Claims
- 1. A method for production of plutonium metal from plutonium oxide, comprising the steps of:
- reacting a mixture consisting essentially of said plutonium oxide with metallic lithium; and
- removing pure liquid plutonium metal from product lithium oxides and unreacted lithium.
- 2. A method as in claim 1, wherein said reacting step is performed at a temperature of 700.degree.-750.degree. C.
- 3. A method as in claim 1, wherein said reacting step is performed in an atmosphere of inert gas at a pressure of about one atmosphere.
- 4. A method as in claim 1, wherein said removing step is by withdrawal of the density stratification layer formed, which is of the greatest density material, following reaction of plutonium oxide with metallic lithium.
- 5. A method for production of plutonium metal from plutonium oxide by metallic lithium reduction, with regeneration of lithium reactant, comprising the steps of:
- reacting said plutonium oxide with metallic lithium; oxides and unreacted lithium;
- subliming said product lithium oxide and unreacted lithium from unreacted plutonium oxide with hihg heat and low pressure;
- recapturing said product lithium oxides;
- reacting said recaptured product lithium oxides with anhydrous hydrochloric acid to produce lithium chloride salt; and
- decomposing product lithium chloride salt by electrolysis to regenerate lithium metal.
- 6. A method for the production of plutonium metal from plutonium oxide as in claim 5, wherein said reacting step of plutonium oxide with metallic lithium is performed at a temperature of 700.degree.-750.degree. C.
- 7. A method for production of plutonium metal from plutonium oxide as in claim 5, wherein the reacting step of said plutonium oxide with metallic lithium is performed in an atmosphere of inert gas at a pressure of about 9.8.times.10.sup.2 Pa to about 9.8.times.10.sup.4 Pa.
- 8. A method for production of plutonium metal from plutonium oxide as in claim 5, wherein sublimination of said recaptured product lithium oxides and lithium occur at about 1200.degree. C. and a pressure of about 1.3.times.10.sup.-4 Pa.
- 9. A method for production of plutonium metal from plutonium oxide by lithium reduction in a metal solvent, comprising the steps of:
- reacting said plutonium oxide with a solution of liquid lithium and solvent metal;
- draining liquid solvent metal containing product plutonium metal away from product lithium oxides and unreacted lithium; and
- removing solvent metal from liquid plutonium metal and solvent metal solution by vacuum distillation.
- 10. A method for production of plutonium metal as in claim 9, wherein said solvent metal is zinc.
- 11. A method for production of plutonium metal from plutonium oxide by lithium reduction in a metal solvent as in claim 9, with regeneration of lithium reductant, additionally comprising the steps of:
- subliming said product lithium oxides and unreacted lithium from unreacted plutonium oxides with high heat and low pressure;
- recapturing said product lithium oxides;
- reacting said recaptured product lithium oxides with anhydrous hydrochloric acid to produce lithium chloride salt; and
- decomposing product lithium cloride salt be electrolysis to regenerate lithium metal.
- 12. A method for production of plutonium metal as in claim 11, wherein said solvent metal is zinc.
Government Interests
The United States Government has rights in this invention pursuant to Contract No. W-7405-ENG-48 between the U.S. Department of Energy and the University of California, for the operation of Lawrence Livermore National Laboratory.