The present invention relates to liquid-crystalline media and to high-frequency components comprising same, especially microwave components for high-frequency devices, such as devices for shifting the phase of microwaves, in particular for microwave phased-array antennas.
Liquid-crystalline media have a been used for some time in electro-optical displays (liquid crystal displays: LCDs) in order to display information.
Recently, however, liquid-crystalline media have also been proposed for use in components for microwave technology, such as, for example, in DE 10 2004 029 429 A and in JP 2005-120208 (A).
As a typical microwave application, the concept of the inverted microstrip line as described by K. C. Gupta, R. Garg, I. Bahl and P. Bhartia: Microstrip Lines and Slotlines, 2nd ed., Artech House, Boston, 1996, is employed, for example, in D. Dolfi, M. Labeyrie, P. Joffre and J. P. Huignard: Liquid Crystal Microwave Phase Shifter. Electronics Letters, Vol. 29, No. 10, pp. 926-928, May 1993, N. Martin, N. Tentillier, P. Laurent, B. Splingart, F. Huert, P H. Gelin, C. Legrand: Electrically Microwave Tunable Components Using Liquid Crystals. 32nd European Microwave Conference, pp. 393-396, Milan 2002, or in Weil, C.: Passiv steuerbare Mikrowellenphasenschieber auf der Basis nichtlinearer Dielektrika [Passively Controllable Microwave Phase Shifters based on Nonlinear Dielectrics], Darmstädter Dissertationen D17, 2002, C. Weil, G. LOssem, and R. Jakoby: Tunable Invert-Microstrip Phase Shifter Device Using Nematic Liquid Crystals, IEEE MTT-S Int. Microw. Symp., Seattle, Wash., June 2002, pp. 367-370, together with the commercial liquid crystal K15 from Merck KGaA. C. Weil, G. Lüssem, and R. Jakoby: Tunable Invert-Microstrip Phase Shifter Device Using Nematic Liquid Crystals, IEEE MTT-S Int. Microw. Symp., Seattle, Wash., June 2002, pp. 367-370, achieve phase shifter qualities of 12°/dB at 10 GHz with a control voltage of about 40 V therewith. The insertion losses of the LC, i.e. the losses caused only by the polarisation losses in the liquid crystal, are given as approximately 1 to 2 dB at 10 GHz in Weil, C.: Passiv steuerbare Mikrowellenphasenschieber auf der Basis nichtlinearer Dielektrika [Passively Controllable Microwave Phase Shifters based on Nonlinear Dielectrics], Darmstädter Dissertationen D17, 2002. In addition, it has been determined that the phase shifter losses are determined primarily by the dielectric LC losses and the losses at the waveguide junctions. T. Kuki, H. Fujikake, H. Kamoda and T. Nomoto: Microwave Variable Delay Line Using a Membrane Impregnated with Liquid Crystal. IEEE MTT-S Int. Microwave Symp. Dig. 2002, pp. 363-366, June 2002, and T. Kuki, H. Fujikake, T. Nomoto: Microwave Variable Delay Line Using Dual-Frequency Switching-Mode Liquid Crystal. IEEE Trans. Micro-wave Theory Tech., Vol. 50, No. 11, pp. 2604-2609, November 2002, also address the use of polymerised LC films and dual-frequency switching-mode liquid crystals in combination with planar phase shifter arrangements.
A. Penirschke, S. Müller, P. Scheele, C. Weil, M. Wittek, C. Hock and R. Jakoby: “Cavity Perturbation Method for Characterization of Liquid Crystals up to 35 GHz”, 34th European Microwave Conference—Amsterdam, pp. 545-548 describe, inter alia, the properties of the known single liquid-crystalline substance K15 (Merck KGaA, Germany) at a frequency of 9 GHz.
A. Gaebler, F. Goelden, S. Müller, A. Penirschke and R. Jakoby “Direct Simulation of Material Permittivites using an Eigen-Susceptibility Formulation of the Vector Variational Approach”, 12MTC 2009—International Instrumentation and Measurement Technology Conference, Singapore, 2009 (IEEE), pp. 463-467, describe the corresponding properties of the known liquid-crystal mixture E7 (likewise Merck KGaA, Germany).
DE 10 2004 029 429 A describes the use of liquid-crystal media in microwave technology, inter alia in phase shifters. It has already investigated liquid-crystalline media with respect to their properties in the corresponding frequency range. In addition, it describes liquid-crystalline media which comprise compounds of the formulae
besides compounds of the formulae
or besides compounds of the formulae
Further liquid crystalline media for microwave applications comprising one or more these compounds, as well as similar ones, are proposed by for microwave applications e.g. in WO 2013/034227 A1 and DE 10 2010 025 572 A1, which discloses, amongst others, liquid crystalline media comprisining compounds of fotmula
But these media are characterized by rather high values of the clearing point and by high rotational viscosities, leading to long response times, which are undesirable for many practical applications. They further do in many cases exhibit nematic phase ranges, which are not adequate for many practical applications. Especially the phase behaviour at low temperature has to be improved for most of them.
Polymer stabilization of liquid crystalline media, as well as doping by chiral dopants, has already been proposed for several types of display applications and for various reasons. However, there has been no respective suggestion for the type of applications envisaged by the instant application.
The known devices for the high frequency-technology comprising these media do still lack sufficient stability and, in particular, fast response.
However, these compositions are afflicted with serious disadvantages. Most of them result, besides other deficiencies, in disadvantageously high losses and/or inadequate phase shifts or inadequate material quality.
For these applications, liquid-crystalline media having particular, hitherto rather unusual and uncommon properties or combinations of properties are required.
Novel liquid-crystalline media having improved properties are thus necessary. In particular, the dielectric loss in the microwave region must be reduced and the material quality (η, sometimes also called figure of merit, short FoM), i.e. a high tunability and, at the same time, a low dielectric loss, must be improved. Besides these requirements increased focus has to be placed on improved response times for several envisaged applications especially for those devices using planar structures such as e.g. phase shifters and leaky antennas.
In addition, there is a steady demand for an improvement in the low-temperature behaviour of the components. Both an improvement in the operating properties at low temperatures and also in the shelf life are necessary here.
There is therefore a considerable demand for liquid-crystalline media having suitable properties for corresponding practical applications.
The invention additionally has the aim of providing improved methods and materials, to achieve polymer stabilised mesogenic phases, in particular nematic phases, which do not have the above-mentioned disadvantages of methods and materials described in prior art. These mesogenic phases comprise a polymer and a low molecular weight mesogenic material. Consequently, they are also called “composite systems”, or short “systems”.
Another aim of the invention is to extend the pool of suitable materials available to the expert. Other aims are immediately evident to the expert from the following description.
Surprisingly, it has now been found that liquid crystalline media comprising one or more compounds of formula T as defined below are characterized by a very good temperature range and especially by an excellent behavior under storage at low temperatures. compared to the state of the art. They are characterized by comparatively wide nematic phase ranges extending to deep temperatures.
Preferably the chiral dopants present in the media according to the ionstant application are mesogenic compounds and most preferably they exhibit a mesophase on their own.
Particularly preferred the media according to the present invention comprise one or more chiral dopants. Preferably these chiral doüpants have an absolute value of the helical twisting power (short HTP) in the range of 1 μm−1 or more to 150 μm−1 or less, preferably in the range from 10 μm−1 or more to 100 μm−1 or less. In case the media comprise at least two, i.e. two or more, chiral dopants, these may have mutually opposite signs of their HTP-values. This condition is preferred for some specific embodiments, as it allows to compensate the chirality of the respective compounds to some degree and, thus, may be used to compensate various temperature dependent properties of the resulting media in the devices. Generally, however, it is preferred that most, or, even more preferred, all of the chiral compounds present in the media according to the present invention have the same sign of their HTP-values.
It has to be noted here that, as a first approximation, the HTP of a mixture of chiral compounds, i.e. of conventional chiral dopants, as well as of chiral reactive mesogens, may be approximated by the addition of their individual HTP values weighted by their respective concentrations in the medium.
In this embodiment, the cholesteric pitch of the modulation medium in the cholesteric phase, also referred to as the chiral nematic phase, can be reproduced to a first approximation by equation (1).
P=(HTP·c)−1 (1)
If the pitch is to be determined more accurately, equation (1) can be correspondingly modified. To this end, the development of the cholesteric pitch in the form of a polynomial (2) is usually used.
P=(HTP·c)−1+(α1·c)−2+(α2·c)−3+ (2)
The polynomial can be continued up to the degree, which enables the desired accuracy.
Typically the parameters of the polynomial (HTP (sometimes also called α1) α2, α3 and so forth) do depend more strongly on the type of the chiral dopant, and, to some degree, also on the specific liquid crystal mixture used.
Obviously, they do also depend on the enantiomeric excess of the respective chiral dopant. They have their respective largest absolute values for the pure enantiomers and are zero for racemates. In this application the values given are those for the pure enantiomers, having an enantiomeric excess of 98% or more, unless explicitly staed otherwise.
If the chiral component (A) consists of two or more compounds, equation (1) is modified to give equation (3).
P=[Σ
i(HTP(i)·ci)]−1 (3)
in which
The temperature dependence of the HTP is usually represented in a polynomial development (4), which, however, for practical purposes often can be terminated already right after the linear element (β1).
HTP(T)=HTP(T0)+β1·(T−T0)+β2·(T−T0)2+ . . . (4)
in which the parameters are as defined above for equation (1) and
Additionally, it has been found that by using an RM, a stabilised liquid liquid crystalline phase which has a broad temperature range and a improved, faster switching times, good tunabilitzy and acceptable loss can be achieved.
Additionally to mesogenic monomers the use of non-mesogenic monomers, such as 2-ethylhexylacrylate, is also possible and in certain instances may be beneficial. It, however, also may be problematic due to the volatile nature of such compounds, leading to problems of loss due to evaporation and inhomogeneity of the mixed monomer/host system.
Also, the use of non-mesogenic compounds can severely lower the clearing point of the liquid liquid crystalline host, leading to a much smaller width of polymer stabilised nematic, which is not desirable for most practical applications.
Using RMs having a cyclohexylene core instead of a core comprising one or more 1,4-pphenylenes has an advantage for the stability against UV irradiation in general and in particular against the UV irradiation used in the polymerisation process. The resultant polymer stabilised phase (composite system) therefore has a high voltage holding ratio (VHR).
Also, it has been found that by using cyclohexylene RMs in combination with a liquid liquid crystalline host comprising fluorophenyl liquid liquid crystalline compounds, the RMs do effectively stabilise this host to give a high VHR, which is necessary for advanced state-of-the-art devices.
Surprisingly, it has now been found that it is possible to achieve liquid-crystalline media having a suitably fast switching times, a suitable, nematic phase range and loss which do not have the disadvantages of the prior-art materials, or at least only do so to a considerably reduced extent.
These improved liquid-crystalline media in accordance with the present invention comprise
wherein
in which
preferably
in which
preferably
in which
preferably
and
in which
P
a-(Spa)s1-(A1-Z1)n1-A2-Q-A3-(Z4-A4)n2-(Spb)s2-Pb P
wherein the individual radicals have the following meanings:
In a first preferred embodiment of the present invention, the liquid-crystalline media in accordance with the present invention comprise comprises one or more compounds of the formula T selected from the group of compounds of formulae T-1 to T-5, preferably of formulae T-1 and T-3
wherein
The chiral compounds of chiral component (A) preferably have a high absolute value of the HTP. They are also referred to as chiral dopants since they are generally added in relatively low concentrations to mesogenic base mixtures. They preferably have good solubility in the achiral component (B). They do not impair the mesogenic or liquid-crystalline properties of the mesogenic medium, or only do so to a small extent, so long as the cholesteric pitch has small values which are much smaller than the wavelength of the light. If the cholesteric pitch is in the order of the wavelength of the light, however, they induce a blue phase having a completely different structure to that of the cholesteric phase. If two or more chiral compounds are employed, they may have the same or opposite direction of rotation and the same or opposite temperature dependence of the twist.
Particular preference is given to chiral compounds having an HTP of 20 μm−1 or more, in particular of 40 μm−1 or more, particularly preferably of 70 μm−1 or more, in the commercial liquid-crystal mixture MLC-6828 from Merck KGaA.
In a preferred embodiment of the present invention, the chiral component (A) consists of two or more chiral compounds which all have the same sign of the HTP.
The temperature dependence of the HTP of the individual compounds may be high or low. The temperature dependence of the pitch of the medium can be compensated by mixing compounds having different temperature dependence of the HTP in corresponding ratios.
For the optically active component, a multiplicity of chiral dopants, some of which are commercially available, is available to the person skilled in the art, such as, for example, cholesteryl nonanoate, R/S-811, R/S-1011, R/S-2011, R/S-3011, R/S-4011, B(OC)2C*H—C-3 or CB15 (all Merck KGaA, Darmstadt).
Particularly suitable dopants are compounds which contain one or more chiral radicals and one or more mesogenic groups, or one or more aromatic or alicyclic groups which form a mesogenic group with the chiral radical.
Suitable chiral radicals are, for example, chiral branched hydrocarbon radicals, chiral ethanediols, binaphthols or dioxolanes, furthermore mono- or polyvalent chiral radicals selected from the group consisting of sugar derivatives, sugar alcohols, sugar acids, lactic acids, chiral substituted glycols, steroid derivatives, terpene derivatives, amino acids or sequences of a few, preferably 1-5, amino acids.
Preferred chiral radicals are sugar derivatives, such as glucose, mannose, galactose, fructose, arabinose and dextrose; sugar alcohols, such as, for example, sorbitol, mannitol, iditol, galactitol or anhydro derivatives thereof, in particular dianhydrohexitols, such as dianhydrosorbide (1,4:3,6-dianhydro-D-sorbide, isosorbide), dianhydromannitol (isosorbitol) or dianhydroiditol (isoiditol); sugar acids, such as, for example, gluconic acid, gulonic acid and ketogulonic acid; chiral substituted glycol radicals, such as, for example, mono- or oligoethylene or propylene glycols, in which one or more CH2 groups are substituted by alkyl or alkoxy; amino acids, such as, for example, alanine, valine, phenylglycine or phenylalanine, or sequences of from 1 to 5 of these amino acids; steroid derivatives, such as, for example, cholesteryl or cholic acid radicals; terpene derivatives, such as, for example, menthyl, neomenthyl, campheyl, pineyl, terpineyl, isolongifolyl, fenchyl, carreyl, myrthenyl, nopyl, geraniyl, linaloyl, neryl, citronellyl or dihydrocitronellyl.
Suitable chiral radicals and mesogenic chiral compounds are described, for example, in DE 34 25 503, DE 35 34 777, DE 35 34 778, DE 35 34 779 and DE 35 34 780, DE 43 42 280, EP 01 038 941 and DE 195 41 820.
Chiral compounds preferably used according to the present invention are selected from the group consisting of the formulae shown below.
Particular preference is given to dopants selected from the group consisting of compounds of the following formulae A-I to A-III:
in which
Particular preference is given to dopants selected from the group consisting of the compounds of the following formulae:
Further preferred dopants are derivatives of the isosorbide, isomannitol or isoiditol of the following formula A-IV:
in which the group
preferably dianhydrosorbitol,
and chiral ethanediols, such as, for example, diphenylethanediol (hydrobenzoin), in particular mesogenic hydrobenzoin derivatives of the following formula A-V:
including the (R,S), (S,R), (R,R) and (S,S) enantiomers, which are not shown,
in which
The compounds of the formula A-IV are described in WO 98/00428. The compounds of the formula A-V are described in GB-A-2,328,207.
Very particularly preferred dopants are chiral binaphthyl derivatives, as described in WO 02/94805, chiral binaphthol acetal derivatives, as described in WO 02/34739, chiral TADDOL derivatives, as described in WO 02/06265, and chiral dopants having at least one fluorinated bridging group and a terminal or central chiral group, as described in WO 02/06196 and WO 02/06195.
Particular preference is given to chiral compounds of the formula A-VI
in which
both are a single bond,
Particular preference is given to chiral binaphthyl derivatives of the formula A-VI-1
in particular those selected from the following formulae A-VI-1a to A-VI-1c:
in which ring B and Z0 are as defined for the formula A-IV, and
Particular p reference is furthermore given to chiral binaphthyl derivatives of the formula A-VI-2
in particular those selected from the following formulae A-VI-2a to A-VI-2f:
in which R0 is as defined for the formula A-VI, and X is H, F, Cl, CN or R0, preferably F.
Polymerisable compounds of formula P preferably used according to the present invention are selected from the group consisting of the following formulae:
in which L in each occurrence, identically or differently, has one of the meanings indicated above and below, r denotes 0, 1, 2, 3 or 4, s denotes 0, 1, 2 or 3, and n denotes an integer between 1 and 24, preferably between 1 and 12, very particularly preferably between 2 and 8, and in which, if a radical is not indicated at the end of a single or double bond, it is a terminal CH3 or CH2 group.
In the formulae P1 to P24,
preferably denotes a group selected from the group consisting of the following formulae:
particularly preferably selected from
The group A2-Q-A3 preferably denotes a group of the formula
in which at least one of the rings is substituted by at least one group L=F. r here is in each case, independently, preferably 0, 1 or 2.
Pa and Pb in the compounds of the formula P and the sub-formulae thereof preferably denote acrylate or methacrylate, furthermore fluoroacrylate.
Spa and Spb in the compounds of the formula I and the sub-formulae thereof preferably denote a radical selected from the group consisting of —(CH2)p1—, —(CH2)p1—O—, —(CH2)p1—O—CO— and —(CH2)p1—O—CO—O— and mirror images thereof, in which p1 denotes an integer from 1 to 12, preferably from 1 to 6, particularly preferably 1, 2 or 3, where these groups are linked to Pa or Pb in such a way that O atoms are not directly adjacent.
Of the compounds of the formula P, particular preference is given to those in which
wherein Pa, Pb, Spa, Spb, s1 and s2 are as defined under formula P above, and preferably Spa/b is alkylene —(CH2)n— wherein n preferably is 3, 4, 5, 6 or 7 and Pa/b preferably a methacrylat- or acrylate moiety. Especially preferred is the use of compounds selected from the group of formulae Pa, Pb, Pc, Pd, Pe, Pf, Pg, Ph and Pi and, in particular the compounds of formula Pa.
In formula P the moiety “A2-Q-A3” preferably is a moiety of formula
wherein preferably at least one of the two phenylene rings is substituted by at least one L, which is different from H, wherein r is independently for each ring, and preferably it is for each ring 0, 1 or 2.
For the compounds of formula P, as well as for its respective sub-formulae, preferably
Pa and Pb are, independently from each other, acrylate or methacrylate, but also fluoroacrylate,
Spa and Spb are, independently from each other, —(CH2)p1—, —(CH2)p1—O—, —O—(CH2)p1—, —(CH2)p1—O—CO—, —CO—O—(CH2)p1—, —(CH2)p1—O—CO—O— or —(CH2)p1—O—CO—O—, wherein p1 is an integer from 1 to 12, preferably from 1 to 6, particularly preferred 1, 2 or 3, and wherein these moieties are linked with Pa or Pb in such a way that no O-atoms are linked directly to on another.
Especially preferred is the use of compounds of formula P, wherein
Suitable and preferred co-monomers for use in polymer precursors for polymer stabilised devices according to the present invention are selected, for example, from the following formulae:
wherein the parameters have the following meanings:
Suitable and preferred co-monomers for use in devices according to the present application operable and/or operating at a temperature where the mesogenic medium is in the blue are for example selected from the group of mono-reactive compounds, which are present in the precursor of the polymer stabilised systems in a concentration in the range from 1 to 9 wt.-%, particularly preferred from 4 to 7 wt.-%. Preferred mono-reactive compounds are the compounds of formulae M1 bis M29, wherein one or more of P1-Sp1- and P2-Sp2- are Rest Raa, such that the compounds have a single reactive group only.
Particularly preferred mono-reactive compounds are the compounds of the following formulae
wherein P1, Sp1 and Raa have the respective meanings given above and P1 preferably is acrylate (CH2═CH—CO—O—) or methacrylate (CH2═C(CH3)—CO—O—).
Amongst these the compounds of the formula
wherein
Particular preference is given to an LC medium, an LC device, preferably for the high frequency technology, in particular for a phase shifter or a microwave antenna e.g. a leaky antenna, a process or the use as described above and below, in which the LC medium or the polymerisable or polymerised component present therein comprises one or more compounds of the following formula:
in which Pa, Pb, Spa, Spb, s1, s2 and L have the meanings indicated above and below, r denotes 0, 1, 2, 3 or 4, and Z2 and Z3 each, independently of one another, denote —CF2—O— or —O—CF2—, preferably Z2 is —CF2—O— and Z3 is —O—CF2— or vice versa or Z2 is —CO—O— and Z3 is —O—CO— or vice versa, and, most preferably, Z2 is —CF2—O— and Z3 is —O—CF2— or Z2 is —CO—O— and Z3 is —O—CO—.
Preferably the liquid-crystalline media used according to the present invention comprise as a polymer precursor or part of a polymer precursor one, two or more reactive mesogens, preferably one or more mono-reactive mesogens and, at the same time, one or more direactive mesogens. Optionally one or more of the reactive mesogens may be replaced by a non-mesogenic, respectively an isotropic, reactive compound, preferably selected from HDMA, HDDMA, EHA, EA, EMA and the like.
In a preferred embodiment of the instant application the liquid-crystalline media used according to the present invention comprise a polymer obtained or obtainable by polymerisation, preferably photopolymerisation of a polymer precursor comprising one, two or more reactive mesogens, preferably one or more mono-reactive mesogens and, at the same time, one or more direactive mesogens. Optionally one or more of the reactive mesogens may be replaced by a non-mesogenic, respectively an isotropic, reactive compound, preferably selected from 2-ethylhexyl acrylate (EHA), 1,3,3-trimethylhexyl acrylate (TMHA), hexanolediacrylate (HDDA), hexanoledimethacrylate (HDDMA), and the like, but also from metylmethacrylate (MMA), ethylacrylate (EA), ethylmethacrylate (EMA) and 6-(4′-cyanobiphenyl-4-yloxy)hexyl acrylate (6CBA), a mesogenic monomer.
Preferably one or more, most preferably all, mono-reactive mesogens are methacrylates and, also preferably one or more, most preferably all, mono-reactive mesogens are selected from the group of the bisacrylates and the mixed acrylates-methacrylates, preferably they are bisacrylates.
Preferably the liquid-crystalline media according to the present invention comprise
In a preferred embodiment of the present invention, the liquid-crystalline media comprise one or more compounds of the formula I and one or more compounds of the formula III.
In a further preferred embodiment of the present invention, the liquid-crystalline media comprise one or more compounds of the formula I and one or more compounds of the formula II.
The liquid-crystalline media in accordance with the present invention likewise preferably comprise one or more compounds of the formula II and one or more compounds of the formula III.
Particular preference is given in accordance with the present invention to liquid-crystalline media which comprise one or more compounds of the formula I, one or more compounds of the formula II and one or more compounds of the formula III.
Additionally the liquid-crystalline media used according to the present invention comprise one or more compounds of the formula IV,
wherein
preferably
particularly preferably
Preferably the liquid crystal media contain one or more chiral dopants preferably having an absolute value of the helical twisting power (HTP) of 20 μm−1 or more, preferably of 40 μm−1 or more, more preferably in the range of 60 μm−1 or more, most preferably in the range of 80 μm−1 or more to 260 μm−1 or less.
The liquid-crystalline media in accordance with the present application preferably comprise in total 15% to 90%, preferably 20% to 85% and particularly preferably 25% to 80%, of compounds of the formula I. The liquid-crystalline media in accordance with the present application preferably comprise in total 1% to 70%, preferably 2% to 65% and particularly preferably 3% to 60%, of compounds of the formula II.
The liquid-crystalline media in accordance with the present application preferably comprise in total 0% to 60%, preferably 5% to 55% and particularly preferably 10% to 50%, of compounds of the formula III.
In a preferred embodiment of the present invention, in which the liquid-crystalline media comprise in each case one or more compounds of the formulae I, II and III, the concentration of the compounds of the formula I is preferably 45% to 75%, preferably 50% to 70% and particularly preferably 55% to 65%, the concentration of the compounds of the formula II is preferably 1% to 20%, preferably 2% to 15% and particularly preferably 3% to 10%, and the concentration of the compounds of the formula III is preferably 1% to 30%, preferably 5% to 25% and particularly preferably 5% to 20%.
In a further preferred embodiment of the present invention, in which the liquid-crystalline media comprise in each case one or more compounds of the formulae I, II and III, the concentration of the compounds of the formula I is preferably 15% to 40%, preferably 20% to 35% and particularly preferably 25% to 30%, the concentration of the compounds of the formula II is preferably 10% to 35%, preferably 15% to 30% and particularly preferably 20% to 25% and the concentration of the compounds of the formula III is preferably 25% to 50%, preferably 30% to 45% and particularly preferably 35% to 40%
In a preferred embodiment of the present invention, in which the liquid-crystalline media comprise in each case one or more compounds of the formulae I and II, but at most 5% and preferably no compounds of the formula III, the concentration of the compounds of the formula I is preferably 10% to 50%, preferably 20% to 40% and particularly preferably 25% to 35% the concentration of the compounds of the formula II is preferably 40% to 70% preferably 50% to 65% and particularly preferably 55% to 60%, and the concentration of the compounds of the formula III is preferably 1% to 4%, preferably 1% to 3% and particularly preferably 0%.
The liquid-crystalline media in accordance with the present application particularly preferably comprise in total 50% to 80%, preferably 55% to 75% and particularly preferably 57% to 70% of compounds of the formula I-1 and/or in total 5% to 70% preferably 6% to 50% and particularly preferably 8% to 20% of compounds selected from the group of the compounds of the formulae I-2 and I-3.
The liquid-crystalline media in accordance with the present application likewise preferably comprise in total 5% to 60% preferably 10% to 50% and particularly preferably 7% to 20% of compounds of the formula II.
In the case of the use of a single homologous compound, these limits correspond to the concentration of this homologue, which is preferably 2% to 20% particularly preferably 1% to 15%. In the case of the use of two or more homologues, the concentration of the individual homologues is likewise preferably in each case 1% to 15%
The compounds of the formulae I to III in each case include dielectrically positive compounds having a dielectric anisotropy of greater than 3, dielectrically neutral compounds having a dielectric anisotropy of less than 3 and greater than −1.5 and dielectrically negative compounds having a dielectric anisotropy of −1.5 or less.
In a preferred embodiment of the present invention, the liquid-crystal medium comprises one or more compounds of the formula CC, wherein
In a preferred embodiment of the present invention, the liquid-crystal medium comprises one or more compounds of the formula CC, wherein
In a preferred embodiment of the present invention, the liquid-crystal medium comprises one or more compounds of the formula CP, wherein
R01 denotes unfluorinated alkyl having 1 to 17, preferably having 3 to 10, C atoms or unfluorinated alkenyl having 2 to 15, preferably 3 to 10, C atoms, preferably alkyl having 3 C atoms, and
R02 denotes unfluorinated alkyl having 1 to 17, preferably having 1 to 5, C atoms or unfluorinated alkenyl having 2 to 15, preferably 3 to 10, C atoms, preferably alkyl having 1 or 2 C atoms.
In a preferred embodiment of the present invention, the liquid-crystal medium comprises one or more compounds of the formula I, preferably selected from the group of the compounds of the formulae I-1 to I-3, preferably of the formulae I-1 and/or I-2 and/or I-3, preferably of the formulae I-1 and I-2, more preferably these compounds of the formula I predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which the parameters have the respective meanings indicated above for formula I and preferably
R11 denotes unfluorinated alkyl having 1 to 7 C atoms or unfluorinated alkenyl having 2 to 7 C atoms,
R12 denotes unfluorinated alkyl having 1 to 7 C atoms or unfluorinated alkenyl having 2 to 7 C atoms or unfluorinated alkoxy having 1 to 7 C atoms,
X11 and X12, independently of one another, denote F, Cl, —OCF3, —CF3, —CN, —NCS or —SF5, preferably F, Cl, —OCF3 or —CN.
The compounds of the formula I-1 are preferably selected from the group of the compounds of the formulae I-1a to I-1d, more preferably these compounds of the formula I-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which the parameters have the respective meanings indicated above for formula I-1 and in which
The compounds of the formula I-2 are preferably selected from the group of the compounds of the formulae I-2a to I-2e and/or from the group of the compounds of the formulae I-2f and I-2g, more preferably these compounds of the formula I-2 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
where in each case the compounds of the formula I-2a are excluded from the compounds of the formulae I-2b and I-2c, the compounds of the formula I-2b are excluded from the compounds of the formulae I-2c and the compounds of the formula I-2g are excluded from the compounds of the formulae I-2f, and
in which the parameters have the respective meanings indicated above for formula I-1 and in which
The compounds of the formula I-3 are preferably compounds of the formula I-3a:
in which the parameters have the respective meanings indicated above for formula I-1 and in which preferably
In an even more preferred embodiment of the present invention, the compounds of the formula I are selected from the group of the compounds I-1a to I-1d, preferably selected from the group of the compounds I-1c and I-1d, more preferably the compounds of the formula I predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
The compounds of the formula I-1a are preferably selected from the group of the compounds I-1a-1 and I-1a-2, more preferably these compounds of the formula I-1a predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The compounds of the formula I-1b are preferably compounds of the formula I-1b-1:
in which
The compounds of the formula I-1c are preferably selected from the group of the compounds of the formulae I-1c-1 and I-1c-4, preferably selected from the group of the compounds of the formulae I-1c-1 and I-1c-2, more preferably these compounds of the formula I-1c predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The compounds of the formula I-1d are preferably selected from the group of the compounds of the formulae I-1d-1 and I-1d-2, preferably the compound of the formula I-1d-2, more preferably these compounds of the formula I-1d predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The compounds of the formula I-2a are preferably selected from the group of the compounds of the formulae I-2a-1 and 1-2a-2, preferably the compounds of the formula I-1a-1, more preferably these compounds of the formula I-2a predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
Preferred combinations of (R11 and R12), in particular in formula I-2a-1, are (CnH2n+1 and CmH2m+1), (CnH2n+1 and O—CmH2m+1), (CH2═CH—(CH2)Z and CmH2m+1), (CH2═CH—(CH2)Z and O—CmH2m+1) and (CnH2n+1 and (CH2)Z—CH═CH2).
Preferred compounds of the formula I-2b are the compounds of the formula I-2b-1:
in which
The preferred combination of (R11 and R12) here is, in particular, (CnH2n+1 and CmH2m+1).
Preferred compounds of the formula I-2c are the compounds of the formula I-2c-1:
in which
The preferred combination of (R11 and R12) here is, in particular, (CnH2n+1 and CmH2m+1).
Preferred compounds of the formula I-2d are the compounds of the formula I-2d-1:
in which
The preferred combination of (R11 and R12) here is, in particular, (CnH2n+1 and CmH2m+1).
Preferred compounds of the formula I-2e are the compounds of the formula I-2e-1:
in which
The preferred combination of (R11 and R12) here is, in particular, (CnH2n+1 and O—CmH2m+1).
Preferred compounds of the formula I-2f are the compounds of the formula I-2f-1:
in which
The preferred combinations of (R11 and R12) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CmH2n+1 and CmH2m+1).
Preferred compounds of the formula I-2g are the compounds of the formula I-2g-1:
in which
The preferred combinations of (R11 and R12) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CmH2n+1 and O—CmH2m+1).
The compounds of the formula II are preferably selected from the group of the compounds of the formulae II-1 to II-4, more preferably these compounds of the formula II predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
denotes
preferably
and preferably
The compounds of the formula II-1 are preferably selected from the group of the compounds of the formulae II-1a and II-1b, preferably selected from the group of the compounds of the formula II-1a, more preferably these compounds of the formula II-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The preferred combinations of (R21 and R22) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CnH2n+1 and CmH2m+1) in the case of formula II-1a and particularly preferably (CnH2n+1 and O—CmH2m+1) in the case of formula II-1b.
The compounds of the formula II-2 are preferably compounds of the formula II-2a:
in which
The preferred combinations of (R21 and R22) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1).
The compounds of the formula II-3 are preferably compounds of the formula II-3a:
in which the parameters have the meanings indicated above for formula II-3 and preferably
The compounds of the formula II-4 are preferably compounds of the formula II-4a:
in which the parameters have the meanings indicated above for formula II-4 and preferably
Further preferred compounds of the formula II are the compounds of the following formulae:
in which
The compounds of the formula III are preferably selected from the group of the compounds of the formulae III-1 to III-7, more preferably these compounds of the formula III predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
where the compounds of the formula III-5 are excluded from the compounds of the formula III-6, and
in which the parameters have the respective meanings indicated above for formula I and preferably
The compounds of the formula III-1 are preferably selected from the group of the compounds of the formulae III-1a to III-1d, more preferably these compounds of the formula III-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which X32 has the meaning given above for formula III-2 and
The compounds of the formula III-2 are preferably selected from the group of the compounds of the formulae III-2a and III-2b, preferably of the formula III-2a, more preferably these compounds of the formula III-2 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The preferred combinations of (R31 and R32) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CnH2n+1 and CmH2m+1).
The compounds of the formula III-3 are preferably compounds of the formula III-3a:
in which
The preferred combinations of (R31 and R32) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CnH2n+1 and CmH2m+1).
The compounds of the formula III-4 are preferably compounds of the formula III-4a:
in which
The preferred combinations of (R31 and R32) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CnH2n+1 and CmH2m+1).
The compounds of the formula III-5 are preferably selected from the group of the compounds of the formulae III-5a and III-5b, preferably of the formula III-5a, more preferably these compounds of the formula III-5 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The preferred combinations of (R31 and R32) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CnH2n+1 and CmH2m+1).
The compounds of the formula III-6 are preferably selected from the group of the compounds of the formulae III-6a and III-6b, more preferably these compounds of the formula III-6 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The preferred combinations of (R31 and R32) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CnH2n+1 and CmH2m+1).
The media in accordance with the present invention optionally comprise one or more compounds of the formula IV
in which
denotes
The liquid-crystalline media in accordance with the present application preferably comprise in total 0 to 40%, preferably 0 to 30% and particularly preferably 5 to 25%, of compounds of the formula IV.
The compounds of the formulae IV are preferably selected from the group of the compounds of the formulae IV-1 to IV-3, more preferably these compounds of the formula IV predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
one of
The preferred combinations of (R41 and R42) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CmH2n+1 and CmH2m+1).
The compounds of the formulae IV-1 are preferably selected from the group of the compounds of the formulae IV-1a to IV-1c, more preferably these compounds of the formula IV-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The preferred combinations of (R41 and R42) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CnH2n+1 and CmH2m+1).
The compounds of the formula IV-2 are preferably compounds of the formula IV-2a:
in which
The preferred combinations of (R41 and R42) here are, in particular, (CnH2n+1 and CmH2m+1), CnH2n+1 and O—CmH2m+1) and (CH2═CH—(CH2)Z and CmH2m+1), particularly preferably (CnH2n+1 and CmH2m+1).
The compounds of the formula IV-3 are preferably compounds of the formula IV-3a:
in which
The preferred combinations of (R41 and R42) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1).
The media in accordance with the present invention optionally comprise one or more compounds of the formula V
in which
denotes
The compounds of the formula V are preferably selected from the group of the compounds of the formulae V-1 to V-3, more preferably these compounds of the formula V predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which the parameters have the respective meanings indicated above under formula V and preferably
one of
denotes
and
in which
The preferred combinations of the pair of parameters (R51 and R52) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1).
The liquid-crystalline media in accordance with the present application preferably comprise in total 5% to 30%, preferably 10% to 25% and particularly preferably 15% to 20%, of compounds of the formula V.
The compounds of the formula V-1 are preferably selected from the group of the compounds of the formulae V-1a to V-1e, more preferably these compounds of the formula V-1 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which the parameters have the meaning given above and preferably
The compounds of the formula V-2 are preferably selected from the group of the compounds of the formulae V-2a and V-2b, more preferably these compounds of the formula V-2 predominantly consist, even more preferably essentially consist and very particularly preferably completely consist thereof:
in which
The preferred combination of the pair of parameters (R51 and R52) here is, in particular, (CnH2n+1 and CmH2m+1).
The compounds of the formula V-3 are preferably compounds of the formulae V-3a and V-3b:
in which
The preferred combinations of the pair of parameters (R51 and R52) here are, in particular, (CnH2n+1 and CmH2m+1) and (CnH2n+1 and O—CmH2m+1), particularly preferably (CnH2n+1 and O—CmH2m+1).
Suitable and preferred polymerisation methods are, for example, thermally induced polymerization or photo polymerisation, preferably photopolymerisation, in particular UV photopolymerisation. One or more initiators can optionally also be added here. Suitable conditions for the polymerisation and suitable types and amounts of initiators are known to the person skilled in the art and are described in the literature. Suitable for free-radical polymerisation are, for example, and preferably, the commercially available photoinitiators Irgacure®184, Irgacure®369, Irgacure®651, Irgacure®784 (preferably), Irgacure®819 (preferably), Irgacure®907 or Irgacure®1300 (all from BASF) or Darocure®1173 (from Ciba AG). If an initiator is employed, its proportion is preferably 0.001% to 5% by weight, particularly preferably 0.001% to 1% by weight.
The polymerisable compounds according to the invention are also suitable for polymerisation without an initiator, which is accompanied by considerable advantages, such as, for example, lower material costs and in particular less contamination of the LC medium by possible residual amounts of the initiator or degradation products thereof. The polymerisation can thus also be carried out without the addition of an initiator. In a preferred embodiment, the LC medium thus comprises no polymerisation initiator.
The polymerisable component or the LC medium may also comprise one or more stabilisers in order to prevent undesired spontaneous polymerisation of the RMs, for example during storage or transport. Suitable types and amounts of stabilisers are known to the person skilled in the art and are described in the literature. Particularly suitable are, for example, the commercially available stabilisers from the Irganox® series (from Ciba AG), such as, for example, Irganox® 1076. If stabilisers are employed, their proportion, based on the total amount of the mixture of LS including the RMs or the polymerisable component, is preferably in the range from 10 ppm to 10,000 ppm, particularly preferably in the range from 50 ppm to 2,000 ppm, most preferably 0.2% or about 0.2%.
The mixtures are characterised as described below before the polymerisation. The reactive components are then polymerised by irradiation once (180 s), and the resultant media are re-characterised.
The polymerisation of the media preferably is carried out by irradiation with a UV lamp (e.g. Dymax, Bluewave 200, 365 nm interference filter) having an effective power of about 3.0 mW/cm2 for 180 seconds. The polymerisation is carried out directly in the test cell/antenna device. To minimize UV induced host degradation a suitable long pass filter is beneficially applied, for example Schott GG395 or GG410.
The polymerisation is carried out at room temperature.
The entire irradiation time which results in maximum stabilisation is typically 180 s at the irradiation power indicated. Further polymerisations can be carried out in accordance with an optimised irradiation/temperature programme.
The total concentration of the polymeriszable compounds in the medium prior to polymerisation preferably is in the range form 1% to 20%, more preferably from 2% to 15% and, most preferably from 2% to 10%.
In a preferred embodiment of the present invention, the medium comprises one or more dielectrically positive compounds of the formula I-1 having a dielectric anisotropy of greater than 3.
The medium preferably comprises one or more dielectrically neutral compounds of the formula I-2 having a dielectric anisotropy in the range from more than −1.5 to 3.
In a preferred embodiment of the present invention, the medium comprises one or more compounds of the formula II.
In a further preferred embodiment of the present invention, the medium comprises one or more compounds of the formula III.
The liquid-crystalline media, preferably or better the nematic component of the liquid ctrystalline media used in accordance with the present invention preferably comprise 10% or less, preferably 5% or less, particularly preferably 2% or less, very particularly preferably 1% or less, and in particular absolutely no compound having only two or fewer five- and/or six-membered rings.
The definitions of the abbreviations (acronyms) are likewise indicated below in Table D or are evident from Tables A to C.
The liquid-crystalline media in accordance with the present invention preferably comprise, more preferably predominantly consist of, even more preferably essentially consist of and very preferably completely consist of compounds selected from the group of the compounds of the formulae T, CC, CP and I to V, preferably T, CC, CP and I to IV and very preferably T, CC, I to III and/or V.
In this application, “comprise” in connection with compositions means that the entity in question, i.e. the medium or the component, comprises the component or components or compound or compounds indicated, preferably in a total concentration of 10% or more and very preferably 20% or more.
In this connection, “predominantly consist of” means that the entity in question comprises 55% or more, preferably 60% or more and very preferably 70% or more of the component or components or compound or compounds indicated.
In this connection, “essentially consist of” means that the entity in question comprises 80% or more, preferably 90% or more and very preferably 95% or more of the component or components or compound or compounds indicated.
In this connection, “completely consist of” means that the entity in question comprises 98% or more, preferably 99% or more and very preferably 100.0% of the component or components or compound or compounds indicated.
Other mesogenic compounds which are not explicitly mentioned above can optionally and advantageously also be used in the media in accordance with the present invention. Such compounds are known to the person skilled in the art.
The liquid-crystal media in accordance with the present invention preferably have a clearing point of 90° C. or more, more preferably 100° C. or more, still more preferably 120° C. or more, particularly preferably 150° C. or more and very particularly preferably 170° C. or more.
The nematic phase of the media in accordance with the invention preferably extends at least from 0° C. or less to 90° C. or more, preferably up to 100° C. or more, more preferably at least from −10° C. or less to 100° C. or more, very preferably at least from −20° C. or less to 100° C. or more and in particular at least from −20° C. or less to 110° C. or more.
The Δ∈ of the liquid-crystal medium in accordance with the invention, at 1 kHz and 20° C., is preferably 1 or more, more preferably 2 or more and very preferably 3 or more.
The Δn of the liquid-crystal media in accordance with the present invention, at 589 nm (NaD) and 20° C., is preferably in the range from 0.200 or more to 0.90 or less, more preferably in the range from 0.250 or more to 0.90 or less, even more preferably in the range from 0.300 or more to 0.85 or less and very particularly preferably in the range from 0.350 or more to 0.800 or less.
In a first preferred embodiment of the present application, the Δn of the liquid-crystal media in accordance with the present invention is preferably 0.50 or more, more preferably 0.55 or more.
The total concentration of the compounds of formula T in the LC medium is preferably in the range from 1.0% or more to 40% or less, in case two or more homologues are used, is preferably the concentration of each homologure in this case is in the range from 1.0% or more to 20% or less. In case one homologue is used, the concentration of the compound of formula T in the LC medium is preferably in the range from 1.0% or more to 30% or less.
In accordance with the present invention, the individual compounds of the formula I are preferably used in a total concentration of 10% to 70%, more preferably 20% to 60%, even more preferably 30% to 50% and very preferably 25% to 45% of the mixture as a whole.
The compounds of the formula II are preferably used in a total concentration of 1% to 20%, more preferably 1% to 15%, even more preferably 2% to 15% and very preferably 3% to 10% of the mixture as a whole, unless explicitly stated otherwise.
The compounds of the formula III are preferably used in a total concentration of 1% to 60%, more preferably 5% to 50%, even more preferably 10% to 45% and very preferably 15% to 40% of the mixture as a whole.
The liquid-crystal media preferably comprise, preferably predominantly consist of and very preferably completely consist of in total 50% to 100%, more preferably 70% to 100% and very preferably 80% to 100% and in particular 90% to 100% of the compounds of the formulae T, CC, CP, I, II, III, IV and V, preferably of the formulae T, CC, I, III, IV and V, more preferably of the formulae T, I, II, III, IV and/or VI.
In the present application, the expression dielectrically positive describes compounds or components where Δ∈>3.0, dielectrically neutral describes those where −1.5Δ∈≦3.0 and dielectrically negative describes those where Δ∈<−1.5. Δ∈ is determined at a frequency of 1 kHz and at 20° C. The dielectric anisotropy of the respective compound is determined from the results of a solution of 10% of the respective individual compound in a nematic host mixture. If the solubility of the respective compound in the host mixture is less than 10%, the concentration is reduced to 5%. The capacitances of the test mixtures are determined both in a cell having homeotropic alignment and in a cell having homogeneous alignment. The cell thickness of both types of cells is approximately 20 μm. The voltage applied is a rectangular wave having a frequency of 1 kHz and an effective value of typically 0.5 V to 1.0 V, but it is always selected to be below the capacitive threshold of the respective test mixture.
Δ∈ is defined as (∈∥−∈⊥), while ∈ave, is (∈∥+2 ∈⊥)/3.
The host mixture used for dielectrically positive compounds is mixture ZLI-4792 and that used for dielectrically neutral and dielectrically negative compounds is mixture ZLI-3086, both from Merck KGaA, Germany. The absolute values of the dielectric constants of the compounds are determined from the change in the respective values of the host mixture on addition of the compounds of interest. The values are extrapolated to a concentration of the compounds of interest of 100%.
Components having a nematic phase at the measurement temperature of 20° C. are measured as such, all others are treated like compounds.
The expression threshold voltage in the present application refers to the optical threshold and is quoted for 10% relative contrast (V10), and the expression saturation voltage refers to the optical saturation and is quoted for 90% relative contrast (V90), in both cases unless expressly stated otherwise. The capacitive threshold voltage (V0), also called the Freeder-icks threshold (VFr), is only used if expressly mentioned.
The parameter ranges indicated in this application all include the limit values, unless expressly stated otherwise.
The different upper and lower limit values indicated for various ranges of properties in combination with one another give rise to additional preferred ranges.
Throughout this application, the following conditions and definitions apply, unless expressly stated otherwise. All concentrations are quoted in percent by weight and relate to the respective mixture as a whole, all temperatures are quoted in degrees Celsius and all temperature differences are quoted in differential degrees. All physical properties are determined in accordance with “Merck Liquid Crystals, Physical Properties of Liquid Crystals”, Status November 1997, Merck KGaA, Germany, and are quoted for a temperature of 20° C., unless expressly stated otherwise. The optical anisotropy (Δn) is determined at a wavelength of 589.3 nm. The dielectric anisotropy (Δ∈) is determined at a frequency of 1 kHz. The threshold voltages, as well as all other electro-optical properties, are determined using test cells produced at Merck KGaA, Germany. The test cells for the determination of Δ∈ have a cell thickness of approximately 20 μm. The electrode is a circular ITO electrode having an area of 1.13 cm2 and a guard ring. The orientation layers are SE-1211 from Nissan Chemicals, Japan, for homeotropic orientation (∈∥) and polyimide AL-1054 from Japan Synthetic Rubber, Japan, for homogeneous orientation (∈⊥). The capacitances are determined using a Solatron 1260 frequency response analyser using a sine wave with a voltage of 0.3 Vrms. The light used in the electro-optical measurements is white light. A set-up using a commercially available DMS instrument from Autronic-Melchers, Germany, is used here. The characteristic voltages have been determined under perpendicular observation. The threshold (V10), mid-grey (V50) and saturation (V90) voltages have been determined for 10%, 50% and 90% relative contrast, respectively.
The liquid-crystalline media are investigated with respect to their properties in the microwave frequency range as described in A. Penirschke, S. Müller, P. Scheele, C. Weil, M. Wittek, C. Hock and R. Jakoby: “Cavity Perturbation Method for Characterization of Liquid Crystals up to 35 GHz”, 34th European Microwave Conference—Amsterdam, pp. 545-548.
Compare in this respect also A. Gaebler, F. Golden, S. Müller, A. Penirschke and R. Jakoby “Direct Simulation of Material Permittivites . . . ”, 12MTC 2009—International Instrumentation and Measurement Technology Conference, Singapore, 2009 (IEEE), pp. 463-467, and DE 10 2004 029 429 A, in which a measurement method is likewise described in detail.
The liquid crystal is introduced into a polytetrafluoroethylene (PTFE) capillary. The capillary has an internal radius of 180 μm and an external radius of 350 μm. The effective length is 2.0 cm. The filled capillary is introduced into the centre of the cavity with a resonance frequency of 30 GHz. This cavity has a length of 6.6 mm, a width of 7.1 mm and a height of 3.6 mm. The input signal (source) is then applied, and the result of the output signal is recorded using a commercial vector network analyser.
The change in the resonance frequency and the Q factor between the measurement with the capillary filled with the liquid crystal and the measurement without the capillary filled with the liquid crystal is used to determine the dielectric constant and the loss angle at the corresponding target frequency by means of equations 10 and 11 in A. Penirschke, S. Müller, P. Scheele, C. Weil, M. Wittek, C. Hock and R. Jakoby: “Cavity Perturbation Method for Characterization of Liquid Crystals up to 35 GHz”, 34th European Microwave Conference—Amsterdam, pp. 545-548, as described therein.
The values for the components of the properties perpendicular and parallel to the director of the liquid crystal are obtained by alignment of the liquid crystal in a magnetic field. To this end, the magnetic field of a permanent magnet is used. The strength of the magnetic field is 0.35 tesla. The alignment of the magnets is set correspondingly and then rotated correspondingly through 90°.
Preferred components are phase shifters, varactors, wireless and radio wave antenna arrays, matching circuit adaptive filters and others.
In the present application, the term compounds is taken to mean both one compound and a plurality of compounds, unless expressly stated otherwise.
The liquid-crystal media according to the invention preferably have nematic phases of in each case at least from −20° C. to 80° C., preferably from −30° C. to 85° C. and very particularly preferably from −40° C. to 100° C. The phase particularly preferably extends to 120° C. or more, preferably to 140° C. or more and very particularly preferably to 180° C. or more. The expression have a nematic phase here means on the one hand that no smectic phase and no crystallisation are observed at low temperatures at the corresponding temperature and on the other hand that no clearing occurs on heating from the nematic phase. The investigation at low temperatures is carried out in a flow viscometer at the corresponding temperature and checked by storage in test cells having a layer thickness of 5 μm for at least 100 hours. At high temperatures, the clearing point is measured in capillaries by conventional methods.
Furthermore, the liquid-crystal media according to the invention are characterised by high optical anisotropy values in the visible range, especially at a wavelength of 589.0 nm (i.e. at the Na“D” line). The birefringence at 589 nm is preferably 0.20 or more, particularly preferably 0.25 or more, particularly preferably 0.30 or more, particularly preferably 0.40 or more and very particularly preferably 0.45 or more. In addition, the birefringence is preferably 0.80 or less.
The liquid crystals employed preferably have a positive dielectric anisotropy. This is preferably 2 or more, preferably 4 or more, particularly preferably 6 or more and very particularly preferably 10 or more.
Furthermore, the liquid-crystal media according to the invention are characterised by high anisotropy values in the microwave range. The birefringence at about 8.3 GHz is, for example, preferably 0.14 or more, particularly preferably 0.15 or more, particularly preferably 0.20 or more, particularly preferably 0.25 or more and very particularly preferably 0.30 or more. In addition, the birefringence is preferably 0.80 or less.
The dielectric anisotropy in the microwave range is defined as
Δ∈r≡(∈r,∥−∈r,⊥).
The tuneability (τ) is defined as
τ≡(Δ∈r/∈r,∥).
The material quality (η), also called figure of merit (FoM) is defined as
η≡(τ/tan δ∈r,max), where
the maximum dielectric loss is
tan δ∈r,max=max. {tan δ∈r,⊥,; tan δ∈r,∥}.
The material quality (η) of the preferred liquid-crystal materials is 6 or more, preferably 8 or more, preferably 10 or more, preferably 15 or more, preferably 17 or more, preferably 20 or more, particularly preferably 25 or more and very particularly preferably 30 or more.
In the corresponding components, the preferred liquid-crystal materials have phase shifter qualities of 15°/dB or more, preferably 20°/dB or more, preferably 30°/dB or more, preferably 40°/dB or more, preferably 50°/dB or more, particularly preferably 80°/dB or more and very particularly preferably 100°/dB or more.
In some embodiments, however, liquid crystals having a negative value of the dielectric anisotropy can also advantageously be used.
The concentration of the chiral dopant, respectively the total concentration of the chiral dopants in the LC medium are preferably in the range from 0.05% or more to 5% or less, more preferably from 0.1% or more to 1% or less, and, most preferably from 0.2% or more to 0.8% or less. These preferred concentration ranges apply in particular to the chiral dopant S-2011, respectively to its enantiomeric form R-2011 (both from Merck KGaA) and for chiral dopants having the same or a similar HTP. For Chiral dopants having either a higher or a lower absolute value of the HTP compared to S-2011 these preferred concentrations have to be decreased, respectively increased proportionally according to the ratio of their HTP values relatively to that of S-2011.
The liquid crystals employed are either individual substances or mixtures. They preferably have a nematic phase.
The term “alkyl” preferably encompasses straight-chain and branched alkyl groups having 1 to 15 carbon atoms, in particular the straight-chain groups methyl, ethyl, propyl, butyl, pentyl, hexyl and heptyl. Groups having 2 to 10 carbon atoms are generally preferred.
The term “alkenyl” preferably encompasses straight-chain and branched alkenyl groups having 2 to 15 carbon atoms, in particular the straight-chain groups. Particularly preferred alkenyl groups are C2- to C7-1E-alkenyl, C4- to C7-3E-alkenyl, C5- to C7-4-alkenyl, C6- to C7-5-alkenyl and C7-6-alkenyl, in particular C2- to C7-1E-alkenyl, C4- to C7-3E-alkenyl and C5- to C7-4-alkenyl. Examples of further preferred alkenyl groups are vinyl, 1E-propenyl, 1E-butenyl, 1E-pentenyl, 1E-hexenyl, 1E-heptenyl, 3-butenyl, 3E-pentenyl, 3E-hexenyl, 3E-heptenyl, 4-pentenyl, 4Z-hexenyl, 4E-hexenyl, 4Z-heptenyl, 5-hexenyl, 6-heptenyl and the like. Groups having up to 5 carbon atoms are generally preferred.
The term “fluoroalkyl” preferably encompasses straight-chain groups having a terminal fluorine, i.e. fluoromethyl, 2-fluoroethyl, 3-fluoropropyl, 4-fluorobutyl, 5-fluoropentyl, 6-fluorohexyl and 7-fluoroheptyl. However, other positions of the fluorine are not excluded.
The term “oxaalkyl” or “alkoxyalkyl” preferably encompasses straight-chain radicals of the formula CnH2n+1—O—(CH2)m, in which n and m each, independently of one another, denote 1 to 10. Preferably, n is 1 and m is 1 to 6.
Compounds containing a vinyl end group and compounds containing a methyl end group have low rotational viscosity.
In the present application, both high-frequency technology and hyper-frequency technology denote applications having frequencies in the range from 1 MHz to 1 THz, preferably from 1 GHz to 500 GHz, more preferably 2 GHz to 300 GHz, particularly preferably from about 5 GHz to 150 GHz.
The liquid-crystal media in accordance with the present invention may comprise further additives and chiral dopants in the usual concentrations. The total concentration of these further constituents is in the range from 0% to 10%, preferably 0.1% to 6%, based on the mixture as a whole. The concentrations of the individual compounds used are each preferably in the range from 0.1% to 3%. The concentration of these and similar additives is not taken into consideration when quoting the values and concentration ranges of the liquid-crystal components and liquid-crystal compounds of the liquid-crystal media in this application.
Preferably the media according to the present invention comprise one or more chiral compounds as chiral dopants in order to adjust their cholesteric pitch. Their total concentration in the media according to the instant invention is preferably in the range 0.1% to 15%, more preferably from 1% to 10% and most preferably from 2% to 6%.
Optionally the media according to the present invention may comprise further liquid crystal compounds in order to adjust the physical properties. Such compounds are known to the expert. Their concentration in the media according to the instant invention is preferably 0% to 30%, more preferably 0.1% to 20% and most preferably 1% to 15%.
The response times are given as rise time (τon) for the time for the change of the relative tuning, respectively of the relative contrast for the electo-optiocal response, from 0% to 90% (t90-t0), i.e. including the delay time (t10-t0), as decay time (Toff) for the time for the change of the relative tuning, respectively of the relative contrast for the electo-optiocal response, from 100% back to 10% (t100-t10) and as the total response time (τtotal)=τon+τoff), respectively.
The liquid-crystal media according to the invention consist of a plurality of compounds, preferably 3 to 30, more preferably 4 to 20 and very preferably 4 to 16 compounds. These compounds are mixed in a conventional manner. In general, the desired amount of the compound used in the smaller amount is dissolved in the compound used in the larger amount. If the temperature is above the clearing point of the compound used in the higher concentration, it is particularly easy to observe completion of the dissolution process. It is, however, also possible to prepare the media in other conventional ways, for example using so-called pre-mixes, which can be, for example, homologous or eutectic mixtures of compounds, or using so-called “multibottle” systems, the constituents of which are themselves ready-to-use mixtures.
All temperatures, such as, for example, the melting point T(C,N) or T(C,S), the transition from the smectic (S) to the nematic (N) phase T(S,N) and the clearing point T(N,I) of the liquid crystals, are quoted in degrees Celsius. All temperature differences are quoted in differential degrees.
In the present invention and especially in the following examples, the structures of the mesogenic compounds are indicated by means of abbreviations, also referred to as acronyms. In these acronyms, the chemical formulae are abbreviated as follows using Tables A to C below. All groups CnH2n+1, CmH2m+1 and CoH2o+1 preferably denote straight-chain alkyl in each case having n, m or oC atoms. Table A lists the codes used for the ring elements of the core structures of the compounds, while Table B shows the linking groups. Table C gives the meanings of the codes for the left-hand or right-hand end groups. Table D shows illustrative structures of compounds with their respective abbreviations.
in which n and m each denote integers, and the three dots “ . . . ” are placeholders for other abbreviations from this table.
The following table shows illustrative structures together with their respective abbreviations. These are shown in order to illustrate the meaning of the rules for the abbreviations. They furthermore represent compounds which are preferably used.
In this table the parameters have the following meanings, l m, n and o are all independently of each of the positive integers different from 0, preferably l is 1 or 2, m and n are preferably selected from 1 to 7, and o preferably is selected from 1 to 6, preferably 1 or 2.
The following table, Table E, shows illustrative compounds which can be used as stabiliser in the mesogenic media in accordance with the present invention. The total concentration of these and similar compounds in the media is preferably 5% or less.
In a preferred embodiment of the present invention, the mesogenic media comprise one or more compounds selected from the group of the compounds from Table E.
The following table, Table F, shows illustrative compounds which can preferably be used as chiral dopants in the mesogenic media in accordance with the present invention.
In a preferred embodiment of the present invention, the mesogenic media comprise one or more compounds selected from the group of the compounds from Table F.
The mesogenic media in accordance with the present application preferably comprise two or more, preferably four or more, compounds selected from the group consisting of the compounds from the above tables.
The liquid-crystal media in accordance with the present invention preferably comprise
The following examples illustrate the present invention without limiting it in any way.
However, it is clear to the person skilled in the art from the physical properties what properties can be achieved and in what ranges they can be modified. In particular, the combination of the various properties which can preferably be achieved is thus well defined for the person skilled in the art.
A liquid-crystal mixture C-1 having the composition and properties as indicated in the following table is prepared and characterized with respect to its general physical properties and its applicability in microwave components at 19 GHz.
This mixture is suitable for applications in the microwave range, in particular for phase shifters or LC based antenna elements in the micro wave (MW) region. In comparison to the Example this mixture clearly exhibits inferior properties. In particular, it is not very stable against storage or deep temperatures.
A liquid-crystal mixture M-1 having the composition and properties as indicated in the following table is prepared.
This mixture is very highly suitable for applications in the microwave range, in particular for phase shifters or LC based antenna elements in the micro wave (MW) region.
| Number | Date | Country | Kind |
|---|---|---|---|
| 14004455.3 | Dec 2014 | EP | regional |