1. Technical Field
The present invention relates to a liquid crystal display device, and more specifically, to a liquid crystal display device comprising an optical-modulation film in which birefringent island-in-the-sea yarns having two or more spinning cores are present in a matrix to considerably reduce production costs and remarkably increase luminance.
2. Background Art
Liquid crystal displays (LCDs), projection displays and plasma display panels (PDPs) which have already secured their markets in the TV field are main for flat panel display technology. It is also expected that field emission displays (FEDs), electro-luminescent displays (ELDs), etc. will gain market share according to their respective characteristics along with the improvement of technologies associated therewith. The application range of LCDs currently expands to notebooks, personal computer monitors, liquid crystal TVs, vehicles, aircrafts, etc. LCDs occupy about 80% of the flat panel market and global sales are strong these days along with the sharply increased demand since the second half of 1998.
Conventional LCDs have a structure in which liquid crystal and an electrode matrix are disposed between a pair of light-absorbent optical films. In LCDs, the liquid crystal is moved by an electric field generated by applying an electric voltage to two electrodes and thus has an optical state depending on the electric field. This process displays an image by polarizing pixels storing information in a specific direction. For this reason, LCDs include a front optical film and a rear optical film to induce this polarization.
LCD devices do not necessarily have a high use efficiency of light emitted from a backlight. This is because 50% or more of the light emitted from the backlight is absorbed by a rear-side optical film. Accordingly, in order to increase the use efficiency of the backlight light in LCD devices, an optical-modulation film is interposed between an optical cavity and a liquid crystal assembly.
More specifically, P-polarized light of light orienting from an optical cavity to a liquid crystal assembly is transferred through an optical-modulation film to the liquid crystal assembly and S-polarized light thereof is reflected from the optical-modulation film to the optical cavity, reflected from a diffusion reflection surface of the optical cavity in a state in which the polarization direction of the light becomes random, and then transferred to the optical-modulation film again. Consequently, the S-polarized light is converted into P-polarized light that can pass through a polarizer of the liquid crystal assembly and then transferred through the optical-modulation film to the liquid crystal assembly.
Selective reflection of the S-polarized light with respect to the incident light on the optical-modulation film and transmission of the P-polarized light are carried out by the difference in refractive index between respective optical layers, determination of an optical thickness of each optical layer according to extension of stacked optical layers and variation in the refractive index of the optical layer, in the state in which a flat sheet optical layer having an anisotropic refractive index and a flat sheet optical layer having an isotropic refractive index are alternately stacked in plural number.
That is, the light incident on the optical-modulation film undergoes the reflection of the S-polarized light and the transmission of the P-polarized light, while passing through the receptive optical layers. As a result, only the P-polarized light of the incident polarized light is transferred to the liquid crystal assembly. Meanwhile, the reflected S-polarized light is reflected from the diffusion reflection surface of the optical cavity in the state in which its polarization state becomes random as mentioned above and then transferred to the optical-modulation film again. Accordingly, loss of light generated from a light source and waste of power can be reduced.
However, this conventional optical-modulation film is fabricated by alternately stacking flat sheet-shaped isotropic optical layers and flat sheet-shaped anisotropic optical layers, which have different refractive indices, and performing an extension process on the stacked structure so that the stacked layer has an optical thickness and a refractive index of the respective optical layers, which can be optimized for selective reflection and transmission of incident polarized light. Accordingly, this fabrication process had a disadvantage of complicated fabrication of the optical-modulation film. In particular, since each optical layer of the optical-modulation film has a flat sheet shape, P-polarized light and S-polarized light have to be separated from each other in response to a wide range of an incident angle of the incident polarized light. Accordingly, this film has a structure in which an excessively increased number of optical layers are stacked, thus disadvantageously involving exponential increase in production costs. In addition, this structure disadvantageously causes optical loss and thus deterioration in optical performance.
Accordingly, in an attempt to solve the afore-mentioned problems of the stack-type optical-modulation film, incorporation of birefringent fibers into a matrix was suggested. This method has advantages of low production costs and easy production, since optical-modulation films are not fabricated in a stack-structure, when general birefringent fibers are used, but disadvantageously cannot improve luminance to a desired level and is thus unsuitable for industrial application, instead of the conventional stack-type optical-modulation film.
Therefore, the present invention has been made in view of the above problems, and it is one object of the present invention to provide a liquid crystal display device provided with an optical-modulation film designed to prevent aggregation of island portions and thus maximize optical modulation efficiency.
It is another object of the present invention to provide birefringent island-in-the-sea yarns provided in the optical-modulation film, which can prevent aggregation of island portions and are chromogenic when used for fabrics.
In accordance with the present invention, the above and other objects can be accomplished by the provision of a liquid crystal display device including: a backlight to irradiate light; an optical-modulation film arranged on the backlight, the optical-modulation film including a matrix and birefringent island-in-the-sea yarns arranged in the matrix to modulate light irradiated from the backlight; and a liquid crystal display panel to realize a predetermined image through the modulated light, wherein each birefringent island-in-the-sea yarn includes island portions, wherein the island portions are arranged based on two or more spinning cores to form partitioned groups.
The peripheral spinning cores may be 3 to 20 in number and more preferably 6 to 10 in number.
The number of island portions arranged with respect to one standard spinning core or one peripheral spinning core may be 10 to 300.
The total number of the island portions may be 50 to 1,500, more preferably, 500 to 1,500, most preferably, 1,000 to 1,500.
The longitudinal cross-sections of the grouped island portions may be circular or polygonal and in this case, the longitudinal cross-sections of the grouped island portions may be identical or different.
The spinning cores may be arranged based on the center of the island-in-the-sea yarn, and more preferably, spinning cores may not be formed in the center of the island-in-the-sea yarn.
The number of the spinning cores may be 3 to 20 and more preferably, 6 to 10.
The single yarn fineness of the island-in-the-sea yarn may be 0.5 to 30 deniers, and more preferably, the single yarn fineness of the island portions may be 0.0001 to 1.0 deniers.
A birefringent interface may be formed at the boundary between the island portion and the sea portion. More preferably, the island portion may be anisotropic and the sea portion may be isotropic.
The island portion may be selected from polyethylene naphthalate (PEN), copolyethylene naphthalate (co-PEN), polyethylene terephthalate (PET), polycarbonate (PC), polycarbonate (PC) alloys, polystyrene (PS), heat-resistant polystyrene (PS), polymethylmethacrylate (PMMA), polybutylene terephthalate (PBT), polypropylene (PP), polyethylene (PE), acrylonitrile butadiene styrene (ABS), polyurethane (PU), polyimide (PI), polyvinyl chloride (PVC), styrene acrylonitrile (SAN) mixtures, ethylene vinyl acetate (EVA), polyamide (PA), polyacetal (POM), phenol, epoxy (EP), urea (UF), melanin (MF), unsaturated polyester (UP), silicon (Si), elastomers and cycloolefin polymers and combinations thereof.
The sea portion may be selected from polyethylene naphthalate (PEN), copolyethylene naphthalate (co-PEN), polyethylene terephthalate (PET), polycarbonate (PC), polycarbonate (PC) alloys, polystyrene (PS), heat-resistant polystyrene (PS), polymethylmethacrylate (PMMA), polybutylene terephthalate (PBT), polypropylene (PP), polyethylene (PE), acrylonitrile butadiene styrene (ABS), polyurethane (PU), polyimide (PI), polyvinyl chloride (PVC), styrene acrylonitrile (SAN) mixtures, ethylene vinyl acetate (EVA), polyamide (PA), polyacetal (POM), phenol, epoxy (EP), urea (UF) melanin (MF), unsaturated polyester (UP), silicon (Si), elastomers and cycloolefin polymers and combinations thereof.
The matrix may be isotropic.
The difference in refractive index between the matrix and the island-in-the-sea yarn with respect to two axial directions may be 0.05 or less and the difference in refractive index between the matrix and the island-in-the-sea yarn with respect to the remaining one axial direction may be 0.1 or more.
Assuming that x-, y- and z-axis refractive indexes of the matrix are nX1, nY1 and nZ1, respectively, and the x-, y- and z-axis refractive indexes of the island-in-the-sea yarn are nX2, nY2 and nZ2, respectively, at least one of x-, y- and z-axis refractive indexes of the matrix may be equivalent to that of the birefringent island-in-the-sea yarn and the refractive indexes of the birefringent island-in-the-sea yarn may be nX2>nY2=nZ2.
The difference in refractive index between the sea portion and the island portion with respect to two axial directions may be 0.05 or less and the difference in refractive index between the sea portion and the island portion with respect to the remaining one axial direction may be 0.1 or more.
Assuming that x- (longitudinal), y- and z-axis refractive indexes of the island portion are nX3, nY3 and nZ3, respectively, and the x-, y- and z-axis refractive indexes of the sea portion are nX4, nY4 and nZ4, respectively, at least one of x-, y- and z-axis refractive indexes of the island portion may be equivalent to that of the sea portion, and an absolute value of the difference in refractive index between nX3 and nX4 may be 0.05 or more.
The refractive index of the sea portion in the island-in-the-sea yarn may be equivalent to the refractive index of the matrix.
The sea portion and the island portion may be present in an area ratio of 2:8 to 8:2, based on the cross-section of the birefringent island-in-the-sea yarn.
The birefringent island-in-the-sea yarns may extend in a longitudinal direction.
The backlight may be CCFL or LED.
The island portions may be arranged based on two or more spinning cores such that the island portions form partitioned groups, wherein the maximum distance between the centers of adjacent island portions present in one group is smaller than the maximum distance between the centers of adjacent island portions present in adjacent two groups.
The optical-modulation film may have a structured surface layer.
The birefringent island-in-the-sea yarns may be woven into a fabric. The fabric may be woven using the birefringent island-in-the-sea yarns as at least one of wefts, wherein the fabric is woven using the birefringent island-in-the-sea yarns as one of wefts and warps and isotropic fibers as the other thereof. The isotropic fibers may be partially or entirely melted.
The island portion may have a melting temperature higher than a melting temperature of the isotropic fibers and/or the sea portion. Preferably, the melting initiation temperature of the island portion may be at least 30° C. higher than a melting temperature of the sea portion.
The weft or warp may be composed of 1 to 200 threads of the island-in-the-sea yarns.
In accordance with another aspect, provided is a group-type birefringent island-in-the-sea yarn applicable to the optical-modulation film of the present invention.
The birefringent island-in-the-sea yarn may include a plurality of island portions and a sea portion surrounding the island portions, wherein the island portions are arranged based on two or more spinning cores, to form partitioned groups, wherein the maximum distance between the centers of adjacent island portions present in one group is smaller than the maximum distance between the centers of adjacent island portions present in two adjacent groups.
The spinning cores may include one standard spinning core arranged in the center of the birefringent island-in-the-sea yarn and a plurality of peripheral spinning cores arranged based on the standard spinning core.
The distances between the standard spinning core and the peripheral spinning cores may be substantially identical or different.
The peripheral spinning cores may be 6 to 10 in number.
The number of island portions arranged with respect to one standard spinning core or one peripheral spinning core may be 10 to 300. The total number of the island portions may be 500 to 1,500.
The number of the spinning cores may be 6 to 10 and the single yarn fineness of the birefringent island-in-the-sea yarn may be 0.5 to 30 deniers.
A birefringent interface may be formed at the boundary between the island portion and the sea portion. More preferably, the island portion may be anisotropic and the sea portion may be isotropic.
The difference in refractive index between the sea portion and the island portion with respect to two axial directions may be 0.05 or less and the difference in refractive index between the sea portion and the island portion with respect to the remaining one axial direction may be 0.1 or more.
The melting initiation temperature of the island portion may be at least 30° C. higher than a melting temperature of the sea portion.
Hereinafter, a brief description will be given of the terms used herein.
Unless specifically mentioned, the term “spinning core” means a specific standard point at which island portions in island-in-the-sea yarns are grouped (partitioned), on the cross-section taken in a longitudinal direction.
The term “standard spinning core” means a spinning core acting as a center and the term “peripheral spinning core” means a remaining spinning core arranged based on the standard spinning core, when the spinning cores are in plural and are composed of one spinning core and other spinning cores arranged based on the one spinning core.
The expression “island portions are partitioned to form groups” means a state in which the island portions of island-in-the-sea yarns are arranged based on one spinning core such that they are partitioned in a predetermined shape, and for example, when two spinning cores are present in island-in-the-sea yarns, the island portions are arranged in a predetermined shape based on respective spinning cores and the island portions are thus partitioned into two groups in the island-in-the-sea yarns. That is, the island portions are divided, depending on the difference in distance therebetween, rather than the difference in shape therebetween.
The expression “partitioned group” means a group formed by the difference in distance between island portions, rather than the difference in shape therebetween.
The expression “fibers are birefringent” means that when light is irradiated to fibers having different refractive indices according to directions, the light incident to the fibers is refracted in two different directions.
The term “isotrope” means a property in which an object has a constant refractive index irrespective of a direction at which light passes through the object.
The term “anisotrope” means a property in which optical properties of an object are varied according to directions of light and an anisotropic object is birefringent and is contrary to isotrope.
The term “optical modulation” means a phenomenon in which irradiated light is reflected, refracted, or scattered, or intensity, wave cycle or characteristics thereof are varied.
The term “melting initiation temperature” means a temperature at which a polymer begins to melt, and the term “melting temperature” means a temperature at which melting occurs most rapidly. Accordingly, when a melting temperature of a polymer is observed by DSC, the temperature at which a melting endothermic peak initially appears is referred to as a “melting initiation temperature” and the temperature plotted at a maximum of the endothermic peak is referred to as a “melting temperature”.
The term “photochromic fiber” means a fiber which does not render color through physical and chemical bonds of color-rendering substances such as dyes or pigments, but renders color using interference of light through structural and optical designs of fibers.
The above and other objects, features and other advantages of the present invention will be more clearly understood from the following detailed description taken in conjunction with the accompanying drawings, in which:
The present invention provides an optical-modulation film which comprises birefringent island-in-the-sea yarns whose island portions are partitioned into groups based on two or more spinning cores and causing formation of optical modulation interfaces between island portions and sea portions, and thus maximizing optical modulation efficiency, as compared to conventional birefringent fibers. The birefringent island-in-the-sea yarns of the present invention (group-type island-in-the-sea yarns) are free of aggregation of island portions in the center thereof, although the number of island portions is 500 or more. As a result, the birefringent island-in-the-sea yarns maximize an optical modulation interface area and thus considerably improve optical modulation efficiency, as compared to conventional island-in-the-sea yarns comprising one spinning core. Accordingly, the birefringent island-in-the-sea yarns advantageously exhibited considerably improved luminance, as compared to conventional birefringent island-in-the-sea yarns wherein only conventional birefringent fibers or one spinning core are present in a matrix.
Furthermore, in addition to application to optical-modulation films, the birefringent island-in-the-sea yarns are considerably advantageous for the preparation of microfibers, since 500 or more island portions can be disposed in one island-in-the-sea yarn and yarn fineness of island portions can thus be reduced. The island-in-the-sea yarns have an advantage of considerably reduced production costs, since 500 or more microfibers can be produced from one island-in-the-sea yarn. In addition, due to excellent optical-modulation effects, the group-type island-in-the-sea yarns render a specific color according to the ratio of sea portions to island portions and diameter of fibers, without adding chromogenic compounds such as dyes and are thus applicable to photochromic fibers.
Hereinafter, the present invention will be illustrated in more detail.
Conventional optical-modulation films have a structure in which an excessively increased number of optical layers are stacked, thus disadvantageously involving exponential increase in production costs and thus deterioration in optical performance. When birefringent fibers are arranged in the matrix, light emitted from a light source is reflected, scattered and refracted on the birefringent interface between the birefringent fibers and the isotropic matrix, thereby inducing optical modulation and improving luminance. The case, when general birefringent fibers are used, has an advantage of low production costs and easy production, since optical-modulation films are not fabricated in a stack-structure, but disadvantageously cannot improve luminance to a desired level and is unsuitable for application to industrial fields, instead of the stack-type conventional optical-modulation film.
Accordingly, the afore-mentioned problem can be solved by introducing an optical-modulation film comprising birefringent island-in-the-sea yarns as birefringent fibers having birefringent interfaces into an LCD device. More specifically, the case where birefringent island-in-the-sea yarns are used is found to exhibit considerably improved optical modulation efficiency and luminance, as compared to the case where conventional birefringent fibers are used. Of the constituent components of island-in-the-sea yarns, the island portions are anisotropic and sea portions partitioning the island portions are isotropic. This case, where the interfaces between a plurality of island portions and a plurality of sea portions constituting the island-in-the-sea yarns as well as the interfaces between the island-in-the-sea yarns and the matrix are birefringent, exhibits considerably improved optical modulation efficiency and is thus industrially applicable as an alternative to stack-type optical-modulation films, as compared to conventional birefringent fibers wherein only the interfaces between the matrix and birefringent fibers are birefringent. Accordingly, as compared to the case where common birefringent fibers are used, the case where birefringent island-in-the-sea yarns are used exhibits superior optical modulation efficiency and birefringent island-in-the-sea yarns which comprise island portions and sea portions exhibiting different optical properties, thus enabling formation of birefringent interfaces therein, can more considerably improve optical modulation efficiency.
Meanwhile, in order to maximize optical modulation efficiency, it is preferred that an area of birefringent interface present in the birefringent island-in-the-sea yarns be wider. For this purpose, the number of island portions present in the birefringent island-in-the-sea yarns should be large. However, conventional island-in-the-sea yarns comprise island portions concentrically arranged based on one spinning core. This cross-sectional structure is normal, when island portions are small in number, while island portions adjacent to spinning cores formed in the center of island-in-the-sea yarns are highly dense and may be aggregated together (island-conjugation) during spinning, when island portions are large in number (about 300 or higher). More specifically,
Accordingly, birefringent island-in-the-sea yarns having general cross-sections of island-in-the-sea yarns have a decreased birefringent interface due to the island conjugation phenomenon, as the number of island portions decreases and cannot disadvantageously improve optical modulation efficiency to a desired level.
In an attempt to solve the afore-mentioned problem, the present invention provides a liquid crystal display device comprising a backlight to irradiate light, an optical-modulation film arranged on the backlight, wherein the optical-modulation film includes a matrix and birefringent island-in-the-sea yarns arranged in the matrix to modulate light irradiated from the backlight, and a liquid crystal display panel to realize a predetermined image through the modulated light, wherein each birefringent island-in-the-sea yarn includes island portions which are arranged based on two or more spinning cores to form partitioned groups. Based on such a structure, the phenomenon in which island portions are excessively concentrated on one spinning core can be prevented, thus preventing island-conjugation. As a result, optical modulation efficiency and luminance are considerably improved.
Hereinafter, the present invention will be illustrated in more detail with reference to the annexed drawings.
First, the LCD device comprises a backlight. Any backlight may be used without particular limitation so long as it is applicable to conventional LCD devices. Preferably, the backlight may be CCFL or LCD.
Next, an optical-modulation film which is arranged on the backlight and includes a matrix and birefringent island-in-the-sea yarns arranged in the matrix, to modulate light irradiated from the backlight will be described in detail. Specifically, the optical-modulation film has a structure in which birefringent island-in-the-sea yarns are randomly arranged within an isotropic matrix. Materials for the matrix that can be used in the present invention include thermoplastic and thermosetting polymers which can transmit a desired range of optical wavelengths and may be a transparent material enabling easy transmission of light. Preferably, the matrix may be amorphous or semicrystalline and may include a monopolymer, a copolymer or a blend thereof. More specifically, examples of suitable matrixes include poly(carbonate) (PC); syndiotactic and isotacticpoly(styrene) (PS); alkyl styrene; alkyl such as poly(methylmethacrylate) (PMMA) and PMMA copolymers, aromatic and aliphatic pendant (meth)acrylate; ethoxide and propoxide (meth)acrylate; multi-functional (meth)acrylate; acrylated epoxy; epoxy; and other ethylene unsaturated compounds; cyclic olefin and cyclic olefin copolymers; acrylonitrile butadiene styrene (ABS); styrene acrylonitrile (SAN) copolymers; epoxy; poly(vinyl cyclohexane); PMMA/poly(vinyl fluoride) blends; poly(phenylene oxide) alloys; styrene block copolymers; polyimide; polysulfone; poly(vinyl chloride); poly(dimethylsiloxane) (PDMS); polyurethane; unsaturated polyester; polyethylene; poly(propylene) (PP); poly(alkane terephthalate) such as poly(ethylene terephthalate) (PET); poly(alkane naphthalate) such as poly(etylene naphthalate) (PEN); polyamide; ionomers; vinyl acetate/polyethylene copolymers; cellulose acetate; cellulose acetate butyrate; fluoro polymers; poly(styrene)-poly(ethylene) copolymers; PET and PEN copolymers such as polyolefin PET and PEN; and poly(carbonate)/aliphatic PET blends. More preferably, examples of suitable matrixes include polyethylene naphthalate (PEN), copolyethylene naphthalate (co-PEN), polyethylene terephthalate (PET), polycarbonate (PC), polycarbonate (PC) alloys (PC+PCTG), polystyrene (PS), heat-resistant polystyrene (PS), polymethylmethacrylate (PMMA), polybutylene terephthalate (PBT), polypropylene (PP), polyethylene (PE), acrylonitrile butadiene styrene (ABS), polyurethane (PU), polyimide (PI), polyvinyl chloride (PVC), styrene acrylonitrile (SAN) mixtures, ethylene vinyl acetate (EVA), polyamide (PA), polyacetal (POM), phenol, epoxy (EP), urea (UF), melanin (MF), non-saturated polyester (UP), silicon (Si), elastomers, cycloolefin polymers (COP, ZEON Co., Ltd. (Japan), JSR Co., Ltd. (Japan)) and combinations thereof. More preferably, the matrix may be composed of the same material as the sea portion of birefringent island-in-the-sea yarns 31. Furthermore, the matrix may also contain an additive, such as an antioxidant, a light stabilizer, a heat stabilizer, a lubricant, a dispersing agent, a UV absorber, white pigment, and a fluorescent whitening agent, so long as the additive does not damage physical properties as mentioned above.
Meanwhile, constituent components and optical properties of the matrix may be identical to those of the sea portions and/or the fibers, taking into consideration various physical properties. In this case, in the lamination process, the matrix may be partially or entirely melted, thus enabling improvement in adhesion between the birefringent island-in-the-sea yarns and the matrix without using additional adhesive. In addition, the matrix may include three layers. More specifically, the three layers may form a stack structure including a skin layer (B layer)/core layer (A layer)/skin layer (C layer). The thickness ratio between the skin layer and the core layer may be about 1:2 but is not limited thereto. The skin layer which corresponds to a fabric and is arranged outside a matrix may have the same melting temperature as the sea portions and/or the fibers, in order to improve the matrix and the birefringent island-in-the-sea yarns. The core layer may be made of a material which has a higher melting temperature than the sea portions and/or fibers, in order to prevent deformation of the matrix due to heat generated by a lamp.
Next, the birefringent island-in-the-sea yarns 31 present in the matrix 30 will be illustrated. As mentioned above, conventional island-in-the-sea yarns has a cross-section in which island portions are concentrically arranged on the basis of one spinning core. This cross-sectional structure is normal, when island portions are small in number, while island portions adjacent to spinning cores formed on the center of island-in-the-sea yarns are highly dense and may be aggregated during spinning, when island portions are large in number (about 300 or higher). That is, as the number of island portions of island-in-the-sea yarns increases, the island portions present at the center thereof are aggregated, thus decreasing the birefringent surface and limiting improvement in optical modulation, when used for optical-modulation films.
Accordingly, in the birefringent island-in-the-sea yarns according to one embodiment of the present invention which comprise a plurality of island portions and sea portions arranged based on the island portions, the problem can be solved by arranging the island portions such that they are partitioned into groups, based on two or more spinning cores. As a result, the phenomenon in which island portions are excessively concentrated on one spinning core can be prevented.
Meanwhile, the total number of island portions present in the birefringent island-in-the-sea yarn according to the present invention may be 38 to 1,500, more preferably, 500 to 1,500 and most preferably, 1,000 to 1,500, when the number of spinning cores is suitably controlled. Furthermore, the number of the island portions arranged in each spinning core may be 10 to 300, more preferably, 100 to 150 and is not limited thereto. Consequently, the number of island portions arranged adjacent to each spinning core may be suitably controlled under the conditions that the island portions are not aggregated and fineness of island-in-the-sea yarns and island portions, fineness of desired microfibers and optical modulation efficiency, as mentioned below, are maximized.
In accordance with a preferred first embodiment of the present invention, the spinning cores may include a standard spinning core arranged in the center of the island-in-the-sea yarns and a plurality of peripheral spinning cores arranged based on the standard spinning core. More specifically,
Meanwhile, the number of peripheral spinning cores may be preferably 3 to 20, more specifically, 6 to 10. As shown in
In accordance with a preferred second embodiment of the present invention, the island-in-the-sea yarns comprise one or more spinning cores arranged in the center thereof, and more preferably, the island-in-the-sea yarns may comprise no spinning core in the center thereof. Hereinafter, only distinguishing characteristics of the second embodiment are described, except description associated with the matrix. More specifically,
Meanwhile, as shown in
Meanwhile, group-type island-in-the-sea yarns used in the present invention will be sufficient, when they have a fineness comparable to single yarn fineness of common island-in-the-sea yarns and preferably have a single yarn fineness of 0.5 to 30 deniers. Of the island-in-the-sea yarns, island portions preferably have a single yarn fineness of 0.0001 to 1.0 deniers, in view of efficient accomplishment of objects of the present invention.
In the birefringent island-in-the-sea yarns according to another embodiment of the present invention, the island portions and sea portions may have different optical properties in order to maximize optical modulation efficiency, and more preferably, the island portions may be anisotropic and the sea portions may be isotropic.
More specifically, in island-in-the-sea yarns comprising optically isotropic sea portions and anisotropic island portions, the levels of substantial equality and in-equality between refractive indexes along spatial axes X, Y and Z affect scattering of polarized light. Generally, scattering performance varies in proportion to the square of the difference in refractive index. Accordingly, as the difference in refractive index according to a specific axis increases, light polarized according to the axis is more strongly scattered. On the other hand, when the difference in refractive index according to a specific axis is low, a ray of light polarized according to the axis is weakly scattered. When the refractive index of sea portions at a specific axis is substantially equivalent to the refractive index of island portions, incident light that is polarized by an electric field parallel to this axis is not scattered, irrespective of the size, shape and density of a portion of the island-in-the-sea yarns, but may pass through the island-in-the-sea yarns. More specifically,
The afore-mentioned optical modulation phenomenon often occurs on the interface between the matrix and the birefringent island-in-the-sea yarns and/or the interface between island portions and sea portions in the birefringent island-in-the-sea yarns. More specifically, optical modulation occurs on the interface between the matrix and the birefringent island-in-the-sea yarn, like common birefringent fibers, when the matrix is optically isotropic. Specifically, the difference in refractive index between the matrix and the island-in-the-sea yarn with respect to two axial directions may be 0.05 or less and the difference in refractive index between the matrix and the island-in-the-sea yarn with respect to the remaining axial direction may be 0.1 or more. Assuming that x-, y- and z-axis refractive indexes of the matrix are nX1, nY1 and nZ1, respectively, and the x-, y- and z-axis refractive indexes of the island-in-the-sea yarn are nX2, nY2 and nZ2, respectively, at least one of x-, y- and z-axis refractive indexes of the matrix may be equivalent to that of the birefringent island-in-the-sea yarn and the refractive index order of island-in-the-sea yarns may be nX2>nY2=nZ2.
Meanwhile, of the birefringent island-in-the-sea yarns, the island portions and the sea portions preferably have different optical properties in view of formation of the birefringent surface. More specifically, when the island portions are anisotropic and the sea portions are isotropic, birefringent surfaces may be formed on the interface therebetween, and more specifically, it is preferred that the difference in refractive index in two axes is 0.05 or less and the difference in refractive index in the remaining axis is 0.1 or more. In this case, P waves pass through birefringent interfaces of island-in-the-sea yarns, while S waves cause optical modulation. More specifically, assuming that x- (longitudinal), y- and z-axis refractive indexes of the island portion are nX3, nY3 and nZ3, respectively, and the x-, y- and z-axis refractive indexes of the sea portion are nX4, nY4 and nZ4, respectively, it is preferred that at least one of x-, y- and z-axis refractive indexes of the island portion be equivalent to that of the sea portion and an absolute value of the difference in refractive index between nX3 and nX4 be 0.05 or more. Most preferably, when the difference in refractive index between sea portions and island portions in island-in-the-sea yarns in a longitudinal direction is 0.1 or more and, with respect to the remaining two axial directions, the refractive index of the sea portion is substantially equivalent to that of the island portion, optical modulation efficiency can be maximized. Meanwhile, the case wherein the matrix and sea portions in the birefringent island-in-the-sea yarns have identical refractive indexes is advantageous for improving optical modulation efficiency.
Consequently, as mentioned above, to maximize optical modulation efficiency of the island-in-the-sea yarns, the island portions and sea portions should have different optical properties and have a wide area of optically-modulated surfaces. For this purpose, the number of island portions should be increased, and preferably, the number of island portions should be greater than 500. However, in conventional island-in-the-sea yarns, when island portions are 500 or more in number, although island portions have an anisotropic refractive index and sea portions have an isotropic refractive index, they may be aggregated, thus disadvantageously causing a decrease in optically modulated interface area and deterioration in optical modulation efficiency. As described in the preceding embodiment of the present invention, in the case where two or more spinning cores are formed and 500 or more (preferably, 1,000 or more) island portions are arranged, aggregation of island portions can be prevented. As a result, optical modulation efficiency of island-in-the-sea yarns is maximized and optical modulation effects and great improvement in luminance can be expected, when birefringent island-in-the-sea yarns according to embodiments of the present invention are incorporated into the optical-modulation film.
Examples of sea portions and/or island portions that can be used in the present invention include polyethylene naphthalate (PEN), copolyethylene naphthalate (co-PEN), polyethylene terephthalate (PET), polycarbonate (PC), polycarbonate (PC) alloys, polystyrene (PS), heat-resistant polystyrene (PS), polymethylmethacrylate (PMMA), polybutylene terephthalate (PBT), polypropylene (PP), polyethylene (PE), acrylonitrile butadiene styrene (ABS), polyurethane (PU), polyimide (PI), poly vinyl chloride (PVC), styrene acrylonitrile (SAN) mixtures, ethylene vinyl acetate (EVA), polyamide (PA), polyacetal (POM), phenol, epoxy (EP), urea (UF), melanin (MF), non-saturated polyester (UP), silicon (Si), elastomers and cycloolefin polymers and combinations thereof. In view of efficient improvement in optical modulation, it is preferable to adopt materials for the island portions and the sea portions which have substantially identical refractive indexes in two axes, but have great difference in refractive index in one axis. However, it is more preferable that when polyethylene naphthalate (PEN) is used as a material for island portions in the birefringent island-in-the-sea yarns 31 and a copolyethylene naphthalate and polycarbonate alloy alone or a combination thereof is used as a material for sea portions, luminance is greatly improved, as compared to birefringent island-in-the-sea yarns made of common materials. In particular, when the polycarbonate alloy is used as the sea portions, birefringent island-in-the-sea yarns with the most excellent optical modulation property can be prepared. In this case, the polycarbonate alloy may be preferably made of polycarbonate and modified polycyclohexylenedimethylene terephthalate glycol (PCTG) and more preferably, use of the polycarbonate alloy consisting of the polycarbonate and modified polycyclohexylenedimethylene terephthalate glycol (PCTG) which are present in a weight ratio of 15:85 to 85:15 is effective for improvement in luminance. When polycarbonate is present in an amount less than 15%, polymer viscosity required for spinning performance is excessively increased and use of a spinning machine is disadvantageously impossible, and when the polycarbonate is present in an amount exceeding 85%, a glass transition temperature increases and spinning tension increases, after discharge from a nozzle, thus making it difficult to secure spinning performance.
Most preferably, use of the polycarbonate alloy consisting of the polycarbonate and modified polycyclohexylenedimethylene terephthalate glycol (PCTG) which are present in a weight ratio of 4:6 to 6:4 is effective for improvement in luminance. Furthermore, in view of efficient improvement in optical modulation efficiency, it is preferable to adopt materials for the island portions and the sea portions which have substantially identical refractive indexes in two axes, but have great difference in refractive index in one axis.
Meanwhile, methods for modifying isotropic materials into birefringent materials are well-known in the art and for example, polymeric molecules are oriented and materials thus become birefringent when they are drawn under suitable temperature conditions.
In view of efficient improvement in optical modulation efficiency, it is preferable to adopt materials for the island portions and the sea portions which have substantially identical refractive indexes in two axes, but have great difference in refractive index in one axis.
Meanwhile, the birefringent island-in-the-sea yarns are arranged in the form of yarns or a fabric in the matrix. First, in the case where birefringent island-in-the-sea yarns are arranged in the form of yarns in the matrix, a plurality of birefringent island-in-the-sea yarns may preferably extend in one direction, and more preferably, the island-in-the-sea yarns may be arranged in the matrix vertically to a light source. In this case, optical modulation efficiency is maximized. Meanwhile, the island-in-the-sea yarns arranged in a row may be dispersed from one another, if appropriate, and the birefringent island-in-the-sea yarns may come in contact with one another or may be separated from one another. In the case where the island-in-the-sea yarns contact one another, they are close together to form a layer. For example, when three or more types of island-in-the-sea yarns, whose cross-sections have different diameters and are circular, are arranged, a triangle, which is obtained by interconnecting the centers of three circles adjacent to one another in the cross-sections perpendicular to their long axial directions, becomes a scalene. In addition, in the cross-sections taken perpendicular to the long axial directions of the island-in-the-sea yarns (cylindrical bodies), the cylindrical bodies are arranged such that the circle in a first layer contacts the circle in a second layer, the circle in the second layer contacts the circle in a third layer and the following layer contacts the next layer adjacent thereto. However, the condition that respective island-in-the-sea yarns contact two or more other island-in-the-sea yarns, which contact one another on the sides of their cylinders, on the side of the cylinder has only to be satisfied. Under this condition, a structure, in which the circle in the first layer contacts the circle in the second layer, the circle in the second layer and the circle in the third layer are spaced apart from each other through a support medium interposed therebetween, and the circle in the third layer contacts the circle in a fourth layer, may be designed.
It is preferred that the lengths of at least two sides of a triangle, which connects the centers of three circles directly contacting each other in the cross-sections perpendicular to the long axial direction of the island-in-the-sea yarn, be approximately identical. In particular, it is preferred that the lengths of three sides of the triangle be approximately identical. Further, in relation to a stack state of island-in-the-sea yarns in a thickness direction of the optical-modulation film, it is preferred that a plurality of layers be stacked such that two adjacent layers sequentially contact each other. Furthermore, it is more preferred that island-in-the-sea yarns in the form of cylinders having a substantially identical diameter be densely filled.
Accordingly, in such a more-preferred embodiment, the island-in-the-sea yarns have a cylindrical shape in which the diameters of circular cross-sections perpendicular to their long axial direction are substantially identical, and island-in-the-sea yarns located more inwardly than the outermost surface layer in the cross-section contact six other cylindrical island-in-the-sea yarns on the side of the cylinder.
Meanwhile, the birefringent island-in-the-sea yarns may be arranged in the form of a fabric in the matrix, as shown in
Meanwhile, it is preferable that the birefringent island-in-the-sea yarns have a volume of 1% to 90% with respect to the optical-modulation film of 1 cm3. When the volume of the island-in-the-sea yarn is 1% or less, a luminance-reinforcement effect is slight. When the volume of the island-in-the-sea yarn exceeds 90%, the amount of scattering increases due to the birefringent interface, disadvantageously causing optical loss.
Furthermore, the number of the birefringent island-in-the-sea yarns arranged in the optical-modulation film of 1 cm3 may 500 to 4,000,000. The island portions in the birefringent island-in-the-sea yarns may greatly affect optical modulation. When the cross-sectional diameters of the island portions in each birefringent island-in-the-sea yarn are smaller than optical wavelengths, refraction, scattering and reflection effects are decreased and optical modulation hardly occur. When the cross-sectional diameters of island portions are excessively large, light is normally reflected from the surface of island-in-the-sea yarns and diffusion in other directions is considerably slight. The cross-sectional diameters of island portions may be varied depending on an intended application of optical bodies. For example, the diameter of fibers may be varied depending on electromagnetic radiation wavelengths important for specific applications and different diameters of fibers are required to reflect, scatter or transmit visible, ultraviolet and infrared rays and microwaves.
Meanwhile, in a preferred embodiment of the present invention, the optical-modulation film of the present invention may have a structured surface layer, and more specifically, the structured surface layer may be formed on the side from which light is emitted. The structured surface layer may be in the form of a prism, lenticular or convex lens. More specifically, the side on the optical-modulation film from which light is emitted may have a curved surface in the form of a convex lens. The curved surface may focus or defocus light permeated into the curved surface. Also, the light-emitting surface may have a prism pattern.
Next, a method for preparing birefringent island-in-the-sea yarns according to the present invention will be described. The birefringent island-in-the-sea yarns may be applied to any general method for preparing island-in-the-sea yarns without particular limitation. Any spinneret or spinning nozzle may be used without restriction of shape so long as it enables preparation of birefringent island-in-the-sea yarns. Spinnerets or spinning nozzles having the substantially identical shape to the arrangement pattern of island portions on the cross-sections of birefringent island-in-the-sea yarns may be generally used. More specifically, any spinneret may be used so long as it can form island-in-the-sea yarns by combining island ingredients extruded from hollow pins or spinning nozzles suitably designed to partition island portions therein with a sea ingredient stream supplied from channels designed to fill the spaces provided therebetween, and extruding the combined stream from a discharge hole, while gradually thinning the stream, and island-in-the-sea yarns have two or more spinning centers. An example of spinnerets suitable for use is shown in
More specifically,
Consequently, the birefringent island-in-the-sea yarns of the present invention, unlike common island-in-the-sea yarns, are free of aggregation of island portions, thus enabling arrangement of 1,000 or more of the island portions and formation of a great number of refractive surfaces, thereby being effective for improvement in optical modulation efficiency and enhancement in luminance.
Furthermore, in the case where a composite fiber is prepared by twisting several to several tens of island-in-the-sea yarns, for example, a composite fiber is prepared by twisting 10 island-in-the-sea yarns, the composite fiber has 100 birefringent interfaces and thus causes at least 100 times of optical modulation. Furthermore, in the case where island-in-the-sea yarns composed of several threads are prepared, for example, island-in-the-sea yarns composed of 10 threads, the composite fiber prepared from the yarns has 100 birefringent interfaces and thus causes at least 100 times of optical modulation. The island-in-the-sea yarns of the present invention may be prepared by a method such as co-extrusion, although not limited thereto.
Accordingly, while conventional island-in-the-sea yarns utilize only island portions left behind after melting sea portions, as microfibers, irrespective of birefringency, the present invention utilizes island-in-the-sea yarns comprising sea portions and island portions having different optical properties, instead of melting the sea portions of island-in-the-sea yarns. In order to accomplish objects of the present invention, the present invention adopts the case where island portions are anisotropic and sea portions are isotropic and vice versa.
Meanwhile, an LCD device, comprising the optical-modulation film will be described with reference to
The principle of the LCD device will be illustrated according to the passage of light. Light is irradiated from a backlight 230 and then transferred to the diffusion plate 241 of the optical film 240. Then, the light passes through the light-diffusing film 242 so that it can be directed vertical to the optical film 240. Then, the light passes through the prism film 243, arrives on the optical-modulation film 244 and at this time, undergoes optical modulation. Specifically, P-waves pass through the optical-modulation film 244 without optical loss. On the other hand, S waves undergo optical modulation (e.g., reflection, scattering, refraction), are reflected on the reflection plate 220 arranged on the rear surface of the cold cathode fluorescent lamp 230, are randomly converted into P— or S waves, and pass through the optical-modulation film 244 again. Then, the waves pass through the polarized light-absorbing film 245 and arrive on the liquid crystal display panel 260. As a result, it is expected that the LCD device into which the optical-modulation film of the present invention is introduced based on the afore-mentioned principle can considerably enhance luminance, as compared to the case of conventional optical-modulation films. In addition, LEDs may be used as light sources, instead of the cold cathode fluorescent lamps 230.
When the group-type birefringent island-in-the-sea yarns are incorporated into an optical-modulation film provided in an LCD device, the phenomenon in which island portions are excessively concentrated on one spinning core can be prevented. In the case where the island-in-the-sea yarns are used in the form of fibers (photochromic fibers), 500 or more island portions can be disposed in one island-in-the-sea yarn and fineness of island portions can thus be reduced. Accordingly, the island-in-the-sea yarns are considerably advantageous for the preparation of microfibers. The island-in-the-sea yarns have an advantage of considerably reduced production costs, since 500 or more microfibers can be produced from one island-in-the-sea yarn. In addition, due to excellent optical-modulation effects, the group-type island-in-the-sea yarns render a specific color according to the ratio of sea portions to island portions and diameter of fibers, without adding chromogenic compounds such as dyes and are thus applicable to photochromic fibers.
Hereinafter, the following Examples and Experimental Examples will be provided for a further understanding of the invention. These examples are for illustrative purposes only and are not intended to limit the scope of the present invention.
An isotropic PC alloy (nx=1.57, ny=1.57, nz=1.57) consisting of polycarbonate (PC) and modified polycyclohexylenedimethylene terephthalate glycol (PCTG) in a ratio of 5:5 was used as a sea ingredient and anisotropic PEN (nx=1.88, ny=1.57, nz=1.57) was used as an island ingredient. In order to obtain island-in-the-sea yarns having the cross-section shown in
An optical-modulation film was fabricated in the same manner as in Example 1 except that birefringent island-in-the-sea yarns, whose cross-section corresponds to that of
An optical-modulation film was fabricated in the same manner as in Example 1 except that birefringent island-in-the-sea yarns, whose cross-section corresponds to that of
An optical-modulation film with a thickness of 400 μm was fabricated in the same manner as in Example 1 except that birefringent island-in-the-sea yarns whose island portions are isotropic PET (nx=ny=nz=1.57) and whose sea portions are isotropic Co-PEN (nx=ny=nz=1.57), and have a cross-section corresponding to that of
A PEN resin of IV 0.53 was polymerized to prepare undrawn yarns 150/24, instead of the birefringent island-in-the-sea yarns used in Example 1. At this time, the yarns were spun at a spinning temperature of 305° C. and a spinning rate of 1,500 M/min. The obtained yarns were drawn three-fold at a temperature of 150° C. to prepare 50/24 drawn yarns. The PEN fibers showed birefrigence and had refractive indices of nx=1.88, ny=1.57 and nz=1.57 in respective directions. An optical-modulation film with a thickness of 400 μm was fabricated in the same manner as Example 1 except that the birefrigence PEN fibers were used, instead of the island-in-the-sea yarns of Example 1.
An optical-modulation film was fabricated in the same manner as in Example 1 except that island-in-the-sea yarns including one spinning core and 200 island portions arranged based on the spinning core, as shown in
An optical-modulation film was fabricated in the same manner as in Example 1 except that island-in-the-sea yarns including one spinning core and 500 island portions arranged based on the spinning core, as shown in
The following physical properties of the optical-modulation films fabricated in Example 1 to 3 and Comparative Example 1 to 4 were evaluated and the results thus obtained are shown in Table 1 below.
The following tests were performed, in order to measure the luminance of the optical-modulation films thus fabricated. A panel was assembled on a 32″ direct lighting type backlight unit provided with a diffusion plate, two diffusion sheets, and the optical-modulation film, and luminance at 9 points was measured using a BM-7 tester (TOPCON, Corp. Korea), and an average luminance value was obtained and shown.
Transmittance was measured in accordance with ASTM D1003 using a COH300A analyzer (NIPPON DENSHOKU Co., Ltd. Japan).
The degree of polarization was measured using an RETS-100 analyzer (OTSKA Co., Ltd., Japan).
The optical-modulation film was immersed in water at 23° C. for 24 hours in accordance with ASTM D570 and variation in sample wt % before and after treatment was measured.
The optical-modulation film was assembled in a 32-inch backlight unit, stood in a thermo-hygrostat at RH 75%, 60° C. for 96 hours and then disassembled. A sprout level of the optical-modulation film was observed with the naked eye and the results thus obtained were marked by ∘, Δ or ×.
The optical-modulation film was irradiated using a 130-mW ultraviolet lamp (365 nm) at a height of 10 cm using SMDT51H (SEI MYUNG VACTRON CO., LTD. Korea) for 10 minutes. Yellow index (YI) before and after treatment was measured using an SD-5000 analyzer (NIPPON DENSHOKU Co., Japan) and a yellowing level was thus evaluated.
As can be seen from Table 1, the optical-modulation films comprising the birefringent island-in-the-sea yarns (Examples 1 to 3) according to the present invention exhibited superior overall optical properties, as compared to the optical-modulation films not using the birefringent island-in-the-sea yarns (Comparative Examples 1 to 4). In particular, the case where island-in-the-sea yarns having the same cross-section as that of
Meanwhile, as can be seen from Comparative Example 1, the case where island portions and sea portions exhibited identical optical properties, although the cross-section of birefringent island-in-the-sea yarns of the present invention was adopted, enhancement in luminance was hardly obtained. In the case where the cross-section of conventional island-in-the-sea yarns including one spinning core was adopted, although island portions and sea portions have different optical properties, also exhibited low optical properties. From these results, it can be confirmed that the case where island portions and sea portions have different optical properties and the cross-section of birefringent island-in-the-sea yarns according to the present invention is adopted exhibited considerably excellent optical properties.
The optical-modulation film of the present invention exhibits superior optical modulation performance and may thus be widely utilized in optical devices such as cameras, cellular phones and high luminance-requiring LCD devices such as LCD and LED TVs.
Although the preferred embodiments of the present invention have been disclosed for illustrative purposes, those skilled in the art will appreciate that various modifications, additions and substitutions are possible, without departing from the scope and spirit of the invention as disclosed in the accompanying claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2009-0131267 | Dec 2009 | KR | national |
| 10-2009-0131268 | Dec 2009 | KR | national |