Low density press-hardening steel having enhanced mechanical properties

Information

  • Patent Grant
  • 11951522
  • Patent Number
    11,951,522
  • Date Filed
    Monday, March 20, 2023
    a year ago
  • Date Issued
    Tuesday, April 9, 2024
    8 months ago
Abstract
A method of forming a shaped steel object is provided. The method includes cutting a blank from an alloy composition including 0.05-0.5 wt. % carbon, 4-12 wt. % manganese, 1-8 wt. % aluminum, 0-0.4 wt. % vanadium, and a remainder balance of iron. The method also includes heating the blank until the blank is austenitized to form a heated blank, transferring the heated blank to a press, forming the heating blank into a predetermined shape to form a stamped object, and decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form a shaped steel object comprising martensite and retained austenite.
Description
INTRODUCTION

This section provides background information related to the present disclosure which is not necessarily prior art.


Press-hardening steel (PHS), also referred to as “hot-stamped steel” or “hot-formed steel” is used in various industries and applications, including general manufacturing, construction equipment, automotive or other transportation industries, home or industrial structures, and the like. It is one of the strongest steels used for automotive body structural applications, having tensile strength properties on the order of about 1,500 mega-Pascal (MPa). Such steel has desirable properties, including forming steel components having high strength-to-weight ratios. For example, when manufacturing vehicles, especially automobiles, continual improvement in fuel efficiency and performance is desirable. PHS components are often used for forming load-bearing components, like door beams, which usually require high strength materials. Thus, the finished state of these steels are designed to have high strength and enough ductility to resist external forces such as, for example, resisting intrusion into the passenger compartment without fracturing so as to provide protection to the occupants. Moreover, galvanized PHS components may provide cathodic protection.


Many PHS processes involve austenitization in a furnace of a sheet steel blank, immediately followed by pressing and quenching of the sheet in dies. Austenitization is typically conducted in the range of about 880° C. to 950° C. There are two main types of PHS processes: indirect and direct. In the direct method, the PHS component is formed and pressed simultaneously between dies, which quenches the steel. In the indirect method, the PHS component is cold formed to an intermediate partial shape before austenitization and the subsequent pressing and quenching steps. The quenching of the PHS component hardens the component by transforming the microstructure from austenite to martensite. An oxide layer often forms during the transfer from the furnace to the dies when the PHS is not pre-coated or pre-treated with an anti-oxidation material. Therefore, after quenching, the oxide must be removed from the PHS component and the dies. The oxide is typically removed, i.e., descaled, by shot blasting.


The PHS component may be coated prior to applicable pre-cold forming (if the indirect process is used) or austenitization. Coating the PHS component provides a protective layer (e.g., galvanic protection or anti-oxidation protection) to the underlying steel component. Such coatings typically include an aluminum-silicon alloy for anti-oxidation protection and/or zinc for cathodic protection. Zinc coatings, for example, act as sacrificial layers and corrode instead of the steel component, even where the steel is exposed. Zinc coatings also generate oxides on PHS components' surfaces, which are removed by shot blasting. Accordingly, alloy compositions that do not require coatings and that provide improved strength and ductility are desired.


SUMMARY

This section provides a general summary of the disclosure, and is not a comprehensive disclosure of its full scope or all of its features.


In various aspects, the current technology provides a method of forming a shaped steel object. The method includes cutting a blank from an alloy composition. The alloy composition includes carbon (C) at a concentration of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % of the alloy composition, manganese (Mn) at a concentration of greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % of the alloy composition, aluminum (Al) at a concentration of greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % of the alloy composition, vanadium (V) at a concentration of greater than 0 wt. % to less than or equal to about 0.4 wt. % of the alloy composition, and a balance of the alloy composition being iron (Fe). The method also includes heating the blank until the blank is austenitized, transferring the heated blank to a press, forming the heated blank into a predetermined shape defined by the press to generate a stamped object, and decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form a shaped steel object including martensite and retained austenite.


In one aspect, the alloy composition further includes zirconium (Zr) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. % of the alloy composition.


In one aspect, the alloy composition further includes at least one of nickel (Ni) at a concentration of greater than 0 wt. % to less than or equal to about 5 wt. % of the alloy composition, molybdenum (Mo) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. % of the alloy composition, niobium (Nb) at a concentration of greater than 0 wt. % to less than or equal to about 0.2 wt. % of the alloy composition, copper (Cu) at a concentration of greater than 0 wt. % to less than or equal to about 3 wt. % of the alloy composition, titanium (Ti) at a concentration of greater than 0 wt. % to less than or equal to about 0.1 wt. % of the alloy composition, nitrogen (N) at a concentration of greater than 0 wt. % to less than or equal to about 0.01 wt. % of the alloy composition, and boron (B) at a concentration of greater than 0 wt. % to less than or equal to about 0.005 wt. % of the alloy composition.


In one aspect, the Mn is at a concentration of greater than or equal to about 6 wt. % to less than or equal to about 10 wt. % and the Al is at a concentration of greater than or equal to about 2 wt. % to less than or equal to about 5 wt. %.


In one aspect, the C is at a concentration of greater than or equal to about 0.1 wt. % to less than or equal to about 0.45 wt. %.


In one aspect, the alloy composition is in the form of a coil.


In one aspect, the heating the blank includes heating the blank to a temperature of greater than or equal to about 900° C. to less than or equal to about 950° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 60 minutes.


In one aspect, the temperature between the Ms temperature of the alloy composition and the Mf temperature of the alloy composition is ambient temperature.


In one aspect, the decreasing the temperature includes decreasing the temperature at a rate of greater than or equal to about 5° Cs−1 to less than or equal to about 300° Cs−1.


In one aspect, the method further includes, prior to the heating the blank until the blank is austenitized, preoxidizing the alloy composition by heating the alloy composition to a temperature of greater than or equal to about 500° C. to less than or equal to about 600° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 60 minutes.


In one aspect, the method further includes, after the decreasing the temperature, tempering the shaped steel object.


In one aspect, the tempering the shaped steel object includes heating the shaped steel object to a temperature greater than or equal to about 150° C. to less than or equal to about 300° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 120 minutes, and cooling the shaped steel object to ambient temperature.


In one aspect, the shaped steel object has a higher strength and a lower weight relative to an equivalent shaped steel object formed from 22MnB5.


In various embodiments, the current technology also provides a method of forming a shaped steel object. The method includes heating a blank to a temperature of greater than or equal to about 900° C. to less than or equal to about 950° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 60 minutes to generate a heated blank. The blank is composed of an alloy composition including carbon (C) at a concentration of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % of the alloy composition, manganese (Mn) at a concentration of greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % of the alloy composition, aluminum (Al) at a concentration of greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % of the alloy composition, vanadium (V) at a concentration of greater than 0 wt. % to less than or equal to about 0.4 wt. % of the alloy composition, zirconium (Zr) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. % of the alloy composition, and a balance of the alloy composition being iron (Fe). The method also includes forming the heated blank into a predetermined shape in a press to generate a stamped object, quenching the stamped object by decreasing the temperature of the stamped object to about ambient temperature to form a shaped steel object including martensite and retained austenite, and tempering the shaped steel object by heating the shaped steel object to greater than or equal to about 150° C. to less than or equal to about 300° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 120 minutes and then decreasing the temperature of the shaped steel object to ambient temperature.


In one aspect, the shaped steel object is an automobile part selected from the group consisting of a pillar, a bumper, a roof rail, a rocker rail, a tunnel, a beam, and a reinforcement.


In various embodiments, the current technology yet further provides an alloy composition. The alloy composition includes carbon (C) at a concentration of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % of the alloy composition, manganese (Mn) at a concentration of greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % of the alloy composition, aluminum (Al) at a concentration of greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % of the alloy composition, vanadium (V) at a concentration of greater than 0 wt. % to less than or equal to about 0.4 wt. % of the alloy composition, zirconium (Zr) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. % of the alloy composition, and a balance of the alloy composition being iron (Fe).


In one aspect, the alloy composition has a higher strength and lower weight after press hardening relative to an equivalent 22MnB5 steel after press hardening.


In one aspect, after press hardening, the alloy composition includes greater than or equal to about 80 wt. % to less than or equal to about 95 wt. % martensite and greater than or equal to about 5 wt. % to less than or equal to about 20 wt. % retained austenite.


In one aspect, after press hardening, the alloy composition has a martensite:retained austenite ratio that increases when a load is applied to the alloy composition.


In one aspect, the current technology provides an automobile part including the alloy composition. The automobile part is a pillar, a bumper, a roof rail, a rocker rail, a tunnel, a beam, or a reinforcement.


Further areas of applicability will become apparent from the description provided herein. The description and specific examples in this summary are intended for purposes of illustration only and are not intended to limit the scope of the present disclosure.





DRAWINGS

The drawings described herein are for illustrative purposes only of selected embodiments and not all possible implementations, and are not intended to limit the scope of the present disclosure.



FIG. 1 is a graph showing a temperature profile used in a method of hot stamping 22MnB5 steel.



FIG. 2 is a flow chart showing aspects of a method for making a shaped steel object according to various aspects of the current technology.



FIG. 3 is a graph showing a temperature profile used in a method of making a shaped steel object according to various aspects of the current technology.



FIG. 4 shows an electron backscatter diffraction (EBSD) image of microstructures of a hot stamped alloy composition made according to various aspects of the current technology.



FIG. 5 is a graphic illustration that demonstrates transformation-induced plasticity.



FIG. 6 is a graph of stress versus strain for hot stamped 22MnB5 and a hot stamped alloy composition according to various aspects of the current technology.



FIG. 7 is a graph of stress versus strain for hot stamped 22MnB5 and a hot stamped alloy composition according to various aspects of the current technology.



FIG. 8 is a graphic illustration demonstrating lattice dilation resulting from the addition of aluminum into an iron lattice.





Corresponding reference numerals indicate corresponding parts throughout the several views of the drawings.


DETAILED DESCRIPTION

Example embodiments are provided so that this disclosure will be thorough, and will fully convey the scope to those who are skilled in the art. Numerous specific details are set forth such as examples of specific compositions, components, devices, and methods, to provide a thorough understanding of embodiments of the present disclosure. It will be apparent to those skilled in the art that specific details need not be employed, that example embodiments may be embodied in many different forms and that neither should be construed to limit the scope of the disclosure. In some example embodiments, well-known processes, well-known device structures, and well-known technologies are not described in detail.


The terminology used herein is for the purpose of describing particular example embodiments only and is not intended to be limiting. As used herein, the singular forms “a,” “an,” and “the” may be intended to include the plural forms as well, unless the context clearly indicates otherwise. The terms “comprises,” “comprising,” “including,” and “having,” are inclusive and therefore specify the presence of stated features, elements, compositions, steps, integers, operations, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof. Although the open-ended term “comprising,” is to be understood as a non-restrictive term used to describe and claim various embodiments set forth herein, in certain aspects, the term may alternatively be understood to instead be a more limiting and restrictive term, such as “consisting of” or “consisting essentially of.” Thus, for any given embodiment reciting compositions, materials, components, elements, features, integers, operations, and/or process steps, the present disclosure also specifically includes embodiments consisting of, or consisting essentially of, such recited compositions, materials, components, elements, features, integers, operations, and/or process steps. In the case of “consisting of,” the alternative embodiment excludes any additional compositions, materials, components, elements, features, integers, operations, and/or process steps, while in the case of “consisting essentially of,” any additional compositions, materials, components, elements, features, integers, operations, and/or process steps that materially affect the basic and novel characteristics are excluded from such an embodiment, but any compositions, materials, components, elements, features, integers, operations, and/or process steps that do not materially affect the basic and novel characteristics can be included in the embodiment.


Any method steps, processes, and operations described herein are not to be construed as necessarily requiring their performance in the particular order discussed or illustrated, unless specifically identified as an order of performance. It is also to be understood that additional or alternative steps may be employed, unless otherwise indicated.


When a component, element, or layer is referred to as being “on,” “engaged to,” “connected to,” or “coupled to” another element or layer, it may be directly on, engaged, connected or coupled to the other component, element, or layer, or intervening elements or layers may be present. In contrast, when an element is referred to as being “directly on,” “directly engaged to,” “directly connected to,” or “directly coupled to” another element or layer, there may be no intervening elements or layers present. Other words used to describe the relationship between elements should be interpreted in a like fashion (e.g., “between” versus “directly between,” “adjacent” versus “directly adjacent,” etc.). As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.


Although the terms first, second, third, etc. may be used herein to describe various steps, elements, components, regions, layers and/or sections, these steps, elements, components, regions, layers and/or sections should not be limited by these terms, unless otherwise indicated. These terms may be only used to distinguish one step, element, component, region, layer or section from another step, element, component, region, layer or section. Terms such as “first,” “second,” and other numerical terms when used herein do not imply a sequence or order unless clearly indicated by the context. Thus, a first step, element, component, region, layer or section discussed below could be termed a second step, element, component, region, layer or section without departing from the teachings of the example embodiments.


Spatially or temporally relative terms, such as “before,” “after,” “inner,” “outer,” “beneath,” “below,” “lower,” “above,” “upper,” and the like, may be used herein for ease of description to describe one element or feature's relationship to another element(s) or feature(s) as illustrated in the figures. Spatially or temporally relative terms may be intended to encompass different orientations of the device or system in use or operation in addition to the orientation depicted in the figures.


Throughout this disclosure, the numerical values represent approximate measures or limits to ranges to encompass minor deviations from the given values and embodiments having about the value mentioned as well as those having exactly the value mentioned. Other than in the working examples provided at the end of the detailed description, all numerical values of parameters (e.g., of quantities or conditions) in this specification, including the appended claims, are to be understood as being modified in all instances by the term “about” whether or not “about” actually appears before the numerical value. “About” indicates that the stated numerical value allows some slight imprecision (with some approach to exactness in the value; approximately or reasonably close to the value; nearly). If the imprecision provided by “about” is not otherwise understood in the art with this ordinary meaning, then “about” as used herein indicates at least variations that may arise from ordinary methods of measuring and using such parameters. For example, “about” may comprise a variation of less than or equal to 5%, optionally less than or equal to 4%, optionally less than or equal to 3%, optionally less than or equal to 2%, optionally less than or equal to 1%, optionally less than or equal to 0.5%, and in certain aspects, optionally less than or equal to 0.1%.


In addition, disclosure of ranges includes disclosure of all values and further divided ranges within the entire range, including endpoints and sub-ranges given for the ranges.


Example embodiments will now be described more fully with reference to the accompanying drawings.


22MnB5 is a press-hardening steel (PHS) that is used for manufacturing various automobile parts. 22MnB5 comprises about 0.22 wt. % carbon (C), about 1.2 wt. % manganese (Mn), about 0.05 wt. % aluminum (Al), about 0.033 wt. % titanium (Ti), about 0.003 wt. % boron (B), and about 0.006 wt. % nitrogen (N). 22MnB5 steel can be hot stamped as a bare uncoated alloy. When uncoated, hot stamped 22MnB5 undergoes oxidation, which must be removed in a subsequent cleaning or descaling process. Therefore, 22MnB5 is often coated with aluminum-silicon (Al—Si) or zinc (Zn) to minimize oxidation and to preclude a subsequent cleaning process. FIG. 1 shows a temperature profile 10 for hot stamping 22MnB5. The temperature profile 10 has a y-axis 12 representing temperature and an x-axis 14 representing time. As shown in the temperature profile 10, 22MnB5 is heated to an austenitization temperature 16 where the 22MnB5 becomes fully austenitized. The 22MnB5 is then formed into a shape at a forming temperature 18 and a decreasing temperature 20 quenches the 22MnB5, until the 22MnB5 reaches ambient temperature 22. Because 22MnB5 has a martensite start (Ms) temperature 24 of about 425° C. and a martensite final (Mf) temperature 26 of about 280° C., when the 22MnB5 reaches ambient temperature 22, the 22MnB5 has a microstructure that is about 100% martensite. The resulting hot pressed steel has an ultimate tensile strength (UTS) of less than about 1500 MPa and a density of about 7.8 g/cm3.


The current technology provides an alloy composition that, after hot pressing, has a higher UTS and a lower density relative to hot pressed 22MnB5. The alloy composition can be used to manufacture any object that is generally made by hot stamping, such as, for example, a vehicle part. Non-limiting examples of vehicles that have parts suitable to be produced by the current method include bicycles, automobiles, motorcycles, boats, tractors, buses, mobile homes, campers, gliders, airplanes, and military vehicles, such as tanks. For example, the alloy composition can be used for automobile parts, such as pillars (e.g., A-pillars and B-pillars), bumpers (e.g., front bumpers and rear bumpers), roof rails, rocker rails, tunnels, beams (e.g., side impact beams), or reinforcements (e.g., door reinforcements).


The alloy composition of the current technology comprises carbon (C) and manganese (Mn) at concentrations that are generally higher than their corresponding concentrations in 22MnB5 steel. These C and Mn concentrations provide a hot stamped steel comprising martensite and retained austenite, which lead to improved UTS and ductility. More particularly, the alloy composition comprises carbon (C) at a concentration of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. %, or greater than or equal to about 0.1 wt. % to less than or equal to about 0.45 wt. %, and manganese (Mn) at a concentration of greater than or equal to about 4 wt. % to less than or equal to about 12 wt. %, greater than or equal to about 5 wt. % to less than or equal to about 11 wt. %, or greater than or equal to about 6 wt. % to less than or equal to about 10 wt. %.


The alloy composition of the current technology also comprises aluminum (Al) at a concentration that is higher than the Al concentration in 22MnB5 steel. This increased Al concentration decreases the density of the resulting hot pressed steel and provides resistance to oxidation. In particular, the alloy composition comprises aluminum (Al) at a concentration of greater than or equal to about 1 wt. % to less than or equal to about 8 wt. %, or greater than or equal to about 2 wt. % to less than or equal to about 6 wt. %.


The alloy composition of the current technology also comprises vanadium (V), which is generally not present in 22MnB5 steel. The vanadium (V) refines the grain size of resulting hot pressed steel and inhibits or minimizes crack propagation, which improves ductility of the resulting hot pressed steel relative to 22MnB5 steel. In particular, the alloy composition comprises vanadium (V) at a concentration of greater than 0 wt. % to less than or equal to about 0.4 wt. %, or greater than or equal to about 0.01 wt. % to less than or equal to about 0.4 wt. %.


Under some conditions, the alloy composition is a solid solution comprising Al and nitrogen (N), which react and generate aluminum nitride (AlN) inclusion particles, which have a size of about 2-10 μm and decrease toughness. Relative to Al, zirconium (Zr) has a higher solubility in the solid solution. Zr reacts with N to form zirconium nitride (ZrN), which has a nanometer grain size and minimal effect on toughness. Therefore, by including Zr, ZrN may form, which minimizes the amount of AlN formed and mitigates the negative effect that AlN has on steel toughness. Accordingly, the alloy composition of the current technology also comprises zirconium (Zr) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. %, or greater than or equal to about 0.005 wt. % to less than or equal to about 0.2 wt. %.


A balance of the alloy composition is iron (Fe).


In various embodiments, the alloy composition further comprises titanium (Ti) at a concentration of greater than 0 wt. % to less than or equal to about 0.05 wt. %, or greater than or equal to about 0.001 wt. % to less than or equal to about 0.033 wt. %.


In various embodiments, the alloy composition further comprises boron (B) at a concentration of greater than 0 wt. % to less than or equal to about 0.005 wt. %, or greater than 0 wt. % to less than or equal to about 0.003 wt. %.


In various embodiments, the alloy composition further comprises nitrogen (N) at a concentration of greater than 0 wt. % to less than or equal to about 0.01 wt. %.


In various embodiments, the alloy composition further comprises molybdenum (Mo) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. %.


In various embodiments, the alloy composition further comprises niobium (Nb) at a concentration of greater than 0 wt. % to less than or equal to about 0.2 wt. %.


In various embodiments, the alloy composition further comprises nickel (Ni) at a concentration of greater than 0 wt. % to less than or equal to about 5 wt. %, greater than or equal to about 0.01 wt. % to less than or equal to about 3 wt. %, or less than or equal to about 3 wt. %.


In various embodiments, the alloy composition further comprises copper (Cu) at a concentration of greater than 0 wt. % to less than or equal to about 3 wt. %.


The alloy composition can include various combinations of C, Mn, Al, V, Zr, Ti, B, N, Mo, Nb, Ni, Cu, and Fe at their respective concentrations described above. In some embodiments, the alloy composition consists essentially of C, Mn, Al, V, Zr, Ti, B, N, Mo, Nb, Ni, Cu, and Fe. As described above, the term “consists essentially of” means the alloy composition precludes additional compositions, materials, components, elements, and/or features that materially affect the basic and novel characteristics of the alloy composition, such as strength and ductility, but any compositions, materials, components, elements, and/or features that do not materially affect the basic and novel characteristics, such as impurities, can be included.


In one embodiment, the alloy composition consists essentially of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, greater than 0 wt. % to less than or equal to about 0.1 wt. % Ti, greater than 0 wt. % to less than or equal to about 0.005 wt. % B, greater than 0 wt. % to less than or equal to about 0.01 wt. % N, greater than 0 wt. % to less than or equal to about 0.5 wt. % Mo, greater than 0 wt. % to less than or equal to about 0.2 wt. % Nb, greater than 0 wt. % to less than or equal to about 5 wt. % Ni, greater than 0 wt. % to less than or equal to about 3 wt. % Cu, and a remaining balance of Fe. In another embodiment, the alloy composition consists of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, greater than 0 wt. % to less than or equal to about 0.1 wt. % Ti, greater than 0 wt. % to less than or equal to about 0.005 wt. % B, greater than 0 wt. % to less than or equal to about 0.01 wt. % N, greater than 0 wt. % to less than or equal to about 0.5 wt. % Mo, greater than 0 wt. % to less than or equal to about 0.2 wt. % Nb, greater than 0 wt. % to less than or equal to about 5 wt. % Ni, greater than 0 wt. % to less than or equal to about 3 wt. % Cu, and a remaining balance of Fe.


In one embodiment, the alloy composition consists essentially of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, and a remainder balance of Fe. In another embodiment, the alloy composition consists of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, and a remainder balance of Fe.


In one embodiment, the alloy composition consists essentially of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, greater than 0 wt. % to less than or equal to about 0.1 wt. % Ti, greater than 0 wt. % to less than or equal to about 0.005 wt. % B, greater than 0 wt. % to less than or equal to about 0.01 wt. % N, and a remainder balance of Fe. In another embodiment, the alloy composition consists of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, greater than 0 wt. % to less than or equal to about 0.1 wt. % Ti, greater than 0 wt. % to less than or equal to about 0.005 wt. % B, greater than 0 wt. % to less than or equal to about 0.01 wt. % N, and a remainder balance of Fe.


In one embodiment, the alloy composition consists essentially of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, greater than 0 wt. % to less than or equal to about 0.5 wt. % Mo, greater than 0 wt. % to less than or equal to about 0.2 wt. % Nb, greater than 0 wt. % to less than or equal to about 5 wt. % Ni, greater than 0 wt. % to less than or equal to about 3 wt. % Cu, and a remainder balance of Fe. In another embodiment, the alloy composition consists of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, greater than 0 wt. % to less than or equal to about 0.5 wt. % Mo, greater than 0 wt. % to less than or equal to about 0.2 wt. % Nb, greater than 0 wt. % to less than or equal to about 5 wt. % Ni, greater than 0 wt. % to less than or equal to about 3 wt. % Cu, and a remainder balance of Fe.


In one embodiment, the alloy composition consists essentially of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, greater than 0 wt. % to less than or equal to about 0.5 wt. % Mo, greater than 0 wt. % to less than or equal to about 5 wt. % Ni, greater than 0 wt. % to less than or equal to about 3 wt. % Cu, and a remainder balance of Fe. In another embodiment, the alloy composition consists of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Zr, greater than 0 wt. % to less than or equal to about 0.5 wt. % Mo, greater than 0 wt. % to less than or equal to about 5 wt. % Ni, greater than 0 wt. % to less than or equal to about 3 wt. % Cu, and a remainder balance of Fe.


In one embodiment, the alloy composition consists essentially of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Mo, greater than 0 wt. % to less than or equal to about 5 wt. % Ni, greater than 0 wt. % to less than or equal to about 3 wt. % Cu, and a remainder balance of Fe. In another embodiment, the alloy composition consists of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % C, greater than or equal to about 4 wt. % to less than or equal to about 12 wt. % Mn, greater than or equal to about 1 wt. % to less than or equal to about 8 wt. % Al, greater than 0 wt. % to less than or equal to about 0.4 wt. % V, greater than 0 wt. % to less than or equal to about 0.5 wt. % Mo, greater than 0 wt. % to less than or equal to about 5 wt. % Ni, greater than 0 wt. % to less than or equal to about 3 wt. % Cu, and a remainder balance of Fe.


In one embodiment, the alloy composition comprises C, Mn, Al, and Fe, and optionally comprises at least one of V, Zr, Ti, B, N, Mo, Nb, Ni, and Cu.


In one embodiment, the alloy composition comprises C, Mn, Al, V and Fe, and optionally comprises at least one of Zr, Ti, B, N, Mo, Nb, Ni, and Cu.


In one embodiment, the alloy composition comprises C, Mn, Al, Zr and Fe, and optionally comprises at least one of V, Ti, B, N, Mo, Nb, Ni, and Cu.


In one embodiment, the alloy composition comprises C, Mn, Al, V, Zr and Fe, and optionally comprises at least one of Ti, B, N, Mo, Nb, Ni, and Cu.


The alloy composition is provided as a rolled coil or as a sheet with a microstructure comprising ferrite and cementite. The alloy composition is either bare (uncoated) and preoxidized, bare and not preoxidized, or coated with Al—Si or Zn. For example, the alloy composition can be preoxidized during manufacturing at a steel mill and provided to a user as a bare, preoxidized coil or sheet. Alternatively, the alloy composition is not preoxidized during manufacturing and is provided to a user as a bare, non-preoxidized coil or sheet. When the alloy composition reaches a user in non-preoxidized form, the user optionally preoxidizes the alloy composition prior to hot stamping. Similarly, non-preoxidized alloy composition can be optionally coated during manufacturing.


With reference to FIG. 2, the current technology provides a method 30 of forming a shaped steel object. The shaped steel object can be any object that is generally made by hot stamping, as described above. The method 30 comprises cutting a blank 32 comprising an alloy composition, which can be provided as a coil or sheet. The alloy composition is optionally coated with, for example, Al—Si or Zn. The alloy composition is the alloy composition according to the current technology described herein. The method then comprises transferring the blank 32 to a furnace or oven 34, and austenitizing the blank 32 by heating the blank 32 to a temperature above a critical transformation temperature (Ac3), at which ferrite transforms into austenite, to generate a heated blank. Heating is performed until the blank is austenitized, i.e., until the blank comprises at least about 99% austenite or about 100% austenite. In various embodiments, the heating comprises heating the blank 32 to a temperature of greater than or equal to about 880° C. to less than or equal to about 1000° C., or greater than or equal to about 900° C. to less than or equal to about 950° C. The heating is performed for a time period of greater than or equal to about 0.5 minutes to less than or equal to about 60 minutes, or greater than or equal to about 1 minute to less than or equal to about 30 minutes.


Optionally by a robotic arm 36, the method 30 comprises transferring the heated blank to a press 38. Here, the method 30 comprises forming the heated blank into a predetermined shape defined by the press to form a stamped object. In various embodiments, the forming comprises stamping the heated blank to generate a stamped object having the predetermined shape.


While in the press 38, and optionally simultaneously with the forming, the method 30 also comprises quenching the stamped object to form a shaped steel object 40. The quenching comprises decreasing the temperature of the stamped object to a temperature between a martensite start (Ms) temperature of the alloy composition and a martensite final (Mf) temperature of the alloy composition to form the shaped steel object 40. The decreasing the temperature comprises decreasing the temperature at a rate of greater than or equal to about 5° Cs−1 to less than or equal to about 300° Cs−1. In various embodiments, the Ms temperature of the alloy composition is a temperature above ambient temperature and the Mf temperature of the alloy composition is a temperature below ambient temperature. As such, in some embodiments, the quenching comprises decreasing the temperature to ambient temperature. In other embodiments, the Ms temperature is below ambient temperature (e.g., when the alloy composition comprises 0.5 wt. % C and 12 wt. % Mn) or the Mf temperature is above ambient temperature (e.g., when the alloy composition comprises 0.05 wt. % C and 4 wt. % Mn). As used herein, “ambient temperature” is standard ambient temperature 25° C. or a temperature greater than or equal to about 10° C. to less than or equal to about 50° C., greater than or equal to about 15° C. to less than or equal to about 40° C., greater than or equal to about 20° C. to less than or equal to about 30° C., greater than or equal to about 22° C. to less than or equal to about 28° C., such as a temperature of about 10° C., about 15° C., about 20° C., about 25° C., about 30° C., about 35° C., about 40° C., about 45° C., or about 50° C. As a result of quenching to a temperature between Ms and Mf, the shaped steel object 40 comprises martensite and retained austenite.


Next, the method 30 comprises performing an optional tempering treatment. As used herein, “tempering” refers to reheating and cooling a hard pressed steel in order to stabilized retained austenite in the hard pressed steel, which enhances strength and ductility. The tempering treatment comprises transferring the shaped steel object to second oven or furnace 42 and heating the shaped steel object for a time period of greater than or equal to about 1 minute to less than or equal to about 120 minutes, or greater than or equal to about 5 minutes to less than or equal to about 60 minutes. In various embodiments, the heating comprises heating the shaped steel object 40 to a temperature of greater than or equal to about 150° C. to less than or equal to about 300° C. The method 30 also includes cooling the shaped steel object back to a temperature between Ms and Mf, such as to ambient temperature in various embodiments.


In some embodiments, the alloy composition is bare, but has not been preoxidized prior to the austenitizing the blank. In such embodiments, the method 30 optionally further comprises, prior to the austenitization, preoxidizing the alloy composition by heating the alloy composition to a temperature of greater than or equal to about 500° C. to less than or equal to about 600° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 60 minutes in air or in a controlled environment comprising N2 (gas). In various embodiments, the method 30 is free of at least one of a preoxidation step, and a descaling step (e.g., shot blasting).


The method 30 is further described in FIG. 3, which shows a graph 50 having a y-axis 52 representing temperature and an x-axis 54 representing time. A line 56 on the graph 50 is a cooling profile for an alloy composition. Here, the blank is austenitized, i.e., heated to a final temperature 58 that is above a critical transformation temperature (Ac3) 60 of the alloy composition. The final temperature 58, as described above, is greater than or equal to about 88° C. to less than or equal to about 1000° C., or greater than or equal to about 900° C. to less than or equal to about 950° C.


The austenitized blank is then stamped or hot formed into a stamped object in a press at a temperature 62 between the final temperature 58 and Ac3 60. The stamped object is then quenched, i.e., cooled, at a constant quench rate of greater than or equal to about 5° Cs−1 to less than or equal to about 300° Cs−1, or great than or equal to about 60° Cs−1 to less than or equal to about 100° Cs−1 until the temperature decreases below a martensite start (Ms) temperature 64, but above a martensite final (Mf) temperature 66, such as to ambient temperature 68 (in some embodiments) to form a shaped steel object.


As discussed above, a result of quenching to a temperature between Ms and Mf, the shaped steel object comprises retained austenite, which provides beneficial properties as discussed further below. If quenching were to be performed to a temperature below Mf, the resulting shaped steel object would be about 100% martensite. Therefore, the amount of retained austenite in the shaped steel object is tunable. For example, a highest retained austenite content is achieved by quenching to a temperature near, but below Ms 64 and a lowest retained austenite content is achieved by quenching to a temperature near, but above Mf 66. As used herein, a temperature “near” Ms 64 or Mf 66 is a temperature within about 200° C. of Ms 64 or Mf 66. Therefore, the amount of retained austenite in the shaped steel object can be tuned or adjusted by quenching to a particular temperature between Ms 64 and Mf 66.


The optional tempering treatment then comprises heating the shaped steel object to a temperature a treatment temperature 70 of greater than or equal to about 150° C. to less than or equal to about 300° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 120 minutes, or greater than or equal to about 5 minutes to less than or equal to about 60 minutes, as described above. Cooling the shaped steel object back to a temperature between Ms 64 and Mf 66, such as ambient temperature 68, completes the method. In some embodiments, the shaped steel object is painted and tempering treatment is performed simultaneously with a paint baking process during, for example, vehicle manufacture.


Shaped steel objects made by the above methods, also referred to herein as “hot stamped alloy”, have a higher strength and a lower weight relative to an equivalent shaped steel object formed from 22MnB5, also referred to as “hot stamped 22MnB5”. The higher strength is a result of the microstructure of the hot stamped alloy, which comprises greater than or equal to about 80 wt. % to less than or equal to about 95 wt. % martensite and greater than or equal to about 5 wt. % to less than or equal to about 20 wt. % retained austenite. Put another way, the microstructure of the hot stamped alloy has a martensite:retained austenite ratio of from about 4:1 to about 19:1. The tempering treatment stabilizes the retained austenite.



FIG. 4 shows an electron backscatter diffraction (EBSD) image of the microstructure of a hot stamped alloy made according to the current method. The image shows that the hot stamped alloy comprises martensite 78 and retained austenite 79. The scale bar is 5 μm.


The presence of retained austenite in the hot stamped alloy increases the UTS and ductility (elongation) relative to an equivalent hot stamped alloy of 22MnB5 steel due to transformation induced plasticity (TRIP). The TRIP is an effect in which retained martensite transforms into structure phase martensite upon application of a load or stress. An example of the TRIP effect is provided in FIG. 5. FIG. 5 shows a first microstructure 80 having grains A-E and retained austenite represented by diamonds 82 located between the grains A-E. When a load or stress is applied, as shown by the arrow, the first microstructure 80 transforms into a second microstructure 84, wherein the retained austenite 82 transforms into martensite represented by circles 86.


Due to the TRIP effect, the martensite:retained austenite ratio increases when a load or stress is applied to the hot stamped alloy. Because hot stamped 22MnB5 steel comprises about 100% martensite, it does not undergo the TRIP effect upon the application of a load or stress. Accordingly, at least partially due to the TRIP effect, the hot stamped alloy of the current technology has an increased strength relative to an equivalent hot stamped alloy of 22MnB5. The hot stamped alloy of the current technology has a UTS of greater than about 1500 MPa, greater than about 1600 MPA, or greater than about 1700 MPA, such as a UTS of greater than about 1500 MPa to less than or equal to about 2200 MPa, or greater than or equal to about 1800 MPa to less than or equal to about 2000 MPa. Also, the hot stamped alloy of the current technology has a ductility (elongation) of greater than or equal to about 7% to less than or equal to about 15%, or greater than or equal to about 10% to less than or equal to about 13%. Relative to an equivalent hot stamped object comprising 22MnB5 steel, the hot stamped alloy composition of the current technology has an increase in UTS of from greater than or equal to about 10% to less than or equal to about 35%, or greater than or equal to about 10% to less than or equal to about 15%.


An example of the increased strength provided by the current alloy composition relative to 22MnB5 steel is shown in FIG. 6. In particular, FIG. 6 provides a graph 90 with a y-axis 92 corresponding to stress (MPa) and an x-axis 94 corresponding to strain (%). The hot stamped 22MnB5 is represented by squares and hot stamped alloy composition of the current technology is represented by stars. As shown by the block arrow, the strength and ductility (elongation) of the hot stamped alloy composition of the current technology are higher than the strength and ductility (elongation) of the hot stamped 22MnB5.



FIG. 7 provides another graph 100 having a y-axis 102 corresponding to stress (MPa) and an x-axis 104 corresponding to strain (%). First curves 106 from an object hot stamped from 22MnB5 and second curves 108 from an object hot stamped from the alloy composition according the current technology are shown on the graph 100. The graph 100 shows that the object hot stamped from the alloy composition according to the current technology has a higher strength and ductility relative to the object hot stamped from 22MnB5 steel.


The lower weight of the shaped steel object is in part due to the increased UTS. Because the shaped steel object has an increased strength relative to an equivalent object hot stamped from 22MnB5, thinner material can be used for a weight reduction of greater than or equal to about 15% to less than or equal to about 20%.


The lower weight is also a result of a high Al concentration. Iron (Fe) has a density of about 7.86 g/cm3 and aluminum (Al) has a density of about 2.7 g/cm3. This difference accounts for a 1.3% density reduction per 1 wt. % Al included in the alloy composition. The high Al concentration of the alloy composition also results in lattice dilation. By replacing a portion of the Fe content with Al, leading to an increased amount of Al relative to 22MnB5, the lower density, but larger Al atoms occupy more lattice space than the heavier and denser Fe atoms. Therefore, a lattice will dilate when iron in the lattice is replaced by Al. An example of lattice dilation is provided in FIG. 8, which shows a lattice 110 comprising Fe atoms 112 shown as circles with solid borders. The lattice 110 is packed as if all the atoms are Fe. An aluminum atom 114 is shown as a shaded circle with a dashed border superimposed on a central Fe atom (not shown). When the central Fe atom is replaced by the Al atom 114, the spacing of the Fe atoms 112 in the lattice 110 is forced to dilate in order to accommodate the relatively larger Al atom 114. The increased amount of space occupied by Al relative to Fe also causes a weight reduction. Through this double mechanism provided by Al, i.e., lower density and lattice dilation, a weight reduction of greater than or equal to about 4% to less than or equal to about 11% relative to an equivalent hot stamped 22MnB5 is achieved.


Between the reduction of material that can be used relative to 22MnB5 due to its higher UTS and ductility (elongation) and the double effect provided by Al, the hot stamped object has a total weight decrease of greater than or equal to about 18% to less than or equal to about 28% relative an equivalent object hot stamped from 22MnB5.


The current technology further provides a shaped steel object made by the above method. The shaped steel object has a higher strength, a higher ductility, and a lower weight relative to a second shaped object that was hot stamped from 22MnB5. The shaped steel object may be part of an automobile or other vehicle as exemplified above.


The foregoing description of the embodiments has been provided for purposes of illustration and description. It is not intended to be exhaustive or to limit the disclosure. Individual elements or features of a particular embodiment are generally not limited to that particular embodiment, but, where applicable, are interchangeable and can be used in a selected embodiment, even if not specifically shown or described. The same may also be varied in many ways. Such variations are not to be regarded as a departure from the disclosure, and all such modifications are intended to be included within the scope of the disclosure.

Claims
  • 1. An alloy composition comprising: carbon (C) at a concentration of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % of the alloy composition,manganese (Mn) at a concentration of greater than or equal to about 4 wt. % to less than or equal to 5.4 wt. % of the alloy composition,aluminum (Al) at a concentration of greater than or equal to about 2 wt. % to less than or equal to about 8 wt. % of the alloy composition,vanadium (V) at a concentration of greater than 0 wt. % to less than or equal to about 0.4 wt. % of the alloy composition,nitrogen (N) at a concentration of greater than 0 wt. % to less than 0.001 wt. % of the alloy composition, anda balance of the alloy composition being iron (Fe).
  • 2. The alloy composition according to claim 1, wherein the alloy composition comprises: zirconium (Zr) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. % of the alloy composition.
  • 3. The alloy composition according to claim 1, wherein the alloy composition comprises ZrN.
  • 4. The alloy composition according to claim 2, wherein the alloy composition comprises at least one of: nickel (Ni) at a concentration of greater than 0 wt. % to less than or equal to about 5 wt. % of the alloy composition,molybdenum (Mo) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. % of the alloy composition,niobium (Nb) at a concentration of greater than 0 wt. % to less than or equal to about 0.2 wt. % of the alloy composition,copper (Cu) at a concentration of greater than 0 wt. % to less than or equal to about 3 wt. % of the alloy composition,titanium (Ti) at a concentration of greater than 0 wt. % to less than or equal to about 0.1 wt. % of the alloy composition,andboron (B) at a concentration of greater than 0 wt. % to less than or equal to about 0.005 wt. % of the alloy composition.
  • 5. The alloy composition according to claim 1, wherein the Al is at a concentration of greater than or equal to 2 wt. % to less than or equal to about 5 wt. %.
  • 6. The alloy composition according to claim 1, wherein the C is at a concentration of greater than or equal to about 0.1 wt. % to less than or equal to about 0.45 wt. %.
  • 7. The alloy composition according to claim 1, wherein the alloy composition has a higher strength and lower weight after press hardening relative to an equivalent 22MnB5 steel after press hardening.
  • 8. The alloy composition according to claim 1, wherein after press hardening, the alloy composition comprises greater than or equal to about 80 wt. % to less than or equal to about 95 wt. % martensite and greater than or equal to about 5 wt. % to less than or equal to about 20 wt. % retained austenite.
  • 9. The alloy composition according to claim 1, wherein after press hardening, the alloy composition has a martensite:retained austenite ratio that increases when a load is applied to the alloy composition.
  • 10. The alloy composition according to claim 1, wherein the C is at a concentration of about 0.5 wt. % of the alloy composition.
  • 11. The alloy composition according to claim 10, wherein the alloy composition has a martensite start (Ms) temperature less than ambient temperature.
  • 12. The alloy composition according to claim 1, wherein the C is at a concentration of about 0.05 wt. % of the alloy composition and the Mn is at a concentration of about 4 wt. %.
  • 13. The alloy composition according to claim 12, wherein the alloy composition has a martensite final (Mf) temperature greater than ambient temperature.
  • 14. The alloy composition according to claim 1, wherein the alloy composition has a critical transformation temperature (Ac3) of greater than or equal to about 880° C. to less than or equal to about 1000° C.
  • 15. An automobile part comprising the alloy composition according to claim 1, wherein the automobile part is a pillar, a bumper, a roof rail, a rocker rail, a tunnel, a beam, or a reinforcement.
  • 16. A method of forming a shaped steel object, the method comprising: heating a blank to a temperature of greater than or equal to about 900° C. to less than or equal to about 950° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 60 minutes to generate a heated blank, the blank being composed of an alloy composition comprising:carbon (C) at a concentration of greater than or equal to about 0.05 wt. % to less than or equal to about 0.5 wt. % of the alloy composition,manganese (Mn) at a concentration of greater than or equal to about 4 wt. % to less than or equal to 5.4 wt. % of the alloy composition,aluminum (Al) at a concentration of greater than or equal to 2 wt. % to less than or equal to about 8 wt. % of the alloy composition,vanadium (V) at a concentration of greater than 0 wt. % to less than or equal to about 0.4 wt. % of the alloy composition,zirconium (Zr) at a concentration of greater than 0 wt. % to less than or equal to about 0.5 wt. % of the alloy composition,nitrogen (N) at a concentration of greater than 0 wt. % to less than 0.001 wt. % of the alloy composition, anda balance of the alloy composition being iron (Fe);forming the heated blank into a predetermined shape to generate a stamped object;quenching the stamped object by decreasing the temperature of the stamped object to about ambient temperature to form a shaped steel object comprising martensite and retained austenite; andtempering the shaped steel object by heating the shaped steel object to greater than or equal to about 150° C. to less than or equal to about 300° C. for a time period of greater than or equal to about 1 minute to less than or equal to about 120 minutes and then decreasing the temperature of the shaped steel object to ambient temperature.
  • 17. The method according to claim 16, further comprising: transferring the heated blank to a press,wherein the heated blank is formed into the predetermined shape defined by the press to generate the stamped object.
  • 18. The method according to claim 16, wherein the shaped steel object is an automobile part selected from the group consisting of a pillar, a bumper, a roof rail, a rocker rail, a tunnel, a beam, and a reinforcement.
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of Ser. No. 17/251,655 filed on Dec. 11, 2020, which is a U.S. National Phase Application under 35 U.S.C. 371 of International Application No. PCT/CN2018/091751 filed on Jun. 19, 2018. The entire disclosures of the above applications are incorporated herein by reference.

US Referenced Citations (128)
Number Name Date Kind
1828325 Kurz Oct 1931 A
2178281 Judge Oct 1939 A
3111436 McGavin Nov 1963 A
3330705 Madrzyk et al. Jul 1967 A
3340102 Kulin et al. Sep 1967 A
3516874 Maker et al. Jun 1970 A
3907614 Bramfitt et al. Sep 1975 A
4086104 Kinoshita et al. Apr 1978 A
4146411 Dewsnap et al. Mar 1979 A
4327156 Dillon et al. Apr 1982 A
4486248 Ackert et al. Dec 1984 A
4533401 Yutori et al. Aug 1985 A
4744836 Pfaffmann May 1988 A
5205145 Ishino et al. Apr 1993 A
5358578 Tischhauser Oct 1994 A
5554233 Heitmann et al. Sep 1996 A
5989647 Remy et al. Nov 1999 A
6270594 Bodnar et al. Aug 2001 B1
6296805 Laurent et al. Oct 2001 B1
6330740 Krempels Dec 2001 B1
6364972 Bauer et al. Apr 2002 B1
6564604 Kefferstein et al. May 2003 B2
7166372 Bose et al. Jan 2007 B2
7393421 Yang Jul 2008 B2
7677070 Kobayashi Mar 2010 B2
7703312 Walter Apr 2010 B2
7727337 Sachdev et al. Jun 2010 B2
7941907 Yang et al. May 2011 B2
8007923 Sakakibara et al. Aug 2011 B2
8141230 Brodt et al. Mar 2012 B2
8252125 Giefers et al. Aug 2012 B2
8440323 Spehner et al. May 2013 B2
8614008 Canourgues et al. Dec 2013 B2
8671729 Verma et al. Mar 2014 B2
8733142 Spehner et al. May 2014 B2
8778261 Nakamura et al. Jul 2014 B2
8888934 Bian Nov 2014 B2
8926770 Kobayashi et al. Jan 2015 B2
8932416 Nakanishi et al. Jan 2015 B2
8992697 Matsuda et al. Mar 2015 B2
9359663 Mizuta et al. Jun 2016 B2
9475113 Naitou et al. Oct 2016 B2
9512499 Tomokiyo et al. Dec 2016 B2
9534268 Ratte Jan 2017 B2
9593392 John et al. Mar 2017 B2
9598745 Hayashi et al. Mar 2017 B2
9605329 Nonaka et al. Mar 2017 B2
9611518 Naitou et al. Apr 2017 B2
9617624 Tanahashi et al. Apr 2017 B2
9644247 Matsuda et al. May 2017 B2
9694415 Shan et al. Jul 2017 B2
9725782 Nonaka et al. Aug 2017 B2
9835194 Chiba et al. Dec 2017 B2
9840751 Hayashi et al. Dec 2017 B2
9850554 Naitou et al. Dec 2017 B2
9896736 Tomokiyo et al. Feb 2018 B2
9909194 Puerta Velasquez et al. Mar 2018 B2
9920407 Nonaka et al. Mar 2018 B2
9945013 Nonaka et al. Apr 2018 B2
10029294 Yamano et al. Jul 2018 B2
10030280 Hayashi et al. Jul 2018 B2
10072324 Nonaka et al. Sep 2018 B2
10260121 Lu et al. Apr 2019 B2
10385415 Wang Aug 2019 B2
10472691 Köyer et al. Nov 2019 B2
10619223 Wang Apr 2020 B2
10822681 Schottler et al. Nov 2020 B2
20090155615 Chen et al. Jun 2009 A1
20090238715 Cho et al. Sep 2009 A1
20100026048 Vlot et al. Feb 2010 A1
20100028190 Wang Feb 2010 A1
20100269957 Akerstrom et al. Oct 2010 A1
20110139308 Peruzzi et al. Jun 2011 A1
20120211131 Altschuler et al. Aug 2012 A1
20120267012 Sohn et al. Oct 2012 A1
20130048161 Matsuda et al. Feb 2013 A1
20130180969 Cheng et al. Jul 2013 A1
20130186527 Bradley Jul 2013 A1
20130199679 Toji et al. Aug 2013 A1
20140020795 Schwinghammer et al. Jan 2014 A1
20140057121 Altschuler et al. Feb 2014 A1
20140065007 Naitou et al. Mar 2014 A1
20140096876 Matsuda et al. Apr 2014 A1
20140212687 Vlot et al. Jul 2014 A1
20140261918 Jin et al. Sep 2014 A1
20140261920 Shan et al. Sep 2014 A1
20140322559 Becker et al. Oct 2014 A1
20150020992 Schottler et al. Jan 2015 A1
20150024237 Tanahashi et al. Jan 2015 A1
20150082636 Gruneklee et al. Mar 2015 A1
20150090377 Murakami et al. Apr 2015 A1
20150114199 Shepard et al. Apr 2015 A1
20150203946 Hammer et al. Jul 2015 A1
20150225830 Nonaka et al. Aug 2015 A1
20160010168 Angles et al. Jan 2016 A1
20160017452 Puerta Velasquez et al. Jan 2016 A1
20160145707 Feuser et al. May 2016 A1
20160145731 Sachdev et al. May 2016 A1
20160147573 Shayesteh et al. May 2016 A1
20160215376 Luther et al. Jul 2016 A1
20160244855 Steinebach et al. Aug 2016 A1
20160319389 Hayashi et al. Nov 2016 A1
20170029913 Bae et al. Feb 2017 A1
20170051372 Tomokiyo et al. Feb 2017 A1
20170149036 Braun May 2017 A1
20170314088 Wang Nov 2017 A1
20170314089 Wang Nov 2017 A1
20170321294 Arlazarov et al. Nov 2017 A1
20170342523 Wang et al. Nov 2017 A1
20180030567 Yi et al. Feb 2018 A1
20180216205 Wang et al. Aug 2018 A1
20180223385 Lu et al. Aug 2018 A1
20180223399 Palzer Aug 2018 A1
20180237877 Wang et al. Aug 2018 A1
20180237892 Schottler et al. Aug 2018 A1
20180251875 Pavlina Sep 2018 A1
20180312954 Yasui et al. Nov 2018 A1
20190127829 Santacreu et al. May 2019 A1
20200063232 Lu et al. Feb 2020 A1
20200157665 Lu et al. May 2020 A1
20200190611 Lu et al. Jun 2020 A1
20200325552 Mraczek et al. Oct 2020 A1
20210002746 Lu et al. Jan 2021 A1
20210087661 Lu et al. Mar 2021 A1
20210189531 Lu et al. Jun 2021 A1
20210198760 Lu et al. Jul 2021 A1
20210222265 Lu et al. Jul 2021 A1
20210276065 Pang et al. Sep 2021 A1
Foreign Referenced Citations (96)
Number Date Country
2378934 Sep 2003 CA
101270453 Sep 2008 CN
101713046 May 2010 CN
102031456 Apr 2011 CN
102284523 Dec 2011 CN
102644028 Aug 2012 CN
102719783 Oct 2012 CN
102758133 Oct 2012 CN
102803519 Nov 2012 CN
102828109 Dec 2012 CN
102906291 Jan 2013 CN
102912219 Feb 2013 CN
103045950 Apr 2013 CN
103108964 May 2013 CN
103547687 Jan 2014 CN
103556048 Feb 2014 CN
103620075 Mar 2014 CN
103842546 Jun 2014 CN
104160050 Nov 2014 CN
104160051 Nov 2014 CN
104195455 Dec 2014 CN
104379272 Feb 2015 CN
104846274 Aug 2015 CN
105026597 Nov 2015 CN
105483531 Apr 2016 CN
105648317 Jun 2016 CN
105658821 Jun 2016 CN
105671435 Jun 2016 CN
105734413 Jul 2016 CN
105886750 Aug 2016 CN
106086683 Nov 2016 CN
106399834 Feb 2017 CN
106521338 Mar 2017 CN
106906421 Jun 2017 CN
106929755 Jul 2017 CN
107002155 Aug 2017 CN
107127238 Sep 2017 CN
107338345 Nov 2017 CN
107338349 Nov 2017 CN
107354385 Nov 2017 CN
107815612 Mar 2018 CN
108359781 Aug 2018 CN
110050084 Jul 2019 CN
111542635 Aug 2020 CN
112176245 Jan 2021 CN
112513310 Mar 2021 CN
112534078 Mar 2021 CN
102009060388 Jun 2011 DE
102012104734 Dec 2013 DE
102015119417 Jun 2016 DE
102017108835 Nov 2017 DE
102017108837 Nov 2017 DE
102018101735 Aug 2018 DE
112016007444 Aug 2019 DE
1878811 Jan 2008 EP
1930450 Jul 2011 EP
2524970 Nov 2012 EP
3013988 May 2016 EP
3020842 May 2016 EP
2866147 Aug 2016 EP
2719788 Nov 2016 EP
3473735 Apr 2019 EP
H0384378 Apr 1991 JP
H09263886 Oct 1997 JP
2000178640 Jun 2000 JP
2003147486 May 2003 JP
2003201549 Jul 2003 JP
2005163123 Jun 2005 JP
2006316309 Nov 2006 JP
2007321168 Dec 2007 JP
2008207279 Sep 2008 JP
2008261023 Oct 2008 JP
2010174302 Aug 2010 JP
2011016149 Jan 2011 JP
2011184768 Sep 2011 JP
5015356 Aug 2012 JP
2013204089 Oct 2013 JP
2016125101 Jul 2016 JP
20110034452 Apr 2011 KR
20160057541 May 2016 KR
711126 Feb 1980 SU
WO-2008102012 Aug 2008 WO
WO-2012120020 Sep 2012 WO
WO-2014024831 Feb 2014 WO
WO-2014037627 Mar 2014 WO
WO-2014128656 Aug 2014 WO
WO-2015102051 Jul 2015 WO
WO-2016079565 May 2016 WO
WO-2016095664 Jun 2016 WO
WO-2016106621 Jul 2016 WO
WO-2017021464 Feb 2017 WO
WO-2018107446 Jun 2018 WO
WO-2019085855 May 2019 WO
WO-2019127240 Jul 2019 WO
WO-2019222950 Nov 2019 WO
WO-2019241902 Dec 2019 WO
Non-Patent Literature Citations (59)
Entry
Altan, Taylan, “Hot-stamping boron-alloyed steels for automotive parts—Part I—Press Technology Tech Cell”; http://www.thefabricator.com/article/presstechnology/hot-stamping-boron-alloyed-steels-for-automotive-parts; Feb. 13, 2007; 3 pages.
Altan, Taylan, “Hot-stamping boron-alloyed steels for automotive parts—Part II—Press Technology Tech Cell”; http://www.thefabricator.com/article/presstechnology/hot-stamping-boron-alloyed-steels-for-automotive-parts-part-ii; Jan. 18, 2007; 2 pages.
Altan, Taylan, “Hot-stamping boron-alloyed steels for automotive parts—Part III—Press Technology Tech Cell”; http://www.thefabricator.com/article/presstechnology/hot-stamping-boron-alloyed-steels-for-automotive-parts-part-iii; Feb. 13, 2007; 2 pages.
Anonymous, “Process to improve oxidation resistance of press hardening steels,” Research Disclosure, Database No. 641010 (Published online: Jul. 28, 2017), 2 pages.
Anonymous, “Steel Definitions, Today's AHSS for Automotive” WorldAutoSteel, [retrieved on Nov. 27, 2019]. Retrieved from the Internet: <URL: https://www.worldautosteel.org/steel-basics/automotive-steel-definitions/ <https://protect-us.mimecast.com/s/qVeXCADQNWCNqxzXcGLKQI>, 5 pages.
Anonymous, “Transformation-Induced Plasticity (TRIP) Steel” WorldAutoSteel, [retrieved on Nov. 27, 2019]. Retrieved from the Internet: <URL:https://www.worldautosteel.org/steel-basics/steel-types/transformation-induced-plasticity-trip-steel/>, 5 pages.
Anonymous, “TRIP steel” Wikipedia, [retrieved on Nov. 27, 2019], retrieved from the Internet: <URL: https://en.wikipedia.org/wiki/TRIP_steel>, 3 pages.
Davis, Joseph R. ed., “Dip, Barrier, and Chemical Conversion Coating,” Metals Handbook Desk Edition, ASM International, 1998, p. 1154-1165 (Year: 1998).
Diekman, F. “Cold and Cryogenic Treatment of Steel,” ASM Handbook, vol. 4A, Steel Heat Treating Fundamentals and Processes, pp. 382-386.
Dossett, John L. et al., “Practical Heat Treating,” Second Edition (ASM International, 2006), pp. 7, 269. ISBN 1615031103 (Year: 2006).
First Office Action for Chinese Patent Application No. 201511036174.4 dated Feb. 28, 2017 with English language machine translation, 20 pages.
First Office Action for Chinese Patent Application No. 201511036174.4 dated Feb. 28, 2017 with English language machine translation; 19 pages.
First Office Action for Chinese Patent Application No. 201680091625.0 dated Jul. 8, 2020 with English language machine translation, 11 pages.
First Office Action for Chinese Patent Application No. 201710222523.4 dated Apr. 27, 2018 and correspondence from China Patent Agent (H.K.) Ltd summarizing Office Action; 9 pages.
First Office Action for Chinese Patent Application No. 201710224443.2 dated May 3, 2018 and correspondence from China Patent Agent (H.K.) Ltd summarizing Office Action; 9 pages.
First Office Action for Chinese Patent Application No. 201810061046.2 dated Mar. 1, 2019 with English language machine translation; 18 pages.
First Office Action for German Patent Application No. 102015119417.1 dated Feb. 16, 2017; 5 pages.
First Office Action for German Patent Application No. 102017108835.0 dated Jul. 24, 2018 and correspondence dated Aug. 8, 2018 from Manitz Finsterwald Patentanwälte PartmbB summarizing contents; 6 pages.
First Office Action for German Patent Application No. 102017108837.7 dated Jul. 25, 2018 and correspondence from dated Aug. 8, 2018 Manitz Finsterwald Patentanwälte PartmbB summarizing contents; 6 pages.
First Office Action for German Patent Application No. 102018101735.9 dated May 3, 2019 with correspondence from Manitz Finsterwald Patentanwälte PartmbB summarizing contents, 6 pages.
Ghanbari, Zahra N. et al., “Zinc Coated Sheet Steel for Press Hardening (Master's Thesis)” Submitted to the Faculty and the Board of Trustees of the Colorado School of Mines, Fall 2014.
Grajcar, Adam et al.; “Phase Equilibrium and Austenite Decomposition in Advanced High-Strength Medium-Mn Bainitic Steels”; www.mdpi.com/journal/metals; Oct. 20, 2016; 14 pages.
International Search Report and Written Opinion for International Application No. PCT/CN2014/095753 dated Oct. 8, 2015; 8 pages (ISA/CN).
International Search Report and Written Opinion for International Application No. PCT/CN2016/110241 dated Sep. 25, 2017, 12 pages (ISA/CN).
International Search Report and Written Opinion for International Application No. PCT/CN2017/119484 dated Sep. 12, 2018, 9 pages (ISA/CN).
International Search Report and Written Opinion for International Application No. PCT/CN2018/088122 dated Feb. 26, 2019, 8 pages (ISA/CN).
International Search Report and Written Opinion for International Application No. PCT/CN2018/091751 dated Mar. 15, 2019, 9 pages (ISA/CN).
Jianfeng Wang et al., U.S. Appl. No. 15/435,418, filed Feb. 17, 2017 entitled “Mitigating Liquid Metal Embrittlement in Zinc-Coated Press Hardened Steels”, 40 pages.
Karbasian, H. et al.; “A review on hot stamping”; Journal of Materials Processing Technology 210; Jul. 19, 2010; pp. 2103-2118.
Kurz, Thomas et al.; “Zinc Coated Press-Hardening Steel: Challenges and Solutions”; Voestalpine (Published Apr. 14, 2015), 12 pages.
Leonard, R. “Continuous Hot Dip Coatings,” Corrosion: Fundamentals, Testing, and Protection, vol. 13A, ASM Handbook, ASM International, 2003, p. 786-796 (Year: 2003).
Liu, Hong-Sheng et al., “Hot Formation Quality of High Strength Steel BR1500HS for Hot Stamping without Cooling System,” Trans. Nonferrous Met. Soc. China (2012), vol. 22, pp. s542-s547.
Lu, Qi et al., International Application No. PCT/CN2017/119484 filed Dec. 28, 2017 entitled “Steel for Hot Stamping With Enhanced Oxidation Resistance,” 39 pages.
Lu, Qi et al., International Application No. PCT/CN2018/088122 filed May 24, 2018 entitled “A Method for Improving Both Strength and Ductility of a Press-Hardening Steel,” 32 pages.
Lu, Qi et al., U.S. Appl. No. 16/460,369, filed Jul. 2, 2019 entitled, “Press Hardened Steel With Surface Layered Homogenous Oxide After Hot Forming,” 50 pages.
Merklein, Marion et al., “A review on tailored blanks—Production, applications and evaluation,” Journal of Materials Processing Technology (2014) 214, pp. 151-164; DOI: 10.1016/j.matprotec.2013.08.015 (Published online Sep. 6, 2013).
Mori, K. et al., “Warm and Hot Stamping of Ultra High Tensile Strength Steel Sheets Using Resistance Heating,” CIRP Annals Manufacturing Technology (2005), vol. 54 (1), pp. 209-212.
Naderi, Malek et al., “Semi-hot Stamping as an Improved Process of Hot Stamping,” J. Mater. Sci. Technol. (2011), vol. 27 (4) pp. 369-376.
Pang, Jiachen et al., International Application No. PCT/CN2018/091751 filed Jun. 19, 2018 entitled “Low Density Press-Hardening Steel Having Enhanced Mechanical Properties,” 44 pages.
Sachdev, Anil K. et al.; U.S. Appl. No. 14/627,579, filed Feb. 20, 2015 entitled “Controlling Liquid Metal Embrittlement in Galvanized Press-Hardened Components”; 49 pages.
Second Office Action for Chinese Patent Application No. 201511036174.4 dated Nov. 16, 2017 with English language machine translation; 15 pages.
Third Office Action for Chinese Patent Application No. 201511036174.4 dated Jul. 2, 2018 with English language machine translation; 26 pages.
Wang, Jianfeng et al.; U.S. Appl. No. 15/417,921, filed Jan. 27, 2017 entitled “Two-Step Hot Forming of Steels”; 45 pages.
Wang, Jianfeng; U.S. Appl. No. 15/141,248, filed Apr. 28, 2016 entitled “Zinc-Coated Hot Formed Steel Component With Tailored Property”; 49 pages.
Wang, Jianfeng; U.S. Appl. No. 15/141,272, filed Apr. 28, 2016 entitled “Zinc-Coated Hot Formed High Strength Steel Part With Through-Thickness Gradient Microstructure”; 45 pages.
Yi, H.L., “Dual-Phase Hot-Press Forming Alloy,” Materials Science and Engineering A, 527 (2010). pp. 4870-4874.
Lu, Qi et al., U.S. Appl. No. 16/958,362, filed Jun. 26, 2020 entitled, “Steel for Hot Stamping With Enhanced Oxidation Resistance,” 41 pages.
Cao et al.; Oxidation Kinetics and Spallation Model of Oxide Scale during Cooling Process of Low Carbon Microalloyed Steel; Sep. 24, 2016; de Gruyter; High Temperature Materials and Processes vol. 36 Issue 9, p. 1-10 (Year: 2016).
Yi et al., Dual-phase hot press forming alloy, 2010, Elsevier, Materials Science and Engineering A, p. 4870-4874 (Year: 2010).
Lu, Qi et al., U.S. Appl. No. 17/153,848, filed Jan. 20, 2021 entitled “Press Hardening Steel With High Oxidation Resistance,” 37 pages.
First Office Action for Chinese Patent Application No. 202010626153.2 dated Jun. 16, 2021 with correspondence dated Jun. 23, 2021 from China Patent Agent (H.K.) Ltd. summarizing contents, 10 pages.
Khanna, A.S., “Introduction to High Temperature Oxidation and Corrosion.” ASM International, Materials Park, OH, p. 123 (2002).
First Office Action for Chinese Patent Application No. 201780098042.5 dated May 26, 2021 with English language machine translation, 20 pages.
Wang, Min et al., “Inverse evaluation of equivalent contact heat transfer coefficient in hot stamping of boron steel.” The International Journal of Advanced Manufacturing Technology, vol. 87, pp. 2925-2932 (2016).
First Office Action for Chinese Patent Application No. 201880095869.5 dated Sep. 15, 2021 with correspondence dated Sep. 17, 2021 from China Patent Agent (H.K.) Ltd. summarizing contents, 9 pages.
Second Office Action for Chinese Patent Application No. 201780098042.5 dated Nov. 17, 2021, with correspondence dated Nov. 22, 2021, from China Patent Agent (H.K.) Ltd summarizing contents; 9 pages.
First Office Action for Chinese Patent Application No. 201880096658.3 dated Nov. 18, 2021, with correspondence dated Nov. 22, 2021, from China Patent Agent (H.K.) Ltd summarizing contents; 8 pages.
Second Office Action for Chinese Patent Application No. 2020106261153.2 dated Mar. 9, 2022, with correspondence dated Mar. 14, 2022, from China Patent Agent (H.K.) Ltd summarizing contents; 12 pages.
Third Office Action for Chinese Patent Application No. 202010626153.2 dated Jun. 24, 2022, and correspondence from China Patent Agent (H.K.) Ltd summarizing Office Action; 22 pages.
Related Publications (1)
Number Date Country
20230226585 A1 Jul 2023 US
Divisions (1)
Number Date Country
Parent 17251655 US
Child 18123592 US