The present application is related generally to x-ray windows.
A hermetic seal in an x-ray window can have demanding requirements. For example, light penetration through the hermetic seal into an interior of an x-ray detection device can result in interference with a signal from a sample. Thus, it can be helpful for the hermetic seal to be opaque. X-ray fluorescence from the hermetic seal can interfere with the signal from the sample, particularly x-ray fluorescence from high atomic number elements in the hermetic seal. Therefore, it can be helpful for the hermetic seal to be made of low atomic number elements.
Many x-ray devices have an internal vacuum and a getter for maintaining this vacuum. Such getters are typically activated more quickly at higher temperatures. Therefore, it can be helpful for the hermetic seal to be able to withstand high temperature. Outgassing of components of such x-ray devices can result in an undesirable rise of internal pressure. Thus, low outgassing of the hermetic seal can also be a useful characteristic. Even small leakage through components of the x-ray device can gradually cause an undesirable rise of internal pressure and malfunctioning of the device. Therefore, it can also be useful for the hermetic seal to have a low leak rate.
An x-ray window thin film can develop internal stress during manufacture or use due to coefficient of thermal expansion mismatch between the x-ray window thin film and a housing to which it is bonded. It can be helpful for the hermetic seal to relieve such stress.
Many different materials are used for the x-ray window thin film and the x-ray device housing. It can be useful for the hermetic seal to be capable of bonding to a large variety of materials.
It has been recognized that it would be advantageous to provide a hermetic seal for an x-ray window which is opaque, which is made of low atomic number elements, which can withstand high temperature, with low outgassing, with low leakage, which is able to relieve stress in the x-ray window thin film, and which can bond to many different materials. The present invention is directed to various embodiments of x-ray windows, and methods of making x-ray windows, that satisfy these needs. Each embodiment may satisfy one, some, or all of these needs.
The x-ray window can comprise a thin film configured for transmission of x-rays, a housing, and an adhesive layer sandwiched between and providing a hermetic seal between the thin film and the housing. The adhesive layer can include liquid crystal polymer.
As used herein, the term “adjoin” means direct and immediate contact.
As used herein, the term “annular” means ring-shaped, but is not limited to a circular shape. The annular shape can have other curved shapes, such as for example elliptical.
As used herein, “cps” means centipoise.
As used herein, “KPa” means kilopascals, “MPa” means megapascals, and “GPa” means gigapascals.
As used herein, in the unit “mbar*L/sec”, “mbar” means millibars, each millibar equal to 100 pascals, “L” means liters, and “sec” means second.
As used herein, “nm” means nanometer(s) and “pm” means micrometer(s).
As illustrated in
The adhesive layer 14 can be or can include epoxy, liquid crystal polymer, or other type of adhesive. For example, ≥50%, ≥75%, ≥90%, ≥95%, ≥99%, or 100% of the adhesive layer 14 can be liquid crystal polymer. The adhesive layer 14 can have certain characteristics for improved performance as will be described in the following few paragraphs.
As illustrated in
If the adhesive layer 14 is not viscous enough, it can wick into channels of the ribbed support structure 24. The adhesive layer 14 in such channels can damage the ribbed support structure 24. The adhesive layer 14 in such channels can block or fluoresce x-rays, which can interfere with an x-ray signal from a sample. Therefore, it can be helpful for the adhesive layer 14 to have high viscosity. Example viscosity values of the adhesive layer 14 include ≥10,000 cps, ≥50,000 cps, ≥80,000 cps, ≥100,000 cps, ≥200,000 cps, or ≥250,000 cps and ≤400,000 cps, ≤600,000 cps, or ≤1,000,000 cps, each at 300° C. All viscosity values herein are static viscosity.
For improved bonding of the thin film 13 to the housing 11, the adhesive layer 14 can have shear thinning properties, with non-Newtonian behavior and a reduction of viscosity when under shear stress.
As illustrated in
These x-ray devices typically have a vacuum in the interior 111 of the housing 11. A getter is commonly used to achieve and maintain this vacuum. Because the getter is more quickly activated at higher temperatures, manufacturing time can be reduced if the thin film 13 is sealed to the housing 11 at a high temperature. Therefore, it can be useful for the adhesive layer 14 to be able to withstand high temperature without degradation. It can be useful for the adhesive layer 14 to have a high melting temperature, or if the adhesive layer 14 is a liquid crystal polymer, to have a high transition temperature TLC (temperature of transition between solid and liquid crystal states). Example transition temperature TLC values of the liquid crystal polymer include ≥200° C., ≥260° C., ≥270° C., ≥300° C., ≥350° C., or ≥400° C. and ≤500° C., ≤600° C., or ≤800° C.
Visible or infrared light can interfere with operation of the x-ray component 12, such as an x-ray detector. Therefore, it can be helpful for the adhesive layer 14 to be opaque. For example, transmissivity of light, with a wavelength of 550 nm, with a wavelength of 800 nm, or both, through the adhesive layer 14 into the interior 111 of the housing 11, can be of ≤10%, ≤3%, or ≤2%.
The adhesive layer 14 can have a low Young's Modulus, low tensile strength and high elongation to compensate for a mismatch of the coefficient of thermal expansion between the thin film 13 and the housing 11. Such properties can allow flexure of the adhesive layer 14 when the thin film 13 and the housing 11 expand or contract at different rates during temperature changes, thus avoiding window fracture or distortion.
Example Young's Modulus values of the adhesive layer 14 include ≥100 MPa, ≥500 MPa, or ≥1 GPa and ≤2 GPa, ≤5 GPa, ≤8 GPa, or ≤12 GPa, each at 25° C. Example tensile strength values of the adhesive layer 14 include ≥100 MPa, ≥125 MPa, ≥150 MPa, or ≥175 MPa and ≤200 MPa, ≤225 MPa, ≤250 MPa, or ≤300 MPa, each at 25° C. Each of these tensile strength values can be for machine direction (roll-out direction of the liquid crystal polymer), transverse direction (transverse to the machine direction / roll-out direction), or both.
Elongation is strain before failure in tensile testing. Elongation is equal to (final length−initial length)/initial length. Example elongation values of the adhesive layer 14 include ≥10%, ≥20%, or ≥30% and ≤40%, ≤50%, or ≤60%, each at 25° C.
The adhesive layer 14 can have isotropic properties, depending on its method of manufacture. Anisotropy of the adhesive layer 14 close or equal to zero might be preferable for uniform bond characteristics. For example, anisotropy of the adhesive layer 14 can be ≤300 MPa, ≤250 MPa, ≤200 MPa, ≤150 MPa, ≤100 MPa, ≤75 MPa, ≤50 MPa, or ≤25 MPa, each at 25° C. Anisotropy is calculated by subtracting tensile strength in the transverse direction from tensile strength in the machine direction.
The thin film 13 and the housing 11 can have low coefficient of thermal expansion values. It can be helpful for the adhesive layer 14 to have a coefficient of thermal expansion close to that of the thin film 13, the housing 11, or both. Example coefficient of thermal expansion values of the adhesive layer 14 include ≥0 m/(m*K), ≥10−6 m/(m*K), or ≥2×10−6 m/(m*K) and ≤5×10−6 m/(m*K), ≤10×10−6 m/(m*K), ≤20×10−6 m/(m*K), ≤30×10−6 m/(m*K), ≤35×10−6 m/(m*K), ≤40×10−6 m/(m*K), or ≤45×10−6 m/(m*K), each at 25° C.
It can be helpful for the adhesive layer 14 to have low outgassing under vacuum after bonding. This property can avoid reduction of an internal vacuum of the final device. Weight loss of the heated adhesive layer 14 can be used to quantify outgassing. For example, weight loss of the adhesive layer 14, prior to placing the adhesive layer 14 between the thin film 13 and the housing 11, can be ≤5%, ≤3%, ≤2%, ≤1%, ≤0.7%, or ≤0.6%, at a temperature of 225° C. during a 24 hour period.
Use of a liquid crystal polymer as the adhesive layer 14 can provide a strong hermetic seal between many different x-ray window thin film 13 materials and many different housing materials, thus reducing gas leakage through the hermetic seal. For example, liquid crystal polymers can bond effectively to silicon, boron, aluminum, stainless steel, nickel, copper, or combinations thereof. The thin film 13, the housing 11, or both can include one or more of these materials. Examples of the leak tightness of the x-ray windows 10, 20, and 50 described herein include average helium leak rate of ≤10−9 mbar*L/sec, ≤10−10 mbar*L/sec, or ≤3×10−10 mbar*L/sec, at a temperature of 25° C., for at least the first 10 hours after forming the hermetic seal.
X-ray windows are commonly used with x-ray detection devices. X-ray fluorescence from material other than the sample measured/detected can interfere with the x-ray signal from the sample. This problem is usually worse if such interfering x-ray fluorescence is from a material with high atomic number. Therefore, it can be helpful if the adhesive layer 14 is made of material(s) with low atomic numbers. For example, ≥70%, ≥80%, ≥90%, or ≥95% of the atoms in the adhesive layer 14 can have an atomic number ≤6. As another example, ≥90%, ≥95%, ≥99%, or 100% of the atoms in the adhesive layer 14 can have an atomic number≤8. Therefore, the adhesive layer 14 can be made primarily of carbon (Z=6), hydrogen (Z=1), and oxygen (Z=8).
Various types of liquid crystal polymer can be used as the adhesive layer 14 in the embodiments described herein. For example, the liquid crystal polymer can be main chain, side chain, linear, cyclic, branched, crosslinked, or combinations thereof. The liquid crystal polymer can be thermotropic or lyotropic. The liquid crystal polymer can be an aromatic polyester. The polymer of the liquid crystal polymer can be formed from the following monomers: 4-hydroxybenzaldehyde, 6-hydroxy-2-naphthaldehyde, 4,4′-biphenol, terephthalaldehyde, ethane-1,2-diol, or combinations thereof. The mesogen used in formation of the liquid crystal polymer can be disc-like, rod-like, amphiphilic, or combinations thereof. The liquid crystal polymers 14 can form regions of highly ordered structure while in the liquid phase.
Proper selection of a width of a mounting surface can improve bonding, reduce leakage, and reduce cost. As illustrated in
It can be useful for the thin film 13 to be strong (especially strong enough to withstand a differential pressure of 1 atm) and allow a high percent transmission of x-rays. The thin film 13 can have sufficient thickness for strength, but not have a thickness that will cause excessive attenuation of x-rays. For example, the thin film 13 can have a thickness Th13 of ≤0.01 micrometers, ≥0.2 micrometers, ≥10 micrometers, or ≥100 micrometers; and ≤500 micrometers, ≤1 millimeter, or ≤5 millimeters. The thickness can depend on material of construction, span-width, differential-pressure, and application. Material of construction for the thin film 13 can include or consist of materials with an atomic number≤14, ≤6, ≤4; and can include beryllium, hydrogen, oxygen, carbon, silicon, and nitrogen.
A differential pressure across the thin film 13 (e.g. a vacuum on one side and air or vacuum on an opposite side) can cause it to bow or deflect excessivley, damaging the x-ray window, and also possibly causing a short circuit by creating an unintended electrical-current path, or, for an x-ray tube, a change in electron-beam focusing. Thus, it can be useful to minimize the deflection distance. The thin film 13 described herein can be made sufficiently strong and thus can have a relatively small deflection distance. For example, the thin film 13 can have a deflection distance of ≤400 micrometers, ≤300 micrometers, ≤200 micrometers, or ≤100 micrometers, with one atmosphere differential pressure across the thin film 13.
It can be useful for x-ray windows to have a high transmissivity of x-rays, including a high transmission of low-energy x-rays. The thin film 13 described herein can have a high transmissivity of x-rays. For example, the thin film 13 can have a transmissivity of ≥50%, ≥60%, ≥70%, ≥74%, or ≥80% for x-rays having an energy of 1.74 keV.
For some applications, it can be useful for x-ray windows to block visible and infrared light transmission in order to avoid creating undesirable noise in sensitive instruments. For example, the thin film 13 described herein can have a transmissivity of ≤10%, ≤3%, or ≤2% for visible light at a wavelength of 550 nanometers and/or a transmissivity of ≤10%, ≤4%, or ≤3% for infrared light at a wavelength of 800 nanometers.
The thin film 13 can include some or all of the properties (e.g. low deflection, high x-ray transmissivity, low visible and infrared light transmissivity) of the x-ray windows described in U.S. Pat. No. 9,502,206, which is incorporated herein by reference in its entirety.
A method of making an x-ray window 50 can comprise some or all of the following steps, which are illustrated in
The method can include placing an adhesive layer 14 between a thin film 13 and a housing 11. Another step in the method can be applying a pressure P to press the thin film 13 and the housing 11 towards each other and towards the adhesive layer 14 sandwiched between them. An additional step in the method can be heating the x-ray window, such as for example in oven 51. Applying the pressure P and heating can be done simultaneously or sequentially. For example, a small weight can be placed on the thin film 13 and the housing 11.
Pressure, duration under such pressure, and temperature can be adjusted for optimal bonding and throughput. Increased pressure can reduce processing time and increase bond strength, but can result in damage to sensitive components or undesirable thinning of the adhesive layer 14. Examples of pressure ranges, particularly applicable if the adhesive layer 14 is liquid crystal polymer, include ≥0.01 KPa, ≥0.1 KPa, ≥0.15 KPa, ≥0.2 KPa, ≥0.5 KPa, ≥1 KPa, or ≥5 KPa and ≤10 KPa, ≤20 KPa, ≤30 KPa, ≤50 KPa, or ≤100 KPa.
Increased temperature can reduce processing time and better fill gaps and holes in the bonded materials, but can result in thermal damage to the adhesive layer 14 or other x-ray window components. The optimal temperature can be selected based on applied pressure P, processing time, temperature sensitivity of components, and desired bonding strength. For example, the x-ray window 50, with liquid crystal polymer as the adhesive layer 14, can be heated to a temperature above the transition temperature TLC of the liquid crystal polymer. For example, the x-ray window 50 can be heated≥10° C., ≥50° C., or ≥70° C. above the transition temperature TLC of the liquid crystal polymer. Further, the x-ray window 50 can be heated≤90° C., ≤100° C., or ≤150° C. above the transition temperature TLC of the liquid crystal polymer. As another example, the x-ray window 50 can be heated to a temperature of ≥100° C., ≥150° C., ≥200° C., ≥250° C., or ≥300° C. and ≤350° C., ≤400° C., ≤500° C., or ≤600° C.
A slow cure at a relatively lower temperature and pressure can result in an improved bond, but can increase cost due to reduced throughput. Examples of processing time (time during which the x-ray window 50 is maintained under pressure P and heat) include 5 minutes, ≥15 minutes, ≥20 minutes, ≥30minutes, or ≥1 hour and ≤2 hours, ≤3 hours, ≤4.5 hours, ≤6 hours, or ≤10 hours.
The liquid crystal polymer can be initially dissolved in a solvent. The solution (liquid crystal polymer and solvent) can be applied to the thin film 13, the housing 11, or both, then baked to remove the solvent and bond the thin film 13 to the housing 11. Alternatively, the liquid crystal polymer can be in pellet form, which can be pressed and placed onto the thin film 13, the housing 11, or both, then baked. The liquid crystal polymer can be formed into a sheet/film. This sheet/film can then be cut to shape and placed on the thin film 13 or the housing 11. The thin film 13 and the housing 11 can be pressed together with the liquid crystal polymer between, then baked. A choice between these methods can be based on manufacture cost of the liquid crystal polymer, final bond strength, manufacture cost of the x-ray window, and isotropic properties of the liquid crystal polymer.
As illustrated in
As illustrated in
As illustrated in
The adhesive layer 14 described above can be one layer of the pair of adhesive layers 64, specifically a proximal adhesive layer 14p, closer to the housing 11 than the other layer, the distal adhesive layer 14d. The proximal adhesive layer 14p, the distal adhesive layer 14d, or both, can have properties as described above for the adhesive layer 14. The pair of adhesive layers 64 can have a same material composition with respect to each other. The housing 11 and the thin film 13 can also have properties as described above. The thin film 13 can be sandwiched between the proximal adhesive layer 14p and the distal adhesive layer 14d.
The x-ray window can further comprise a ring 61 located at an opposite side of the distal adhesive layer 14d from the thin film 13. Thus, the distal adhesive layer 14d can be sandwiched between the ring 61 and the thin film 13. In one embodiment, the ring 61 can be metallic. The ring can comprise an iron-nickel-cobalt alloy, such as for example Kovar (ASTM F 15 Alloy). In order to avoid thermal expansion mismatch, the ring 61 and the housing 11 can have a same material composition with respect to each other. Thus, both can be metallic, both can comprise an iron-nickel-cobalt alloy, or both can include Kovar. Use of the ring 61 can improve bonding the hermetic seal.
This application is a continuation of U.S. patent application Ser. No. 17/210,299, filed on Mar. 23, 2021, which is a continuation of U.S. patent application Ser. No. 16/433,202, filed on Jun. 6, 2019, which claims priority to U.S. Provisional Patent Application No. 62/694,503, filed on Jul. 6, 2018, which are incorporated herein by reference.
| Number | Date | Country | |
|---|---|---|---|
| 62694503 | Jul 2018 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 17210299 | Mar 2021 | US |
| Child | 17671861 | US | |
| Parent | 16433202 | Jun 2019 | US |
| Child | 17210299 | US |