Patent Grant
9677611
The present invention relates to a low-friction lubrication assembly comprising at least first and second members, the surfaces or coatings thereof are in sliding contact with each other such that under presence of at least one friction reducing agent (oxygen containing compound) a specific and unique tribofilm develops comprising hydrogen and/or hydroxyl groups.
In the present state of the art, low friction under lubricated tests is generally attainable through the formation of CH3-terminated tribofilms or in the presence of solid lamellar compounds such as MoS2 or boric acid, for example. However, almost typical friction coefficients obtained are not lower than 0.04 and lower than 0.1, and therefore values lower than 0.04 have hardly been reported so far.
Global environmental problems such as global warming and ozone layer destruction are coming to the fore. As it has been said that the global warming is significantly affected by CO2 emission, the reduction of CO2 emission, notably the setting of CO2 emission standards, has become a big concern to each country. One of the challenges to reduce CO2 emission is to lower an energy loss due to friction loss of machines, facilities and the like, particularly to improve vehicle fuel efficiency or fuel economy that depends on the performance of engine sliding members and a lubricating oil applied thereto. There are the following approaches to improve the vehicle fuel efficiency: (1) lowering the viscosity of the lubricating oil, thereby reducing viscous resistance in hydrodynamic lubrication regions and agitation resistance in the engine; and (2) adding a suitable friction modifier and other additives into the lubricating oil so as to reduce friction losses under the conditions of mixed lubrication and boundary lubrication.
A patent literature 1 discloses a low-friction sliding member with a base material having a surface and a hard carbon thin film formed on at least a part of the surface of the base material, wherein a tribofilm having at least one functional group selected from the group consisting of an ether linkage, an oxido and a hydroxyl group is formed on the hard carbon thin film when the hard carbon thin film is in slidable contact with an opposite member in the presence of an organic oxygen-containing compound.
The present invention aims to suggest a low-friction lubrication assembly showing improved sliding characteristics over low friction assemblies shown in the art.
The problem is solved with a low friction assembly comprising:
a first member relatively slidable against a second member, the first member having chemical affinity with an OH-group on its sliding surface; and
one or more oxygen containing compounds located on the sliding surface of the first member and being able to produce a tribofilm to be located on the sliding surface of the first member having the chemical affinity, through hydrogen bond interactions with the OH-group.
Hereinafter, a low friction assembly of the present invention will be discussed in detail.
As discussed above, the low friction assembly of the present invention comprises:
a first member relatively slidable against a second member, the first member having chemical affinity with an OH-group on its sliding surface; and
one or more oxygen containing compounds located on the sliding surface of the first member and being able to produce a tribofilm to be located on the sliding surface of the first member having the chemical affinity, through hydrogen bond interactions with the OH-group.
Essential is the creation of a hydrogen bond interaction between a H or OH-terminated surface of the first member and specific polar molecules present in an oxygen containing compound (lubricant) which can be gaseous or liquid. In particular, said hydrogen bonding interaction, on the one hand, and the oxygen containing compound (lubricant) determined H-terminated surfaces of the first and/or second member, on the other hand, serve to establish a unique low-friction lubrication assembly or system which allows to reduce friction values to the range of friction coefficient below 0.04 and in specific cases below 0.01.
On other words, in a two-way mechanism the tribochemical reaction of the surface atoms such as C, Al, Si, etc of the first and/or second member with the hydroxyl groups present in the molecules of the oxygen containing compound (lubricant) occurs and thereafter the oxygen containing compound (lubricant) molecules adsorb on that OH-terminated surface by hydrogen bonding. Thus the newly created friction interface (including the oxygen containing compound (lubricant)) is either an H-terminated surface or a mixed OH- and/or H-terminated surface wherein any amount of more than 50% OH may be beneficial over a purely H-terminated surface.
In case of biological material, for example as a second member, proteins comprising for example OH- and SH-groups, may organize on the OH- or H-terminated surface of the first member.
In a preferred embodiment, the second member further comprises a hydroxyl group on the sliding surface, preferably an OH-terminated sliding surface, and the tribofilm is also attached to the sliding surface of the second member through hydrogen bonding in response to a sliding movement.
Further, the first member comprises preferably at least one selected from the group consisting of an amorphous material and a crystallized material.
In a further preferred embodiment the first member comprises at least one selected from the group consisting of Si, SiO2, Al2O3, Si3N4, MgO or any single metal or mixed metal combination of oxides, nitrides and carbides (for example silicon carboxide, oxynitride and carbonitride) and more generally a material formed of elements having a chemical affinity and propension to form hydroxides compounds (for example Metal (OH)x). Which ever its chemical composition and crystal structure, the first sliding member can also be coated with a diamond and diamond-like carbon.
The diamond-like carbon contains preferably hydrogen in an amount of not more that 10 atomic %, more preferably the diamond-like carbon is formed of diamond-like carbon of a-C type or ta-C type containing substantially no hydrogen.
The second member comprises preferably at least one selected from the group consisting of an amorphous material and a crystallized material.
In a further preferred embodiment, the second member is formed of the same materials as those (as listed above) of the first member, or comprises at least one selected of the group consisting of C, Fe, Al, Mg, Cu, Fe alloy, Al alloy, Mg alloy and Cu alloy.
Preferably, the oxygen containing compound (friction modifier or lubricant) has at least one hydroxyl group in its chemical formulae.
Further, the oxygen containing compound comprises preferably at least one of the group consisting of an alcohol, a carboxylic acid, an ester, an ether, a ketone, an aldehyde and a carbonate, and/or a derivative of at least one of the group consisting of an alcohol, a carboxylic acid, boric acid, an ester, an ether, a ketone, an aldehyde and a carbonate.
In a further preferred embodiment, the oxygen containing compound comprises at least one selected from the group consisting of poly alpha-olefin (PAO), glycerol monooleate (GMO), glycerol, H2O and peroxides, more preferably the oxygen containing compound comprises H2O2 or a mixture of H2O and H2O2, in particular H2O2. In another preferred embodiment the oxygen containing compound (lubricant) is glycerol. In still another preferred embodiment, the oxygen containing compound (lubricant) is found in synovial liquid, in particular lubricin-OH. In a further preferred embodiment the oxygen containing compound (lubricant) is PAO-ester.
In a further preferred embodiment, the oxygen containing compound comprises polyalcohols which include at least one selected from the group consisting of inositol, pyrogallol, urushiol, pyrocatechol, resorcinol, hydroquinone, fullerenol, penthaerythritol, other saccharides, their isomers, derivatives and substitution compounds. Examples of the above-mentioned saccharides are agarose, adenosine triphosphate, apiose, amylase, amylopectin, sugar glass, arabinoxylan, alkylglycoside, alginic acid, sodium alginate, aldaric acid, aldose, altrose, aldonic acid, arbutin, allose, idose, inulin, uronic acid, erythritol, erythrose, oligosaccharide, carrageenan, galactose, carboxymethyl cellulose, reducing sugar, xanthan gum, rare sugar, xylan, xylitol, xylulose, xylose, cycloglucan, chitin, chitosan, guar gum, glycogen, glycosaminoglycan, glycosyl group, glyceraldehyde, glucuronoxylan, glucuronolactone, glucuronic acid, glucosamine, glucose, glucomannan, gluconic acid, gulose, ketose, kerato sulfate, gentiobiose, collodion, chondroitin, chondroitin sulfate, saponin, digitonin, cycloawaodorin, cyclodextrin, cytidylic acid, sinigrin, dihydroxy acetone, starch nitrate, cane sugar, GF2, sucralose, sucrose, refined sugar, cellulose, cellulose ester, cellobiose, thickening agent, sorbitol, sorbose, tagatose, polysaccharide, talose, monosaccharide, deoxyribose, dextrin, dermatan sulfate, invert sugar, starch, sugar alcohol, glycoprotein, threose, trehalose, nicotinamide adenine dinucleotide phosphate, nicotinamide adenine dinucleotide, disaccharide, glycoside, hyaluronic acid, fucoidan, fucose, psicose, ptaquiloside, fructose, pectin, heparin, hemicellulose, maltose, mannitol, mannose, lactose, rhamnose, lyxose, ribulose, ribose, rutin and the like.
In a further preferred embodiment, the oxygen containing compound comprises a mixture of at least one of the above-listed polyalcohols and glycerol.
In a further preferred embodiment, the oxygen containing compound comprises a mixture of at least one of the above-listed polyalcohols and H2O.
Preferably, the oxygen containing compound is liquid or gaseous, nanoparticles or thin organic deposited films by any available deposition techniques (Langmuir Blodgett films for example).
Preferably, the sliding surface of the first member is subject to pretreatment before being slid against the second member.
Contaminants (contamination substances) such as fats and oils and the like will be felt uneasy particularly in processing (high precision processing) for precision machines or in precision machines per se; however, such contaminants cannot be present if volatile substances such as H2O2, alcohol or the like is used as the oxygen containing compound (lubricant). Accordingly, it will be understood that the oxygen containing compound is effective for the sliding action (sliding action, for example, in a step of removing a metal die) in a processing step for precision machines such as “watches” and the like, or effective for sliding sections of the precision machines. The oxygen containing compound tends to easily volatilize particularly in cold and warm climates thereby being optimum in contaminant preventing effect. The above-mentioned high precision processing includes a cold processing and a warm processing. The cold processing is a plastic working at a temperature lower than a recrystallization temperature of a metal. The warm processing is a plastic working upon heating a metal material in a temperature range lower than the recrystallization temperature.
Preferably, said pretreatment comprises cleaning; mechanical activation, in particular polishing with specific agent such as H2O2; chemical treatment, in particular by application of H2O2 after physical treatment by laser or electron beam treatment.
Preferably, the sliding surface of the first member is hydrogen-free before application of the oxygen containing compound (OH group containing lubricant) and establishing sliding contact to the second member but build an OH-terminated sliding surface upon entering into sliding contact with the second member, under preceding or simultaneous application of the above-mentioned oxygen containing compound (OH group containing lubricant) on the sliding surface of the first member.
The low-friction lubrication assembly of the present invention is suitable for any application wherein very low friction between two members is desired. The assembly can for example be used in the field of mechanics, physics or medicine. In particular, the assembly is suitable for use in a combustion engine, medical devices (endoscope, catheter, syringe, needle, blood collection tube, medical electronic pump and the like), micromechanical devices, and nanomechanical devices (MEMS; Micro Electromechanical System, NEMS; Nano Electromechanical System, particularly precision machines such as watches or the like), and other low friction requiring systems (shavers, compressors, pumps, gears, bearings and the like). Additionally, tools to be used for machining may encounter a problem in which friction and adhesion occur not only in cutting sections but also at the face and flank thereof due to cutting pieces rolled in; however, by virtue of these low friction assemblies, reduction in driving force during the machining can be expected while a tool life can be largely extended owing to preventing the adhesion.
Regarding the first and second members of the new low friction assembly, a wide variety of materials and combinations is given. Accordingly, the present invention is primarily focused on determining the first member while the second member can reach from biological material, such as for example considering the lubrication assembly being formed by a medicine endoscope and the skin surface of the human body or the surface of inner vessels of the human body up to applications where metals or metal coated surfaces slide on each other such as, machine tooling or engine design, such as sliding components in internal combustion engines. Preferably, at least the first member comprises a smooth surface, said surface being comprised of a thin layer coating such as DLC coating on metal or semi-metal comprising base materials.
The low friction properties of the new system are considered to be based on the unique combination of a sliding surface of the first member comprising an OH-terminated surface, at least after having been in contact with an oxygen containing compound (OH-group containing lubricant), said OH-terminating surface being able to establish hydrogen bonding with a gaseous or liquid lubricant, such as glycerol. The OH-terminated sliding surface is adapted to oppose an OH-terminated opposite surface either established by the lubricant deposition of OH-group on the sliding surface of the second member or the sliding surface of the second member itself establishing an interactive hydrogen bond between the OH-terminated sliding surface of the first and second member and the OH-groups of the oxygen containing compound (lubricant). Preferably, DLC coatings are being used on the side of the first member.
Preferably, there will be a pretreatment of the sliding surface of at least the first member to reduce roughness and install OH hydroxyl groups on the polished surface.
Hereinafter, the present invention is explained in further detail by means of several embodiments thereof in conjunction with the accompanying drawings.
In
Such treatment can be of mechanical (polishing), chemical or mechanochemical (H2O2), or other cleaning or physical nature (electron or ion bombardment) all intended for activating atoms present at the sliding surface.
Preferably, the thickness of the OH-tribofilm is usually in the nanometer range and the OH-tribofilm has a termination made both of hydroxyl groups (OH) and H atoms but even more preferably the termination is made of OH-atoms. It is much preferable to have more than 50% of OH groups on the surface. Even more favorable is 100% of OH groups.
The OH-tribofilm can advantageously form hydrogen bonding with various molecules such as alcohols, esters, ethers, acids, amines, imides, thiols, peroxides and water, and others (boric acid for example). Generally, all molecules susceptible to have hydrogen bonding with water can be candidates.
The termination of the OH-tribofilm with the hydrogen bond-attached molecules has preferably a H-terminated surface.
It has been confirmed that the friction between such H-terminated and OH terminated surfaces is extremely low due to the repulsive forces between positively charged hydrogen atoms. Because of the electronegativity of oxygen atoms, the OH-terminated surface is even more repulsive.
The OH-tribofilm is continuously re-formed if it is needed by the tribochemical reaction.
Due to hydrogen termination between the two sliding surfaces formed by the oxygen containing compound (lubricant) in between, repulsive forces are formed in between the contacting sliding surfaces, the first and second member which is even increased in case of hydroxyl group termination between the two sliding surfaces which is also preferred in view of a high flexibility of a COH-bonding with the OH compound being free to rotate around a C—O bond to assume a stationary position. As compared with well known “OH-terminated surface” having a high surface energy and the property of being not wetted with water within hydrogen bond, “C—OH terminated surface” has a low surface energy and the property of tending to be wetted with water. The reason for this is supposed that “C—H terminated surface” is very strong, and “H” of “C—H terminated surface” cannot form a hydrogen bond with a water molecule under steric hindrance. In this regard, in the hydrogen bond of “C—H 0”, it is preferable that three atoms are generally in alignment with each other. In contrast, as shown in
Preferably, glycerol is used as the oxygen containing compound (lubricating agent) and, due to having 3 OH groups and capable of having three hydrogen bonds per module, allows the molecule to stay longer on a OH terminated surface but having some repulsiveenergy as C—O and C—C bonds are free to rotate around their axle. A glycerol lubricating system can optimize its configuration to have better hydrogen bonding situations considering the different bonding forces in view of the preferred alignment of O—H—O groups. Generally, H-terminated surfaces between the first member and the oxygen containing compound (lubricant)) and/or between the first and second members appear to be more preferable than the provision of OH-terminated surfaces.
In preferred embodiments of the present invention the first member has a coating of a hydrogen free amorphous carbon layer (a-C) or a hydrogen free tetrahedral carbon layer (ta-C). The second member has preferably also a coating of a hydrogen free amorphous carbon layer (a-C) or a hydrogen free tetrahedral carbon layer (ta-C). Particularly preferred are the following combinations of first and second members: a-C coating and a-C coating; ta-C coating and a-C coating; a-C coating and ta-C coating; ta-C coating and ta-C coating. Particularly preferred base materials on which to apply these coatings are SCM415 (carburization) or heat treated SUJ2. The above-mentioned a-C and ta-C are respectively located in ranges shown in a ternary state diagram of
A preferred oxygen containing compound (lubricant) for these members is glycerol.
The hydrogen-free carbon layer such as DLC reacts with OH-groups of the oxygen containing compound (lubricant) immediately upon contact with the oxygen containing compound (lubricant). This leads to the formation of an OH-terminated sliding surface.
With DLC and other materials of interest in particular as the first and second members, a two-steps mechanism is provided: first the creation of an OH-terminated surface based on the tribochemical reaction of surface atoms of the members, such as C, Se, Si, etc. with the hydroxyl groups present in the members of the oxygen containing compound (lubricant). Then the molecules of the oxygen containing compound (lubricant) may adsorb on that crated OH-terminated surface by hydrogen bonding creating a new friction interface of the first and/or second member comprising an H- and/or OH-terminated surface is developed. Thus, repulsive forces along said interface facilitate a new type of low friction lubricated assembly to be created.
Hereinafter, the present invention will be discussed with reference to Examples and Comparative Examples; however, the present invention is not limited to these Examples.
Examples 1 to 9 and Comparative Examples 1 to 4
Plates and pins shown in Table 2 were produced respectively by forming coatings on base materials thereof. Respective produced plates and pins had respectively film thicknesses, surface roughnesses and surface hardnesses as shown in Table 2, similarly.
(Vibration Friction Wear Test (SRV Friction Test))
The obtained plate and pin were set on a vibration friction wear testing machine produced by Optimol Instruments Prüftechnik GmbH, upon which the plate and pin were wetted with a lubricating oil (oil) and underwent a vibration friction wear test (SRV (pin-on-plate) friction test) thereby measuring a friction coefficient. An obtained result is also shown in Table 2.
In further preferred embodiments of the present invention the first member is made of steel, DLC coated steel or Al2O3. Preferably, the second member is also made of steel, DLC coated steel or Al2O3. Particularly preferred are the following combinations of first and second members: steel and Al2O3; DLC/steel and Al2O3; DLC/Al2O3 and DLC/Al2O3; steel and steel; Al2O3 and Al2O3; Al2O3 and DLC/Al2O3; DLC/steel and steel; DLC/Al2O3 and steel; DLC/steel and DLC/steel.
A preferred lubricant for these members is glycerol. The following Table 3 contains experimental data for a combination of glycerol as lubricant with members made of steel, DLC coated steel and Al2O3.
A further preferred oxygen containing compound (lubricant) for these members is PAO-ester. The following Table 4 contains experimental data for a combination of PAO-ester as the oxygen containing compound (lubricant) with members made of steel, DLC coated steel and Al2O3.
In case of using PAO-ester or glycerol lubrication, the friction coefficient is largely lowered even in a ruby (Al2O3)/hydrogen-free DLC system. This is apparent from
Additionally, in case of using PAO-ester or glycerol lubrication as same as the above, the friction coefficient is largely lowered even in a ruby (Al2O3)/steel (Fe; iron) system. This is apparent from
Hereinafter, technical bases of the present invention derived from the above-discussed embodiments will be discussed.
(1) A low-friction lubrication assembly comprising: a first member relatively slidable against a second member, the first member having chemical affinity with an OH-group on its sliding surface; and one or more oxygen containing compounds located on the sliding surface of the first member and being able to produce a tribofilm to be located on the sliding surface of the first member having the chemical affinity, through hydrogen bond interactions with the OH-group.
(2) A low-friction lubrication assembly as described in (1), wherein the second member further has chemical affinity with an OH group, and the tribofilm is also able to be formed on a sliding surface of the second member through hydrogen bond interactions with the OH-group in response to sliding motion.
(3) A low-friction lubrication assembly as described in (1), wherein at least one OH group termination is provided onto the sliding surface in the first member after a certain sliding motion.
(4) A low-friction lubrication assembly as described in (1) or (3), wherein the tribofilm is formed to be located on the sliding surface of the first member through hydrogen bond interactions between at least one OH termination provided to the surface of the first member and an OH group in the oxygen containing compound.
(5) A low-friction lubrication assembly as described in any of (1) to (4), wherein at least one OH group termination is further provided onto the sliding surface of the second member after a certain sliding motion.
(6) A low-friction lubrication assembly as described in (1) to (5), wherein the tribofilm is further formed to be located on the sliding surface of the second member through hydrogen bond interactions between at least one OH termination provided to the surface of the second member and an OH group in the oxygen containing compound.
(7) A low-friction lubrication assembly as described in any of (1) to (6), wherein the first member comprises at least one selected from the group consisting of an amorphous material and a crystallized material.
(8) A low-friction lubrication assembly as described in any of (1) to (7), wherein the first member comprises at least one selected from the group consisting of Si, SiO2, Al2O3, Si3N4, MgO or any single metal or mixed metal combination of oxides, nitrides and carbides.
(9) A supper low-friction lubrication assembly as described in any of (1) to (8), wherein the first member comprises at least one selected from the group consisting of silicon carboxide, oxinitride and carbonitride, a material formed of elements having a chemical affinity and tendency to form hydroxides (for example Metal (OH)x), diamond and diamond-like carbon.
(10) A low-friction lubrication assembly as described in (8) or (9), wherein the diamond-like carbon contains hydrogen in an amount of not more that 10 atomic %.
(11) A low-friction lubrication assembly as described in (10), wherein the diamond-like carbon is formed of diamond-like carbon of a-C type containing substantially no hydrogen or diamond-like carbon of ta-C type.
(12) A low-friction lubrication assembly as described in any of (1) to (11), wherein the second member comprises at least one selected from the group consisting of an amorphous material and a crystallized material.
(13) A low-friction lubrication assembly as described in any of (1) to (12), wherein the second member comprises at least one selected from the group consisting of Si, SiO2, Al2O3, Si3N4, MgO or any single metal or mixed metal combination of oxides, nitrides and carbides.
(14) A supper low-friction lubrication assembly as described in any of (1) to (13), wherein the second member comprises at least one selected from the group consisting of silicon carboxide, oxinitride and carbonitride, a material formed of elements having a chemical affinity and a tendency to form hydroxides (for example Metal (OH)x), diamond and diamond-like carbon.
(15) A low-friction lubrication assembly as described in any of (1) to (12), wherein the second member comprises at least one selected from the group consisting of C, Fe, Al, Mg, Cu, Fe alloy, Al alloy, Mg alloy and Cu alloy.
(16) A low-friction lubrication assembly as described in any of (1) to (15), wherein the oxygen containing compound has at least one hydroxyl group attached to the sliding surface.
(17) A low-friction lubrication assembly as described in any of (1) to (16), wherein the oxygen containing compound comprises at least one of the group consisting of an alcohol, a carboxylic acid, an ester, an ether, a ketone, an aldehyde and a carbonate, and/or a derivative of at least one of the group consisting of an alcohol, a carboxylic acid, an ester, an ether, a ketone, an aldehyde and a carbonate.
(18) A supper low-friction lubrication assembly as described in any of (1) to (17), wherein the oxygen containing compound contains one or more OH groups.
(19) A low-friction lubrication assembly as described in any of (1) to (17), wherein the oxygen containing compound comprises at least one selected from the group consisting of poly alpha-olefin (PAO), glycerol monooleate (GMO), Glycerol, H2O and peroxides.
(20) A low-friction lubrication assembly as described in (1) to (19), wherein the oxygen containing compound comprises H2O2, a mixture of H2O and H2O2, or a mixture of H2O2 and glycerol.
(21) A low-friction lubrication assembly as described in any of (1) to (19), wherein the oxygen containing compound comprises polyalcohol.
(22) A low-friction lubrication assembly as described in (21), wherein the polyalcohol comprises at least one selected from the group consisting of inositol, pyrogallol, urushiol, pyrocatechol, resorcinol, hydroquinone, fullerenol, penthaerythrithol, other saccharides, and their isomers, derivatives and substitution compounds.
(23) A low-friction lubrication assembly as described in (1) to (22), wherein the oxygen containing compound comprises a mixture of at least one of the polyalcohols and glycerol.
(24) A low-friction lubrication assembly as described in (1) to (22), wherein the oxygen containing compound comprises a mixture of at least one of the polyalcohols and H2O.
(25) A low-friction lubrication assembly as described in any of (1) to (24), wherein the oxygen containing compound is found in synovial liquid.
(26) A low-friction lubrication assembly as described in any of (1) to (25), wherein the oxygen containing compound is found in lubricin.
(27) A low-friction lubrication assembly as described in any of (1) to (26), wherein the oxygen containing compound is found in lubricin-OH.
(28) A low-friction lubrication assembly as described in (1) to (27), wherein the oxygen containing compound is liquid or gaseous, nanoparticles or thin organic deposited films by any available deposition techniques, in particular Langmuir Blodgett films.
(29) A low-friction lubrication assembly as described in any of (1) to (28), wherein the sliding surface of the first member is subject to pretreatment before being slid against the second member.
(30) A low-friction lubrication assembly as described in any of (1) to (29), wherein the sliding surface of the second member is further subject to pretreatment before being slid against the first member.
(31) A low-friction lubrication assembly as described in (29) to (30), wherein said pretreatment comprises cleaning; mechanical activation, in particular polishing; chemical treatment by application of the oxygen containing compound; or physical treatment by laser treatment, ion beam treatment or electron beam treatment.
(32) A supper low-friction lubrication assembly as described in (31), wherein the oxygen containing compound for carrying out the chemical treatment is high in volatility.
(33) A supper low-friction lubrication assembly as described in (32), wherein the oxygen containing compound high in volatility is H2O2.
(34) A low-friction lubrication assembly as described in any of (1) to (33), wherein the sliding surface of the first member is hydrogen-free before application of the oxygen containing compound and establishing sliding contact to the second member but comprises an OH-terminated sliding surface upon entering into sliding contact with the second member, under preceding or simultaneous into application of the oxygen containing compound on the sliding surface of the first member.
(35) A combustion engine, wherein the low-friction lubrication assembly as described in (1) to (34) is applied to the combustion engine.
(36) A medical device, wherein the low-friction lubrication assembly as described in (1) to (34) is applied to the medical device.
(37) A medical device as described in (36), wherein the medical device is endoscope, catheter, syringe, needle, blood collection tube, or medical electronic pump.
(38) A shaver, wherein the low-friction lubrication assembly as described in (1) to (34) is applied to the shaver.
(39) A watch, a compressor, a pump, a gear, a machining tool (bite) and a bearing, wherein the low-friction lubrication assembly as described in (1) to (34) is applied to the watch, the compressor, the pump, the gear, the machining tool and the bearing.
(40) A precision processing, wherein the low-friction lubrication assembly as described in (1) to (34) is applied to the precision processing.
(41) A precision processing as described in (40), wherein the precision processing is a cold processing or a warm processing.
(42) A precision instrument, wherein the low friction lubrication assembly as described in (1) to (34) is applied to the precision instrument.
(43) A watch to which a low-friction lubrication assembly is applied, wherein the low-friction lubrication assembly comprises: a first member relatively slidable against a second member, the first member having chemical affinity with an OH-group on its sliding surface; and one or more oxygen containing compounds located on the sliding surface of the first member and being able to produce a tribofilm to be located on the sliding surface of the first member having the chemical affinity, through hydrogen bond interactions with the OH-group.
(44) A watch as described in (43), wherein the second member further has chemical affinity with an OH group, and the tribofilm is also able to be formed on a sliding surface of the second member through hydrogen bond interactions with the OH-group in response to sliding motion.
(45) A watch as described in (43), wherein at least one OH group termination is provided onto the sliding surface of the first member after a certain sliding motion.
(46) A watch as described in (43) or (45), wherein the tribofilm is formed to be located on the sliding surface of the first member through hydrogen bond interactions between at least one OH termination provided to the surface of the first member and an OH group in the oxygen containing compound.
(47) A watch as described in any of (43) to (46), wherein at least one OH group termination is further provided onto the sliding surface of the second member after a certain sliding motion.
(48) A watch as described in any of (43) to (47), wherein the tribofilm is further formed to be located on the sliding surface of the second member through hydrogen bond interactions between at least one OH termination provided to the surface of the second member and an OH group in the oxygen containing compound.
(49) A watch as described in any of (43) to (48), wherein the first member contains at least Al2O3.
(50) A watch as described in any of (43) to (49), wherein the second member contains at least one selected from the group consisting of Fe and Fe alloy.
(51) A watch as described in any of (43) to (50), wherein the oxygen containing compound contains at least one selected from the group consisting of poly alpha-olefin (PAO), glycerol monooleate (GMO) and glycerol.
(52) A watch as described in any of (43) to (51), wherein the first member is made of Al2O3, the second member is made of Fe or Fe alloy, and the oxygen containing compound is glycerol.
(53) A watch as described in any of (43) to (52), wherein the first member made of Al2O3 is a fluke disposed in an anchor, and the second member made of Fe or Fe alloy is an escapement wheel.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2006-125623 | Apr 2006 | JP | national |
| 2006-234759 | Aug 2006 | JP | national |
The present application is a continuation application of U.S. application Ser. No. 12/298,665, filed on Oct. 27, 2008, which is the U.S. national stage of International Application No. PCT/JP2007/059178, filed on Apr. 27, 2007, which claims priority from Japanese Patent Application No. 2006-125623 filed Apr. 28, 2006 and Japanese Patent Application 2006-234759 filed Aug. 31, 2006. The entire disclosures of each of the-above-referenced applications are incorporated herein by reference.
| Number | Name | Date | Kind |
|---|---|---|---|
| 5300951 | Yamazaki | Apr 1994 | A |
| 6806242 | Shirahama et al. | Oct 2004 | B2 |
| 6858567 | Akao | Feb 2005 | B2 |
| 7134381 | Ueno et al. | Nov 2006 | B2 |
| 7427162 | Kano et al. | Sep 2008 | B2 |
| 7458585 | Hamada et al. | Dec 2008 | B2 |
| 7771821 | Martin et al. | Aug 2010 | B2 |
| 7833951 | Hayashi et al. | Nov 2010 | B2 |
| 7951756 | Konishi et al. | May 2011 | B2 |
| 20020191493 | Hara | Dec 2002 | A1 |
| 20040241448 | Kano et al. | Dec 2004 | A1 |
| 20050025975 | Okamoto et al. | Feb 2005 | A1 |
| 20050064196 | Martin et al. | Mar 2005 | A1 |
| 20050082139 | Ishikawa et al. | Apr 2005 | A1 |
| 20050084390 | Ueno et al. | Apr 2005 | A1 |
| 20050100701 | Hamada et al. | May 2005 | A1 |
| 20060240996 | Hayashi et al. | Oct 2006 | A1 |
| 20060263604 | Martin et al. | Nov 2006 | A1 |
| 20090186783 | Martin et al. | Jul 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 1 338 641 | Aug 2003 | EP |
| 1 510 594 | Mar 2005 | EP |
| 1 201 734 | Jun 2006 | EP |
| 1 503 113 | May 2008 | EP |
| 52-008857 | Jan 1977 | JP |
| 08-225795 | Sep 1996 | JP |
| 10-204466 | Aug 1998 | JP |
| 2003-238982 | Aug 2003 | JP |
| 2004-262960 | Sep 2004 | JP |
| 2004-359727 | Dec 2004 | JP |
| 2005-061610 | Mar 2005 | JP |
| 2005-089735 | Apr 2005 | JP |
| 2005-090738 | Apr 2005 | JP |
| 2005-097570 | Apr 2005 | JP |
| 2005-098289 | Apr 2005 | JP |
| 2005-098495 | Apr 2005 | JP |
| 2005098495 | Apr 2005 | JP |
| 2006-213745 | Aug 2006 | JP |
| WO-0159043 | Aug 2001 | WO |
| WO-2007126057 | Nov 2007 | WO |
| Entry |
|---|
| Robertson, J., in Tribology of Diamond-like Films, Donnet, C., Erdemir, A., Eds. Springer, 2008, p. 14. |
| Walters, J.K., Gilkes, K.W.R., Wicks, J.D., Newport, R.J., “Progress in modeling the chemical bonding in tetrahedral amorphous carbon”, Phys. Rev. B, 1998, 58(13), 8267-8276. |
| F. J. Clough, B. Kleinsorge, W. I. Milne and J. Robertson (1996). Tetrahedral Amorphous Carbon Thin Film Transistors. MRS Proceedings, 423, 39 doi:10.1557/PROC-423-39. |
| “About Testing method for Watch Oils”, The Horological Institute of Japan, Dec. 15, 1959, pp. 1-11. |
| Advisory Action U.S. Appl. No. 12/298,665 dated Sep. 26, 2011. |
| Andersson, J. et al., “Frictional behavior of diamondlike carbon films in vacuum and under varying water vapor pressure”, Surface and Coatings Technology, 2003, vols. 163-164, pp. 535-540. |
| F.J. Clough et al., 1996, “Tetrahedral Amorphous Carbon Thin Film Transistors”, MRS Proceedings, 423, 39 doi: 10.1557/PROC-423-39. |
| Final Office Action U.S. Appl. No. 12/298,665 dated Apr. 13, 2012. |
| Final Office Action U.S. Appl. No. 12/298,665 dated Jun. 2, 2011. |
| Japanese Industrial Standard, “Chromium Molybdenum Steels,” JIS G 4105, 1979, pp. 1-11. |
| Japanese Industrial Standard, “High carbon chromium bearing steels,” JIS G 4805, 1999, pp. 1-31. |
| Kakuta K. “World of Friction—Macro and Micro—Tribology”, Journal of the Horological Institute of Japan, 1996, No. 159, pp. 41-48. |
| Kano, M., et al. “Ultralow friction of DLC in presence of glycerol mono-oleate (GMO)”, Tribology Letters, Feb. 2005, vol. 18, No. 2, pp. 245-251. |
| Non-Final Office Action U.S. Appl. No. 12/298,665 dated Dec. 3, 2010. |
| Non-Final Office Action U.S. Appl. No. 12/298,665 dated Nov. 15, 2011. |
| Notice of Allowance U.S. Appl. No. 12/298,665 dated Feb. 4, 2013. |
| Office Action JP Patent Appln. No. 2006-263818 dated Nov. 15, 2011. |
| Office Action JP Patent Appln. No. 2008-513293 dated Jul. 1, 2011. |
| Office Action Japanese Patent Application No. 2006-263818 dated May 29, 2012. |
| Office Action U.S. Appl. No. 12/298,665 dated Oct. 26, 2012. |
| Robertson, J., in Tribology of Diamond-like Films, Donnet, C., Erdemir, A., Eds., Springer, 2008, p. 14. |
| Walters J.K., “Progress in modeling teh chemical bonding in tetrahedral amorphous carbon”, Phys Rev. B, 1998, 58(13), 8267-8276. |
| Yasuda et al., “Ultralow friction of DLC in presence of glycerol mono-oleate (GMO)”, Tribology Letters, 2005, vol. 18(2), pp. 245-251. |
| Yuji Akao, “Development for New Lubricant for Watch Mechanism”, Dec. 20, 2000, Micromechatronics, vol. 45, No. 1, 2001, pp. 27-33. |
| Number | Date | Country | |
|---|---|---|---|
| 20130190216 A1 | Jul 2013 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 12298665 | US | |
| Child | 13797346 | US |