);


Zal2 represents a single bond, —O—, —S—, —CO—, —CO—O—, —OCO—, —O—CO—O—, —OCH2—, —CH2O—, —SCH2—, —CH2S—, —CF2O—, —OCF2—, —CF2S—, —SCF2—, —(CH2)n1-, —CF2CH2—, —CH2CF2—, —(CF2)nal—, —CH═CH—, —CF═CF—, —C≡C—, —CH═CH—COO—, —OCO—CH═CH—, —(CRal3Ral4)nal, —CH(-Spal1-Xal1)—, —CH2CH(-Spal1-Xal1)—, or —CH(-Spal1-Xal1)CH(-Spal1-Xal1);


Lal1, Lal2, and Lal3 each independently represent a hydrogen atom, a fluorine atom, a chlorine atom, a bromine atom, an iodine atom, —CN, —NO2, —NCO, —NCS, —OCN, —SCN, —C(═O)N(Ral3)2, —C(═O)Ral3, an optionally substituted silyl group having 3 to 15 carbon atoms, an optionally substituted aryl or cycloalkyl group or 1 to 25 carbon atoms, wherein one or two or more hydrogen atoms may be replaced by a halogen atom (fluorine atom, chlorine atom);


Ral3 represents an alkyl group having 1 to 12 carbon atoms; Ral4 represents a hydrogen atom or an alkyl group having 1 to 12 carbon atoms; nal represents an integer of 1 to 4;


pal1 and pal2 each independently represent 0 or 1; mal1, mal2 and mal3 each independently represent an integer of 0 to 3; and nal1, nal2 and nal3 each independently represent an integer of 0 to 3.


General Formula (ii):



embedded image


In the formula, Zii1 represents a single bond, —CH═CH—, —CF═CF—, —C≡C—, —COO—, —OCO—, —OCOO—, —OOCO—, —CF2O—, —OCF2—, —CH═CHCOO—, —OCOCH═CH—, —CH2—CH2COO—, —OCOCH2—CH2—, —CH═C(CH3)COO—, —OCOC(CH3)═CH—, —CH2—CH(CH3)COO—, —OCOCH(CH3)—CH2—, —OCH2CH2O—, or an alkylene group having 2 to 20 carbon atoms, and one or two or more non-adjacent —CH2— in the alkylene group may be substituted with —O—, —COO—, or —OCO—;


Aii1 represents a divalent 6-membered ring aromatic group, a divalent 6-membered ring heteroaromatic group, a divalent 6-membered ring aliphatic group, or a divalent 6-membered heteroaliphatic group, wherein a hydrogen atom in these cyclic structures may be substituted with a halogen atom, P11—S11—, a monovalent organic group having a polar group represented by the general formula (K), or Ri1, but at least one is substituted with P11—S11—; in the case where a plurality of each of Zii1 and Aii1 are present, these may be the same as or different from each other;


mii1 represents an integer of 1 to 5;


Rii1 and Rii2 each independently represent a hydrogen atom, a linear or branched alkyl group having 1 to 40 carbon atoms, a halogenated alkyl group, or Pi1-Spi1-, and —CH2— in the alkyl group may be substituted with —CH═CH—, —C≡C—, —O—, —NH—, —COO—, or —OCO—, but —O— is not continuous, at least one of Rii1 and Rii2 represents a monovalent organic group having a polar group represented by the general formula (K), and one or two or more P11—S12 in the general formula (ii), one or two or more monovalent organic groups having a polar group represented by the general formulae (K), and one or two or more Rii1.


The above P11—S12— (wherein P11 represents a polymerizable group, and represents a substituent selected from the group represented by the general formulae (R-I) to (R-IX)), a monovalent organic group having a polar group represented by the general formula (K) (wherein the general formula (K) has a partial structure represented by any of the general formulae (K-1) to (K-23)), and Ri1 (wherein Ri1 represents a hydrogen atom, a linear or branched alkyl group having 1 to 40 carbon atoms, a halogenated alkyl group, or Pi1-Spi1-, and —CH2— in the alkyl group may be substituted with —CH═CH—, —C≡C—, —O—, —NH—, —COO—, or —OCO—, but —O— is not continuous.


In the general formula (ii), Zii1 preferably represents a single bond, —CH═CH—, —C≡C—, —COO—, —OCO—, —OCOO—, —OOCO—, —CH═CHCOO—, —OCOCH═CH—, —CH2—CH2COO—, —OCOCH2—CH2—, —CH═C(CH3)COO—, —OCOC(CH3)═CH—, —CH2—CH(CH3)COO—, —OCOCH(CH3)—CH2—, —OCH2CH2O—, or a linear or branched alkylene group having 1 to 40 carbon atoms, or a group in which one or two or more non-adjacent —CH2— in the alkylene group are substituted with —O—, more preferably represents a single bond, —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH2—CH2COO—, —OCOCH2—CH2—, —CH═C(CH3)COO—, —OCOC(CH3)═CH—, —CH2—CH(CH3)COO—, —OCOCH(CH3)—CH2—, —OCH2CH2O—, or a linear or branched alkylene group having 1 to 40 carbon atoms, or a group in which one or two or more non-adjacent —CH2— in the alkylene group are substituted with —O—, a single bond, a linear or branched alkylene group having 2 to 15 carbon atoms, or a group in which one or two or more non-adjacent —CH2— in the alkylene group are substituted with —O—, and still more preferably represents a single bond, CH2—CH2COO—, —OCOCH2—CH2—, —CH═C(CH3)COO—, —OCOC(CH3)═CH—, —CH2—CH(CH3)COO—, —OCOCH(CH3)—CH2—, —OCH2CH2O—, or an alkylene group having 2 carbon atoms (ethylene group (—CH2CH2—)) or a group in which one —CH2— in the ethylene group is substituted with —O— (—CH2O—, —OCH2—), or a linear alkylene group having 3 to 13 carbon atoms or a group in which one or two or more non-adjacent —CH2— in the alkylene group are substituted with —O—.


Aii1 preferably represents a divalent 6-membered aromatic group or a divalent 6-membered aliphatic group, but a divalent unsubstituted 6-membered aromatic group or a divalent unsubstituted 6-membered aliphatic group is preferable, and a hydrogen atom in these cyclic structures is preferably not substituted or substituted with an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or a halogen atom. Preferred is a divalent unsubstituted 6-membered aromatic group or a group in which a hydrogen atom in this cyclic structure is substituted with a fluorine atom, or a divalent unsubstituted 6-membered cyclic aliphatic group, and preferred is a 1,4-phenylene group, a 2,6-naphthalene group or a 1,4-cyclohexyl group in which a hydrogen atom on the substituent may be substituted with a halogen atom, an alkyl group or an alkoxy group, but at least one substituent is substituted with Pi1-Spi1-.


mii1 preferably represents an integer of 2 to 5, and more preferably represents an integer of 2 to 4.


General Formula (iii):




embedded image


In the general formula (iii), Riii1 is an alkyl group having 1 to 15 carbon atoms, in which at least one —CH2— in the alkyl group may be substituted with —O— or —S— and has at least one —(CH2)2— may be substituted with —CH═CH— or —C≡C—, and in these groups, at least one hydrogen atom may be substituted with a halogen atom;


Aiii1 and Aiii4 are each independently 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, naphthalene-2,6-diyl, decahydronaphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, tetrahydropyran-2,5-diyl, 1,3-dioxane-2,5-diyl, pyrimidine-2,5-diyl, pyridine-2,5-diyl, fluorene-2,7-diyl, phenanthrene-2,7-diyl, anthracene-2,6-diyl, perhydrocyclopenta [a] phenanthrene-3,17-diyl, or 2,3,4,7,8,9,10,11,12,13,14,15,16,17-tetradecahydrocyclopent a [a] phenanthrene-3,17-diyl, and in these rings, at least one hydrogen atom may be substituted with a fluorine atom, a chlorine atom, an alkyl group having 1 to 12 carbon atoms, an alkenyl group having 2 to 12 carbon atoms, an alkoxy group having 1 to 11 carbon atoms, or an alkenyloxy group having 2 to 11 carbon atoms, and at least one hydrogen atom in these groups may be substituted with a fluorine atom or a chlorine atom;


Ziii1 is a single bond or alkylene having 1 to 10 carbon atoms, and in the alkylene, at least one —CH2— may be substituted with —O—, —CO—, —COO—, —OCO—, or —OCOO—, at least one —(CH2)2— may be substituted with —CH═CH— or —C≡C—, and in these groups, at least one hydrogen atom may be substituted with a halogen atom;


Siii1 is a single bond or an alkylene group having 1 to 10 carbon atoms, and in the alkylene group, at least one —CH2— may be substituted with —O—, —CO—, —COO—, —OCO—, or —OCOO—, at least one —(CH2)2— may be substituted with —CH═CH— or —C≡C—, and in these groups, at least one hydrogen may be substituted with a halogen atom;


Kiii1 and Kiii2 are each independently a hydrogen atom, a halogen atom, an alkyl group having 1 to 5 carbon atoms, or an alkyl group having 1 to 5 carbon atoms in which at least one hydrogen atom is substituted with a halogen atom (for example, a fluorine atom);


niii1 is 0, 1, 2, 3, or 4;


Riii2 is a group represented by formula (iii-1) or formula (iii-2).




embedded image


In formula (iii-1) and formula (iii-2),


Siii2 and Siii3 are each independently a single bond or an alkylene group having 1 to 10 carbon atoms, and in the alkylene group, at least one —CH2— may be substituted with —O—, —NH—, —CO—, —COO—, —OCO—, or —OCOO—, and at least one —(CH2)2— may be substituted with —CH═CH— or —C≡C—, and in these groups, at least one hydrogen atom may be substituted with a halogen atom;


Siii1 is ═CH— or ═N—;


Xiii1 is a group represented by —OH, —NH2, —OR3, —N(R3)2, Formula (Xiii1), —COOH, —SH, —B(OH)2, or —Si (R3)3, wherein R3 is a hydrogen atom or an alkyl group having 1 to 10 carbon atoms, and in the alkyl group, at least one —CH2— may be substituted with —O— or —CH═CH—, and in these groups, at least one hydrogen atom may be substituted with a halogen atom; Formula (Xiii1):




embedded image


(wherein niii2 is an integer of 1 to 5.)


General Formula (iv):



embedded image


Since the compound represented by the general formula (iv) has a partial structure represented by Ki1, when used in a liquid crystal composition, it is possible to align the compound on a substrate holding the liquid crystal composition (liquid crystal layer) and liquid crystal molecules can be held in a state of being aligned in the vertical direction. Since the compound represented by the general formula (iv) has a polar partial structure represented by Ki1, it is considered that the compound is adsorbed to the substrate holding the liquid crystal composition (liquid crystal layer) and that the compound has a partial structure represented by Ki1 at the end of the compound, so that liquid crystal molecules are held in a state of being aligned in the vertical direction. Therefore, according to the liquid crystal composition using the polymerizable compound of the present embodiment, it is possible to align liquid crystal molecules without providing the PI layer (vertical alignment of liquid crystal molecules is induced when no voltage is applied, and horizontal alignment of liquid crystal molecules can be achieved when voltage is applied). Therefore, the liquid crystal composition containing the compound (iv) is suitably used to aid in the vertical alignment of liquid crystal molecules.


In addition, the present inventors have found that a liquid crystal composition containing the compound (iv) in the present embodiment has a partial structure represented by Ki1, whereby not only the alignment of liquid crystal molecules but also the storage stability of the liquid crystal composition can be secured.


Further, since the liquid crystal composition containing the compound (iv) represented by the general formula (iv) has a polymerizable group at a specific position as a substituent of Ai2 or Ai3 or a substituent of Ki1, it is possible to maintain a better orientation.


In view of the above, the compound (iv) in the liquid crystal composition of the present embodiment may have a partial structure represented by Ki1 at the terminal of the molecule, preferably at the end of the main chain of the molecule, and the chemical structure of the binding target to which the partial structure represented by Ki1 is bonded is not particularly limited as long as it does not inhibit the function of the liquid crystal composition.


Specific examples of the compound represented by the general formula (iv) will be described below.


Ki1 in the general formula (iv) is preferably a linear or branched alkyl group having 3 to 40 carbon atoms, a linear or branched halogenated alkyl group having 3 to 40 carbon atoms, or a linear or branched cyanated alkyl group having 3 to 40 carbon atoms, wherein at least two or more secondary carbon atoms in Ki1 are substituted with —(C═Xi1)— and/or —(CH—CN)—, at least two or more secondary carbon atoms in Ki1 are preferably substituted with —(C═Xi1)—, at least three or more secondary carbon atoms are preferably substituted with —(C═Xi1)—, and at least four or more secondary carbon atoms are preferably substituted with —(C═Xi1)—. Xi1 is preferably an oxygen atom from the viewpoint of improving the voltage holding ratio (VHR). Ki1 preferably represents a linear or branched alkyl group having 3 to 30 carbon atoms, a linear or branched halogenated alkyl group, or a linear or branched cyanated alkyl group, and a secondary carbon atom in the alkyl group may be substituted with —(C═CH2)—, —(C═CHRi3)—, —(C═CRi32)—, —CH═CH—, —C≡C—, or —O— so long as oxygen atoms are not directly adjacent to each other, more preferably represents a linear or branched alkyl group having 3 to 20 carbon atoms or a linear or branched cyanated alkyl group, and a secondary carbon atom in the alkyl group may be substituted with —(C═CH2)—, —(C═CHR3)—, —(C═CRi32)—, or —O— so long as oxygen atoms are not directly adjacent to each other, and more preferably represents a branched alkyl group having 3 to 20 carbon atoms or a branched cyanated alkyl group, and a secondary carbon atom in the alkyl group may be substituted with —(C═CH2)—, or —O— so long as oxygen atoms are not directly adjacent to each other. Ri3 is preferably a linear or branched alkyl group having 1 to 10 carbon atoms, preferably an alkyl group having 1 to 7 carbon atoms, preferably an alkyl group having 1 to 3 carbon atoms, and a secondary carbon atom in the alkyl group may be substituted with —O—, —CH═CH—, or —C═C— so long as oxygen atoms are not directly adjacent to each other.


It is also preferred that the hydrogen atom in Ki1 is substituted with a polymerizable group, i.e., Pi1-Spi1-. When a polar group and a polymerizable group are present in the Ki1, a better orientation is obtained.


Ki1 preferably represents the general formula (K-24).




embedded image


In the formula, Yi1 represents a linear or branched alkyl group having 3 to 20 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and at least two or more secondary carbon atoms in these alkyl groups are substituted with —(C═Xi1)— and/or —(CH—CN)—, and the secondary carbon atom in the alkyl groups may be substituted with —CH═CH—, —C≡C—, —O—, —NH—, —COO—, or —OCO— so long as oxygen atoms are not directly adjacent to each other, and the hydrogen atom in these alkyl groups may be substituted with Pi1-Spi1-, wherein Xi1 represents an oxygen atom, a sulfur atom, NH, or NRi3;


Si1 and Si3 each independently represent an alkylene group having 1 to 6 carbon atoms or a single bond, and —CH2— in the alkylene group may be substituted with —CH═CH—, —C≡C—, —(C═CH2)—, —(C═CHRi3)—, —(C═CRi32)—, —O—, —NH—, —(C═O)—, —COO—, or —OCO— so long as oxygen atoms are not directly adjacent to each other;


Si2 represents a carbon atom, a nitrogen atom, or a silicon atom;


Ri2 represents a hydrogen atom, a linear or branched alkyl group having 1 to 20 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and a secondary carbon atom in these groups may be substituted with —O—, —CH═CH—, —C≡C—, —C(═Xi1)—, or —CH(—CN)— so long as oxygen atoms are not directly adjacent to each other;


Pi1 represents a polymerizable group;


Spi1 represents a spacer group or a single bond;


ni1 represents an integer of 1 to 3; ni2 and ni3 each independently represent an integer of 0 to 2, but when Si2 represents a carbon atom or a silicon atom, ni1+ni2+ni3 is 3, and when Si2 represents a nitrogen atom, ni1+ni2+ni3 is 2. Ri3 has the same meaning as Ri3 in the general formula (i), and in the case where a plurality of each of Ri2, Xi1, Yi1, Si1, Si3, Pi1, and Spi1 are present in the general formula (K-1), these may be the same as or different from each other.


Si1 and Si3 in the general formula (K-1) are preferably a linear or branched alkylene group having 1 to 6 carbon atoms or a single bond, and —CH2— in the alkylene group may be substituted with —CH═CH—, —(C═CH2)—, —O—, —(C═O)—, —COO—, or —OCO— so long as oxygen atoms are not directly adjacent to each other, and more preferably a single bond, a linear alkylene group having 1 to 6 carbon atoms, or a group in which —CH2— in the alkylene group is substituted with —O— so long as oxygen atoms are not directly adjacent to each other. Si1 and Si3 specifically and preferably represent —(CH2)n-, —O—(CH2)n-, —(CH2)n-O—, —(CH2)n-O— (CH2)m-, —COO— (CH2)n-, or —OCO— (CH2)n- (n and m represent an integer of 1 to 6).


Si2 is preferably a carbon atom. Ri2 preferably represents a hydrogen atom or a linear or branched alkyl group having 1 to 10 carbon atoms, and —CH2— in the alkyl group may be substituted with —O—, —C(═Xi1)—, or —CH(—CN)— (wherein —O— is not continuous), preferably represents a hydrogen atom or a linear or branched alkyl group having 1 to 7 carbon atoms. And —CH2— in the alkyl group may be substituted with —O—, —C(═Xi1)—, or —CH(—CN)— (wherein —O— is not continuous), and more preferably a hydrogen atom or a linear alkyl group having 1 to 3 carbon atoms.


Yi1 is an alkyl group having 3 to 20 carbon atoms, a linear or branched halogenated alkyl group having 3 to 20 carbon atoms, or a linear or branched cyanated alkyl group having 3 to 20 carbon atoms, wherein at least two or more secondary carbon atoms in Yi1 are substituted with —(C═Xi1)— and/or —(CH—CN)—, and at least two or more secondary carbon atoms in Yi1 are preferably substituted with —(C═X1)—. Xi1 is preferably an oxygen atom from the viewpoint of improving the voltage holding ratio (VHR). Yi1 preferably represents a linear or branched alkyl group having 3 to 10 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and a secondary carbon atom in the alkyl group may be substituted with —(C═CH2)—, —(C═CHRi3)—, —(C═CRi32)—, —CH═CH—, —C≡C—, or —O— so long as oxygen atoms are not directly adjacent to each other, more preferably represents a linear or branched alkyl group having 3 to 7 carbon atoms or a cyanated alkyl group, and a secondary carbon atom in the alkyl group may be substituted with —(C═CH2)—, —(C═CHRi3)—, —(C═CRi32)—, or —O— so long as oxygen atoms are not directly adjacent to each other, and more preferably represents a linear or branched alkyl group having 3 to 7 carbon atoms, and a secondary carbon atom in the alkyl group may be substituted with —O— so long as oxygen atoms are not directly adjacent to each other. In addition, the hydrogen atom in the alkyl group may be substituted with pi1-Spi1-.


It is preferable that Yi1 represents a group selected from the general formula (Y-1) from the viewpoint of improving the alignment property of the liquid crystal.




embedded image


In the formula, WiY1 represents a single bond or an oxygen atom; a broken line represents a single bond or a double bond; RiY1 represents a hydrogen atom, a linear or branched alkyl group having 1 to 20 carbon atoms, or Pi1-Spi1-, and a secondary carbon atom in the alkyl group may be substituted with —O—, —CH═CH—, —C≡C—, or —CO— so long as oxygen atoms are not directly adjacent to each other, when the broken line represents a single bond, and RiY1 represents ═CH2, ═CHRiY4, or ═CRiY42 when the broken line represents a double bond, and RiY4 represents a hydrogen atom or a linear or branched alkyl group having 1 to 20 carbon atoms, and a secondary carbon atom in the alkyl group may be substituted with —O—, —CH═CH—, or —C≡C— so long as oxygen atoms are not directly adjacent to each other; RiY3 represents the same meaning as RiY1 when the broken line represents a single bond; RiY2 represents a hydrogen atom, a linear or branched alkyl group having 1 to 20 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and the secondary carbon atom in these alkyl groups may be substituted with —CH═CH—, —C≡C—, —O—, —NH—, —COO—, —OCO—, —C(═O)—, or —CH2(—CN)— so long as oxygen atoms are not directly adjacent to each other and RiY2 represents Pi1-Spi1-; niY1 is 0 when the broken line represents a double bond, and niY1 is 1 when the broken line represents a single bond; niY2 represents an integer of 0 to 5; Pi1 represents a polymerizable group; Spi1 represents a spacer group or a single bond; and in the case where a plurality of RiY1, RiY3, RiY4, Pi1, and Spi1 are present, these may be the same as or different from each other; and the structure of the formula binds to Si3 at *.


RiY1 is preferably a hydrogen atom or a linear or branched alkyl group having 1 to 10 carbon atoms, preferably a hydrogen atom or an alkyl group having 1 to 7 carbon atoms, preferably a hydrogen atom or an alkyl group having 1 to 3 carbon atom when the broken line represents a single bond, and a secondary carbon atom in the alkyl group may be substituted with —O—, —CH═CH— or —C≡C— so long as oxygen atoms are not directly adjacent to each other. Specifically, RiY1 preferably represents a hydrogen atom, and from the viewpoint of improving heat resistance, RiY1 preferably represents an alkyl group having 1 to 3 carbon atoms, an alkoxy group having 1 to 3 carbon atoms, —CO—CH3, or —CH2—O—CH3. Further, from the viewpoint of improving heat resistance, RiY1 preferably represents Pi1-Spi1-. When RiY1 represents Pi1-Spi1-, it is considered that the decomposition product generated by the decomposition of the compound represented by the general formula (i) by heat is polymerized, so that the increase in impurities can be prevented and the adverse effect on the liquid crystal composition is reduced. Pi1 represents a polymerizable group, and preferably represents an acryloyl group, a methacryloyl group, or a substituent selected from the group represented by the general formulae (P-1) to (P-15) described later. Spi1 preferably represents a linear alkylene group having 1 to 18 carbon atoms or a single bond, more preferably represents a linear alkylene group having 2 to 15 carbon atoms or a single bond, and still more preferably represents a linear alkylene group having 2 to 8 carbon atoms or a single bond.


When the broken line represents a double bond, it represents ═CH2, ═CHRiY4, or ═CRiY42, and it preferably represents CH2. RiY4 is preferably a linear or branched alkyl group having 1 to 10 carbon atoms, preferably an alkyl group having 1 to 7 carbon atoms, preferably an alkyl group having 1 to 3 carbon atoms, and a secondary carbon atom in the alkyl group may be substituted with —O—, —CH═CH—, or —C≡C— so long as oxygen atoms are not directly adjacent to each other.


A preferred group of RiY3 is the same as the preferred group of RiY1 in the case where the broken line represents a single bond. niY1 is preferably 0.


Preferable combinations of RiY1 and RiY3 include both hydrogen atoms, both alkyl groups having 1 to 3 carbon atoms, both alkoxy groups having 1 to 3 carbon atoms, and both —CH2—O—CH3. When one of RiY1 and RiY3 represents Pi1-Spi1- or —CO—CH3, it is preferable that the other represents a hydrogen atom. niY2 is preferably an integer of 0 to 3, more preferably 0, 1, or 2, and still more preferably 0 or 1.


RiY2 is preferably a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, preferably an alkyl group having 1 to 7 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and preferably an alkyl groups having 1 to 3 carbon atoms.


In addition, it is preferable that the secondary carbon atom in the alkyl group is substituted with —O—, —(C═Xi2)—, or —(CH2—CN)— so long as oxygen atoms are not directly adjacent to each other. X12 is preferably an oxygen atom from the viewpoint of improving VHR. RiY2 preferably represents Pi1-Spi1-. When RiY2 represents Pi1-Spi1-, it is considered that the decomposition product generated by the decomposition of the compound represented by the general formula (i) by heat is polymerized, so that the increase in impurities can be prevented and the adverse effect on the liquid crystal composition is reduced.


More specifically, the general formula (Y-1) is preferably a formula (Y-1-1), (Y-1-2), (Y-1-3a), (Y-1-3b), or (Y-1-4).




embedded image


In the formulae, niY11 represents 0 or 1, RiY21 represents an alkyl group having 1 to 10 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and the secondary carbon atom in these alkyl groups may be substituted with —CH═CH—, —C≡C—, —O—, —NH—, —COO—, —OCO—, —(C═O)—, or —(CH2—CN)— so long as oxygen atoms are not directly adjacent to each other, and RiY21 represents Pi1-Spi1-, RiY31 and RiY32 each independently represent a hydrogen atom or a linear or branched alkyl group having 1 to 10 carbon atoms, and the secondary carbon atom in the alkyl group may be substituted with —O—, —CH═CH—, —C≡C—, or —CO— so long as oxygen atoms are not directly adjacent to each other, and RiY31 and RiY32 represent Pi1-Spi1-.


RiY21 is preferably an alkyl group having 1 to 7 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and more preferably an alkyl group having 1 to 3 carbon atoms. RiY21 preferably represents Pi1-Spi1-. RiY31 and RiY32 are preferably a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or an alkoxy group having 1 to 5 carbon atoms, and preferably represent a hydrogen atom or an alkyl group having 1 to 3 carbon atoms, an alkoxy group having 1 to 3 carbon atoms, —CO—CH3, —CH2—O—CH3. It is preferable that at least one of RiY31 and RiY32 represents Pi1-Spi1-.


From the viewpoint of improving compatibility with a liquid crystal compound, it is preferable to have a structure of the formula (Y-1-1). As the formula (Y-1-1), the formulae (Y-1-1a) to (Y-1-1h) are preferable.




embedded image


embedded image


In the formulae, niY11 represents 0 or 1.


From the viewpoint of improving compatibility with the liquid crystal compound and heat resistance, it is preferable to have a structure of the formula (Y-1-2). As the formula (Y-1-2), the formulae (Y-1-2a) to (Y-1-2f) are preferable.




embedded image


In the formulae, niY11 represents 0 or 1. From the viewpoint of improving heat resistance, it is preferable to have a structure of the formula (Y-1-3a) and the formula (Y-1-3b). As the formula (Y-1-3a), the formula (Y-1-3aa) is preferable and as the formula (Y-1-3b), the formula (Y-1-3ba) is preferable.




embedded image


In the formulae, niY11 represents 0 or 1.


From the viewpoint of improving alignment property and voltage holding ratio of the liquid crystal composition, it is preferable to have a structure of the formula (Y-1-4).


As the formula (Y-1-4), the formulae (Y-1-4a) to (Y-1-4f) are preferable. In particular, the structures (Y-1-4a) to (Y-1-4c) are preferable because the balance between the compatibility of the liquid crystal compound and the alignment property of the liquid crystal composition is well-balanced.




embedded image


In the formulae, niY11 represents 0 or 1.


Yi1 preferably represents a group selected from the general formula (Y-2).




embedded image


In the formula, WiY1, RiY3, and RiY2 have the same meanings as WiY1, RiY3, and RiY2 in the general formula (Y-1), respectively.


The general formula (Y-2) preferably represents the general formula (Y-2-1).




embedded image


In the formula, niY11, RiY21, and Ri31 have the same meanings as niY11, RiY21, and Ri31 in the general formula (Y-1-1), respectively.


In addition, Yi1 preferably represents a group selected from the general formula (Y-3) from the viewpoint of improving heat resistance.




embedded image


In the formula, RiY1, RiY2, RiY3, niY1, and niY1 have the same meanings as RiY1, RiY2, RiY3, niY1, and niY1 in the general formula (Y-1), respectively.


The general formula (Y-3) preferably represents the general formula (Y-3-1) to the general formula (Y-3-4).




embedded image


In the formulae, RiY21, RiY31, RiY32, and niY11 have the same meanings as RiY21, RiY31, RiY32, and niY11 in the general formula (Y-1-1), respectively.


More specifically, the general formula (Y-3-1) is preferably the general formula (Y-3-11).




embedded image


In the formula, RiY21 has the same meaning as RiY21 in the general formula (Y-3-1).


In addition, Yi1 preferably represents a group selected from the general formula (Y-4) from the viewpoint of improving heat resistance.




embedded image


In the formula, RiY1, RiY2, RiY3, niY1, and niY1 have the same meanings as RiY1, RiY2, RiY3, niY1, and niY1 in the general formula (Y-1), respectively.


The general formula (Y-4) preferably represents the general formula (Y-4-1) to the general formula (Y-4-3b).




embedded image


In the formulae, RiY21, RiY31, RiY32, and niY11 have the same meanings as RiY21, RiY31, RiY32, and niY11 in the general formula (Y-1-1), respectively.


More specifically, the general formula (Y-4-1) is preferably the general formula (Y-4-11).




embedded image


In the formula, RiY21 has the same meaning as RiY21 in the general formula (Y-4-1).


Pi1 preferably represents a substituent selected from the group represented by the following formulae (P-1) to (P-15). From the viewpoint of handling convenience and reactivity, any one of the substituents represented by the formulae (P-1) to (P-3) and (P-14), (P-15) is preferred, and the formulae (P-1) and (P-2) are more preferred.




embedded image


embedded image


In the formulae, the black dot on the right end represents a bonding site.


Spi1 preferably represents a linear alkylene group having 1 to 18 carbon atoms or a single bond, more preferably represents a linear alkylene group having 2 to 15 carbon atoms or a single bond, and still more preferably represents a linear alkylene group having 2 to 8 carbon atoms or a single bond.


ni1 preferably represents 1 or 2 from the viewpoint of improving alignment property of the liquid crystal and solubility in the liquid crystal compound. ni2 preferably represents 0 or 1, and more preferably represents 1 from the viewpoint of improving alignment property.


ni3 preferably represents 0 or 1.


The general formula (K-24) preferably represents a group selected from the general formula (K-24A) or (K-24B).




embedded image


In the formulae, Si1, Si2, Si3, Yi1, Pi1, and Spi1 have the same meanings as Si1, Si2, Si3, Yi1, Pi1, and Spi1 in the general formula (K-1), niA1 represents an integer of 1 to 3, niA3 represents an integer of 0 to 2, niB1 represents an integer of 1 to 2, and niB3 represents 0 or 1, but when Si2 represents a carbon atom or a silicon atom, niA1+niA3 is 3 and niB1+niB3 is 2, when Si2 represents a nitrogen atom, niA1+niA3 is 2, niB1 is 1, and niB3 is 0.


Ki1 in the formula (i) is an important structure for vertically aligning the liquid crystal composition, and since the polar group and the polymerization group are adjacent to each other, better alignment property can be obtained and good solubility in the liquid crystal composition is also exhibited. Therefore, when the alignment property of liquid crystal is important, the general formula (K-24B) is preferable. On the other hand, when the solubility in a liquid crystal compound is important, the general formula (K-24A) is preferable. Preferred examples of the general formulae (K-24A) to (K-24B) include the following formulae (K-24A-1) to (K-24A-4) and formulae (K-24B-1) to (K-24B-6), and from the viewpoint of solubility in the liquid crystal composition, the formulae (K-24A-1) to (K-24A-3) are preferable, and from the viewpoint of alignment property, the formulae (K-24B-2) to (K-24B-4) are preferable, and the formulae (K-24A-1), (K-24B-2), and (K-24B-4) are particularly preferable.




embedded image


In the formulae, Si1, Yi1, and Pi1 independently have the same meanings as Si1, Yi1, and Pi1 in the general formula (K-24), respectively.


The general formula (K-24) preferably represents a group selected from the general formulae (K-24-1), (K-24-2), (K-24-3a), (K-24-3b), (K-24-4a), (K-24-4b), (K-24-Y2), (K-24-Y3), and (K-24-Y4).




embedded image


embedded image


In the formulae, niY11, RiY21, RiY31, and RiY32 independently have the same meanings as niY11, RiY21, RiY31, and RiY32 in the general formulae (Y-1-1) to (Y-4), respectively, Spi1 and Pi1 have the same meanings as Spi1 and Pi1 in the general formula (i), respectively, RiK1 represents an alkylene group having 1 to 6 carbon atoms or a single bond, and —CH2— in the alkylene group may be substituted with —CH═CH—, —C≡C—, or —O— so long as oxygen atoms are not directly adjacent to each other, and niK1 and niK2 each independently represent 0 or 1.


RiK1 is preferably a linear alkylene group having 1 to 6 carbon atoms, and more preferably a linear alkylene group having 1 to 3 carbon atoms. Preferred groups of RiY21, RiY31, RiY32, Spi1, and Pi1 are the same as RiY21, RiY31, RiY32, Spi1, and Pi1 of the general formulae (Y-1-1) to (Y-1-4), (Y-2) to (Y-4), and the general formula (i).


Further, Ki1 preferably represents the general formulae (K-25) to (K-28)




embedded image


In the formulae, Si1, Pi1, and Spi1 have the same meanings as Si1, pi1, and Spi1 in the general formula (K-24), respectively, RK21 represents a linear or branched alkyl group having 1 to 10 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and at least one or more secondary carbon atoms in these alkyl groups may be substituted with —CH═CH—, —C≡C—, —O—, or —NH— so long as oxygen atoms are not directly adjacent to each other, and ni4 and niK21 each independently represent 0 or 1.


RK21 preferably represents a linear or branched alkyl group having 1 to 5 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group, and more preferably represents a linear alkyl group having 1 to 3 carbon atoms or a cyanated alkyl group. In addition, at least one or more secondary carbon atoms in these alkyl groups are preferably substituted with —O— so long as oxygen atoms are not directly adjacent to each other. Specifically, RK21 is preferably an alkyl group having 1 to 3 carbon atoms, an alkoxy group having 1 to 3 carbon atoms, or a cyanated alkyl group having 1 to 3 carbon atoms.


The general formula (K-25) preferably represents the following general formulae (K-25-1) to (K-25-3).




embedded image


In the formulae, Si1, Pi1, Spi1, ni4, and niK21 have the same meanings as Si1, Pi1, Spi1, ni4, and niK21 in the general formula (K-25), respectively, RK211 represents a linear or branched alkyl group having 1 to 3 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group.


The general formula (K-26) preferably represents the following general formulae (K-26-1) and (K-26-2).




embedded image


In the formulae, Si1 has the same meaning as Si1 in the general formula (K-26), RK211 represents a linear or branched alkyl group having 1 to 3 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group.


The general formula (K-27) preferably represents the following general formula (K-27-1).




embedded image


In the formula, Si1, Pi1, Spi1, and ni4 have the same meanings as Si1, Pi1, Spi1, and niK21 in the general formula (K-27), respectively, RK211 represents a linear or branched alkyl group having 1 to 3 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group.


The general formula (K-28) preferably represents the following general formula (K-28-1).




embedded image


In the formula, Si1, Pi1, Spi1, and ni4 have the same meanings as Si1, Pi1, Spi1, and niK21 in the general formula (K-28), respectively, RK211 represents a linear or branched alkyl group having 1 to 3 carbon atoms, a halogenated alkyl group, or a cyanated alkyl group.


Preferred groups of Si1, pi1, and Spi1 are the same as Si1, Pi1, and Spi1 in the general formula (K-24).


In formula (i), Zi1 and Zi1 preferably represent a single bond, —CH═CH—, —C≡C—, —COO—, —OCO—, —OCOO—, —OOCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═C(CH3)COO—, —OCOC(CH3)═CH—, —CH2—CH(CH3)COO—, —OCOCH(CH3)—CH2—, —OCH2CH2O—, a linear or branched alkylene group having 1 to 40 carbon atoms, or a group in which one or two or more non-adjacent —CH2— in the alkylene group is substituted with —O—; more preferably represent a single bond, —COO—, —OCO—, —CH═CHCOO—, —OCOCH═CH—, —CH═C(CH3)COO—, —OCOC(CH3)═CH—, —CH2—CH(CH3)COO—, —OCOCH(CH3)—CH2—, —OCH2CH2O—, a linear or branched alkylene group having 1 to 10 carbon atoms, or a group in which one or two or more non-adjacent —CH2— in the alkylene group is substituted with —O—; more preferably represent a single bond, a linear alkylene group having 2 to 15 carbon atoms, or a group in which one or two or more non-adjacent —CH2— in the alkylene group is substituted with —O—; and still more preferably represent a single bond, —COO—, —OCO—, —OCOO—, —OOCO—, —OCH2CH2O—, or an alkylene group having 2 carbon atoms (ethylene group (—CH2CH2—)), a group in which one of —CH2— in the ethylene group is substituted with —O— (—CH2O—, —OCH2—), or a group in which one of —CH2— in the ethylene group is substituted with —COO— or —OCO— (—CH—CHCOO—, —OCOCH—CH—).


Ri1 preferably represents a linear or branched alkyl group having 1 to 20 carbon atoms, or a halogenated alkyl group, and the secondary carbon atom in the alkyl group is preferably substituted with —O— so long as oxygen atoms are not directly adjacent to each other, and more preferably represents a linear or branched alkyl group having 3 to 18 carbon atoms, and the secondary carbon atom in the alkyl group may be substituted with —O— so long as oxygen atoms are not directly adjacent to each other. From the viewpoint of improving the alignment property of the liquid crystal compound, the carbon atom number of Ri1 is preferably 3 or more, preferably 4 or more, and preferably 5 or more.


Ai1 preferably is a divalent 6-membered aromatic group, a divalent 6-membered heteroaromatic group, a divalent 6-membered aliphatic group, or a divalent 6-membered heteroaliphatic group, a divalent 5-membered aromatic group, a divalent 5-membered heteroaromatic group, a divalent 5-membered aliphatic group, or a divalent 5-membered heteroaliphatic group, and specifically, preferably represents a cyclic structure selected from a 1,4-phenylene group, a 1,4-cyclohexylene group, an anthracene-2,6-diyl group, a phenanthrene-2,7-diyl group, a pyridine-2,5-diyl group, a pyrimidine-2,5-diyl group, a naphthalene-2, 6-diyl group, a cyclopentane-1,3-diyl group, an indan-2,5-diyl group, a 1,2,3,4-tetrahydronaphthalene-2,6-diyl group, and a 1,3-dioxane-2,5-diyl group, and the cyclic structure is preferably unsubstituted or substituted with Li1.


Li1 preferably is an alkyl group having 1 to 12 carbon atoms, a halogenated alkyl group having 1 to 12 carbon atoms, an alkoxy group having 1 to 12 carbon atoms, a halogenated alkoxy group having 1 to 12 carbon atoms, a halogen atom, a cyano group, or a nitro group. Ail preferably represents a divalent 6-membered aromatic group or a divalent 6-membered aliphatic group, but a divalent unsubstituted 6-membered aromatic group or a divalent unsubstituted 6-membered aliphatic group, or a group in which a hydrogen atom in these cyclic structures is substituted with an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, or a halogen atom is preferable, a divalent unsubstituted 6-membered aromatic group or a group in which a hydrogen atom in the cyclic structure is substituted with a fluorine atom, or a divalent unsubstituted 6-membered aliphatic group is preferable, and a 1,4-phenylene group, 2,6-naphthalene group, or 1,4-cyclohexyl group in which a hydrogen atom on the substituent may be substituted with a halogen atom, an alkyl group or an alkoxy group is more preferable.


Ai2 and Ai3 preferably are each independently a divalent 6-membered aromatic group, a divalent 6-membered heteroaromatic group, a divalent 6-membered aliphatic group, or a divalent 6-membered heteroaliphatic group, a divalent 5-membered aromatic group, a divalent 5-membered heteroaromatic group, a divalent 5-membered aliphatic group, or a divalent 5-membered heteroaliphatic group, and specifically, preferably represent a cyclic structure selected from a 1,4-phenylene group, a 1,4-cyclohexylene group, an anthracene-2,6-diyl group, a phenanthrene-2,7-diyl group, a pyridine-2,5-diyl group, a pyrimidine-2,5-diyl group, a naphthalene-2,6-diyl group, a cyclopentane-1,3-diyl group, an indan-2,5-diyl group, a 1,2,3,4-tetrahydronaphthalene-2,6-diyl group, and a 1,3-dioxane-2,5-diyl group, and the cyclic structure is preferably unsubstituted or substituted with L, Pi1-Spi1-, or Ki1. Ai3 also preferably represents a cyclic structure selected from a 1,3-phenylene group, a 1,3-cyclohexylene group, and a naphthalene 2,5-diyl group.


Preferred groups of Li1 are the same as Li1 in Ai1. Ai2 and Ai3 preferably represent a divalent 6-membered aromatic group or a divalent 6-membered aliphatic group, but a divalent unsubstituted 6-membered aromatic group or a divalent unsubstituted 6-membered aliphatic group, or a group in which the hydrogen atom in these cyclic structures is substituted with an alkyl group having 1 to 6 carbon atoms, an alkoxy group having 1 to 6 carbon atoms, a halogen atom, or P-Sp- is preferable, a divalent unsubstituted 6-membered aromatic group, a group in which a hydrogen atom in the cyclic structure is substituted with a fluorine atom, or a divalent unsubstituted 6-membered aliphatic group is preferable, and a 1,4-phenylene group, a 2,6-naphthalene group, or a 1,4-cyclohexyl group in which a hydrogen atom on the substituent may be substituted with a halogen atom, an alkyl group, an alkoxy group, or P-Sp- is more preferable.


In addition, Ai3 is preferably substituted with Ki1.


Here, the general formula (i) has at least one Pi1-Spi1- as a substituent of Ai2 or Ai3 or as a substituent of Ki1, but from the viewpoint of further improving reliability, the number of polymerizable groups in the general formula (i) is preferably 2 or more, and more preferably 3 or more. In the case where the reliability is important, polyfunctionalization can be easily achieved by introducing a polymerization group into Ai2 or Ai3, so that a strong polymer can be constructed. The substituted position of Pi1-Spi1- in Ai2 or Ai3 is preferably the vicinity of Ki1, and it is more preferable that Ai3 is substituted with Pi1-Spi1-.


mi1 preferably represents an integer of 0 to 3, and more preferably represents an integer of 0 to 1.


The compound represented by the general formula (iv) is preferably a compound represented by the following general formula (iv-1).




embedded image


In the formula, Ri1, Ai1, Ai2, Zi1, Zi2, mi1, Pi1, and Spi1 independently have the same meanings as Ri1, Ail, Ai2, Zi1, Zi2, mi1, Pi1, and Spi1 in the general formula (iv), respectively, Yi1 has the same meaning as Yi1 in the general formula (K-24), RiK1, niK1, and niK2 independently have the same meanings as RiK1, niK1, and niK2 in the general formula (K-24-1), respectively, Li11 represents an alkyl group having 1 to 3 carbon atoms, m3 represents an integer of 0 to 3, and mi4 represents an integer of 0 to 3, but mi3+mi4 represents 0 to 4.


The compound represented by the general formula (iv-1) is preferably the following general formulae (iv-1-1), (iv-1-2), (iv-1-3a), (iv-1-3b), (Iv-1-4), (iv-1-Y2), (iv-1-Y3), and (iv-1-Y4).




embedded image


embedded image


In the formula, Ri1, Ai1, Ai2, Zi1, Zi2, mi1, Pi1, and Spi1 independently have the same meanings as Ri1, Ai1, Ai2, Zi1, Zi2, mi1, Pi1, and Spi1 in the general formula (iv), respectively, RiK1, RiY21, Ri3Y1, Ri3Y2, niK1, niK2, and niY11 independently have the same meanings as RiK1, RiY21, Ri31, Ri32, niK1, niK2, and niY11 in the general formulae (K-24-1) to (K-24-3), Li11 represents an alkyl group having 1 to 3 carbon atoms, mi3 represents an integer of 0 to 3, and mi4 represents an integer of 0 to 3, but mi3+mi4 represents 0 to 4.


The preferred groups of each symbol in the general formula (iv-1), and the general formulae (iv-1-1), (iv-1-2), (iv-1-3) are the same as the preferred groups in the general formula (i), the general formula (K-1), and the general formulae (K-1-1) to (K-1-3).


In addition, the compound represented by the general formula (iv) is preferably a compound represented by the following general formulae (iv-2) to (iv-5).




embedded image


In the formulae, Ri1, Ai1, Ai2, Zi1, Zi2, mil, Pi1, and Spi1 independently have the same meanings as Ri1, Ai1, Ai2, Zi1, Zi2, mi1, Pi1, and Spi1, respectively; ni4, niK21, and RK21 independently have the same meanings as ni4, niK21, and RK21 in the general formula (K-24); Ri22 represents an alkylene group having 1 to 6 carbon atoms or a single bond, and —CH2— in the alkylene group may be substituted with —CH═CH—, —C≡C—, or —O— so long as oxygen atoms are not directly adjacent to each other; Li11 represents an alkyl group having 1 to 3 carbon atoms; ni22 represents 0 or 1; mi23 represents an integer of 0 to 3; and mi24 represents an integer of 0 to 3, but mi23+mi24 represents 0 to 4.


Ri22 is preferably a linear alkylene group having 1 to 6 carbon atoms, and more preferably a linear alkylene group having 1 to 3 carbon atoms. The preferred groups of RiY21, RiY31, RiY32, Spi1, and Pi1 are the same as RiY21, RiY31, RiY32, Spi1, and Pi1 in the general formulae (Y-1-1) to (Y-1-3) and the general formula (i). The preferred groups of each symbol in the general formula (iv-2) are the same as the preferred groups in the general formula (iv) and the general formula (K-24).


The general formula (iv) preferably represents the following general formulae (R-1) to (R-6).




embedded image


In the formulae, Ri1, Ki1, and Li1 have the same meanings as Ri1, Ki1, and Li1 in the general formula (iv), respectively.


More specific examples of the general formula (iv) include, but are not limited to, the following formulae (R-1-1) to (R-6-7)




embedded image


embedded image


embedded image


In the formulae, Ri1, Pi1, Si1, and Yi1 independently have the same meanings as Ri1, Pi1, Si1, and Yi1 in the general formula (iv) and the general formula (K-1), respectively.


The lower limit of the content of the first monomer in the liquid crystal composition of the present invention is preferably 0.4% by mass, preferably 0.43% by mass, preferably 0.44% by mass, preferably 0.45% by mass, preferably 0.46% by mass, preferably 0.47% by mass, preferably 0.48% by mass, preferably 0.49% by mass, preferably 0.5% by mass, preferably 0.52% by mass, preferably 0.55% by mass, preferably 0.57% by mass, preferably 0.6% by mass, preferably 0.62% by mass, preferably 0.65% by mass, preferably 0.67% by mass, preferably 0.7% by mass, preferably 0.72% by mass, preferably 0.75% by mass, preferably 0.77% by mass, preferably 0.8% by mass, preferably 0.82% by mass, preferably 0.84% by mass, preferably 0.87% by mass, and preferably 0.9% by mass. The upper limit of the content of the first monomer in the liquid crystal composition of the present invention is preferably 6.0% by mass, preferably 5.7% by mass, preferably 5.5% by mass, preferably 5.3% by mass, preferably 5.0% by mass, preferably 4.8% by mass, preferably 4.5% by mass, preferably 4.0% by mass, preferably 3.8% by mass, preferably 3.6% by mass, preferably 3.5% by mass, preferably 3.0% by mass, preferably 2.5% by mass, preferably 2.3% by mass, preferably 2.1% by mass, preferably 2% by mass, preferably 1.8% by mass, preferably 1.6% by mass, preferably 1.5% by mass, preferably 1% by mass, preferably 0.95% by mass, preferably 0.9% by mass, preferably 0.85% by mass, preferably 0.8% by mass, preferably 0.75% by mass, preferably 0.7% by mass, preferably 0.65% by mass, preferably 0.6% by mass, preferably 0.55% by mass, preferably 0.53% by mass, preferably 0.5% by mass, and preferably 0.48% by mass.


Specific examples thereof include compounds represented by the following formulae (P-K-1) to (P-39), which is a first monomer exhibiting a favorable spontaneous orientation.




embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


The second monomer according to the present invention has a second mesogenic skeleton and a polymerizable group represented by the general formula (PG2) linked to the second mesogenic skeleton, and has a chemical structure different from the first monomer. It preferably does not contain the polar group represented by the general formula (K).


The second mesogenic skeleton according to the present invention is preferably represented by the general formula (Me2):




embedded image


In the above general formula (Me2), ZMe2 represents a single bond, —CH═CH—, —CF═CF—, —C≡C—, —COO—, —OCO—, —OCOO—, —OOCO—, —CF2O—, —OCF2—, —CH═CHCOO—, —OCOCH═CH—, —CH2—CH2COO—, —OCOCH2—CH2—, —CH═C(CH3)COO—, —OCOC(CH3)═CH—, —CH2—CH(CH3)COO—, —OCOCH(CH3)—CH2—, —OCH2CH2O—, or an alkylene group having 2 to 20 carbon atoms, and one or two or more non-adjacent —CH2— in the alkylene group may be substituted with —O—, —COO—, or —OCO—; AMe2 represents a 1,4-phenylene group, a 1,4-cyclohexylene group, a 2,7-phenanthrene group, or a naphthalene-2,6-diyl group, and the hydrogen atom in these cyclic structures may be substituted with a halogen atom, an alkoxy group having 1 to 10 carbon atoms, or P21—Sp21-, and in the case where a plurality of each of ZMe2 and AMe2 are present, these may be the same as or different from each other; mMe2 represents an integer of 1 to 5, and in the formula (Me2), the black dot at the left end and the black dot at the right end represent a bonding site.


The polymerizable group represented by the general formula (PG2) according to the present invention is any one of the following formulae (R-I) to (R-IX).




embedded image


In the formulae (R-I) to (R-IX), R21, R31, R41, R51, and R61 are each independently a hydrogen atom, an alkyl group having 1 to 5 carbon atoms, or a halogenated alkyl group having 1 to 5 carbon atoms; W1 is a single bond, —O—, or a methylene group; T1 is a single bond or —COO—; and p1, t1, and q1 are each independently 0, 1, or 2.


Of these, in the above (PG1) and (PG2), Pi1 is each independently preferably formula (R-I), formula (R-II), formula (R-III), formula (R-IV), formula (R-V), or formula (R-VII), more preferably formula (R-I), formula (R-II), formula (R-III), or formula (R-IV), and more preferably formula (R-I), still more preferably an acryl group or a methacryl group, and even still more preferably a methacryl group.


In the above general formula (PG2), S21 is preferably a single bond or an alkylene group having 1 to 3 carbon atoms, and more preferably a single bond.


The number of polymerizable groups represented by the general formula (PG2) in one molecule of the second monomer according to the present invention is preferably 2 to 4, and more preferably 2 to 3.


The role of the first monomer is that a polar group is adsorbed to a substrate, a film, an electrode or the like, and a mesogenic group of the first monomer is further provided with a connection site with another monomer with a polymerizable group while ensuring compatibility with the liquid crystal molecule. On the other hand, the role of the second monomer is considered to be the connection with the first monomer, the provision of the pretilt angle, and the stability of the pretilt angle. Therefore, when the content of the second monomer is not a predetermined amount, it is considered that the degree of crosslinking is low, a stable polymer layer cannot be formed, and the stability (change with time) of the pretilt angle is lowered.


The second monomer according to the present invention is preferably one kind or two or more kinds selected from the group consisting of polymerizable compounds represented by the following general formulae (RM-1) and (RM-2).




embedded image


In the above general formula (RM-1), ZM1 and ZM2 are represented by the following formulae:




embedded image


In the above formula (ZM1), XM11 to XM15 each independently represent one kind or two or more kinds selected from the group consisting of an alkyl group having 1 to 15 carbon atoms, —CF3, a fluorine atom, an alkoxy group having 1 to 15 carbon atoms, and a chlorine atom, or the formula (RM-S11), but at least one of XM11 to XM15 represents the formula (RM-S11).




embedded image


In the above formula (ZM2), XM21 to XM25 each independently represent one kind or two or more kinds selected from the group consisting of an alkyl group having 1 to 15 carbon atoms, —CF3, a fluorine atom, an alkoxy group having 1 to 15 carbon atoms, and a chlorine atom, or the formula (RM-S21), but at least one of XM21 to XM25 represents the formula (RM-S21).


In the above formula (RM-S11) and the above formula (RM-S21), SM11 and SM21 each independently represent an alkylene group having 1 to 12 carbon atoms or a single bond, and —CH2— in the alkylene group may be replaced by —O—, —COO—, —OCO—, or —OCOO—, in which oxygen atoms are not directly bonded to each other, and


RM11 and RM21 each independently represent any one of the above formulae (R-I) to (R-IX);


LM1 and LM2 each independently represent a single bond, —O—, —CH2—, —OCH2—, —CH2O—, —CO—, —C2H4—, —COO—, —OCO—, —CH═CH—COO—, —COO—CH═CH—, —OCO—CH═CH—, —CH═CH—OCO—, —COOC2H4—, —OCOC2H4—, —C2H4OCO—, —C2H4COO—, —OCOCH2—, —CH2COO—, —CH═CH—, —CF═CH—, —CH═CF—, —CF═CF—, —CF2—, —CF2O—, —OCF2—, —CF2CH2—, —CH2CF2—, —CF2CF2—, or —C≡C—, and in the case where a plurality of LM2 are present, these may be the same as or different from each other.


MM1 represents a 1,4-phenylene group, a 1,4-cyclohexylene group, or a naphthalene-2,6-diyl group, and the hydrogen atom contained in these groups may be substituted with a fluorine atom, a chlorine atom, or an alkyl group having 1 to 8 carbon atoms, a halogenated alkyl group, a halogenated alkoxy group, an alkoxy group, a nitro group, or





*—SM1—RM1  [Chem. 85]


(wherein SM1 represents an alkylene group having 1 to 12 carbon atoms or a single bond, and —CH2— in the alkylene group may be replaced by an oxygen atom, —COO—, —OCO—, or —OCOO—, in which oxygen atoms are not directly bonded to each other and RM1 represents any one of the above formulae (R-I) to (R-IX)), in the case where a plurality of MM1 are present, these may be the same as or different from each other, and


mM1 represents 0, 1 or 2.


In the case where a plurality of SM11, SM21, SM1, RM11, RM21, and/or RM1 are present, these may be the same as or different from each other.




embedded image


In the above general formula (RM-2), XM1 to XM8 each independently represent a hydrogen atom or a fluorine atom;


SM2 and SM3 each independently represent an alkylene group having 1 to 12 carbon atoms or a single bond, and —CH2— in the alkylene group may be replaced by an oxygen atom, —COO—, —OCO—, or —OCOO—, in which oxygen atoms are not directly bonded to each other; and


RM2 and RM3 represents any one of the above formulae (R-I) to (R-IX).


The lower limit of the content of the second monomer in the liquid crystal composition of the present invention is preferably more than 0.4% by mass, preferably 0.43% by mass, preferably 0.44% by mass, preferably 0.45% by mass, preferably 0.46% by mass, preferably 0.47% by mass, preferably 0.48% by mass, preferably 0.49% by mass, preferably 0.5% by mass, preferably 0.52% by mass, preferably 0.55% by mass, preferably 0.57% by mass, preferably 0.6% by mass, preferably 0.62% by mass, preferably 0.65% by mass, preferably 0.67% by mass, preferably 0.7% by mass, preferably 0.72% by mass, preferably 0.75% by mass, preferably 0.77% by mass, preferably 0.8% by mass, preferably 0.82% by mass, preferably 0.84% by mass, preferably 0.87% by mass, and preferably 0.9% by mass. The upper limit of the content of the second monomer in the liquid crystal composition of the present invention is preferably 3% by mass, preferably 2.5% by mass, preferably 2.3% by mass, preferably 2.1% by mass, preferably 2% by mass, preferably 1.8% by mass, preferably 1.6% by mass, preferably 1.5% by mass, preferably 1% by mass, preferably 0.95% by mass, preferably 0.9% by mass, preferably 0.85% by mass, preferably 0.8% by mass, preferably 0.75% by mass, preferably 0.7% by mass, preferably 0.65% by mass, preferably 0.6% by mass, preferably 0.55% by mass, preferably 0.53% by mass, preferably 0.5% by mass, and preferably 0.48% by mass.


In the above general formula (RM-1), ZM1 represents the general formula (ZM1):




embedded image


It is preferable that one or two of XM11 to XM15 represent the general formula (RM-S11), and it is more preferable that XM13 represents the general formula (RM-S11).


In the general formula (RM-1), ZM2 represents the general formula (ZM2):




embedded image


It is preferable that one or two of XM21 to XM25 represent the general formula (RM-S21), and it is more preferable that XM23 represents the general formula (RM-S21).


RM11 and RM21 each independently preferably represents the formula (R-1) or the formula (R-2).


In the general formula (RM-1), MM1 is preferably a 1,4-phenylene group, and the hydrogen atom contained in these groups may be substituted with a fluorine atom, a chlorine atom, or an alkyl group having 1 to 8 carbon atoms, a halogenated alkyl group, a halogenated alkoxy group, an alkoxy group having 1 to 8 carbon atoms, a nitro group, or the general formula (RM-S11).


The polymerizable compound in which MM1 is a 1,4-phenylene group has a sufficiently high polymerization rate.


In the general formula (RM-1), LM1, LM2 each independently preferably represent —OCH2—, —CH2O—, —C2H4—, —COO—, —OCO—, —CH═CH—COO—, —COO—CH═CH—, —OCO—CH═CH—, —CH═CH—OCO—, —COOC2H4—, —OCOC2H4—, —C2H40CO—, —C2H4COO—, —CH═CH—, —CF═CH—, —CH═CF—, —CF═CF—, —CF2O—, —OCF2—, —CF2CH2—, —CH2CF2—, —CF2CF2—, —C≡C—, or a single bond. In addition, in order to improve compatibility with liquid crystal molecules, it is more preferable that the length of the linking group connecting the rings of LM1 and LM2 is an even number of atoms.


In the above general formula (RM-1), mM1 preferably represents 0 or 1. The second monomer, in which mM1 represents 0 or 1, exhibits a high compatibility with other liquid crystal compounds.


In the liquid crystal composition according to the present invention, the content of the second monomer represented by the general formula (RM-1) with respect to the entire liquid crystal composition is preferably more than 0.4% by mass, preferably 0.43% by mass, preferably 0.44% by mass, preferably 0.45% by mass, preferably 0.46% by mass, preferably 0.47% by mass, preferably 0.48% by mass, preferably 0.49% by mass, preferably 0.5% by mass, preferably 0.52% by mass, preferably 0.55% by mass, preferably 0.57% by mass, preferably 0.6% by mass, preferably 0.62% by mass, preferably 0.65% by mass, preferably 0.67% by mass, preferably 0.7% by mass, preferably 0.72% by mass, preferably 0.75% by mass, preferably 0.77% by mass, preferably 0.8% by mass, preferably 0.82% by mass, preferably 0.84% by mass, preferably 0.87% by mass, and preferably 0.9% by mass. In the liquid crystal composition of the present invention, the upper limit of the content of the second monomer represented by the general formula (RM-1) is preferably 3% by mass, preferably 2.5% by mass, preferably 2.3% by mass, preferably 2.1% by mass, preferably 2% by mass, preferably 1.8% by mass, preferably 1.6% by mass, preferably 1.5% by mass, preferably 1.4% by mass, preferably 1.2% by mass, preferably 1% by mass, preferably 0.95% by mass, preferably 0.9% by mass, preferably 0.85% by mass, preferably 0.8% by mass, preferably 0.75% by mass, preferably 0.7% by mass, preferably 0.65% by mass, preferably 0.6% by mass, preferably 0.55% by mass, preferably 0.53% by mass, preferably 0.5% by mass, and preferably 0.48% by mass. In addition, a preferred range of the content of the general formula (RM-1) is more than 0.4% by mass to 1.4% by mass, and more preferably more than 0.45% by mass to 1.3% by mass.


As the second monomer represented by the general formula (RM-1) according to the present invention, specifically it is preferable that one kind or two or more kinds selected from the group of polymerizable compounds represented by the following general formula (RM-1-1) and the general formula (RM-1-2).




embedded image


In the above general formula (RM-1-1) and the general formula (RM-1-2), R107 represents P107—S107—; R110 represents P110—S110—; P107 and P110 each independently represent any one of the above formulae (R-1) to (R-15); S107 and S110 each independently represent a single bond or an alkylene group having 1 to 15 carbon atoms, and one or two or more —CH2— in the alkylene group may be substituted with —O—, —OCO—, or —COO— so long as oxygen atoms are not directly adjacent to each other;


R108, R109, R111, and R112 each independently represent an alkyl group having 1 to 3 carbon atoms, an alkoxy group having 1 to 3 carbon atoms, a fluorine atom, a hydrogen atom, or any one of the above formulae (R-1) to (R-15);


A15 represents a 1,4-phenylene group, a 1,4-cyclohexylene group, a pyridine-2,5-diyl group, a pyrimidine-2,5-diyl group, a naphthalene-2,6-diyl group, an indane-2,5-diyl group, a 1,2,3,4-tetrahydronaphthalene-2,6-diyl group, or a 1,3-dioxane-2,5-diyl group, and these groups are unsubstituted or may be substituted with an alkyl group having 1 to 12 carbon atoms, a halogen (fluorine atom, chlorine atom), a cyano group, or a nitro group;


L15 represents a single bond, —OCH2—, —CH2O—, —C2H4—, —COO—, —OCO—, —CH═CRa—COO—, —CH═CRa—OCO—, —COO—CRa═CH—, —OCO—CRa═CH—, —(CH2)Y—COO—, —(CH2)Y—OCO—, —OCO—(CH2)Y—, —COO— (CH2)Y—, —CH═CH—, —CF2O—, —OCF2—, or —C≡C— (wherein Ra each independently represent a hydrogen atom or an alkyl group having 1 to 3 carbon atoms, and Y represents an integer of 1 to 4); and


X15, X16, X17, and X18 each independently represent a hydrogen atom, an alkyl group having 1 to 3 carbon atoms, or a fluorine atom.


In the above general formula (RM-1-1) and the general formula (RM-1-2), S107 and S110 are preferably a single bond or an alkylene group having 1 to 6 carbon atoms (one or two or more —CH2— in the alkylene group may be substituted with —O— so long as oxygen atoms are not directly adjacent to each other), and particularly preferably a single bond.


In the above general formula (RM-1-1), A15 is preferably an unsubstituted 1,4-phenylene group or naphthalene-2,6-diyl group, or a 1,4-phenylene group or naphthalene-2,6-diyl group substituted with an alkyl group having 1 to 12 carbon atoms, a halogen (fluorine atom, chlorine atom), a cyano group, or a nitro group, and more preferably an unsubstituted 1,4-phenylene group or naphthalene-2,6-diyl group, or a 1,4-phenylene group or naphthalene-2,6-diyl group substituted with an alkyl group having 1 to 3 carbon atoms or a fluorine atom. In this case, the number of substituents in A15 is preferably 0 to 2.


In the above general formula (RM-1-1) and the general formula (RM-1-2), from the viewpoint of compatibility, it is preferable that L15 is a single bond or the number of atoms of the linking portion connecting between the rings in L15 is an even number (for example, Y is preferably 2 or 4).


In the liquid crystal composition according to the present invention, the content of the second monomer represented by the general formula (RM-1-1) and the general formula (RM-1-2) with respect to the entire liquid crystal composition is preferably more than 0.4% by mass, preferably 0.43% by mass, preferably 0.44% by mass, preferably 0.45% by mass, preferably 0.46% by mass, preferably 0.47% by mass, preferably 0.48% by mass, preferably 0.49% by mass, preferably 0.5% by mass, preferably 0.52% by mass, preferably 0.55% by mass, preferably 0.57% by mass, preferably 0.6% by mass, preferably 0.62% by mass, preferably 0.65% by mass, preferably 0.67% by mass, preferably 0.7% by mass, preferably 0.72% by mass, preferably 0.75% by mass, preferably 0.77% by mass, preferably 0.8% by mass, preferably 0.82% by mass, preferably 0.84% by mass, preferably 0.87% by mass, and preferably 0.9% by mass. In the liquid crystal composition of the present invention, the upper limit of the content of the second monomer represented by the general formula (RM-1-1) and the general formula (RM-1-2) is preferably 3% by mass, preferably 2.5% by mass, preferably 2.3% by mass, preferably 2.1% by mass, preferably 2% by mass, preferably 1.8% by mass, preferably 1.6% by mass, preferably 1.5% by mass, preferably 1.4% by mass, preferably 1.2% by mass, preferably 1% by mass, preferably 0.95% by mass, preferably 0.9% by mass, preferably 0.85% by mass, preferably 0.8% by mass, preferably 0.75% by mass, preferably 0.7% by mass, preferably 0.65% by mass, preferably 0.6% by mass, preferably 0.55% by mass, preferably 0.53% by mass, preferably 0.5% by mass, and preferably 0.48% by mass.


The second monomer represented by the general formula (RM-1-2) according to the present invention is preferably one kind or two or more kinds of polymerizable compounds represented by the general formula (IV).




embedded image


In the general formula (IV), R7 and R8 each independently represent any of the above formulae (R-1) to (R-15), and X1 to X8 each independently represent a trifluoromethyl group, a trifluoromethoxy group, a methoxy group, a methyl group, a fluorine atom, or a hydrogen atom.


The structure of the biphenyl skeleton in the general formula (IV) is more preferably the formulae (IV-11) to (IV-21), and particularly preferably the formula (IV-20).




embedded image


embedded image


The polymerizable compound containing a skeleton represented by the formulae (IV-11) to (IV-21) has an optimum orientation regulating force after polymerization, and a good orientation state can be obtained.


Specifically, the compound represented by the general formula (RM-1) according to the present invention is preferably any of compounds represented by Formula (XX-1) to the general formula (XX-29), and more preferably any of compounds represented by Formula (XX-1) to Formula (XX-7) and Formula (XX-23).




embedded image


embedded image


embedded image


embedded image


In Formula (XX-1) to the general formula (XX-29), Spxx represents an alkylene group having 1 to 8 carbon atoms or —O—(CH2)s— (wherein s represents an integer of 2 to 7, and the oxygen atom is bonded to the ring).


In Formula (XX-1) to the general formula (XX-29), the hydrogen atom in the 1,4-phenylene group may further be substituted with —F, —Cl, —CF3, —CH3, or any one of Formulae (R-1) to (R-15).


Moreover, as the compound represented by the general formula (RM-1), for example, polymerizable compounds such as Formula (M1) to Formula (M18) are preferable.




embedded image


embedded image


In addition, polymerizable compounds such as Formula (M19) to Formula (M34) are also preferable.




embedded image


embedded image


embedded image


The hydrogen atoms in the 1,496-phenylene group and naphthalene group in Formula (M19) to Formula (M34) may further be substituted with —F, —Cl, —CF3, or —CH3.


In addition, polymerizable compounds such as Formula (M35) to Formula (M65) are also preferable.




embedded image


embedded image


embedded image


embedded image


In the liquid crystal composition according to the present invention, the content of the second monomer represented by Formulae (M1) to (M67) with respect to the entire liquid crystal composition is preferably more than 0.4% by mass, preferably 0.43% by mass, preferably 0.44% by mass, preferably 0.45% by mass, preferably 0.46% by mass, preferably 0.47% by mass, preferably 0.48% by mass, preferably 0.49% by mass, preferably 0.5% by mass, preferably 0.52% by mass, preferably 0.55% by mass, preferably 0.57% by mass, preferably 0.6% by mass, preferably 0.62% by mass, preferably 0.65% by mass, preferably 0.67% by mass, preferably 0.7% by mass, preferably 0.72% by mass, preferably 0.75% by mass, preferably 0.77% by mass, preferably 0.8% by mass, preferably 0.82% by mass, preferably 0.84% by mass, preferably 0.87% by mass, and preferably 0.9% by mass. In the liquid crystal composition of the present invention, the upper limit of the content of the second monomer represented by the general formula (RM-1) is preferably 3% by mass, preferably 2.5% by mass, preferably 2.3% by mass, preferably 2.1% by mass, preferably 2% by mass, preferably 1.8% by mass, preferably 1.6% by mass, preferably 1.5% by mass, preferably 1.4% by mass, preferably 1.2% by mass, preferably 1% by mass, preferably 0.95% by mass, preferably 0.9% by mass, preferably 0.85% by mass, preferably 0.8% by mass, preferably 0.75% by mass, preferably 0.7% by mass, preferably 0.65% by mass, preferably 0.6% by mass, preferably 0.55% by mass, preferably 0.53% by mass, preferably 0.5% by mass, and preferably 0.48% by mass. In addition, the preferable range of the content of the second monomer represented by Formula (M1) to Formula (M67) with respect to the entire liquid crystal composition is preferably more than 0.4% by mass to 1.4% by mass, and more preferably more than 0.45% by mass to 1.3% by mass.


In the above general formula (RM-2), RM2 and RM3 each independently preferably represent any one of the above Formula (R-1) and Formula (R-2).


In the above general formula (RM-2), SM2 and SM3 each independently preferably represent an alkylene group having 1 to 6 carbon atoms (—CH2— in the alkylene group may be replaced by an oxygen atom, —COO—, —OCO—, or —OCOO—, in which oxygen atoms are not directly bonded to each other) or a single bond.


In the liquid crystal composition according to the present invention, the content of the second monomer represented by the general formula (RM-2) with respect to the entire liquid crystal composition is preferably more than 0.4% by mass, preferably 0.43% by mass, preferably 0.44% by mass, preferably 0.45% by mass, preferably 0.46% by mass, preferably 0.47% by mass, preferably 0.48% by mass, preferably 0.49% by mass, preferably 0.5% by mass, preferably 0.52% by mass, preferably 0.55% by mass, preferably 0.57% by mass, preferably 0.6% by mass, preferably 0.62% by mass, preferably 0.65% by mass, preferably 0.67% by mass, preferably 0.7% by mass, preferably 0.72% by mass, preferably 0.75% by mass, preferably 0.77% by mass, preferably 0.8% by mass, preferably 0.82% by mass, preferably 0.84% by mass, preferably 0.87% by mass, and preferably 0.9% by mass. In the liquid crystal composition of the present invention, the upper limit of the content of the second monomer represented by the general formula (RM-1) is preferably 3% by mass, preferably 2.5% by mass, preferably 2.3% by mass, preferably 2.1% by mass, preferably 2% by mass, preferably 1.8% by mass, preferably 1.6% by mass, preferably 1.5% by mass, preferably 1.4% by mass, preferably 1.2% by mass, preferably 1% by mass, preferably 0.95% by mass, preferably 0.9% by mass, preferably 0.85% by mass, preferably 0.8% by mass, preferably 0.75% by mass, preferably 0.7% by mass, preferably 0.65% by mass, preferably 0.6% by mass, preferably 0.55% by mass, preferably 0.53% by mass, preferably 0.5% by mass, and preferably 0.48% by mass.


Preferred examples of the compound represented by the general formula (RM-2) according to the present invention include polymerizable compounds represented by the following Formula (RM-2-1) to Formula (RM-2-52).




embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


In addition, the specific content of the polymerizable monomer represented by the above Formulae (RM-2-1) to (RM-2-52) is preferably more than 0.4% by mass and 1.4% by mass or less, more preferably 0.42% by mass or more and 1.3% by mass or less, still more preferably 0.43% by mass or more and 1.2% by mass or less, particularly preferably 0.44% by mass or more and 1% by mass or less, and most preferably 0.45% by mass or more and 0.8% by mass or less.


In the liquid crystal composition according to the present invention, the content ratio of the first monomer to the second monomer (first monomer/second monomer) is preferably 0.5 to 10, preferably 0.6 to 8, preferably 0.7 to 6, preferably 0.72 to 5.5, preferably 0.73 to 5.2, preferably 0.74 to 4.5, preferably 0.75 to 4, preferably 0.77 to 3.5, preferably 0.8 to 3.3, and preferably 0.82 to 3.


When the mixing ratio of the first monomer and the second monomer is within the range described above, it is preferable from the viewpoints of stability of the pretilt angle, low temperature stability, and vertical alignment, and in particular, when the lower limit value of the content mass ratio of the first monomer to the second monomer (first monomer/second monomer) is 0.7, three effects of stability of the pretilt angle, low temperature stability, and vertical alignment are obtained.


In the liquid crystal composition according to the present invention, it is preferable to contain one kind or two or more kinds of compounds having a polar group represented by the general formula (K) as the first monomer and one kind or two or more kinds of compounds selected from the general formulae (RM-1) and (RM-2) as the second monomer. The first monomer and the second monomer may be each one kind, but a combination of monomers having different skeletons, such as a combination of one kind of the first monomer and two kinds of the second monomer, a combination of two kinds of the first monomer and one kind of the second monomer, and a combination of two kinds of the first monomer and two kinds of the second monomer, may be used.


The liquid crystal composition according to the present invention preferably exhibits a liquid crystal phase at (25° C.), more preferably exhibits a nematic phase, and is preferably a nematic liquid crystal composition having a negative dielectric anisotropy.


In addition to the first monomer and the second monomer, the liquid crystal composition according to the present invention preferably contains one kind or two or more kinds of compounds selected from compounds represented by the general formulae (N-1), (N-2) and (N-3). These compounds correspond to dielectrically negative compounds (the sign of Δε is negative and the absolute value thereof is greater than 2).


Moreover, the Δε of the compound is a value extrapolated from the measured value of the dielectric anisotropy of the composition prepared by adding the compound to a composition having a substantially neutral dielectric property at 25° C. The content is expressed by %, which means % by mass.




embedded image


In the formulae, RN11, RN12, RN21, RN22, RN31, and RN32 each independently represent an alkyl group having 1 to 8 carbon atoms, and one or non-adjacent two or more —CH2— in the alkyl group may be each independently substituted with —CH═CH—, —C≡C—, —O—, —CO—, —COO—, or —OCO—;


AN11, AN12, AN21, AN22, AN31, and AN32 each independently represent a group selected from the group consisting of: (a) a 1,4-cyclohexylene group (in which one of —CH2— or two or more of —CH2— that are not adjacent to each other present in the group may be replaced by —O—), (b) a 1,4-phenylene group (in which one of —CH═ or two or more of —CH═ that are not adjacent to each other present in the group may be replaced by —N═), (c) a naphthalene-2,6-diyl group, a 1,2,3,4-tetrahydronaphthalene-2,6-diyl group, or a decahydronaphthalene-2,6-diyl group (in which one of —CH═ or two or more of —CH═ that are not adjacent to each other present in the naphthalene-2,6-diyl group or the 1,2,3,4-tetrahydronaphthalene-2,6-diyl group may be replaced by —N═), and (d) a 1,4-cyclohexenylene group, in which the group (a), the group (b), the group (c), and the group (d) each independently may be substituted with a cyano group, a fluorine atom, or a chlorine atom;


ZN11, ZN12, ZN21, ZN22, ZN31, and ZN32 each independently represent a single bond, —CH2CH2—, —(CH2)4—, —OCH2—, —CH2O—, —COO—, —OCO—, —OCF2—, —CF2O—, —CH═N—N═CH—, —CH═CH—, —CF═CF—, or —C≡C—;


XN21 represents a hydrogen atom or a fluorine atom;


TN31 represents —CH2— or an oxygen atom;


nN11, nN12, nN21, nN22, nN31 and nN32 each independently represent an integer of 0 to 3, provided that nN11+nN12, nN21+nN22, and nN31+nN32 each independently are 1, 2, or 3, and in the case where a plurality of each of AN11 to AN32 and ZN11 to ZN32 are present, these may be the same as or different from each other.


The compound represented by any of the general formulae (N-1), (N-2), and (N-3) is preferably a compound having a negative value for Δε, in which the absolute value thereof is greater than 3.


In the general formulae (N-1), (N-2), and (N-3), RN11, RN12, RN21, RN22, RN31, and RN32 each independently preferably represent an alkyl group having 1 to 8 carbon atoms, an alkoxy group having 1 to 8 carbon atoms, an alkenyl group having 2 to 8 carbon atoms, or an alkenyloxy group having 2 to 8 carbon atoms, and preferably represent an alkyl group having 1 to 5 atoms, an alkoxy group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms. R11, R21, and R31 each independently further preferably represent an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms; R12, R22, and R32 each independently more preferably represent an alkyl group having 1 to 5 carbon atoms, an alkoxy group having 1 to 5 carbon atoms, or an alkenyloxy group having 2 to 5 carbon atoms.


Moreover, in the case where the cyclic structure, to which the terminal group (RN11, RN12, RN21, RN22, RN31, and RN32) is bonded, is a phenyl group (aromatic group), the group preferably represents a linear alkyl group having 1 to 5 carbon atoms, a linear alkoxy group having 1 to 4 carbon atoms, or an alkenyl group having 4 to 5 carbon atoms, and in the case where the cyclic structure, to which the terminal group is bonded, is a saturated cyclic structure, such as cyclohexane, pyrane, or dioxane, the group preferably represents a linear alkyl group having 1 to 5 carbon atoms, a linear alkoxy group having 1 to 4 carbon atoms, or a linear alkenyl group having 2 to 5 carbon atoms. For stabilizing the nematic phase, the total number of the carbon atom and the oxygen atom if any is preferably 5 or less, and the group is preferably linear.


The alkenyl group is preferably selected from groups represented by any of the formulae (R1) to (R5). (The black dot in each formula represents a carbon atom in the cyclic structure.)




embedded image


In the case where Δn is demanded to be increased, AN11, AN12, AN21, AN22, AN31, and AN32 each independently preferably represent an aromatic group, and in the case where the response speed is demanded to be increased, each independently preferably represent an aliphatic group, preferably represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, a 2-fluoro-1,4-phenylene group, a 3-fluoro-1,4-phenylene group, a 3,5-difluoro-1,4-phenylene group, a 2,3-difluoro-1,4-phenylene group, a 1,4-cyclohexenylene group, a 1,4-bicyclo[2.2.2]octylene group, a pyperidin-1,4-diyl group, a naphthalen-2,6-diyl group, a decahydronaphthalen-2,6-diyl group, or a 1,2,3,4-tetrahydronaphthalen-2,6-diyl group, more preferably represent the following structures:




embedded image


and more preferably represent a trans-1,4-cyclohexylene group, a 1,4-cyclohexenylene group, or a 1,4-phenylene group.


ZN11, ZN12, ZN21, ZN22, ZN31, and ZN32 each independently preferably represent —CH2O—, —CF2O—, —CH2CH2—, —CF2CF2—, or a single bond, more preferably represent —CH2O—, —CH2CH2—, or a single bond, and particularly preferably —CH2O— or a single bond.


XN21 preferably represents a fluorine atom.


TN31 preferably represents an oxygen atom.


nN11+nN12, nN21+nN22, and nN31+nN32 each independently are preferably 1 or 2, and a combination where nN11 is 1, and nN12 is 0, a combination where nN11 is 2, and nN12 is 0, a combination where nN11 is 1, and nN12 is 1, a combination where nN11 is 2, and nN12 is 1, a combination where nN21 is 1, and nN22 is 0, a combination where nN21 is 2, and nN22 is 0, a combination where nN31 is 1, and nN32 is 0, and a combination where nN31 is 2, and nN32 is 0 are preferred.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1) may be 1%, 10%, 20%, 30%, 40%, 50%, 55%, 60%, 65%, 70%, 75%, and 80%. The upper limit of the preferred content thereof may be 95%, 85%, 75%, 65%, 55%, 45%, 35%, 25%, and 20%.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-2) may be 1%, 10%, 20%, 30%, 40%, 50%, 55%, 60%, 65%, 70%, 75%, and 80%. The upper limit of the preferred content thereof may be 95%, 85%, 75%, 65%, 55%, 45%, 35%, 25%, and 20%.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-3) may be 1%, 10%, 20%, 30%, 40%, 50%, 55%, 60%, 65%, 70%, 75%, and 80%. The upper limit of the preferred content thereof may be 95%, 85%, 75%, 65%, 55%, 45%, 35%, 25%, and 20%.


In the case where it is demanded that the viscosity of the composition of the present invention is kept low, and a composition having a high response speed is provided, it is preferred that the lower limit is low, and the upper limit is low. Moreover, in the case where it is demanded that Tni of the composition of the present invention is kept high, and a composition having good temperature stability is provided, it is preferred that the lower limit is low, and the upper limit is low. Moreover, in the case where it is demanded that the dielectric anisotropy is increased for keeping the driving voltage low, it is preferred that the lower limit is high, and the upper limit is high.


Examples of the compound represented by the general formula (N-1) include the group of compounds represented by the following general formulae (N-1a) to (N-1g):




embedded image


In the formula, RN11 and RN12 have the same meanings as RN11 and RN12 in the general formula (N-1); nNa12 represents 0 or 1; nNb11 represents 0 or 1; nNc11 represents 0 or 1; nNd11 represents 0 or 1; nNe11 represents 1 or 2; nNf12 represents 1 or 2; nNg11 represents 1 or 2; ANe11 represents a trans-1,4-cyclohexylene group or a 1,4-phenylene group; ANg11 represents a trans-1,4-cyclohexylene group, a 1,4-cyclohexenylene group, or a 1,4-phenylene group, provided that in the case where nNg11 is 1, ANg11 represents a 1,4-cyclohexenylene group and in the case where nNg11 is 2, at least one ANg11 represents a 1,4-cyclohexenylene group; and ZNe11 represents a single bond or an ethylene group, provided that in the case where nNe11 is 1, ZNe11 represents an ethylene group. In the case where nNe11 is 2, at least one ZNe11 represents an ethylene group.


More specifically, the compound represented by the general formula (N-1) is preferably a compound selected from the group of compounds represented by the general formulae (N-1-1) to (N-1-22).


The compound represented by the general formula (N-1-1) is the following compound:




embedded image


In the formula, RN111 and RN112 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN111 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents a propyl group, a pentyl group or a vinyl group. RN112 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group or a butoxy group.


The compound represented by the general formula (N-1-1) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of A is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a small value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-1) may be 5%, 10%, 13%, 15%, 17%, 20%, 23%, 25%, 27%, 30%, 33%, or 35%.


Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 50%, 40%, 38%, 35%, 33%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, 13%, 10%, 8%, 7%, 6% %, 5%, or 3%.


Moreover, the compound represented by the general formula (N-1-1) is preferably a compound selected from the group of compounds represented by the formulae (N-1-1.1) to (N-1-1.22), preferably compounds represented by the formulae (N-1-1.1) to (N-1-1.4), and preferably compounds represented by the formulae (N-1-1.1) and (N-1-1.3).




embedded image


embedded image


The compounds represented by the formulae (N-1-1.1) to (N-1-1.22) may be used solely or may be used as a combination, and based on the total amount of the composition of the present invention, the lower limit of the preferred content of the sole compound or the combination of the compounds may be 5%, 10%, 13%, 15%, 17%, 20%, 23%, 25%, 27%, 30%, 33%, or 35%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 50%, 40%, 38%, 35%, 33%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, 13%, 10%, 8%, 7%, 6% %, 5%, or 3%.


The compound represented by the general formula (N-1-2) is the following compound:




embedded image


In the formula, RN121 and RN122 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN121 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, a butyl group, or a pentyl group. RN122 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents a methyl group, a propyl group, a methoxy group, an ethoxy group or a propoxy group.


The compound represented by the general formula (N-1-2) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a small value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-2) may be 5%, 7%, 10%, 13%, 15%, 17%, 20%, 23%, 25%, 27%, 30%, 33%, 35%, 37%, 40%, or 42%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 50%, 48%, 45%, 43%, 40%, 38%, 35%, 33%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, 13%, 10%, 8%, 7%, 6%, or 5%.


Moreover, the compound represented by the general formula (N-1-2) is preferably a compound selected from the group of compounds represented by the formulae (N-1-2.1) to (N-1-2.22), and preferably compounds represented by the formulae (N-1-2.3) to (N-1-2.7), (N-1-2.10), (N-1-2.11), (N-1-2.13), and (N-1-2.20); in the case where the improvement of Δε is important, the compounds represented by the formulae (N-1-2.3) to (N-1-2.7) are preferred; in the case where the improvement of TNI is important, the compounds represented by the formulae (N-1-2.10), (N-1-2.11), and (N-1-2.13) are preferred; and in the case where the improvement of the response speed is important, the compound represented by the formula (N-1-2.20) is preferred.




embedded image


embedded image


The compounds represented by the formulae (N-1-2.1) to (N-1-2.22) may be used solely or may be used as a combination, and based on the total amount of the composition of the present invention, the lower limit of the preferred content of the sole compound or the combination of the compounds may be 5%, 10%, 13%, 15%, 17%, 20%, 23%, 25%, 27%, 30%, 33%, or 35%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 50%, 40%, 38%, 35%, 33%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, 13%, 10%, 8%, 7%, 6%, 5%, or 3%.


The compound represented by the general formula (N-1-3) is the following compound:




embedded image


In the formula, RN131 and RN132 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN131 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, or a butyl group. RN132 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 3 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents a 1-propenyl group, an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-3) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of A is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-3) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


Moreover, the compound represented by the general formula (N-1-3) is preferably a compound selected from the group of compounds represented by the formulae (N-1-3.1) to (N-1-3.21), preferably compounds represented by the formulae (N-1-3.1) to (N-1-3.7) and (N-1-3.21), and preferably the compounds represented by the formulae (N-1-3.1), (N-1-3.2), (N-1-3.3), (N-1-3.4), and (N-1-3.6).




embedded image


embedded image


The compounds represented by the formulae (N-1-3.1) to (N-1-3.4), (N-1-3.6), and (N-1-3.21) may be used solely or may be used as a combination, and a combination of the formulae (N-1-3.1) and (N-1-3.2), and a combination of two kinds or three kinds selected from the formulae (N-1-3.3), (N-1-3.4), and (N-1-3.6) are preferred. Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the sole compound or these compounds may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-4) is the following compound:




embedded image


In the formula, RN141 and RN142 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN141 and RN142 each independently preferably represent an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represent a methyl group, a propyl group, an ethoxy group, or a butoxy group.


The compound represented by the general formula (N-1-4) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a small value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-4) may be 3%, 5%, 7%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, 13%, 11%, 10%, or 8%.


Moreover, the compound represented by the general formula (N-1-4) is preferably a compound selected from the group of compounds represented by the formulae (N-1-4.1) to (N-1-4.14), preferably compounds represented by the formulae (N-1-4.1) to (N-1-4.4), and preferably the compounds represented by the formulae (N-1-4.1), (N-1-4.2), and (N-1-4.4).




embedded image


The compounds represented by the formulae (N-1-4.1) to (N-1-4.14) may be used solely or may be used as a combination, and based on the total amount of the composition of the present invention, the lower limit of the preferred content of the sole compound or these compounds may be 3%, 5%, 7%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, 13%, 11%, 10%, or 8%.


The compound represented by the general formula (N-1-5) is the following compound:




embedded image


In the formula, RN151 and RN152 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN151 and RN152 each independently preferably represent an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represent an ethyl group, a propyl group, or a butyl group.


The compound represented by the general formula (N-1-5) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a small value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-5) may be 5%, 8%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 33%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


Moreover, the compound represented by the general formula (N-1-5) is preferably a compound selected from the group of compounds represented by the formulae (N-1-5.1) to (N-1-5.6), and preferably compounds represented by the formulae (N-1-5.1), (N-1-5.2), and (N-1-5.4).




embedded image


The compounds represented by the formulae (N-1-5.1), (N-1-5.2), and (N-5-1.4) may be used solely or may be used as a combination, and based on the total amount of the composition of the present invention, the lower limit of the preferred content of the sole compound or these compounds may be 5%, 8%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 33%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-10) is the following compound:




embedded image


In the formula, RN111 and RN1102 each independently have the same meanings as RN11 and RN12 in the general formula (N-1). RN1101 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, a butyl group, a vinyl group, or a 1-propenyl group. RN1102 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-10) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value. Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-10) may be 5%, 10%, 13%, 15% 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


Moreover, the compound represented by the general formula (N-1-10) is preferably a compound selected from the group of compounds represented by the formulae (N-1-10.1) to (N-1-10.14), preferably compounds represented by the formulae (N-1-10.1) to (N-1-10.5), (N-1-10.13), and (N-1-10.14), and preferably compounds represented by the formulae (N-1-10.1) (N-1-10.2), (N-1-10.13), and (N-1-10.14).




embedded image


The compounds represented by the formulae (N-1-10.1), (N-1-10.2), (N-1-10.13), and (N-1-10.14) may be used solely or may be used as a combination, and based on the total amount of the composition of the present invention, the lower limit of the preferred content of the sole compound or these compounds may be 5%, 10% 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-11) is the following compound:




embedded image


In the formula, RN1111 and RN1112 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1111 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, a butyl group, a vinyl group, or a 1-propenyl group. RN1112 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-11) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of A is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a small value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-11) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


Moreover, the compound represented by the general formula (N-1-11) is preferably a compound selected from the group of compounds represented by the formulae (N-1-11.1) to (N-1-11.14), preferably compounds represented by the formulae (N-1-11.1) to (N-1-11.14), and preferably compounds represented by the formulae (N-1-11.2) and (N-1-11.4).




embedded image


embedded image


The compounds represented by the formulae (N-1-11.2) and (N-1-11.4) may be used solely or may be used as a combination, and based on the total amount of the composition of the present invention, the lower limit of the preferred content of the sole compound or these compounds may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-12) is the following compound:




embedded image


In the formula, RN1121 and RN1122 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1121 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, or a butyl group. RN1122 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-12) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-12) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-13) is the following compound:




embedded image


In the formula, RN1131 and RN1132 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1131 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, or a butyl group. RN1132 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-13) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-13) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-14) is the following compound:




embedded image


In the formula, RN1141 and RN1142 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1141 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, or a butyl group. RN1142 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-14) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-14) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-15) is the following compound:




embedded image


In the formula, RN1151 and RN1152 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1151 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, or a butyl group. RN1152 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-15) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-15) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-16) is the following compound:




embedded image


In the formula, RN1161 and RN1162 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1161 preferably represents an alkyl group having a 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, or a butyl group. RN1162 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-16) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-16) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-17) is the following compound:




embedded image


In the formula, RN1171 and RN1172 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1171 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents an ethyl group, a propyl group, or a butyl group. RN1172 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-17) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-17) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-18) is the following compound:




embedded image


In the formula, RN1181 and RN1182 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1181 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represents a methyl group, an ethyl group, a propyl group, or a butyl group. RN1182 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms, and preferably represents an ethoxy group, a propoxy group, or a butoxy group.


The compound represented by the general formula (N-1-18) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of A is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-18) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


Moreover, the compound represented by the general formula (N-1-18) is preferably a compound selected from the group of compounds represented by the formulae (N-1-18.1) to (N-1-18.5), preferably compounds represented by the formulae (N-1-18.1) to (N-1-18.3), and preferably compounds represented by the formulae (N-1-18.2) and (N-1-18.3).




embedded image


The compound represented by the general formula (N-1-20) is the following compound:




embedded image


In the formula, RN1201 and RN1202 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1201 and RN1202 each independently preferably represent an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represent an ethyl group, a propyl group, or a butyl group.


The compound represented by the general formula (N-1-20) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-20) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-21) is the following compound:




embedded image


In the formula, RN1211 and RN1212 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1211 and RN1212 each independently preferably represent an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represent an ethyl group, a propyl group, or a butyl group.


The compound represented by the general formula (N-1-21) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-21) may be 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (N-1-22) is the following compound:




embedded image


In the formula, RN1221 and RN1222 each independently have the same meanings as RN11 and RN12 in the general formula (N-1).


RN1221 and RN1222 each independently preferably represent an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represent an ethyl group, a propyl group, or a butyl group.


The compound represented by the general formula (N-1-22) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of Δε is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a large value.


Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-1-22) may be 1%, 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 35%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, 13%, 10%, or 5%.


Moreover, the compound represented by the general formula (N-1-22) is preferably a compound selected from the group of compounds represented by the formulae (N-1-22.1) to (N-1-22.12), preferably compounds represented by the formulae (N-1-22.1) to (N-1-22.5), and preferably compounds represented by the formulae (N-1-22.1) to (N-1-22.4).




embedded image


The compound represented by the general formula (N-2) is preferably a compound selected from the group of compounds represented by the following general formulae (N-2-1) to (N-2-3).


The compound represented by the general formula (N-2-1) is the following compound:




embedded image


In the formula, RN211 and RN212 each independently have the same meanings as RN21 and RN22 in the general formula (N-2).


The compound represented by the general formula (N-2-2) is the following compound:




embedded image


In the formula, RN221 and RN222 each independently have the same meanings as RN21 and RN22 in the general formula (N-2).


The compound represented by the general formula (N-2-3) is the following compound:




embedded image


In the formula, RN231 and RN232 each independently have the same meanings as RN21 and RN22 in the general formula (N-2).


The compound represented by the general formula (N-3) is preferably a compound selected from the group of compounds represented by the general formula (N-3-2):




embedded image


In the formula, RN321 and RN322 each independently have the same meanings as RN31 and RN32 in the general formula (N-3).


RN321 and RN322 each preferably represent an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and preferably represent a propyl group or a pentyl group.


The compound represented by the general formula (N-3-2) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the improvement of A is important, the content of the compound is preferably large; in the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value; and in the case where TNI is important, a high effect may be obtained by setting the content thereof to a small value. Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (N-3-2) may be 3%, 5%, 10%, 13%, 15%, 17%, 20%, 23%, 25%, 27%, 30%, 33%, or 35%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 50%, 40%, 38%, 35%, 33%, 30%, 28%, 25%, 23%, 20%, 18%, 15%, 13%, 10%, 8%, 7%, 6%, or 5%.


Moreover, the compound represented by the general formula (N-3-2) is preferably a compound selected from the group of compounds represented by the formulae (N-3-2.1) to (N-3-2.3).




embedded image


The liquid crystal composition according to the present invention preferably contains one kind or two or more kinds of compounds represented by the general formula (L) in addition to the compounds represented by the first monomer and the second monomer. The compound represented by the general formula (L) corresponds to a compound that is dielectrically nearly neutral (i.e., a value of A of −2 to 2).




embedded image


In the formula, RL1 and RL2 each independently represent an alkyl group having 1 to 8 carbon atoms, in which one or non-adjacent two or more of —CH2— in the alkyl group each independently may be substituted with —CH═CH—, —C≡C—, —O—, —CO—, —COO—, or —OCO—;


nL1 represents 0, 1, 2, or 3;


AL1, AL2, and AL3 each independently represent a group selected from the group consisting of (a) a 1,4-cyclohexylene group (in which one of —CH2— or two or more of —CH2— that are not adjacent to each other present in the group may be replaced by —O—), (b) a 1,4-phenylene group (in which one of —CH═ or two or more of —CH═ that are not adjacent to each other present in the group may be replaced by —N═), and (c) a naphthalene-2,6-diyl group, a 1,2,3,4-tetrahydronaphthalene-2,6-diyl group, or a decahydronaphthalene-2,6-diyl group (in which one of —CH═ or two or more of —CH═ that are not adjacent to each other present in the naphthalene-2,6-diyl group or the 1,2,3,4-tetrahydronaphthalene-2,6-diyl group may be replaced by —N═), the group (a), the group (b) and the group (c) may be each independently substituted with a cyano group, a fluorine atom, or a chlorine atom,


ZL1 and ZL2 each independently represent a single bond, —CH2CH2—, —(CH2)4—, —OCH2—, —CH2O—, —COO—, —OCO—, —OCF2—, —CF2O—, —CH═N—N═CH—, —CH═CH—, —CF═CF—, or —C≡C—,


in the case where nL1 is 2 or 3, and a plurality of AL2 are present, these may be the same as or different from each other; in the case where nL1 is 2 or 3, and a plurality of ZL2 are present, these may be the same as or different from each other; and compounds represented by the general formulae (N-1), (N-2), and (N-3) are excluded.


The compound represented by the general formula (L) may be used solely or as a combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kind of the compound used may be, for example, one kind in one embodiment of the present invention. Alternatively, the kinds thereof may be two kinds, three kinds, four kinds, five kinds, six kinds, seven kinds, eight kinds, nine kinds, or ten kinds in other embodiments of the present invention.


In the composition of the present invention, the content of the compound represented by the general formula (L) is necessarily controlled appropriately in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, the birefringence, the process adaptability, the drop marks, the burn-in, and the dielectric anisotropy.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L) may be 1%, 10%, 20%, 30%, 40%, 50%, 55%, 60%, 65%, 70%, 75%, or 80%. The upper limit of the preferred content thereof may be 95%, 85%, 75%, 65%, 55%, 45%, 35%, or 25%.


In the case where it is demanded that the viscosity of the composition of the present invention is kept low, and a composition having a high response speed is provided, it is preferred that the lower limit is high, and the upper limit is high. Moreover, in the case where it is demanded that Tni of the composition of the present invention is kept high, and a composition having good temperature stability is provided, it is preferred that the lower limit is high, and the upper limit is high. Furthermore, in the case where it is demanded that the dielectric anisotropy is increased for keeping the driving voltage low, it is preferred that the lower limit is low, and the upper limit is low.


In the case where the reliability is important, both RL1 and RL2 are preferably alkyl groups; in the case where the decrease of the volatility of the compound is important, both of them are preferably alkoxy group; and in the case where the decrease of the viscosity is important, at least one of them is preferably an alkenyl group.


The number of a halogen atom present in the molecule is preferably 0, 1, 2, or 3, preferably 0 or 1, and in the case where the compatibility with the other liquid crystal molecules is important, preferably 1.


In the case where the cyclic structure, to which RL1 or RL2 is bonded, is a phenyl group (i.e., an aromatic group), RL1 and RL2 each independently preferably represent a linear alkyl group having 1 to 5 carbon atoms, a linear alkoxy group having 1 to 4 carbon atoms, or an alkenyl group having 4 to 5 carbon atoms, and in the case where the cyclic structure, to which RL1 or RL2 is bonded, is a saturated cyclic structure, such as cyclohexane, pyrane, or dioxane, RL1 and RL2 each independently preferably represent a linear alkyl group having 1 to 5 carbon atoms, a linear alkoxy group having 1 to 4 carbon atoms, or a linear alkenyl group having 2 to 5 carbon atoms. For stabilizing the nematic phase, the total number of the carbon atom and the oxygen atom if any is preferably 5 or less, and the group is preferably linear.


The alkenyl group is preferably selected from groups represented by any of the formulae (R1) to (R5). (The black dot in each formula represents a carbon atom in the cyclic structure.)




embedded image


nL1 is preferably 0 in the case where the response speed is important, preferably 2 or 3 for improving the upper limit temperature of the nematic phase, and preferably 1 for balancing these factors. Moreover, the compounds having different values are preferably combined for satisfying the characteristics demanded in the composition.


In the case where Δn is demanded to be increased, AL1, AL2, and AL3 each preferably represent an aromatic group, and in the case where the response speed is demanded to be increased, each preferably represent an aliphatic group, each independently preferably represent a trans-1,4-cyclohexylene group, a 1,4-phenylene group, a 2-fluoro-1,4-phenylene group, a 3-fluoro-1,4-phenylene group, a 3,5-difluoro-1,4-phenylene group, a 1,4-cyclohexenylene group, a 1,4-bicyclo[2.2.2]octylene group, a pyperidin-1,4-diyl group, a naphthalen-2,6-diyl group, a decahydronaphthalen-2,6-diyl group, or a 1,2,3,4-tetrahydronaphthalen-2,6-diyl group, more preferably represent the following structures:




embedded image


and more preferably represent a trans-1,4-cyclohexylene group or a 1,4-phenylene group.


ZL1 and ZL2 are preferably single bond in the case where the response speed is important.


The number of a halogen atom in the molecule of the compound represented by the general formula (L) is preferably 0 or 1. The halogen atom is preferably a fluorine atom or a chlorine atom, and more preferably a fluorine atom.


The compound represented by the general formula (L) is preferably a compound selected from the group of compounds represented by the following general formulae (L-1) to (L-7).


The compound represented by the general formula (L-1) is the following compound:




embedded image


In the formula, RL11 and RL12 each independently have the same meanings as RL1 and RL2 in the general formula (L).


RL11 and RL12 each preferably represent a linear alkyl group having 1 to 5 carbon atoms, a linear alkoxy group having 1 to 4 carbon atoms, or an alkenyl group having 2 to 5 carbon atoms.


The compound represented by the general formula (L-1) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound may be 1%, 2%, 3%, 5%, 7%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%, or 55%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 95%, 90%, 85%, 80%, 75%, 70%, 65%, 60%, 55%, 50%, 45%, 40%, 35%, 30%, or 25%.


In the case where it is demanded that the viscosity of the composition of the present invention is kept low, and a composition having a high response speed is provided, it is preferred that the lower limit is high, and the upper limit is high. Moreover, in the case where it is demanded that Tni of the composition of the present invention is kept high, and a composition having good temperature stability is provided, it is preferred that the lower limit is intermediate, and the upper limit is intermediate. Furthermore, in the case where it is demanded that the dielectric anisotropy is increased for keeping the driving voltage low, it is preferred that the lower limit is low, and the upper limit is low.


The compound represented by the general formula (L-1) is preferably a compound selected from the group of compounds represented by the general formula (L-1-1):




embedded image


In the formula, RL12 has the same meaning as in the general formula (L-1).


The compound represented by the general formula (L-1-1) is preferably a compound selected from the group of compounds represented by the formulae (L-1-1.1) to (L-1-1.3), preferably the compounds represented by the formulae (L-1-1.2) or (L-1-1.3), and preferably a compound represented by the formula (L-1-1.3).




embedded image


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-1.3) may be 1%, 2%, 3%, 5%, 7%, or 10%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 20%, 15%, 13%, 10%, 8%, 7%, 6%, 5%, or 3%.


The compound represented by the general formula (L-1) is preferably a compound selected from the group of compounds represented by the general formula (L-1-2):




embedded image


In the formula, RL12 has the same meaning as in the general formula (L-1).


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-2) may be 1%, 5%, 10%, 15%, 17%, 20%, 23%, 25%, 27%, 30%, or 35%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 60%, 55%, 50%, 45%, 42%, 40%, 38%, 35%, 33%, or 30%.


Moreover, the compound represented by the general formula (L-1-2) is preferably a compound selected from the group of compounds represented by the formulae (L-1-2.1) to (L-1-2.4), and preferably the compounds represented by the formulae (L-1-2.2) to (L-1-2.4). In particular, the compound represented by the formula (L-1-2.2) is preferred for improving the response speed of the composition of the present invention. Furthermore, in the case where a high Tni is demanded rather than the response speed, the compound represented by the formula (L-1-2.3) or (L-1-2.4) is preferably used. The content of the compounds represented by the formulae (L-1-2.3) and (L-1-2.4) is preferably not 30% by mass or more for improving the solubility at a low temperature.




embedded image


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-2.2) may be 10%, 15%, 18%, 20%, 23%, 25%, 27%, 30%, 33%, 35%, 38%, or 40%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 60%, 55%, 50%, 45%, 43%, 40%, 38%, 35%, 32%, 30%, 27%, 25%, or 22%.


Based on the total amount of the composition of the present invention, the lower limit of the preferred total content of the compound represented by the formula (L-1-1.3) and the compound represented by the formula (L-1-2.2) may be 10%, 15%, 20%, 25%, 27%, 30%, 35%, or 40%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 60%, 55%, 50%, 45%, 43%, 40%, 38%, 35%, 32%, 30%, 27%, 25%, or 22%.


The compound represented by the general formula (L-1) is preferably a compound selected from the group of compounds represented by the general formula (L-1-3):




embedded image


In the formula, RL13 and RL14 each independently represent an alkyl group having 1 to 8 carbon atoms or an alkoxy group having 1 to 8 carbon atoms.


RL13 and RL14 each preferably represent a linear alkyl group having 1 to 5 carbon atoms, a linear alkoxy group having 1 to 4 carbon atoms, or a linear alkenyl group having 2 to 5 carbon atoms.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-3) may be 1%, 5%, 10%, 13%, 15%, 17%, 20%, 23%, 25%, or 30%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 60%, 55%, 50%, 45%, 40%, 37%, 35%, 33%, 30%, 27%, 25%, 23%, 20%, 17%, 15%, 13%, or 10%.


Moreover, the compound represented by the general formula (L-1-3) is preferably a compound selected from the group of compounds represented by the formulae (L-1-3.1) to (L-1-3.13), and preferably the compounds represented by the formula (L-1-3.1), (L-1-3.3), or (L-1-3.4). In particular, the compound represented by the formula (L-1-3.1) is preferred for improving the response speed of the composition of the present invention. Furthermore, in the case where a high Tni is demanded rather than the response speed, the compounds represented by the formulae (L-1-3.3), (L-1-3.4), (L-1-3.11), and (L-1-3.12) are preferably used. The total content of the compounds represented by the formulae (L-1-3.3), (L-1-3.4), (L-1-3.11), and (L-1-3.12) is preferably not 20% or more for improving the solubility at a low temperature.




embedded image


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-3.1) may be 1%, 2%, 3%, 5%, 7%, 10%, 13%, 15%, 18%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 20%, 17%, 15%, 13%, 10%, 8%, 7%, or 6%.


The compound represented by the general formula (L-1) is preferably a compound selected from the group of compounds represented by the general formula (L-1-4) and/or (L-1-5):




embedded image


In the formula, RL15 and RL16 each independently represent an alkyl group having 1 to 8 carbon atoms or an alkoxy group having 1 to 8 carbon atoms.


RL15 and RL16 each preferably represent a linear alkyl group having 1 to 5 carbon atoms, a linear alkoxy group having 1 to 4 carbon atoms, or a linear alkenyl group having 2 to 5 carbon atoms.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-4) may be 1%, 5%, 10%, 13%, 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 25%, 23%, 20%, 17%, 15%, 13%, or 10%.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-5) may be 1%, 5%, 10%, 13% 15%, 17%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 25%, 23%, 20%, 17%, 15%, 13%, or 10%.


Moreover, the compound represented by the general formulae (L-1-4) and (L-1-5) is preferably a compound selected from the group of compounds represented by the formulae (L-1-4.1) to (L-1-5.3), and preferably the compounds represented by the formula (L-1-4.2) or (L-1-5.2).




embedded image


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-4.2) may be 1%, 2%, 3%, 5%, 7%, 10%, 13%, 15%, 18%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 20%, 17%, 15%, 13%, 10%, 8%, 7%, or 6%.


Two or more kinds of compounds selected from the group of compounds represented by the formulae (L-1-1.3), (L-1-2.2), (L-1-3.1), (L-1-3.3), (L-1-3.4), (L-1-3.11), and (L-1-3.12) are preferably combined, and two or more kinds of compounds selected from the group of compounds represented by the formulae (L-1-1.3), (L-1-2.2), (L-1-3.1), (L-1-3.3), (L-1-3.4), and (L-1-4.2) are preferably combined. Based on the total amount of the composition of the present invention, the lower limit of the preferred total content of these compounds may be 1%, 2%, 3%, 5%, 7%, 10%, 13%, 15%, 18%, 20%, 23%, 25%, 27%, 30%, 33%, or 35%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 80%, 70%, 60%, 50%, 45%, 40%, 37%, 35%, 33%, 30%, 28%, 25%, 23%, or 20%. In the case where the reliability of the composition is important, two or more kinds of compounds selected from the group of compounds represented by the formulae (L-1-3.1), (L-1-3.3), and (L-1-3.4) are preferably combined, and in the case where the response speed of the composition is important, two or more kinds of compounds selected from the group of compounds represented by the formulae (L-1-1.3) and (L-1-2.2) are preferably combined.


The compound represented by the general formula (L-1) is preferably a compound selected from the group of compounds represented by the general formula (L-1-6):




embedded image


In the formula, RL17 and RL18 each independently represent a methyl group or a hydrogen atom.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-1-6) may be 1%, 5%, 10%, 15%, 17%, 20%, 23%, 25%, 27%, 30%, or 35%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 60%, 55%, 50%, 45%, 42%, 40%, 38%, 35%, 33%, or 30%.


Moreover, the compound represented by the general formula (L-1-6) is preferably a compound selected from the group of compounds represented by the formulae (L-1-6.1) to (L-1-6.3)




embedded image


The compound represented by the general formula (L-2) is the following compound:




embedded image


In the formula, RL21 and RL22 each independently have the same meanings as RL1 and RL2 in the general formula (L).


RL21 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and RL22 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms.


The compound represented by the general formula (L-1) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the case where the solubility at a low temperature is important, a high effect may be obtained by setting the content thereof to a large value, and on the other hand, in the case where the response speed is important, a high effect may be obtained by setting the content thereof to a small value. Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-2) may be 1%, 2%, 3%, 5% 7%, or 10%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 20%, 15%, 13%, 10%, 8%, 7%, 6%, 5%, or 3%.


Moreover, the compound represented by the general formula (L-2) is preferably a compound selected from the group of compounds represented by the formulae (L-2.1) to (L-2.6), and preferably the compounds represented by the formulae (L-2.1), (L-2.3), (L-2.4), and (L-2.6).




embedded image


The compound represented by the general formula (L-3) is the following compound:




embedded image


In the formula, RL31 and RL32 each independently have the same meanings as RL1 and RL2 in the general formula (L).


RL31 and RL32 each preferably represent an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms.


The compound represented by the general formula (L-3) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-3) may be 1%, 2%, 3%, 5%, 7%, or 10%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content thereof may be 20%, 15%, 13%, 10%, 8%, 7%, 6%, 5%, or 3%.


In the case where a high birefringence is obtained, a high effect may be obtained by setting the content thereof to a large value, and on the other hand, in the case where a high Tni is important, a high effect may be obtained by setting the content thereof to a small value. Moreover, in the case where the drop marks and the burn-in characteristics are improved, the range of the content thereof is preferably set to the intermediate.


Moreover, the compound represented by the general formula (L-3) is preferably a compound selected from the group of compounds represented by the formulae (L-3.1) to (L-3.7), and preferably the compounds represented by the formulae (L-3.2) to (L-3.7).




embedded image


The compound represented by the general formula (L-4) is the following compound:




embedded image


In the formula, RL41 and RL42 each independently have the same meanings as RL1 and RL2 in the general formula (L).


RL41 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and RL42 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms.


The compound represented by the general formula (L-4) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the composition of the present invention, the content of the compound represented by the general formula (L-4) is necessarily controlled appropriately in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, the birefringence, the process adaptability, the drop marks, the burn-in, and the dielectric anisotropy.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-4) may be 1%, 2%, 3%, 5%, 7%, 10%, 14%, 16%, 20%, 23%, 26%, 30%, 35%, or 40%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content of the compound represented by the formula (L-4) may be 50%, 40%, 35%, 30%, 20%, 15%, 10%, or 5%.


The compound represented by the general formula (L-4) is preferably, for example, the compounds represented by the formulae (L-4.1) to (L-4.3).




embedded image


In accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence, the compound represented by the formula (L-4.1) may be contained, the compound represented by the formula (L-4.2) may be contained, both the compounds represented by the formulae (L-4.1) and (L-4.2) may be contained, and all the compounds represented by the formulae (L-4.1) to (L-4.3) may be contained. Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-4.1) or (L-4.2) may be 3%, 5%, 7%, 9%, 11%, 12%, 13%, 18%, or 21%. The upper limit of the preferred content thereof may be 45%, 40%, 35%, 30%, 25%, 23%, 20%, 18%, 15%, 13%, 10%, or 8%.


In the case where both the compounds represented by the formulae (L-4.1) and (L-4.2) are contained, based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compounds may be 15%, 19%, 24%, or 30%. The upper limit of the preferred content thereof may be 45%, 40%, 35%, 30%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (L-4) is preferably, for example, the compounds represented by the formulae (L-4.4) to (L-4.6), and preferably the compound represented by the formula (L-4.4).




embedded image


In accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence, the compound represented by the formula (L-4.4) may be contained, the compound represented by the formula (L-4.5) may be contained, and both the compounds represented by the formulae (L-4.4) and (L-4.5) may be contained.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-4.4) or (L-4.5) may be 3%, 5%, 7%, 9%, 11%, 12%, 13%, 18%, or 21%. The preferred upper limit thereof may be 45%, 40%, 35%, 30%, 25%, 23%, 20%, 18%, 15%, 13%, 10%, or 8%.


In the case where both the compounds represented by the formulae (L-4.4) and (L-4.5) are contained, based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compounds may be 15%, 19%, 24%, or 30%. The preferred upper limit thereof may be 45%, 40%, 35%, 30%, 25%, 23%, 20%, 18%, 15%, or 13%.


The compound represented by the general formula (L-4) is preferably the compounds represented by the formulae (L-4.7) to (L-4.10), and particularly preferably the compound represented by the formula (L-4.9).




embedded image


The compound represented by the general formula (L-5) is the following compound:




embedded image


In the formula, RL51 and RL52 each independently have the same meanings as RL1 and RL2 in the general formula (L).


RL51 preferably represents an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and RL52 preferably represents an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 4 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms.


The compound represented by the general formula (L-5) may be used solely, or two or more of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


In the composition of the present invention, the content of the compound represented by the general formula (L-5) is necessarily controlled appropriately in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, the birefringence, the process adaptability, the drop marks, the burn-in, and the dielectric anisotropy.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-5) may be 1%, 2%, 3%, 5%, 7%, 10%, 14%, 16%, 20%, 23%, 26%, 30%, 35%, or 40%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content of the compound represented by the formula (L-5) may be 50%, 40%, 35%, 30%, 20%, 15%, 10%, or 5%.


The compound represented by the general formula (L-5) is preferably the compounds represented by the formulae (L-5.1) and (L-5.2), and particularly preferably the compound represented by the formula (L-5.1).


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compounds may be 1%, 2%, 3%, 5%, or 7%. The upper limit of the preferred content of the compounds may be 20%, 15%, 13%, 10%, or 9%.




embedded image


The compound represented by the general formula (L-5) is preferably the compounds represented by the formulae (L-5.3) and (L-5.4).


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compounds may be 1%, 2%, 3%, 5%, or 7%. The upper limit of the preferred content of the compounds may be 20%, 15%, 13%, 10%, or 9%.




embedded image


The compound represented by the general formula (L-5) is preferably the compounds represented by the formulae (L-5.5) to (L-5.7), and particularly preferably the compound represented by the formula (L-5.7).


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compounds may be 1%, 2%, 3%, 5%, or 7%. The upper limit of the preferred content of the compounds may be 20%, 15%, 13%, 10%, or 9%.




embedded image


The compound represented by the general formula (L-6) is the following compound:




embedded image


In the formula, RL61 and RL62 each independently have the same meanings as RL1 and RL2 in the general formula (L); and XL61 and XL62 each independently represent a hydrogen atom or a fluorine atom.


RL61 and RL62 each independently preferably represent an alkyl group having 1 to 5 carbon atoms or an alkenyl group having 2 to 5 carbon atoms, and it is preferred that one of XL61 and XL62 represents a fluorine atom, and the other thereof represents a hydrogen atom.


The compound represented by the general formula (L-6) may be used solely, or two or more kinds of the compounds may be used in combination. The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be used as an appropriate combination in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, four kinds, or five or more kinds.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-6) may be 1%, 2%, 3%, 5%, 7%, 10%, 14%, 16%, 20%, 23%, 26%, 30%, 35%, or 40%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content of the compound represented by the formula (L-6) may be 50%, 40%, 35%, 30%, 20%, 15%, 10%, or 5%. The content thereof is preferably large in the case where the increase of Δn is important, and the content thereof is preferably small in the case where the deposition at a low temperature is important.


The compound represented by the general formula (L-6) is preferably the compounds represented by the formulae (L-6.1) to (L-6.9).




embedded image


The kinds of the compounds capable of being used in combination are not particularly limited, and from one to three kinds of these compounds are preferably contained, and from one to four kinds thereof are more preferably contained. Moreover, a broad molecular weight distribution of the selected compounds is effective for the solubility, and therefore, for example, one kind selected from the compounds represented by the formula (L-6.1) and (L-6.2), one kind selected from the compounds represented by the formula (L-6.4) and (L-6.5), one kind selected from the compounds represented by the formula (L-6.6) and (L-6.7), and one kind selected from the compounds represented by the formula (L-6.8) and (L-6.9) are preferably appropriately combined. Among these, the compounds represented by the formulae (L-6.1), (L-6.3), (L-6.4), (L-6.6), and (L-6.9) are preferably contained.


Moreover, the compound represented by the general formula (L-6) is preferably the compounds represented by the formulae (L-6.10) to (L-6.17), and particularly preferably the compound represented by the formula (L-6.11).




embedded image


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compounds may be 1%, 2%, 3%, 5%, or 7%. The upper limit of the preferred content of the compounds may be 20%, 15%, 13%, 10%, or 9%.


The compound represented by the general formula (L-7) is the following compound:




embedded image


In the formula, RL71 and RL72 each independently have the same meanings as RL1 and RL2 in the general formula (L); AL71 and AL72 each independently have the same meanings as AL2 and AL3 in the general formula (L), in which hydrogen atoms on AL71 and AL72 each independently may be replaced by a fluorine atom; ZL71 has the same meaning as ZL2 in the general formula (L); and XL71 and XL72 each independently represent a hydrogen atom or a fluorine atom.


In the formula, RL71 and RL72 each independently preferably represent an alkyl group having 1 to 5 carbon atoms, an alkenyl group having 2 to 5 carbon atoms, or an alkoxy group having 1 to 4 carbon atoms; AL71 and AL72 each independently preferably represent a 1,4-cyclohexylene group or a 1,4-phenylene group, in which hydrogen atoms on AL71 and AL72 each independently may be replaced by a fluorine atom; ZL71 preferably represents a single bond or —COO—, and preferably a single bond; and XL71 and XL72 each preferably represent a hydrogen atom.


The kinds of the compounds capable of being used in combination are not particularly limited, and the compounds may be appropriately combined in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, and the birefringence. The kinds of the compound used may be, for example in one embodiment of the present invention, one kind, two kinds, three kinds, or four kinds.


In the composition of the present invention, the content of the compound represented by the general formula (L-7) is necessarily controlled appropriately in accordance with the demanded capabilities, such as the solubility at a low temperature, the transition temperature, the electric reliability, the birefringence, the process adaptability, the drop marks, the burn-in, and the dielectric anisotropy.


Based on the total amount of the composition of the present invention, the lower limit of the preferred content of the compound represented by the formula (L-7) may be 1%, 2%, 3%, 5%, 7%, 10%, 14%, 16%, or 20%. Based on the total amount of the composition of the present invention, the upper limit of the preferred content of the compound represented by the formula (L-7) may be 30%, 25%, 23%, 20%, 18%, 15%, 10%, or 5%.


In the case where an embodiment where the composition of the present invention has a high Tni is demanded, the content of the compound represented by the formula (L-7) is preferably large, and in the case where an embodiment with a low viscosity is demanded, the content thereof is preferably small.


Moreover, the compound represented by the general formula (L-7) is preferably the compounds represented by the formulae (L-7.1) to (L-7.4), and preferably the compound represented by the formula (L-7.2).




embedded image


Moreover, the compound represented by the general formula (L-7) is preferably the compounds represented by the formulae (L-7.11) to (L-7.13), and preferably the compound represented by the formula (L-7.11).




embedded image


Moreover, the compound represented by the general formula (L-7) is preferably the compounds represented by the formulae (L-7.21) to (L-7.23). The compound represented by the formula (L-7.21) is preferable.




embedded image


Moreover, the compound represented by the general formula (L-7) is preferably the compounds represented by the formulae (L-7.31) to (L-7.34), and preferably the compound represented by the formula (L-7.31) and/or (L-7.32).




embedded image


Moreover, the compound represented by the general formula (L-7) is preferably the compounds represented by the formulae (L-7.41) to (L-7.44), and preferably the compound represented by the formula (L-7.41) and/or (L-7.42).




embedded image


Moreover, the compound represented by the general formula (L-7) is preferably the compounds represented by the formulae (L-7.51) to (L-7.53).




embedded image


The liquid crystal composition of the present invention may contain, in addition to the compounds described above, common nematic liquid crystal, smectic liquid crystal, cholesteric liquid crystal, an antioxidant, a UV absorber, a photostabilizer, an infrared absorber, etc.


Examples of the antioxidant include hindered phenols represented by the general formula (H-1) to the general formula (H-4).




embedded image


In the general formula (H-1) to the general formula (H-4), RH1 represents an alkyl group having 1 to 10 carbon atoms, an alkoxy group having 1 to 10 carbon atoms, an alkenyl group having 2 to 10 carbon atoms, or an alkenyloxy group having 2 to 10 carbon atoms. One —CH2— or two or more non-adjacent —CH2— present in the group may each independently be substituted with —O— or —S—, and one or two or more hydrogen atoms present in the group may each independently be substituted with a fluorine atom or a chlorine atom. More specifically, an alkyl group having 2 to 7 carbon atoms, an alkoxy group having 2 to 7 carbon atoms, an alkenyl group having 2 to 7 carbon atoms, or an alkenyloxy group having 2 to 7 carbon atoms is preferable. An alkyl group having 3 to 7 carbon atoms or an alkenyl group having 2 to 7 carbon atoms is more preferable.


In general formula (H-4), MH4 represents an alkylene group having 1 to 15 carbon atoms (one or more —CH2— in the alkylene group may each be substituted with —O—, —CO—, —COO—, or —OCO— so long as oxygen atoms are not directly adjacent to each other), —OCH2—, —CH2O—, —COO—, —OCO—, —CF2O—, —OCF2—, —CF2CF2—, —CH═CH—COO—, —CH═CH—OCO—, —COO—CH═CH—, —OCO—CH═CH—, —CH═CH—, —C≡C—, a single bond, a 1,4-phenylene group (any hydrogen atom in the 1,4-phenylene group may be substituted with a fluorine atom), or a trans-1,4-cyclohexylene group, but preferably represents an alkylene group having 1 to 14 carbon atoms. Considering volatility, the number of carbon atoms is preferably large. Considering viscosity, the number of carbon atoms is preferably not excessively large. Thus, the number of carbon atoms is more preferably 2 to 12, more preferably 3 to 10, more preferably 4 to 10, more preferably 5 to 10, and more preferably 6 to 10.


In the general formula (H-1) to the general formula (H-4), one —CH═ or two or more non-adjacent —CH═ in the 1,4-phenylene group may each be substituted with —N═. Hydrogen atoms in the 1,4-phenylene group may each independently be substituted with a fluorine atom or a chlorine atom.


In the general formula (H-1) to the general formula (H-4), one —CH2— or two or more non-adjacent —CH2— in the 1,4-cyclohexylene group may each be substituted with —O— or —S—. In the 1,4-cyclohexylene group, hydrogen atoms may each independently be substituted with a fluorine atom or a chlorine atom.


Specific examples include, for example, the formula (H-11) to the formula (H-15).




embedded image


When the liquid crystal composition of the present invention contains an antioxidant, the content thereof is preferably 10 ppm by mass or more, preferably 20 ppm by mass or more, and preferably 50 ppm by mass or more. The upper limit when the antioxidant is contained is 10000 ppm by mass, but is preferably 1000 ppm by mass, preferably 500 ppm by mass, and preferably 100 ppm by mass.


The liquid crystal composition of the present invention has a dielectric anisotropy (Δε) at 20° C. of −2.0 to −8.0, preferably −2.0 to −6.0, more preferably −2.0 to −5.0, and particularly preferably −2.5 to −5.0.


The refractive index anisotropy (Δn) of the liquid crystal composition of the present invention at 20° C. is 0.08 to 0.14, but is more preferably 0.09 to 0.13, and particularly preferably 0.09 to 0.12. More specifically, in order to comply with a small cell gap, it is preferably 0.10 to 0.13, and in order to comply with a large cell gap, it is preferably 0.08 to 0.10.


The viscosity of the liquid crystal composition of the present invention at 20° C. is 10 to 50 mPa·s, but is preferably 10 to 45 mPa·s, preferably 10 to 40 mPa·s, preferably 10 to 35 mPa·s, preferably 10 to 30 mPa·s, more preferably 10 to 25 mPa·s, and particularly preferably 10 to 22 mPa·s.


The rotational viscosity (γ1) of the liquid crystal composition of the present invention at 20° C. is 50 to 160 mPa·s, but is preferably 55 to 160 mPa·s, preferably 60 to 160 mPa·s, preferably 60 to 150 mPa·s, preferably 60 to 140 mPa·s, preferably 60 to 130 mPa·s, preferably 60 to 125 mPa·s, more preferably 60 to 120 mPa·s, more preferably 60 to 115 mPa·s, more preferably 60 to 110 mPa·s, and particularly preferably 60 to 100 mPa·s.


The nematic phase-isotropic liquid phase transition temperature (Tni) of the liquid crystal composition of the present invention is 60° C. to 120° C., but is preferably 70° C. to 100° C. and particularly preferably 70° C. to 85° C.


For example, when the entire liquid crystal composition according to the present invention exhibits negative dielectric anisotropy, the liquid crystal composition preferably includes the first and second monomers, one kind or two or more kinds of compounds selected from the compounds represented by the general formulae (N-1), (N-2), and (N-3), and the compound represented by the general formula (L).


Among the entire liquid crystal composition according to the present invention, it is preferable that the upper limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1), the general formula (N-2), the general formula (N-3), and the general formula (L) is 100% by mass, 99% by mass, 98% by mass, 97% by mass, 96% by mass, 95% by mass, 94% by mass, 93% by mass, 92% by mass, 91% by mass, 90% by mass, 89% by mass, 88% by mass, 87% by mass, 86% by mass, 85% by mass, or 84% by mass.


Moreover, among the entire liquid crystal composition according to the present invention, it is preferable that the lower limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1), the general formula (N-2), the general formula (N-3), and the general formula (L) is 78% by mass, 80% by mass, 81% by mass, 83% by mass, 85% by mass, 86% by mass, 87% by mass, 88% by mass, 89% by mass, 90% by mass, 91% by mass, 92% by mass, 93% by mass, 94% by mass, 95% by mass, 96% by mass, 97% by mass, 98% by mass, or 99% by mass.


Among the entire liquid crystal composition according to the present invention, it is preferable that the upper limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 100% by mass, 99% by mass, 98% by mass, 97% by mass, 96% by mass, 95% by mass, 94% by mass, 93% by mass, 92% by mass, 91% by mass, 90% by mass, 89% by mass, 88% by mass, 87% by mass, 86% by mass, 85% by mass, or 84% by mass.


Moreover, among the entire liquid crystal composition according to the present invention, it is preferable that the lower limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 78% by mass, 80% by mass, 81% by mass, 83% by mass, 85% by mass, 86% by mass, 87% by mass, 88% by mass, 89% by mass, 90% by mass, 91% by mass, 92% by mass, 93% by mass, 94% by mass, 95% by mass, 96% by mass, 97% by mass, 98% by mass, or 99% by mass.


Among the entire liquid crystal composition according to the present invention, it is preferable that the upper limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 100% by mass, 99% by mass, 98% by mass, 97% by mass, 96% by mass, 95% by mass, 94% by mass, 93% by mass, 92% by mass, 91% by mass, 90% by mass, 89% by mass, 88% by mass, 87% by mass, 86% by mass, or 85% by mass.


Moreover, among the entire liquid crystal composition according to the present invention, it is preferable that the lower limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 78% by mass, 80% by mass, 81% by mass, 83% by mass, 85% by mass, 86% by mass, 87% by mass, 88% by mass, 89% by mass, 90% by mass, 91% by mass, 92% by mass, 93% by mass, 94% by mass, 95% by mass, 96% by mass, 97% by mass, or 98% by mass.


Among the entire liquid crystal composition according to the present invention, it is preferable that the upper limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 100% by mass, 99% by mass, 98% by mass, 97% by mass, 96% by mass, 95% by mass, 94% by mass, 93% by mass, 92% by mass, 91% by mass, 90% by mass, 89% by mass, 88% by mass, 87% by mass, 86% by mass, or 85% by mass.


Moreover, among the entire liquid crystal composition according to the present invention, it is preferable that the lower limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 78% by mass, 80% by mass, 81% by mass, 83% by mass, 85% by mass, 86% by mass, 87% by mass, 88% by mass, 89% by mass, 90% by mass, 91% by mass, 92% by mass, 93% by mass, 94% by mass, 95% by mass, 96% by mass, 97% by mass, or 98% by mass.


Among the entire liquid crystal composition according to the present invention, it is preferable that the upper limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 100% by mass, 99% by mass, 98% by mass, 97% by mass, 96% by mass, 95% by mass, 94% by mass, 93% by mass, 92% by mass, 91% by mass, 90% by mass, 89% by mass, 88% by mass, 87% by mass, 86% by mass, or 85% by mass.


Moreover, among the entire liquid crystal composition according to the present invention, it is preferable that the lower limit of the proportion of the components composed only of one kind or two or more kinds of the first monomer, one kind or two or more kinds of the second monomer, and the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 78% by mass, 80% by mass, 81% by mass, 83% by mass, 85% by mass, 86% by mass, 87% by mass, 88% by mass, 89% by mass, 90% by mass, 91% by mass, 92% by mass, 93% by mass, 94% by mass, 95% by mass, 96% by mass, 97% by mass, or 98% by mass.


In addition, in the liquid crystal composition according to the present invention, in the case where the alignment property is important, the composition essentially includes eleven kinds or two or more kinds of the first monomer and one kind or two or more kinds of the second monomer, and preferably includes the general formula (N-1-1), the general formula (N-1-2), the general formula (N-1-3), or the general formula (N-1-4).


In addition, in the liquid crystal composition according to the present invention, in the case where the response speed is important, the composition essentially includes one kind or two or more kinds of the first monomers and one kind or two or more kinds of the second monomers, and preferably includes the general formula (N-1-10) or the general formula (N-1-11).


In addition, in the liquid crystal composition according to the present invention, in the case where the alignment property is important, the composition essentially includes eleven kinds or two or more kinds of the first monomer and one kind or two or more kinds of the second monomer, and preferably includes the general formula (N-1-1), the general formula (N-1-2), the general formula (N-1-3), or the general formula (N-1-4).


In addition, in the liquid crystal composition according to the present invention, in the case where the response speed is important, the composition essentially includes one kind or two or more kinds of the first monomers and one kind or two or more kinds of the second monomers, and preferably includes the general formula (N-1-10) or the general formula (N-1-11).


In addition, in the liquid crystal composition according to the present invention, in the case where the alignment property is important, the composition essentially includes one kind or two or more kinds of the first monomer and one kind or two or more kinds of the second monomer, and preferably includes the general formula (N-1-1), the general formula (N-1-2), the general formula (N-1-3), or the general formula (N-1-4).


In addition, in the liquid crystal composition according to the present invention, in the case where the response speed is important, the composition essentially includes one kind or two or more kinds of the first monomers and one kind or two or more kinds of the second monomers, and preferably includes the general formula (N-1-10) or the general formula (N-1-11).


Among the entire liquid crystal composition according to the present invention, it is preferable that the upper limit of the proportion of the components composed only of the general formula (N-1-4), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 99% by mass, 98% by mass, 97% by mass, 96% by mass, 95% by mass, 94% by mass, 93% by mass, 92% by mass, 91% by mass, 90% by mass, 89% by mass, 88% by mass, 87% by mass, 86% by mass, 85% by mass, or 84% by mass.


Moreover, among the entire liquid crystal composition according to the present invention, it is preferable that the lower limit of the proportion of the components composed only of the compounds represented by the general formula (N-1-4), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), and the general formula (L) is 78% by mass, 80% by mass, 81% by mass, 83% by mass, 85% by mass, 86% by mass, 87% by mass, 88% by mass, 89% by mass, 90% by mass, 91% by mass, 92% by mass, 93% by mass, 94% by mass, 95% by mass, 96% by mass, 97% by mass, or 98% by mass.


Among the entire liquid crystal composition according to the present invention, it is preferable that the upper limit of the proportion of the components composed only of the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), the general formula (L-1), the general formula (L-3), the general formula (L-4), the general formula (L-5), and the general formula (L-6) is 99% by mass, 98% by mass, 97% by mass, 96% by mass, 95% by mass, 94% by mass, 93% by mass, 92% by mass, 91% by mass, 90% by mass, 89% by mass, 88% by mass, 87% by mass, 86% by mass, 85% by mass, 84% by mass, 83% by mass, 82% by mass, 81% by mass, or 80% by mass.


Moreover, among the entire liquid crystal composition according to the present invention, it is preferable that the lower limit of the proportion of the components composed only of the compounds represented by the general formula (N-1a), the general formula (N-1b), the general formula (N-1c), the general formula (N-1d), the general formula (N-1e), the general formula (L-1), the general formula (L-3), the general formula (L-4), the general formula (L-5), and the general formula (L-6) is 68% by mass, 70% by mass, 71% by mass, 73% by mass, 75% by mass, 78% by mass, 80% by mass, 81% by mass, 83% by mass, 85% by mass, 86% by mass, 87% by mass, 88% by mass, 89% by mass, 90% by mass, 91% by mass, 92% by mass, 93% by mass, 94% by mass, 95% by mass, 96% by mass, 97% by mass, or 98% by mass.


A liquid crystal display element that uses the liquid crystal composition of the present invention has a notable feature, i.e., high-speed response. Furthermore, a satisfactory tilt angle is obtained, there are no or very little unreacted polymerizable compound, and the voltage holding ratio (VHR) is high. Thus, issues such as alignment defects and display defects do not arise or are satisfactorily suppressed. Since the tilt angle and the residual amount of the polymerizable compound can be controlled easily, the energy cost for production is easily optimized and reduced. Thus, the liquid crystal display element is optimum for improving the production efficiency and for mass production.


A liquid crystal display element that uses the liquid crystal composition of the present invention is particularly useful in active matrix-driving liquid crystal display elements and can be used in liquid crystal display elements of PSA mode, PSVA mode, VA mode, PS-IPS mode, or PS-FFS mode.


The liquid crystal display element according to the present invention preferably includes a first substrate and a second substrate disposed opposite to each other, a common electrode provided on the first substrate or the second substrate, a pixel electrode provided on the first substrate or the second substrate and having a thin film transistor, and a liquid crystal layer including a liquid crystal composition provided between the first substrate and the second substrate. If necessary, an alignment film for controlling the alignment direction of the liquid crystal molecules may be provided on the opposite surface side of at least one of the first substrate and/or the second substrate so as to come into contact with the liquid crystal layer. As the alignment film, a vertical alignment film and a horizontal alignment film can be appropriately selected together with the driving mode of the liquid crystal display element, and a known alignment film such as a rubbing alignment film (for example, polyimide) or a photo alignment film (for example, a decomposition type polyimide) can be used. Further, a color filter may be provided as appropriate on the first substrate or the second substrate, and a color filter may be provided on the pixel electrode or the common electrode.


Two substrates of a liquid crystal cell used in the liquid crystal display element according to the present invention can be formed of flexible transparent material such as glass or plastic. One of the substrates may be formed of a non-transparent material such as silicon. A transparent substrate that has a transparent electrode layer can be obtained by, for example, sputtering indium tin oxide (ITO) on a transparent substrate such as a glass plate.


A color filter can be manufactured by a pigment dispersing method, a printing method, an electrodeposition method, a dyeing method, or the like. For example, according to a method for manufacturing a color filter by a pigment dispersing method, a curable color composition for a color filter is applied to the transparent substrate, patterning is performed, and the composition is cured under heating or irradiation with light. This process is performed for each of three colors, red, green and blue, to manufacture pixel portions for a color filter. In addition, pixel electrodes that include active elements, such as TFTs, thin-film diodes, metal-insulator-metal resistive elements, etc., can be formed on the substrate.


It is preferable that the first substrate and the second substrate face each other so that the common electrode and the pixel electrode layer are inside.


The distance between the first substrate and the second substrate may be adjusted via a spacer. In this case, the adjustment is preferably made so that the thickness of the light control layer is 1 to 100 m. The thickness is more preferably 1.5 to 10 m. When a polarizer is used, the product of the refractive index anisotropy Δn of the liquid crystal and the cell thickness d is preferably adjusted to maximize the contrast. When two polarizers are provided, the polarizing axis of each polarizer can be adjusted to improve the viewing angle and contrast. Moreover, a retardation film can be used to widen the viewing angle. Examples of the spacer include glass particles, plastic particles, alumina particles, and photoresist materials. Then a sealing agent such as an epoxy-based thermosetting composition is screen-printed onto the substrate while leaving a liquid crystal injection inlet, the substrates are bonded to each other, and the sealing agent is cured under heating.


Examples of the method for injecting the liquid crystal composition into a gap between the two substrates include a common vacuum injection method and an ODF method.


A second aspect of the present invention is a liquid crystal display element, wherein the liquid crystal display element includes: a first substrate and a second substrate disposed opposite to each other; a liquid crystal layer filled between the first substrate and the second substrate; on the first substrate, an electrode layer having a plurality of gate bus lines and data bus lines arranged in a matrix, a thin film transistor provided in an intersection portion between the gate bus line and the data bus line, and a pixel electrode driven by the thin film transistor per each pixel; a common electrode formed on the first substrate or the second substrate; and a resin component obtained by curing a polymerizable compound having two or more kinds of biphenyl skeletons between the first substrate and the second substrate, and has no alignment film on at least one substrate surface.


In order to obtain satisfactory liquid crystal alignment performance, an appropriate polymerization rate is desirable. Thus, the method for polymerizing the polymerizable compound or the polymerizable monomer and the spontaneous orientation monomer contained in the liquid crystal composition of the present invention is preferably a polymerization method that involves applying an active energy ray, such as an ultraviolet ray or an electron beam singly or in combination or sequentially. When ultraviolet rays are used, a polarized light source or an unpolarized light source may be used. When polymerization is conducted by having the liquid crystal composition interposed between the two substrates, at least the irradiation-side substrate must have transparency appropriate for the active energy ray. Alternatively, after a particular part only is polymerized through a mask under irradiation with light, the conditions such as an electric field, a magnetic field, a temperature, etc., may be changed to change the alignment state of the unpolymerized portion, and then an active energy ray may be applied to conduct polymerization. In particular, in conducting ultraviolet ray exposure, it is preferable to apply an AC electric field to the liquid crystal composition during ultraviolet ray exposure. The AC electric field applied is preferably AC having a frequency of 10 Hz to 10 kHz and more preferably 60 Hz to 10 kHz. The voltage is selected depending on the desired pretilt angle of the liquid crystal display element. In other words, the pretilt angle of the liquid crystal display element can be controlled by adjusting the voltage applied. In a PSVA-mode liquid crystal display element, the pretilt angle is preferably controlled to 80 DD to 89.9 DD from the viewpoints of alignment stability and contrast.


There are no particular restrictions on the temperature at the time of irradiation with an active energy ray such as an ultraviolet ray or electron beam used in polymerizing polymerizable compounds contained in the liquid crystal composition of the present invention. For example, when the liquid crystal composition of the present invention is applied to a liquid crystal display element including a substrate having an alignment film, the temperature during irradiation is preferably within a temperature range at which the liquid crystal state of the liquid crystal composition is maintained. Polymerization is preferably conducted at a temperature near room temperature, i.e., typically 15° C. to 35° C.


On the other hand, when the liquid crystal composition of the present invention is applied to a liquid crystal display element including a substrate not having an alignment film, for example, the temperature range may be wider than a temperature range during irradiation applied to a liquid crystal display element having a substrate having the alignment film.


Examples of the lamp used to generate an ultraviolet ray include a metal halide lamp, a high-pressure mercury lamp, and an ultra-high-pressure mercury lamp. The ultraviolet ray applied is preferably an ultraviolet ray in the wavelength range outside the absorption wavelength range of the liquid crystal composition. If needed, some part of the ultraviolet ray may be cut before use. The intensity of the ultraviolet ray applied is preferably 0.1 mW/cm2 to 100 W/cm2 and more preferably 2 mW/cm2 to 50 W/cm2. The amount of energy of the ultraviolet ray applied can be appropriately adjusted but is preferably 10 mJ/cm2 to 500 J/cm2 and more preferably 100 mJ/cm2 to 200 J/cm2. In applying the ultraviolet ray, the intensity may be varied. The time for applying the ultraviolet ray is appropriately selected based on the intensity of the ultraviolet ray applied, but is preferably 10 to 3600 seconds and more preferably 10 to 600 seconds.


EXAMPLES

The present invention will be described in further detail with reference to examples below, but the present invention is not limited to these examples. Note that “%” for the compositions of Examples and Comparative Examples below denotes “% by mass”. In Examples, the following abbreviations are used to describe compounds.


The properties measured in Examples are as follows.


Tni: nematic phase-isotropic liquid phase transition temperature (° C.)


Δn: refractive index anisotropy at 20° C.


f: viscosity at 20° C. (mPa·s)


γ1: rotational viscosity at 20° C. (mPa·s)


Δε: dielectric anisotropy at 20° C.


K33: elastic modulus K33 at 20° C. (PN)


In Examples, the following abbreviations are used to describe compounds.


(Side Chain)

-n —CnH2n+1 a linear alkyl group having n carbon atoms


n- CnH2n+1— a linear alkyl group having n carbon atoms


—On —OCnH2n+1 a linear alkoxy group having n carbon atoms


nO— CnH2n+1O— a linear alkoxy group having n carbon atoms


—V —CH═CH2


V— CH2═CH—


—V1 —CH═CH—CH3


1V— CH3—CH═CH—


-2V —CH2—CH2—CH═CH2


V2- CH2═CH—CH2—CH2


-2V1 —CH2—CH2—CH═CH—CH3


1V2- CH3—CH═CH—CH2—CH2


(Linking Group)

—CFFO— —CF2—O—


—OCFF— —O—CF2


-1O— —CH2—O—


—O1- —O—CH2


—COO— —COO—


—OCO— —OCO—


<Cyclic Structure>



embedded image


embedded image


The evaluations of “low temperature storage stability”, “vertical alignment”, “burn-in test (pretilt angle change with time)” and “reliability” in Examples and Comparative Examples were carried out by the following method.


(Evaluation Test for Low Temperature Storage Stability)

The liquid crystal composition was filtered through a membrane filter (manufactured by Agilent Technologies, PTFE 13 m-0.2 m), and allowed to stand for 15 minutes under vacuum reduced pressure conditions to remove dissolved air. This was weighed in an amount of 0.5 g in a vial that had been washed with acetone and sufficiently dried, and allowed to stand in an environment of −20° C. for 20 days. Then, the presence or absence of precipitation was observed visually, and the results were determined in the following 4 grades.


A: No deposition can be observed.


B: Deposited after 2 weeks.


C: Deposited after 1 week.


D: Deposition can be observed.


(Evaluation Test for Vertical Alignment 1)

A first substrate having a transparent electrode layer composed of a common electrode having a uniform entire surface and a color filter layer and having no alignment film (a common electrode substrate) and a second substrate having a pixel electrode layer containing a transparent pixel electrode driven by an active element and having no alignment film (pixel electrode substrate) were produced. The liquid crystal composition was dropped on the first substrate, and held with the second substrate, and the sealing material was cured under a condition of 110° C. for 2 hours under normal pressure, so as to provide a liquid crystal cell having a cell gap of 3.2 m (without an insulating film). The alignment unevenness such as vertical alignment and drop marks herein was observed using a polarizing microscope and evaluated by the following four grades.


A: Uniform vertical alignment was observed over the entire surface.


B: Alignment defects were observed slightly, which was an allowable level.


C: Alignment defects were observed, which was an unallowable level.


D: Alignment defects were significantly severe.


(Evaluation Test for Vertical Alignment 2)

A first substrate having a transparent electrode layer composed of a common electrode patterned on an insulating layer and a color filter layer and having no alignment film (a common electrode substrate) and a second substrate having a pixel electrode layer containing a transparent pixel electrode driven by an active element and having no alignment film (pixel electrode substrate) were produced. The liquid crystal composition was dropped on the first substrate, and held with the second substrate, and the sealing material was cured under a condition of 110° C. for 2 hours under normal pressure, so as to provide a liquid crystal cell having a cell gap of 3.2 m (with an insulating film). The alignment unevenness such as vertical alignment and drop marks herein was observed using a polarizing microscope and evaluated by the following four grades. Observation was carried out by using the polarizing microscope and evaluated by the following four grades.


A: Uniform vertical alignment was observed over the entire surface.


B: Alignment defects were observed slightly, which was an allowable level.


C: Alignment defects were observed, which was an unallowable level.


D: Alignment defects were significantly severe.


(Evaluation Method for Liquid Crystal Burn-in (Pretilt Angle Change with Time))


First, a polyimide alignment film inducing vertical alignment was applied to an ITO coated substrate, and then a liquid crystal composition was injected into a liquid crystal cell (cell gap 3.5 μm) containing the ITO coated substrate subjected to rubbing treatment of the polyimide alignment film by a vacuum injection method. Thereafter, the liquid crystal cell to which the liquid crystal composition was injected was applied with a voltage of 10 V at a frequency of 100 Hz, and then irradiated with an ultraviolet ray using a high-pressure mercury lamp through a filter that cuts off an ultraviolet ray of 325 nm or less. At this time, the illuminance measured under the condition of a center wavelength of 365 nm was adjusted to 100 mW/cm2, and the light was irradiated with an ultraviolet ray having the integrated light quantity of 10 J/cm2. The ultraviolet irradiation condition was set as irradiation condition 1.


Under this irradiation condition 1, a pretilt angle is given to the liquid crystal molecules in the liquid crystal cell.


Then, by using a fluorescent UV lamp, the illuminance measured at a central wavelength of 313 nm was adjusted to 3 mW/cm2, and further the light was irradiated with an ultraviolet ray having the integrated light quantity of 20 J/cm2 to obtain a liquid crystal display element. The ultraviolet irradiation condition was set as irradiation condition 2. By irradiation condition 2, the residual amount of the polymerizable compound in the unreacted liquid crystal cell that has not reacted under irradiation condition 1 is reduced.


After irradiation with ultraviolet rays, a display defect (burn-in) was evaluated by a change in pretilt angle.


First, the pretilt angle of the liquid crystal display element was measured to obtain a pretilt angle (initial). The liquid crystal display element was irradiated with a backlight for 10 hours while applying a rectangular wave of 30 V at a frequency of 100 Hz. Thereafter, the pretilt angle was measured to obtain a pretilt angle (after the test). A value obtained by subtracting the pretilt angle (after the test) from the measured pretilt angle (initial) was defined as a pretilt angle change amount (=absolute value of pretilt angle change) [ ].


The pretilt angle was measured using an OPTIPRO manufactured by Shintech. The magnitude of the voltage of 30V is several times larger than the normal driving voltage, which is an acceleration test.


When the pretilt angle change amount is closer to 0 [0], there is less possibility that a display failure due to a change in the pretilt angle will occur. In this study, the change amount of 1.3 [0] or less was set as the allowable limit range for display unevenness.


(Preparation and Evaluation Results of Liquid Crystal Composition)

In this example, the first monomer represented by the following formulae (P-1) to (P-35) was used.




embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


embedded image


Comparative Example 1, Examples 1 to 3

A liquid crystal composition of the following LC-A was prepared, and its physical properties were measured.


The components of the liquid crystal composition and the results of its physical properties were as shown in Table 1.











TABLE 1







LC-A



















3-Cy-Cy-2
17.5



3-Cy-Cy-4
3



3-Cy-Ph-O1
15



3-Ph-Ph-1
9



3-Cy-Ph-Ph-2
8



3-Cy-1O-Ph5-O1
7.5



3-Cy-Cy-1O-Ph5-O2
17



2-Cy-Ph-Ph5-O2
6.5



3-Cy-Ph-Ph5-O2
8



3-Cy-Ph-Ph5-O4
8.5



Total (%)
100



TNI [° C.]
75.4



Δn
0.111



γ1 [mPa · s]
118



Δε
−3.1










As Example 1, a liquid crystal composition LC-1 was prepared by adding 1.50 parts by weight of a compound represented by Formula (P-1) and 0.50 parts by weight of a compound represented by Formula (XX-5), with regard to 100 parts by weight of a liquid crystal composition LC-A. As Example 2, a liquid crystal composition LC-2 was prepared by adding 1.50 parts by weight of a compound represented by Formula (P-1) and 1.00 part by weight of a compound represented by Formula (XX-5), with regard to 100 parts by weight of a liquid crystal composition LC-A. As Example 3, a liquid crystal composition LC-3 was prepared by adding 1.50 parts by weight of a compound represented by Formula (P-1) and 1.50 parts by weight of a compound represented by Formula (XX-5), with regard to 100 parts by weight of a liquid crystal composition LC-A. As Example 4, a liquid crystal composition LC-4 was prepared by adding 0.50 parts by weight of a compound represented by Formula (P-1) and 1.50 parts by weight of a compound represented by Formula (XX-5), with regard to 100 parts by weight of a liquid crystal composition LC-A. Further, as Comparative Example 1, a liquid crystal composition LC-5 was prepared by adding 1.50 parts by weight of a compound represented by Formula (P-1) and 0.30 parts by weight of a compound represented by Formula (XX-5), with regard to 100 parts by weight of a liquid crystal composition LC-A.













TABLE 2







Liquid Crystal





Composition
Compound
Compound



LC-A
(P-1)
(XX-5)




















Example 1
LC-1
100
1.50
0.50


Example 2
LC-2
100
1.50
1.00


Example 3
LC-3
100
1.50
1.50


Example 4
LC-4
100
0.50
1.50


Comparative
LC-5
100
1.50
0.30


Example 1









The results of low temperature storage stability, vertical alignment (1), vertical alignment (2), and pretilt angle change amount were as shown in Table 3.














TABLE 3










Pretilt



Low


Angle



Temperature
Vertical
Vertical
Change



Storage
Alignment
Alignment
Amount



Stability
(1)
(2)
(°)





















Example 1
LC-1
A
A
A
1.0


Example 2
LC-2
A
A
A
0.6


Example 3
LC-3
B
A
B
0.4


Example 4
LC-4
A
B
B
0.3


Comparative
LC-5
A
A
A
2.0


Example 1









Examples 1 to 4 showed a pretilt angle change amount sufficiently smaller than that of Comparative Example 1, and it was confirmed that there were little display unevenness and burn-in. In Examples 1 to 4, the amount of the second monomer (XX-5) added is larger than that in Comparative Example 1, so that the strength of the polymer is increased and the stability is considered to be excellent. In Examples 1 to 3, the ratio of the first monomer (P-1) to the second monomer (XX-5) is sufficient, so that the vertical alignment is considered high.


(Comparative Example 2, Examples 5 to 8) A liquid crystal composition of the following LC-B was prepared, and its physical properties were measured. The components of the liquid crystal composition and the results of its physical properties were as shown in Table 4.











TABLE 4







LC-B



















3-Cy-Cy-2
11.5



3-Cy-Cy-4
12.5



3-Cy-Cy-5
3



3-Cy-Cy-V1
10



3-Cy-Ph-O1
4.5



1V2-Ph-Ph-1
2



3-Cy-Ph-Ph-1
9



3-Cy-Ph-Ph-2
5.5



3-Cy-Ph-Ph5-O2
10



3-Ph-Ph5-O2
12



3-Cy-Ph5-O2
7



3-Cy-Cy-Ph5-O2
10



2O-Y-O5
3



Total (%)
100



TNI [° C.]
75.2



Δn
0.111



γ1 [mPa · s]
138



Δε
−3.42










As Example 5, a liquid crystal composition LC-6 was prepared by adding 0.50 parts by weight of a compound represented by Formula (P-26) and 0.50 parts by weight of a compound represented by Formula (XX-2), with regard to 100 parts by weight of a liquid crystal composition LC-B. As Example 6, a liquid crystal composition LC-7 was prepared by adding 0.50 parts by weight of a compound represented by Formula (P-26) and 1.00 part by weight of a compound represented by Formula (XX-2), with regard to 100 parts by weight of a liquid crystal composition LC-B. As Example 7, a liquid crystal composition LC-8 was prepared by adding 0.50 parts by weight of a compound represented by Formula (P-26) and 1.50 parts by weight of a compound represented by Formula (XX-2), with regard to 100 parts by weight of a liquid crystal composition LC-B. As Example 8, a liquid crystal composition LC-9 was prepared by adding 0.50 parts by weight of a compound represented by Formula (P-26) and 1.50 parts by weight of a compound represented by Formula (XX-2), with regard to 100 parts by weight of a liquid crystal composition LC-B. Further, as Comparative Example 2, a liquid crystal composition LC-10 was prepared by adding 1.50 parts by weight of a compound represented by Formula (P-26) and 0.30 parts by weight of a compound represented by Formula (XX-2), with regard to 100 parts by weight of a liquid crystal composition LC-B.













TABLE 5







Liquid Crystal





Composition
Compound
Compound



LC-B
(P-26)
(XX-2)




















Example 5
LC-6
100
1.00
0.50


Example 6
LC-7
100
1.00
1.00


Example 7
LC-8
100
1.00
1.50


Example 8
LC-9
100
0.50
1.50


Comparative
LC-10
100
0.50
0.30


Example 2









The results of low temperature storage stability, vertical alignment (1), vertical alignment (2), and pretilt angle change amount are shown below.














TABLE 6










Pretilt



Low


Angle



Temperature
Vertical
Vertical
Change



Storage
Alignment
Alignment
Amount



Stability
(1)
(2)
(°)





















Example 5
LC-6
A
A
A
0.8


Example 6
LC-7
A
A
A
0.4


Example 7
LC-8
B
A
B
0.2


Example 8
LC-9
A
B
B
0.2


Comparative
LC-10
A
A
A
1.5


Example 2









Examples 5 to 7 showed a pretilt angle change amount sufficiently smaller than that of Comparative Example 2, and it was confirmed that there were little display unevenness and burn-in. In Examples 5 to 7, the amount of the second monomer (R-1) added is larger than that in Comparative Example 2, so that the strength of the polymer is increased and the stability is considered to be excellent. In Examples 4 to 6, the ratio of the first monomer (Formula (P-26)) to the second monomer (Formula (XX-2)) is sufficient, so that the vertical alignment is considered high.


Example 9 to Example 29

Liquid crystal compositions were prepared by adding a compound represented by Formula (P-2), Formula (P-4), Formula (P-5), Formula (P-6), Formula (P-13), Formula (P-14), or Formula (P-15) as the first monomer and the second monomer (XX-5), with regard to 100 parts by weight of a liquid crystal composition LC-A to provide Example 9 to Example 29. The ratio of each example is shown in the following table.













TABLE 7








Liquid

First Monomer
Second Monomer














Crystal
% by
Compound
% by
Compound
% by



Composition
weight
1
mass
2
mass





Example 9
LC-A
100
(P-2) 
1.2
(XX-5)
0.6


Example 10
LC-A
100
(P-2) 
1.2
(XX-5)
0.9


Example 11
LC-A
100
(P-2) 
1.2
(XX-5)
1.6


Example 12
LC-A
100
(P-4) 
1.5
(XX-5)
0.6


Example 13
LC-A
100
(P-4) 
1.5
(XX-5)
0.9


Example 14
LC-A
100
(P-4) 
1.5
(XX-5)
1.6


Example 15
LC-A
100
(P-5) 
1.2
(XX-5)
0.6


Example 16
LC-A
100
(P-5) 
1.2
(XX-5)
0.9


Example 17
LC-A
100
(P-5) 
1.2
(XX-5)
1.6


Example 18
LC-A
100
(P-6) 
0.6
(XX-5)
0.6


Example 19
LC-A
100
(P-6) 
0.6
(XX-5)
0.9


Example 20
LC-A
100
(P-6) 
0.6
(XX-5)
1.6


Example 21
LC-A
100
(P-13)
1.2
(XX-5)
0.6


Example 22
LC-A
100
(P-13)
1.2
(XX-5)
0.9


Example 23
LC-A
100
(P-13)
1.2
(XX-5)
1.6


Example 24
LC-A
100
(P-14)
1.2
(XX-5)
0.6


Example 25
LC-A
100
(P-14)
1.2
(XX-5)
0.9


Example 26
LC-A
100
(P-14)
1.2
(XX-5)
1.6


Example 27
LC-A
100
(P-15)
1.2
(XX-5)
0.6


Example 28
LC-A
100
(P-15)
1.2
(XX-5)
0.9


Example 29
LC-A
100
(P-15)
1.2
(XX-5)
1.6









The results of low temperature storage stability, vertical alignment (1), vertical alignment (2), and pretilt angle change amount are shown below.














TABLE 8







Low






Temperature
Vertical
Vertical
Pretilt Angle



Storage
Alignment
Alignment
Change Amount



Stability
(1)
(2)
(°)




















Example 9
A
A
A
1.0


Example 10
A
A
A
0.7


Example 11
A
A
B
0.4


Example 12
A
A
A
1.1


Example 13
A
A
A
0.8


Example 14
A
A
B
0.5


Example 15
A
A
A
0.8


Example 16
A
A
A
0.5


Example 17
A
A
B
0.3


Example 18
A
A
A
0.4


Example 19
A
A
A
0.2


Example 20
A
B
B
0.1


Example 21
A
A
A
1.0


Example 22
A
A
A
0.7


Example 23
A
A
B
0.4


Example 24
A
A
A
1.0


Example 25
A
A
A
0.7


Example 26
A
A
B
0.3


Example 27
A
A
A
0.9


Example 28
A
A
A
0.8


Example 29
A
A
A
0.4









Examples 9 to 29 showed a pretilt angle change amount sufficiently smaller than that of Comparative Example, and it was confirmed that there were little display unevenness and burn-in. In Examples 9 to 29, the amount of the second monomer (XX-5) added is larger than that in Comparative Example 2, so that the strength of the polymer is increased and the stability is considered to be excellent.


Example 30 to Example 36

Liquid crystal compositions were prepared by adding 0.50 parts by weight of a compound represented by Formula (P-20), Formula (P-25), Formula (P-27), Formula (P-28), Formula (P-29), Formula (P-22), or Formula (P-35) as the first monomer and 0.50 parts by weight of the second monomer (XX-2), with regard to 100 parts by weight of a liquid crystal composition LC-B to provide Example 30 to Example 36. The ratio of each example is shown in the following table.













TABLE 9










First Monomer
Second Monomer














Liquid Crystal
% by

Added

Added



Composition
weight
Compound 1
Amount (%)
Compound 2
Amount (%)
















Example 30
LC-B
100
(P-20)
1.0
(XX-2)
0.5


Example 31
LC-B
100
(P-25)
1.0
(XX-2)
0.5


Example 32
LC-B
100
(P-27)
1.0
(XX-2)
0.5


Example 33
LC-B
100
(P-28)
1.0
(XX-2)
0.5


Example 34
LC-B
100
(P-29)
1.0
(XX-2)
0.5


Example 35
LC-B
100
(P-33)
1.0
(XX-2)
0.5


Example 36
LC-B
100
(P-35)
1.0
(XX-2)
0.5









The results of low temperature storage stability, vertical alignment (1), vertical alignment (2), and pretilt angle change amount are shown below.














TABLE 10







Low






Temperature
Vertical
Vertical
Pretilt Angle



Storage
Alignment
Alignment
Change Amount



Stability
(1)
(2)
(°)




















Example 30
A
A
A
0.8


Example 31
A
A
A
0.9


Example 32
A
A
A
0.7


Example 33
A
A
A
0.8


Example 34
A
A
A
1.0


Example 35
A
A
A
1.1


Example 36
A
A
A
1.1









In Examples 30 to 36, it was confirmed that a pretilt change amount was sufficiently smaller than that of the comparative example. It is thought that the increase in the amount of the second monomer increases the strength of the polymer, provides excellent stability and improved tilt angle stability.


Example 37 to Example 45

Liquid crystal compositions were prepared by adding compounds represented by Formula (P-1), and Formula (P-4), Formula (P-5), or Formula (P-26) as the first monomer and compounds represented by Formula (XX-5) and Formula (XX-1), Formula (XX-7), or Formula (XX-15) as the second monomer, with regard to 100 parts by weight of a liquid crystal composition LC-A to provide Example 37 to Example 45. The ratio of each example is shown in the following table.













TABLE 11










First Monomer
Second Monomer


















Liquid


Added

Added

Added

Added



Crystal
% by
Compound
Amount
Compound
Amount
Compound
Amount
Compound
Amount



Composition
weight
1
(%)
2
(%)
1
(%)
2
(%)




















Example 37
LC-A
100
(P-1)
1.0
(P-4)
0.2
(XX-5)
0.3
(XX-1)
0.5


Example 38
LC-A
100
(P-1)
1.0
(P-5)
0.4
(XX-5)
0.3
(XX-7)
0.3


Example 39
LC-A
100
(P-1)
1.0
 (P-26)
1.0
(XX-5)
0.3
 (XX-15)
0.5


Example 40
LC-A
100
(P-1)
1.2
(P-4)
0.2
(XX-5)
0.3
(XX-1)
0.2


Example 41
LC-A
100
(P-1)
1.2
(P-5)
0.4
(XX-5)
0.3
(XX-7)
0.4


Example 42
LC-A
100
(P-1)
1.2
 (P-26)
1.0
(XX-5)
0.3
 (XX-15)
0.7


Example 43
LC-A
100
(P-1)
1.5
(P-4)
0.2
(XX-5)
0.3
(XX-1)
0.5


Example 44
LC-A
100
(P-1)
1.5
(P-5)
0.4
(XX-5)
1.5
(XX-7)
0.5


Example 45
LC-A
100
(P-1)
1.5
 (P-26)
1.0
(XX-5)
1.5
 (XX-15)
0.5









The results of low temperature storage stability, vertical alignment (1), vertical alignment (2), and pretilt angle change amount are shown below.














TABLE 12







Low






Temperature
Vertical
Vertical
Pretilt Angle



Storage
Alignment
Alignment
Change Amount



Stability
(1)
(2)
(°)




















Example 37
A
A
A
0.8


Example 38
A
A
A
1.1


Example 39
A
A
A
1.1


Example 40
A
A
A
1.1


Example 41
A
A
A
1.0


Example 42
A
A
A
1.1


Example 43
A
A
A
1.0


Example 44
A
A
A
0.5


Example 45
A
A
A
0.6









In Examples 37 to 45, it was confirmed that a pretilt change amount was sufficiently smaller than that of the comparative example. It is thought that the increase in the amount of the second monomer increases the stability of the polymer, provides improved tilt angle stability.


In Examples 37 to 45, the low temperature storage stability, vertical alignment, and pretilt change amount were evaluated in the case where two kinds of the first monomers and two kinds of the second monomers were used. It was confirmed that a pretilt change amount was sufficiently smaller than that of the comparative example. It was confirmed that the pretilt change amount which was sufficiently smaller than that of the comparative example was also exhibited even when two kinds of monomers were added. It was also confirmed that the low temperature storage stability was improved by adding a polymerizable compound. When the solubility of the first monomer and the second monomer in the liquid crystal is low, the concentration of one component may be lowered, and further, a different spontaneous orientation monomer may be added to improve the vertical alignment.


Further, in place of the liquid crystal compositions LC-A and LC-B, compositions composed of compounds and mixing ratios as shown below were prepared, and the prepared liquid crystal compositions were designated as LC-C to LC-H.















TABLE 13






LC-C
LC-D
LC-E
LC-F
LC-G
LC-H





















3-Ph-Ph-1
 11
 13
 8
12.5




3-Cy-1O-Ph5-O1

 16

6




3-Cy-1O-Ph5-O2



6.5




3-Cy-Ph-O1


 14

7



3-Cy-Ph-O2


 14





2-Cy-Cy-1O-Ph5-O2



15




3-Cy-Cy-1O-Ph5-O2
 16

 21
2




2-Cy-Ph-Ph5-O2
 6

 6
6
8.5
3


3-Cy-Ph-Ph5-O2
 7

 8

8.5
8.5


3-Cy-Ph-Ph5-O3



7




3-Cy-Ph-Ph5-O4
 6

 12
9




3-Cy-Cy-2
 24
 21
 17
18
23.5
8


3-Cy-Cy-4
 7


7.5
10
7.5


3-Cy-Ph5-O2
 7



13
7


5-Cy-Ph5-O2
 7







3-Ph-Ph5-O2

 14



16


3-Cy-Cy-Ph5-O2





10


4-Cy-Cy-Ph5-O2




9



5-Cy-Cy-Ph5-O2




5
8


3-Cy-Cy-Ph-1
 3
 10






3-Cy-Ph-Ph-1
 3







3-Cy-Ph-Ph-2
 3
 10

6




5-Cy-Ph-Ph-2

 16

4.5




3-Ph-Ph5-Ph-2




7.5
8


4-Ph-Ph5-Ph-2




8



3-Cy-Cy-V





14.5


3-Cy-Cy-V-1





9.5


Total (%)
100
100
100
100
100
100


TNI [° C.]
 77
 77
75.9
75.5
75.3
74.4


Δn
0.112
0.112
0.109
0.102
0.106
0.107


γ1 [mPa·s]
−3
−3
−2.9
−2.6
−2.67
−2.87


Δε
110
110
124
87
93
79









The compounds represented by Formula (P-1), (P-2), (P-3), (P-7), (P-15), (P-28), or (P-32) as the first monomer and the compounds represented by Formula (XX-1), (XX-2), (XX-5), (XX-7), and (XX-15) as the second monomer were mixed with each of the liquid crystal compositions LC-C to LC-H at an appropriate concentration, and the alignment test was evaluated in the same manner as described above. As a result, it was confirmed that the alignment property was improved in comparison with the comparative example.


Example 46 to Example 53

A liquid crystal composition of the following LC-A was prepared, and its physical properties were measured. The components of the liquid crystal composition and the results of its physical properties were as shown in Tables 14 and 15.


Liquid crystal compositions were prepared by adding compounds represented by Formula (P-36), Formula (P-37), Formula (P-48), Formula (P-49), Formula (P-50), Formula (P-51), Formula (P-52), or Formula (P-53) as the first monomer and compounds represented by Formula (XX-5) or Formula (XX-21) as the second monomer, with regard to 100 parts by weight of a liquid crystal composition LC-A to provide Example 46 to Example 53. The ratio of each example is shown in the following table.













TABLE 14










First Monomer
Second Monomer


















Liquid


Added

Added

Added

Added



Crystal
% by
Compound
Amount
Compound
Amount
Compound
Amount
Compound
Amount



Composition
weight
1
(%)
2
(%)
1
(%)
2
(%)





Example 46
LC-A
100
(P-36)
0.2
(P-37)
0.4
(XX-5)
0.6
(XX-21)



Example 47
LC-A
100
(P-36)
0.2
(P-37)
0.4
(XX-5)
0.3
(XX-21)
0.3 


Example 48
LC-A
100
(P-36)
0.2
(P-38)
0.4
(XX-5)
0.6
(XX-21)



Example 49
LC-A
100
(P-36)
0.2
(P-38)
0.4
(XX-5)
0.3
(XX-21)
0.15


Example 50
LC-A
100
(P-39)
0.5


(XX-5)
0.3
(XX-21)



Example 51
LC-A
100
(P-39)
0.7


(XX-5)
 0.45
(XX-21)



Example 52
LC-A
100
(P-40)
0.5


(XX-5)
0.6
(XX-21)



Example 53
LC-A
100
(P-40)
0.5


(XX-5)
0.3
(XX-21)
0.3 









The results of low temperature storage stability, vertical alignment (1), vertical alignment (2), and pretilt angle change amount are shown below.














TABLE 15







Low






Temperature
Vertical
Vertical
Pretilt Angle



Storage
Alignment
Alignment
Change Amount



Stability
(1)
(2)
(°)




















Example 46
A
A
A
0.5


Example 47
A
A
A
0.4


Example 48
A
A
A
0.5


Example 49
A
A
A
0.7


Example 50
A
A
A
0.8


Example 51
A
A
A
0.8


Example 52
A
A
A
0.5


Example 53
A
A
A
0.5









In Examples 46 to 53, it was confirmed that a pretilt change amount was sufficiently smaller than that of the comparative example. It is thought that the increase in the amount of the second monomer increases the stability of the polymer, provides improved tilt angle stability.


In Examples 46 to 53, the low temperature storage stability, vertical alignment, and pretilt change amount were evaluated in the case where two kinds of the first monomers and two kinds of the second monomers were used. It was confirmed that a pretilt change amount was sufficiently smaller than that of the comparative example. It was confirmed that the pretilt change amount which was sufficiently smaller than that of the comparative example was also exhibited even when two kinds of monomers were added. It was also confirmed that the low temperature storage stability was improved by adding a polymerizable compound. When the solubility of the first monomer and the second monomer in the liquid crystal is low, the concentration of one component may be lowered, and further, a different spontaneous orientation monomer may be added to improve the vertical alignment.


Moreover, the cell obtained by enclosing the liquid crystal composition containing the first monomer and the second monomer was set in a polarizing microscope in which a polarizer and an analyzer were arranged orthogonally, and the transmitted light was observed. When the liquid crystal molecules are vertically aligned, the light cannot be transmitted through the action of the polarizing plate, and the cell is displayed in black. When the above samples were evaluated by this test method, it was confirmed that no alignment unevenness occurred in all the samples and uniform vertical alignment was exhibited.


Further, when the pretilt angle generated by the polymerization by ultraviolet light irradiation was evaluated, it was confirmed that an appropriate tilt angle was given to all the samples. It has been confirmed that the liquid crystal display element using these has a sufficiently fast response since a sufficient pretilt angle is given.


Also, in this evaluation, in order to evaluate the polymer stability of each monomer in a state where the initial pretilt angle was constant, a substrate with a polyimide alignment film that induces vertical alignment was used when the pretilt angle change amount was confirmed. It was also confirmed that the same results were obtained when a liquid crystal cell having a cell gap of 3.2 m was used, which was composed of a first substrate having no alignment film (common electrode substrate) and a second substrate having no alignment film (pixel electrode substrate), and obtained by dropping a liquid crystal composition onto the first substrate, and holding the liquid crystal composition with the second substrate, and curing the sealing material.


In addition, it is considered that the pretilt change with time in the present invention is affected by the hardness of the polymer film, and a harder polymer film is formed by preparing the polymer film under the conditions of the present invention.

Claims
  • 1. A liquid crystal composition, comprising: one kind or two or more kinds of a first monomer having a first mesogenic skeleton, at least one polymerizable group represented by the general formula (PG1) linked to the first mesogenic skeleton, and at least one polar group linked to the mesogenic skeleton or the polymerizable group; andone kind or two or more kinds of a second monomer having a second mesogenic skeleton and a polymerizable group represented by the general formula (PG2) linked to the second mesogenic skeleton, and having a chemical structure different from that of the first monomer, in an amount of more than 0.4% by mass: *—S11—P11  (PG1)*—S21—P21  (PG2)whereinP11 and P21 each independently represent a group represented by any of the following formulae (R-I) to (R-IX):
  • 2. The liquid crystal composition according to claim 1, wherein the polar group is an atomic group of a polar element having a hetero atom selected from the group consisting of N, O, S, P and Si.
  • 3. The liquid crystal composition according to claim 1, comprising the first monomer having a polar group represented by the following general formula (K) and a second monomer having no polar group represented by the general formula (K): *—Sik—Kik  (K)wherein Sik represents a single bond or an alkylene group having 1 to 15 carbon atoms, and one —CH2— or two or more —CH2— that are not adjacent to each other in the alkylene group may be substituted with —O—, —OCO—, or —COO— so long as oxygen atoms are not directly adjacent to each other, andKik is represented by the following formulae (K-1) to (K-28):
  • 4. The liquid crystal composition according to claim 1, wherein a content mass ratio of the first monomer to the second monomer (first monomer/second monomer) is 0.5 to 10.
  • 5. The liquid crystal composition according to claim 1, wherein the first mesogenic skeleton is represented by the general formula (Me1):
  • 6. The liquid crystal composition according to claim 1, wherein the polar group is represented by the following formulae (K-1-1) to (K-28):
  • 7. The liquid crystal composition according to claim 1, wherein the content of the first monomer is 0.2 to 5.0% by mass.
  • 8. The liquid crystal composition according to claim 1, wherein the content of the second monomer is more than 0.4 to 3.0% by mass.
  • 9. The liquid crystal composition according to claim 1, wherein the second monomer is one kind or two or more kinds selected from the group consisting of polymerizable compounds represented by the following general formulae (RM-1) and (RM-2):
  • 10. The liquid crystal composition according to claim 1, further comprising a compound selected from the group consisting of compounds represented by the general formulae (N-1), (N-2), and (N-3):
  • 11. The liquid crystal composition according to claim 1, further comprising a compound represented by the general formula (L):
Priority Claims (1)
Number Date Country Kind
2017-127451 Jun 2017 JP national
PCT Information
Filing Document Filing Date Country Kind
PCT/JP2018/022689 6/14/2018 WO 00