Liquid-crystalline mixtures, in particular ferroelectric liquid-crystalline mixtures

Ferroelectric liquid crystals have recently attracted interest as a display medium in electrooptical assemblies (for example Lagerwall et al., "Ferroelectric Liquid Crystals for Displays", SID Symposium, October Meeting 1985, San Diego, Calif. USA).
For practical use of ferroelectric liquid crystals in electrooptical displays, chiral, tilted, smectic phases, such as S.sub.c phases, are required (R. B. Meyer, L. Liebert, L. Strzelecki and P. Keller, J. Physique 36, L-69 (1975).vertline., which are stable over a broad temperature range. This aim can be achieved by means of compounds which themselves form such phases, for example S.sub.c phases, or, however, by doping compounds which form non-chiral, tilted, smectic phases, with optically active compounds (M. Brunet, C. Williams, Ann. Phys. 3, 237 (1978).vertline..
Furthermore, a unitary planar orientation of the liquid crystals is necessary in order to achieve a high contrast ratio when ferroelectric liquid-crystal mixtures are used in electrooptical assemblies. It has been shown that a unitary planar orientation in the S.sub.c phase can be achieved if the phase sequence of the liquid-crystal mixture with decreasing temperature is as follows:
Isotropic T nematic T smectic A T smectic C.
(for example K. Flatischler et al., Mol. Cryst. Liq. Cryst. 131, 21 (1985); T. Matsumoto et al., p. 468-470, Proc. of the 6th Int. Display Research Conf., Japan Display, 30 Sep. - 2 Oct. 1986, Tokyo, Japan; M. Murakami et al., ibid., p. 344-347).
For ferroelectric (chiral smectic) liquid-crystal mixtures, the condition that the pitch of the helix must be large, i.e. greater than 5 .mu.m, in the S.sub.c * phase and must be very large, i.e. greater than 10 .mu.m or infinite, in the N* phase must additionally be fulfilled.
The optical switching time .tau.[.mu.s] of ferroelectric liquid-crystal systems, which should be as short as possible, depends on the rotation viscosity of the system .gamma.[mPas], the spontaneous polarization P.sub.s [nC/cm.sup.2 ] and the electric field strength E[V/m], in accordance with the equation ##EQU1## Since the field strength E is determined by the electrode separation in the electrooptical assembly and by the applied voltage, the ferroelectric display medium must have low viscosity and high spontaneous polarization in order that a short switching time is achieved.
Finally, besides thermal, chemical and photochemical stability, a small optical anisotropy .DELTA.n, preferably <0.13, and a small positive or, preferably, negative dielectric anisotropy .DELTA..epsilon. are required. (S. T. Lagerwall et al., "Ferroelectric Liquid Crystals for Displays" SID Symposium, Oct. Meeting 1985, San Diego, Calif., USA).
It is only possible to satisfy all these demands using mixtures comprising several components. The basis (or matrix) used here is preferably compounds which if possible themselves already have the desired phase sequence I.fwdarw.N.fwdarw.S.sub.1 .fwdarw.S.sub.c. Further components of the mixture are often added to reduce the melting point and to broaden the S.sub.c and usually also the N phase, to induce optical activity, for pitch compensation and to match the optical and dielectric anisotropy; however, the rotation viscosity, for example, should if possible not be increased at the same time.
It is known that certain derivatives of phenylpyrimidine, in particular 5-alkyl-2(4-alkoxyphenyl)pyrimidines, are capable of forming S.sub.c, S.sub.A and N phases (D. Demus and H. Zaschke, "Flussige Kristalle in Tabellen", [Liquid Crystals in Tables], VEB Deutscher Verlag fur Grundstoffindustrie, Leipzig 1974, pp. 260-261) and, in addition, can be converted into ferroelectric liquid-crystal mixtures by addition of optically active dopes [L. M. Blinov et al., Sow. Phys. lisp. 27 (7), 492 (1984); L. A. Beresnew et al., Ferroelectrics, 59 (321]/1 (1984), presented at the 5th Conference of Soc. Countries on Liquid Crystals, Odessa, USSR, Oct. 1983; DE-A-3,515,347, EP-A 0,206,228 and EP-A 0,225,195].
It is furthermore known that lower melting points and a broadening of the liquid-crystalline phases desired can be achieved by mixing several liquid-crystalline compounds [D. Demus et al., Mol. Cryst. Liq. Cryst. 25, 215 (1974), J. W. Goodby, Ferroelectrics 49, 275 (1983)], and that the melting-point depression is the more pronounced the more the mixture components also differ structurally. (J. S. Dave et al., J. Chem. Soc. 1955, 4305). It was thus to be presumed that particularly low mixture melting points, and thus low phase-transition points of the S.sub.c phase, are obtained when compounds are mixed which, on the one hand, are significantly different structurally, but, on the other hand, are sufficiently similar to be readily miscible.
DE-C 2,257,588 discloses a 5-butoxy-2(4-pentoxyphenyl)-pyrimidine, but this only forms a nematic phase.
In DE 3,831,226.3, it has been found that, as the base component, compounds of the type 5-alkoxy-2(4-alkoxyphenyl)pyrimidines of the general formula (I) ##STR2## in which C.sub.n H.sub.2n+1 and C.sub.x H.sub.2x+1 are straight-chain alkyl radicals in which n is an integer from 6 to 14 and x is an integer f rom 2 to 14, are particularly highly suitable [lacuna] the matrix (base) for liquid-crystalline mixtures, in particular ferroelectric liquid-crystalline mixtures; of them, at least two different compounds a' and a" are present in the mixture. For the most part, they exhibit the desired phase sequence ITNTS.sub.A TS.sub.c with decreasing temperature. Compared with the known 5-alkyl-2-(4-alkoxyphenyl)pyrimidines, they have considerably broader S.sub.c phases and higher transition temperatures of the S.sub.c TS.sub.A transition. In addition, the S.sub.c phase is even formed in the case of a lower number of carbon atoms in the alkyl(oxy) chains, for example even when n =8 and x 2 or n =6 and x 6. Compared with the known 5-alkyl-2-(4-alkoxyphenyl)pyrimidines, this gives a greater choice of homologous, readily miscible compounds having S.sub.c phases for preparing the mixture. Due to their higher phase-transition temperatures S.sub.A to S.sub.c (for example 70.degree. to 90.degree. C.) and their broader S.sub.c phases, they also make it possible to prepare mixtures having very broad S.sub.c phases (for example up to about 68.degree. C.) and high transition temperatures S.sub.A /S.sub.c.
The mixtures of DE 3,831,226.3 of compounds of the formula (I) are already very highly suitable as a matrix for ferroelectric liquid-crystalline mixtures. However, they also have a large optical anisotropy (.DELTA.n) and a large positive dielectric anisotropy (.DELTA..epsilon.). In addition, the nematic phase, depending on the chain length n or x of the substituents, is still narrow.
By adding at least one compound (cyclohexanecarboxylate) of the general formula (II), i.e. a compound of type b, ##STR3## the parameters [.DELTA.n] and [.DELTA..epsilon.] can simultaneously be optimized and the width of the nematic phase can be matched to practical requirements.
In the general formula (II):
R.sup.1 is an alkyl chain having 10 to 16 carbon atoms or an alkoxy chain having 8 to 14 carbon atoms, and R.sup.2 is an alkyl chain having 2 to 9 carbon atoms. These compounds are described in DE-A 3,731,639. They develop their favorable action even when added in amounts from about 2 mol %, relative to the mixture of the components of type a and b. When added in amounts from about 10 and up to about 40 mol %, the nematic phase is broadened by about 8 to 18.degree. C. and the smectic phase by about 6.degree. to 15.degree. C. In addition, it is very advantageous that the addition only insignificantly increases the rotation viscosity of the base mixture according to the invention, which is already very low per se.
The melting point and the lower phase-transition temperature of the S.sub.c phase of the mixtures can be reduced, if they are too high, by adding at least one compound (alkenyloxyphenylpyrimidine derivative) of the general formula (III), i.e. a compound of type c, to mixtures of compounds of type a alone or additionally containing compounds of type b: ##STR4##
In the general formula (III), R.sup.3 is a branched or straight-chain alkyl radical having 7 to 16 carbon atoms or a straight-chain or branched alkoxy radical having 6 to 14 carbon atoms, and y is an integer f rom 4 to 14. These compounds are described in DE-A 3,731,638. Added amounts of from about 10 to 35 mol %, relative to the overall mixture, reduce the lower temperature limit of the S.sub.c phase by up to 5.degree. C. The other favorable physical properties of the mixtures are generally not impaired by this addition.
To reduce the melting point and the lower temperature limit of the S.sub.c phase, it is also possible to add, together with or in place of compounds of type c, other compounds of the formula (IV), i.e. of type d, ##STR5## where m and p, independently of one another, are integers from 6 to 14. When amounts of from about 10 to 25 mol % of the compound of type d or mixtures with compounds of type c, relative to the overall mixture, are added to mixtures of compounds of type a or a and b, the lower temperature limit of the S.sub.c phase is reduced by up to 10.degree. C.
Some of these components, and also certain mixtures, are already known from the prior art. However, since the development, in particular of ferroelectric liquid-crystal mixtures, can in no way be regarded as complete, the manufacturers of display elements are interested in a very wide variety of mixtures. A further reason for this, amongst others, is that conclusions on the quality of the liquid-crystalline mixtures too can only be made by considering the interactions of the liquid-crystalline mixtures with the individual assemblies of the display elements or of the cells (for example the orientation layer).
The object of the present invention is therefore to provide compositions of suitable components for liquid-crystalline base mixtures, but also for ferroelectric liquid-crystalline mixtures, which satisfy as many as possible of the abovementioned criteria, have, in particular, a low melting point and furthermore result in improved contrast in a display.
The invention relates to the liquid-crystalline base mixtures characterized below, which contain, on the one hand, compounds A from DE 3,831,226.3, but, on the other hand, also contain at least one carboxylate C of the general formula (V), (VI), (VII), (VIII) or (IX) as a mixture component.
The invention furthermore relates to liquid-crystalline mixtures having favorable values for the optical anisotropy and the dielectric anisotropy and having a broad nematic phase which is sufficient for practical use.
A preferred subject-matter of the invention are likewise ferroelectric liquid-crystalline mixtures having a short switching time, the phase sequence I.fwdarw.N*.fwdarw.S.sub.A, S.sub.c *, the pitch in the nematic phase being >15 .mu.m and in the S.sub.c * phase being >5 .mu.m, and having a negative .DELTA..epsilon. and .DELTA.n<0.15, and which contain a chiral dope C in addition to the components A and the carboxylates B.
The novel invention relates to liquid-crystalline mixtures containing, as component A, at least two 5-alkoxy-2-(alkoxyphenyl)pyrimidines of the general formula (I) ##STR6## in which the alkyl radicals are straight-chain alkyl radicals in which n is an integer from 6 to 14 and x is an integer from 2 to 14, and, if appropriate, one or more cyclohexanecarboxylates of the general formula (II) ##STR7## in which R.sup.1 is an alkyl radical having 10 to 16 carbon atoms or an alkoxy radical having 8 to 14 carbon atoms, and R.sup.2 is an alkyl radical having 2 to 9 carbon atoms, and, if appropriate, one or more alkenyloxyphenylpyrimidine derivatives of the general formula (III) ##STR8## in which R.sup.3 is an alkyl chain having 7 to 16 carbon atoms or an alkoxy chain having 6 to 14 carbon atoms, and y is an integer from 4 to 14, and, if appropriate, one or more alkylpyrimidinealkoxyphenyl derivatives of the general formula (IV) ##STR9## in which m and p, independently of one another, are integers from 6 to 14, and if appropriate as component B (for ferroelectric liquid-crystal mixtures), at least one optically active compound from the group
a) optically active esters made from .alpha.-chlorocarboxylic acids and mesogenic phenols,
b) optically active esters of N-acylproline,
c) optically active esters of 1,3-dioxolane-4-carboxylic acids, and
d) optically active esters of oxirane-2-carboxylic acids,
wherein the liquid-crystal mixtures furthermore contain at least one carboxylate of the general formula (V), (VI), (VII), (VIII) or (IX) as a mixture component: ##STR10## where k may be an integer from 6 to 14, and
l may be an integer from 2 to 14, ##STR11## where m may be an integer from 5 to 14, and
l may be an integer from 2 to 14, ##STR12## where p may be an integer from 7 to 14, and
r may be an integer from 4 to 14, ##STR13## where s may be an integer from 6 to 14, and
t may e an integer from 6 to 14, ##STR14## where R.sup.2 is straight-chain or branched (C.sub.1 -C.sub.12)alkyl or alkenyl, it being possible for one or two non-adjacent CH.sub.2 groups to be replaced by O and/or S atoms,
Y is F, Cl, Br, CN or CF.sub.3 and
R.sup.1 is branched (C.sub.3 -C.sub.9)alkyl, benzyl or phenyl.
Preferred liquid-crystal mixtures are those which contain, as component C, at least one 4-(5-alkylpyrimidin-2-yl)phenyl carboxylate of the general formula (V) ##STR15## where k may be an integer from 6 to 14, and
l may be an integer from 4 to 14.
Likewise preferred mixtures are those which contain, as component C, at least one 4-(5-alkoxypyrimidin-2-yl)-phenyl carboxylate of the general structure (VI) ##STR16## where m may be an integer from 6 to 14, and
l may be an integer from 4 to 14.
Preferred liquid-crystalline mixtures are also those which contain, as component C, at least one benzoate of the general structure (VII) ##STR17## where p may be an integer from 7 to 14, and
r may be an integer from 4 to 14.
Likewise preferred mixtures are those which contain, as component C, at least one benzoate of the general structure (VIII) ##STR18## where s may be an integer from 6 to 14, and
t may be an integer from 6 to 14.
In addition, preferred mixtures are those which contain, at least as one component, a racemate of the structure (IX) ##STR19## where R.sup.2 is straight-chain or branched (C.sub.1 -C.sub.12)alkyl or alkenyl, it being possible for one or two non-adjacent CH.sub.2 groups to be replaced by O and/or S atoms,
Y is F, Cl or CF.sub.3 and
R.sup.1 is branched (C.sub.3 -C.sub.9)alkyl, benzyl or phenyl.
Particularly preferred liquid-crystal mixtures are those which contain, as component C, the racemate of at least one .alpha.-halocarboxylate of the structure (IXa) ##STR20## where R.sup.2 may be an alkyl radical or an alkenyl radical having 1 to 12 carbon atoms whose CH.sub.2 group bonded to the aromatic rings may also be replaced by O and/or [lacuna], and y is F or Cl.
Very particularly suitable here are the .alpha.-halocarboxylic acids of the structures (IXb) and (IXc) ##STR21##
It has now been found that the FLC mixtures according to the invention which contain, as component C, 2 to 25 mol-%, in particular 10 to 25 mol-%, of mixtures of individual compounds of the general structures (V) and/or (VI) and/or (VIII) and/or (VIII) and/or (IX) have an upper phase-transition point which is up to 10.degree. C. lower than the corresponding mixtures without the components according to the invention.
Furthermore, the contrast is increased by up to 10% and, in some cases, the switching times are also reduced by the addition.
Through the specific addition of the abovementioned compounds of the formulae (V to IX), the physical parameters [.DELTA.n] and [.DELTA..epsilon.] of the mixture can be optimized, i.e. matched to the particular specific requirements of the display element.
Surprisingly, it has furthermore been observed that liquid-crystalline mixtures which contain 2 to 15 mol-% of racemic mixtures of one or more esters of the general structure (IX) have a melting point which is lower by up to 5.degree. C. and an upper S.sub.c phase transition point which is lower by up to 10.degree. C. than the corresponding base mixture without this (these) component(s). The contrast of the mixtures according to the invention is up to 20% higher than that of the base mixtures. Doping with a racemic mixture of the .alpha.-chlorocarboxylate (IXb) ##STR22## has proven particularly suitable here.
The liquid-crystal mixtures according to the invention are suitable both as base mixtures and, when chiral dopes B are added, as novel ferroelectric liquid-crystal mixtures which are particularly suitable for practical use in electrooptical switching and display elements.
As already proposed (DE 3,831,226.3), the following dopes have proven particularly suitable for the purpose of the invention:
a) optically active esters made from .alpha.-chlorocarboxylic acids and mesogenic phenols as in DE-A 3,703,228, and, in particular, the optically active ester of the formula below ##STR23## where r=4 to 8 b) optically active esters of N-acylproline as in DE-A 3,644,522
c) optically active esters of 1,3-dioxolane-4-carboxylic acids as in DE-A 3,713,273
d) optically active esters of oxirane-2-carboxylic acids as in DE-A 3,718,174.
These dopes frequently induce ferroelectric behavior even when added in small amounts from 0.5 and in particular from 3 mol-%, relative to the overall mixture. The upper limit for the amount added is 30 mol-%.
The addition of these dopes generally further reduces the melting point and the lower temperature limit of the S.sub.c * phase. In addition, depending on the nature and amount of the dope, the upper temperature limit of the S.sub.c * phase may be reduced or increased and the width of the N* phase may be changed, which should be taken into account when preparing the matrix mixture. As is known, the optically active dope induces helical twisting in the S.sub.c phase and in the N phase, which converts these phases into the S.sub.c * phase and N* phase respectively. The pitch and the rotation sense of these helices in the N* phase depend on the nature and amount of the optically active dope. They must frequently be compensated by adding a further dope which induces a helix with the opposed rotation sense. In general, a ferroelectric liquid-crystal mixture should have a helix with a pitch of greater than 10 .mu.m in the N* phase and of at least 5 .mu.m in the S.sub.c * phase. The compounds used for compensation of the pitch should preferably not induce in the mixture any spontaneous polarization or should only do so to a negligibly small extent, or should induce a spontaneous polarization with the same sign as the optically active dope.
If pitch compensation is necessary, the following combinations are particularly suitable in the mixtures according to the invention:
a.sub.1) Optically active .alpha.-chlorocarboxylates induce a negative P.sub.s and a helix with negative rotation sense. For compensation, derivatives of citronellol of the general formula (N) are advantageously added ##STR24##
In this formula, q is an integer from 6 to 16, A is an oxygen atom or a chemical bond, and B is a pyrimidine-2,5-diyl ring, it being possible for the phenylene ring bonded thereto to be in the 2- or 5-position. For pitch compensation, up to 4 mol %, relative to the overall mixture, or one mole of citronellol derivative are required per 7 to 13 moles of .alpha.-chlorocarboxylate.
b.sub.1) Optically active N-acylproline esters having the S configuration at the asymmetric carbon atom which induce a positive P.sub.s and a negative pitch in the mixtures according to the invention can be compensated by adding optically active oxirane-2-carboxylates as in DE-A 3,718,174 having a positive P.sub.s and, in particular, a 2-R-3-R configuration. The amount to be added is up to 6 mol %, relative to the overall mixture or 1 mole of oxirane-2-carboxylate per 5 to 9 moles of N-acylproline ester.
c.sub.1) The compensation in the case of optically active 1,3-dioxolane-4-carboxylates having the R configuration, which likewise induce a positive P.sub.s and a negative pitch, is likewise expediently carried out as described under b,) using oxirane-2-carboxylates.
The use of oxirane-2-carboxylates as described in b.sub.1) and c.sub.1) has the additional advantage that these compounds themselves induce a very high positive P.sub.s and thus increase the P.sub.s of the overall mixture and shorten the switching time.
The values of spontaneous polarization P.sub.s [nC /CM.sup.2 ], the contrast K, the optical switching time .tau. [.mu.s], the dielectric anisotropy .DELTA..epsilon. and the optical anisotropy .DELTA.n were determined for the ready-to-use ferroelectric liquid-crystal mixtures (all measurements at 25.degree. C.).
The P.sub.s values are measured by the method of H. Diamant et al. (Rev. Sci. Instr., 28, 30, 1957), where measurement cells with an electrode separation of 2 .mu.m and ground polyamide as the orientation layer are used.
To determine .tau. and K, the measurement cell is clamped between crossed analyzer and polarizer on the rotary stage of a polarizing microscope.
To determine the contrast (K), the measurement cell is positioned, by rotation, so that a photodiode indicates minimum light transmission (dark state). The microscope illumination is adjusted so that the photodiode indicates the same light intensity for all cells. After a switching operation, the light intensity changes (bright state), and the contrast is calculated from the ratio of the light intensities in these states.
The switching time .tau. is determined using a photodiode by measuring the time taken for the light signal to increase from a signal height of 10 to 90 %. The switching voltage comprises rectangular pulses and is +10 V/.mu.m.
The phase-transition temperatures are determined using a polarizing microscope from the texture changes on heating. By contrast, the melting point is determined using a DSC instrument. The phase-transition temperatures between the phases
______________________________________Nematic (N or N*)Smectic-C (S.sub.c or S.sub.c *)Smectic-A (S.sub.A or S.sub.A *)Crystalline (X)______________________________________
are given in .degree.C., and the values are between the phase symbols in the phase sequence.

Example 1
a) a liquid-crystalline mixture comprising the following eight components
______________________________________5-octoxy-2-(4-hexoxyphenyl)pyrimidine 14 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 5 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 15 mol-%5-octoxy-2-(4-decoxyphenyl)pyrimidine 8 mol-%5-octoxy-2-(4-dodecoxyphenyl)pyrimidine 8 mol-%5-octyl-2-(4-decoxyphenyl)pyrimidine 13 mol-%[4-(5-decylpyrimidin-2-yl)]phenyl trans- 17 mol-%4-pentylcyclohexanecarboxylate ##STR25##[4-(5'-octylpyrimidin-2-yl)]phenyl 20 mol-%heptanoate (= compound of the general formula V)exhibits the following liquid-crystalline phaseranges:X -5 S.sub.c 71 S.sub.A 78 N 93 I______________________________________
b) The following mixture, which is claimed in DE 3,831,226.3 and differs from the mixture 1a only in that it contains no component of the general formula V, is suitable for comparing the physical properties. This mixture comprising seven components has the following liquid-crystalline phase ranges:
______________________________________X -1 S.sub.c 81 S.sub.A 87 N 103 I______________________________________
Compared with the mixture 1b, the mixture 1a according to the invention has a melting point (X) which is lower by 4.degree. C. and an upper S.sub.c phase-range limiting temperature which is lower by 10.degree. C.
Example 2
a) A liquid-crystalline mixture comprising the following eight components
______________________________________5-octoxy-2-(4-hexoxyphenyl)pyrimidine 16 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 6 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 15 mol-%5-octoxy-2-(4-decoxyphenyl)pyrimidine 8 mol-%5-octoxy-2-(4-dodecoxyphenyl)pyrimidine 8 mol-%5-octyl-2-(4-dodecoxyphenyl)pyrimidine 13 mol-%[4-(5-decylpyrimidin-2-yl)]phenyl trans- 19 mol-%4-pentylcyclohexanecarboxylate ##STR26##[4-(5'-octylpyrimidin-2-yl)]phenyl 15 mol-%heptanoate (= compound of the general formula V)exhibits the following liquid-crystalline phaseranges:X -5 S.sub.c 75 S.sub.A 80 N 87 I______________________________________
b) The following mixture, which is claimed in DE 3,831,226.3 and differs from the mixture 2a only in that it contains no component of the general formula V, is suitable for comparing the physical properties.
This mixture comprising seven components has the following liquid-crystalline phase ranges:
______________________________________X -2 S.sub.c 81 S.sub.A 86 N 104 I______________________________________
Compared with the mixture 2b, the mixture 2a according to the invention has a melting point which is lower by 3.degree. C. and an upper S.sub.c phase-range limiting temperature which is lower by 6.degree. C.
Example 3
a) A liquid-crystalline mixture comprising the following eight components
______________________________________5-octoxy-2-(4-decoxyphenyl)pyrimidine 15 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 6 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 15 mol-%5-octoxy-2-(4-decoxyphenyl)pyrimidine 8 mol-%5-octoxy-2-(4-dodecoxyphenyl)pyrimidine 8 mol-%5-octyl-2-(4-dodecoxyphenyl)pyrimidine 14 mol-%[4-(5-decylpyrimidin-2-yl)]phenyl trans- 14 mol-%4-pentylcyclohexanecarboxylate ##STR27##[4-(5-octylpyrimidin-2-yl)]phenyl 20 mol-%heptanoate (= compound of the general formula V)exhibits the following liquid-crystalline phaseranges:X -3.5 S.sub.C 69 S.sub.A 80 N 92 I______________________________________
b) The following mixture, which is claimed in DE 3,831,226.3 and differs from the mixture 3a only in that it contains no component of the general formula V, is suitable for comparing the physical properties.
This mixture comprising seven components has the following liquid-crystalline phase ranges:
______________________________________X 0 S.sub.c 80 S.sub.A 88 N 102 I______________________________________
In comparison, the mixture 3a according to the invention has a melting point which is 3.5.degree. C. lower and an upper S.sub.c phase-range limiting temperature which is 11.degree. C. lower.
Example 4
a) A liquid-crystalline mixture comprising the following eight components
______________________________________5-octoxy-2-(4-hexoxyphenyl)pyrimidine 16 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 6 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 16 mol-%5-octoxy-2-(4-decoxyphenyl)pyrimidine 8 mol-%5-octoxy-2-(4-dodecoxyphenyl)pyrimidine 8 mol-%5-octyl-2-(4-dodecoxyphenyl)pyrimidine 14 mol-%[4-(5-decylpyrimidin-2-yl)]phenyl trans- 22 mol-%4-pentylcyclohexanecarboxylate ##STR28##4-(5-decylpyrimidin-2-yl)phenyl 10 mol-%dodecanoate (= compound of the general formula V)exhibits the following liquid-crystalline phaseranges:X -5.5 S.sub.c 79 S.sub.A 84 N 94 I______________________________________
b) The following mixture, which is claimed in DE 3,831,226.3 and differs from the mixture 4a only in that it contains no component of the general formula V, is suitable for comparing the physical properties.
This mixture comprising seven components has the following liquid-crystalline phase ranges:
______________________________________X -2 S.sub.c 81 S.sub.A 86 N 104 I______________________________________
In comparison, the mixture 4a according to the invention has a melting point which is 3.5.degree. C. lower and an upper S.sub.c phase-range limiting temperature which is 2.degree. C. lower.
Example 5
a) A liquid-crystalline mixture comprising the following nine components
______________________________________5-octoxy-2-(4-decoxyphenyl)pyrimidine 7.5 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 4 mol-%5-octoxy-2-(4-hexoxyphenyl)pyrimidine 9 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 9.5 mol-%5-octyl-2-(4-decoxyphenyl)pyrimidine 9.5 mol-%5-octyl-2-(4-hexoxyphenyl)pyrimidine 14 mol-%5-octyl-2-(4-octoxyphenyl)pyrimidine 13 mol-%[4-(5-decylpyrimidin-2-yl)]phenyl trans- 28.5 mol-%4-pentylcyclohexanecarboxylate ##STR29##4-(5-octylpyrimidin-2-yl)phenyl 5 mol-%decanoate (= compound of the general formula V)exhibits the following liquid-crystalline phaseranges:X -3 S.sub.c 68 N 94 I______________________________________
b) A comparable mixture which differs from the mixture 5a only in that it contains no component of the general formula V has the following liquid-crystalline phase ranges:
______________________________________X -2 S.sub.c 80 N 99 IThe addition of the component of the generalformula V has thus resulted in a reduction of themelting point by 1.degree. C.______________________________________
Example 6
a) A liquid-crystalline mixture comprising the following eight components
______________________________________5-octoxy-2-(4-hexoxyphenyl)pyrimidine 16 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 6 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 15 mol-%5-octoxy-2-(4-decoxyphenyl)pyrimidine 8 mol-%5-octoxy-2-(4-dodecoxyphenyl)pyrimidine 8 mol-%5-octyl-2-(4-dodecoxyphenyl)pyrimidine 13 mol-%[4-(5-decylpyrimidin-2-yl)]phenyl trans- 19 mol-%4-pentylcyclohexanecarboxylate ##STR30##4-(5-octylpyrimidin-2-yl)phenyl 15 mol-%undecanoate (= compound of the general formula V)exhibits the following liquid-crystalline phaseranges:X -5 S.sub.c 75 S.sub.A 80 N 87 I______________________________________
b) The following mixture, which is claimed in DE 3,831,226.3 and differs from the mixture 6a only in that it contains no component of the general formula V, is suitable for comparing the physical properties.
This mixture comprising seven components has the following liquid-crystalline phase ranges:
______________________________________X -2 S.sub.c 81 S.sub.A 86 N 104 I______________________________________
In comparison, the mixture 6a according to the invention has a melting point which is 3.degree. C. lower and an upper S.sub.c phase-range limiting temperature which is 6.degree. C. lower.
Example 7
The following ferroelectric mixtures comprising the following components ##STR31##
In Table 1 below, the property features of the examples are reproduced in a summarized form.
TABLE 1__________________________________________________________________________Concentration Switching time Polarization Phase-transition temperatures X Y Contrast .tau. P.sub.s X.fwdarw.S.sub.c * S.sub.c *.fwdarw.S.sub.A * S.sub.A *.fwdarw.N* N*.fwdarw.IExample Mol % Mol % K .mu.s nC .multidot. cm.sup.-2 .degree.C. .degree.C. .degree.C. .degree.C.__________________________________________________________________________7a 94 0 6.4 75 -10 -1 80 85 997b 79 15 4.6 65 -10.5 -8 73 79 92__________________________________________________________________________ The results in columns 5 and 7 show very clearly the improvement in the switching time by 10 .mu.s and in the melting point by 7.degree. C. with increased concentration of the compound of the general formula V.
Example 8
a) A ferroelectric mixture comprising the following components
__________________________________________________________________________mixture from Example 2a 94 mol-% ##STR32## 6 mol-%4-[2-((S)-7-methylnonoxy)pyrimidin-5-yl]phenyl (2S,3S)-2-chloro-3-methylpentanoateexhibits the following LC rangesX -9 S.sub.c * 72 S.sub.A * 78 N* 93 I__________________________________________________________________________
At 25.degree. C., this mixture has a polarization of -9 nC.cm.sup.-2 and, in a switching field of 10 V.mu.m.sup.-1, a switching time of 55 .mu.s.
For comparison, a mixture based on the base mixture of Example 2b is suitable.
b) The ferroelectric mixture comprising
__________________________________________________________________________mixture from Example 2b 94 mol-% ##STR33## 6 mol-%4-[2-((S)-7-methylnonoxy)pyrimidin-5-yl]phenyl (2S,3S)-2-chloro-3-methylpentanoateexhibits the following liquid-crystalline phase ranges:X -7 S.sub.c 79 S.sub.A 84 N 99 I__________________________________________________________________________
At 25.degree. C., this mixture has a spontaneous polarization of -9 nC cm.sup.-2, a contrast of 5.6 and, in a switching field of 10 V.mu.m.sup.-1, a switching time of 60 .mu.s.
Compared with the mixture 9a, this mixture contains no component of the general formula VI and, in comparison, has a melting point which is 2.degree. C. higher and a switching time which is 5 .mu.s longer.
Example 9
A ferroelectric mixture comprising the following four components
__________________________________________________________________________mixture from Example 2b 64 mol-% ##STR34## 15 mol-%4-(decylpyrimidin-2-yl)phenyl nonanoate (compound of the general formulaV) ##STR35## 15 mol-%4-(5-decylpyrimidin-2-yl)phenyl undecanoate (compound of the generalformula V) ##STR36## 6 mol-%4-[2-(S)-7-methylnonoxypyrimidin-5-yl] phenyl(2S,3S)-2-chloro-3-methylpentanoateexhibits the following liquid-crystalline phase ranges:X -11 S.sub. c * 75 S.sub.A * 90 N* 85 I__________________________________________________________________________
At 25.degree. C., this mixture has a polarization of -8.7 nC cm.sup.-2 a contrast of 6.6 [lacuna] in a switching field of 10 V.mu.m.sup.-1, a switching time of 50 .mu.s.
Compared with the mixture 8b, which differs from the mixture 9 only in that it contains no compound of the general formula V, the mixture 9 has a contrast which is higher by 18%, a melting point which is lower by 4.degree. C. and a switching time which is shorter by 10 .mu.s.
Example 10
A ferroelectric mixture comprising the following components
__________________________________________________________________________mixture from Example 2a 89 mol-% ##STR37## 5 mol-%4-(2-nonoxypyrimidin-5-yl)phenyl2-chloro-4-methyl-pentanoate (racemate)(compound of the general formula IX) ##STR38## 6 mol-%4-(2-nonoxypyrimidin-5-yl)phenyl(2S,3S)-2-chloro-3-methylpentanoatehas the phase sequenceX -9 S.sub.c * 72 S.sub.A * 77 N* 88 I__________________________________________________________________________
At 25.degree. C., this mixture has a polarization of -8.7 nC cm.sup.-2, a contrast of 8 and, in a switching field of 10 V.mu.m.sup.-1, a switching time of 60 .mu.s.
Compared with the ferroelectric mixture of Example 7b, the contrast is 45% higher. The addition of the racemic .alpha.-chlorocarboxylate thus results in an increase in the contrast and a reduction in the melting point by 1.degree. C.
Example 11
a) A ferroelectric mixture comprising the following components
__________________________________________________________________________mixture from Example 3a 88 mol-% ##STR39## 12 mol-%4-(2-nonoxypyrimidin-5-yl)phenyl(2S,3S)-2-chloro-3-methylpentanoatehas the phase sequenceX -7 S.sub.c * 68 S.sub.A * 74 N* 85 I__________________________________________________________________________
At 25.degree. C., this mixture has a polarization of -20n C cm.sup.-2 [sic], a contrast of 8.2 and, in a switching field of 10V.mu.m.sup.-1, a switching time of 18 .mu.s.
b) A ferroelectric mixture comprising
__________________________________________________________________________mixture from Example 3a 85 mol-% ##STR40## 12 mol-%4-(2-nonoxypyrimidin-5-yl)phenyl(2S,3S)-2-chloro-3-methylpentanoate ##STR41## 3 mol-%4-(2-nonoxypyrimidin-5-yl)phenyl 2-chloro-4-methyl-pentanoate (racemate)__________________________________________________________________________
has the phase sequence
______________________________________X -8 S.sub.c * 68 S.sub.A * 75 N* 85.5 I______________________________________
At 25.degree. C., this mixture has a polarization of -20 nC cm.sup.-2, a contrast of 8.9 and, in a switching field of 10 V.mu.m.sup.-1, a switching time of 17 .mu.s. Compared with the ferroelectric mixture in Example 11a, the contrast is higher. The addition of the racemic .alpha.-chlorocarboxylate thus results in an increase in the contrast by 9%.
Examples 12a-c
The following ferroelectric mixtures comprising the following components ##STR42##
In Table 2 below, the property features (at 25.degree. C.) of the examples have been summarized.
TABLE 2__________________________________________________________________________Concentration Switching time Polarization Phase-transition temperatures X Y Contrast .tau. P.sub.s X.fwdarw.S.sub.c * S.sub.c *.fwdarw.S.sub.A * S.sub.A *.fwdarw.N* N*.fwdarw.IExample Mol % Mol % K .mu.s nC .multidot. cm.sup.-2 .degree.C. .degree.C. .degree.C. .degree.C.__________________________________________________________________________12a 94 0 4.5 43 -9.8 -6 70 77 8612b 91 3 4.6 44 -9.6 -5.3 69 77 8512c 88 6 5.8 45 -9.2 -5.5 68 76 84__________________________________________________________________________ The results in columns 3 and 4 show very clearly the improvement in the contrast with the increase in the concentration of the racemic mixture of the chlorocarboxylate (Y).
Examples 13a-c
The following ferroelectric mixtures comprise the following components ##STR43##
In Table 3 below, the property features (at 25.degree. C.) of the examples are reproduced in a summarized form.
TABLE 3__________________________________________________________________________Concentration Switching time Polarization Phase-transition temperatures X Y Contrast .tau. P.sub.s X.fwdarw.S.sub.c * S.sub.c *.fwdarw.S.sub.A * S.sub.A *.fwdarw.N* N*.fwdarw.IExample Mol % Mol % K .mu.s nC .multidot. cm.sup.-2 .degree.C. .degree.C. .degree.C. .degree.C.__________________________________________________________________________13a 94 0 4.5 43 -9.8 -6 71 78 8913b 91 3 4.7 52 -9.5 -6 71 77 8813c 88 6 6.2 53 -9.2 -6 70 77 86__________________________________________________________________________ The results in columns 3 and 4 show very clearly the improvement in the contrast with the increase in the concentration of the racemic mixture of the chlorocarboxylate (Y).
Example 14
a) A liquid-crystalline mixture comprising the following five components
______________________________________5-octoxy-2-(4-decoxyphenyl)pyrimidine 21 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 12 mol-%5-octoxy-2-(4-hexoxyphenyl)pyrimidine 25 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 27 mol-% ##STR44## 15 mol-%4'-hexoxyphenyl 4-octoxybenzoate(= compound of the general formula VII)has the following liquid-crystalline phase ranges:X 8 S.sub.c 72.3 S.sub.A 86.1 N 93 I______________________________________
b) A mixture without addition of 15 mol-% of the compound of the general formula (VII) has, by contrast, the following liquid-crystalline phase ranges:
______________________________________X 13 S.sub.c 81.5 S.sub.A 95.5 N 98 I______________________________________
Compared with mixture 14b, the mixture 14a according to the invention additionally contains a component of the general formula (VII) and has, in comparison, a melting point which is lower by 5.degree. C. and an upper S.sub.c phase-range limiting temperature which is lower by 9.5.degree. C.
Example 15
A liquid-crystalline mixture comprising the following five components
______________________________________mixture from Example 14b 80 mol-% ##STR45## 20 mol-%4-hexoxyphenyl 4'-decoxybenzoate(compound of the general formula VII)has the following liquid-crystalline phase ranges:X 9 S.sub.c 72.6 S.sub.A 87.3 N 92.5 I______________________________________
Compared with the mixture 14b, the mixture additionally contains a component of the general formula (VII) and has, in comparison, a melting point which is lower by 4.degree. C. and an S.sub.c phase-range limiting temperature which is lower by 9.degree. C.
Example 16
A liquid-crystalline mixture comprising the following six components
______________________________________5-octoxy-2-(4-decoxyphenyl)pyrimidine 20 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 11 mol-%5-octoxy-2-(4-hexoxyphenyl)pyrimidine 24 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 25 mol-% ##STR46## 9 mol-%4-hexoxyphenyl 4'-decoxybenzoate(= compound of the general formula VII) ##STR47## 11 mol-%4-hexoxyphenyl 4-octoxybenzoate(compound of the general formula VII)has the following liquid-crystalline ranges:X 6 S.sub.c 72.3 S.sub.A 85.2 N 92 I______________________________________
b) A four-component mixture which differs from the liquid-crystal mixture 16a only in that it contains no compound of the general formula (VII) has the following liquid-crystalline phase ranges:
______________________________________X 13 S.sub.c 81.5 S.sub.A 95.5 N 98 I______________________________________
Compared with the mixture 16b, the mixture 16a according to the invention has a melting point which is lower by 7.degree. C. and a upper S.sub.c phase-range limiting temperature which is lower by 9.degree. C.
Example 17
A ferroelectric mixture comprising the following components
__________________________________________________________________________mixture from Example 3a 82 mol-% ##STR48## 3 mol-%Racemate of 4-(2-nonoxypyrimidin-5-yl)phenyl2-chloro-4-methylpentanoate ##STR49## 9 mol-%4-pentylphenyl 4'-hexoxybenzoate(compound of the general formula VIII) ##STR50##4-(2-nonoxypyrimidin-5-yl)phenyl (2S,3S)- 6 mol-%2-chloro-3-methylpentanoatehas the following LC ranges:X -9 S.sub.c * 61 S.sub.A * 70 N* 85 I__________________________________________________________________________
At 20.degree. C., this mixture has a polarization of -8.2 nC cm.sup.-2, a contrast of 5.7 and, in a switching field of 10 V.mu.m.sup.-1, a switching time of 54 .mu.s. Comparison with the mixture from Example 12b confirms that the addition of the ester of the general formula (VIII) reduces the melting point by 4.degree. C. and increases the contrast by 24%.
Example 18
a) A liquid-crystalline mixture comprising the following nine components
______________________________________5-octoxy-2-(4-hexoxyphenyl)pyrimidine 14 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 5 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 15 mol-%5-octoxy-2-(4-decoxyphenyl)pyrimidine 8 mol-%5-octoxy-2-(4-dodecoxyphenyl)pyrimidine 8 mol-%5-octyl-2-(4-dodecoxyphenyl)pyrimidine 13 mol-%[4-(5-decylpyrimidin-2-yl)]phenyl 17 mol-%trans-4-pentylcyclohexanecarboxylate ##STR51## 13 mol-%4-(5-octylpyrimidin-2-yl)phenyl heptanoate(= compound of the general formula V) ##STR52## 7 mol-%4-(10-decylpyrimidin-2-yl)phenyl undecanoate(compound of the general formula V)exhibits the following liquid-crystalline phase ranges:X -3 S.sub.c 73 S.sub.A 81 N 94 I______________________________________
b) A comparable mixture which differs from the mixture 18A only in that it contains no component of the general formula (V) has the following liquid-crystalline phase ranges:
______________________________________X -1 S.sub.c 81 S.sub.A 87 N 103 I______________________________________
The mixture according to the invention thus has a melting point which is lower by 2.degree. C. and an upper S.sub.c phase-range limiting temperature which is lower by 8.degree. C.
Example 19
A ferroelectric liquid-crystalline mixture comprises the following ten components
______________________________________5-octoxy-2-(4-butoxyphenyl)pyrimidine 13.2 mol %5-octoxy-2-(4-hexoxyphenyl)pyrimidine 14 mol %5-octoxy-2-(4-octoxyphenyl)pyrimidine 5.5 mol %5-octoxy-2-(4-decoxyphenyl)pyrimidine 7 mol %5-octoxy-2-(4-dodecoxyphenyl)pyrimidine 7 mol %[4-(5-decylpyrimidin-2-yl)]phenyl trans- 16.7 mol %4-pentylcyclohexanecarboxylate5-octyl-2-(4-dodecoxyphenyl)pyrimidine 11.4 mol %[4-(5'-octylpyrimidin-2-yl)]phenyl heptanoate 13.2 mol %4-(2-nonoxypyrimidin-5-yl)phenyl 2-fluoro- 6 mol %4-methylpentanoate(compound of the general formula IX)4-(2-nonoxypyrimidin-5-yl)phenyl (2S,3S)- 6 mol %2-chloro-3-methylpentanoateexhibits the following liquid-crystalline phase ranges:X -8 S.sub.c * 73 S.sub.A * 80 N* 90 I______________________________________
and has, at 25.degree. C., a spontaneous polarization of 9.4 nC cm.sup.-2, a contrast of 5.8 and a switching time of 65 .mu.s.
By comparison, the claimed ferroelectric FLC mixture from Example 7a, which differs from the abovementioned ferroelectric mixture only in that it contains no racemate (IX), has the following phase ranges:
______________________________________X -1 S.sub.c * 80 S.sub.A * 85 N* 99 I______________________________________
In comparison, the abovementioned ferroelectric mixture has a melting point which is lower by 7.degree. C.
Example 20
a) A liquid-crystalline mixture comprising the following six components
______________________________________5-oxtoxy-2-(4-hexoxyphenyl)pyrimidine 20.2 mol-%5-octoxy-2-(4-octoxyphenyl)pyrimidine 9.4 mol-%5-octoxy-2-(4-butoxyphenyl)pyrimidine 21.4 mol-%5-octoxy-2-(4-decoxyphenyl)pyrimidine 17 mol-%[4-(5-decylpyrimidin-2-yl)]phenyl 12 mol-%trans-4-pentylcyclohexanecarboxylate ##STR53## 20 mol-%[4-(5'-octoxypyrimidin-2-yl)]phenyl decanoate(= compound of the general formula VI)exhibits the following liquid-crystalline phase ranges:X 8 S.sub.c 80 S.sub.A 92 N 100 I______________________________________
b) The following mixture, which is claimed in DE 3,831,2265.3 and differs from the mixture 20a only in that it contains no component of the general formula (VI), is suitable for comparison of the physical properties. This mixture comprising five components has the following liquid-crystalline phase ranges:
______________________________________X 10 S.sub.c 84 S.sub.A 93 N 105 I______________________________________
In comparison with the mixture lb, the mixture 20a according to the invention has a melting point (X) which is lower by 2.degree. C. and an upper S.sub.c phase-range limiting temperature which is lower by 4.degree. C.

Number	Name	Date
4855429	Heppke et al.	Aug 1989
5064566	Hopf et al.	Nov 1991
5071589	Dubal et al.	Dec 1991

Number	Date	Country
0248335	Dec 1987	EPX
0275522	Jul 1988	EPX
0288813	Nov 1988	EPX
0292954	Nov 1988	EPX
0355561	Feb 1990	EPX
3831226	Mar 1989	DEX

Liquid-crystalline mixtures, in particular ferroelectric liquid-crystalline mixtures

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Priority Claims (1)

PCT Information

US Referenced Citations (3)

Foreign Referenced Citations (6)