Patent Application
20140335400
1. Field of the Invention
The invention relates to a lithium battery having electrode tabs and in particular to a lithium battery having a pluality of electrode tabs, each electrode tab having an insulation layer.
2. Description of the Related Art
The lithium battery has been developed vigorously and applied in various field from portable electronic products to electric vehicles. The lithium battery having high capacity and high power has been developed continuously. However, it causes a complicated design of battery and danger. The general methods includes using safety valve, resistor member with positive temperature coefficient, current interrupt device, radiator in battery design; and monitoring the change of voltage, electricity and temperature of each unit of battery by an electric circuit board. However, the above methods of safety design cannot completely prevent the lithium battery from the internal short.
There are several factors to cause internal short, for example, contaminant in the process, over-charging, over-discharging, improperly heating and external pressure resulting in crack and deformation of structure. The degree of the internal short and the damage are different relying on the different factors. Definitely, the selection of cathode material, anode material, separator strip and electrolyte are the main factors to affect the damage degree of the battery.
It never becomes the best method to solve the problem of the lithium battery safety by try and error. It should focus on the materials of basic components of battery, design of battery structure and arrangement of stack of battery units. The two front items may be developed by the factories that manufacture the cells of batteries, and the last item combining with battery management and monitoring systems may be developed by the assembly factories. The best method for preventing from inefficiency is to establish a thermal runaway model of the lithium battery according to basic theory.
According to Journal of power sources 194 (2009) 550-557, there are four typical internal shorts that release energy and rise temperature as the internal short happens. Four typical internal shorts are type I: the internal short happening between two electricity collectors; type II: the internal short happening between anode electricity collector (copper) and cathode active substance; type III: the internal short happening between cathode electricity collector (aluminum) and anode active substance; and type IV: the internal short happening between cathode active substance and anode active substance wherein type III may release the largest energy and rise the highest temperature, showing a most serious internal short. Therefore, there is a need to enhance the safety of battery by a protective mechanism that may prevent the electrode tab of the cathode plate (aluminum) from contacting the anode active substance to cause the internal short as the separator contracts.
Therefore, the inventor conducted researches according to the scientific approach in order to improve and resolve the above drawback, and finally proposed the present invention, which is reasonable and effective.
It is an object of present invention to provide a lithium battery having electrode tabs.
In order to achieve the above object, there is provided a lithium battery having a housing, the lithium battery comprising a cathode plate entirely disposed in the housing, having a cathod active substance and a cathode electrode tab formed at an edge of the cathode plate in longitudinal direction; an anode plate entirely disposed in the housing, having an anode active substance and an anode electrode tab formed at an edge of the anode plate in longitudinal direction; and a separator strip interposed between the cathode plate and the anode plate, wherein each of the cathode electrode tab and the anode electrode tab has an insulation layer coating on a predetermined area that covers from a boundary of the cathode electrode tab and the cathode plate or the anode electrode tab and the anode plate, so as to prevent the cathode electrode tab from contacting the anode active substance or the anode electrode tab from contacting the cathode active substance to cause an internal short as the separator contracts. The predetermined area has height of 1 to 2 mm from the boundry, but not to 3 mm because it may affect a welded portion for welding a conductive lead.
The lithium battery having a pluality of electrode tabs, each electrode tab having an insulation layer according to the present invention can avoid a rapid hazard by a mechanism of suppressing the voltage sharply down to zero with the voltage dropping slowly and the temperature rising slowly when internal short of the cell continuously occurred. Therefore, it can prevent thermal runaway of the lithium battery.
The technical content of invention will be explained in more detail below with reference to a few figures. However, the figures are intended solely for illustration and not to limit the inventive concept.
Next, a method for manufacturing a lithium battery 10 having a tab with an insulation layer includes steps of coating an insulation layer on a cathode electrode tab 101 of a cathode plate 102; and winding a stack of the cathode plate 102 having cathode electrode tab 101 and the anode plate having an anode electrode tab 103 to form the lithium battery 10, for example, Z winding type lithium battery. After winding the stack of the cathode plate 102 and the anode plate, the lithium battery 10 is activated. The insulation layer includes polyethylene oxide), aluminum oxide and ethanol with parts of 1˜2:2˜4:50˜100, preferred parts of 2:4:100, wherein ethanol is a solvent for mixing polyethylene, oxide) and aluminum oxide. The insulation layer has height of 1 to 2 mm from the bottom of the cathode electrode tab and the anode electrode tab. The insulation layer has a thickness of 1˜5 μm.
Next, the lithium battery 10 having a tab with an insulation layer proceeds a safety test. Also, the lithium battery 10 is disassembled to observe the internal change thereof after the safety test.
(High Temperature Test of 130° C.)
The lithium battery is placed in a oven with temperature rising to 130° C. and retaining 50 minutes. As shown in
The three sets of the lithium battery having a tab without an insulation layer should have serious internal short based on the result that the voltages are not stable. On the other hand, the three sets of the lithium battery having a tab with an insulation layer should only have minor internal short based on the result that the voltages are stable. Also, it can be observed that the separator of the lithium battery having a tab without an insulation layer is contracted under the anode plate to cause the internal short happening between cathode electricity collector (aluminum) and anode active substance. In contrast, the lithium battery having a tab with an insulation layer has a minor internal short and stable voltage because the tab has an insulation layer.
The lithium battery is disassembled to observe the internal change thereof after the 130° C. test. It can be found that the separator the lithium battery having a tab without an insulation layer is contracted seriously under the cathode tab and changes color, even produces stains on the cathode plate. It is obvious the lithium battery having a tab without an insulation layer has a serious internal short. In contrast, the separator of the lithium battery having a tab with an insulation layer is contracted slightly and does not change color, and does not produce black dots on the cathode plate. Therefore, the lithium battery having a tab with an insulation layer has a minor internal short.
(High Temperature Test of 150° C.)
The lithium battery is placed in a oven with temperature rising to 150° C. and retaining 50 minutes. As shown in
Also, it can be observed that the separator of the lithium battery having a tab without an insulation layer is contracted under the anode plate to cause the internal short happening between cathode electricity collector (aluminum) and anode active substance. In contrast, the lithium battery having a tab with an insulation layer has a minor internal short and stable voltage because the tab has an insulation layer.
(Nail Penetration Test)
The nail penetration test is a durable test of cell of battery under the internal short, which determines whether the battery can pass the test by happening explosion or catching fire. The test may use a tungsten nail with a tip diameter of 5 mm to press but not to penetrate the housing of the battery by controlling the forward velocity of 10 mm/s. Accordingly, the cathode plate and the anode plate are pressed to form an internal short in a local area. The tungsten nail stops forward when measuring a transient voltage declining rate of a battery equal to or higher than 100 mV. The changes of appearance, voltage and temperature of the battery are observed. Also, IR image thermometer can be used to observe the temperature diffusion and distribution of the battery for understanding the internal short of the battery. Therefore, it is a relatively simple method of short circuit test.
Therefore, it can be found that the lithium battery having a tab with an insulation layer is safer than the lithium battery having a tab without an insulation layer based on the change of voltage and temperature of the high temperature tests of 130° C. or 150° C. . Also, it can be observed that the lithium battery having a tab without an insulation layer may happen bag-breaking and catching fire under 150° C. due to the internal short.
The lithium battery is disassembled to observe the internal change thereof after the 130° C. test. It can be found that the separator the lithium battery having a tab without an insulation layer is contracted seriously under the cathode tab and changes color, even produces stains on the cathode plate. Also, it can be observed that the lithium battery having a tab without an insulation layer happens bag-breaking and catching fire under 150° C. due to the internal short. Therefore, the mechanism of the internal short should be two stages that firstly the separator is contracted due to the external high temperature that causes the tab of cathode plate to contact with anode plate bringing short, and then the internal short gets serious to increase the heat generation and the separator is contracted more seriously to cause the internal short getting serious, even igniting electrolyte to catch fire.
In the nail penetration test, the curves indicating the lithium battery having a tab with an insulation layer are not obviously different to the curves indicating the lithium battery having a tab without an insulation layer in the temperature change. However, it can be found that the lithium battery having a tab with an insulation layer happens bag-breaking and catching fire slower than the lithium battery having a tab without an insulation layer. The amount of flame produed from the lithium battery having a tab with an insulation layer is less than the amount of flame produed from the lithium battery having a tab without an insulation layer.
Therefore, it can enhance battery safety at high temperature and reduce the internal short by coating an insulation layer including aluminum oxide on tabs.
The invention is not limited to these embodiments, but various variations and modifications may be made without departing from the scope of the invention.
This application is a Continuation-in-Part Applications of U.S. application Ser. No. 13/404,013 filed on Feb. 24, 2012. The entire disclosure is incorporated herein by reference.