Patent Grant
9139467
Typical optical fibers include a core material and a cladding material, with each of the core and the cladding traditionally being fabricated largely from fused silica and having dissimilar refractive indices. A fiber can be formed by drawing a preform, which is a large mass that includes the core and cladding materials arranged in a shape that can resemble the cross-section of the finished fiber, but is much larger. The preform can be drawn in a fiber drawing tower during which the preform is heated and stretched from one end to form the optical fiber.
Optical fibers need to be able to operate at progressively higher power levels as performance demands continue to grow. A leading impairment to high power systems, and particularly high-power-per-unit-bandwidth systems, is stimulated Brillouin scattering (SBS), which is an acousto-optic interaction that manifests noise in low power applications and acts as a highly-efficient power reflector in high power applications. While there are optical fiber-based applications that do not have strict requirements on the laser spectrum, many systems such as spectroscopic lidar systems and coherently-phased fiber laser arrays rely principally on the ability to achieve a desired wavelength and spectral purity. SBS remains a serious stumbling block to the improvement of such systems.
In an attempt to decrease SBS, a variety of silica-based fibers possessing unconventional core compositions have been developed. Exemplifying such silica-based novel fibers are those derived using yttrium aluminum garnet (YAG) crystals. Unfortunately, while these materials show promise in decreasing SBS, such core compositions are very difficult if not impossible to realize using the chemical vapor deposition methods conventionally employed to manufacture optical fiber. Fiber designs including tailored acoustic velocity profiles of the fiber core and cladding that spread the SBS interaction over multiple acoustic frequencies have also been employed to lessen SBS. With careful fiber design, pure silica clad fibers with alumina-doped silica cores have also been formed to increase the acoustic wave loss, thereby decreasing the nonlinear interaction time and the Brillouin gain coefficient. While each of these complex and costly fabrication methods have been proven to partly suppress SBS or offer moderate enhancements in power levels, sufficient narrow-linewidth power scaling will remain impossible without a paradigm shift in the approach to the management of SBS.
What are needed in the art are optical fibers that exhibit extremely low, even zero, Brillouin scattering. In addition, what are needed in the art are facile, economical methods for forming such fibers.
According to one embodiment, an optical fiber is disclosed. The optical fiber includes a core material and a clad material. More specifically, the core material is the interaction product of a precursor core material and the clad material, and the precursor core material and the clad material have photoelastic constants of opposite sign.
In one embodiment, the precursor core has a single component and the precursor core and the clad material can have photoelastic constants of opposite sign. According to another embodiment, the precursor core can include multiple precursor core materials, and one or more of the precursor core materials can have a photoelastic constant of opposite sign to that of the clad material. In this embodiment, the photoelastic constant of the precursor core can be the same or opposite of the photoelastic constant of the clad material. In those embodiments in which the photoelastic constant of the precursor core is of the same sign as that of the clad material, the absolute value of the photoelastic constant of the precursor core can be about 0.5 or less of the photoelastic constant of the clad material.
Also disclosed are methods for forming an optical fiber. For example, a method can include drawing a fiber preform, the fiber preform including a core component and clad component. The core component can include a precursor core material and the clad component can be formed of a clad material. In addition, the precursor core material and the clad material can have photoelastic constants of opposite signs. In one embodiment, at least one component of the core component and the clad material can have photoelastic constants of opposite signs. The fiber preform can be drawn at a draw temperature at which the precursor core material is molten.
a) is an end-on view of a fiber as described herein.
b) presents an example of a splice of a segment of a fiber as described herein (left-side of image) to standard telecom fiber (right-side of image).
Repeat use of reference characters in the present specification and drawings is intended to represent the same or analogous features or elements of the present disclosure.
Reference will now be made in detail to various embodiments of the disclosure, one or more examples of which are illustrated in the accompanying drawings. Each example is provided by way of explanation of the subject matter, not limitation thereof. In fact, it will be apparent to those skilled in the art that various modifications and variations can be made in the present disclosure without departing from the scope or spirit of the subject matter. For instance, features illustrated or described as part of one embodiment, can be used on another embodiment to yield a still further embodiment.
The present disclosure relates generally to optics, and more particularly to optical fiber systems and methods. According to disclosed methods and systems, an optical fiber can be formed that exhibits very low Brillouin scattering (also referred to throughout this disclosure as Brillouin activity or Brillouin activity), and in one embodiment, having zero Brillouin activity. In addition, disclosed fibers can exhibit very large Brillouin frequency shift and athermal Brillouin characteristics, i.e., the Brillouin frequency shift of the fibers can be essentially immune to change in temperature and/or a-tensic characteristics, in which the Brillouin frequency shift of the fibers can be essentially immune to change in strain.
Also disclosed are methods for forming the fibers. Briefly, an optical fiber can be formed from a preform that includes a clad glass and a core precursor material. The clad material can include a glass having a photoelastic (Pockels) constant that is either positive or negative, and the precursor core material can be a material that can have a photoelastic constant of the opposite sign as the clad material. For instance, if the clad glass is a silica, which has a positive photoelastic constant, the core precursor material can have a negative photoelastic constant, and vice versa. In one embodiment, the precursor core can be a multi-component precursor core comprising a plurality of precursor core materials and one or more of the precursor core materials can have a photoelastic constant that is of the opposite sign as the clad material. In another embodiment, the precursor core can comprise a single precursor core material having a photoelastic constant of opposite site to that of the clad material.
In addition, the precursor core material can have a melting temperature that is lower than the draw temperature of the clad material.
Formation methods include drawing the fiber at a temperature greater than the melting temperature of the precursor core material, leading to formation of a multi-order (e.g., binary, ternary, etc.) glass core in the formed fiber. More specifically, the glass core of the formed fiber is the interaction product of the of the molten precursor core material with the partially dissolved clad material. The core precursor and clad materials are selected such that they exhibit miscibility above the melting temperature of the core temperature and the core material is thus formed during the fiber draw. During formation, the glass core interaction product is quickly quenched so as to avoid phase separation thus forming a multi-order glass core that is one homogeneous (glassy) phase the composition of which includes both compounds.
The formation process utilized to form the disclosed fibers can be highly beneficial as the core material of the formed fiber is the multi-order interaction product of the precursor material(s) that have positive and/or negative photoelastic constants. Attempts to form fibers including such core materials according to traditional fiber forming methods would not succeed. According to a traditional fiber forming method, the final core material would first be formed as a core preform and then the preform would be drawn to alter the shape of the preform while retaining the material make-up of the preform. When considering a final fiber core of the interaction products as described herein, however, a preform of the final core material would phase-separate during the fiber draw. In the presently disclosed methods the interaction product core material is formed at the time of the fiber draw, rather than previous to the draw as in traditional methods. Thus, the final product core material is formed at the draw and then quickly quenched; preventing the phase separation that would ensue if the fibers were to be formed according to traditional formation methods.
Beneficially, it has been found that the photoelastic characteristics of the precursor core material and the clad material can be tailored upon development in the core of the multi-order glass system during fiber formation. The complementarity of the photoelastic coefficients of the precursor materials used in forming the core glass and the homogenous nature of the product core material provides for the very low Brillouin scattering levels of the formed fibers.
In one embodiment, the disclosed fibers can have a Brillouin gain coefficient of less than about 10−10 meters per Watt (m/W). For instance, a fiber can have a Brillouin gain coefficient of less than about 5×10−1 m/W, less that about 10−11 m/W, less than about 10−12 m/W, or less than about 10−13 m/W. In one embodiment the Brillouin gain coefficient can be between about 4.5×10−11 m/W and about 2×10.16 m/W. The Brillouin gain coefficient is defined as follows for a given optical wavelength (λ):
gg=2πn1p122/cλρVgΔvB
where
Since the SBS threshold is inversely proportional to this quantity, the requisite gB will depend on the amount of optical power desired for a fiber system.
The fibers can have a very high Brillouin frequency. The Brillouin frequency can be determined from the product of two times the acoustic velocity of the acoustic mode times the refractive index of the optical mode divided by the optical wavelength. For example, for wavelengths near 1550 nm, a fiber can have a Brillouin frequency greater than about 10 GHz, greater than about 12 GHz, or greater than about 13 GHz. For instance, a fiber can have a Brillouin frequency from about 13 GHz to about 16 GHz. The fibers can also exhibit little change in Brillouin characteristics with regard to temperature. For instance, the frequency can change by less than about 1000 kHz per degree Kelvin (kHz/K), or less than about 750 kHz/K. In one embodiment, the fibers can be athermal with regard to Brillouin frequency. For instance, Brillouin frequency can change by less than about 20 kHz/K, less than about 15 kHz/K, or less than about 10 kHz/K.
The fibers can also exhibit little change in Brillouin characteristics with regard to strain. For instance, the frequency can change by less than about 500 MHz per % of elongation, or less than about 400 kHz/% elongation. In one embodiment, the fibers can be a-tensic with regard to frequency. For instance, frequency can change by less than about 20 MHz/% elongation, less than about 15 MHz/% elongation, or less than about 1 MHz/% elongation.
In general, the low Brillouin gain fibers can be formed according to a preform draw process.
Furthermore, the clad component 14 can be doped with any of a variety of dopants to achieve a desired Brillouin scattering property, refractive index, thermal expansion coefficient, and/or draw temperature such that it draws into fiber at a temperature above the melt temperature of the precursor core material.
The core component 12 can include a precursor core material that has a photoelastic constant that is opposite in sign to the photoelastic constant of the clad material. More specifically, all or only a portion of the precursor core material(s) that form the core component 12 can have a photoelastic constant that is opposite in sign to that of the clad material. For example, in one embodiment, the core component 12 can include a plurality of different precursor core materials in a composite precursor core. In this embodiment, at least one of the plurality of precursor core materials can have a photoelastic constant that is opposite in sign to the photoelastic constant of the clad material. In another embodiment, the core component 12 can be formed of a single precursor core material that has a photoelastic constant that is opposite in sign to the photoelastic constant of the clad material. In this embodiment, the precursor core can have a photoelastic constant that is opposite in sign to the photoelastic constant of the clad material.
In those embodiments in which the precursor core component 12 is a composite of precursor core materials, at least one precursor core material can have a photoelastic constant that is opposite in sign to the photoelastic constant of the clad material. In this embodiment, the overall photoelastic constant of the core component 12 can be either of the same sign or the opposite sign as that of the clad material. For instance, some silicates such as magnesium aluminum silicate as may be utilized as the core component 12 can include a constituent material that has a negative photoelastic constant (e.g., alumina, magnesia) in conjunction with a constituent material that has a positive photoelastic constant (e.g., silica). The overall photoelastic constant of such a silicate precursor core component may be low and positive. Similarly, a precursor core component 12 such as YAG can have a low and positive photoelastic constant overall and can include both alumina (a negative photoelastic constant) and yttria (a positive photoelastic constant). When these multiple precursor core materials are combined as a composite precursor core component with a clad material to form a preform, the composite core component can have an overall photoelastic constant that is of the opposite sign to that of the clad material. However, in another embodiment, the composite core component can have an overall photoelastic constant that is of the same sign as that of the clad material. When this is the case, the absolute value of the photoelastic constant of the composite core component can be significantly less than the absolute value of the photoelastic constant of the clad component (or the clad material). For instance, the absolute value of the photoelastic constant of the composite core component can be about 0.5 or less of the photoelastic constant of the clad component. In one embodiment, the absolute value of the photoelastic constant of the composite core component can be about 0.35 or less of the photoelastic constant of the clad component, or about 0.25 or less in some embodiments.
In one embodiment, the core component 12 can include an aluminum-based compound having a negative photoelastic constant, including, without limitation, an aluminate, an aluminosilicate, an aluminophosphate, an aluminoborate, and so forth. In one embodiment, the core component 12 can include aluminum oxide, Al2O3, e.g., sapphire. For instance, the entire core component can be formed of a single material that has a negative photoelastic constant and this core component can be combined with a clad component formed entirely of a single material that has a positive photoelastic constant.
In addition to the relationship of the photoelastic constants of the core and clad components, the preform materials can also have a thermal relationship. More specifically, the core component 12 can have a melting temperature that his less than the draw temperature of the clad component 14.
It should be understood that precursor core materials for use in forming the core component 12 are not limited to aluminum-based materials, and other materials can alternatively be utilized and paired with a clad material that has a photoelastic constant of the opposite sign (or larger absolute value, as discussed above) and appropriate draw temperature (i.e., the draw temperature of the clad component 14 is greater than the melting temperature of the core component 12). For example, the core component 12 can include spinel (MgAl2O4), barium oxide (BaO), β-barium borate (BaB2O4), and so forth as precursor core materials that can melt at the fiber draw temperature and result in a multi-order glass core that is the interaction product of the precursor core material(s) and dissolved clad material.
During fiber formation, as the core component becomes molten, it interacts with dissolved cladding material resulting in the formation of a multi-order glass core in the formed fiber. Thus, the formed fiber can be an all-glass optical fiber including an outer clad and an inner glass core of a composition that differs from the core precursor material(s).
In addition to the benefits previously mentioned, the formation technique of the optical fibers can provide an optical fiber with a very high concentration of desirable materials in the core. For instance, when considering formation of an optical fiber by use of an aluminum-based oxide core precursor material, the formed fiber can include a very high concentration of alumina, and in particular, much higher than possible according to conventional formation processes in which an alumina may at most be included as a dopant in the core due to phase separation issues as discussed previously. For example, the core of the all-glass optical fiber can have an aluminum oxide concentration of greater than about 15 mole percent of the core component, or greater than about 20 mole percent, in one embodiment. For instance, the all-glass fiber can have an aluminum oxide concentration in the core of from about 20 mole percent to about 90 mole percent of the core component, or from about 30 mole percent to about 80 mole percent of the core component, or about 55 mole percent of the core component. In one embodiment, a fiber can have an average alumina concentration of 54 mole percent of the core component and a Brillouin gain coefficient of less than about 10−12 m/W, for instance about 3×10−13, which is nearly 100 times lower than commercial fiber as currently known and the lowest specified value known to date. In another embodiment, a fiber formed with an average alumina concentration of about 38 mole percent was found to be athermal in its Brillouin frequency.
The core component 12 can also include one or more dopants as are known in the art for inclusion in an optical fiber core such as active dopants. For instance, the core component 12 can include as dopant one or more selected Group III and IV elements, rare earth elements, transition metals, and so forth. In one embodiment, the core component 12 can be doped with a transition metal or lanthanide ion.
The optical fibers can include high concentrations of the aforementioned Group III and IV elements, rare earth elements, and/or transition metal dopants. Thus, disclosed methods can be a route to formation of high dopant content optical fibers.
The core component 12 can be provided in any suitable form. For instance, the precursor core material(s) of the core component 12 can be provided as a plurality of chips, as a powder, or in any other form. Moreover, the precursor core material can be provided in a crystalline form or in an amorphous form.
In one embodiment, the core component 12 can be formed by compacting powders of the precursor core material to form a solid rod. This may serve to limit the amount of air removal during the fiber formation. In another embodiment, however, it may be preferred to provide the core component 12 in the form of a powder or particle mixture, with no compacting prior to loading the core component 12 in the cladding component 14.
A preform 10 can be formed by first forming the clad component 14 with the desired geometry. In the example of
The core component 12 can be in any suitable starting formation, such as a boule, window, slug, a plurality of chips, a powder, and so forth. For example, the core component 12 can be a compacted powder including the precursor for the desired core material and shaped in the form of a boule.
Referring again to
The system 20 includes a hot zone 30, such as can be included in a fiber drawing tower furnace. As an example, the hot zone 30 can apply heat that is sufficient to soften the material of the clad component 24 and to melt the core precursor material of the core component 26. Specifically, the hot zone 30 can be set to a temperature that is above the melting point of the core precursor material and at which the clad component 24 is sufficiently soft so as to draw as desired. Temperatures for the hot zone 30 during a drawing process can depend upon materials included in the preform 22, the size of the preform 22 and the fiber 28, and the like.
The draw temperature at which the precursor core material is molten and the clad component 24 is at a viscosity to provide an acceptable draw can be only slightly above the melting temperature of the core component 26 (i.e., the one or more precursor core materials), For instance, the draw temperature can be less than about 10° C. above the melting temperature of the precursor core material(s), for instance between about 1° C. and about 10° C. above the melting temperature of the precursor core material. This may be preferred in an embodiment in which the melting temperature of the core component 26 and the targeted drawing temperature of the clad component 24 can be quite close to one another. However, as an alternative example, the drawing temperature of the hot zone 30 can be greater than about 10° C. higher than the melting temperature of the core component 26, for example greater than about 20° C. higher, greater than about 50° C. higher, or more. Furthermore, the expansion coefficients of the precursor core material(s) and the cladding material can be substantially similar, or even substantially the same. However, it is to be understood that the expansion coefficient of the precursor core material and the cladding material can also differ.
In general, the draw can be carried out under atmospheric conditions. This is not a requirement, however, and the draw can alternatively be carried out under vacuum (e.g., complete or partial vacuum), in a reducing atmosphere, or under an inert atmosphere. While not wishing to be bound to any theory, drawing under a vacuum may improve the rate of removal of any volatile by-products from the resultant fiber.
According to the example of
The resultant core can be single-mode or multimode. The optical fiber 28 can be wound around a take-up reel 34 as it leaves the hot zone 30, such that it can cool and solidify. The optical fiber 28 can subsequently be run through a polymer bath (not shown), such that a jacketing material can be coated onto the optical fiber 28.
Beneficially, fabrication of an optical fiber 28 from a preform 22 can be accomplished in a facile manner. Specifically, upon forming the preform 22, the resultant optical fiber 28 can be formed in a manner similar to typical fibers formed of traditional materials. However, the optical fiber 28 can exhibit superior optical performance due to the multi-order glass core. It is to be understood that the system 20 in the example of
The inner cladding 74 can be, e.g., a pump cladding, and can be formed from a positive or negative photoelastic constant material such as an oxide glass material having a positive photoelastic constant. The outer cladding 76 and the inner cladding 74 can be formed of the same or different glasses such as different respective glass materials or the same glass material with different dopants. The core 72 can include a multi-order glass, similar to as described above in the examples of
The core and/or clad of a given fiber is not limited to having a circular cross-section. For instance, as shown in
Disclosed optical fibers represent a marked advancement for a plurality of applications such as telecommunication, sensor, and high energy laser systems. In one embodiment, the optical fibers can be beneficially utilized in lidar applications, such as upper atmosphere helium lidar as may be utilized in climate studies. For example, it has been suggested that the ideal laser for such applications would be a 100 MHz spectral width, pulsed ytterbium system, however with currently available systems it is impossible to obtain the necessary power due to SBS. The disclosed optical fibers can provide a route to obtaining this ideal system. Similarly, the National Aeronautics and Space Administration has been working to develop a carbon dioxide lidar system for some time, but has been unable to obtain the necessary power in the developmental systems. The disclosed optical fibers could solve such problems.
Disclosed fibers can also be utilized in development of systems that could beneficially utilize a narrow linewidth, such as sensor applications (e.g., oxygen sensors). In addition, disclosed fibers can be formed to longer lengths with lower losses, which could be useful in forming Raman-shifters. Narrow linewidth lasers that can be utilized at any wavelength present multiple possibilities, including use in applications in which dye lasers are currently utilized.
The disclosure may be further understood with reference to the Examples, set forth below.
A single-crystalline sapphire rod of unknown purity, measuring about 2.8 mm in diameter by 100 mm in length (Almaz Optics, Marlton, N.J.), was sleeved inside an F300 fused silica tube (Hereaus-Tenevo, Buford, Ga.) measuring about 3 mm inner diameter by 30 mm outer diameter. This preform assembly was drawn at 2100° C. on a Heathway optical fiber draw tower (Clemson University) into fiber at a rate of 20 m/min with a target diameter of 150 μm. The 2100° C. draw temperature exceeded the 2050° C. melting point of the sapphire permitting fiberization using the molten core approach described herein. As the draw temperature was higher than that usually employed to fabricate silica optical fiber, the draw tension was reduced with the final diameter of the fiber fluctuating between about 125 and about 170 μm over the 450 meters of fiber that was drawn. However, this was beneficial as it permitted a single draw to yield a range of fiber diameters that were consistent over several meter lengths that could be reliably tested.
For molten-core derived fibers, the diameter influences the core composition due to core/clad dissolution- and diffusion-related processes. Thus, each fiber section of differing diameter had concomitantly a different alumina concentration. Accordingly, one draw permitted a systematic evaluation of properties as a function of alumina concentration. All fiber lengths utilized in the Brillouin measurements were less than two meters where the diameter and core composition largely were constant. The fiber was coated during the draw with a standard single coating (DSM Desotech Inc., Elgin, Ill.) to a final diameter of about 270 μm.
Elemental analysis was conducted under high vacuum, using energy dispersive x-ray (EDX) spectroscopy in secondary electron (SE) mode on a Hitachi SU-6600 analytical variable pressure field emission scanning electron microscope. Prior to examination, the fibers were sleeved and UV epoxy cured into silica glass ferrules and their ends mechanically polished to a 1 micron finish. The fiber samples were sputter coated with carbon prior to analysis to provide a conductive layer to mitigate any charging effects from the glass. The refractive index profile at arbitrary positions along the length of the fiber was measured at 980 nm by Interfiber Analysis Inc. using a spatially resolved Fourier transform technique.
Spectral attenuation measurements were performed on a typical 4.5 meter segment of the drawn fiber. In the visible range, a tungsten light source was used whereas; for IR measurements, the broadband light source option on the Hewlett-Packard 7095 series optical spectrum analyzer was used.
A heterodyne system was used to measure the Brillouin gain spectrum (BGS) of the various fibers. Briefly, the system launched a narrow-linewidth signal at 1534 nm (λo=1534 nm) through a circulator and into a fiber being tested. The Stokes' signal generated in the test fiber passed back through the circulator, was optically filtered and amplified, and was finally analyzed with a heterodyne receiver. As a control, a standard single mode fiber (SMF-28™, Corning Incorporated) was used. In order to measure the temperature dependence of the frequency, the test fibers were immersed in a heated water bath, controlled from room temperature (21.5° C.) up to the boiling point (100° C.), such that measurements over a temperature range of about 80K could be made.
Table 1 compiles the maximum concentration of alumina and the core size measured from four sections of the sapphire-derived optical fiber.
Due to the strength of the Brillouin gain, Brillouin scattering data could only be obtained for Fibers A-C. As can be seen, the maximum alumina content in Fiber D was about 54 mole percent
The Brillouin properties of the fibers were measured in order to obtain data over a range of compositions (Table 1). The Brillouin gain was far too low to obtain a measurement for Fiber D. While the peak frequency could be measured for Fiber C, the signal-to-noise ratio was far too low to yield a reliable spectral width measurement. The data was analyzed using an additive model in order to determine the physical properties of the alumina constituent. While the core diameters are fairly large (Table 1), these fibers are not truly bulk material and are acoustic anti-guides since alumina increases the acoustic velocity of the core relative to that of the pure silica cladding.
Measured features of the Brillouin spectra are summarized in Table 2.
The measured acoustic velocities are plotted as a function of alumina concentration for the sapphire-derived fiber samples tested, along with the best-fit additive model to the data, in
‡The photoelastic constant was assumed to have the same value as that of bulk sapphire.
Inspection of the table suggests a significant advantage in utilizing high-alumina content optical fibers for the realization of an ultra-low Brillouin gain media.
In summary of the Brillouin gain measurements, in glasses with a large quantity of alumina, the increase in acoustic velocity, acoustic frequency, Brillouin spectral width, and mass density, coupled with the decrease in photoelastic constant, all cooperate to impart a tremendous reduction to the Brillouin gain, which only is offset partly by an increased refractive index. The fiber sample with the highest measured alumina content (Fiber D) was found to have a calculated Brillouin gain coefficient of around 3.1×10−13 m/W, or around 19 dB lower than commercial SMF-28™. Broadening the optical signal spectrum to 1 GHz affords an additional 7 dB reduction in the Brillouin gain at a wavelength of 1534 nm. This would increase the SBS threshold to levels comparable to that of stimulated Raman scattering in conventional single mode fiber materials.
This example provides details on the fabrication of BaO-doped silica fibers. Characterizations of the fibers included determination of the refractive index profiles, attenuation spectra, compositional profiles, Brillouin spectra, and strain- and temperature-dependencies of the Brillouin scattering frequency. From these, the physical attributes of the bulk glassy baria were determined utilizing an additive model.
Fiber Fabrication
As-purchased BaO powder (99.99% purity; Sigma Aldrich, St. Louis, Mo.) was sleeved inside an HSQ (Heraeus) fused silica tube measuring about 3.5 mm inner diameter by 30 mm outer diameter. This preform was drawn on a Heathway draw tower (Clemson University, Clemson, S.C.) at a temperature of about 1975° C. This temperature was chosen because BaO possesses a melting temperature of about 1920° C. fulfilling the requirement of the process that the core phase melt at a temperature below which the cladding glass draws into fiber. Between 100 and 200 meters each of fiber at (uncoated) diameters of 125 μm, 150 μm, and 175 μm were collected. The fibers all were coated with a standard single acrylate coating (DSM Desotech, Elgin, Ill.). The three fibers of this study were designated ‘E,’ ‘F,’ and ‘G,’ in order of increasing baria content. In the present case, these were the 150 μm, 175 μm, and 125 μm fibers, respectively. While data for all the fibers were similar, where appropriate data for Fiber G is shown as the illustrative example since it represented the highest baria content.
Refractive Index Profiles and Attenuation Spectra
The refractive index profiles (RIPs) were measured by Interfiber Analysis (Livingston, N.J.) at a wavelength of about 1000 nm (with an uncertainty of ±0.00005) using a spatially resolved Fourier transform technique. The measured refractive index difference, Δn, at a wavelength of 1000 nm was assumed to be the same as at the Brillouin probe wavelength of 1534 nm, since it could not be measured at the longer test wavelength. Thus the refractive index of silica was taken to be its value at 1534 nm (1.444) and Δn was assumed from the RIPs. Spectral attenuation measurements were performed on ˜1-2 meter segments of the drawn fiber. Over the range from 700-950 nm, a tungsten light source was used along with a miniature spectrometer (Ocean Optics Inc.). For the longer-wavelength measurements (up to 1700 nm), the broadband light source option on a Hewlett-Packard 7095 series optical spectrum analyzer was used.
Compositional Profiles
Compositional analyses of the BaO-derived fiber cross-sections were performed under high vacuum, using energy dispersive x-ray (EDX) spectroscopy in secondary electron (SE) mode on a Hitachi SU-6600 analytical variable pressure field emission scanning electron microscope (with ±0.01% elemental uncertainty) at an operating voltage of 20 kV. Prior to examination, the fibers were sleeved and UV epoxy cured into silica glass ferrules and their ends mechanically polished to a 1 micron finish. The fiber samples were sputter-coated with carbon prior to analysis in order to provide a conductive layer to mitigate charging effects from the glass. Throughout this example, [BaO] is defined to be the BaO concentration in units of mole percent.
Brillouin Spectra
The Brillouin spectra of the fibers were recorded utilizing a heterodyne system. The system launches a narrow-linewidth signal at 1534 nm (λo=1534 nm) through a circulator and into the test fiber. The Stokes' signal generated in this fiber passes back through the circulator, is optically filtered and amplified, and finally is analyzed with a heterodyne receiver. Spectra were recorded for a number of applied strains (E, defined here to be a fractional elongation), including the zero-strain case, and temperatures (T), also including room temperature. In order to measure the temperature dependence of the Brillouin frequency, the test fibers were immersed in a heated water bath, controlled from room temperature (21.5° C.) up to the boiling point (100° C.), such that measurements over a temperature range of about 80K could be made. In order to measure the strain dependence, one end of the test fiber was affixed to a rigid plate via an epoxy and the other end to a linear translation stage possessing a calibrated micrometer, wherein a linear stretch could be applied. It is noted that the measurements of all Brillouin spectra were performed on <1.5 meter segments of fiber in order to avoid any inhomogeneous spectral broadening due to any lengthwise variations in the fiber composition.
Thermo-Optic and Strain-Optic Coefficients
The measured Brillouin frequency is a function of the modal index (nm), acoustic velocity (V), and optical wavelength (λ0) as 2 nmV/λo and taking the derivative with respect to temperature or strain yields
which possesses both optical (dn/d(T,ε)) and acoustic (dV/d(T,ε)) terms. The optical terms are proportional to the thermo-optic coefficient (TOC) and strain-optic coefficient (SOC), and the acoustic terms are the thermo-acoustic and strain-acoustic coefficients (TAC and SAC, respectively). Hence, to estimate how the acoustic velocity is influenced by strain or temperature, some knowledge or estimates of the TOC or SOC were needed.
These values were estimated by use of a fiber ring laser that was constructed utilizing a segment (˜2 m) of test fiber for which determination of the TOC or SOC was desired. Since the laser was intentionally constructed to possess a plethora of longitudinal lasing modes, collecting the output of the laser with a detector and observing the resulting electrical output with an electrical spectrum analyzer (ESA) disclosed the free spectral range (FSR) of the laser in addition to the presence higher order harmonics of the FSR at the ESA. The FSR of this laser is a function of any strain (ε) or change in temperature (ΔT) of the test fiber, and thus any changes in strain or temperature will result in a change in measured frequency given by
where M is the harmonic number on which the measurement is performed, c is the speed of light, and Q, in the case of strain, is defined to be Q=−½no3(SOC), with the SOC defined from the photoelastic constants and Poisson ratio (vp) to be SOC=p12−νp(p11+p12). Q is simply the TOC in the case of temperature. Clearly, the larger the M value, the more accurate will be the measurement. In Eq. (2), n is the mode index of the test fiber, which is a function of both temperature and strain, as n=n0+εQ+ΔT(TOC) with n0 being the zero-strain room-temperature value. The test fiber length is similarly dependent on strain and temperature with l=lo+εlo+ΔTξlo where ξ is the linear thermal expansion coefficient. Since the core is held rigidly in the fiber, the linear thermal expansion coefficient of silica (i.e., the cladding) is assumed for each fiber. Finally, the product NL is found from a measurement of the zero-strain, room-temperature FSR (FSR0) as NL=(c/FSR0)−lono.
Results
Table 4, below presents a summary of the fiber characteristics including the peak refractive index difference and baria concentrations (in both wt % and mol %) for all three fibers fabricated and studied in this example. The modal index for each fiber was calculated from its RIP, and these values also are provided in Table 4. Additionally, the measured attenuation coefficients at 1534 nm also can be found in Table 4. The attenuation spectrum for Fiber G is provided in
Previously, the spectral distribution of Brillouin scattering involving the HOMs was continuous, whereas in the present case, distinct peaks appear. This is especially apparent in the Fiber E spectrum, where an additional peak near 10.3 GHz appears, rather than having a continuum-like distribution on the red side of the peak.
The measurement of the TOC and SOC for each fiber was facilitated with a ring laser configuration as described. Measurements of the change in FSR versus temperature were much more linear than those versus strain. This is currently believed to be due to the optical mode distribution in the fibers being different for both measurements (thermal and strain). If the distribution of optical modes excited in the multimode fiber changes with some measurement condition, then so does the effective modal index in the ring laser, thereby influencing the measurement of the FSR by obscuring the change in the material values. In the case of temperature, the fiber was coiled and kept firmly in a heated bath such that movement of the fiber was kept minimal. However, in the case of strain, the fiber was stretched linearly with one fiber end translated with respect to the other. Hence with the latter, due to the motion of a small quantity of fiber beyond the translation stage, the ring became somewhat distorted as the measurement progressed, and thus probably resulted in changes in the distribution of optical modes excited in the BaO-doped test fiber. This led to a wide uncertainty range in the SOC measurements summarized in Table 4. By far, the worst-quality SOC data originated from Fiber E, which is consistent with the relative quality of the Brillouin spectra, and was probably related to the quality of splice achieved with this fiber.
A rod of transparent ceramic spinel (Technology Assessment & Transfer, Inc., Millersville, Md.) was sleeved into a high purity silica tube and drawn at 2175° C. on a custom-built fiber draw tower (Clemson University). Because spinel is exceedingly refractory, with a (congruent) melting point of about 2135° C., a thick-walled silica tube (3.5 mm inner diameter, 40 mm outer diameter) was used for the cladding. By employing a thick-walled cladding tube, the effective draw temperature can be raised to above the melting point of the core phase, as required by the molten core method. Several hundred meters of 125 micron diameter silica-clad spinel-derived glass (i.e., now magnesium aluminosilicate) core fiber was drawn and coated with a conventional telecommunications UV-cured polymer coating, and two segments with different core sizes (and hence compositions), denoted hereafter as H and I, were utilized in the example. The refractive index profiles (RIPs) were measured (Interfiber Analysis, Livingston, N.J.) at a wavelength of 1000 nm, and the compositions were determined by energy dispersive X-ray (EDX) analysis (Clemson University). A representative optical image of the fiber (Fiber H) is shown in
In order to characterize the fibers' acousto-optic properties, the Brillouin spectrum was measured using a heterodyne method. The heterodyne setup consists of a 1,534 nm source, an optical circulator, amplifier, and heterodyne receiver. The test fiber was spliced at the end of a circulator, through which a 1,534 nm source was launched and the backward propagating Stokes' signal from the sample fiber passed back through the circulator to be filtered, amplified, and measured using the heterodyne receiver with a 1 MHz resolution. As an aside, an intermediate single mode fiber (SMF, Corning SMF-28™) was used between the circulator and the sample fiber. The splicing of the sample fiber to standard telecom-grade SMF was accomplished utilizing a standard SMF-SMF routine on a Vytran GPX glass processing system. An example of such a splice is shown in
Results
The Brillouin spectra are shown in
By way of comparison,
The Brillouin spectra from both fibers were considerably broadened due to the acoustically anti-guiding nature of the fibers. In fact, the spectral width of the core interaction was broadened to well over 200 MHz, diminishing its contribution relative to the cladding for Fiber H, and hence enabling a largely un-obscured measurement of the spectral width of the pure silica cladding; i.e., the intrinsic Brillouin line-width for silica. A value of 23 MHz was obtained; strikingly similar to that of bulk silica. The remaining measured values are summarized in Table 5. The core diameter, 2a, was defined to be the full-width at the half maximum of the RIP (Δn). The acoustic velocities (V) were determined from the measured Brillouin frequencies (v), modal indices (nmode), and optical wavelength (Δ) using V=Δv/2nmode. The acoustic velocity in the cladding was taken to be that of silica in the present glass system. The modal indices and cutoff wavelengths for single mode operation for the fibers were calculated from the RIPs and are also provided in Table 5. The cutoff wavelengths ware consistent with purely single mode fibers at the Brillouin test wavelength of 1534 nm. The attenuation coefficient (also in Table 5) at this wavelength was measured utilizing a cutback method, and, while reasonable for the present analysis, its value is likely dominated by impurities in the commercial precursor crystal, as no effort was undertaken to optimize its purity.
In order to characterize the bulk properties of both the magnesia and alumina components of the core after transition to the glassy state, a ternary additive model, described in detail elsewhere was applied to the data. In short, all constituent materials (including silica) were assumed to obey a law of mixtures. The parameter used to weight the effect of each oxide component was the total volume of glass occupied by that component. This was calculated using molar percentage of the constituents present in the glass, measured by EDX, and the molar volume. Utilizing this model, the bulk values of the acoustic velocity, mass density, refractive index, etc. could be determined as fit parameters for each individual oxide species. The assumption was that these respective species could be treated as ‘separable’ and did not experience effects such as with, for example, the Al—P join in AlPO4, wherein the net refractive index was actually lower than either the Al2O3 or P2O5 components taken individually.
This additive model described was used in conjunction with another boundary-value model in order to implement the fit-to-data. More specifically, since the compositional profile was not uniform, but rather graded, it was approximated by an eight-layer step-like one. Since each layer possessed a unique composition, each layer also had a unique set of material values, i.e. acoustic velocity, refractive index, etc. The values for the bulk components (magnesia and alumina) were iterated until the calculated values for the optical and acoustic modes best fit those measured for each fiber, and then the results for the two fibers were averaged. The final results are summarized in Table 6 and the uncertainty was half the difference between the best-fit parameters for Fibers H and I.
The spectra measured for the two fibers were highly acoustically-antiguiding, resulting from the fact that both magnesia and alumina increased the acoustic velocity relative to silica, resulting in very broad Brillouin spectra. Therefore it can be concluded that magnesia increases the acoustic velocity when added to silica. Additionally, while the model accommodates acoustically anti-guiding fibers by determining a complex propagation constant (which includes the waveguide attenuation term), the waveguide loss term greatly dominates the material damping associated with the addition of alumina and magnesia. Therefore due to uncertainties in the fitting, reliable measurements of the visco-elastic damping loss for magnesia could not be made.
The deduced densities of the alumina and magnesia were lower than their crystalline counterparts, as were the acoustic velocities. However, the alumina density value was somewhat larger relative to previous observations. One possible explanation is the presence of magnesia and its effect on the glass network.
While there may be some effects brought about by the presence of magnesia, the density and acoustic velocity modeling parameters deduced suggest that alumina and magnesia can be treated as independent species in the drawn fiber. Alternatively, the coordination may have imprinted from the precursor crystal and rapid processing and quenching of the resultant glass simply made the final glassy phase more closely resemble the precursor crystalline phase.
Also interesting is the fact that the deduced refractive index contributions from both the alumina and magnesia are higher than their respective crystalline counterparts.
What have been described above are examples. It is, of course, not possible to describe every conceivable combination of components or methodologies for purposes of describing the subject matter, but one of ordinary skill in the art will recognize that many further combinations and permutations of the subject matter are possible. Accordingly, the disclosure is intended to embrace all such alterations, modifications, and variations that fall within the scope of this application, including any appended claims.
This application claims filing benefit of U.S. Provisional Patent Application Ser. No. 61/808,370 having a filing date of Apr. 4, 2013, which is incorporated herein by reference in its entirety.
This invention was made with Government support under Contract No. W911NF-12-1-0602 awarded by the United States Department of Defense. The Government has certain rights in the invention.
| Number | Name | Date | Kind |
|---|---|---|---|
| 8406599 | Dragic | Mar 2013 | B1 |
| 8750655 | Dragic | Jun 2014 | B1 |
| Number | Date | Country | |
|---|---|---|---|
| 20140301706 A1 | Oct 2014 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61808370 | Apr 2013 | US |