Patent Application
20210187477
The present invention relates to a process for production of water-absorbing textile material such as non-woven, woven or other textile materials types and related absorbing products.
In art there are known processes to manufacture an absorbent textile material, which can be divided in two distinct classes: a) processes with textile fibers and polymeric absorbents, b) processes with prefabricated textile materials and reactive liquid media.
Forwards are discussed only the processes with prefabricated textile materials and reactive liquid media.
b) Processes with Prefabricated Textile Materials and Reactive Liquid Media
Particularity of these processes consists in that, a traditional prefabricated textile material like nonwoven, woven, knitted or braided type, is impregnated with a fluid mass in solution, emulsion or suspension form, and a polymeric absorbent is generated in situ during the drying of the impregnated wet textile material, or after drying and applying of an adequate thermal treatment. Representative processes that are known in the art: b1) processes with polymerizable impregnation mass and b2) processes with cross-linkable impregnation mass.
b1) Processes with Polymerizable Impregnation Mass
In these processes, a liquid used for impregnation produces in-situ polymerization of partially neutralized acid vinyl monomers directly on a synthetic nonwoven substrate. These processes can be found in U.S. Pat. Nos. 4,537,590; 4,540,454; 4,573,988; 4,676,784; 5,567,478; 5,962,068; 6,417,425 and 6,645,407.
b2) Processes with Cross-linkable Impregnation Mass
In these processes, the textile material prefabricated as: nonwoven, woven or other known type is impregnated with a fluid mass in the form of solution or emulsion, that contains polymers in dissolution or dispersion state, or in mixture with auxiliary materials which are cross-linking agents active at temperatures and induce generation in situ of a polymeric absorbent. In this class can be seen more variants:
i) Processes with Impregnation Mass that Contain a Self-crosslinking Synthetic Polymer.
Various processes are described in which a substantially linear acrylic polymer is cross linked through its pendant groups. The pendant groups will react with each other upon appropriate heating. Any combination of monomers that will undergo such reaction can be used as in U.S. Pat. Nos. 4,057,521; 4,861,539; 4,962,172; 4,963,638; 5,280,079 and 5,413,747.
The impregnation mass based on self-crosslinking polymers has the disadvantage that the cross-linking is not complete and because of this reason more than 10% of end product is lost during processes associated with extraction of monomers, initiators and organic solvents residue used during polymerization. Moreover, the free absorbency of the resulting cross linked polymers has a low value (less than 50 g/g in 0.9% NaCl solution), and the product is not safe.
ii) Processes with Impregnation Mass that Contain Synthetic Polymers and Cross-linking Agents
It is further known from U.S. Pat. Nos. 2,988,539; 3,393,168 and 3,514,419 that water swellable cross-linked carboxylic copolymers can be prepared. However, these prior art copolymers are all cross-linked during copolymerization or cross-linked after polymerization with subsequent neutralization of the carboxylic acid groups to form water swellable polyelectrolytes and hence these prior art polyelectrolytes cannot be cross-linked in situ as a coating on a substrate or as a flexible film thereof.
U.S. Pat. Nos. 3,926,891; 3,980,663 and 4,155,957 present chemical structures of the principal classes of combinations that can be used as cross-linking agents for polymers with free carboxylic chemical functions. Also is shown that cross-linking reaction occurs based on mechanism known as nucleophilic displacement on saturated carbon. The carboxylate ion on polymer acts as nucleophile while cross-linking agent is the substrate for nucleophilic attack.
Cheng et al. in U.S. Pat. Nos. 5,693,707 presents an aqueous polymer composition comprising 10 to 40 wt % of a polymer in water, the polymer consisting essentially of 20-90 wt % alpha,beta.-ethylenically unsaturated carboxylic acid monomer, 10-80 wt % one or more softening monomers, the aqueous composition being adjusted to pH 4-6 with alkali metal hydroxide or alkaline earth metal hydroxide and further containing 0.1 to 3 wt % zirconium crosslinking salt. Such aqueous compositions are applied to nonwoven and woven substrates to make absorbent textile web.
Goldstein et al. in U.S. Pat. No. 6,506,696 shows that the method of forming the high performance nonwoven webs of this invention comprises: applying an aqueous polymeric emulsion containing a polymer having dual cross-linkable functionality to a synthetic based nonwoven web, wherein the dual cross-linkable polymer incorporates acetoacetate functionality and carboxylic acid functionality; removing water and cross-linking the cross-linkable polymer with an effective amount of a polyaldehyde and an effective amount of a polyaziridine compound.
Soerens Dave Allen in U.S. Pat. No. 7,205,259 presents an absorbent binder desiccant composition which is capable of spontaneous cross-linking after application to a substrate, at a temperature of about 120° C. or less. The absorbent binder desiccant composition includes a monoethylenically unsaturated polymer, such as carboxylic acid, sulphonic acid, or phosphoric acid, or salts thereof, or a quaternary ammonium salt, and an acrylate or methacrylate ester that contains an alkoxysilane functionality, or a monomer capable of co-polymerization with a compound containing a trialkoxy silane functional group and subsequent reaction with water to form a silanol group, and a desiccant component. The absorbent binder desiccant composition is particularly suitable for use in manufacturing a wide variety of humidity control articles.
A diversity of chemical compositions (polymers and cross-linking agents) besides of multiple variants of control of cross-linking reactions are found in art in U.S. Pat. Nos. 3,983,271; 4,066,584; 4,320,040; 4,418,163; 4,731,067; 4,855,179; 4,880,868; 4,888,238; 5,698,074; 5,997,791; 6,150,495; 6,162,541; 6,241,713; 6,773,746 and 6,824,650.
iii) Processes with Impregnation Mass that Contain Biopolymers and Cross-linking Agents
Weerawarna et al. in U.S. Pat. No. 7,300,965 provides a mixed polymer network having superabsorbent properties. The composition is obtainable by reacting a carboxyalkyl cellulose and a synthetic water-soluble polymer having carboxylic acid or carboxylic acid derivative substituents with a crosslinking agent. The cross-linking agent reacts with at least one of the carboxyalkyl cellulose or water-soluble polymer to provide the network. Suitable cross-linking agents include cross-linking agents that are reactive toward carboxylic acid groups.
Representative organic cross-linking agents that are reactive toward carboxylic acid groups include diols and polyols, diamines and polyamines, diepoxides and polyepoxides, polyoxazoline functionalized polymers, and aminols having one or more amino groups and one or more hydroxy groups.
Representative inorganic cross-linking agents that are reactive toward carboxylic acid groups include polyvalent cations and polycationic polymers. Exemplary inorganic cross-linking agents include aluminum chloride, aluminum sulfate, and ammonium zirconium carbonate with or without carboxylic acid ligands such as succinic acid (dicarboxylic acid), citric acid (tricarboxylic acid), and butane tetracarboxylic acid (tetracarboxylic acid). Water soluble salts of trivalent iron and divalent zinc and copper can be used as cross-linking agents. Representative carboxylic acid cross-linking agents includes di- and polycarboxylic acids. U.S. Pat. Nos. 5,137,537; 5,183,707 and 5,190,563 describe the use of C2-C9 polycarboxylic acids that contain at least three carboxyl groups (e.g., citric acid and oxydisuccinic acid) as crosslinking agents. Suitable polycarboxylic acid crosslinking agents include citric acid, tartaric acid, malic acid, succinic acid, glutaric acid, citraconic acid, itaconic acid, tartrate monosuccinic acid, maleic acid, 1,2,3-propane tricarboxylic acid, 1,2,3,4-butanetetracarboxylic acid, all-cis-cyclopentane tetracarboxylic acid, tetrahydrofuran tetracarboxylic acid, 1,2,4,5-benzenetetracarboxylic acid, and benzenehexacarboxylic acid. The cross-linking can be achieved by heating at a temperature and for a period sufficient to effect the cross-linking. The carboxymethyl cellulose solution containing cross-linking agent or synthetic water-soluble polymer and cross-linking agent can be air-dried or solvent precipitated followed by cross-linking. Cross-linking time and temperature will depend on the cross-linking agent and polymers used.
Sun et al. in U.S. Pat. No. 6,689,378 presents methods of immobilizing uncomplexed cyclodextrins and complexed cyclodextrins to polysaccharide containing substrates, such as cellulose fibers by covalently bonding. The cellulose/cyclodextrin compositions can be used in all types of cellulose fiber containing articles, such as tissues and personal care articles.
Useful polymeric anionic reactive compounds are compounds having repeating units containing two or more anionic functional groups that will covalently bond to hydroxyl groups of the substrate. Exemplary polymeric anionic reactive compounds include the ethylene/maleic anhydride copolymers described in U.S. Pat. 4,210,489. Vinyl/maleic anhydride copolymers and copolymers of epichlorohydrin and maleic anhydride or phthalic anhydride are other examples. Copolymers of maleic anhydride with olefins can also be considered, including poly(styrene/maleic anhydride)
Copolymers and terpolymers of maleic anhydride that could be used are disclosed in U.S. Pat. No. 4,242,408.
The cross-linkable impregnation mass, similar to polymerizable systems in situ have disadvantage that the cross-linking is not complete in conditions of thermal treatment mentioned, existing permanent the possibility that during uses of textile products to extract besides soluble polymer also cross-linking agent, this being more dangerous for the human healthy comparatively with the monomers or polymerization auxiliary residues. Presence of biopolymers in mixture for treating of textile materials, not contribute to improving the chemical transformation yield that occurs during cross-linking. Referring to uses of macromolecular cross-linking agents, these products being in their turn result of synthesis processes are not mentioned their purity or the extractability in aqueous solutions used as swelling media.
A particular drawback of known processes in the art for obtaining absorbent textiles is that those products are not ecological. Majority of polymeric absorbents discussed above, are products of synthesis, which because of their chemical structure have not the capacity of biodegradation in specific active biological media, i.e. the domestic compost. Moreover, absorbent textiles that contain biopolymers, although are biodegradable, have small values of free absorbency. Another drawback of known absorbent textiles is that the polymer network included in such textiles was obtained through the use of crosslinking agents that might present health hazards to end users.
The present invention eliminates the disadvantages of processes known in art for obtaining absorbent textiles, by providing a new process for treating textiles and forming new textile composite article with improved water absorbance and biodegradability. The new process makes use of an aqueous textile-impregnating polymeric composition in solution form and containing at least two types of soluble polymers—a synthetic polymer and a natural polymer, the composition being devoid of separate non-polymer crosslinking agent. The two types of polymers are combined in a predefined ratio that is chosen such that when the textile is impregnated with the polymeric composition and is exposed to heat treatment, the polymers interpenetrate into the textile fibers and undergo self crosslinking into the textile. The resulting composite textile in dry form has a free absorbance capability which is higher by at least 10% when compared to the non-impregnated textile material, depending on the liquid medium type that is in contact. The resulting textile is also characterized by high biodegradability. More specifically, the resulting composite textile in dry form has a free absorbance capability which is higher by at least 10%, preferably higher by at least 20%, more preferably higher by 30%, 40% 50%, 60%, 70%, 80%, 90% or higher, when compared to the non-impregnated textile material.
The terms fabric, textile, web, with or without being combined with the word “material” are used in this specification interchangeably.
Another object of the invention is to provide a textile composite article comprising fibers and polymers network interpenetrating the textile fibers, the polymers network comprising natural polymer crosslinked to synthetic polymer in the absence of non-polymeric crosslinking agent. The textile composite article has a water absorbance by at least 50% higher in comparison to same textile without said polymers network interpenetrating into the textile fibers.
Another object of the present invention is to provide a new type of polymeric composition, in which the natural polymer activates the biodegradation of the synthetic polymer and confers to the system superior biodegradability.
Another object of the present invention is to provide a new type of polymeric composition made of at least two types of soluble polymers—a synthetic polymer and a natural polymer, in which the natural polymer activates under heat the crosslinking of the synthetic polymer and confers to a textile impregnated with such composition and dried, superior free absorbance when exposed to aqueous liquids.
The natural polymer is a biopolymer that functions as both cross-linking agent of the synthetic polymer and as activator of biodegradation processes.
Another object of the present invention is to provide a textile composite article having an internal pattern of an interpenetrating polymeric material which penetrates at least partially within the textile, leading to a pattern of impregnated areas in the textile. Following heat treatment and drying of the impregnated textile, a textile composite article is obtained, having improved water absorbance when exposed to aqueous liquids.
Another object of the present invention is to provide a new type of polymeric network composition in stable aqueous solution which is compatible with different additives used in the textile industry, for example plasticizers, active surface agents, dyers, perfumes, anti-odorants, bacteriostatic agents etc., without affecting the water absorptive performance or biodegradability of the textile material.
Another object of the present invention is to provide a new type of polymeric network composition, in solution form, which is suited to be used as impregnation mass for any nonwoven, woven or knitted textile materials made either from synthetic fibers (polypropylene, polyester, polyvinyl alcohol, etc), from natural fibers (cellulose, viscose, cotton, wool, PLA, etc.), or from mixtures of synthetic and natural fibers, preferably with a density of 30-90 g/m2. The textile materials may be biodegradable by themselves such as for example when made of PLA or may become biodegradable following impregnation with the polymeric network and drying to form the composite absorbent textile of the invention.
Another object of the present invention is to provide a new type of polymeric aqueous composition, which after heat-driven elimination of water from textile material impregnated with such composition followed by self crosslinking, it gives rise to a composite absorbent textile material with free spaces that permit fast access and absorption of liquid media in the textile material when the textile is exposed to aqueous liquids.
The combination ratio of the two polymers in water is preferably chosen to obtain an aqueous solution that is thermodynamically stable and suitable for impregnation into fabrics, and that undergoes self-cross-linking under controlled thermal conditions (temperature and time).
A textile material treated according to the invention with the polymeric composition is characterized by improved water absorbance and biodegradability. With reference to biodegradability, when the textile comes into contact with an aqueous biological media and starts absorbency of this media, the composite polymeric material impregnated within the textile is swelling and is transforming in a gel like material within the textile or on its surface (textile function as a support).
According to other embodiments of the present invention, there is provided a polymeric composite solution for use in forming an absorbent textile material that both in dry form and gel form resulting after swelling in different aqueous media, it is still safe when in contact with the human body and which is environmentally friendly, conferring a pronounced ecologic character to textile materials used.
According to another aspect, the invention provides a process for the preparation of polymeric composite aqueous solution to be used in improving water absorbency of substrates e.g. fabrics treated with the polymeric composite, the process comprising the following steps:
a) preparation of alkaline base solution
b) preparation of aqueous solution of synthetic polymer (SP) in acidic form, which is treated afterwards with the alkaline solution from (a) to obtain the salt form, at a concentration of between 1% and 10%, preferably between 2 and 5% by weight,
c) preparation under heating of aqueous solution of natural polymer NP at a concentration between 1% and 10%, preferably between 2 and 5% by weight
d) mixing under heating and stirring the SP solution obtained in (b) in salt form, with the NP solution obtained in (c) to obtain aqueous stable composite solution of polymers suitable to be used as impregnation mass that confers high water absorbance to textile materials and optionally
e) adding to the aqueous composite solution obtained in (d) at least one auxiliary material selected from the list of plasticizers, surface agents, deodorants, perfume and preservatives.
According to preferred embodiments, synthetic polymers (SPs) used in the invention are made of monomers bearing carboxylic acid or carboxylic acid anhydride groups. More specifically, SPs suitable to be used in this invention are linear or branched graft homo- or copolymers made from vinyl acidic monomers such as acrylic acid, maleic anhydride, itaconic anhydride and similar, optionally in association with other types of vinylic monomers that do not necessarily contain carboxylic acid functions.
Preferably, the natural polymer is a biopolymer selected from a protein, soybean protein, collagen, collagenic biopolymer, gelatin, collagen hydrolysate, albumin, guar or starch and casein.
Preferably, the synthetic polymer is a copolymer based on maleic anhydride (maleic acid), e.g. copolymers of styrene maleic anhydride (SMA), copolymers olefins with maleic anhydride such as of isobutylene and maleic anhydride (e.g. commercially available copolymers sold under the tradename Isobam™) or copolymers of methyl vinyl ether and maleic acid (e.g. commercially available copolymers sold under the tradename Gantrez™), poly(decyl vinyl ether-alt-maleic anhydride), poly(ethyl vinyl ether-alt-maleic anhydride), poly(maleic acid-co-propene), poly(n-butyl vinyl ether-alt-maleic anhydride), poly(octadecene-alt-maleic anhydride), polypropylene-alt-maleic acid) or poly(maleic acid-co-dodecyl methacrylate).
According to preferred embodiments, the content of total free carboxylic acid groups in the SPs of the invention range from 0.009 to 0.015 mole/gram SP. More specifically, the free carboxylic acid groups of synthetic polymer SP are in salt state, corresponding to a degree of neutralization between 49 to 99%, preferably between 60 to 95%, and most preferably between 65 to 90%.
According to preferred embodiments, the average molecular weight of SP used in the invention is from 50 KDa to 1,000 KDa, preferably from 100 KDa to 750 KDa, more preferably from 150 KDa to 500 kDa.
According to preferred embodiments the natural polymer NP used in the invention is a biopolymer selected from polypeptides, proteins, polysaccharides, polyesters and lignin (in native forms or modified by chemical or enzymatic hydrolysis). More preferably the NPs used in the invention are water soluble phospholipids such as lecithin, polypeptides or proteins such as gelatin, albumin and the like; or polysaccharides such as cellulose, alginate, dextran, chitosan, and the like; that have at least one of the following characteristics:
a) average molecular weight from 5 to 100 KDa preferably from 25 to 50 KDa, more preferably from 75 to 100 KDa.
b) free chemical groups such as amine or hydroxyl in a relative concentration from 0.005 to 0.01 mole/grams NP, more preferably from 0.001 to 0.002 mole/grams NP.
c) hydrophilic, capable to form hydrogels in water environment and capable of integration within the textile fibers.
According to preferred embodiments the biopolymer used in the invention has the capability of cross-linking due to its NH2 or OH groups that crosslink to COOH groups in the synthetic polymer under high temperature conditions and for selected periods of time, to form ester and amide bonds between polymers skeletons. Furthermore, the biopolymer of the invention activates the biodegradation of the textile impregnated with composite solution of SP and NP of the invention.
According to further preferred embodiments, the polymers composite solution used in the invention is a stable solution and may further contain at least one additive selected from plasticizers, antibacterial agents, surfactants, deodorants, perfume, preservatives etc. The polymers composite solution is suitable for impregnation into fabrics and also suitable for self-cross-linking under controlled conditions of temperature and time.
Preferably, the textile density is between 30 to 90 g/m2 in order to allow sufficient penetration of composite polymer solution into the textile material.
The invention will now be described with reference to the drawings, wherein:
Polymeric composite solution which is within the objects of this invention is a new type of textiles treatment hereinafter termed Impregnation Composition (IC) which is used for treating any type of textiles, preferably nonwoven textiles, to produce high absorbent textile materials.
The polymer composite solution comprises synthetic polymer in the form of salt (SP), natural polymer (NP), additives (A) and water (W).
The ratio between a textile material TEX (before treatment) to impregnation composition IC[IC=SP+NP+A] is from 85:25 to 99:1% by dry weight.
The ratio between the synthetic polymer (SP) in salt form to natural polymer (NP) SP/NP is from 70:30 to 95:5% by dry weight.
The ratio of additives (A) to polymers A/(SP+NP) is from 0.5 to 5% dry weight.
Water content in the composite polymer solution is from 79 to 99% by weight. The synthetic polymer salt, SP may be a commercially available polymer, having the following characteristics:
a) linear copolymers or branched graft homo- or copolymers that contain vinyl acidic monomers as: acrylic acid, maleic anhydride, itaconic anhydride and similar in association or not with other types of vinylic monomers which does not contain carboxylic groups.
b) content of total free carboxylic groups from 0.009:0.0095 mol/gram to 0.01:0.0.15 mol/grams
c) Free carboxylic groups of synthetic polymer, SP are in salt state, corresponding to a degree of neutralization between 49-99%, preferable between 60-95%, and most preferable between 65-90%;
d) The salt state of synthetic polymer is obtained by using strong inorganic base substances such as hydroxides, bicarbonates or carbonates of lithium, sodium, potassium or ammonium, preferred hydroxides of lithium, sodium, potassium or ammonium.
e) The average molecular weight of synthetic polymer, SP is from 50,000 Da to 1,000,000 Da, preferable from 100,000 Da to 750,000 Da, and most preferable from 150,000 Da to 500,000 Da.
The natural polymer, NP is preferably a commercially available biopolymer which belongs to the following classes of substances: proteins, carbohydrates, bio-polyesters or lignin (as native forms or modified by chemical or enzymatic hydrolysis); preferable are proteins and carbohydrates integral soluble in water and which have the following characteristics:
d) The average molecular weight from 5,000 to 100,000 Da preferable from 25,000 to 50,000 more preferable from 75,000 to 100,000 Da.
e) Free chemical functions as NH2; OH—CH2; OH—C6H3-5; as single type or more types which have content from 0.001 to 0.002 preferable from 0.005 to 0.01 mol /grams.
Suitable additives, A are: plasticizers, antibacterial agents, active surface agents, deodorants, perfume, preservatives etc., in quantities that are correlated with other properties than absorbency.
The polymer composite solution is a stable solution of polymer materials SP and NP, without phase separation under conditions of storage or ulterior processing. Without being bound to theory, the polymer composite solution can interpenetrate within the textile fibers and self cross-link under conditions of thermal treatment at temperatures between 100 to 250° C. and during periods of preferably between 2 to 30 minutes.
The resulting textile is a composite textile article having an internal pattern of an interpenetrating polymeric material which penetrates at least partially within the textile. Following heat treatment at temperatures being 100 to 250 ° C. and drying of the impregnated textile, a textile composite article is obtained, having improved water absorbance when exposed to aqueous liquids.
A schematic representation of the process that occurs between a textile material and the polymers network under heating conditions, to provide the textile composite article of the invention is shown in
Preparation of polymeric composite aqueous solution to be used in improving water absorbency of substrates e.g. fabrics treated with the polymeric composite, comprises the following steps:
a) preparation of alkaline base solution
b) preparation of aqueous solution of synthetic polymer (SP) in acidic form, which is treated afterwards with the alkaline solution from (a) to obtain the salt form, at a concentration of between 1% and 10%, preferably between 2 and 5% by weight,
c) preparation under heating of aqueous solution of natural polymer NP at a concentration between 1% and 10%, preferably between 2 and 5% by weight
d) mixing under heating and stirring the SP solution obtained in (b) in salt form, with the NP solution obtained in (c) to obtain aqueous stable composite solution of polymers suitable to be used as impregnation mass that confers high water absorbance to textile materials and optionally
e) adding to the aqueous composite solution obtained in (d) at least one auxiliary material selected from the list of plasticizers, surface agents, deodorants, perfume and preservatives.
Textile materials to be used with the polymer composite solution include prefabricate textile materials as: nonwoven, woven or any other type known in art and commercially available, formed from synthetic fibers or natural fibers or a mixture of synthetic and natural fibers. Preferred textile materials are made of synthetic fibers with a density of 30-90 g/m2, preferable 40-80 g/m2 and more preferable 50-70 g/m2.
Impregnation of the textile material is done using any equipment known in art, for example spray devices; foulard; roll coating; reverse roll coating; knife devices etc.
Further processing of the wet textile material depends of initial density of material and of impregnation degree so chosen. For example:
a) if the density of the textile material has been initially higher than 70 g/m2 , then the wet textile material is first dried in a stream of hot air at temperature of 50-90° C., preferable at temperature of 55-85° C., and most preferable at temperature of 60-80° C., so the solid composite (textile+composite polymer) resulted to have a humidity content less than 12% by weight, preferable less than 10% by weight, and most preferable less than 8% by weight and then the supplementary thermal treatment in hot air steam at temperature of 90-180° C., preferable at temperature of 100-170° C., and most preferable at temperature of 110-160° C., during a period of 5-180 minutes, preferable 10-150 minutes, and most preferable of 15-120 minutes;
b) if the density of textile material has been initially less than 70 g/m2 the wet textile material is subdue to a single thermal treatment at temperature of 100-150, during 180-300 seconds, preferable at temperature of 140-180 ° C. during 60-180 seconds and more preferable at temperature of 200-250° C. during 30-120 seconds.
Following the thermal treatment the textile material is let to cool at room temperature and in the end is packed.
The resulting textile material has improved water absorbance and can be used in a variety of applications such as for example cleaning wipes, household or institutional cleaning or maintenance, hand wipes, hand towels which allow a user to feel that the towel remains dry, but which also allow for absorption of moisture, personal hygiene, cosmetic or sanitary wipes, baby wipes, facial tissues, the core in panties or wound dressings, hygienic absorbent pads and any other same application.
The viscosity of the solution was evaluated using a viscosimeter ViscoStar Plus, Fungilab, Spain using a volume of solution correlated to the type of spindle L1 at 25° C. temperature.
The stability of the polymer solution used for impregnation was assessed to be stable or unstable if the analyte solution showed sediment after centrifugation of a volume of 25 ml solution at 5000 rpm for 30 minutes. Tests were performed with a laboratory centrifuge GLC-2B Sorvall, Thermo Scientific at ambient temperature.
The following measurements are made:
Mtex,[grams], mass of the dried textile material used for impregnation by weighing at a semi-analytical balance
Mtwstart, [grams]—mass of wet starting material by weighing the sample
Mtid—[grams]—mass of drained textile material after impregnation
MIC—[grams]—mass of dried polymeric composite material found in the textile after impregnation evaluated by the formula:
MIC=Mtex*IMD/100, grams
The degree of impregnation of a textile material is established using the formula:
[IMD]dry=IMC/(Mtex+MIC)*100, %
Absorbency of non-impregnated textile material Q1 is obtained by using the formula:
Q1=(M-tex wet-M-tex)/M-tex, , (g/g)
The textile sample is weighted at technical balance obtaining the value Mtex. Then is impregnated with a chosen mass of liquid:distilled water, an impregnating solution or other type of solution by using a laboratory spray device. The wet material thus obtained is weighted again and the value is Mtwstart. If this value is higher than the impregnation degree (IMD)—pre-established the wet sample is subdue to a squeezing process with the aid of a glass rod to eliminate the excess of impregnation liquid so that it finally is obtained a wet sample with the mass Mtid. Next, the wet sample is kept for 30 minutes, in a closed glass beaker to avoid evaporation of the liquid.
The absorbency of textile material sample is obtained with formula:
Q2-TEXIC=[Mtid−(MTex+M IC)]/(Mtex+M IC), (g/g)
RQ represents the ratio between absorbency of an impregnated textile material Q2 and absorbency of the same textile material non-impregnated Q1.
Relative absorbency is calculated by using the formula:
[RQ]1=Q2/Q1 or
[RQ]2=[(RQ1)−1]*100, (%)
Stock solutions of synthetic polymer, natural polymer and inorganic base are prepared as follows:
42.6 g of SMAc styrene/maleic acid copolymer [prepared as in U.S. Pat. No. 7,985,819] in powder form having an 8% moisture content with an average molecular weight of 450,000 Da containing 0.0091 mol/g free carboxylic groups together with 358 g of demineralized water were added to a mixing vessel with agitation and the content was mixed for 1 hour at 80° C. to complete dissolution of the synthetic polymer and is end by cooling the polymer solution to 40° C. Finally, 400 g of SMAc polymer solution of 10% by dry weight is obtained.
Is prepared 400 g of NaOH solution of 10% dry weight (from 98.9% pure sodium hydroxide pellets) and demineralized water using a mixing vessel with agitation fitted with a heating-cooling jacket.
400 g of gelatin type A solution with 200 Bloom and 14% moisture content (as natural polymer-NP) of 10% dry weight were prepared by dissolving 46.5 g of natural polymer in 354 g of demineralized water using a mixing vessel by stirring with a rotor speed not higher than 60 rpm, during a period of 1 hour at a temperature of 40° C. so as to ensure the perfect homogenization of the solution.
Further, the 3 types of solutions prepared above were used to prepare 3 sets of composite solutions by diluting with demineralized water the stock solutions as follows:
All composite solutions corresponding to the three sets were characterized in terms of their viscosity and stability in the sense that the sample is unstable if it contains the insoluble phase and that the sample is stable if it is a homogeneous solution without the insoluble phase. The results obtained are presented in Table-1 and
From
In these examples, is presented the absorbency value to demineralized water (conductivity 2 micro S) of some nonwoven fabrics containing viscose fiber with density of 50 g/m2 with different impregnation degree with polymeric solutions' concentration of 1% by weight containing SMAc (mentioned in Example 1) with neutralization degree of 59% generated with NaOH and various values of gelatin content and which additionally contains 1.5% by dry weight to the content of the polymeric composition.
Textile materials having a mass of 0.5 g were impregnated with composite solutions prepared according to the method described in Example 1 by spraying with a laboratory device so as finally to obtain the impregnation degree pre-established, IMD, to the dry mass of the sample of dried fabric material. Further, the wet textile samples were placed in a hanging state in an oven with air circulation, preheated to 180 ° C. and are maintained at this temperature for 4 minutes. Finally, the sample was removed from the oven and allowed to cool at ambient temperature. Then the textile material was subjected to the absorbency test according to the methodology described in the chapter “Test methods”.
In these examples are presented the impregnation of a textile material consisting of viscose fibers with a density of 50 g/m2 using a solution of synthetic polymer SMAc with neutralization degree of 64% done by using NaOH, 3.6% gelatin to the polymeric composite at degree of impregnation of 20% with thermal treatment of 200° C. for 100 seconds using the same oven with air circulation mentioned in the previous examples. Finally, the absorbency of the textile sample was evaluated against various liquid media represented by simulated fluid secreted by the human body (Margareth R. C. Marques et al, Simulated Biological Fluids with Possible Application in Dissolution Testing, Dissolution Technologies Aug. 2011, 1) The results are presented in Table-3
In this example is presented the influence of the temperature and the time of the thermal treatment at what is subjected a sample of textile material with a density of 50 g/m2 in order to obtain an absorbent textile material on the relative absorption RQ1. The results are presented in
The data obtained show that the thermal treatment of the impregnated fabrics must be in such manner as to obtain the highest value for absorbency. The lower values of the maximum result either because of a low crosslinking degree or because the degree of crosslinking of the polymeric composite is too high.
This example shows the influence of the type of fiber from which the fabric is done subjected to impregnation.
For this purpose, a composite polymer solution having the chemical composition coinciding with Exp-2 was used.
Have been used textile materials from polypropylene fiber (PP-fiber), polyester fibers (PET-fiber) viscose fibers (Viscose-fiber).
The results obtained are presented in
In these examples is presented the influence of the type of biopolymer used for the preparation of composite material according to the invention on the absorbency of a textile material using the preparation technology for the composite from Example land the methodology of impregnation of the textile material from example 3 .
Instead of gelatin have been used gum guar (G4129 Sigma Aldrich) and soluble starch (S9765 Sigma Aldrich).
1. A polymer composite solution for treating any type of prefabricate textile material for production of high absorbent materials. The treated materials are preferable nonwoven.
2. The polymer solution comprises synthetic polymer SP in salt form, natural polymer NP, and optionally additives A and water W.
3. The ratio between prefabricate textile material TEX to impregnation composition IC=(SP+NP+A is from 85:25 to 99:1% by dry weight.
4. The ratio between the synthetic polymer salt SP to natural polymer NP is SP:NP from 70:30 to 95:5% by dry weight.
5. The ratio between additives A to polymers (SP+NP) is 0.5:5% by dry weight.
6. Water content of polymer solution is 79:99% by weight.
7. The synthetic polymer SP preferably in salt form is a commercially available polymer, with the following characteristics:
8. The natural polymer NP is preferably a commercially available biopolymer which belong to the following classes of substances: proteins, carbohydrates, bio-polyesters or lignin (as native forms or modified by chemical or enzymatic hydrolysis); preferable are the proteins and carbohydrates integral soluble in water and which have the following characteristics:
10. The polymer composite solution is a stable solution without phenomena of phase separation in conditions of storage or ulterior processing. 11. The polymer solution can generate three-dimensional macromolecular network material, in dry state by cross-linking in the inner of fibrous mass, in conditions of thermal treatment at temperature of 100-250° C. during 2-20 minutes.
12. Process for the preparation of polymeric composite aqueous solution to be used in improving water absorbency of substrates e.g. fabrics treated with the polymeric composite, the process comprising the following steps:
13. Textile materials to be used are nonwoven, woven or any other type known in art and commercial available, formed from synthetic fibers or natural fibers or a mixture of synthetic and natural fibers, preferred being the textile materials formed from synthetic fibers with a density of 30-90 g/m2, preferable 40-80 g/m2 and more preferable 50-70 g/m2.
14. The polymer composite solution is used as a treating agent to obtain absorbent textile materials, as follows:
impregnation of textile material using any equipment known in art, for example (spray devices; foulard; roll coating; reverse roll coating; knife devices etc.);
The processing of wet textile material depends of initial density of material and of impregnation degree so chosen:
a) if the density of textile material has been initially higher than 70 g/m2 the wet textile material is first dried in current of hot air at temperature of 50-90° C., preferable at temperature of 55-85° C., and most preferable at temperature of 60-80° C., so the solid composite resulted to have a humidity content less than 12% by weight, preferable less than 10% by weight, and most preferable less than 8% by weight and then the supplementary thermal treatment in hot air current at temperature of 90-180° C., preferable at temperature of 100-170° C., and most preferable at temperature of 110-160° C., during a period of 5-180 minutes, preferable 10-150 minutes, and most preferable of 15-120 minutes;
b) if the density of textile material has been initially less than 70 g/m2 the wet textile material is subdue to a single thermal treatment at temperature of 100-150 ° C., during 180-300 seconds, preferable at temperature of 140-180 ° C. during 60-180 seconds and more preferable at temperature of 200-250° C. during 30-120 seconds.
Following thermal treatment, the treated textile material is let to cool at room temperature and in the end is packed.
15. The resulting textile material with improved water absorbance can be used in a variety of applications such as for example: cleaning wipes, household or institutional cleaning or maintenance, hand wipes, hand towels which allow a user to feel that the towel remains dry, but which also allow for absorption of moisture, personal, cosmetic or sanitary wipes, baby wipes, facial tissues, hygienic absorbent pads and any other same application.
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/US2019/025361 | 4/2/2019 | WO | 00 |
| Number | Date | Country | |
|---|---|---|---|
| 62651417 | Apr 2018 | US |