Patent Application
20140234017
The present invention relates to long light metal billets for use in, e.g., extruding, and methods for manufacturing the same.
It has been conventionally known to manufacture an alloy piece billet by pressing alloy pieces made of a light metal (see, e.g., PATENT DOCUMENT 1). Out of such methods for manufacturing an alloy piece billet, various manufacturing methods configured to enhance yield have been known.
It has been known that, for example, as in PATENT DOCUMENT 2, while an upper punch is brought into contact with pieces with which the interior of a die is filled to confine the pieces, a lower punch is moved relatively upward to the die to press the pieces from below, and subsequently, the upper punch is moved downward to further press the pieces, thereby forming a long green compact.
Furthermore, a method has been known in which as in PATENT DOCUMENT 3, a first alloy billet, alloy pieces, and a second alloy billet are stacked in a die sequentially from bottom to top, the stack in the die is compressed under pressure such that alloy particles enter the first and second alloy billets, thereby producing an integrally formed long alloy billet.
PATENT DOCUMENT 1: Japanese Patent Publication No. H06-57305
PATENT DOCUMENT 2: Japanese Patent Publication No. H05-70802
PATENT DOCUMENT 3: Japanese Patent Publication No. 2010-24545
However, the manufacturing method of PATENT DOCUMENT 2 is intended only for long green compacts having a length of 30-80 mm, and consideration is not given to longer green compacts.
Furthermore, in the manufacturing method of PATENT DOCUMENT 3, the task in which the alloy pieces are appropriately interposed between the first alloy billet and the second alloy billet is troublesome.
It is therefore an object of the present invention to manufacture a long light metal billet of high quality by a simple method without using light metal pieces.
In order to achieve the above object, in this invention, a plurality of short light metal billets manufactured of light metal pieces are pressed in a long container having a larger inside diameter.
Specifically, a method for manufacturing a long light metal billet according to a first aspect of the invention includes: a preparation step of preparing a plurality of short light metal billets obtained by pressing light metal pieces; a stacking step of stacking the plurality of short light metal billets in a long container having an inside diameter that is larger than an outside diameter of each of the short light metal billets; and a compression step of pressing the plurality of short light metal billets in the long container at a temperature higher than room temperature, compressing the short light metal billets until the outside diameter of each of the short light metal billets becomes equal to the inside diameter of the long container, and joining the short light metal billets together at an interface between each adjacent pair of the short light metal billets by friction.
With the configuration, when the light metal powder is to be pressed, it can be also compressed at room temperature, and the light metal pieces are not used in the long container; thus, a long light metal billet is easily manufactured. Furthermore, since junction between each adjacent pair of the short billets is ensured by friction, a highly marketable long light metal billet which is resistant to handling is obtained.
According to a second aspect of the invention, in the first aspect of the invention, in the compression step,
e(δ−15)×(P/98.06)3×e((T−273)/20)>50
may be satisfied where δ represents a compression percentage given by (D−d)/D×100(%), D represents the inside diameter of the long container, d represents the outside diameter of each of the short light metal billets, P represents a contact pressure (MPa), and T represents a temperature (K).
With the configuration, even when the short light metal billets are not compressed at high temperature and high pressure, junction between each adjacent pair of the short light metal billets at the corresponding interface is ensured by selecting an appropriate compression percentage, thereby obtaining a strong long light metal billet which is not broken even with a small shock during transportation.
According to a third aspect of the invention, a plurality of short light metal billets obtained by pressing light metal pieces are stacked in a long container having an inside diameter that is larger than an outside diameter of each of the short light metal billets, are pressed in the long container at a temperature higher than room temperature, and are compressed until the outside diameter of each of the short light metal billets becomes equal to the inside diameter of the long container, thereby joining the short light metal billets together at an interface between each adjacent pair of the short light metal billets by friction.
With the configuration, when the light metal powder is to be pressed, it can be also compressed at room temperature, and the light metal pieces are not used in the long container; thus, a long light metal billet is easily manufactured. Furthermore, since junction between each adjacent pair of the short billets is ensured by friction, a highly marketable long light metal billet which is resistant to handling is obtained.
As described above, according to the present invention, a plurality of short light metal billets are pressed in a long container at a temperature higher than room temperature, and are compressed until the outside diameter of each of the short light metal billets becomes equal to the inside diameter of the long container, and thus, the short light metal billets are joined together at the interface between each adjacent pair of the short light metal billets by friction; therefore, a long light metal billet of high quality can be manufactured by a simple method without using light metal pieces.
An embodiment of the present invention will be described hereinafter with reference to the drawings.
Next, in a preheating step, the short light metal billets 1 are preheated to an appropriate temperature. This preheating step is not always required.
Next, in a stacking step, the plurality of short light metal billets 1 are stacked in a long container 2 having an inside diameter D that is larger than the outside diameter d of each of the short light metal billets 1. The number of the short light metal billets 1 may be any number greater than or equal to two. The long container 2 includes an unshown heating unit, such as a heater, and can keep an appropriate temperature T (K). An oxide film is formed at an interface 4 between each adjacent pair of the short light metal billets 1 before being pressed, and thus, the interface 4 can be visually identified.
Next, in a compression step, the plurality of short light metal billets 1 are pressed from above an upper surface of the uppermost short light metal billet 1 in the long container 2 at the temperature T higher than room temperature by a piston 3, and are compressed until the contact pressure reaches a predetermined contact pressure. In this case, it is preferable to satisfy the following expression (1):
where the compression percentage δ is given by (D−d)/D×100(%), D represents the inside diameter of the long container 2 (the outside diameter of the long light metal billet 5), d represents the outside diameter of each of the short light metal billets 1, P represents the contact pressure (MPa), and T represents the temperature (K).
When the compression step is performed under conditions satisfying the expression, the short light metal billets 1 are joined together at the interface 4 between each adjacent pair of the short light metal billets 1 by friction, and are bonded together to the extent that the interface 4 cannot be visually identified as illustrated in
As such, light metal pieces do not need to be inserted into the long container 2, and the long light metal billet 5 is very easily manufactured.
Drop Test
Next, a destructive test of a long light metal billet 5 manufactured by the manufacturing method was carried out.
In the test, it was assumed that the long light metal billet 5 dropped during handling for the transportation of the long light metal billet 5, and the long light metal billet 5 was kept in a horizontal position, and was freely dropped from a height of 40 cm to determine whether or not the long light metal billet 5 was broken.
In the manufacturing method, test specimens of long light metal billets 5 were prepared at different compressibilities δ (%), different temperatures T (K), and different contact pressures P (MPa), and were tested.
Test results at different compressibilities δ in
Therefore, according to the long light metal billet 5 of this embodiment and the method for manufacturing the same, the plurality of short light metal billets 1 are pressed in the long container 2 at a temperature higher than room temperature, are compressed until the outside diameter of each of the short light metal billets 1 becomes equal to the inside diameter D of the long container 2, and are thus joined together at the interface 4 by friction, thereby manufacturing a long light metal billet 5 of high quality by a simple method without using light metal pieces.
The embodiment of the present invention may be configured as follows.
Specifically, although, in the embodiment, the short light metal billet 1 is formed from light metal pieces made of a flat magnesium alloy plate having, e.g., a length of several millimeters, a material of the short light metal billet 1 is not limited to the above material, and the short light metal billet 1 may be formed from light metal pieces made of, e.g., magnesium, aluminum, an aluminum alloy, titanium, or a titanium alloy.
The foregoing embodiments are merely preferred examples in nature, and are not intended to limit the scope, applications, and use of the invention.
Many modifications and other embodiments of the inventions set forth herein will come to mind to one skilled in the art to which these inventions pertain having the benefit of the teachings presented in the foregoing descriptions and the associated drawings. Therefore, it is to be understood that the inventions are not to be limited to the specific embodiments disclosed and that modifications and other embodiments are intended to be included within the scope of the appended claims. Although specific terms are employed herein, they are used in a generic and descriptive sense only and not for purposes of limitation.
As described above, the present invention is useful for long light metal billets of light metal, such as a magnesium alloy, for use in, e.g., extruding, and methods for manufacturing the same.
1 SHORT LIGHT METAL BILLET
2 LONG CONTAINER
3 PISTON
4 INTERFACE
5 LONG LIGHT METAL BILLET
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2012/004095 | 6/25/2012 | WO | 00 | 1/28/2013 |