Low oxygen cubic boron nitride and its production

Abstract

A method for improving the toughness of a CBN product made by a high temperature/high pressure (HP/HT) process commences by forming a blend of an oxygen getter and CBN product-forming feedstock. The blend is subjected to a CBN high temperature/high pressure (HP/HT) process for forming a CBN product. The amount of oxygen getter in the blend is sufficient to improve the toughness of the CBN product. The resulting CBN product desirably has an oxygen content of less than about 300 ppm. Oxygen getters include Al, Si, and Ti. The HP/HT process is conducted in the absence or presence of catalytic materials.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS

[0001] None

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH

[0002] Not applicable.

BACKGROUND OF THE INVENTION

[0003] The present invention relates to cubic boron nitride (CBN) materials and more particularly to a CBN product, which has very high toughness and high thermal stability.

[0004] Cubic boron nitride (CBN) is the second hardest material known to man after diamond. The manufacture of CBN by the high pressure/high temperature (HP/HT) process is known in the art and is typified by the process described in U.S. Pat. No. 2,947,617, a basic monocrystalline CBN case. U.S. Pat. No. 4,188,194 describes a process for making sintered polycrystalline CBN compacts which utilizes pyrolytic hexagonal boron nitride (PBN) in the absence of any catalyst. An improvement on such direct conversion process is disclosed in U.S. Pat. No. 4,289,503 wherein boric oxide is removed from the surface of the HBN powder before the conversion process. U.S. Pat. No. 5,106,792 manufactures a CBN composite mass from a mixture of different structural forms of graphitic boron nitride (GBN) in the absence of any catalyst.

[0005] A compact is a mass of abrasive particles bonded together in a self-bonded relationship (see U.S. Pat. Nos. 3,852,078 and 3,876,751); by means of a bonding medium (U.S. Pat. Nos. 3,136,615, 3,233,988, 3,743,489, 3,767,371, and 3,918,931); or by means of combinations thereof. A composite compact is a compact bonded to a substrate material, such as cemented metal carbide. U.S. Pat. No. 3,918,219 teaches the catalytic conversion of hexagonal boron nitride (HBN) to CBN in contact with a carbide mass to form a composite CBN compact. Compacts or composite compacts may be used in blanks for cutting tools, drill bits, dressing tools, and wear parts (see, for example, U.S. Pat. Nos. 3,136,615 and 3,233,988).

[0006] Polycrystalline CBN compacts often are used in machining hard ferrous alloy workpieces due to their relatively non-reactivity with ferrous workpieces. Accordingly, CBN materials often are formed into cutting, milling, and turning tools. The toughness of the CBN crystals, as measured by a standard friability test, can be a factor in grinding performance. The friability test involves ball milling a quantity of product under controlled conditions and sieving the residue to measure the breakdown of said product. The toughness index (TI) is measured at room temperature, and the thermal toughness index (TTI) is measured after the product has been fired at a high temperature. In many cases, the tougher the crystal, the longer the life of the crystal in a grinding or machining tool and, therefore, the longer the life of the tool. This leads to less tool wear and, ultimately, lower overall tool cost.

[0007] Corrigan, et al., “Direct Transition Among Allotropic Forms of Boron Nitride at High Pressures and Temperatures”, The Journal of Chemical Physics, Vol 63. No. 9, page 3812 (Nov. 1, 1975) discusses the effects of impurities (e.g., oxygen) in the HP/HT conversion of HBN to CBN (see page 3814). Dreger, et al., “Sublimation and Decomposition Studies on Boron Nitride and Aluminum Nitride”, J. Phys. Chem., 66, p. 1556 (1962) proposes heating BN to 1200°-2000° C. to evolve nitrogen gas and leave a coating of boron. Vacuum firing of isotropic HBN to remove boron oxide preparatory to metallizing is mentioned in U.S. Pat. No. 3,926,571 at col. 3. Preliminary drying of HBN is disclosed in U.S. Pat. No. 4,150,098 at col. 3. Finally, U.S. Pat. No. 4,289,503 pre-treats HBN at a temperature in the HBN thermal decomposition range by vacuum firing or heating under inert atmosphere to remove boric oxide and leave a surface coating of boron. The pre-treated HBN, then, is converted into CBN.

BRIEF SUMMARY OF THE INVENTION

[0008] Regardless of the technique employed to manufacture CBN product, the toughness index (TI) of the CBN product can be improved by conducting the high temperature/high pressure (HP/HT) manufacturing process in the presence of an oxygen getter. Oxygen getters include, inter alia, Al, Si, and Ti. The HP/HT process is conducted conventionally, including in the absence or presence of catalytic materials. Optionally, the HBN feedstock to the HP/HT process can be pre-treated to remove oxides therefrom.

[0009] Another aspect of the present invention is a CBN product having an oxygen content of less than about 300 ppm, advantageously less than about 200 ppm, and preferably less than about 100 ppm.

[0010] Advantages of the present invention include the ability to improve the toughness index of any CBN product, regardless of how it is manufactured. Another advantage is the ability to improve the toughness index of a CBN product without deleteriously adversely affecting other desired properties of the CBN product. A further advantage is the ability to make an ultra-low oxygen-containing CBN product. These and other advantages will be apparent to those skilled in the art based on the present disclosure.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011] For a fuller understanding of the nature and objects of the present invention, reference should be made to the following detailed description taken in conjunction with the accompanying drawings, in which:

[0012] FIG. 1 plots crystal toughness versus oxygen content for a variety of CBN crystals as manufactured;

[0013] FIG. 2 plots crystal toughness versus oxygen content for a variety of CBN crystals that have been subjected to heat treatment;

[0014] FIG. 3 plots crystal toughness versus oxygen content for CBN crystals as manufactured using one catalyst system; and

[0015] FIG. 4 plots crystal toughness versus oxygen content for CBN crystals manufactured using one catalyst system and which have been subjected to heat treatment.

[0016] The drawings will be described in more detail below.

DETAILED DESCRIPTION OF THE INVENTION

[0017] The present invention is directed to CBN crystals having measured oxygen levels below, for example, about 300 ppm. Such crystals can be grown by any known chemistry under conditions that exclude oxygen, such as, for example, by including oxygen gettering materials (an “oxygen getter”) in the growth chemistry. Suitable oxygen getters include, for example, Al, Si, or Ti, which form very stable oxides, can act to lower the oxygen in the synthesis chemistry to yield crystals having oxygen levels below the target about 300 ppm.

[0018] The amount of oxygen getter added to the feedstock is sufficient to lower the oxygen content of the CBN product to the desired level, i.e., achieve a desired target TI. Excess amounts of oxygen getter can be used at the risk of affecting other desired properties of the CBN product. Broadly, then, the amount of oxygen getter can range from about 0.005 to 0.5 wt-% of the feedstock to the reaction cell.

[0019] The oxygen getter, for example, Al, Si, or Ti, can be present in the reaction cell in one or more of the following forms: (a) elemental metal, and (b) any compound whose free energy of formation is higher than that of the oxide, carbide, nitride, etc., of the metal. The oxygen getter is converted into an oxide during the CBN manufacturing process. Such oxygen getter oxides generally are not incorporated into the CBN crystals, making their removal by subsequent processing practical and not cost prohibitive.

[0020] Any technique for production of CBN crystals can be used in accordance with the present invention. Thus, sintered CBN crystals, compacts and re-sintered CBN material can have its toughness improved by reducing the amount of oxygen present. In the catalytic formation of CBN, catalytic and bonding materials may be used, such as detailed in U.S. Pat. Nos. 3,233,988 and 3,918,219 with reference to catalytically formed CBN compacts and U.S. Pat. Nos. 3,743,489 and 3,767,371 with respect to bonding mediums. Single crystal CBN also can be made in the presence of catalyst metal or alloy from HBN.

[0021] A preferred direct conversion process is taught in U.S. Pat. No. 4,188,194 wherein a sintered polycrystalline CBN compact is made by placing preferentially oriented pyrolytic hexagonal boron nitride (PBN) in a reaction cell wherein the boron nitride is substantially free of catalytically active materials. Reaction cell conditions include a pressure of between about 50 and 100 Kbars and a temperature of at least about 1800° C. within the CBN stable region of the BN phase diagram. When HBN is milled to a small particle size, an improved process is disclosed in U.S. Pat. No. 4,289,503 wherein the boric oxide is removed from the surface of the HBN powder before the conversion process. U.S. Pat. No. 5,106,792 manufactures a CBN/CBN composite mass from mixtures of different structural forms of GBN. U.S. Pat. No. 4,673,414 re-sinters polycrystalline CBN by a catalyst-free HP/HT process. Variations on these processes also are known in the art. The disclosure of these citations is expressly incorporated herein by reference. Thus, a HP/HT process for forming a CBN product and a CNB product-forming feedstock can be found in the references cited herein.

[0022] While the invention has been described with reference to a preferred embodiment, those skilled in the art will understand that various changes may be made and equivalents may be substituted for elements thereof without departing from the scope of the invention. In addition, many modifications may be made to adapt a particular situation or material to the teachings of the invention without departing from the essential scope thereof. Therefore, it is intended that the invention not be limited to the particular embodiment disclosed as the best mode contemplated for carrying out this invention, but that the invention will include all embodiments falling within the scope of the appended claims. In this application all units are in the metric system and all amounts and percentages are by weight, unless otherwise expressly indicated. Also, all citations referred herein are expressly incorporated herein by reference.

EXAMPLES

Example 1

[0023] FIG. 1 shows crystal toughness, as measured by a standard toughness test, versus oxygen content, as measured by a LECO oxygen and nitrogen analyzer (Model TC436, supplied by Leco Corporation, 3000 Lakeview Avenue, St. Joseph, Mich.) for a variety of CBN products. These CBN products were made from catalyst systems containing primarily alkali and alkaline earth metal nitrides, amides, hydroxides, and hydrides. Similarly, FIG. 2 shows crystal toughness after thermal treatment at 800° C. for 30 minutes versus oxygen content. Thermal treatment of the CBN product is intended to simulate the thermal profile experienced by the CBN crystals during wheel manufacture. The data for FIGS. 1 and 2 also are set forth in Table 1, below.

TABLE 1
Average		Weight
Oxygen		Assigned for		Thermal
Concentration	Standard	Linear	Toughness	Toughness
(ppm)	Deviation	Regression	Index (TI)	Index (TTI)
1091	71	0.000198	53.1	54.6
1072	72	0.000193	65.4	64.9
996	37	0.00073	65.6	64.9
856	25	0.0016	51.1	49.3
1803	119	7.06 E − 05	54.7	40.8
1674	137	5.33 E − 05	54.5	45.6
1471	29	0.001189	53.1	64.8
393	32	0.000977	67.4	64.8
335	17	0.00346	72.8	68.1
611	50	0.004	66.5	68
1321	18	0.003086	56.5	54.4
1261	80	0.000156	60.1	55.6
1225	21	0.002268	62.2	67.2
1189	65	0.000237	62.7	66

[0024] It is clear that the average toughness of the CBN crystals increases with decreasing oxygen content for the variety of materials tested. The strength of the effect of oxygen content is approximately 50% higher (line slope in FIG. 2 versus FIG. 1) for materials after thermal treatment.

Example 2

[0025] The materials tested for FIGS. 1 and 2 represent a wide variety of synthesis chemistries, as noted above. If the tests are restricted to materials synthesized using a single chemistry system the influence of oxygen content on toughness becomes more pronounced. Thus TI testing of CBN crystals manufactured using a lithium nitride, lithium hydride, lithium hydroxide catalyst system was undertaken. The results of these tests are displayed in FIGS. 3 and 4, and in Table 2, below.

TABLE 2
Average		Weight
Oxygen		Assigned for		Thermal
Concentration	Standard	Linear	Toughness	Toughness
(ppm)	Deviation	Regression	Index (TI)	Index (TTI)
1803	119	7.06 E − 05	54.7	40.8
1674	137	5.33 E − 05	54.5	45.6
1471	29	0.001189	53.1	52.9
611	50	0.004	66.5	68
1321	18	0.003086	56.5	54.4
1261	80	0.00156	60.1	55.6
1225	21	0.002268	62.2	67.2
1189	65	0.000237	62.7	66

[0026] As shown in FIGS. 3 and 4, the impact of oxygen content on toughness after thermal treatment is particularly high, as can be seen from the slopes of the curves. The improved correlation arises because fewer variables are uncontrolled when using the same catalyst system to synthesize crystals with varying oxygen content.

[0027] These test results lead to the conclusion that lower oxygen content improves toughness of CBN crystals, regardless of the chemistry used to synthesize the CBN crystals. Such tougher crystals are expected to exhibit a longer life in grinding or machining and, therefore, lead to a longer life of the tool. A long tool life leads to less tool wear and, ultimately, lower overall tool cost.

Example 3

[0028] In this example, Variant I represents CBN crystals made with a Li3N, LiOH, LiH catalyst system. Variant II represents CBN crystals made with a Li3N LiH catalyst system in which the total amount of Li was the same as in the Variant I runs. Three runs of each catalyst system were conducted. The data recorded is set forth in Table 3, below.

	TABLE 3
		Avg.	Std.
	Oxygen (ppm)	Oxygen	Dev.
Material	Run 1	Run 2	Run 3	(ppm)	Oxygen	TI	TTI	TI-TTI
Variant I	1879	1863	1666	1803	119	54.7	40.8	13.9
Variant II	1305	1316	1341	1321	18	56.5	54.4	2.1

[0029] These results demonstrate that the use of oxygen containing catalysts contributes oxygen to the product CBN crystals, which lowers the TI and TTI of such crystals.

Example 4

[0030] In these series of runs, Variant I represents Variant I of Example 2. Variant III represents the same catalyst system, but with 0.12 wt-% of elemental Si added. Variant IV represents the same catalyst system, but with 0 .2 wt-% of Si3N4 added (same Si content in Variant III). The data recorded is set forth in Table 4, below.

	TABLE 4
		Avg.	Std.
	Oxygen (ppm)	Oxygen	Dev.
Material	Run 1	Run 2	Run 3	(ppm)	Oxygen	TI	TTI	TI-TTI
Variant I	1879	1863	1666	1803	119	54.7	40.8	13.9
Variant III	1195	1250	1121	1189	65	62.7	66.0	−3.3
Variant IV	1236	1201	1239	1225	21	62.2	67.2	−5.0

[0031] These results demonstrate that both elemental Si as well as silicon nitride are effective oxygen getters. Impressive is the increase in thermal toughness index compared to room temperature toughness index.

Example 5

[0032] In this series of runs the affect of different concentrations of oxygen getter was evaluated. Variant V used the LiNH2, LiH catalyst system with 0.75 wt-% of Si3N4 added. Variant VI used the same catalyst system, but with 1.8 wt-% of Si3N4 added. The results recorded are set forth in Table 5, below.

	TABLE 5
		Avg.	Std.
	Oxygen (ppm)	Oxygen	Dev.
Material	Run 1	Run 2	Run 3	(ppm)	Oxygen	TI	TTI	TI-TTI
Variant I	1879	1863	1666	1803	119	54.7	40.8	13.9
Variant V	392	362	426	393	32	67.4	64.8	2.6
Variant VI	343	315	346	335	17	72.8	68.1	4.7

[0033] These results again show improvement in toughness by dint of the addition of an oxygen getter. These results also demonstrate that, for the chemistry tested, the higher oxygen getter content is needed in order to lower the oxygen content to around the desired 300 ppm level. While the data reported herein has not yet achieved the target 300 ppm level of oxygen, it does demonstrate that for any given CBN chemistry, its toughness can be improved by lowering the oxygen content thereof. It also demonstrates that the target 300 ppm level can be achieved.

Claims

1. A method for improving the toughness of a CBN product made by a high temperature/high pressure (HP/HT) process, which comprises the steps of: (a) forming a blend of an oxygen getter and CBN product-forming feedstock; (b) subjecting said blend to a CBN high temperature/high pressure (HP/HT) process for forming a CBN product; the amount of oxygen getter in said blend being sufficient to improve the toughness of said CBN product.

2. The method of claim 1, wherein said oxygen getter is one or more of Al, Si, or Ti.

3. The method of claim 1, wherein the amount of oxygen getter is between about 0.005 and 0.5 wt-%.

4. The method of claim 2, wherein the amount of oxygen getter is between about 0.005 and 0.5 wt-%.

5. The method of claim 2, wherein said oxygen getter is in the form of one or more of an elemental metal, metal carbide, or metal nitride.

6. The method of claim 4, wherein said oxygen getter is in the form of one or more of an elemental metal, metal carbide, or metal nitride.

7. The method of claim 1, wherein the amount of oxygen getter is adequate to lower the oxygen content of said CBN product to less than about 300 ppm.

8. The method of claim 1, wherein said HPIHT process is conducted in one or more of the absence of a catalyst or the presence of a catalyst.

9. The method of claim 8, wherein said HP/HT process is conducted in the presence of a catalyst devoid of oxygen content.

10. The method of claim 7, wherein said HP/HT process is conducted in the presence of a catalyst devoid of oxygen content.

11. The method of claim 1, wherein said oxygen getter is removed from said CBN product.

12 The method of claim 7, wherein said oxygen getter is removed from said CBN product.

13. The method of claim 9, wherein said oxygen getter is removed from said CBN product.

14. The method of claim 10, wherein said oxygen getter is removed from said CBN product.

15. The product of the process of claim 7.

16. The product of the process of claim 10.

17. The product of the process of claim 12.

18. The product of the process of claim 14.