Patent Application
20170342660
The invention relates to a crêping doctor blade for manufacture of tissue and related paper products. The crêping doctor blade is made from a hardened steel strip that has its wear resistance enhanced by application of a thin cermet coating, using a Thermal Spray coating technique.
In the paper industry, crêping doctor blades are used for the manufacture of tissue and other related paper products. Creping doctor blades may be made of different materials such as Carbon steel strip, tool steel strip, composites and polymers. In addition, different types of coating may be applied by Thermal Spray coating in order to reinforce the working edge of the crêping doctor blade such as described in U.S. Pat. No. 7,244,340 B2.
In many Tissue mills Ceramic coated blades are the chosen crêping doctor blades due to the fact that they have relatively high hardness and therefore wear resistance but also they can accommodate the high temperatures that result from operation in contact with a steam filled ‘Yankee’ cylinder. In addition, they are not susceptible to one of the major wear mechanisms that limits the useful life of steel blades i.e. adhesive wear. The service life of ceramic coated crêping doctor blades is longer than even the best hardened steel blades but is still not consistently as long as is required for modern efficient tissue mills. This can be due to limitations in the hardness that can be achieved with ceramic coatings and also by the relationship between hardness and toughness, where extremely hard coatings can be prone to chipping at the important working edge of the blade.
One further drawback of ceramic coated crêping doctor blades is the fact that they are usually deposited by a plasma spraying process and therefore need a soft bond coat such as Ni—Cr. During the life of the blade, as wear proceeds, this bond coat can become exposed on the surface upon which the web impacts during crêping, leading to the need to make adjustments to the machine set-up to maintain paper quality.
An object of the present invention is to provide a coated crêping doctor blade that gives longer service lives in tissue making applications than the existing ceramic coated crêping doctor blades due to the improved wear resistance and anti-chipping properties. A further object is to provide a coated crêping doctor blade that produces tissue with consistent paper quality with a minimal need for the machine operators to progressively modify the operating conditions.
The invention is defined in the claims.
Ceramic coated crêping doctor blades have achieved wide acceptance in the tissue making industry because they generally offer a good service life whilst being compatible with most Yankee cylinders. In related industries tungsten carbide coated blades have been preferred to ceramic coated blades due to their superior wear resistance. In tissue making, the use of tungsten carbide blades has been limited by fears of damage occurring to the Yankee cylinders. Additional concerns regarding the use of tungsten carbide coated blades in crêping applications relate to their capability to withstand the higher temperatures that need to be endured by a crêping doctor blade. Whilst tungsten carbide coatings perform well in applications where the primary degradation mechanisms are abrasive wear or slurry erosion, their performance in circumstances where adhesive wear is one of the primary wear mechanisms is not widely documented. Adhesive wear (micro-welding) is known to be the main wear mechanism for steel blades in contact with Yankee cylinders.
In an attempt to overcome the limited resistance of tungsten carbide to high temperatures, related alternative coating solutions were sought by the inventors. Surprisingly, a cermet coating was found that was quoted as having a maximum service temperature of 700° C. but still had a quoted hardness greater than of HV0.3 1000. Furthermore, the identified cermet coating had a relatively low volume of metallic matrix (between 15 and 20 vol. %), to minimise the risk of coating suffering from adhesive wear during extended contact with a Yankee cylinder.
Initial HVOF spray trials using the manufacturer's spray parameters for the powder detailed in this invention were successful in producing a dense coating (<2% porosity) with art unexpectedly high hardness in excess of HV0.3 1100. Furthermore, testing the adhesion and general toughness of the coating revealed that it overcame some of the limitations presented by ceramic coatings.
Further development of the spray parameters led to improvements in both porosity and hardness with no significant reduction in toughness. The hardness levels in the optimised coating were on average HV0.3 1250 and porosity was less than 1.5%. It was possible to grind the resulting coating in the geometry required for common crêping applications with a high degree of dimensional stability and no evidence of chipping at the working edge or anywhere else.
Analysis of the cermet coating by SEM/EDS revealed the following chemical composition:
It should be noted that the SEM/EDS analysis is semi-quantitative and involves a certain inaccuracy, in particular for the light elements. The measured analysis for carbon is thus inaccurate and given for completeness only.
The cermet coating of this invention can be applied by any Thermal Spray coating process i.e. Plasma, HVOF or HVAF, or any combination of one or more of them. The optimum deposition method found for this coating was HVOF.
The particle size of the powder and the method of manufacturing of the powder play a significant role in achieving the low levels of porosity necessary to deliver the optimum hardness for this application.
The wear resistance and more importantly the effect of extended contact with a Yankee cylinder were assessed by carrying out trials on a small scale wear testing rig that was designed to simulate the crêping process. After extended contact the marks on the cylinder of the crêping simulator were of a level similar to the marks that occur after a similar length of exposure using a standard reference steel blade. These results gave the inventors the confidence to proceed to full tissue mill trials
Tissue Mill Trials
A series of five blades of this invention with a coating based on WOKA 7502 powder from Oerlicon Metco, were trialled at a tissue mill that routinely uses traditional Ceramic coated crêping doctor blades. The trial parameters were as follows:
Vibration monitoring was used during the trial to establish the stability of the interaction between the blade and the Yankee cylinder. The continuous monitoring of the vibrations revealed excellent and consistent results throughout the blade life. The measured levels of vibration were marginally lower and more consistent when compared to previous ceramic coated blades, according to the mill staff. The vibration results indicate zero or insignificant chatter.
The paper quality of the produced tissue was tested and found to be within the acceptable range. After the initial fine tuning of the process on the first paper roll, only minor changes were made to the crepe ratio and MD/CD ratio during the trial to maintain this paper quality. The build-up of coating and paper on the backside of the blade appeared to he minimal for the life of the blade, lending to excellent creping results.
The first trial blade lasted for a period of time that corresponded to 153% of the average life of a ceramic coated crêping blade and 134% of the life of the ceramic coated crêping blade that was used immediately prior to the trial: The amount of sheet breaks during the trial were minimal and acceptable to the mill staff. The examination of the first trial blade on removal due to a sheet break that was unrelated to the blade performance, revealed that it would have been possible to use the blade for a further period of life.
Further trial blades performed in a similar manner to the first blade with service lives well in excess of expectations with acceptable paper quality and minimal evidence of vibrations.
| Number | Date | Country | Kind |
|---|---|---|---|
| 14197073.1 | Dec 2014 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/SE2015/051325 | 12/10/2015 | WO | 00 |