The above and other features and advantages of the present invention will become more apparent by describing in detail exemplary embodiments thereof with reference to the attached drawings.
The present invention will now be described with reference to the accompanying drawings, in which exemplary embodiments of the invention are shown. The invention may, however, be embodied in many different forms and should not be construed as being limited to the embodiments set forth herein; rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the concept of the invention to those skilled in the art.
In the drawings, whenever the same element reappears in subsequent drawings, it is denoted by the same reference numeral.
For the sake of convenience of understanding, some key terms and phrases are first presented.
A “plastic material formulation” may comprise a homopolymer, a thermoplastic, a copolymer, a polymer blend, a thermoset, a polymer blend, any one of the above material containing performance additives, fillers, or fibers, or any other similar types of polymer material formulations.
The “deposition of a reflective metal coating over the mirror surface of the plastic part” may be accomplished by vacuum deposition, spin coating, spraying, vacuum metallization, sputtering, or any other similar process capable of depositing the reflective metal coating on the order of several microns.
“Low-cost” may be defined as a favorable cost differential as compared to glass of the same dimensional configuration for use as spherical mirrors.
A “glass counterpart” is defined to be a glass spherical mirror of the same dimensional configuration and possesses equivalent functionalities as that of the plastic spherical mirror.
As used herein, the words “may” and “may be” are to be interpreted in an open-ended, non-restrictive manner. At minimum, “may” and “may be” are to be interpreted as definitively including structure or acts recited.
In an embodiment of the present invention, a plastic injection molding process is used for fabricating the plastic part 20 of a plastic spherical mirror. In the present embodiment of the present invention, the plastic injection molding process is capable of providing a dimensional tolerance of +/−0.0001 inch for a parabolic plastic mirror that ranges from a diameter of from about five inches to about 36 inches, in certain preferred embodiments of the present invention. Although the tooling for the plastic injection molding process is relatively expensive, the cost per each plastic part 20 manufactured is however very low. A plurality of complex geometries is reproducible using the plastic injection molding process according to an embodiment of the present invention and may be limited only by the manufacturability of a metal mold.
In an embodiment of the present invention, a metal mold's final finish may be implemented by means of machining and polishing or other similar finishing methods capable of producing an adequate finish quality, such as an A1 grade or a grade that is considered as the finest finish available for a plastic part 20.
In the embodiment of the present invention, using the plastic injection molding process, plastic parts up to about 36 inches in length may be produced. The procedures used in the plastic injection molding process are well known in the art; and therefore, detail description thereof is shall not be discussed herein.
In the present embodiment, a metal mold for plastic injection molding process is able to provide plus or minus 0.030 inch tolerance for a general envelope dimension and a spherical radius tolerance of plus or minus 0.05% for the plastic part. The aforementioned tolerances are comparable to the glass spherical mirrors. The metal mold is able to hold a tolerance of about +/−0.0001 inch.
In an embodiment of the present invention, a plurality of plastic material formulations 50 may each be used for fabricating the plastic spherical mirror 10 in which a plurality of performance criteria are satisfied, such as material strength, thermal stability, water absorption, mold shrinkage, material flow into the mold, UL recognition, manufacturing considerations, surface density, lubricant content, and scratch resistance.
In an embodiment of the present invention, the plastic material formulations 50 may comprise one of the following: optical-grade polycarbonate, natural-grade polycarbonate, UV-grade polycarbonate, polyetherimide, glass-filled grade polyetherimide, PMMA (acrylic), and other comparable plastic materials having similar performance criteria. The selection of the plastic material formulation 50 may be based on the degree of precision for the mold tooling as well as experimental results from part testing.
In an embodiment of the present invention, a vacuum metallization or a vacuum deposition process may be used for coating a metal layer over the mirror surface 40 of the trimmed plastic part 25 as illustrated in
Referring to
(a) designing the plastic part 20 so that the mirror surface 40 is supported for preventing distortion or twisting by designing a plurality of wall structures onto the entire edge of a mirror edge (S100);
(b) designing and placing a plurality of injection gates precisely with the intent of ensuring the elimination of remnants or knit lines created by plastic resin flow (S102);
(c) determining a preferred physical size of the plastic part 20 for satisfying a plurality of optical performance requirements and physical design requirements (S104);
(d) designing and placing a plurality of support walls in the plastic part 20 so that the final design dimensions of the plastic part 20 matches that of a glass counterpart (S106);
(e) selecting a plastic material formulation based upon an ability to resist deformation according to a plastic part 20 quality specification (S108);
(f) polishing a mirror surface of the metal mold to an excellent optical grade finish (S110);
(g) heating and/or chilling the mold cavity to form an optimal curvature on the mirror surface of the metal mold (S12);
(h) depositing a thin layer of a reflective metal coating on the mirror surface 40 of the plastic part 20 (S114); and
(i) forming a protective overcoat onto the metalized mirror surface (S116).
Referring to
Referring to
(i) designing the plastic part 20 so that the mirror surface of the plastic part 20 is supported for preventing distortion or twisting by designing a plurality of ejector pins, for example, 28 ejector pins around the edge of the plastic part 20 serving to allow for part removal from the metal mold without distorting the surface geometry or damaging the mirror surface 40 finish (S200);
(ii) designing a plurality of plastic injection gates and placing the plastic injection gates precisely and evenly in the plastic part (S202);
(iii) determining a preferred physical size of the plastic part 20 for satisfying a plurality of optical performance requirements and physical design requirements (S204);
(iv) designing and placing a plurality of support walls strategically in the plastic part 20 (S206);
(v) selecting an optical-grade polycarbonate, polyetherimide, or PMMA (acrylic) as the plastic material formulation for use as the plastic spherical mirror (S208);
(vi) polishing the mirror surface of the metal mold to an A1 finish, wherein the metal is fabricated using a high grade steel (S210);
(vii) heating and/or chilling a mold cavity to form an optimal curvature on the mirror surface of the metal mold (S212);
(viii) depositing a thin layer of a reflective metal coating onto the mirror surface 40 of the plastic part 20 using vacuum metallization or vacuum deposition at preferably a thickness of, four to eight microns (S214);
(ix) spray coating a protective overcoat on the metalized mirror surface of the plastic part 20 (S216); and
(x) maintaining sphericity on the mirror surface 40 of the plastic spherical mirror at a tolerance of +/−0.05% (S218).
Referring to
It will be apparent to those skilled in the art that various modifications and variations can be made to the structure of the present invention without departing from the scope or spirit of the invention. In view of the foregoing, it is intended that the present invention cover modifications and variations of this invention provided they fall within the scope of the following claims and their equivalents.
This application claims the priority benefit of the U.S. provisional application Ser. No. 60/839,740, filed on Aug. 23, 2006. All disclosure of this US provisional application is incorporated herein by reference.