Patent Application
20110163389
The present disclosure relates to semiconductor devices with precision resistors. The present disclosure is particularly applicable to semiconductors with low capacitance precision resistors formed in a bulk silicon substrate.
With the vertical scaling of gate stacks and implementation of pre-metalized gates and replacement gates in semiconductor devices, the ability to pattern a precision resistor in the gate pattern is becoming extremely difficult. A precision resistor can be moved into the diffusion substrate. However, building the resistor into the bulk substrate carries a large capacitive penalty.
A need therefore exists for methodology enabling the formation of a low capacitance precision resistor in the bulk substrate, and for the resulting device.
An aspect of the present disclosure is a semiconductor device comprising low capacitance resistor segments in a portion of the source/drain region of a substrate.
Another aspect of the present disclosure is a method of fabricating a resistor comprising low capacitance resistor segments in a portion of the source/drain region of a substrate.
Additional aspects and other features of the present disclosure will be set forth in the description which follows and in part will be apparent to those having ordinary skill in the art upon examination of the following or may be learned from the practice of the present disclosure. The advantages of the present disclosure may be realized and obtained as particularly pointed out in the appended claims.
According to the present disclosure, some technical effects may be achieved in part by a method of fabricating a resistor, the method comprising: forming a source/drain region on a substrate; patterning a portion of the source/drain region to form segments; etching the segments to substantially separate an upper section of each segment from a lower section of each segment; and filling the space between the segments with an insulating material.
Aspects of the present disclosure include forming the source/drain region on a silicon substrate, wherein the segments comprise silicon. Another aspect includes patterning the source/drain region to form silicon segments connected by a pad at each end. Other aspects include partially filling spaces between the silicon segments with an insulating material, e.g., an oxide, leaving a portion of each silicon segment exposed, and etching the exposed portion of the silicon segments. Further aspects include forming shallow trench isolation (STI) regions on the substrate, and partially filling the spaces between the silicon segments while forming the STI regions. Additional aspects include etching the exposed portion of the silicon segments by wet etching. Further aspects include masking the pads prior to etching, to maintain connection between the upper section and bottom section of each segment at each end. Another aspect includes converting the silicon segments to polycrystalline silicon, e.g., by implanting a dopant into the silicon segments to amorphize the silicon, and annealing the amorphized silicon. Other aspects include controlling a resistance value of the resistor by selecting a length of the silicon segments, the number of silicon segments, and/or the dopant implanted into the silicon segments.
Another aspect of the present disclosure is a semiconductor device comprising: a source/drain region on a substrate; resistor segments patterned in a portion of the source/drain region and electrically connected at each end by a pad, each resistor segment comprising a lower section, closest to the substrate, substantially separated from an upper section, further from the substrate.
Aspects include a semiconductor device including a substrate of silicon and the resistor segments being formed of silicon. Further aspects include an insulating material filling the spaces between the sections. Another aspect includes the upper and lower sections being substantially separated by wet etching the silicon resistor segments. An additional aspect includes a dopant implanted in the silicon resistor segments. Other aspects include a semiconductor device wherein the silicon is polycrystalline, and the insulating material is an oxide. Further aspects include the number of resister segments ranging from 1 to 3.
Additional aspects and technical effects of the present disclosure will become readily apparent to those skilled in the art from the following detailed description wherein embodiments of the present disclosure are described simply by way of illustration of the best mode contemplated to carry out the present disclosure. As will be realized, the present disclosure is capable of other and different embodiments, and its several details are capable of modifications in various obvious respects, all without departing from the present disclosure. Accordingly, the drawings and description are to be regarded as illustrative in nature, and not as restrictive.
The present disclosure is illustrated by way of example, and not by way of limitation, in the figures of the accompanying drawing and in which like reference numerals refer to similar elements and in which:
In the following description, for the purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of exemplary embodiments. It should be apparent, however, that exemplary embodiments may be practiced without these specific details or with an equivalent arrangement. In other instances, well-known structures and devices are shown in block diagram form in order to avoid unnecessarily obscuring exemplary embodiments.
The present disclosure addresses and solves the high capacitance problem attendant upon forming a precision resistor, e.g., in a bulk substrate. In accordance with embodiments of the present disclosure, resistor segments and end pads are formed on a substrate. The resistor segments are then substantially separated from the substrate. Consequently, the resistor segments are electrically connected to each other, but not capacitively coupled to the substrate.
Methodology in accordance with embodiments of the present disclosure includes forming resistor segments in the source/drain regions of a substrate, and substantially separating the segments from the substrate.
Still other aspects, features, and technical effects will be readily apparent to those skilled in this art from the following detailed description, wherein preferred embodiments are shown and described, simply by way of illustration of the best mode contemplated. The disclosure is capable of other and different embodiments, and its several details are capable of modifications in various obvious respects. Accordingly, the drawings and description are to be regarded as illustrative in nature, and not as restrictive.
After completion of normal source/drain lithography a resistor structure is set to be a multiple of minimum source/drain widths.
STI processing proceeds, filling the trenches with a dielectric material 201, for example an oxide, as illustrated in
Adverting to
Using the remaining dielectric material 201 as a soft mask, the silicon of the resistor fingers 101 is etched using a wet-etch technique which is silicon-plane sensitive. Etchants, such as tetramethylammonium hydroxide (TMAH), ammonium hydroxide (NH4OH), and potassium hydroxide (KOH), may be used for etching the silicon. The resulting structure is illustrated in
Adverting to
The resistor structure is then implanted in a conventional manner to amorphize the silicon layer, which is then annealed to convert the silicon into polycrystalline. The polycrystalline exhibits an improved temperature coefficient of resistance (TCR) over the initial single crystal. The conversion of the silicon may alternatively be performed prior to formation of the semiconductor gate, or later during source/drain formation.
The embodiments of the present disclosure can achieve several technical effects, including porting of the resistor into the substrate for a bulk device without paying a capacitive penalty. The present disclosure enjoys industrial applicability in any of various types of highly integrated semiconductor devices.
In the preceding description, the present disclosure is described with reference to specifically exemplary embodiments thereof. It will, however, be evident that various modifications and changes may be made thereto without departing from the broader spirit and scope of the present disclosure, as set forth in the claims. The specification and drawings are, accordingly, to be regarded as illustrative and not as restrictive. It is understood that the present disclosure is capable of using various other combinations and embodiments and is capable of any changes or modifications within the scope of the inventive concept as expressed herein.