The present disclosure relates to a solid-state battery, and a method of making the same.
Solid state batteries (SSBs) provide an alternative to conventional lithium-ion batteries with liquid electrolytes. Typically, SSBs include solid electrodes and a solid electrolyte material. The solid electrolytes are resistant to lithium dendrites, which can lead to internal short circuits and are an alternative to flammable and unstable liquid battery electrolytes. Solid electrolytes for SSBs are typically used as separators between the two electrodes and must be highly conductive to lithium ions, but have very low electronic conductivity. As a result, SSBs may have very low self-discharge rates. Because of the materials used, SSBs reduce electrolyte leakage and reactions between the electrolyte and active materials, as well as providing a long shelf life and high energy density.
SSBs have the potential to provide other benefits over conventional lithium ion batteries, such as better energy density. Typically, in order to provide an energy density of more than about 700 Wh/L, a SSB must use lithium metal as the anode material. However, enabling lithium metal in a SSB is challenging due to lithium dendrite growth in the solid electrolyte separator, volume change of the anode during cycling, degradation of the lithium/electrolyte interface, and incompatibility with various solid electrolyte materials. One of the alternatives to a lithium metal based anode is lithium titanate (LTO). An LTO anode coupled with a high voltage cathode, such as LMNO, may be capable of delivering around 700 Wh/L. In addition, using LTO as the anode material typically provides benefits such as low volume change and good compatibility with various solid electrolytes, making LTO an attractive material for use in a SSB.
Various methods of forming SSBs have been developed. Yet, fabricating a high energy density SSB has been a challenge, for example due to high sensitivity of suitable solid electrolytes to atmospheric moisture. It has also been difficult to achieve good interfacial resistance between active material of the electrodes and the solid electrolyte particles. For example, sintering at high temperatures of about 900° C. is used to provide interfacial contact between the electrolyte and the active material, but poses issues for carbon as an electronic conductor due to the high temperatures.
According to an embodiment, a solid-state battery is disclosed. The solid-state battery includes a positive electrode, a negative electrode, and a separator between the positive and negative electrodes. The negative electrode includes reduced lithium titanate (LTO) particles and solid electrolyte particles. Additionally, the negative electrode lacks electronically conductive additives.
According to one or more embodiments, the reduced LTO particles may be pristine LTO particles processed in a reducing atmosphere at a temperature of about 300-1200° C. Further, the reducing atmosphere may be a gas environment containing CO, H2, hydrocarbons, H2/N2, H2/Ar, or combinations thereof. In some embodiments, the reduced LTO particles may include oxygen defects. In other embodiments, the reduced LTO particles may include dopants. The dopants may be Mg2+, Zn2+, Al3+, Ni2+, Mo6+, Cu2+, or a combination thereof. In one or more embodiments, the electronically conductive additives may be carbon or metallic particles.
According to an embodiment, a method for forming a solid-state electrode assembly is disclosed. The method includes providing reduced LTO particles; mixing the reduced LTO particles with solid electrolyte particles to form a mixture; fabricating the mixture into an anode sheet; arranging the anode sheet with a separator sheet and a cathode sheet to form a stack; laminating the stack; and sintering the stack to form the assembly.
According to one or more embodiments, the fabricating may include tape casting the anode sheet. In some embodiments, the sintering may be in an inert atmosphere. Further, the inert atmosphere may be an argon or nitrogen atmosphere. In one or more embodiments, the providing may include processing pristine LTO in a reduced atmosphere at a temperature of about 300-1200° C. According to one or more embodiments, the method may further include doping pristine LTO with Mg2+, Zn2+, Al3+, Ni2+, Mo6+, Cu2+, or a combination thereof to form the reduced LTO particles. In some embodiments, the mixing may include selecting a ratio of reduced LTO particles to solid electrolyte based on predetermined desired capacity and rate capability.
According to an embodiment, a method for forming a solid-state electrode assembly is disclosed. The method includes providing a mixture of pristine LTO particles and solid electrolyte particles; fabricating the mixture into an anode sheet; arranging the anode sheet with a separator sheet and a cathode sheet to form a stack; laminating the stack; and sintering the stack in a reducing atmosphere to reduce the pristine LTO to reduced LTO.
According to one or more embodiments, the sintering may be in a gas environment containing CO, H2, hydrocarbons, H2/N2, H2/Ar, or combinations thereof. In some embodiments, the sintering may not reduce the separator and cathode sheets. In one or more embodiments, the sintering may be performed at at least about 300° C. In some embodiments, the fabricating may include tape casting the anode sheet. According to one or more embodiments, the method may further include selecting a ratio of pristine LTO particles to solid electrolyte to form the mixture based on predetermined desired capacity and rate capability of the reduced LTO.
As required, detailed embodiments of the present invention are disclosed herein; however, it is to be understood that the disclosed embodiments are merely exemplary of the invention that may be embodied in various and alternative forms. The figures are not necessarily to scale; some features may be exaggerated or minimized to show details of particular components. Therefore, specific structural and functional details disclosed herein are not to be interpreted as limiting, but merely as a representative basis for teaching one skilled in the art to variously employ the present invention.
Engineering the characteristics of the two separate conduction channels within the electrodes is particularly difficult for an all solid-state battery (SSB) cell. A major challenge of utilizing LTO in SSBs is the low electronic conductivity of LTO, which leads to poor rate performance. Unlike in traditional lithium ion batteries (where the electronic conductivity in LTO anode is enhanced by adding 1-3 wt. % carbon particles to the electrode slurry which is cast on a metal current collector, where the carbon particles forms a percolation network inside the electrode providing good pathway for electrons), using an anode structure containing carbon for a SSB is challenging because the SSB fabrication requires high temperature sintering (>700° C.), typically in air or an oxygen environment which may lead to carbon combustion. Performing the same operation in an inert environment may also fail because, at high temperatures, carbon may act as a reductant for the active material and solid electrolyte. Reduction of active material and solid electrolyte may lead to a loss of electronic conduction, ionic conduction, or both. This last problem may be overcome through the use of an oxide additive that is stable at high temperatures and electronically conductive, but achieving high conductivities is rare and often expensive.
Moreover, providing either conduction channel through the thickness of the electrode with a solid additive material may be difficult, since direct particle-to-particle contact is necessary for efficient conduction, either between conductive particles of solid material, or between conductive particles of solid material and the particles of the active material. Because both the electronic and ionic conduction additives require solid-solid contact with the active material particles, adding one component interferes with function of the other component. In some cases, the metallic particles (or electronic additive) may settle in between the solid electrolyte particles or solid electrolyte and active particles during the fabrication process, which may hinder the ionic conduction pathway leading to poor performance.
As shown by blocked pathway 175 in
The present disclosure relates to maintaining both electronic and ionic conduction pathways within the positive electrode using a modified LTO active material and solid electrolyte particles. Thus, the present disclosure may reduce the need for an additional electronic conductor, such as carbon or metallic particles.
The active material 250 is a modified lithium titanate (LTO-e) which has improved electronic conductivity over stoichiometric LTO (having an electronic conductivity <10−9 S/cm). In some embodiments, the LTO-e may be a doped LTO, in another embodiment LTO-e may be a doped LTO or a pristine LTO reduced with oxygen defects. The LTO-e may be doped with Mg2+, Zn2+, Al3+, Ni2+, Mo6+, Cu2+, or a combination thereof, to improve the electronic conductivity. In other embodiments, the oxygen defects are introduced by processing pristine LTO particles in a reducing atmosphere, to form reduced LTO particles. The processing in a reducing atmosphere is generally done at high temperature using a gas environment containing hydrogen (e.g., CO, H2, hydrocarbons, H2/N2, H2/Ar) or other reducing gas mixture(s). The processing in a reducing atmosphere takes place at a high temperature, such as from about 300 to 1200° C. In another embodiment, the processing is at about 400 to 1100° C., and in yet another embodiment at about 500 to 1000° C. For example, LTO powder may be exposed to a reducing atmosphere at about 900° C. for about 10 hours to form LTO-e. The LTO-e in the anode 210 forms a continuous network for electronic conduction throughout the battery. Ionic pathways 170 are shown between the active material 250 and the solid electrolyte 240. Conductive pathways are shown between active material 250. According to one or more embodiments, ionic pathways 170 between the active material 250 and solid electrolyte 240 are not blocked by electronic additives, such as carbon or metallic particles, as in
By either doping or valence reduction in LTO, a change in the electronic band structure may result in an appreciable change in electronic conductivity in the LTO-e. When pristine LTO particles are processed in a reducing atmosphere, the reducing gas may react with the oxygen in the LTO to form H2O. When oxygen is removed from the structure, a compensating reduction in valence of titanium may occur to balance the electrical charge (Ti4+ to Ti3+). Doping LTO or heating it in a reducing atmosphere may improve the electronic conductivity of the LTO-e by several orders in magnitude. In some embodiments, the two approaches may be combined. For example, LTO doped with Mo and heated at about 800° C. for about 5 hours in a 10% H2/Ar environment was shown to have an electronic conductivity of 10−2 S/cm, an improvement by 7 orders-of-magnitude. This alteration of the electronic conductivity may not display any significant decrease in capacity or rate capability over a conventional SSB electrode, and maintains a high capacity.
The present disclosure also relates to forming the SSB with the LTO-e active material. The LTO-e may either be formed through a reduction process before incorporation into the SSB electrode, or reduced after being incorporated into the SSB electrode.
According to an embodiment, pristine LTO may be reduced to LTO-e prior to incorporation into the SSB electrode. In this embodiment, LTO-e powder is mixed with solid electrolyte particles to form an anode composite mixture. The ratio of LTO-e to solid electrolyte may be optimized to obtain the capacity and rate capability appropriate for the application. The powder composite mixture would then be fabricated into a thin sheet or sheet, forming the anode sheet. The sheet may be fabricated by any method such as, but not limited to, tape casting. Similarly, an electrolyte separator sheet containing only solid electrolyte and a cathode sheet containing cathode active material and solid electrolyte would be separately fabricated. The anode, separator, and cathode sheets are then arranged to form a stack, and then the stack is laminated. The laminated sheets are then sintered at high temperature to farm a single electrochemical unit composed of dense layers with close particle-particle contacts. Sintering of the stack is completed in an inert atmosphere (e.g., argon or nitrogen).
According to another embodiment, pristine LTO may be used instead of LTO-e as the starting material. The ratio of pristine LTO to solid electrolyte may be optimized to obtain the capacity and rate capability appropriate for the application. The electrode and separator sheets are first fabricated and arranged, as described above, with the pristine LTO. After lamination, the stack containing pristine LTO is sintered. During the sintering the process, the stack is sintered at high temperature (e.g., 300-1200° C.) in a reducing atmosphere instead of inert atmosphere. In this method, the other components in the cell (other than the pristine LTO) are selected such that they are not affected by the reducing gas environment. During the sintering process, pristine LTO would be converted into LTO-e without affecting the other components in the SSB.
An LTO-e based SSB may be useful for 12 V auxiliary or starter batteries. Conventional LTO based Li-ion batteries for 12 V applications have problems with gas generation inside the cell at high temperature, which limits their use under the hood in the engine compartment. A SSB based on LTO would not suffer from this problem, and in fact, would perform significantly better at higher temperatures, both in terms of rate capability and cycle life.
The LTO-e based SSB described in the above embodiments may enable use of higher voltage cathode materials, further enhancing usable cell energy density to about 700 Wh/L. For Li-ion cell technology, increasing cell energy density through using higher voltage cathode materials is difficult due to the low operating voltage window of liquid electrolyte. Since solid electrolyte materials have high operating voltage windows, it could enable using higher voltage cathode materials. An LTO-e based SSB may also offer significant improvement in safety due to the elimination of a liquid electrolyte, which is present in the conventional Li-ion. In addition, an LTO-e based SSB may also result in simpler thermal management in a pack because of the high thermal stability of the solid electrolyte, which will reduce the cost at the pack level. As a result, LTO-e based SSBs may provide safe, high performance, and cost-effective solutions in the full suite of vehicle traction batteries, including EVs, PHEVs, and HEVs.
According to one or more embodiments, a SSB with an LTO-e active material is disclosed. A SSB based on a LTO-e active material may require little or no electronic conductive additive, as the LTO-e has improved electronic conductivity. As such, the processing complexity and potential incompatibilities in optimum processing conditions can be reduced. In addition to reducing processing complexity, the elimination of an electronically conductive additive allows for a higher loading of active material in the electrodes which enhances energy density, and allows for use of larger primary particles of LTO-e (over pristine LTO). Thus, providing a higher calendared density than is achievable for finer particles, and improved performance capabilities.
While exemplary embodiments are described above, it is not intended that these embodiments describe all possible forms of the invention. Rather, the words used in the specification are words of description rather than limitation, and it is understood that various changes may be made without departing from the spirit and scope of the invention. Additionally, the features of various implementing embodiments may be combined to form further embodiments of the invention.