This application is a National Stage application of International Application No. PCT/IB2013/060078, filed Nov. 12, 2013, which claims the benefit of International Application No. PCT/IB2012/057329, filed Dec. 14, 2012.
The invention relates to high voltage stable and high density lithium metal oxide powderous compounds, containing a core having stoichiometrically controlled lithium content and an electron insulating surface. The compounds may comprise known elements such as Mg, Ti, Zr, Er, Nd, Nb and Al for obtaining improved high voltage electrochemical performances and improved energy density. Also a method to manufacture these materials is disclosed. The lithium transition metal oxide powder can be used as a cathode active material in rechargeable lithium batteries.
Due to their high energy density, rechargeable lithium and lithium-ion batteries can be used in a variety of portable electronics applications, such as cellular phones, laptop computers, digital cameras and video cameras. Commercially available lithium-ion batteries typically consist of graphite-based anode and LiCoO2-based cathode materials. As today's consumer electronics demand rechargeable batteries with higher energy density, there is a surge towards LiCoO2-based materials with increased specific capacity for more demanding end applications.
Two common ways to improve the energy density are (a) to increase the charge voltage, typically 4.5V or even 4.6V vs. Li metal when fitted in coin cells, and 4.35V and 4.4V vs. graphite when fitted in full cells, which requires more robust cathode materials which can be charged at higher voltage and (b) to increase the packing density, which requires to increase the particle size of the powder particles. Industrial applicability of these two approaches is however limited by side problems. On one hand, increasing the charge voltage leads to unstable behavior of the electrode, resulting in cathode degradation linked with electrolyte decomposition. As lithium is removed from LixCoO2 (x<1), oxidation of Co3+ to an unstable oxidation state Co4+ follows. The higher the charge voltage, the higher the amount of Cot Large concentrations of Co4+ increase unwanted side reactions between electrolyte and charged cathode. These side reactions result in poor safety, poor cycling stability at elevated voltage and of poor storage properties of charged cathode at elevated temperature. On the other hand, increasing the particle size to increase the packing density impairs power capabilities of rechargeable batteries. In order to meet the power requirements, the battery as a whole and particularly the active cathode material itself must have a sufficient high rate performance. Increasing the mean particle size reduces the solid-state lithium diffusion length which eventually results in lowered rate performance.
Careful studying of published results on cathode materials allows to better understanding the limitations of LiCoO2 based rechargeable lithium batteries. A fundamental limitation of state of the art LiCoO2-based materials development lies in the Li-excess and particle size dilemma. In WO2010-139404, the authors illustrate the relationship between packing density, mean particle size and lithium excess used for the preparation of state of the art Mg and Ti doped LiCoO2. In short, the higher the packing density, the higher the particle size and the higher the Li-excess, expressed as Li:Co>>1.00—typically Li:Co is around 1.05—used for the synthesis. The mechanism is based on a so-called “lithium-flux effect” where the Li-excess acts as a flux enhancing the growth of LiCoO2 particles which eventually increases the packing density. Typical packing densities of ca. 3.70 g/cm3 are achieved for 18 μm particles. Authors also emphasize that large pressed densities are preferable and obtained with monolithic, potato-shaped and non agglomerated primary LiCoO2 particles. Use of larger Li:Co excesses to achieve larger monolithic particles results however in poor electrochemical performances, with lower C-rate and lower discharge capacity, which in return cancels energy density gains achieved by increasing the particle size. Such large Li:Co values also increase pH, free base content and carbon content, which impairs safety, storage and bulging properties of charged cathodes. Levasseur, in Chem. Mater., 2002, 14, 3584-3590 establishes a clear relationship between the increase of structural defect concentrations, as evidenced by means of 7Li MAS NMR, and the increase of Li:Co excess.
As a consequence, current state of the art synthesis does not allow to achieve dense, monolithic LiCoO2-based particles with reduced Li:Co excess. Partial improvements have been achieved but the above basic problems have not yet been fully resolved. Hence there is clearly a need for high capacity LiCoO2 based cathodes which can be cycled in a stable manner in real cells at higher voltages.
In the prior art several approaches have been suggested to cope with this problem. To achieve high voltage stability, LiCoO2 materials are usually coated (for example with Al2O3) or otherwise chemically modified (e.g. by providing a fluorinated surface). A problem is that coated dense LiCoO2 often has a lower reversible capacity, so that a part of the gain of energy density by charging to higher voltage is annulled by lower intrinsic capacity. This effect can be observed for aluminum oxide protective and LiF protective coatings, but similar effects are observed for other coating approaches such as ZrO2, AlPO4 . . . .
US2012/0052381 discloses a positive electrode active material comprising a lithium-transition metal composite oxide having at least one metallic compound selected from the group consisting of an aluminum compound, a zinc compound, a zirconium compound, a magnesium compound, and a rare earth compound—such as erbium—adhered to a surface of the lithium-transition metal composite oxide.
US2009/0136854 discloses a lithium composite oxide represented by the general formula LixM1-yLyO2 (where 0.85≦x≦1.25, 0≦y≦0.50) and element M is at least one selected from the group consisting of Ni and Co, and element L is at least one selected from the group consisting of alkaline earth elements, transition metal elements, rare earth elements, Group IIIb elements and Group IVb elements. A surface layer of the active material particles includes an element being at least one selected from the group consisting of Al, Mn, Ti, Mg, Zr, Nb, Mo, W and Y.
Studying the literature furthermore tells us that coating might not be necessary at all to achieve high voltage stability. Chen a Dahn (Electrochem. Solid-State Lett., Volume 7, Issue 1, pp. A11-A14 (2004)) for example report that a fresh prepared LiCoO2 could cycle in a stable manner at 4.5V if tested in coin cells with Li metal anodes. Such an approach might be correct for coin cells but the effect cannot be reproduced in real commercial cells. These results are confirmed by the fact that now, several years after the publication, special treated—and not pure—LiCoO2 is commercially sold for high voltage applications.
Currently no other strategies are known which lead to high voltage performances. It is an object of the present invention to define a cathode material having a high packing density, high rate performance, improved discharge capacity and showing high stability during extended cycling at high charge voltage for high end secondary battery applications.
The present invention discloses a cathode material having a high packing density, a high rate performance, improved discharge capacity and showing high stability during extended cycling at high charge voltage.
Viewed from a first aspect, the invention can provide a lithium metal oxide powder for use as a cathode material in a rechargeable battery, consisting of a core material and a surface layer, the core having a layered crystal structure consisting of the elements Li, a metal M and oxygen, wherein the Li to M molar ratio is between 0.98 and 1.01, and preferably between 0.99 and 1.00, wherein the metal M has the formula M=Co1-a M′a, with 0≦a≦0.05, preferably 0<a≦0.03, and more preferably 0<a≦0.01; wherein M′ is either one or more metals of the group consisting of Al, Ga and B; and the surface layer consisting of a mixture of the elements of the core material and inorganic N- and N′-based oxides, wherein N is either one or more metals of the group consisting of Mg, Ti, Fe, Cu, Ca, Ba, Sn, Sb, Na, Zn and Si; and wherein N′ is either one or more metals of the group consisting of the 4d transition metals and the rare-earth metals. In one embodiment N′ is either one or more metals of the group consisting of Y, Zr, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, Ce, Pr, Nd, Gd, Dy, and Er. In one embodiment, the Li content is stoichiometrically controlled, meaning that the ratio Li/M=1.00±0.01.
The core has a layered structure—it is known that lithium cobaltite consists of layers of lithium that lie between slabs or layers of octahedra formed by cobalt and oxygen atoms—and may be substantially free from oxygen vacancies and Li substitution for M in the MO2 layers of the layered crystal structure. Also, the core material may be substantially free from paramagnetic metals such as Co2+ and intermediate spin Co3+ and Co4+. All of the metals in M may be diamagnetic and trivalent. The Li in the core may thus occupy a crystallographic site surrounded by trivalent diamagnetic metals. In one embodiment the thickness of the surface layer is less than 100 nm. In another embodiment, the thickness of the surface layer may be less than 0.008 times the average particle size D50.
In one embodiment, the powder has the general formula LiCo1-a-b-cM′a M″b M′″c O2, with 0≦a≦0.05, 0≦b≦0.02 and 0≦c≦0.02, M′ comprising either one or more elements from the group B, Al, Ga; M″ comprising either one or more elements from the group Mg, Ti, Fe, Cu, Ca, Ba, Y, Sn, Sb, Na, Zn, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, Ce, Pr, Nd, Gd, Dy, Er and Yb; M′″ comprising either one or more elements from the group F, P, S, Zr. The elements F, P and S may be present on the surface under the form of LiF, Li3PO4 and Li2SO4. In another embodiment, the concentration of M′ and M″ at the surface of the lithium metal oxide powder is at least 5 times the concentration of M′ and M″ in the bulk of the powder. In still another embodiment, M′ and M″ consists of Al, Mg, Ti and either one or more of Nd, Nb and Er; the Al content being between 0.1 and 1 mol %, the Mg content being between 0.1 and 1 mol %, and the Ti content between 0.1 and 0.5 mol %. The lithium metal oxide powder of the different embodiments may have a mean particle size D50 of at least 5 μm, preferably at least 8 μm, and more preferably at least 12 μm. In one embodiment the powder has a mean particle size D50 of at least 15 μm.
In one embodiment the powder has a 7Li MAS NMR spectrum characterized by a single Li contribution centered around −0.5 ppm, and wherein the powder has a reversible electrode capacity of at least 200 mAh/g, preferably 210 mAh/g and most preferably 215 mAh/g when used as an active component in a cathode which is cycled between 3.0 and 4.6 V vs. Li+/Li at a discharge rate of 0.1 C, preferably at 1 C at 25° C. This lithium metal oxide powder may have a 1 C rate capacity fading below 60%, preferably below 40% and most preferably below 30%. The lithium metal oxide powder may also have a 1 C capacity fading inferior to 60%, preferably inferior to 40% and most preferably inferior to 30%.
In another embodiment, the lithium metal oxide powder has a spin lattice relaxation time T1 of at least 500 ms, preferably at least 750 ms and most preferably at least 900 ms. The lithium metal oxide powder of the invention may also have a total base content of less than 50 μmol/g, preferably less than 25 μmol/g, and more preferably less than 15 μmol/g. In one embodiment, the lithium metal oxide powder may have a carbon content less than 50 ppm, preferably <35 ppm, and more preferably 25 ppm. In another embodiment, the lithium metal oxide powder may have an electrical conductivity less than 10−4 S/cm, preferably less than 10−5 S/cm.
The lithium metal oxide powder of the invention may comprise at least 97 mol % of a stoichiometric compound having the general formula Li Co1-aMa O2, with 0<a≦0.05, preferably 0<a≦0.01, and M comprising either one or more elements from the group Al, B and Ga.
In still another embodiment, the lithium metal based powder has a bimodal particle shape distribution with a small and a large particle size fraction, where the small particle size fraction has a D50≦5 μm and represents between 3 to 20 Vol %, and where the large particle size fraction has a D50≧12 μm, preferably D5≧15 μm. It is possible, in some embodiments to have a pressed density of at least 3.40 g/cm3, preferably at least 3.70 g/cm3, and most preferably at least 3.80 g/cm3 for the powder.
Viewed from a second aspect, the invention can provide a method for manufacturing a lithium metal oxide powder, the metal M having the formula M=Co1-aM′a, with 0≦a≦0.05, preferably 0≦a≦0.01, wherein M′ is either one or more metals of the group consisting of Al, Ga and B, comprising the steps of:
Viewed from a third aspect, the invention can provide a method for manufacturing a lithium metal oxide powder consisting of a core material and a surface layer, the core material having a layered crystal structure consisting of the elements Li, a metal M and oxygen, wherein the Li to M molar ratio is between 0.98 and 1.01, and preferably between 0.99 and 1.00, wherein the metal M has the formula M=Co1-aM′a, with 0≦a≦0.05, preferably 0≦a≦0.01, wherein M′ is either one or more metals of the group consisting of Al, Ga and B; and the surface layer consisting of a mixture of the elements of the core material and inorganic N- and N′-based oxides, wherein N is either one or more metals of the group consisting of Mg, Ti, Fe, Cu, Ca, Ba, Sn, Sb, Na, Zn and Si; and wherein N′ is at least one metal of the group consisting of the 4d transition metals and the rare-earth metals.
comprising the steps of:
In some embodiments, each of the sintering step at T1 and the sintering step at T2 is performed during a time between 6 and 24 hours.
In an alternative embodiment, the invention can provide a method for manufacturing the lithium metal oxide powder described before, comprising the steps of:
In the method embodiments above, the first and the second Co- or Co and M′-comprising precursor may be the same “M-precursor” compound. When a=0, M=Co, and M′ is absent and when a>0 for each Co-comprising precursor powder mentioned above; the first, the second and the third Co-comprising precursor powders may be either one of the group consisting of cobalt oxide, cobalt oxy-hydroxide, cobalt hydroxide, cobalt carbonate and cobalt oxalate. In one embodiment, the first, the second and the third Co-comprising precursor powders further comprise at least one element of the group consisting of Al, Ti, Mg, F and Ca.
In another embodiment, in the methods described before, the ratio of the average particle sizes of the Li-enriched lithium metal oxide and the second Co- or Co and M′-comprising precursor powder is at least 3:1, preferably at least 4:1 and most preferably at least 5:1. The particles of the Li-enriched lithium metal oxide and the second M-comprising precursor powders retain a bimodal particle size distribution upon second firing. In still another embodiment the pressed density of the bimodal particle size powder is at least 0.1 g/cm3 higher than the pressed density of the Li-enriched lithium metal oxide.
Viewed from a fourth aspect, the invention can provide the use of the lithium metal oxide powder described before as a cathode in an electrochemical cell.
a:
7Li MAS NMR spectrum of LCO-1 at full scale. Lines marked with asterisks (*) indicate spinning sidebands and are artifacts from the measurements.
b:
7Liu MAS NMR spectrum of LCO-1 at 50 times expanded intensity scale (116 MHz, spinning 30 kHz, synchronized echo). Lines marked with asterisks (*) indicate spinning sidebands and are artifacts from the measurements.
a:
7Li MAS NMR spectrum of Ex1 at full scale. Lines marked with asterisks (*) indicate spinning sidebands and are artifacts from the measurements.
b:
7Li MAS NMR spectrum of Ex1 at 100 times expanded intensity scale (116 MHz, spinning 30 kHz, synchronized echo). Lines marked with asterisks (*) indicate spinning sidebands and are artifacts from the measurements.
In the drawings and the following detailed description, preferred embodiments are described in detail to enable practice of the invention. Although the invention is described with reference to these specific preferred embodiments, it will be understood that the invention is not limited to these preferred embodiments. But to the contrary, the invention includes numerous alternatives, modifications and equivalents as will become apparent from consideration of the following detailed description and accompanying drawings.
In some embodiments, the invention concerns lithium metal oxide powder consisting of a core material and a surface layer, the core having a layered crystal structure consisting of the elements Li, a metal M and oxygen, wherein the Li to M molar ratio is between 0.98 and 1.01, and preferably between 0.99 and 1.00, wherein the metal M has the formula M=Co1-aM′a, with 0≦a≦0.05, wherein M′ is either one or more metals of the group consisting of Al, Ga and B; and the surface layer consisting of a mixture of the elements of the core material and inorganic N- and N′-based oxides, wherein N is either one or more metals of the group consisting of Mg, Ti, Fe, Cu, Ca, Ba, Y, Sn, Sb, Na, Zn, Zr and Si; and wherein N′ is either one or more metals of the group consisting of Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, La, Ce, Pr, Nd, Gd, Dy, Er and Yb. In one embodiment N=Mg and Ti, and N′ is either Nb, or Nd, or Er. In another embodiment the surface layer comprises inorganic oxides of Mg, Ti and Zr.
In one embodiment, the core of the material of the present invention has the formula Li1.00±0.01MO2 wherein M has the formula M=Co1-aM′a with 0≦a≦0.05, wherein M′ is either one or more metals of the group consisting of Al, Ga and B and wherein the Li to M molar ratio is between 0.98 and 1.01, and preferably between 0.99 and 1.00. In another embodiment the core material has hexagonal layered crystal structure described as an ordered rock salt-type crystal structure with space group R-3m. The core may be substantially free from structural defects such as oxygen vacancies and Li substitution for M in the MO2 layers, and also substantially free from paramagnetic metals such as Co2+, intermediate spin Co3+ and Co4+.
The existence of a defect-free core is an inherent feature of the cathode material of the actual invention. The inventors observed that a defect-free core, enabling faster diffusion of Li ions into the particles, is related to the high observed rate performance and improved discharge capacity of the disclosed cathode materials.
The surface layer has an inhomogeneous composition compared to the core with a compositional gradient of the different M, M′, Li and O elements. The surface is enriched of elements N and N′ such as Mg, Ti, Fe, Cu, Ca, Ba, Y, Sn, Sb, Na, Zn, Zr, Si, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, Ce, Pr, Nd, Gd, Dy and Er; and, in one embodiment, is formed by segregation from the core and accumulation of these metal dopants at the surface of the particles. In the core, these dopants are substantially absent. Authors could not indisputably establish the chemical nature of the oxides formed at the surface and therefore speculate that, for example in the case of Mg, Si and Ti doping, possible forms, but not limited to, are LiMO2, MgO, CoO, Co1-φ1MgφO with φ≦1, Co3O4, Mg6Co3-δO4 with δ≦1, TiO2, Li2TiO3, SiO2, LiεSiλOπ with 2≦ε≦8, 1≦λ≦2 and 3≦π≦7, Li2ZrO3, Li6Zr2O7, LiNdO3, LiNdO2, LiErO2. These assumptions are supported by the XPS experiments where the binding energies observed for Co, Mg and Ti, Al, Zr, Er, Nd, Nb are typical of oxygen environment and the low electrical conductivity of the particles as the above mentioned oxides are expected to be strong insulators. Also, the binding energies of Co and M′ (Al, B, Ga) are typical of 0 and Li environment as found in LiMO2 described in trigonal R-3m crystal system. Where it is said that the surface layer consisting of a mixture of the elements of the core material (Li, M, O) and inorganic N- and N′ based oxides, by “N- or N′-based” oxides are meant also those oxides incorporating Li atoms.
The surface is densely and continuously connected to the core and cannot be physically separated from the particle. Hence in another embodiment the concentration in N and N′ metals—with increasing distance from the surface—decreases, possibly in a gradient-like manner and approaches zero in the inside of the particles. The N- and N′-enriched surface of the particles feature two additional and unexpected properties:
The surface layer is typically between 20 nm to 200 nm, and preferably between 20 nm and 100 nm thick, and is primarily affected by two parameters:
(i) the N and N′ content: the thickness increases when the N and N′ content increases.
(ii) the particle size distribution of the powder materials. The lower the particle size for a given amount of N and N′, the thinner the surface layer. A too thick layer is not desirable as it results in increased polarization and eventually in lower rate performance. Conversely, a too thin layer is also not advantageous as it will provide bad shielding against electrolyte and be less efficient in preventing parasitic-reactions.
As initially said, an essential feature of LiCoO2-based cathode materials is a high packing density, which allows increasing the energy density of commercial secondary batteries. In the present invention, a preferred morphology embodiment to achieve high packing density consists in monolithic, potato-shaped and non-agglomerated particles. A monolithic particle does not exhibit inner porosity, and it does not consist of agglomerates of smaller primary particles. A typical particle size (D50) is a least 5 μm or even at least 10 μm, and preferably above 15 μm. The pressed density is typically in the range of over 3.40 g/cm3 and preferably at least 3.70 g/cm3. In one embodiment, the pressed density is as high as 3.90 g/cm3. In another embodiment the pressed density is at least 3.40 g/cm3 for a powder with an average particle size above 6 μm. In still another embodiment the pressed density is at least 3.75 g/cm3 for a powder with an average particle size above 15 μm.
In a method embodiment for manufacturing a lithium metal oxide powder consisting of a core material and a surface layer, the core material having a layered crystal structure consisting of the elements Li, a metal M and oxygen, wherein the Li to M molar ratio is between 0.98 and 1.01, and preferably between 0.99 and 1.00, wherein the metal M has the formula M=Co1-aM′a, with 0≦a≦0.05, preferably 0≦a≦0.01, wherein M′ is either one or more metals of the group consisting of Al, Ga and B; and the surface layer consisting of a mixture of the elements of the core material and inorganic N- and N′-based oxides, wherein N is either one or more metals of the group consisting of Mg, Ti, Fe, Cu, Ca, Ba, Y, Sn, Sb, Na, Zn, Zr and Si; and wherein N′ is either one or more metals of the group consisting of Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, Ce, Pr, Nd, Gd, Dy, and Er;
the method comprises the steps of:
(i) providing a first mixture of a first Co- or Co and M′-comprising and a first Li-comprising precursor powder, the first mixture having a Li to metal molar ratio >1.01,
(ii) sintering the first mixture in an oxygen comprising atmosphere at a temperature T1 of at least 600° C., thereby obtaining a Li-enriched lithium metal oxide powder,
(iii) providing a second Co- or Co and M′-comprising precursor powder, and
(iv) mixing the Li-enriched lithium metal oxide compound and the second Co- or Co and M′-comprising precursor powder, thereby obtaining a second mixture wherein the Li to M molar ratio is between 0.98 and 1.01, and preferably between 0.99 and 1.00, and
(v) sintering the second mixture in an oxygen comprising atmosphere at a temperature T2 of at least 600° C.;
wherein either one or more of the Li-enriched lithium metal oxide powder, the first Co- or Co and M′-comprising, the first Li-comprising, and the second Co- or Co and M′-comprising precursor powders further comprises at least one element of the group consisting of Mg, Ti, Fe, Cu, Ca, Ba, Y, Sn, Sb, Na, Zn, Zr and Si; and the same or another precursor comprises at least one metals of the group consisting of Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, Ce, Pr, Nd, Gd, Dy, and Er.
Later in the text, steps (i) and (ii) are further referred as “the first firing” and steps (iii), (iv) and (v) as the “second firing”. Different implementations of the actual invention are possible, especially regarding the process conditions, the nature of the different precursors and their sequence of blending.
The first M-comprising precursor and second M-comprising precursor can be a mixture of cobalt containing precursor and M′ containing precursor. Examples of suitable cobalt containing precursors include cobalt oxide, hydroxide, oxyhydroxide, carbonate and oxalate. The M′ containing precursor can be an oxide, hydroxide or organic complex, preferably having sub-micrometric powderous morphology in order to achieve homogeneous distribution and easy blending process.
In several embodiments, either one of the Li-enriched lithium metal oxide, the first M-, the second M- and the first Li-comprising precursor powders further comprises dopants (M′, N, N′) from the group consisting of Al, Ga, B, Mg, Ti, Fe, Cu, Ca, Ba, Y, Sn, Sb, Na, Zn, Zr, Si, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, Ce, Pr, Nd, Gd, Dy and Er. In one of the method embodiments, either one or both of the first M- and the first Li-comprising precursor powders further comprise at least one element of the group consisting of Mg, Ti, Fe, Cu, Ca, Ba, Y, Sn, Sb, Na, Zn, Zr, Si, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, Ce, Pr, Nd, Gd, Dy, Er, F, P and S. A homogeneous distribution of N and N′ dopant elements is of primary importance and can be improved by using this process embodiment. In an alternative process embodiment, the homogeneous dispersion of N and N′ dopants is improved when the second M-comprising precursor powder further comprises at least one element of the N, N′ dopant element group consisting of Mg, Ti, Fe, Cu, Ca, Ba, Y, Sn, Sb, Na, Zn, Zr, Si, Nb, Mo, Ru, Rh, Pd, Ag, Cd, Sc, Ce, Pr, Nd, Gd, Dy and Er. Examples of suitable compounds comprising N, N′ elements are oxides (such as MgO, TiO2, SiO2, . . . ), fluorites (such as MgF2 . . . ) with sub-micrometric particle size. Examples of suitable compounds comprising N′ elements are preferably sub-micrometric oxide powders such as ZrO2, Nb2O5, Nd2O3, Er2O3; hydrated nitrates such as Nd(NO3)3.6H2O and Er(NO3)3.5H2O and fluorides . . . .
In one particular embodiment, Ti, Mg, Zr and Nb, are preferably in the form of TiO2, MgO, ZrO2, Nb2O5. Particles with a D50 of respectively less than 100 nm for ZrO2 and TiO2, and less than 1 μm for Nb2O5 and MgO are added to either one or both of the first and second mixtures described above. In one embodiment, Nd and Er in their hydrated nitrate salt are added to the LiCoO2 particles using a wet process. This method allows achieving homogeneous distribution of rare-earth metals on the particles. On the other hand, a dry method, based on nano-sized rare-earth oxide powder, is preferred as it offers a cheap and more convenient route for mass production.
In another embodiment, Al, preferably in the form of Al2O3 particles with a D50 of less than 100 nm is added to the second mixture described above. In another particular embodiment the Li-enriched lithium metal oxide compound is LiCoO2 with dense monolithic particles of at least 5 and preferably at least 10 to 20 micrometers. Many commercial prior art LiCoO2 materials already have this desired morphology.
In yet another particular embodiment the second M comprising precursor features a particle size distribution with a D50 of less than ⅓, preferably less than ¼ of the D50 of the Li-enriched lithium metal oxide compound. In one embodiment, the size ratio between the second M comprising precursor and the Li-enriched lithium metal oxide compound is ⅙. In the latter case and after the second firing, a bimodal distribution is obtained wherein the LiMO2-based particles originating from the second M comprising precursor are small enough to (a) support a very high C rate and (b) fit nicely in the voids of the larger lithium metal oxide particles packing, which allows for low porosity electrodes and a high volumetric energy density.
The Li-enriched lithium metal oxide compound, referred as the state of the art compound, obtained after the first sintering step, is further characterized by:
On the contrary, by finely controlling the lithium stoichiometry, the cathode materials of the present invention, obtained after the second sintering step, are characterized by:—a unique NMR contribution centered around 0 ppm,
The Li content of the materials of the present invention is stoichiometrically controlled meaning that the Li:M molar ratio is in the range of 0.98-1.01. Authors have observed that if the targeted Li:M is above 1.01, then the electrochemical performances, such as lower discharge capacity and lower high voltage stability, and physical properties such as an increase of base content and carbon content, of the resulting material are inferior. Likewise, if the targeted Li:M is below 0.98, then the materials, though retaining very good high voltage stability, undergo two undesirable effects: (i) less active materials is available and the discharge capacity is lowered, and, (ii) a surface enriched in cobalt-based spinel is formed at the surface of particles, which increases the cell polarization.
The inventors have made two surprising observations, which are believed to be essential aspects of the invention:
First Observation:
The core of the particles is lithium stoichiometric and substantially free from defects. The lithium metal oxide according to the present invention shows electrochemical properties different from those of lithium metal oxides, which are prepared according to state of the art methods, and which contain the same components as the lithium metal oxide of the present invention. This change in physical properties can be observed by 7Li-NMR. In 7Li-NMR, when a strong magnetic field is externally applied to a lithium-containing material, Li chemical shift values will be shifted due to various hyperfine interactions between a lithium nucleus having a nuclear magnetic moment and the unpaired electrons of metal components contained in the lithium-containing material. The local structural and electronic characteristics of a specific component in the crystal structure of the lithium-containing material can be assessed by measuring the different contributions to the 7Li NMR spectrum caused by such chemical shift values.
In a state of the art Ti and Mg-doped lithium cobalt oxide (in the Examples below the materials LCO-1, LCO-3, LCO-4, LCO-6 & LCO-7), prepared according to a conventional method, a sharp peak at around −0.5 ppm in 7Li NMR spectra, and additional peaks having their center of mass at around 185 ppm, 5 ppm, −7 ppm, −16 ppm and −40 ppm, are observed (see
In comparison with this, it can be seen that the lithium metal oxide of the present invention shows a unique Li peak around −0.5 ppm though having the same components and composition as those of a lithium metal oxide prepared according to a state of the art method. Consequently, Ex 1 to 9 (see below) contain only one Li site environment solely surrounded by diamagnetic trivalent metal ions such as Co3+)(t2g6eg0) or Al3+ (2p6). The core of the Example materials is therefore substantially free from paramagnetic impurities, structural defects and dopants N such as Mg2+, Ti3+ or Ti4+.
This observation is further confirmed by the measurement of the T1 spin-lattice relaxation time which clearly evidences that paramagnetic spin concentration is larger in the state of the art LiCoO2-based materials when compared to the cathode materials of the present invention.
Second Observation:
When dopants N and N′ are present, the surface is formed during the second sintering by spontaneous segregation of the dopants from the core. The exact mechanism of this “in-situ” coating is unknown but authors assume that it is privileged when the lithium stoichiometry is finely controlled and Li:M molar ratio of 0.98-1.01. In this case a cooperative reaction occurs where the core of the particle becomes lithium stoichiometric and N and N′ dopants such as Mg and Ti, Zr, Nb, Nd and Er are expelled and accumulated at the surface of the particles and at the grain boundary. As mentioned above, this is corroborated by NMR observations.
Linked to this, another important feature of the cathode materials of the present invention are their “insulating” nature. These cathode materials have conductivities which are at least 2-3 orders lower than those of the least conductive currently known cathode material. For example, commercial LiCoO2 has a relatively high electrical conductivity in the range of 10−2 to 10−3 S/cm. That such insulating cathodes can yield excellent electrochemical performance, namely a large discharge capacity and C-rate performance, is a surprise because it is commonly accepted that high electrical conductivity is needed for the Li+ cation diffusion within the solid cathode and across the interface between electrolyte and cathode.
It is believed that the low conductivity provided by the surface layer is the main reason for the high voltage stability of the cathode materials of the present invention. When a LiCoO2-based cathode is charged to high voltage—meaning the cathode is strongly de-intercalated—we achieve a LixCoO2 (x>>1) composition where most of the cobalt ions are in the 4+ valence state. Tetravalent-cobalt containing LixCoO2 is a very strong oxidizer and is highly reactive. The electrolyte becomes thermodynamically unstable when in contact with such an oxidizing surface. A reaction with the electrolyte (being the reducing agent) is strongly preferred energetically. Even at low temperature—during normal cycling of a LiCoO2 cathode at high voltage—this reaction proceeds slowly but continuously. Reaction products cover the cathode surface and the electrolyte is decomposed, and both effects continuously cause a deterioration of the electrochemical performance of the battery. Also, a loss of capacity and a strong increase of resistance—by polarization—is observed.
Obviously, a cathode material protected by an insulating surface layer will solve this problem by physically separating tetravalent cobalt ions from the electrolyte and eventually preventing further electrolyte reduction. By careful selection of the compounds, such as Mg, Zr, Si and Ti, Zr, Nb, Nd and Er, the process allows to achieve an in-situ coating of the final powder with a layer that is enriched in oxidized compounds, like MgO and TiO2, and Zr, Nb, Nd, Er oxides that may also be lithiated. This inert coating layer provides additional safety when the powders are in contact with the electrolyte of the battery.
Measurement of the electrical conductivity is performed under an applied pressure of 63.7 MPa in the 4-probe configuration. In the description and claims the value of 63 MPa is also mentioned as round-off, when the actual pressure of 63.7 MPa is applied.
Electrochemical performances are tested in CR2032 coin type cells, with a Li foil as counter electrode in a lithium hexafluorite (LiPF6) type electrolyte at 25° C. The active material loading is 10.5 (±0.5) mg/cm2. Cells are charged to 4.3V and discharged to 3.0V to measure rate performance and capacity. The high voltage discharge capacity and capacity retentions during extended cycling are measured at 4.5V and 4.6V charge voltages. A specific capacity of 160 mAh/g is chosen for the determination of the discharge rates. For example, for the discharge at 2 C, a specific current of 320 mA/g is used. The following table is a description of the test that is used for all of the coin cells in this description:
The following definitions are used for data analysis: Q: capacity, D: Discharge, C: Charge, followed by a number to indicate cycle number. For example, the slow high voltage discharge capacity DQ7 is measured during the 7th cycle in the 4.5 (or 4.6)-3.0V range at 0.1 C. The fast high voltage discharge capacity DQ8 is measured during the 8th cycle in the 4.5 (or 4.6)-3.0V range at 1 C.
Irreversible capacity Qirr (%) is ((CQ1−DQ1)/CQ1)×100.
Rate performance is defined by the ratio of DQ at respectively 0.2, 0.5, 1, 2 and 3 C versus DQ at 0.1 C, converted to and expressed in %.
Capacity fade rate—expressed in %—at 0.1 C per 100 cycles is calculated as follows: (1−(DQ31/DQ7))×100/23. Likewise, capacity fade rate at 1 C per 100 cycles is: (1−(DQ32/DQ8))×100/23.
Energy fade rates at 0.1 C and 1 C are calculated in a similar way than capacity fade rate but instead of the discharge capacity DQ the discharge energy (defined as DQ×average discharge voltage) is used in the calculation.
Polarization is measured at cycle 1 and is defined as the difference between the average voltage during the first charge and the first discharge.
7Li magic angle spinning (MAS) NMR spectra is recorded on a Bruker 300 Avance spectrometer at 116 MHz (7.05 T magnet), with a standard 2.5 mm Bruker MAS probe. A combination of single-pulse and Hahn echo sequences is used in MAS conditions (30 kHz spinning speed). The single-pulse sequence with tπ/2=2.0 μs requires a first-order phasing process with a sin(x)/x baseline correction due to the dead time of the spectrometer. The rotor-synchronized Hahn echo sequence [tπ/2−τ1−tπ−τ2] (with τ1=τ2 being equal to one rotor period, i.e. 33.33 microseconds) is used to facilitate the phasing of all the signals and to ensure the observation of possible very wide signals which are lost during the receiver dead time, while refocusing the interactions with electron spins. The 90° pulse duration is equal to tπ/2=2.0 μs. A recycle time of 100 s is used. The isotropic chemical shifts, expressed in ppm, have been obtained using 1M LiCl dissolved in H2O as external reference.
T1 spin-lattice relaxation times are measured using the inversion-recovery sequence on static samples. The T1 is determined by single exponential fitting of the magnetization recovery intensity as function of the recovery delay (from 100 μs to 100 s).
X-ray photoelectron spectroscopy (XPS) measurements are carried out using a Kratos Axis Ultra spectrometer fitted with a focused monochromatized Al Kα radiation (hu=1486.6 eV). For the Ag 3d5/2 line, the full width at half-maximum is 0.58 eV under the recording conditions. The analyzed area of the sample is 300×700 μm2. Peaks are recorded using a constant pass energy of 20 eV. The pressure in the analysis chamber is ca. 5×10−7 Pa. To prevent the sample from moisture and air exposure, sampling is performed in an argon dry box which is directly connected, through a transfer chamber, to the XPS spectrometer. Short acquisition time control spectra are recorded at the beginning and at the end of each experiment to confirm the non-degradation of the samples. The binding energy scale is calibrated from LiCoO2 peaks (Co2p, Co3p and O1s). Core peaks are analyzed using a non-linear Shirley-type background. The peak positions and areas are optimized by a weighted least-square fitting method using 70% Gaussian and 30% Lorentzian line shapes. Quantification was performed on the basis of Scofield's relative sensitivity factors. For depth profiling experiments, the depth has been calculated relatively to a sample of Ta2O5 for which an argon etching speed of 0.32 nm/s has been observed.
The base content is a material surface property that can be quantitatively measured by the analysis of reaction products between the surface and water. If powder is immersed into water a surface reaction occurs. During the reaction the pH of the water increases (“base dissolves”) so the base is quantified by a pH titration. The result of the titration is the “soluble base content” (SBC). The content of soluble base can be measured as follows: 100 ml of de-ionized water is added to 7.5 g of cathode, followed by stirring for 8 minutes. Settling-down is allowed for typically 3 minutes, then the solution is removed and passed through a 1 μm syringe filter, thereby achieving >90 g of a clear solution which contains the soluble base. The content of soluble base is titrated by logging the pH profile during addition of 0.1 M HCl at a rate of 0.5 ml/min until the pH reaches 3 under stirring. A reference voltage profile is obtained by titrating suitable mixtures of LiOH and Li2CO3 dissolved in low concentration in DI water. In almost all cases two distinct plateaus are observed. The upper plateau is OH−/H2O followed by CO32−/HCO3−, the lower plateau is HCO3−/H2CO3. The inflection point between the first and second plateau as well as the inflection point after the second plateau is obtained from the corresponding minima of the derivative dpH/d Vol of the pH profile. The second inflection point generally is near to pH 4.7. Results are listed as micromole of base per g of cathode.
The amount of base which goes into solution is very reproducible, and is directly related to surface properties of the cathode. Since these have a significant influence on the stability (i.e. safety and overcharge/high T storage properties of the final battery) there is a correlation between base content and stability. The soluble base content is discussed more in detail in WO2012-107313.
Preparation of Li:Co stoichiometrically-controlled lithium cobalt based oxides These examples demonstrate that Li:Co stoichiometrically-controlled doped lithium cobalt based oxides featuring a 7Li MAS NMR spectrum characterized by a single Li contribution centered around −0.5 ppm and an increased T1 spin-lattice relaxation time is also characterized by a high voltage cycling stability. The improved stability, single contribution 7Li MAS NMR spectrum and longer T1 are obtained by optimizing lithium to metal ratio.
The characterization of Examples 1 and 2 will demonstrate that Li-stoichiometry controlled LiCoO2-based cathode materials, i.e. having a Li/Co ratio of 1.00±0.01, comprising a core where Li atoms occupy a single site surrounded by trivalent diamagnetic metals, and having an electron insulating surface comprising the elements of the core material (Li, Co) and inorganic metal oxides comprising Mg and Ti show improved features for high voltage applications.
Preparation of LCO-1: 0.25 mol % titanium and 0.5 mol % magnesium doped Co(OH)2 as precursor for LiCoO2 is prepared in a pilot line according to the process explained in WO2010-139404 (a single firing process of the precursors at a temperature between 960° C. and 1020° C.—this process is being used also for LCO-3, -4, -6 & -7). A state of the art titanium and magnesium doped LiCoO2 (noted LCO-1) is obtained by means of a standard high temperature solid state synthesis (=the first firing step) by mixing the precursor with Li2CO3. Typical Li:Co molar ratio used in the Li2CO3— doped Co(OH)2 blend is 1.06 to 1.12. The average particle size of LCO-1 is 20 μm. The final Li:Co mol ratio of LCO-1 after firing measured by ICP is 1.053 and will be used to determine Li:Co ratio for examples 1 and 2. LCO-1 is also referred to as the lithium doped cobalt oxide “parent” of Example 1 and Example 2.
Preparation of Example 1 (noted Ex1): 95 mol % of LCO-1 and 5 mol % of 0.25 mol % Ti and 0.5 mol % Mg doped Co(OH)2; corresponding to respectively 95.24 wt. % and 4.76 wt. %; are mixed in order to target a final Li:Co mol ratio of 1.000. The mass of reagents has been calculated assuming a cobalt weight content in LCO-1 and Co(OH)2 of respectively 60.21 wt. % and 63.40 wt. %, resulting in an absolute error of less than 0.2% in the calculation of Li:Co. The homogeneous mixture is placed in an alumina crucible and heated (=the second firing step) at 925° C. for 12 hours under constant air flow. After cooling, the resulting powder (Ex1) is sieved and characterized. The average particle size of Ex1 is found to be 20 μm.
Preparation of Example 2 (noted Ex2): 94 mol % of LCO-1 and 6 mol % of 0.25 mol % Ti and 0.5 mol % Mg doped Co(OH)2; corresponding to respectively 94.28 wt. % and 5.72 wt. %; are mixed in order to target a final Li:Co mol ratio of 0.990±0.002. The homogeneous mixture is placed in an alumina crucible and heated at 925° C. for 12 hours under constant air flow. After cooling, the resulting powder (Ex2) is sieved and characterized. The average particle size of Ex2 is found to be 20 μm.
The characterization of Example 3 will demonstrate that Li-stoichiometry controlled LiCoO2-based cathode materials, comprising a core where Li atoms occupy a single site surrounded by trivalent diamagnetic metals, where Co is partly substituted by Al3+, and having an electron insulating surface comprising the elements of the core material (Li, Co and Al) and inorganic metal oxides comprising Mg and Ti, show improved high voltage features and large pressed densities.
Preparation of LCO-3: state of the art titanium and magnesium doped LiCoO2 (noted LCO-3) is obtained by means of a standard high temperature solid state synthesis by dry-mixing powders of Co3O4 with TiO2, MgO and Li2CO3. LCO-3 contains 0.25 mol % titanium and 0.25 mol % magnesium. Typical Li:Co molar ratio used for the blend is 1.10. The average particle size of LCO-3 is 18 μm. The final Li:Co mol ratio of LCO-3 after firing—as measured by ICP—is 1.070, and is used to set the Li:(Co+Al) ratio for Example 3.
Preparation of Example 3 (noted Ex3): A cathode powder material is prepared by mixing 85.40 wt. % of LCO-3, 10.51 wt. % Co3O4 with mean particle size of 3 μm, 3.47 wt % Li2CO3, 0.05 wt % of MgO, 0.05 wt % of TiO2 and 0.52 wt % Al2O3, so as to adjust the Al:Co mol ratio to 0.01:0.99 (or 1 mol % Al substitution on Co sites) and the final Li:(Co+Al) molar ratio to 1.000±0.002. The homogeneous mixture is placed in an alumina crucible and heated at 980° C. for 12 hours under constant air flow. After cooling, the resulting powder (Ex3) is sieved and characterized. The average particle size of Ex3 is found to be 16 μm, and a bimodal distribution is obtained.
The characterization of Example 4 will demonstrate that LiCoO2-based cathode materials comprising a core with Li stoichiometry control, where Li occupy a single site surrounded by trivalent diamagnetic metals, and having an electron insulating surface comprising the elements of the core material (Li, Co) and inorganic metal oxides comprising Mg and Ti, are suitable for high power applications where maintaining high C-rate and high average voltage are required.
Preparation of LCO-4: state of the art titanium and magnesium doped LiCoO2 (noted LCO-4) is obtained by means of a standard high temperature solid state synthesis by dry-mixing powders of Co3O4 with TiO2, MgO and Li2CO3. LCO-4 contains 0.18 mol % titanium and 0.40 mol % magnesium. Typical Li:Co molar ratio used for the blend is 1.03. The average particle size of LCO-4 is 6 μm. The final Li:Co mol ratio of LCO-4 after firing—as measured by ICP—is 1.015, and is used to set the Li:Co ratio for Example 4.
Preparation of Example 4 (noted Ex4): 98.5 mol % of LCO-4 and 1.5 mol % of Ti (0.18 mol %) and Mg (0.4 mol %) doped Co3O4; corresponding to respectively 98.77 wt. % and 1.23 wt. %; are mixed homogeneously in order to target a final Li:Co mol ratio of 1.000±0.002. The mass of reagents has been calculated assuming a cobalt weight content in LCO-3 and Co3O4 of respectively 60.21 wt. % and 73.42 wt. %. The mixture is placed in an alumina crucible and heated at 1000° C. for 12 hours under constant air flow. After cooling, the resulting powder (Ex4) is sieved and characterized.
The characterization of Example 5 will demonstrate that high electrochemical performances are only achieved when targeting a lithium stoichiometry of 1.00±0.01. Lithium over stoichiometry, as usually observed in state-of the art LiCoO2-based materials, lead to systematic impairment of the discharge capacity, C-rate and high voltage stability.
Preparation of Example 5a-5e (noted Ex5a-5e): A cathode powder material is prepared by mixing 88.91 wt. % of LCO-3, 10.94 wt. % Co3O4 with mean particle size of 3 μm, 0.12 wt % of MgO and 0.03 wt % of TiO2. Li2CO3 is further added so as to adjust the final Li:Co (or Li:M) ratio to 1.00 (Ex5a), 1.01 (Ex5b), 1.02 (Ex5c), 1.03 (Ex5d) and 1.04 (Ex5e). The homogeneous mixture are placed in alumina crucibles and heated at 980° C. for 12 hours under constant air flow. After cooling, the resulting powders (Ex5a-5e) are sieved and characterized.
The electrochemical properties of Ex5a-5e are shown in Table 1. The rate discharge capacity DQ7 and DQ8 and the 3 C rate performances are strongly improved when the Li:M ratio decreases and is close to 1.00±0.01. The capacity fading at 4.5V is also significantly improved when the Li:M ratio is near stoichiometry. The electrical conductivity is also strongly decreased when Li:M tends to 1.00 and 3 to 4 orders of magnitude lower compared to LCO-3. These properties are clear evidence supporting the mechanism of “electron insulating in-situ coating” where the amount of segregated Mg and Ti increases when Li:M is near stoichiometry. The benefits of a Li-stoichiometric core and of the Mg and Ti enriched surface for high voltage applications are eventually clearly highlighted.
Changes in physical and electrochemical properties of the lithium cobalt based oxides prepared according to the present invention have been characterized before and after the second firing used to control and adjust the Li:M stoichiometry.
SEM Analyses
Surface imaging is performed using a scanning electron microscope (SEM) and is shown on
XRD Analyses
The crystal structure of the lithium cobalt based oxides has been investigated by means of X-ray diffraction. XRD patterns of LCO-1 and Example 1 are shown on
Likewise, XRD patterns of LCO-3, LCO-4, Ex3 and Ex4 are interpreted using the same structural model and similar lattice parameters. Though containing large surface base contents such as LiOH and Li2CO3, LCO-1, LCO-3 and LCO-4 XRD patterns don't allow identifying such compounds, suggesting that their content is below XRD detection limit and/or that the surface base are in amorphous forms.
The XRD pattern of Ex2 is shown on
For Ex3, the homogeneous substitution of Co by Al is confirmed by the increase of the ‘reduced’ c/a ratio defined as (c/(√24a)−1)×1000, being 18.56 and 18.90 for LCO-3 (no Al) and Ex3 (containing 1 mol % Al), respectively. The increase of the c/a ratio upon Al doping of LiCoO2 is in good agreement with other works (such as Myung et al., Solid State Ionics Volume 139, Issues 1-2, 2 Jan. 2001, Pages 47-56 and Gaudin et al., J. Phys. Chem. B, 2001, 105, 8081-8087).
Analysis of Li-Salt Impurities
The surface base and carbon contents of the different materials are listed on Table 2. The base and carbon contents are strongly reduced after the second firing for Ex1, Ex2, Ex3 and Ex4 when compared to LCO-1, LCO-3 and LCO-4. This result supports, as shown by SEM, that the surfaces of LCO-1, LCO-3 and LCO-4 are partly covered with unreacted excess Li salts, such as LiOH and Li2CO3, and that the surfaces of Ex1, Ex2, Ex3 and Ex4 are mostly free from such impurities.
X-Ray Photoelectron Spectroscopy (XPS) Analysis
The chemical composition of the surfaces of the particles of LCO-1 and Ex1 has been investigated by means of XPS. Full scale XPS spectra are shown on
The cobalt 2p and 3p XPS peaks are shown on
(e.g. Daheron et al., J. Phys. Chem. C, 2009, 113, 5843).
The XPS analysis is however revealing clear differences in the chemical composition of the surface of the particles of LCO-1 and Ex1:
The evolution of Mg and Ti as function of particle depth has been monitored for Ex-1 by means of XPS depth profiling as shown on
Electrical Conductivity
The electrical conductivity of the different materials is listed in Table 4.
The electrical conductivity of Ex1 to 4 is three orders of magnitude lower than for the corresponding lithium doped cobalt oxides parents LCO-1, LCO-3 and LCO-4. It is the author's opinion that the lower conductivity originates from two contributions:
The pressed density of the parent phases and examples have been measured and results are shown in Table 5.
The pressed density is measured as follows: 3 grams of powder is filled into a press mold with a diameter “d” of 1.300 cm. A uniaxial load of 2.8t, corresponding to a pressure of 207 MPa, is applied for 30 seconds. After relaxing the load, the thickness “t” of the pressed powder is measured. The pellet density is then calculated as follows: 3/(π×(d/2)2×t) in g/cm3.
All the materials feature very high pressed densities in excess of 3.40 g/cm3 for LCO-4 and Ex4 with an average particle size of 6 μm and in excess of 3.75 g/cm3 for LCO-1, LCO-3, Ex1, Ex2 and Ex3 with an average particle size above 15 μm. The pressed density of Ex3 is increased by 0.1 g/cm3 when compared to LCO-3 which is attributed to the ability of the 3 μm particles to accommodate the vacancies resulting from the packing of 18 μm particles.
7Li MAS NMR
7Li magic angle spinning nuclear magnetic resonance (MAS NMR) spectra of the different Examples are displayed on
One can distinguish two types of patterns:
The sharp peak centered on −0.5 ppm is attributed to lithium ions surrounded by only trivalent diamagnetic Co3+(t2g6eg0) ions as reported in literature (cf. Levasseur et al., Solid State Ionics 2000, 128, 11). A unique Li site solely surrounded by diamagnetic trivalent metal ions is therefore observed for Ex1, Ex2, Ex3 and Ex4.
For LCO-1, LCO-3 and LCO-4, additional paramagnetic contributions at ca. 185 ppm, 5 ppm, −7 ppm, −16 ppm and −40 ppm are resulting from structural defects induced by two main contributions:
The 7Li MAS NMR spectrum of Ex2, despite the presence of spinel-based impurity still features a unique resonance around −0.5 ppm. This characteristics clearly establishes that Ex2, though targeting a Li:Co=0.99, comprises a stoichiometrically controlled LiCoO2 where Li ions accommodate a trivalent diamagnetic metal surrounding and a lithium-free spinel impurity, most probably present at the surface of the particles.
In addition, substitution of the Co3+ by Al3+, both trivalent diamagnetic metal ions, does not modify the 7Li MAS NMR signal of Ex3, which conserves a unique resonance around −0.5 ppm, unambiguously confirming that lithium ions occupy a unique site solely surrounded by trivalent diamagnetic metals. Likewise, this finding can be extended to substitution of Co3+ ions by trivalent diamagnetic metals such as Al3+, Ga3+ and B3+ that will not modify the 7Li MAS NMR signal of Li-stoichiometric LiCo1-aM′aO2 with M′=Al, B and Ga.
The relative absence of structural defects is further characterized by measuring the T1 spin-lattice relaxation time as shown in Table 6. The T1 value of LCO-1, LCO-2 and LCO-4 is not defined and cannot be accurately determined due to several spin-lattice relaxation mechanisms. The characteristic relaxation time of each individual mechanism is however shorter than 0.1 s. On the other hand, T1 values for Ex1-4 are successfully determined by a single exponential fit of the magnetization recovery as shown on
Both the single 7Li MAS NMR contribution and longer T1 value demonstrate the relatively low concentration of structural defects in Ex1, Ex2, Ex3 and Ex4 when compared to LCO-1, LCO-3 and LCO-4.
In conclusion, 7Li MAS NMR, XPS analyses and electrical conductivity allow to make an unambiguous description of the structure of Ex1, Ex2, Ex3 and Ex4 materials which comprises a core with Li stoichiometry control where Li occupy a single site surrounded by trivalent diamagnetic metals such as low spin Co3+ (t2g6eg0) and Al3+, and an electron insulating surface comprising inorganic metal oxides comprising Mg, Ti, Si, Co and Li.
Electrochemical Performances
The electrochemical performances of Examples 1-4 are shown in Table 7. The electrochemical properties are unexpectedly improved compared to LCO-1, LCO-3 and LCO-4. At 4.3V, Ex1, Ex2, Ex3 and Ex4 show very small irreversible capacity and better rate performance compared to LCO-1, LCO-3 and LCO-4. 4.5V high voltage performances of Ex1, Ex2, Ex3 and Ex4 are enhanced and feature very high capacity and very good cycle life. 4.6V performances of Ex1, Ex2, Ex3 and Ex4 are exceptional with a capacity fading at 1 C below 40% and are, to the extent of authors knowledge, unequalled in literature. These data show a perfect correlation between the relatively low defect concentration as evidenced by 7Li MAS NMR and the improved high voltage properties of stoichiometrically controlled LiCo1-xMxO2.
The energy density at 0.1 C for 4.5V and 4.6V, defined as the product of the pressed density, average voltage and discharge capacity, of Ex1, Ex2, Ex3 and Ex4 are enhanced when compared to LCO-1, LCO-2 and LCO-3, respectively. The association of high energy density and improved cycle life make Ex1, Ex2, Ex3 and Ex4 suitable for applications such as portable electronics. One can notice that the capacity fading of Ex4, though being significantly improved compared to LCO-4, is higher than Ex1, Ex2 and Ex3. This effect is a direct consequence of the lower particle size of Ex4 which causes a thinner surface layer—as the amount of added Mg and Ti is similar for all samples—offering less protection towards electrolyte decomposition.
Table 8 shows the discharge capacity, C-rate performances and average voltage at 4.4V of Ex4 and LCO-4. At 15 C, the C-rate and average voltage of Ex4 are improved when compared to LCO-4 resulting in an increase of the specific energy Es, defined as the product of the average discharge voltage and discharge capacity, by about 4%. Ex4, by featuring improved cycle life and specific energy is highly suitable for high power applications where maintaining high specific energy at high C-rate is required.
This example will demonstrate that other surface compositions are possible, including 4d elements such as Zr or Nb and rare earth elements such as Nd and Er. The samples with Li:M=1.00±0.01 and insulating surface containing Mg, Ti, Zr, Nb, Nd and Er have very good high voltage properties.
Preparation of LCO-6: state of the art titanium and magnesium doped LiCoO2 (noted LCO-6) is obtained by means of a standard high temperature solid state synthesis by dry-mixing powders of Co3O4 with TiO2, MgO and Li2CO3. LCO-6 contains 0.25 mol % titanium and 0.25 mol % magnesium. Typical Li:Co molar ratio used for the blend is 1.10. The average particle size of LCO-6 is 18 μm as shown on SEM image
Example 6a is prepared by mixing in a first step LCO-6 with nano-size ZrO2 powder. In a second step, 89.046 wt % of LCO-6/Zr 02 and 10.954 wt % Co3O4 (3 μm average particle size) are mixed. To the Co3O4, Li2CO3, Al2O3, TiO2 and MgO powders are added so as to adjust the final molar ratio as follows: Li:(Co+Al)=1.000 and Al=0.180 mol %, Ti=0.283 mol %, Mg=0.348 mol % and Zr=0.200 mol %, being expressed against Co content. The homogeneous mixture is placed in an alumina crucible and heated at 980° C. for 12 hours under constant air flow. After cooling, the resulting powder (Ex6a) is sieved and characterized. The average particle size of Ex6a is found to be 16 μm, and a bimodal distribution is obtained, similar to the one shown in
Example 6b is prepared by mixing in a first step LCO-6 with micron-sized Nb2O5 powder. In a second step, 89.046 wt % of LCO-6/Nb2O5 and 10.954 wt % Co3O4 (3 μm average particle size) are mixed. To the Co3O4, Li2CO3, Al2O3, TiO2 and MgO powders are added so as to adjust the final molar ratio as follows: Li:(Co+Al)=1.000 and Al=0.180 mol %, Ti=0.283 mol %, Mg=0.348 mol % and Nb=0.200 mol %, being expressed against Co content. The homogeneous mixture is placed in an alumina crucible and heated at 980° C. for 12 hours under constant air flow. After cooling, the resulting powder (Ex6b) is sieved and characterized. The average particle size of Ex6b is found to be 16 μm, and a bimodal distribution is obtained, similar to the one shown in
Example 6c is prepared by wet-mixing in a first step 89.046 wt % of LCO-6 and 10.954 wt % Co3O4 (3 μm average particle size) with neodymium nitrate hexahydrate. 12.146 g of neodymium nitrate hexahydrate are dissolved into 100 mL of de-ionized water and added to 2 kg of the LCO-6 and Co3O4 mixture. The mixture is placed in a bottle and homogenized overnight by rolling the bottle. The mixture is then dried at 120° C. and SEM images show that neodymium-based particles adhere to the surface of LCO-6 and Co3O4 particles as shown on
Nd=0.115 mol %, being expressed against Co content. The homogeneous mixture is placed in an alumina crucible and heated at 980° C. for 12 hours under constant air flow. After cooling, the resulting powder (Ex6c) is sieved and characterized. The average particle size of Ex6c is found to be 16 μm, and a bimodal distribution is obtained, similar to the one shown in
Example 6d is prepared by wet-mixing in a first step 89.046 wt % of LCO-6 and 10.954 wt % Co3O4 (3 μm average particle size) with erbium nitrate pentahydrate. 10.603 g of erbium nitrate pentahydrate are dissolved into 100 mL of de-ionized water and added to 2 kg of the LCO-6 and Co3O4 mixture. The mixture is placed in a bottle and homogenized overnight by rolling the bottle. The mixture is then dried at 120° C. and SEM images show that erbium-based particles adhere to the surface of LCO-6 and Co3O4 particles as shown on
Tables 9 and 10 show the electrochemical properties at 4.5 and 4.6V of LCO-6 and Ex6a-6d. Table 11 shows the physical properties of LCO-6 and Ex6a-6d. The LCO-6 sample, containing large Li-excess, has poor electrochemical performances at 4.5V, with low capacity and high fading rate. LCO-6 also contains large amounts of C and base impurities. Ex6a-6d with Li:(Co+Al)=1.000 have a very low conductivity and very low C and base impurity contents. These samples have therefore very low electrical conductivity, 4 to 5 orders of magnitude lower than LCO-6, as the surface is enriched with elements such as Mg, Ti, Zr, Nb, Nd and Er. The electrochemical performances at both 4.5 and 4.6V are exceptional with very high capacity thanks to Li:(Co+Al)=1.000 and improved stability thanks to insulating surface layer compared to LCO-6. Lastly, as Ex6a-6d feature bimodal distribution, the pressed density is improved by at least +0.5 g/cm3 compared to LCO-6.
As the surface base and carbon contents of the different materials in Table 11 show, the base and carbon contents are strongly reduced after the second firing for Ex6a-d when compared to LCO-6. This result supports, as can be confirmed by SEM on
This example will demonstrate that Mg and Ti free Li1.00CoO2 has a very high discharge capacity and good rate performance, but, as the insulating protecting layer is not formed, has higher electronic conductivity and inferior high voltage cycle stability compared to Ex1-6.
Preparation of LCO-7: state of the art LiCoO2 (noted LCO-7) is obtained by means of a standard high temperature solid state synthesis by dry-mixing powders of Co3O4 with Li2CO3 at mass production scale. Typical Li:Co molar ratio used for the blend is 1.07. The average particle size of LCO-7 is 19 μm. The final Li:Co mol ratio of LCO-7 after firing—as measured by ICP—is 1.040, and is used to set the Li:Co=1.010, 1.000, 0.990 and 0.980 ratio for Examples 7a, 7b, 7c and 7d.
Examples 7a, 7b, 7c and 7d are prepared by mixing LCO-7 and Co3O4 powders in the following wt % ratio: (97.60, 2.40), (96.82, 3.18), (96.06, 3.94) and (95.31, 4.69) so as to adjust the Li:Co ratio to 1.010, 1.000, 0.990 and 0.980, respectively. The homogeneous mixtures are placed in an alumina crucible and heated at 980° C. for 12 hours under constant air flow. After cooling, the resulting powders (Ex7a to Ex7d) are sieved and characterized.
The electrochemical performances of LCO-7 at 4.5V and Ex7a-7d at 4.6V and electronic conductivity values are shown on Table 12.
Discharge capacity DQ1 has a local maximum at Li:Co=1.00 while the C-rate and 4.6V stability are continuously improving when Li:Co decreases. Contrary to Example 5, the conductivity does not decrease significantly when Li:Co decreases, as no insulating surface layer is formed at the surface of the particles. The absence of an insulating surface layer—that normally provides a shield against unwanted side reactions with electrolyte—explains why the 4.6V stability is not as good as other examples featuring this insulating protective layer. When Li:Co<1.00, then stability improves as traces of CoOx (x˜4/3) are formed at the surface of the particles and start offering efficient shielding against parasitic reactions. The DQ1 is however decreasing and the polarization, defined as the difference between the average voltage during charge and discharge at cycle 1, is increasing dramatically.
This example will demonstrate that the insulating nature of the surface layer increases when Mg content increases. Increasing the insulating properties of the surface layer of Li1.00CoO2 core allows improving the safety of the materials.
Preparation of Examples 8a, 8b, 8c and 8d: Examples 8a, 8b, 8c, 8d have been prepared in the same way as Ex3 except that no Al has been added and that sufficient MgO has been added so as to adjust the Mg content to 0.22, 0.48, 0.75 and 1.00 mol %, respectively.
The electrical conductivity of Examples 8a, 8b, 8c and 8d is shown in Table 13. The electrical conductivity decreases continuously when the Mg content increases, meaning that the insulating nature of the Mg and Ti containing surface layer is increased. Authors believe that the thickness of the MgO-based surface layer increases when Mg increases, resulting in an improved insulating behaviour. As the influence of Mg as shown here is independent of further elements being present in the surface layer, such as Zr, Er, Nd, Nb, the experiments also illustrates the influence of the increasing Mg content for N and N′ doped products.
The effect of this insulating behavior on safety has been evaluated by means of DSC experiments performed on charged electrodes at 4.5V. After charging, the coin cells are disassembled in a glove box and the cathode is washed using DMC. After washing and drying, the electrode is soaked with electrolyte and placed in a sealed container for DSC measurement. This experiment is performed on Ex 7b, 8b and 8d and the data are shown on
Ex7b does not feature any insulating protective surface layer and the DCS experiment in characterized by a sharp exothermic contribution. This is the result of a fast and intense parasitic reaction of the charged material with electrolyte. When the Mg content increases from 8b to 8d, the exothermic contribution is broadened and shifts towards higher T, meaning that the intensity of the electrolyte decomposition is slowed down by the insulating protective layer at the surface of the particles.
Preparation of Example 9: Example 9 is prepared by mixing 89.046 wt % of LCO-6 and 10.954 wt % Co3O4 (3 μm average particle size). To the Co3O4, Li2CO3, Al2O3, TiO2 and MgO powders are added so as to adjust the final molar ratio as follows: Li:(Co+Al)=1.000, and Al=0.180 mol %, Ti=0.283 mol %, Mg=0.348 mol % being expressed against Co content. The homogeneous mixture is placed in an alumina crucible and heated at 980° C. for 12 hours under constant air flow using mass production equipments. After cooling, the resulting powder (Ex9) is sieved and characterized. The average particle size of Ex9 is found to be 16 μm, and a bimodal distribution is obtained.
Ex9 has an electronic conductivity of 1.01E-05 S/cm, pressed density of 3.88 g/cm3, DQ7 of 194.1 mAh/g at 4.5V and 1 C capacity fading rate of 3.1%. Ex9 is fitted in a 800 mAh polymer type fullcell using graphite anode and lithium hexafluorophosphate (LiPF6) salt at a concentration of 1.0 mol/L in a mixed solvent of EC (ethylene carbonate) and DEC (diethyl carbonate) in a volume ratio of 1/2 as non-aqueous electrolyte. The cell is subsequently cycles 500 times at 1 C charge and 1 C discharge rate between 4.35 and 3.0 V at both room temperature (
One can conclude that the combination of a Li-stoichiometric core and protective insulation layer as described in the present invention is very promising for commercial mass applications, such as portable electronics.
Filing Document | Filing Date | Country | Kind |
---|---|---|---|
PCT/IB2013/060078 | 11/12/2013 | WO | 00 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO2014/091331 | 6/19/2014 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
7235193 | Park | Jun 2007 | B2 |
20060063070 | Chiga et al. | Mar 2006 | A1 |
20090148772 | Kawasato | Jun 2009 | A1 |
20100310940 | Kim | Dec 2010 | A1 |
Number | Date | Country |
---|---|---|
2002008651 | Jan 2002 | JP |
2003 221234 | Aug 2003 | JP |
2004 119218 | Apr 2004 | JP |
2005 190900 | Jul 2005 | JP |
2005524204 | Aug 2005 | JP |
2006092820 | Apr 2006 | JP |
2008311132 | Dec 2008 | JP |
2010 535699 | Nov 2010 | JP |
2006 019229 | Jan 2016 | JP |
2003092099 | Nov 2003 | WO |
Entry |
---|
Supplemental European Search Report for EP 13 86 2777, dated Nov. 9, 2016. |
Chen, Z., et al., “Methods to Obtain Excellent Capacity Retention in LiCoO2 Cycled to 4.5 V”, Electrochimica Acta, Elsevier Science Publishers, vol. 49, No. 7 (Mar. 15, 2004), pp. 1079-1090. |
Fey, G.T.K, et al., “Nanoparticulate Coatings for Enhanced Cyclability of LiCoO2 Cathodes”, Journal of Power Sources, vol. 146, No. 1-2 (Aug. 26, 2005), pp. 65-70. |
Xu, H.Y., et al., “Improving the Electrochemical Behavior of LiCoO2 Electrode by Mixed Zr-Mg Doping”, Journal of Power Sources, vol. 148, (Sep. 15, 2005), pp. 90-94. |
Supplemental Partial European Search Report for EP 13 86 2777, dated Jun. 16, 2016. |
Number | Date | Country | |
---|---|---|---|
20150380722 A1 | Dec 2015 | US |
Number | Date | Country | |
---|---|---|---|
Parent | PCT/IB2012/057329 | Dec 2012 | US |
Child | 14650972 | US |