LOCAL TWO-LAYER THERMAL BARRIER COATING

Abstract

A turbine blade with a ceramic thermal barrier coating system has a substrate designed as a blade platform and as a blade airfoil. On the substrate is a first ceramic layer as a thermal barrier coating, which protects the substrate in the exposed high temperature region and there is locally an increase of the thermal barrier coating for locally reinforcing the thermal barrier. The increase includes a material that is different from the material of the first ceramic layer. The local reinforcement is arranged over the first ceramic layer, without the first ceramic layer having a reduced layer thickness. The local reinforcement is provided at most on 30% of the area of the blade airfoil and is arranged close to a platform extending over the entire pressure side in the direction of flow and with an extent thereto in the radial direction of the blade airfoil is at most 30%.

Description

FIELD OF INVENTION

The invention relates to a thermal barrier coating system with a thermal barrier coating, a two-layer thermal barrier coating being applied locally in a highly stressed region.

BACKGROUND OF INVENTION

Ceramic thermal barrier coatings (TBC) are used to protect components for use at high temperatures from heat input. This is the case with turbine blades. For example, EP 2 845 924 A1 discloses using coating systems comprising a first ceramic layer of fully or partly stabilized zirconia and on it a layer that has a pyrochlore structure, such as gadolinium zirconate.

Because of greater thermal stresses in the case of turbine blades of a turbine, there are local temperature peaks in the pressure region of the turbine blade. This leads to greater consumption of the metallic protective layer or to spalling of the TBC. The use of cooling air holes would lead to the consumption of compressor air, and consequently to a reduction of efficiency.

Without countermeasures, the maximum running time of the turbine would be reduced.

SUMMARY OF INVENTION

An object of the invention is therefore to solve the aforementioned problem.

The object is achieved by a coating system according to the claims.

BRIEF DESCRIPTION OF THE DRAWINGS

In the figures

FIG. 1 shows a component with a coating system and

FIGS. 2 to 5 show various views of the configuration according to the invention.

The figures and the description only show exemplary embodiments of the invention.

DETAILED DESCRIPTION OF INVENTION

FIG. 1 shows a cross section through a blade airfoil of a turbine blade 1.

There is a suction side 7 and a pressure side 4, the turbine blade 1 being subjected to a flow of hot gas at an inflow edge 10 and having an outflow edge 13.

In the case of the turbine blade 1, there is a highly stressed region 22 in the region of the pressure side 4.

The turbine blade 1 is flowed around by a hot gas in the direction of flow 11.

FIG. 2 shows a plan view of a turbine blade 1, which has a blade airfoil 19 and a fastening region 16, shown simplified here.

In a local region 22, there is increased thermal stress. In this region there is a local reinforcement 36, 36′, 36″ (FIGS. 3, 4 and 5).

The local reinforcement 36, 36′, 36″ is advantageously arranged close to a platform 21 and advantageously can extend with a transitional region 39 (FIG. 5) over the entire pressure side 4 in the direction of flow 11.

Perpendicularly or in a radial direction thereto, that is to say in the direction 40, the extent is a maximum of 50%, in particular at most 30%. In the case of a turbine blade 1, this figure advantageously relates only to the blade airfoil 19.

In order to allow for this increased thermal stress, the thickness of the thermal barrier coating is increased locally.

FIGS. 3 and 4 show cross sections of the configuration according to the invention.

The increase in the layer thickness does not take place as a result of increased application of the same material of the surrounding layer 33, but instead a second material, different from the first material, is applied locally.

The first ceramic layer 33 is arranged on the blade airfoil 19 and the blade platform 21 of a turbine blade 1.

Advantageously, the thermal barrier coating 33 on the turbine blade 1 is a zirconium-based layer, in particular a layer of partly stabilized zirconia, and the reinforced TBC is achieved by local application of a pyrochlore layer 36, 36′, 36″, in particular based on gadolinium zirconate.

The material of the local reinforcement 36, 36′, 36″ is advantageously also fully stabilized zirconia.

The material of the local reinforcement 36, 36′, 36″ is advantageously made to be at least 10%, in particular 20%, more porous than the first ceramic layer 33.

In particular, like the first ceramic layer 33, it 36, 36′, 36″ likewise comprises partly stabilized zirconia.

In this case, as shown in FIG. 3, the second material of the local reinforcement 36, 36′, 36″ may be applied to the underlying ceramic layer 33, that is to say the layer thickness of the thermal barrier coating 33 underneath the reinforcement 36′ is just as thick as it is around the local reinforcement 36′.

Similarly, it is possible to make the underlying thermal barrier coating 33 somewhat thinner in the region of the local reinforcement 36″, so that there is a recess 34, in which the other material is applied locally, to be precise is applied in such a way that a thickening is obtained (FIG. 4).

The first ceramic layer 33 advantageously has a thickness of 350 μm-500 μm.

The local reinforcement 36, 36′, 36″ advantageously has a thickness of up to 300 μm, in particular up to 250 μm.

Advantageously, the local reinforcement 36, 36′, 36″ is at least 10%, in particular at least 30%, thinner than the first ceramic layer 33.

FIG. 5 shows only a plan view of the blade airfoil region 19 of the component 1.

Between the region that has only the first thermal barrier coating 33 and the local reinforcement 36, 36′, 36″ (FIGS. 3 and 4) there may also be a transitional region 39, which has a gradient in the composition of the first ceramic layer 33 and the local reinforcement 36′, 36″.

The transitional region 39 likewise represents a local area.

Claims

1.-12. (canceled)

13. A turbine blade with a ceramic thermal barrier coating system, at least comprising: a substrate designed as a blade platform and as a blade airfoil, optionally a metallic bond coat on the substrate,wherein on the substrate or optionally on the metallic bond coat there is a first ceramic layer as a thermal barrier coating, which protects the substrate for the most part or completely in the exposed high temperature region and that there is locally an increase of the thermal barrier coating for locally reinforcing the thermal barrier,wherein the increase comprises a material that is different from the material of the first ceramic layer,wherein the local reinforcement is arranged over the first ceramic layer, without the first ceramic layer having a reduced layer thickness,wherein the local reinforcement is provided at most on 30% of the area of the blade airfoil and wherein the local reinforcement is arranged close to a platform extending over the entire pressure side in the direction of flow and with an extent thereto which in the radial direction of the blade airfoil is at most 30%.

14. The turbine blade as claimed in claim 13, in which the material of the first ceramic layer comprises zirconia,in particular partly stabilized zirconia.

15. The turbine blade as claimed in claim 13, in which the material of the local reinforcement comprises a pyrochlore,in particular comprises gadolinium zirconate.

16. The turbine blade as claimed in claim 13, in which the material of the local reinforcement comprises fully stabilized zirconia.

17. The turbine blade as claimed in claim 13, in which the material of the local reinforcement is at least 10%,in particular 20%, more porous than that of the first ceramic layer,in particular likewise comprises partly stabilized zirconia.

18. The turbine blade as claimed in claim 13, in which a transitional region in the composition is present between the local reinforcement and the surrounding first ceramic layer.

19. The turbine blade as claimed in claim 13, in which the local reinforcement is made at least 10%,in particular at least 30%, thinner than the underlying first ceramic layer in this region of the local reinforcement.

20. The turbine blade as claimed in claim 13, in which the first ceramic layer has a thickness of 350 μm to 500 μm and/or the local reinforcement has a thickness of up to 300 μm, in particular up to 250 μm.