Patent Grant
10321980
The invention relates to lithium silicate glass ceramic and glass which comprise trivalent metal oxide selected from Y2O3, La2O3, Yb2O3, Bi2O3 and mixtures thereof and are particularly suitable for use in dentistry, preferably for the preparation of dental restorations.
Lithium silicate glass ceramics are characterized as a rule by very good mechanical properties, which is why they have been used for a long time in the dental field and there primarily for the preparation of dental crowns and small bridges. The known lithium silicate glass ceramics usually contain as main components SiO2, Li2O, Na2O or K2O, and nucleating agents such as P2O5.
DE 24 51 121 describes lithium disilicate glass ceramics which contain K2O and Al2O3. They are prepared from corresponding nuclei-containing starting glasses which are heated to temperatures of from 850 to 870° C. for the crystallization of lithium disilicate.
EP 827 941 describes sinterable lithium disilicate glass ceramics for dental purposes, which also contain K2O or Na2O in addition to La2O3. The lithium disilicate crystal phase is produced at a temperature of 850° C.
Lithium disilicate glass ceramics which also contain La2O3 and K2O are known from EP 916 625. A heat treatment is carried out at 870° C. for the formation of lithium disilicate.
EP 1 505 041 describes lithium silicate glass ceramics containing K2O, which, when lithium metasilicate is present as main crystal phase, can be very satisfactorily mechanically processed e.g. by means of CAD/CAM processes, in order to then be converted by further heat treatment at temperatures of from 830 to 850° C. into high-strength lithium disilicate glass ceramics.
EP 1 688 398 describes similar K2O— and Al2O3-containing lithium silicate glass ceramics which additionally are substantially free from ZnO. A heat treatment at 830 to 880° C. is applied to them to produce lithium disilicate.
U.S. Pat. No. 5,507,981 describes processes for producing dental restorations and glass ceramics that can be used in these processes. These are in particular lithium disilicate glass ceramics which usually contain Na2O or K2O.
U.S. Pat. No. 6,455,451 relates to lithium disilicate glass ceramics which also contain K2O. However, the production of the desired lithium disilicate crystal phase requires high temperatures of from 800 to 1000° C.
WO 2008/106958 discloses lithium disilicate glass ceramics for veneering zirconium oxide ceramics. The glass ceramics contain Na2O and are produced by heat treatment of nuclei-containing glasses at 800 to 940° C.
WO 2009/126317 describes GeO2-containing lithium metasilicate glass ceramics which also comprise K2O. The glass ceramics are processed to form dental products primarily by machining.
WO 2011/076422 relates to lithium disilicate glass ceramics which also contain K2O in addition to high levels of ZrO2 or HfO2. The crystallization of lithium disilicate takes place at temperatures of from 800 to 1040° C.
The known lithium disilicate glass ceramics have in common that they require heat treatments at more than 800° C. in order to effect the precipitation of lithium disilicate as main crystal phase. A large quantity of energy is therefore necessary to prepare them. Further, in the known glass ceramics the alkali metal oxides K2O or Na2O as well as ZrO2 are as a rule present as essential components which are apparently required for the production of the glass ceramics with the desired properties and in particular the formation of the desired lithium disilicate main crystal phase.
There is therefore a need for lithium silicate glass ceramics during the preparation of which the crystallization of lithium disilicate can be effected at lower temperatures. Further, it should also be possible to prepare them without the alkali metal oxides K2O or Na2O as well as ZrO2, previously regarded as necessary, and they should be suitable in particular for the preparation of dental restorations primarily in view of their optical and mechanical properties.
This object is achieved by the dental lithium silicate glass ceramic according to the attached claims. Also a subject of the invention are the dental starting glass, the dental lithium silicate glass with nuclei, the process for the preparation of the dental glass ceramic and the dental lithium silicate glass with nuclei according to the attached claims.
The lithium silicate glass ceramic according to the invention is characterized in that it comprises trivalent metal oxide selected from Y2O3, La2O3, Yb2O3, Bi2O3 and mixtures thereof, wherein the glass ceramic is essentially free K2O and Na2O.
The trivalent metal oxide is preferably selected from Y2O3, Yb2O3, Bi2O3 and mixtures thereof.
It is preferred that the glass ceramic comprises the trivalent metal oxide or mixtures thereof in an amount of 0.1 to 15, in particular 2.0 to 10.0, preferably 2.0 to 8.0 and particularly preferably 2.4 to 6.0 wt.-%.
It is particularly surprising that the formation of the glass ceramic according to the invention with lithium disilicate as main crystal phase is achieved even in the absence of various components regarded as necessary for conventional glass ceramics, such as in particular K2O and Na2O, and even at very low and thus advantageous crystallization temperatures of in particular 630 to 720° C. The glass ceramic also has a combination of optical and mechanical properties as well as processing properties that are very advantageous for use as dental material.
Further, a glass ceramic is preferred which comprises less than 0.1 wt.-% MgO and ZnO. The glass ceramic is particularly preferably essentially free of MgO and ZnO.
A glass ceramic is also preferred, which excludes lithium silicate glass ceramic comprising at least 6.1 wt.-% ZrO2.
Further, a glass ceramic is also preferred, which excludes lithium silicate glass ceramic comprising at least 8.5 wt.-% transition metal oxide selected from the group consisting of oxides of yttrium, oxides of transition metals with an atomic number of 41 to 79 and mixtures of these oxides.
The glass ceramic according to the invention preferably comprises 55.0 to 85.0, in particular 60.0 to 80.0 and preferably 66.0 to 78.0 wt.-% SiO2.
It is also preferred that the glass ceramic comprises 13.0 to 21.0 and in particular 13.0 to 20.0 and particularly preferably 15.0 to 18.0 wt.-% Li2O.
It is further preferred that the molar ratio between SiO2 and Li2O is from 1.7 to 3.1 and in particular from 1.8 to 3.0. It is very surprising that the production of lithium disilicate is achieved within this broad range. Specifically at ratios of less than 2.0 customary materials form lithium metasilicate instead of lithium disilicate.
The glass ceramic according to the invention can also comprise nucleating agents. P2O5 is particularly preferably used for this. The glass ceramic preferably comprises 0 to 8.0, in particular 2.0 to 8.0, preferably 2.5 to 6.0 and particularly preferably 3.0 to 5.0 wt.-% P2O5.
In a further preferred embodiment, the glass ceramic comprises at least one and preferably all of the following components:
The glass ceramic according to the invention can moreover also comprise additional components which are selected in particular from oxides of divalent elements, further oxides of tetravalent elements, further oxides of pentavalent elements, oxides of hexavalent elements, melt accelerators, colourants and fluorescent agents.
In particular the alkaline earth metal oxides, preferably CaO, BaO, MgO, SrO or a mixture thereof and preferably MgO and/or CaO come into consideration as oxides of divalent elements. They can be used in amounts of 0 to 5.0 wt.-%.
The term “further oxides of tetravalent elements” refers to oxides of tetravalent elements with the exception of SiO2. Examples of suitable further oxides of tetravalent elements are TiO2, SnO2 and GeO2.
The term “further oxides of pentavalent elements” refers to oxides of pentavalent elements with the exception of P2O5.
Examples of suitable further oxides of pentavalent elements are Ta2O5 and Nb2O5.
Examples of suitable oxides of hexavalent elements are WO3 and MoO3.
A glass ceramic is preferred which comprises at least one oxide of divalent elements, at least one further oxide of tetravalent elements, at least one further oxide of pentavalent elements and/or at least one oxide of hexavalent elements.
Examples of melt accelerators are fluorides.
Examples of colourants and fluorescent agents are oxides of d- and f-elements, such as the oxides of Ti, V, Sc, Mn, Fe, Co, Ta, W, Ce, Pr, Nd, Tb, Er, Dy, Gd, Eu and Yb. Metal colloids, e.g. of Ag, Au and Pd, can also be used as colourants and in addition can also act as nucleating agents. These metal colloids can be formed e.g. by reduction of corresponding oxides, chlorides or nitrates during the melting and crystallization processes. The metal colloids can be present in the glass ceramic in an amount of 0.005 to 0.5 wt.-%.
The term “main crystal phase” used below refers to the crystal phase which has the highest proportion by volume compared with other crystal phases.
In one embodiment, the glass ceramic according to the invention comprises lithium metasilicate as main crystal phase. In particular, the glass ceramic comprises more than 5 vol.-%, preferably more than 10 vol.-% and particularly preferably more than 15 vol.-% lithium metasilicate crystals, relative to the total glass ceramic.
In a further particularly preferred embodiment, the glass ceramic comprises lithium disilicate as main crystal phase. In particular the glass ceramic comprises more than 10 vol.-%, preferably more than 20 vol.-% and particularly preferably more than 30 vol.-% lithium disilicate crystals, relative to the total glass ceramic.
The lithium disilicate glass ceramic according to the invention is characterized by particularly good mechanical properties and can be produced e.g. by heat treatment of the lithium metasilicate glass ceramic according to the invention. However, it can be formed in particular by heat treatment of a corresponding starting glass or of a corresponding lithium silicate glass with nuclei.
It has surprisingly been shown that the lithium disilicate glass ceramic according to the invention has very good mechanical and optical properties and processing properties even in the absence of components regarded as essential for conventional glass ceramics. The combination of its properties even allows it to be used as dental material and in particular material for the preparation of dental restorations.
The lithium disilicate glass ceramic according to the invention has in particular a fracture toughness, measured as KIC value, of at least 1.8 MPa·m0.5 and in particular at least 2.0 MPa·m0.5.
This value was determined using the Vickers method and calculated using Niihara's equation.
The invention also relates to a lithium silicate glass with nuclei that are suitable for forming lithium metasilicate and/or lithium disilicate crystals, wherein the glass comprises the components of the above-described glass ceramics according to the invention. Thus this glass comprises trivalent metal oxide selected from Y2O3, La2O3, Yb2O3, Bi2O3 and mixtures thereof, wherein the glass is essentially free of K2O and Na2O. For preferred embodiments of this glass reference is made to the preferred embodiments described above of the glass ceramics according to the invention.
The glass with nuclei according to the invention can be produced by heat treatment of a correspondingly composed starting glass according to the invention. The lithium metasilicate glass ceramic according to the invention can then be formed by a further heat treatment, and in turn be converted into the lithium disilicate glass ceramic according to the invention by further heat treatment, or the lithium disilicate glass ceramic according to the invention can also preferably be formed directly from the glass with nuclei. The starting glass, the glass with nuclei and the lithium metasilicate glass ceramic can consequently be regarded as precursors for the production of the high-strength lithium disilicate glass ceramic.
The glass ceramics according to the invention and the glasses according to the invention are present in particular in the form of powders, granulates or blanks, e.g. monolithic blanks, such as platelets, cuboids or cylinders, or powder compacts, in unsintered, partly sintered or dense-sintered form. They can easily be further processed in these forms. They can, however, also be present in the form of dental restorations, such as inlays, onlays, crowns, veneers, facets or abutments.
The invention also relates to a process for the preparation of the glass ceramic according to the invention and the glass with nuclei according to the invention, in which a correspondingly composed starting glass, the glass with nuclei according to the invention or the lithium metasilicate glass ceramic according to the invention is subjected to at least one heat treatment in the range of 450 to 950° C., in particular 450 to 750 and preferably 480 to 720° C.
The starting glass according to the invention therefore comprises trivalent metal oxide selected from Y2O3, La2O3, Yb2O3, Bi2O3 and mixtures thereof, wherein the starting glass is essentially free of K2O and Na2O. In addition, it preferably also comprises suitable amounts of SiO2 and Li2O, in order to allow the formation of a lithium silicate glass ceramic, and in particular a lithium disilicate glass ceramic. Further, the starting glass can also comprise still further components, such as are given above for the lithium silicate glass ceramic according to the invention. All those embodiments are preferred for the starting glass which are also given as preferred for the glass ceramic.
In the process according to the invention, the glass with nuclei is usually prepared by means of a heat treatment of the starting glass at a temperature of in particular from 480 to 510° C. The lithium disilicate glass ceramic according to the invention is then preferably produced from the glass with nuclei through further heat treatment at usually 600 to 750 and in particular 630 to 720° C.
Thus, much lower temperatures are used according to the invention for the crystallization of lithium disilicate than with the conventional lithium disilicate glass ceramics. The energy thus saved represents a clear advantage. Surprisingly, this low crystallization temperature is even possible in the absence of components, such as K2O and Na2O as well as ZrO2, regarded as essential for conventional glass ceramics.
To prepare the starting glass, the procedure is in particular that a mixture of suitable starting materials, such as carbonates, oxides, phosphates and fluorides, is melted at temperatures of in particular 1300 to 1600° C. for 2 to 10 h. To achieve a particularly high homogeneity, the obtained glass melt is poured into water in order to form a glass granulate, and the obtained granulate is then melted again.
The melt can then be poured into moulds to produce blanks of the starting glass, so-called solid glass blanks or monolithic blanks.
It is also possible to put the melt into water again in order to prepare a granulate. This granulate can then be pressed, after grinding and optionally addition of further components, such as colourants and fluorescent agents, to form a blank, a so-called powder compact.
Finally, the starting glass can also be processed to form a powder after granulation.
The starting glass, e.g. in the form of a solid glass blank, a powder compact or in the form of a powder, is then subjected to at least one heat treatment in the range of from 450 to 950° C. It is preferred that a first heat treatment is initially carried out at a temperature in the range of 480 to 510° C. to prepare a glass according to the invention with nuclei which are suitable for forming lithium metasilicate and/or lithium disilicate crystals. This first heat treatment is preferably carried out for a period of 10 min to 120 min and in particular 10 min to 30 min. The glass with nuclei can then preferably be subjected to at least one further heat treatment at a higher temperature and in particular more than 570° C. to effect crystallization of lithium metasilicate or lithium disilicate. This further heat treatment is preferably carried out for a period of 10 min to 120 min, in particular 10 min to 60 min and particularly preferably 10 min to 30 min. To crystallize lithium disilicate, the further heat treatment is usually carried out at 600 to 750 and in particular 630 to 720° C.
In a preferred embodiment of the process, therefore
The duration of the heat treatments carried out in (a) and (b) is preferably as given above.
The at least one heat treatment carried out in the process according to the invention can also take place during hot pressing or sintering-on of the glass according to the invention or the glass ceramic according to the invention.
Dental restorations for use in the oral cavity, such as bridges, inlays, onlays, crowns, veneers, facets or abutments, can be prepared from the glass ceramics according to the invention and the glasses according to the invention. The invention therefore also relates to their use for the preparation of dental restorations. It is preferred that the glass ceramic or the glass is shaped into the desired dental restoration by pressing or machining.
The pressing is usually carried out under increased pressure and increased temperature. It is preferred that the pressing is carried out at a temperature of 700 to 1200° C. It is further preferred to carry out the pressing at a pressure of 2 to 10 bar. During pressing, the desired shape change is achieved by viscous flow of the material used. The starting glass according to the invention and in particular the glass with nuclei according to the invention, the lithium metasilicate glass ceramic according to the invention and the lithium disilicate glass ceramic according to the invention can be used for the pressing. The glasses and glass ceramics according to the invention can be used in particular in the form of blanks, e.g. solid blanks or powder compacts.
The machining is usually carried out by material removal processes and in particular by milling and/or grinding. It is particularly preferred that the machining is carried out within the framework of a CAD/CAM process. The starting glass according to the invention, the glass with nuclei according to the invention, the lithium metasilicate glass ceramic according to the invention and the lithium disilicate glass ceramic according to the invention can be used for the machining. The glasses and glass ceramics according to the invention can be used in particular in the form of blanks, e.g. solid blanks or powder compacts, e.g. in unsintered, partly sintered or dense-sintered form. The lithium metasilicate glass ceramic according to the invention and lithium disilicate glass ceramic according to the invention are preferably used for the machining. The lithium disilicate glass ceramic can also be used in a not fully crystallized form which was produced by heat treatment at a lower temperature. This has the advantage that an easier machining, and thus the use of simpler equipment for the machining, is possible. After the machining of such a partly crystallized material, it is usually subjected to a heat treatment at a higher temperature and in particular 630 to 720° C. in order to effect further crystallization of lithium disilicate.
In general, after the preparation of the dental restoration shaped as desired by pressing or machining, it can also in particular be heat-treated in order to convert the precursors used, such as starting glass, glass with nuclei or lithium metasilicate glass ceramic, into lithium disilicate glass ceramic or to increase the crystallization of lithium disilicate or to reduce the porosity, e.g. of a porous powder compact used.
However, the glass ceramic according to the invention and the glass according to the invention are also suitable as coating material of e.g. ceramics and glass ceramics. The invention is therefore also directed towards the use of the glass according to the invention or the glass ceramic according to the invention for coating in particular ceramics and glass ceramics.
The invention also relates to a process for coating ceramics and glass ceramics, in which the glass ceramic according to the invention or the glass according to the invention is applied to the ceramic or glass ceramic and is exposed to increased temperature.
This can take place in particular by sintering-on and preferably by pressing-on. With sintering-on, the glass ceramic or the glass is applied to the material to be coated, such as ceramic or glass ceramic, in the usual way, e.g. as powder, and then sintered at increased temperature. With the preferred pressing-on, the glass ceramic according to the invention or the glass according to the invention is pressed on, e.g. in the form of powder compacts or monolithic blanks, at an increased temperature of e.g. 700 to 1200° C., applying pressure, e.g. 2 to 10 bar. The methods described in EP 231 773 and the press furnace disclosed therein can be used in particular for this. A suitable furnace is e.g. the Programat EP 5000 from Ivoclar Vivadent AG, Liechtenstein.
It is preferred that, after conclusion of the coating process, the glass ceramic according to the invention is present with lithium disilicate as main crystal phase, as such glass ceramic has particularly good properties.
Because of the above-described properties of the glass ceramic according to the invention and the glass according to the invention as its precursor, they are suitable in particular for use in dentistry. A subject of the invention is therefore also the use of the glass ceramic according to the invention or the glass according to the invention as a dental material and in particular for the preparation of dental restorations or as a coating material for dental restorations, such as crowns, bridges and abutments.
Finally, the glasses and glass ceramics according to the invention can also be mixed together with other glasses and glass ceramics in order to produce dental materials with properties set as desired. Compositions and in particular dental materials which comprise the glass according to the invention or the glass ceramic according to the invention in combination with at least one other glass and/or one other glass ceramic therefore represent a further subject of the invention. The glass according to the invention or the glass ceramic according to the invention can therefore be used in particular as main component of an inorganic-inorganic composite or in combination with a plurality of other glasses and/or glass ceramics, wherein the composites or combinations can be used in particular as dental materials. The combinations or composites can particularly preferably be present in the form of sintered blanks. Examples of other glasses and glass ceramics for the preparation of inorganic-inorganic composites and of combinations are disclosed in DE 43 14 817, DE 44 23 793, DE 44 23 794, DE 44 28 839, DE 196 47 739, DE 197 25 553, DE 197 25 555, DE 100 31 431 and DE 10 2007 011 337. These glasses and glass ceramics belong to the silicate, borate, phosphate or aluminosilicate group. Preferred glasses and glass ceramics are of SiO2—Al2O3—K2O type (with cubic or tetragonal leucite crystals), SiO2—B2O3—Na2O type, alkali-silicate type, alkali-zinc-silicate type, silicophosphate type, SiO2—ZrO2 type and/or lithium-aluminosilicate type (with spodumene crystals). By mixing such glasses or glass ceramics with the glasses and/or glass ceramics according to the invention, for example the coefficient of thermal expansion can be set as desired in a broad range of from 6 to 20·10−6 K−1.
The invention is explained in more detail below by means of examples.
A total of 15 glasses and glass ceramics according to the invention with the composition given in Table I were prepared by melting corresponding starting glasses followed by heat treatment for controlled nucleation and crystallization.
For this, the starting glasses weighing from 100 to 200 g were first melted from customary raw materials at 1400 to 1500° C., wherein the melting was very easily possible without formation of bubbles or streaks. By pouring the starting glasses into water, glass frits were prepared which were then melted a second time at 1450 to 1550° C. for 1 to 3 h for homogenization.
In the case of Examples 1 and 3 to 15, the obtained glass melts were then poured into preheated moulds in order to produce glass monoliths.
In the case of Example 2, the obtained glass melt was cooled to 1400° C. and converted to a finely divided granulate by pouring into water. The granulate was dried and ground to a powder with a particle size of <90 μm. This powder was moistened with some water and pressed to form a powder compact at a pressure of 20 MPa.
The glass monoliths (Examples 1 and 3-15) as well as the powder compact (Example 2) were then converted by thermal treatment to glasses and glass ceramics according to the invention. The thermal treatments used for controlled nucleation and controlled crystallization are also given in Table I. The following meanings apply
It can be seen that a first heat treatment in the range of 480 to 510° C. resulted in the formation of lithium silicate glasses with nuclei and these glasses crystallized by a further heat treatment already at 630 to 720° C. within only 20 to 30 min to glass ceramics with lithium disilicate or lithium metasilicate as main crystal phase, as was established by X-ray diffraction tests.
The produced lithium silicate glass ceramics were able to be very satisfactorily machined in a CAD/CAM process or hot-pressed into the form of various dental restorations, which were also provided with a veneer if required.
They were also able to be applied by hot pressing as coatings onto in particular dental restorations, e.g. in order to veneer the latter as desired.
The glass ceramic according to Example 14 was ground to powder with an average particle size of <90 m.
In a first variant, the obtained powder was pressed with or without pressing auxiliaries to powder compacts and the latter were partly or densely sintered at temperatures of from 800 to 1100° C. and then further processed by machining or by hot pressing to form dental restorations.
In a second variant, the obtained powder was pressed with or without pressing auxiliaries to powder compacts and the latter were then further processed by machining or by hot pressing to form dental restorations. In particular, the dental restorations obtained after the machining were then densely sintered at temperatures of 900 to 1100° C.
With both variants, it was possible to prepare in particular crowns, caps, partial crowns and inlays as well as coatings on dental ceramics and dental glass ceramics.
A glass with the composition according to Example 2 was prepared by mixing corresponding raw materials in the form of oxides and carbonates for 30 min in a Turbula mixer and then melting the mixture at 1450° C. for 120 min in a platinum crucible. The melt was poured into water in order to obtain a finely divided glass granulate. This glass granulate was melted again at 1530° C. for 150 min in order to obtain a glass melt with particularly high homogeneity. The temperature was reduced to 1500° C. for 30 min and cylindrical glass blanks with a diameter of 12.5 mm were prepared by pouring into pre-heated, separable steel moulds or graphite moulds. The obtained glass cylinders were then nucleated at 510° C. and stress-relieved.
The nucleated glass cylinders were then processed by hot pressing at a pressing temperature of 970° C. and a pressing time of 6 min using an EP600 press furnace, Ivoclar Vivadent AG, to form dental restorations, such as inlays, onlays, veneers, partial crowns, crowns, laminating materials and laminates. In each case, lithium disilicate was detected as main crystal phase.
| Number | Date | Country | Kind |
|---|---|---|---|
| 11185336 | Oct 2011 | EP | regional |
This application is a continuation application of U.S. application Ser. No. 14/001,184, filed Aug. 23, 2013, which is the National Stage filing of International patent application PCT/EP2012/070221, filed on Oct. 11, 2012, which claims priority to European patent application No. 11185336.2 filed on Oct. 14, 2011, the disclosures of which are incorporated herein by reference in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 2684911 | Stookey | Jul 1954 | A |
| 3006775 | Chen | Oct 1961 | A |
| 3022180 | Morrissey et al. | Feb 1962 | A |
| 3161528 | Eppler | Dec 1964 | A |
| 3252778 | Goodman et al. | May 1966 | A |
| 3463647 | Kosiorek | Aug 1969 | A |
| 3804608 | Gaskell et al. | Apr 1974 | A |
| 3816704 | Borom et al. | Jun 1974 | A |
| 3977857 | Mattox | Aug 1976 | A |
| 4155888 | Mooth | May 1979 | A |
| 4189325 | Barrett et al. | Feb 1980 | A |
| 4414282 | McCollister et al. | Nov 1983 | A |
| 4473653 | Rudoi | Sep 1984 | A |
| 4480044 | McAlinn | Oct 1984 | A |
| 4515634 | Wu et al. | May 1985 | A |
| 4671770 | Bell et al. | Jun 1987 | A |
| 4963707 | Zyokou et al. | Oct 1990 | A |
| 4977114 | Horinouchi et al. | Dec 1990 | A |
| 5176961 | Crooker et al. | Jan 1993 | A |
| 5219799 | Beall et al. | Jun 1993 | A |
| 5432130 | Rheinberger et al. | Jul 1995 | A |
| 5507981 | Petticrew et al. | Apr 1996 | A |
| 5618763 | Frank et al. | Apr 1997 | A |
| 5628564 | Nenyei et al. | May 1997 | A |
| 5691256 | Taguchi et al. | Nov 1997 | A |
| 5698019 | Frank et al. | Dec 1997 | A |
| 5698482 | Frank et al. | Dec 1997 | A |
| 5702514 | Petticrew | Dec 1997 | A |
| 5707777 | Aoai et al. | Jan 1998 | A |
| 5872069 | Abe | Feb 1999 | A |
| 5874376 | Taguchi et al. | Feb 1999 | A |
| 5925180 | Frank et al. | Jul 1999 | A |
| 5938959 | Wang | Aug 1999 | A |
| 5968856 | Schweiger et al. | Oct 1999 | A |
| 6066584 | Krell et al. | May 2000 | A |
| 6095682 | Hollander et al. | Aug 2000 | A |
| 6106747 | Wohlwend | Aug 2000 | A |
| 6121175 | Drescher et al. | Sep 2000 | A |
| 6048589 | Suzuki | Nov 2000 | A |
| 6157004 | Bizzio | Dec 2000 | A |
| 6163020 | Bartusch et al. | Dec 2000 | A |
| 6174827 | Goto et al. | Jan 2001 | B1 |
| 6252202 | Zychek | Jun 2001 | B1 |
| 6267595 | Gratz | Jul 2001 | B1 |
| 6270876 | Abe et al. | Aug 2001 | B1 |
| 6287121 | Guiot et al. | Sep 2001 | B1 |
| 6342458 | Schweiger et al. | Jan 2002 | B1 |
| 6376397 | Petticrew | Apr 2002 | B1 |
| 6420288 | Clausbruch et al. | Jul 2002 | B2 |
| 6441346 | Zychek | Aug 2002 | B1 |
| 6455451 | Brodkin | Sep 2002 | B1 |
| 6458728 | Nagata et al. | Oct 2002 | B1 |
| 6485849 | Petticrew | Nov 2002 | B2 |
| 6514890 | Nagata et al. | Feb 2003 | B1 |
| 6514893 | Schweiger et al. | Feb 2003 | B1 |
| 6517623 | Brodkin et al. | Feb 2003 | B1 |
| 6524982 | Nagata et al. | Feb 2003 | B1 |
| 6593257 | Nagata et al. | Jul 2003 | B1 |
| 6703332 | Peng | Mar 2004 | B2 |
| 6802894 | Brodkin et al. | Oct 2004 | B2 |
| 6818573 | Petticrew | Nov 2004 | B2 |
| 7162321 | Luthardt et al. | Jan 2007 | B2 |
| 7316740 | Rheinberger et al. | Jan 2008 | B2 |
| 7452836 | Apel et al. | Nov 2008 | B2 |
| 7655586 | Brodkin et al. | Feb 2010 | B1 |
| 7806694 | Brodkin et al. | Oct 2010 | B2 |
| 7816291 | Schweiger et al. | Oct 2010 | B2 |
| 7867930 | Apel et al. | Jan 2011 | B2 |
| 7867933 | Apel et al. | Jan 2011 | B2 |
| 7871948 | Apel et al. | Jan 2011 | B2 |
| 7892995 | Castillo | Feb 2011 | B2 |
| 7993137 | Apel et al. | Aug 2011 | B2 |
| 8042358 | Schweiger et al. | Oct 2011 | B2 |
| 8047021 | Schweiger et al. | Nov 2011 | B2 |
| 8444756 | Schweiger et al. | May 2013 | B2 |
| 20010006174 | Brennan | Jul 2001 | A1 |
| 20010031446 | Petticrew | Oct 2001 | A1 |
| 20020009600 | Peng et al. | Jan 2002 | A1 |
| 20020010063 | Schweiger et al. | Jan 2002 | A1 |
| 20020022563 | Schweiger et al. | Feb 2002 | A1 |
| 20020031670 | Goto et al. | Mar 2002 | A1 |
| 20020035025 | Schweiger et al. | Mar 2002 | A1 |
| 20020160694 | Wood et al. | Oct 2002 | A1 |
| 20040182538 | Lambrecht | Sep 2004 | A1 |
| 20050098064 | Schweiger et al. | May 2005 | A1 |
| 20050127544 | Brodkin | Jun 2005 | A1 |
| 20060040142 | Xuelu et al. | Feb 2006 | A1 |
| 20060082033 | Hauptmann et al. | Apr 2006 | A1 |
| 20060139091 | Fratti | Jun 2006 | A1 |
| 20060257823 | Pfeiffer et al. | Nov 2006 | A1 |
| 20060257824 | Pfeiffer et al. | Nov 2006 | A1 |
| 20070023971 | Saha et al. | Feb 2007 | A1 |
| 20070042889 | Apel et al. | Feb 2007 | A1 |
| 20080044488 | Zimmer et al. | Feb 2008 | A1 |
| 20080120994 | Schweiger et al. | May 2008 | A1 |
| 20080199823 | Miller | Aug 2008 | A1 |
| 20090023574 | Holand et al. | Jan 2009 | A1 |
| 20090038344 | Apel et al. | Feb 2009 | A1 |
| 20090038508 | Apel et al. | Feb 2009 | A1 |
| 20090042166 | Craig et al. | Feb 2009 | A1 |
| 20090256274 | Castillo | Oct 2009 | A1 |
| 20090258778 | Castillo | Oct 2009 | A1 |
| 20100083706 | Castillo | Apr 2010 | A1 |
| 20110030423 | Johannes et al. | Feb 2011 | A1 |
| 20110256409 | Ritzberger et al. | Oct 2011 | A1 |
| 20120094822 | Castillo et al. | Apr 2012 | A1 |
| 20120148988 | Castillo et al. | Jun 2012 | A1 |
| 20120248642 | Ritzberger et al. | Oct 2012 | A1 |
| 20120309607 | Durschang et al. | Dec 2012 | A1 |
| 20140141960 | Borczuch-Laczka et al. | May 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 2163792 | Dec 1994 | CA |
| 2213390 | Mar 1998 | CA |
| 2239865 | Dec 1998 | CA |
| 2239869 | Dec 1998 | CA |
| 2252660 | May 1999 | CA |
| 2351154 | Dec 2001 | CA |
| 2451121 | May 1975 | DE |
| 4303458 | Jan 1994 | DE |
| 4314817 | Nov 1994 | DE |
| 4423793 | Feb 1996 | DE |
| 4423794 | Feb 1996 | DE |
| 4428839 | Feb 1996 | DE |
| 19647739 | Mar 1998 | DE |
| 19725553 | Dec 1998 | DE |
| 19725555 | Dec 1998 | DE |
| 10031431 | Jan 2002 | DE |
| 102007011337 | Sep 2008 | DE |
| 231773 | Aug 1987 | EP |
| 0827941 | Mar 1998 | EP |
| 0916625 | May 1999 | EP |
| 1152641 | Nov 2001 | EP |
| 1505041 | Feb 2005 | EP |
| 1577275 | Feb 2006 | EP |
| 1688398 | Aug 2006 | EP |
| 752243 | Jul 1956 | GB |
| 2284655 | Jun 1995 | GB |
| H10323354 | Dec 1998 | JP |
| 1174418 | Mar 1999 | JP |
| 2001019485 | Jan 2001 | JP |
| 2001019486 | Jan 2001 | JP |
| 2001019487 | Jan 2001 | JP |
| 2001019488 | Jan 2001 | JP |
| 2005-062832 | Mar 2005 | JP |
| 2007028787 | Mar 2007 | WO |
| 2008106958 | Sep 2008 | WO |
| 2009126317 | Oct 2009 | WO |
| 2011076422 | Jun 2011 | WO |
| Entry |
|---|
| Jakovac, M., et al., Measurement of ion elution from dental ceramics, Journal of the European Ceramic Society, May 6, 2006, vol. 26, pp. 1695-1700. |
| Apel, E., et al., “Influence of Zr02 on the crystallization and properties of lithium disilicate glass-ceramics derived from multi-component system,” Journal of European Ceramic Society, 2007, 27, 1571-1577. |
| Durschang, Dr. Bernhard, “Report of Results,” Fraunhofer Institute for Silicate Research ISC Glass and Mineral Materials, 2015. |
| McMillan, P.W., et al., “The Structure and Properties of a Lithium Zinc Silicate Glass-Ceramic,” Journal of Material Science 1966, I. 269-279. |
| Deubener, J., et al., “Induction time analysis of nucleation and crystal grown in di- and metasilicate glasses,” Journal of Non-Crystalline Solids, 1993, 163, 1-12. |
| Holand, W., et al., “Glass-ceramic technology,” American Chemical Society 2002, Westerville OH, USA. |
| Holand, W., et al., “Control of nucleation in glass ceramics,” Phil. Trans. Soc. Lond. A 2003, 361, 575-589. |
| Holand, W., et al., “Principles and phenomena of bioengineering with glass-ceramics of dental restoration,” Journal of the European Ceramics Society 2007, 27, 1571-1577. |
| Ivoclar Vivadent, Inc., IPS e.max lithium disilicate, 627329, Rev. Feb. 2009. |
| Borom, M.P., et al., “Strength and Microstructure in Lithium Disilicate Glass Ceramics,” J. Am. Ceram. Soc., 1975, 68, 385-391. |
| Stookey, S.D., “Chemical Machining of Photosensitive Glass,” Ind. Eng. Chem. 45:115-118 (1993). |
| Von Clausbruch, et al., “Effect of ZnO on the Crystallization, Microstructure, and Properties of Glass-Ceramics in the SiO2—Li2O—K2O—P2O5 System,” Glastech. Ber. Glass Sci. Technol. 74(8)223-229(2001). |
| Von Clausbruch, et al., “Effect of P2O5 on the Crystallization and Microstructure of Glass-Ceramics in the SiO2—Li2O—Zn)—P2O5 System,” Glastech. Ber. Glass Sci. Technol. 74(8)223-229(2001). |
| Oliveria et al., “Sintering and Crystallization of a Glass Powder in the Li2O—ZrO2—SiO2 System,” J. Amer. Ceramic Soc. 81(3): 777-780 (1998). |
| Giassi, et al., “Injection Moulding of LiO2—ZrO2—SiO2—A12O3 (LZSA) Glass Ceramics,” Glass Technol., 46(3), 277-280 (2005). |
| http://en.wikipedia.org/wiki/Nucleation; Sep. 20, 2012. |
| International Agency for Research on Cancer (IARC) Working Group, “Arsenic and Arsenic Compounds,” IARC Monographs; Arsenic, Metals, Fibres, and Dusts, vol. 100C, pp. 41-39, 2012. |
| International Agency for Research on Cancer (IARC) Working Group, “Antimony Trioxide and Antimony Trisulfide,” IARC Monographs on the Evaluation of Carcinogenic Risks to Humans, vol. 47, pp. 291-305, 1989. |
| Montedo, et al., “Low Thermal Expansion Sintered LZSA Glass Ceramics,” American Ceramic Society Bulletin, vol. 87, No. 7, pp. 34-40, Jul. 2008. |
| Number | Date | Country | |
|---|---|---|---|
| 20160302897 A1 | Oct 2016 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14001184 | US | |
| Child | 15193202 | US |